By J. A. Snyder, W. L. Finlay

SEVERAL notable studies of the effects of sub- stitutional solutes have been reported. Outstanding among these for its elucidation of general principles, is the summarized work of Hume-Rothery and coworkers.1 For a systematic study of the effects of substitutional solutes on the mechanical properties of the solvent lattice, the work of Brick, Martin, and Angier² on copper; of Frye and coworkers³,4,5 on copper and silver; and of Lacy and Gensamer6 and of Austin7 on iron may be mentioned. Titanium is one of the few elements offering the possibility of a similar study of interstitial solutes since, unlike most metallic elements, it exhibits extended solid solubility for most of the interstitial solutes—hydrogen, boron, nitrogen, oxygen, and carbon. This paper reports a survey of the effects of dilute solutions of nitrogen, oxygen, and carbon on the mechanical properties of high-purity alpha titanium. Previous Work: Van Arkel and De Boer showed" that high purity titanium was quite ductile and De Boer, Burgers and Fast established".' that not only were oxygen and nitrogen very soluble in solid titanium but that, long before the limit of solid solubility of either had been reached, these interstitial solutes rendered the metal brittle. Their electrical resistance data as a function of

Jan 1, 1951

By T. E. Eagan, W. R. McCrackin

IN dealing with segregation in babbitt, and its effect on the final cast structure, which is a bearing, it is obviously impossible to cover all of the compositions manufactured. Each composition, of course, will exhibit certain specific types of segregation. However, as examples,, two compositions of babbitt are presented: one a tin-base of well-known analysis and the other a lead-base, which in the past few years has found wide usage. Bearings usually are cast either statically or centrifugally; therefore the effect of these two methods on segregation is presented. EXPERIMENTAL PROCEDURE A slab of babbitt 1/2 in. thick by 5 in. wide and 17 in. long was cast, using a book mold with the long edge vertical. An A.S.T.M. grade 2 babbitt was used (3.5 per cent copper, 7.5 per cent antimony, remainder tin), to which 0.10 per cent tellurium had been added. Unfortunately, no metal without tellurium was available. The mold to hold the babbitt was heated to approximately 300°F., the temperature being judged by the babbitter. The pouring temperature of the babbitt was 875°F. (470°C.). One slab was made by allowing the babbitt to cool without stirring. The other slab was stirred during the entire cooling cycle. This stirring consisted of a vigorous churning or puddling into the mold until complete solidification had taken place. Three samples were removed from these slabs. One was taken at the extreme bottom, another half way to the top, and another at the extreme top, all at the center of the width. Chemical, macroscopic and microscopic examination was made of all samples. Table I shows the chemical analyses obtained at the described positions [ ] in the slab. The analyses show no serious amount of gravity segregation. Microscopic examination from edge to edge of the slab showed little change in structure. From top to bottom there was a progressive coarsening of the grain size in the stirred slab but little change in the slab that was not stirred (Fig. I). No definite exhibit of segregation could be detected. In line with our experimental study on the tin-base babbitts, we cast an almost duplicate slab using A.S.T.M. Alloy No. 15, containing 0.9 to 1.25 per cent tin, 14.75 to 15.5. per cent antimony, 0.80 to 1.25 per cent arsenic and 0.4 per cent copper. The slab was 16 in. long and 3/8 in. thick, cast with the long side vertical. One slab was allowed to cool normally and the other was stirred continually during cooling. The pouring temperature of the babbitt was

Jan 1, 1944

By Cyril Wells, Robert F. Mehl

The purpose of this investigation was to prepare high-purity iron-carbon alloys, to determine as precisely as possible the A3(GOS), the Acm(SE), and the A1(PSK) transformation temperatures in the meta-stable iron-iron carbide system (up to 1.4 per cent C), and to study the influence of carefully controlled and constant rates of heating and cooling (1/8 to 2o C. per minute) upon the transformation temperature and upon the resulting microstructure. Apart from the general metallurgical importance attending the completion of such a task, it will be noted that highly precise transformation temperatures are of interest and importance in the thermodynamic study of this system1. Several determinations of the iron-iron carbide diagram have been made2. These suffer generally from the low purity of the alloys used, and from the application of methods of investigation of low sensitivity. Attempts to compare and weight the many data available in an effort to construct as accurate a diagram as possible have, in the main, been unsuccessful. In general, the wide differences in the results of different workers, the lack of complete analytical data, the omission of important details relating to the heat-treatment of the alloys, and the meager description of the methods of investigation applied, render such a process of averaging nearly meaningless. It may be seen from the summaries by Epstein2 and Körber and Oelsenl that variations as great as 30' C. exist in the reported data on the A3 temperatures in iron-carbon alloys. Fortunately, the Aa temperature in pure iron is now known to be 910" C. ± 1° C.3 The best recent work on iron-carbon alloys is that of Esser4 on hypoeutectoid steels and that of Sato5 on both hypoeutectoid and hyper-eutectoid steels. Esser made a dilatometric and magnetic study of iron and iron-carbon alloys containing 0.06 to 0.86 per cent C, for which a high purity is claimed. Presumably the electrolytic iron was reasonably pure, but the alloys contained considerable impurities, on the average totaling 0.35 per

Jan 1, 1937

By Keijiro Nishio

At a time of great antiquity when our Yomato tribe had not yet found its way throughout the country, there lived in Japan barbarous tribes of the stone age, whose dwellings were vertical caves covered with roof's of twigs and weeds. In a cave lately discovered at the village of Morita, 10 miles west from the port of Aomori, there were found pieces of micaceous iron-ore and psilomelane, with oval holes pierced from both sides. Apparently these objects were regarded as ornaments or curios, without being applied to any practical use. Among the traditions given in the Nihonshoki, an ancient history of Japan, there is one relating to the mining industry. According to this tradition, in the mythological age Izanami-no-Mikoto gave birth to Kanayamahiko-no-Mikoto, god of mines, and Amaterasu-Okami (the sun-goddess) was armed with swords. It came to pass at one time that she concealed herself in Ama-no-Iwato ("Heavenly Cave"), and several gods made contrivances to entice her out. Among them, Ishikori-dome, a smith, made a mirror with copper obtained from the Ama-no-Kagoyama, by means of a pair of bellows known as the Ama-no-habuki, which was made of a deer-skin. It is recorded also that Susanb-no-Mikoto, her younger brother, observed the abundance of gold and silver in Korea, where his descendants were to reign, and urged them to provide themselves with boats to convey them across the Sea of Japan. In the course of time he accomplished his object, proceeding to Korea with his son, Isotakeru-no-Mikoto. These accounts

Jan 1, 1913

By H. G. Moulton

THE INCREASING scale of mining operations over the past decade, particularly in connection with the exploitation of large bodies of comparatively low-grade copper ores, has made necessary the study of the behavior of rock under failure. When extractions of as high as 40,000 tons a day are reached in steam-shovel operations and as high as 20,000 tons per day in underground mining operations, it is evident that excavations soon become of such size that the behavior of the rock will often be dependent on fundamental principles applicable to more or less homogeneous materials under stress, rather than on weathering or local planes of weakness. In the ordinary rock excavations encountered in civil-engineering practice, such as excavations for subways, highways, railroads, etc., rock faces are not carried to depths sufficient to develop any pressures, or consequently any failures, except those due to loose masses resulting from local planes of weakness. When, however, orebodies whose tonnage is measured by hundreds of thousands are to be extracted by steam-shovel operations in open pits, it is necessary to determine if possible in advance the slopes that the sides of the pits will assume, for these slopes influence the shape of the excavations and thereby the amount of ore that may be extracted by the open-pit method. When large orebodies are mined underground at depths of 300 to 500 ft. (91 to 152 m.) by caving methods, the surface subsiding as the ore is withdrawn, it is necessary to determine in advance the outermost limits of fracture in the subsiding surface, for on the delineation of these limits depends the location of surface improvements, mills, smelters, etc. and also the location of development work, such as hoisting shafts, main haulage levels, and all other underground openings that must remain undisturbed during the period of ore extraction. Heretofore, in civil-engineering practice, it has been assumed that earth and rock behave differently in failure. For the calculation of earth

Jan 2, 1920

By Sidney Powers

CONTENTS PAGE Distribution of fields 4 History of development 6 Origin of oil 7 Structure, accumulation and migration 8 Reservoir rocks 9 Methods of drilling and exploration 10 Oil-field statistics : 12 Description by regions: United States: Appalachian region ; 12 East-central states 17 Kansas 18 Oklahoma : 19 Texas : 24 Arkansas : 32 Louisiana 33 Mississippi ....... 34 Rocky Mountain region : 34 California 37 Canada 41 Mexico 43 Cuba 46 Bibliography 46 THE purpose of this brief account- of the occurrence of petroleum in North America is to make available to those who have a knowledge of geology, but who are not engaged in the petroleum industry, a few salient facts about the location of oil and gas fields, their productivity, the important structural types of accumulation and the age of the rocks containing petroleum. A few useful data and statistics are furnished, yet not complete statistics that are available elsewhere. Geology has been treated in simple terms because the reader is presumed to have little interest in the names of formations and of oil sands. Mineral deposits are more or less analogous. Whether oil or metals, minerals are found in rocks, largely in sedimentary rocks which carry water or have at one time carried it. A genetic or accumula-

Jan 1, 1931

By R. G. Hudson, L. Yang

In electrochemical separation of metals, it is necessary to control the potential applied between the electrodes so that only the desired electrode reactions can occur. A knowledge of the minimum potential needed for a given electrode reaction to take place continuously is therefore pertinent to the success of the process. In molten chloride systems at high temperatures, activation polarization is believed to be small,1,2 so the minimum potential needed for the electrolytic decomposition of a molten metal chloride MC1n (n = valence of the metal ion) is therefore essentially the equilibrium electrode potential E of the metal-chlorine galvanic cell in the solution. If the decomposition products are pure M and chlorine at a pressure of p atm, E*Eo-rt/nf in [i] Since EO (the standard electrode potential of MCln) is a constant at a given temperature and R (the gas constant), and F (the Faraday's constant) are all constants, the variation of E with the electrolytic bath conditions is largely determined by the effect of the latter on the activity of the metal chloride amcln (standard state = pure MC1,). Measurement of E and study of how amCin varies with temperature and concentration, the nature of the solvent, and that of the coexisting solutes are therefore pertinent in the selection of optimum operating conditions for the electrochemical separation of metals. Because of its low melting point, high decomposition potentials of its components, and the low solubility of heavier metals in it, the LiC1-KC1 eutectic melt is a useful solvent and has been used in the electrodeposition of Mo,3Ce,4 and u5 metals. Senderoff and Brenner3 measured the potentials of Zn/Zn++, Fe/Fe++, Cu/Cu+, Mo/Mo+++, and Ag/Ag+ against an Ag/AgCl (pure) reference electrode at 600°C and a concentration of 4.1 mole pct of each chloride and came to the conclusion that complex ion formation occurred in some of the melts. Laitinen and LiUe gave an electromotive force series at 450°C for a number of {Metal/Metal ions (unit activity)) electrodes in LiC1-KC1 eutectic melt, the {pt/pt++ (unit activity)) electrode being chosen as the reference. Walker and Danly7 studied the ther-modynamic properties of NiC12 in LiC1-KC1 eutectic melt over a wide range of temperatures and concentrations by measuring the electrode potential between a nickel electrode and a chlorine electrode in the melt. Since potential measurements made by using the chlorine reference electrode are of more direct significance both in the study of electrochemical separation and in the evaluation of the thermodynamic properties of the melt, it is therefore decided to measure the electrode potentials of cells of the type {M/MCin (mole fraction = N) in LiC1-KC1 eutectic melt/Cl2 over a range of N values and temperature for a number of metal chlorides. The results should indicate the order by which the various metals plate out on the cathode and how this order is affected by temperature and the concentration of the metal chloride in the solu-

Jan 1, 1960

By Robert M. Keeney

Important recent developments in the melting and annealing of non-ferrous metals include: 1. Melting of nickel silver in the vertical ring induction furnace. 2. Electric melting of stereotype metal. 3. The rotary-drum gas-fired brass melting furnace. 4. The low-frequency coreless induction furnace. 5. Finishing annealing of brass sheets with city gas1 replacing wood in the large brass-rolling mill. 6. Electric annealing of brass and copper tubing and sheets. 7. Replacement of oil by gas and electricity in the annealing of nickel-silver shells and stampings. Melting Nickel Silver in Vertical Ring Induction Furnace Although over 90 per cent. of the output of the brass rolling mills in the United States is now melted in electric furnaces,2 until recently a considerable part of the output of nickel silver has been the product of the pit fire. The application of the electric furnace to the melting of nickel silver has been slow for several reasons: (I) Until recently no lining has been available that gave a satisfactory life in the vertical ring induction furnace when melting nickel silver; (2) the rocking arc furnace so widely used in the foundry does not appear to have been favored by the rolling mill for melting nickel silver, possibly because the gases present may affect the quality of the alloy; and (3) the exclusive rights to the use of the high-frequency coreless induction furnace (which has proved very satisfactory for melting nickel silver) for the wrought brass industry are controlled by one concern. A little over one year ago the first vertical ring induction furnace to be used for melting nickel silver in the Naugatuck Valley was placed in operation. This was followed by two more in the same mill, and by

Jan 1, 1930

By A. K. Mukherjee, J. E. Dorn

A modified Peierls model is Presented for the rationalization of the asymmetric plastic behavior of single crystals of bcc metals. The model assumes that the asymmetry of slip arises from a tendency toward asymnetric splitting of the a/2[111] screw dislocation. The approach differs from former theories however insofar as it assumes that the splitting is so minor ttut only the core energy is modified and that no real partial dislocations exist. As a consequence, the concepts of a line energy of a partial dislocation, interaction between partial dislocations, constriction energies, and stacking fault energies are not invoked. Instead the present analysis is based on a specialization of the Peierls mechanism which assumes an asymmetric dislocation core which is modified by the effective stress and permits cross slip. The theoretical predictions on the stress-temperature -strain rate and orientation relationship agree qualitatively with the limited experimental data that are currently available. Additional experimental work over wider ranges of conditions is suggested to provide more complete evaluation of the possible validity of this theory. RECENT experimental investigations on the low-temperature thermally activated deformation of bcc metals have confirmed the existence of several unique orientation effects. These will be described with the aid of the standard stereographic projection shown in Fig. 1. If slip were determined exclusively by crystal symmetry, the deformation characteristics would be symmetrical about X; = 0 and independent of whether the specimen were subjected to a tension or a compression stress, regardless of what combinations of slip planes might be operative. Experiments, however, reveal that neither of these symmetry based predictions are valid. A schematic representation of the commonly observed asymmetry of both the yield stress and the plane of slip is shown in Fig. 2. A reversal of the direction of stressing results in an inversion of the asvmmetric behavior. 1) Asymmetry bf Yielding. A detailed investigation on the asymmetric yielding in an Fe-2.7 pct Si alloy was repoEted by Tabka, Tikeuchi, and Furubayashi,1 Similar trends have been observed by Keh and Nakada on iron,' Stein on molybdenum,3 Bowen, Christian, and Taylor4 on columbium, Sherwood, Guiu, Kim, and pratt5 on Ta, Cb, and Mo. The degree of asymmetry not only depends on the atomic number and alloying but, in all cases that have been examined, it also increases with a decrease in the test temperature. 2) Asymmetry of the Slip Plane. Asymmetric $I-~: curves of the type shown in Fig. 2 have been found for several Fe-Si alloys6-8,1 and columbium.4 There is general agre_ement that near X: = 30 deg slip occurs by the [111](211) mode so that ?1 = 30 deg. As X; decreases it appears that [111](211) to [111](101) cross slip takes place leading to slip band traces on intermediate planes. And as xi approaches 0 deg, sharp

Jan 1, 1970

By James P. Kimball

Sulphur is always present in mineral coal of every variety. In the oxidized state it may exist as sulphuric acid in combination with a base. In the unoxidized state it exists in combination with iron as bisulphide of iron. It is also supposed by some chemists to exist in unknown combinations with the organic elements of the coal. This supposition requires the demonstration as a fact that certain coals yield more sulphur than what may exist in a free state, or what belongs to recognized combinations, not only with the accompanying iron but with other inorganic bases abundantly occurring in coals, but which unfortunately are very rarely estimated. This practically as well as theoretically important question it is at present impossible to decide, simply for want of available thorough ultimate coal analyses including the ash. Such analyses, at the best imperfect, are luborious and intricate, and therefore seldom made, the much simpler proximate analyses, so-called, being resorted to by most chemists for technical purposes, and commonly substituted for more scientific work even in the laboratories of government surveys. And it is unfortunate enough that few ultimate analyses are extended to the composition of the ash, much less to its relation to the original constitution of the coal. Sulphur chiefly occurs in most coals in the form of yellow pyrites (pyrite) and white pyrites (marcasite), both minerals, characterized by differences in crystalline form and in physical properties as well as in color, but having the same chemical composition (FeS2). No coal is entirely free from one or both of these dimorphous forms of bisulphide of iron. It may be disseminated through the mass so as to be invisible, in plates or scales between the laminæ of the coal, or in conspicuous segregations or nodules, sometimes of considerable dimensions. Coals greatly differ as to the proportion of sulphur which they contain. They also differ as to the relative proportion in which its several forms of combination occur. Such qualitative and qnantitative disparities arc scarcely, if at all, more marked in separate coal seams of a uniform type than in different parts of one and the same coal seam, whether it be considered locally as constituted of several

Jan 1, 1880

GENERAL COMMITTEE GERALD F. G. SHERMAN, Chairman. ARTHUR NOTMAN, Secretary. NORMAN CARMICHAEL, JOHN C. GREENWAY, W. L. CLARK, W. G. McBRIDE, B. BRITTON GOTTSBERGER, FOREST RUTHERFORD. General Committee on Transportation WALTER DOUGLAS, Chairman. CLEVELAND E. DODGE, Secretary. ARTHUR S. DWIGHT, JOHN C. GREENWAY, JULIUS KRUTTSCHNITT, JR. Committee at El Paso W. D. GORDON, ROBERT McCART, JR., W. W. ROSE. Committee at Santa Rita JOHN M. SULLY, Chairman.

Jan 12, 1916

By Yves Dardel

INTRODUCTION SINCE the first determination of Dumas1 in 1880, many authors have tried to measure the solubility of hydrogen in solid aluminum, or at least the amount of dissolved gas in it. However, the interpretation of the results which have been obtained is still difficult. Sieverts,2 then Baukloh and Oesterlen,3 during their gassing experiments could not determine any solubility of hydrogen in solid aluminum. On the other hand, Portevin, Chaudron and Moreau,4 leaving the determination of the hydrogen solubility beyond the scope of their experiments, measured only the amount of gas that they could extract by high voltage positive ion bombardment and found up to 151 cm3 of gas per 100 g of metal. Winterhager,5 by repeated vacuum extraction during severe cold rolling, extracted up to 161 cm3 per 100 g. In both series of experiments, the extracted gas contained chiefly hydrogen with a small amount of nitrogen, carbon monoxide, carbon dioxide and methan. Later, Schmidt and von Schweinitz6 as well as Chaudron and Moreau7 showed the importance of the adsorbed layer of hydrogen, the extracted quantities being proportional to the surface and not to the weight of the sample, when its cleaning was not perfect. In earlier experiments, Steinhauser8 extracted from more massive samples nothing but a little amount (< 0. 5 cm3 per 100 g) of hydrogen, carbon monoxide and methane. Thus, according to these experiments the quantity of dissolved gas is probably very small and the effect of the surface could falsify the results of the extraction. However, owing to the care taken by Chaudron and his coworkers, it was clear that all the hydrogen extracted could not come from the superficial layer, or that the links which bound hydrogen to the surface were so strong that the usual method of cleaning could not destroy them. After the main parts of the experiments reported here had already been carried out, Eborall and Ransley9 published the results which they obtained with an analysor having an accuracy of 0.03 cm3 per 100 g, while that of the usual apparatus was only about 0.2 cm3 per 100 g. During all their experiments the adsorbed layer would have been a difficulty, for the value of the adsorbed hydrogen was approximately equal to that of the dissolved amount. [ ] Since always keeping the same adsorbed layer is very difficult, an error in the correction for the adsorption can be made when using the apparatus of Eborall and Ransley, as well as the earlier apparatus,

Jan 1, 1948

By C. Altstetter, Y. Huang, E. de Lamotte

Nitrogen was introduced into pure niobium (colutn-bium) and dilute Nb- Zr alloy wires by equilibration with pure nitrogen gas at high temperatures. Room-temperature hardness was correlated with the alloy composition, heat treatment, and microstructure. Hardness was found to be most sensitive to the amount of nitrogen in solution; however, a significant hardening up to 500 Dph look place upon aging of quenched alloys. A coarse dispersion of nitride did not significantly increase the hardness of the material though the nitride was found to have a hardness of 1400 Khn. BY now the marked effect of nitrogen on the properties of bcc refractorv metals is we ll-documented. There are few studies, however, in which the state of the solute has been carefully controlled. Indeed, the composition-temperature-pressure relationships in nitrogen-refractory metal systems have been determined precisely for only niobium and tantalum.&apos;-4 Most investigations on niobium have dealt with alloys High-nitrogen alloys cleaved on (100) planes and had negligible ductility. Precipitation was found to occur in either a discontinuous or a continuous fashion, depending on the composition and cooling rates. Upon cooling, the precipitation first proceeded discontinu-ously by the nucleation of nilride needles at subbound-aries and subsequent growth of a two-phase microcon-stituent. At lower temperatures continuous precipitation occurred in the subgrain interior ahead of the discontinuous precipitation interface. containing nitrogen, carbon, and oxygen in significant but uncontrolled and, in several instances, undetermined amounts. Thus, there has been some uncertainty regarding the presence and the distribution of precipitates. This paper presents results which relate the hardness and microstructure to the heat treatment and nitrogen content of niobium and Nb-Zr alloys. Niobium rod* produced by the Wah Chang Corp.

Jan 1, 1968

By H. H. Uhlig

SINCE its first mention in the literature in the eighteenth century1,2 the phenomenon of passivity in metals has stimulated much speculation and attendant controversy as to its nature and cause. No one of the numerous theories so far proposed has been generally accepted. ? Faraday,7 in 1836, associated the passivity of iron with a protective film over the surface of the metal, which materially prevents or slows down reaction with corrosive environments. His theory was that oxidizing acids like nitric acid form an unstable oxygen or oxide layer over the iron surface, which protects the underlying metal from further attack. This concept was simple yet plausible, and without alteration has frequently been assigned in present-day discussions as explanation of the passivity of many metals. With the advent in recent times of stainless steels, it is not surprising that this oxide film theory of passivity proposed by Faraday has been used to explain the phenomenal corrosion resistance of stainless steels and other passive alloys. The passive alloys, such as the chrome-iron alloys, are supposedly covered with a protective oxide film, which forms on exposure of the alloy to air, is extremely stable and self-healing, and accounts for the remarkable resistance of these alloys to corrosion. Within the past few years, several investigators, following the theory of film protection, have attempted to gauge the resistance of the supposed film on steels. Brennert8 and Donker and Dengg9 determined the poten-tial at which a negative ion (e.g., Cl-) moving in an electric field reacted with the metal anode, as detected by increased current flow or change in potential of the steel electrode in an electrolytic cell. The potential corresponding to reaction Brennert called the film break-through potential.

Jan 1, 1939

By E. Cortese

Phosphate occurs in many places in Egypt, in two main zones: one in Upper Egypt, along the Nile Valley, principally on the right side, and one near the Red Sea coast. In the Nile zone, the principal layers of phosphate rock are to be found: in the mountains east of Mahamid (right side of the valley); in the hills near Sibaiya, also called Sebaieh (both sides); in the hills of Agula, Hagaza and Gurn (right side); and further on, along the camel road leading from Kena to Kosseir, a few miles east of Legheita&apos;s Oasis. Following that track, after having crossed the watershed, underlain by rocks like granite, serpentine, porphyry, and diabase, one comes again to the Cretaceous formation containing considerable quantities of phosphate, at Gebel Duwi, Gebel Nakheil, and Gebel Kosseir El Kadim, not far from the coast. More to the north, in the hills near Safaga Bay (Um El Uettat El Wasif) is another rich bed of the same formation. There are reports of phosphate existing near Suez and in the Sinai peninsula, and possibly some other zones can be traced or discovered in the future. The mines are well developed on the right bank of the Nile at Sharawna (near Sebaieh Station) and along the Red Sea coast, at Safaga and near Kosseir. Prospecting work has been done at Gebel Duwi, Gebel Gurn, Agula, Hagaza, and near Mahamid. The phosphatic formation in Egypt is quite variable, not only from place to place, but even within small areas. The phosphate is all of Cretaceous age, as is proved by the fossils found in it. It is considered to belong to the Campanian or, more appropriately, to the Maestrichtian series. The principal fossils are: Alectryonia Villei Coq. sp.; Roudereia Aures-sensis Coq. sp. = R. Drui Mun. Chalm.; Trigonoarca multidentata, Newton.; Cardita libyca, Zittel; Libycoceras Ismaely, Zittel; Nautilus sp.; Ancystrodon libycum Dam.; Corax pristodontus Ag.; Lamma biauriculata Zittel sp. Above the Maestrichtian beds, we have the Danian series, unconform-ably covered by Lower Eocene beds. Under the phosphate is a grayish marly clay, and beneath this, bluish-gray scaly shales resting on the Nubian sandstone (Santonian).

Jan 1, 1918

By Hansheinz Portisch, Harold Margolin

A surface expansion was found to occur sometime after etching in Ti-A1 alloys containing 9.5 to 12.5 wt pct Al. The structure formed, grew, and disappeared with tzrrze. The surface expansion was followed by microscope observations and interferometric and lattice parameter measurements. Activation energy measurements for the growth of the "expansion structure" and chemical analysis indicated that the phenomenon occurred as a result of hydrogen pzckup during etching. It is proposed that hydrogen initially enters octahedral sites of Ti3Al coherent with a Ti and later shifts to the tetrahedral sites. It is postulated that expansion occurs when hydrogen enters the tetrahedral sites. The expansion structure disappeared, it is proposed, because of diffusion of hydrogen from the surface into the body of the alloy and because of loss of coherency of Ti3Al. In examining Ti-A1 alloys, Ence and arolinl observed markings on the surface of specimens. These markings did not appear after electropolishing only, but rather appeared only after etching. The markings appeared to grow as a function of time after etching and later seemed to disappear. Although the markings had some similarity to precipitates, showing, frequently, a Widmanstatten type of arrangement, the observation that other microstructural markings continue to be seen within the new structure suggested that it was actually not a precipitate. The source of this structure was unknown and an attempt was made in the present investigation to develop some understanding of its nature. It has been labeled expansion structure. 1) EXPERIMENTAL PROCEDURE A) Alloys. Alloys in the range 6.5 to 14.5 wt. pct A1 were studied. Bars, 4 in. sq, forged from Bureau of Mines (73 Bhn) titanium consumably arc-melted 4-lb ingots,&apos; as well as 50-g arc-melted buttons of desired aluminum contents were used. The 50-g buttons also used Bureau of Mines titanium (73 Bhn) and aluminum of 99.99 pct purity. Buttons containing up to 8.5 wt pct A1 were hot-rolled from a furnace at 900&apos; . Those with higher aluminum contents were hand-forged on a titanium anvil, and heated with an oxygen-hydrogen torch in the region of 1200" to 1300°c. Frequent reheating kept the samples at the desired temperature range. After a reduction of about 30 pct, the samples were water-quenched. To eliminate any contamination picked up either during hot rolling or forging, at least 1 mil of the surface of the sample was taken off. B) Heat Treatment. Prior to heat treatment all alloys were vacuum-annealed to remove hydrogen. Samples were annealed at 900&apos; until a vacuum of 10&apos;5 mm Hg was established. After this treatment, the samples were wrapped in molybdenum sheet and heat-treated in argon-filled quartz capsules, which were broken under water or iced brine at the conclusion of the heat treatment. All heat treatments under dynamic vacuum were performed in a rapid-quench furnace. This consisted of a molybdenum-lined quartz tube attached to a vacuum system and through a stopcock to a beaker of water. At the completion of the heat treatment the vacuum stopcock was closed, the furnace shut off, and dropped below the quartz tube. Then immediately the inlet stopcock was opened and water admitted until the tube was filled. The steam formed was allowed to escape through the inlet stopcock. This method was used in heat treatments up to llOO°C. C) Metallography. Specimens for metallographic examination were ground, then electropolished using a Disa Electropol machine with a perchloric acid electr01te. Specimens were etched with R-etch.3 A standard etching time of 3 min was used, with the specimen being agitated during immersion. D) Sample Preparation for X-ray Analysis. Samples 0.2 to 0.5 mm in diam were produced from heat-treated rods which were turned to 2 mm diam on a lathe and then rotation-etched. An etchant consisting of 1 pt HF, 7 pt HN03, and 12 pt HzO was satisfactory. With the rod rotating in a vertical position at 50 to 100 rpm, a needle with uniform dimensions could be obtained. Care had to be taken to insure that the rod was at the center of rotation, otherwise cavitation developed. If a small unevenness developed, it was possible to grind it off with a fine emery paper. E) X-ray Diffraction. All X-ray work was done on a North American Phillips X-ray diffraction apparatus and a Jarrell Ash microfocus X-ray unit. The Phillips unit was used with a copper target and nickel filter. The Jarrell Ash unit was fitted with a cobalt target and iron filter. For the Phillips unit 35 kva and 20 ma were used, whereas for the microfocus unit with the 100-p fixed-focus gun 40 kv and 1.5 ma were used. It was found that alignment of cameras on the Jarre11 Ash unit was very critical. The X-ray beam contains an intense area which is not the beam center. The cameras were aligned with the intense region by monitoring the beam coming out of the camera with a Geiger counter. Adjustments were made until a maximum intensity was obtained. A Phillips diffractometer with a Brown chart recorder furnished some of the lattice parameter data. The divergence slit up to 80 deg 28 was I deg; above 80 deg, a 4-deg opening was used, while the scatter slit was1 deg and the receiving slit had a 0.003-in. opening. The general scanning rate was 1 deg per min, while peaks of special interest were rescanned at -j deg per min. For elevated-temperature X-ray diffraction a Uni-cam High Temperature Camera with a film diameter

Jan 1, 1969

By A. C. Watts

FOR several years, a mine in Colorado experienced considerable trouble from small fires caused by the blasting of coal. Although a well-known make of permissible powder was used, it was first thought that the powder ignited gas that might be present and that this, in turn, set fire to line brattices or to the coal. Experiments were, therefore, conducted with another make of powder, but the results convinced the superintendent of the mine, Robt. Williams, Jr., that the fires were not caused by the powder but by the high-voltage electric current used for detonating the shots. The mine "makes" gas very freely, giving off from three-fourths to a million cubic feet of methane per 24 hours. The coal is a good grade bituminous of a very free burning quality. Electric shot-firing from the outside after all men and animals were outside had been practiced for a number of years. The shooting circuit was connected with the main power circuit at the mouth of each entry. Shooting circuit switches were mounted in boxes, which were kept locked with the handle of the switch, in open position, showing through the bottom of the box. The door of the box could not be shut and locked when the shooting switch was closed. At the entrance to each room, or working place, a small switch, called the miner&apos;s switch, was placed on the shooting line. It was the duty of the miner, when entering his place at the beginning of the shift, to see that this switch was open and that it was kept open until he left the place at the end of the shift to go out of the mine. Grounded return was used for main power lines. The current was 500 volts, direct current, with 100 to 300 amp. The nearest working face was 9600 ft. from the shot-firers&apos; switch outside the mine and the most remote working face was 2 ½ miles. The various working faces were scattered over a wide area between these two points.

Jan 9, 1925

Jan 1, 1957

By H. H. Stoek

The fundamental reasons underlying the choicc of a method of mining a coal seam are safety of operation, cheapness of producing the coal and the character of the product as a saleable article. From the standpoint of safety, open or strip coal mining is always preferable, as many of the dangers inherent to underground work are absent, such as explosions of gas and dust, falls of roof and coal, and also to a great extent those due to haulage and the use of explosives, thus eliminating three of the chief causes of accident from which about 75 per cent. of the underground accidents in coal mines occur. The conditions under which coal is stripped also make the work much safer than ordinary quarry work, as the depth of the pit is usually comparatively small. Prom the standpoint of low mining cost, there is much misapprehension and many of the costs given are misleading in that they do not take into account such items as the destruction of the surface for future use, the full cost of the removal of the overburden, depreciation, amortization, coal depletion, loss of time through floods and from bad weather in winter, etc. Coal is no doubt often put on the cars at less cost by stripping than by underground mining, but by no means always so, as is too generally assumed. In some cases coal must be obtained by stripping or not at all, because the small amount of overburden renders underground mining impossible.

Jan 1, 1918

By J. N. Sicking, F. H. Brinkman

A new method for obtaining equilibrium vaporization ratios (K-values) for reservoir fluids has been developed and tested. By application of the method, complex experimental measurements of liquid and vapor phase compositions are eliminated. This simplified technique reduces the cost of experimental equilibrium-ratio data for reservoir studies of condensates and volatile crude-oil systems. The method is designed for systems of constant composition and, therefore, is best suited for depletion studies where compositional changes at high pressures are minor. The basic data required, in addition to the composition of the initial reservoir fluid, are the relative vapor-liquid volumes and densities at reservoir temperature and variom reservoir pressures. Tests demonstrated that the method predicts equilibrium ratios accurately for condensates. A single test on a crude oil was not conclusive; further testing will be necessary before the accuracy of the method can be determined for crude-oil systems. In addition to determining equilibrium ratios, the calculation method provides information on the physical properties of the "plus" component in the vapor and liquid phases. The "plus" component is that mixture of components heavier than the least volatile fraction analyzed. This information is useful in studies of both natural depletion and cycling operations for condensate reservoirs where the heptanes-plus component in the gas phase is produced from the reservoir. INTRODUCTION As more volatile oil and condensate reservoirs are found, the use of phase behavior techniques to predict their performance is increasing in importance. These techniques have long been used for condensate fields and have more recently been applied to crude-oil fields containing oils of medium-to-high volatility. In these phase behavior methods, equilibrium ratios (K-values) are used to predict compositional changes in the reservoir fluids—thereby accounting for the recoverable oil that exists in the gas phase. The reliability of the predictions depends to a large extent on the equilibrium ratios used. These values must be obtained for each component for the entire pressure range being investigated. Unfortunately, because of the complex nature of hydrocarbon mixtures, accurate K-values are hard to obtain. The equilibrium ratios for a particular component will vary not only with the temperature and pressure, but also with over-all composition of the system. The importance of composition is quite critical at elevated pressures, but becomes negligible at pressures below about 300 psia. Therefore, because most phase behavior problems involve the high-pressure region, each fluid system becomes a special case. Experimental programs to determine characteristic K-values are quite difficult and time-consuming. Thus, it is often necessary to resort to approximations of the K-value data. Charts giving K-values for various mixtures and classes of mixtures are available in the literature. However, there are two major difficulties in using them: (1) the K-values of the "plus" component (that mixture of components heavier than the last one analyzed) must be obtained by extrapolation from the K-values of the other components; and (2) the K-values obtained must finally be adjusted by trial and error to agree with observed volumetric data. To eliminate these difficulties, a new method of determining equilibrium ratios was developed. Briefly, after the composition of the system as a whole has been analyzed, the method uses empirical correlations and the gross fluid properties of the system (relative vapor-liquid volumes and densities) to calculate K-values. Because the calculative procedure is long, it is best solved on a digital computer. About one hour of machine time on an IBM 650 computer is required to develop a K-chart for the fluid being examined. DEVELOPMENT OF THE METHOD OF OBTAINING K-VALUES Equilibrium ratios are defined as the ratio of the mole fraction of a component in the vapor phase to its mole fraction in the liquid phase. This statement is expressed in Eq. 1. A typical plot of equilibrium ratios for a particular system is shown in Fig. 1. It should be noted that, at pressures near the saturation pressure, the K-values appear to converge to a common point. This apparent convergence point is called the convergence pressure and is a characteristic of the system involved. Various empirical correlations of K-values have been noted. It has been observed that an isothermal plot of