Search Documents

By H. L. Tedrow

FACED with a scarcity of labor in its operations at Alma, Colo., the London Mines and Milling Co. has been employing women for several months in its sorting and crushing plant. The results so far obtained indicate that women can be used successfully and to good advantage on a number of various jobs around the surface plant of an ordinary mine. Eight women are now employed as sorters to pick waste out of the ore as it passes by them on a sorting belt. After a short period of breaking in they have become adept at their work and are doing better work than that formerly done by the class of labor obtainable. They are continually warned and instructed, particularly from the standpoint of safety and their physical strength.

Jan 1, 1942

By F. W. Luerssen, J. F. Elliott

F LUSHING the early slag from a stationary open Fhearth having a high percentage of hot metal in its charge is necessary in order to remove silica from the system. The flush slag is strongly oxidizing and is somewhat acidic. It has, however, considerable capacity to extract phosphorus from the bath and it also removes considerable manganese. It seems probable that factors which control the distribution of phosphorus and manganese between slag and metal in the refining period also should be dominant in the flush and postflush periods. Several studies, as summarized elsewhere,1,2 support the viewpoint that conditions closely approaching equilibrium for these elements are rather readily established during the refining period. Over the years these studies have repeatedly demonstrated that 1—high slag v01ume, 2—low bath and slag temperature, 3—basic slag, and 4—strongly oxidizing slag favor rapid elimination of phosphorus from the bath to the slag. They also show that the following conditions favor retention of manganese in the bath: 1—low slag volume, 2—high bath and slag temperature, 3— basic slag, and 4—minimum oxidizing power of slag. When it is considered that the flush slag often carries as high as 75 pct of the manganese charged and only 25 to 60 pct of the phosphorus charged, it is evident that in removing silica much manganese is sacrificed but phosphorus removal is far from conplete. Because of overriding circumstances, this is accepted in most operations and actually it is considered to be inevitable. This may account for the fact that little attention has been paid to conditions affecting the elimination of phosphorus and manganese in the flush slag. A recent study of the behavior of various charge oxides has developed considerable information on the flush and postflush periods. Because the data are felt to be of general interest, they have been brought together and Presented in this paper. The object is to show the various factors in the flush and postflush periods which influence elimination of phosphorus and manganese. Physical Conditions During and After Flushing Physical conditions existing during the flush vary from plant to plant, from shop to shop, from furnace to furnace, and even from heat to heat. They are strongly influenced by the physical and chemical character of the charge oxide which is ordinarily necessary to provide sufficient oxidizing power early in the heat. Invariably the period is characterized by a vigorous reaction between the principal re-actants: the hot metal being added and the charge oxide. During the flush, it is probable that the slag acts to some extent as an oxidizer; but, because of the critical influence of the behavior of the charge oxid'e on flushing action, it seems apparent that the oxide itself is the dominant oxidizer. Fig. 1 shows the course of two heats which were selected as being typical of the group studied. Heat A was charged with 55 pet hot metal, based on the total metallics charged, and heat B had 57 pct hot metal. As indicated in Table I and Fig. 1, the melt-down slag, which is not usually voluminous and which is principally FeO, expands greatly in volume and will show rather high levels of SiO2, MnO, and P2O5 very soon after the beginning of the hot metal addition. Simultaneously, large volumes of CO are liberated which cause violent mixing of slag and metal. It is of interest to note that the time required to bring carbon down to a low level is very much longer than that required for the removal of silicon, manganese, or phosphorus. At the end of flush, carbon in the bath is still approximately 2 pct. When strongly reducing hot metal is brought into contact with strongly oxidizing conditions within the furnace! it is probable that the rate of mass transfer to the slag (and atmosphere) of silicon, manganese, phosphorus, and carbon initially depends principally on the rates at which the two participating phases are brought into contact That is, it depends on the nature of the various reactions. Later in the flush period, when the scrap is virtually all dissolved and the action of the bath has settled down to a steady and somewhat gentle boil, it is likely that other factors, such as the transfer of oxygen across the slag-metal interface, become dominant. The temperature of the slag-metal system is far from uniform. Heat is being driven by the flame down through the slag. Bubbling and surging of the metal also frequently brings portions of the bath in contact with the flame. At areas of contact between the ore and liquid metal, or slag and liquid metal, the oxidizing reactions generate much heat. On the other hand, scrap is being melted which tends to absorb large quantities of heat. Because the liquid bath is high in carbon, the steel scrap is brought into solution rapidly. This can proceed at a rather low temperature; and until much of the scrap has been taken into solution, the bath temperature would not be expected to increase appreciably. Consideration of these factors leads to the conclusion that during the flush period the slag should be rather hot and the bath relatively cold. Both observation and temperature measurements bear this out. Experimental Data The extended program of charge oxide evaluation permitted study of the widely varying conditions existing during the flushing period. Slag and metal analyses and bath temperatures reported herein (Tables I and 11) were obtained toward the latter portion of the work. Four different types of charge oxide, sinter, two types of hydraulic cement-bonded soft ores, and a pyrobonded agglomerate were used in the study. Although the heats reported were from only one 205 ton furnace, they show variations in flush slag analyses all the way from 25 pct FeO, which is typical with the use of a hard natural charge ore, to 45 pct FeO which resulted when a very poorly agglomerated fine ore was used. The physical behavior of the flushes showed a correspondingly wide variation from well controlled reactions to violent surges following periods of inac-

Jan 1, 1956

INTRODUCTION In the preceding chapters we have discussed the various elements of mineral economic analysis, their interrelationships, and the most accepted and advanced techniques by which these elements are manipulated to provide the decision maker quantitative measurements for judging alternate investment opportunities. Regardless of how carefully the economic evaluation is made, and how comprehensive the study of economic parameters has been, uncertainty still remains a significant factor in the outcome of the analysis. The investor or money manager is acutely aware of the uncertainty factor. Many of the economic parameters are functions of economic forecasts and value estimates that can- not be known with any degree of certainty. The postulated DCF-ROR is based upon certain estimates representing "best guess" values, and a single point parameter DCF-ROR analysis represents a combination of "best guesses." The wise decision maker looks at such an analysis and asks the "what if" questions. What if the production cost is 10% higher than the estimate? What if there is an overrun in construction costs? What if the mineral price falls lower than expected? What will be the effect of a higher royalty rate? Many more such questions may arise in trying to assess the total risk involved in funding a mineral project. Prior to the advent of the computer it was difficult to answer all such anticipated questions because of the many laborious calculations involved. Now, with the aid of the computer, most of these questions can be answered by the analyst at the same time the original computations are made by using the process of sensitivity analysis. Sensitivity analysis shows the effect of critical parameter changes upon the DCF-ROR or other profitability measure. When probability of occurrence can be associated with the various parameter value levels, sensitivity analysis becomes probabilistic analysis, and the risk factor can be quantitized in terms of total probability. SENSITIVITY ANALYSIS The determination of the sensitivity of the profitability index (usually the DCF-ROR) to changes in the various economic parameters, taking them one at a time, is called sensitivity analysis. The analysis may be performed for any number of parameters involved in the DCF-ROR computation. Generally, in mineral evaluations the most sensitive and most tested parameters are: the metal or mineral price, the operating cost, the annual production grade, and the initial capital invest-

Jan 1, 1980

By Irving B. Cadoff, Ernest Levine

The crack formation and propagation in the single -phase Cu-4 pct Ag alloys were studied. The alloys were loaded in mercury to various stress levels, the mercury was removed, and the specimen examined for cracks. Cracks were found to develop below the fracture stress; the frequency of such cracks increased with increasing stress level. Some cracks were nmpropagative. Fracture in mercury was found to occur by the link-up of cracks formed at various stress levels rather than by the growth and propagation of a single crack. If the mercury environment is removed prior to a critical amount of crack formation, then continued loading results in ductile fracture. The appearance of the cracks at selected grain boundaries is related to the relative orientation of the boundaries, as are the propaga-tive characteristics of the crack. The mercury interaction appears to be one of lowering the strength of the metal-metal bonds in the high-stress area of the grain boundary. GRIFFITH'S microcrack theory1 proposed a critical crack size above which a crack in an elastic material grows with decreasing energy at a stress of From his theory it was proposed that the presence of a liquid tends to lower the surface energy of the microcrack faces2 leading to a decrease in the critical crack size necessary for spontaneous fracture propagation. stroh3 proposed that the stress concentration at a grain boundary due to pile-up may initiate a microcrack at the grain boundary. petch4 and Stroh5 evaluated the stress distribution at the head of a pile-up in a polycrystal-line material and deduced that the critical crack size and hence of is dependent on the grain size. Experimental verification of this dependence was found by petch6 for hydrogen embrittlement of steel. Studies in stress-corrosion cracking7 have provided a picture of fracture which shows that initial separations occur in a scattered, independent fashion in regions of high tensile stress. A minimum or threshold stress is necessary to produce a sufficient stress concentration to initiate frac- ture. These separations join up to form a crack. The extension of fracture is largely discontinuous and consists of a joining up of cracks. In recent worka evidence of this scattered crack network was found in a Cu-Ag alloy embrittled by mercury. For the Cu alloy-Hg couple, the crack path has also been found to be dependent on the orientation of adjacent grains, and with the addition of zinc to mercury a reduction in embrittlement along with a change in fracture morphology was found.9 In this present study, a mercury-dewetting method was used to observe crack initiation and fracture morphology when a Cu-4 pct Ag alloy is deformed in mercury and Hg-Zn solutions. PROCEDURE Specimens of Cu-4 pct Ag were prepared as in previous crack-path studies.' The specimens were heated at 770°C for 24 hr and water-quenched Tension tests using a table-model Instron were carried out in mercury and in various concentrations of Hg-Zn. Loading was in steps up to the fracture stress, with the load being removed and the specimen examined for surface cracks at each step. The specimens were dewetted after each load to permit examination of the surface structure and rewetted prior to continued loading. The specimens were wetted by electro polish ing in phosphoric acid, rinsing in alcohol, and then immersing in a pool of mercury. Dewetting was accomplished by flame heating the specimen for 30 sec in a vacuum. Some surface contamination was found, but not enough to obscure crack configurations and grain boundaries. RESULTS Fracture Characteristics in Mercury. Fig. 1 is a stress-strain curve showing the progressive step-wise loading of the specimen. As may be seen from the graph, the first position stopped at a is at a stress 5000 psi below the expected fracture stress of 25,000 psi. Examination of the specimen after removal of mercury showed only one crack. The appearance of this crack at a stress far below the fracture stress of this alloy in mercury did not affect the stress-strain curve in any manner. The specimen was then recoated with mercury and deformation was continued (curve b, Fig. 1) raising the stress by 4000 psi, and the same procedure re~eated. The initial crack was located and appeared as in Fig. 2 (crack lb). In this figure the crack is

Jan 1, 1964

By J. T. Norton, Joseph Gurland

IN spite of the extended use and high state of practical development of the cemented tungsten carbides, the structure of these alloys is still a matter of considerable controversy. The characteristic high rigidity and rupture strength of sintered compacts have been attributed to a continuous skeleton of tungsten carbide grains, formed during the sintering process. This view is based mainly on the work of Dawihl and Hinnuber,1 who reported that a sintered compact of 6 pct Co maintained its shape and some of its strength after the binder was leached out with boiling hydrochloric acid. After leaching, only 0.04 pct Co was reported to remain in the compact. They also showed that the assumed increasing discontinuity of such a skeleton, as the cobalt content is increased, could be made to account for the observed discontinuous increase of the coefficients of thermal expansion, the loss of rigidity, and the impaired cutting performance of alloys of more than 10 pct Co. Contradictory evidence was cited by Sanford and Trent,' who mentioned that a sintered compact was destroyed by reacting the binder with zinc and leaching out the resulting Zn-Co alloy. The skeleton theory also does not account for the observed change of strength of sintered compacts as a function of cobalt content. If the skeleton is responsible for the strength, the latter would be expected to decrease with increasing binder content. Actually, the strength increases and reaches a maximum around 20 pct Co. In addition, tungsten carbide is brittle and undoubtedly very notch sensitive. The highest value found in the literature for the transverse rupture strength of pure tungsten carbide prepared by sintering is 80,000 psi.3 herefore, such a skeleton does not easily account for a rupture-strength value of 300,000 psi and higher, commonly found in sint.ered tungsten carbide-cobalt compacts. In view of the conflicting data present in the literature, experiments were undertaken to determine whether the sintering of tungsten carbide-cobalt alloys leads to the formation of a carbide skeleton or whether the densification behavior and the properties of cemented compacts are consistent with a structure of isolated carbide grains in a matrix of binder metal. The specimens were prepared from powders of commercial grade. Tungsten carbide powder ranged in particle size from 0 to 5x10-4 cm. Mixtures of tungsten carbide and cobalt were ball milled in hexane for 48 hr in tungsten carbide lined mills. After milling, the specimens were pressed in a rectangular die (1x1/4x1/4 in.) at 16 tons per sq in. NO pressing lubricant was used. Sintering of the tungsten carbide-cobalt compacts was carried out in a vertical tube furnace equipped with a dilatometer (Fig. I), by means of which the change of length of the powder compacts could be followed from room temperature to 1500°C. An atmosphere of 20 pct H, 80 pct N was maintained inside the furnace. Decarburization of the samples was prevented by the presence of small rings of graphite inside the furnace tube. The temperature of the sample was measured by a platinum-platinum-rhodium thermocouple, which also was part of a temperature control system able to maintain a constant temperature within ±100C. Pure tungsten carbide compacts were prepared by sintering the carbide without binder or by evaporating the binder from sintered compacts in vacuum at 2000°C. Since complete densification of these samples was not desired, they were sintered only to 60 or 80 pct of the theoretical density of tungsten carbide. The specimens were prepared for metallographic examination by polishing with diamond powders and etching with a 10 pct solution of alkaline potassium ferricyanide. Cobalt etches light yellow and the carbide gray. The amount of porosity is exaggerated since it is difficult to avoid tearing out carbide particles, especially from incompletely sintered samples. Experimental Observations A number of specific experiments were carried out in order to study some particular aspect of the sintering problem. The details of these experiments, together with their results, are as follows: Electrolytic Leaching: The binder was removed by electrolytic leaching from sintered tungsten carbide-cobalt compacts for the purpose of determining the continuity of the carbide phase. The method used was based on the work of Cohen and coworkers4 on the electrolytic extraction of carbides from annealed steels. If the sample is made the anode, using a 10 pct hydrochloric acid solution as the electrolyte, the binder is dissolved, but the rate of solution of tungsten carbide is negligible. A current density of 0.2 amp per sq in. was applied. As shown in Fig.

Jan 1, 1953

By J. M. Eldridge, P. Balk

Phosphosilicate glass films were formed, by reacting gaseous P2O5 with SiO2, over a large range of temperature (800° to 1200°C) and gas phase composition (nearly two orders of magnitude of effective P2Ospressure). The film compositions generally corresponded with the liquidus curve, delineating the maximum solubility of the tridymite Phase of SiO 2 in phosphosilicate liquid solution at the temperature of film formation. It is shown that the P2O5 concentration of the phosphosilicate liquid film tends to decrease by reaction with the underlying SiO 2 layer until the liquidus curve is reached. The validity of the thermodynamic argument used in this explanation is supported by the results of a determination of the composition of borosili-cute films, prepared by reacting gaseous B2O3 with SiO2 at different temperatures. The kinetics of phosphosilicate film formation were described by a model predicated on a steady-state diffusion of P2O5 through the film. UNDERSTANDING of the processes leading to formation of phosphosilicate and borosilicate glasses is of great importance for producing passivating layers on FET devices. Passivating films with optimum characteristics are preferably formed in a separate step, independent of the doping of the semiconductor.' The results of an investigation carried out to gain improved insight into the mechanism of glass formation are presented in this paper. It would be expected that application of the known Pz05-Si02 and B 2 O 3-SiO2 phase diagrams should be useful in extending understanding of the glass-forming processes. However, the question of the propriety of treating thermally grown SiO2 in these binary oxide systems by the methods of equilibrium thermodynamics must be considered when this application is attempted. Although Sah et a1.' and Allen et al. 3 investigated the kinetics of formation of phosphosilicate glass (PSG), they failed to adequately relate their diffusion models to the occurrence of experimentally observed phases in the PSG/SiO 2/Si system. Horuichi and yamaguchi4 investigated the diffusion of boron through an oxide layer and described their results in terms of a model similar to that of Sah and coworkers. More recently, Kooi 5 and Snow and Deal6 reported the compositions of PSG films formed by depositing P2 O 5 onto SiO2. These compositions apparently coincide with those at the liquidus curve delineating the maximum solubility of crystalline SiO2 in phosphosilicate liquid solutions. These authors did not discuss the thermodynamic implications of their results on the structure of thermally grown SiO2 films. The structure of thermally grown Sio2 films and that of vitreous silica are generally thought to be quite similar. Since the solubility of a substance depends on its structure, it is relevant that the solubility of vitreous silica in water7 is highly reproducible, like the solubility of thermally grown SiOz in phosphosilicate liquid. Furthermore, the vitreous silica-water system appears to be in true thermodynamic equilibrium (viz., the same solubility value can be approached from both supersaturated and under-saturated solutions). Sosman7 suggested that a type of two-dimensional lattice may form at the silica/solution interface, resulting in the observed solubility behavior that is characteristic of a crystalline solid. An alternative explanation may be that vitreous silica has a microcrystalline grain structure. Other investigators have suggested that vitreous silica has essentially the structure of B cristobalite,' or is composed of microcrystals of p tridymite or cristobalite, or a mixture of both. Presumably the grain size would be sufficiently large to minimize any appreciable contribution of the grain boundaries to the solubility of the crystalline matrix. The present investigation was carried out to clarify the significance of the boundaries in the Pa,-SiO, and B2O3-SiO2 Systems in determining PSG and BSG (borosilicate) film compositions. Furthermore, the kinetic data for PSG film formation were extended, using a wider range of formation parameters than were previously reported. One model describing the kinetics of film formation will be presented that is compatible with the thermodynamics of the Pa5-Si02 system. EXPERIMENTAL PROCEDURE Glass Film Preparation. SiO2 films (1000 to 8000A thick) were obtained by oxidation of silicon substrates in dry O2 at 1100°C. PSG and BSG films were prepared by exposing these layers to gaseous oxides obtained by reacting high-purity POC13 and BBr3, respectively, with O2. A double-columned saturator was used to ensure complete saturation of the N 2 carrier

Jan 1, 1969

By J. D. Mote, J. E. Dorn

This investigation was undertaken to study the effects of piledup arrays of dislocations on inducing slip, twinning, and fracturing in magnesium bicrystals. A series of variously oriented bicrystals of magnesium having a vertical grain boundary were prepared and tested in tension. It was found that piled-up arrays of dislocations at the grain boundary could, under appropriate conditions, induce slip, twinning- and cracking. The results that were obtained substantiate, at least qualitatively, the general dislocation mechanism for transmission of strain across grain boundaries and the Petch-Stroh concept of fracturing. WHEREAS single crystals of magnesium generally exhibit extensive deformation, coarse-grained poly-crystalline magnesium at subatmospheric temperatures fractures after a few percent elongation.' Although a small amount of ductility is obtained, several features of this fracturing are characteristic of typical brittle behavior. Over a rather broad temperature range the fracture stress is insensitive to the test temperature and the fracture stress increases linearly with the reciprocal of the square root of the mean grain diameter. The course of fracturing is predominantly intergranular, but small fragments of adjacent grains frequently adhere to the fractured surface.2 The brittle behavior of polycrystalline magnesium is attributable to the limited number of facile deformation mechanisms it exhibits at low temperatures. For a general deformation of a randomly oriented polycrystalline aggregate, each grain must exhibit at least five independent mechanisms of deformation to permit accommodation of the imposed deformation from grain to grain.= Although minor amounts of prismatic slip occur in corners of grains where stress concentrations are known to be high, glide in polycrystalline magnesium at low temperatures takes place almost exclusively by basal slip.' The common type of twinning, which takes place on the (1012) pyramidal planes, can under the most favorable orientations, lead to a. strain of only 6.9 pet; the contribution of twinning to the tensile strain would indeed be much less than this in a randomly oriented polycrystalline aggregate of magnesium. Since the three mechanisms of basal slip are coplanar, they are equivalent to only two independent mechanisms, a number insufficient for a general deformation. Consequently, once the permissible twinning has taken place in conjunction with basal slip, no further plastic deformation is possible because of interference to slip at the boundaries of dissimilarly oriented grains. At this stage brittle fracturing takes place due to high stress concentrations at the juncture of slip bands with the grain boundaries; the predominance of intergranular fracturing in magnesium, in preference to transcrystalline fracturing which is prevalent in zinc, has not yet been rationalized. A more atomistic description of the plastic behavior and fracture characteristics of magnesium follows from the analyses made by stroh4 on the stresses induced by piledup arrays of dislocations. Slip first takes place by dislocation motion in the most favorably oriented grains. As the dislocations approach the boundary of a dissimilarly oriented adjacent grain they begin to form an array of dislocations with its attendant stress field. Piledup arrays of screw and edge dislocations introduce high localized shear stresses at the spur of the array; piledup arrays of edge dislocations also induce high tensile stresses localized in the vicinity of the grain boundary. Whereas the shear stresses can induce slip to take place, the tensile stresses, if sufficiently high, can cause fracturing. The localized shear stress will be relieved if sufficient numbers of mechanisms of deformation become operative in the original and the adjacent grain to permit accommodation of the dislocations in the grain boundary. In this event a ductile behavior will be obtained. But if the number of deformation mechanisms is insufficient for complete migration of dislocation arrays into the grain boundary, the tensile stresses due to the edge components of piledup dislocation arrays will continue to increase with increasing applied stress until fracturing takes place. Whereas face-centered-cubic metals have a sufficient number of mechanisms of slip for accommodation of dislocations in their grain boundaries to exhibit ductile behavior, hexagonal-close-packed metals, in general, do not. Consequently, hexagonal-close-packed metals are usually brittle except when conditions such as alloying or temperature permit facile slip by a number of mechanisms. The arguments presented above suggest that the mechanical behavior of magnesium depends on whether or not dislocation arrays in adjacent grains can enter the grain boundary. When such accommodation is possible, ductile behavior is expected; but when such accommodation is impossible, fracturing will ensue. To further test the validity of these arguments it was considered advisable to study the

Jan 1, 1961

By Nathaniel Herz

(San Francisco Meeting, September, 1915) THE use of zinc dust for precipitating the precious metals from cyanide solutions is well established now in many places, and has many advantages over the shavings method of precipitation. Although much work has been clone on methods of testing zinc dust, as yet no absolutely positive test has been devised to determine the value of the material. Certain facts are known, but often it happens that results on a working scale are not as expected from the laboratory tests. The purpose of this paper is to record some observations made while testing. a large variety of zinc-dust samples in the laboratory. W. J. Sharwood1 has described standard analytical methods, which have been followed, with the changes noted. The regular determinations include zinc oxide, by solution in ammonia and ammonium chloride, lead, and precipitating efficiency. In some cases cadmium was determined by a method similar to that described by J. E. Clennell.2 I will discuss the precipitating-efficiency test in detail. The procedure is as follows: "A solution of potassium silver cyanide is prepared by dissolving 10 grams of silver cyanide (AgCN) and 5 grams of `99 0' potassium cyanide in a little water and diluting up to 1000 cc. It is then adjusted by addition of a little more KCN or AgCN until the solution indicates from 0.12% to 0.15% free KCN by titration with standard silver nitrate. The titration is best made by using a 10-cc. or 20-cc. sample, adding 1 cc. of 2 % potassium iodide, and a slight excess of ammonia, as the end point is then sharper. Or 15 grains of pure crystallized KAg(CN)2 may he dissolved in a liter of water and 1.5 grams KCN added. "Weigh out 0.5 grain zinc dust into a 300-cc. beaker. Add a few cubic centimeters of water and stir until, zinc is well mixed, then pour in 250 cc. of the prepared solution, stirring vigorously. See that all lumps are broken up, and continue stirring for fully five minutes. Stir occasionally (at least every 10 minutes) until the end of two hours from the addition of the solution. Then filter upon an 11-cm. filter, wash precipitate thoroughly, sprinkle with test lead, wrap it carefully in the paper, plaice in a scorifier with about 20 grams test lead, burn paper cautiously in muffle, scorify five minutes, cupel at low temperature and weigh silver. Milligrams silver obtained from 0.5 gram zinc X 0.0606 = percentage precipitating efficiency."'

Jan 8, 1915

By E. C. Harder

J. T. SINGEWALD, JR., Baltimore, Md.-I might say a word further in regard to the Miguel-Burnier district. I am sorry Mr. Harder is not here. I had hoped to be able to ask him a few questions in regard to some of the features of those deposits. This Miguel-Burnier district is the other district that I referred to that lies in the State of Minas Geraes. The interpretation that Mr. Harder gives to, these deposits is the same as that given by Harder' and Chamberlin in a previous paper, and that is that they consist of lenticular deposits of sedimentary origin in a series of rocks that also include lenses of limestone, but they seem to think that the manganese ores occur at a definite horizon and at a horizon different from the limestone. We found that the manganese ores occur at several horizons, as also do the limestone lenses, and the limestone masses are of the same shape as the manganese orebodies, so that our own feeling was that these manganese ores simply represent concentrations within the zone of oxidation formed as. a result of decomposition and replacement of this limestone. To the east of Miguel-Burnier there is a big bend in the railroad which cuts through, at right angles to the strike, this series of rocks. Here is shown very well both the local character of the limestone lenses and the local character of the manganese lenses in that, though the distance across the bend is only a couple of hundred yards, the limestone and. ,manganese lenses do not match up at all, and it also shows plainly that both occur at more than one horizon.. Consequently there is no reason why the manganese ore could not represent alterations of this limestone. The mine workings do not as yet give very definite information on this point in that they are all comparatively shallow and within what would be the zone of oxidation so that what they will grade into below that depth, we do not know. On the other hand, the character of the ore suggests that it may, represent such -a product in the zone of oxidation in that it tends to be quite earthy; whereas, if the manganese had been there originally as such it would have undergone the same metamorphism that the other rocks have undergone and one would have expected that it would have been converted into a hard manganese ore that would today stand out pretty much as do the iron ores of that same region and not have the soft, earthy texture which is a prevailing characteristic.

Jan 4, 1917

By R. E. Barnes

An overall view of the perlite industry is concisely presented. The geology, mining, milling, processing, and applications of perlite, as well as the present status of the perlite industry are treated. Perlite, in strict petrological usage, describes a specific variety of volcanic glass in which strain, incident to cooling, yielded a concentric structure of fracturing which may be visible either to the naked eye or under a microscope. In commercial usage, the term perlite includes any naturally occurring acidic glass of volcanic origin that will expand when heated to a suitable temperature. The name perlite is a derivation of perlstein which originally defined "certain glassy rocks (hyaloliparites, hyalo-rhyolites) with numerous concentric cracks, from the fancied resemblance of broken out fragments to pearls."1 While perlite has been known to geologists for many years, it was not until 1941, while investigating perlite for use in enamel, that an assayer in Superior, Ariz., noted the unusual expansion characteristics of the ore. Further investigations were delayed until following World War II when many small plants were built and experimentation in the treatment and uses of perlite began. The Perlite Inst. was organized in 1949 to promote the development of the new industry, establish commercial standards through research, and to explore new uses and markets. The Institute, located in New York, represents some 50 producers in the U.S., Canada, Australia, England, France, Germany, Greece, Japan, Mexico, and New Zealand. In 1949, 71,l002 short tons of crude perlite were produced, sold or used by U. S. producers, and this figure increased to 325,0003 short tons by 1959. Such a rate of increase indicates the rapid and continuing growth of the perlite industry. GEOLOGY Perlite ore in its crude form has been found in seven of the mountainous western states, since un-devitrified siliceous volcanic rocks are limited to this section of the U. S. Commercially operated perlite deposits are normally of Eocene and Oli-gocene age.4 These deposits are often several hundred feet thick and may extend over hundreds of acres. In 1959, 13 companies in six states produced crude perlite, although the output in New Mexico comprised 79 pct of the total domestic crude output. Other states in order of their production were: Nevada, Arizona, California, Colorado, and Utah.5 Foreign deposits of perlite which are either producing or under exploration are Australia, Canada, Greece, Hungary,6 Iceland, Ireland, Japan, Mexico, New Zealand, and Sardinia. The ore may exhibit a variety of characteristics depending partially on its water content and eruption history and may range through many shades from black to white. While these characteristics may vary slightly among deposits, perlite ore from a particular source is normally quite uniform. Available chemical analyses of perlites from a large sampling of domestic deposits were recently assembled by the Technical Committee of Perlite Institute and are presented in Table I. While the ranges given do not apply to a particular perlite, they are an indication of the chemical analysis which may be expected from any presently commercially operated deposit. The specific gravity of the perlite ore ranges between 2.2 and 2.4, and its bulk density when crushed and sized is 75 to 90 Ib per cu ft. MINING AND MILLING Perlite ore is quarried from open pits by conventional power equipment, although blasting has been occasionally employed. The rock is then stock-piled until needed. While the milling of perlite may seem a simple process compared to that required for basic metals, or even other nonmetals, the need for accurate control of particle size becomes extremely important in further processing. The first step in this operation is the primary crusher, which is normally a jaw crusher. Following crushing, the material is dried, if necessary, in a rotary dryer and conveyed to a secondary grinder which may be a rod mill, hammer-mill, or cone crusher. However, the crushing characteristics of the perlite, caused by incipient cooling fractures, requires it be removed from the grinding operation once it is reduced to the required size so as to prevent overgrinding. Following the grinding operations, various size screens are used to separate the ore according to particle sizes required for particular uses. Most plants use two or more stages of crushing with perhaps four stages of screening.

Jan 1, 1961

By G. W. P. Rengstorff

In an effort to find an oxidation-resistant alloy of molybdenum, binary and ternary alloys containing aluminum, chromium, cobalt, iron, nickel, silicon, titanium, tungsten, vanadium, and zirconium were screened. Fourteen other alloying additions were also tested. Many of the alloys were more oxidation-resistant than molybdenum, but none were entirely satisfactory. MOLYBDENUM oxidizes extremely rapidly above 1450°F in air. At 1800°F, a loss of metal at the rate of 0.1 in. in 4 hr is typical. The high speed of this oxidation may be judged by comparison with the oxidation rate of 0.1 in. per year (0.00005 in. in 4 hr), sometimes taken as the maximum permissible oxidation rate at 1800°F for a satisfactory Fe-Cr-Ni alloy. Great strides have been made in the development of coatings and cladding to protect molybdenum from oxidizing atmospheres. These developments in surface protection will undoubtedly make it possible to take advantage of the excellent hot strength of molybdellum and its alloys in many new applications. Still, even the best coating can protect molybdenum only as long as the surface layer is unbroken. Research was undertaken to determine whether an alloy of molybdenum could be found which would resist oxidation. Such an alloy would not deteriorate suddenly when the protective surface layer was destroyed in a small area. In seeking an alloy of molybdenum to resist oxidation, the physical properties of molybdenum could not be sacrificed entirely. The development of an alloy with the desired resistance to oxidation was not achieved. The information obtained on the effect of a large number of elements on the oxidation of molybdenum is, however, of value in the development of coatings. Indeed, many of the alloys tested for oxidation resistance were already known to have poor mechanical properties but were tested to aid in the development of coatings. Oxidation of Molybdenum The rapid oxidation of molybdenum is usually attributed to the volatility of Moo,,. Gulbransen and Wysong have shown that molybdenum oxidizes very slowly up to 850°F, the temperature at which the oxide film begins to evaporate. Melting as well as evaporation of molybdenum oxides promotes the oxidation of molybdenum. MoO melts at 1465°F. MOO, the oxide which is believed to form at the metal-oxide interface, combines with MoO, to form a eutectic having a melting point of 1432°F.' The liquid oxide, even if nonvolatile, could cause poor resistance to oxidation by allowing easy transport of molybdenum and oxygen ions through the oxide. Actually, a sudden increase in the rate of oxidation of molybdenum at 1460°F has been observed to coincide with the appearance of a liquid phase. The formation of a volatile oxide is not unique with molybdenum. The problem is also encountered with vanadium, tungsten, and some of the Pt-Pd group of metals. Vanadium not only forms the volatile V2O3 but, like molybdenum, forms a liquid oxide coating. Few attempts have been made, however, to prevent the rapid oxidation of these metals by alloying. Oxidation of Molybdenum Alloys At the beginning of this work, very little was known of the oxidation resistance of molybdenum alloys. It was known that molybdenum disilicide (with 37 pct Si) has extremely good oxidation resistance,' but this compound is so brittle that it has few uses. It is an effective protective coating for molybdenum when allowance can be made for its brittleness. Chromium was known to retard the oxidation of molybdenum,' but at least 50 pct Cr was necessary to have an appreciable effect. Other, unpublished, reports show that a few other alloys have been given preliminary tests, but the results have not been promising." Choice of Alloys to be Investigated An alloying element might be expected to protect molybdenum in either of two ways: Its oxide might combine with molybdenum oxide to form a stable, nonvolatile complex oxide (a molybdate); or the oxide of the alloying element might form in preference to molybdenum oxide, developing an impervious layer which would prevent the formation of a volatile molybdenum oxide. The knowledge available about the formation of molybdates was meager. Therefore, the initial study was made on alloys of molybdenum with elements having especially stable oxides. On this basis, binary and ternary alloys containing the following six elements were investigated: aluminum, chromium, titanium, zirconium, silicon, and vanadium. Nickel was also added as an alloying element. Although it does not form a more stable oxide than molybdenum, it does impart some oxidation resistance to copper and iron. Its inclusion in the study was fortunate because its alloys proved to be the most promising of those first tested. Apparently nickel formed a stable molybdate. Because nickel was effective in reducing the oxidation rate of molybdenum, the elements iron, cobalt, and tungsten were added to the list. The ten alloying elements mentioned form ten binary and 45 ternary alloying systems with molybdenum. A series of alloys was tested in each of these systems. In addition, at least one test was made on the effect of each of the following alloying elements:

Jan 1, 1957

By D. W. Frommer

Processing nonmagnetic taconites by selective flocculation-desliming and flotation requires large volumes of water. If impounded without treatment, these off-process waters require excessively large areas for containment. To discharge the waste water into natural waterways would contribute to stream pollution and likely would not be permitted. In U.S. Bureau of Mines experiments conducted in the Twin Cities Metallurgy Research Center's 900-lb per hr pilot plant, approximately 85% of water requirements for the flotation-based treatment of a Michigan nonmagnetic taconite were met by reclaimed water. Water reclamation of the off-process streams from flotation was accomplished by controlled additions of lime, sodium carbonate, and a synthetic flocculant to reduce turbidities to 51000 ppm equivalent SiO*, while maintaining a Ca(II) content of =16 ppm in the finished effluent. Flotation concentrates of good quality were obtained using the reclaimed water. The cost of chemicals used in water reclamation was approximately equal to the savings in flotation reagents attributed to recycling of the water. Water quality is perhaps as important to flotation as are the reagents used. The character of water is extremely variable, depending on whether the source is a well, lake, or stream, upon the season and temperature, upon prior use, and upon the character of the watershed. All of these factors influence the water hardness and the quantity of other dissolved inorganic salts, turbidity, dissolved and suspended organic matter, dissolved gases, and pH. Frequently, the differences in water quality can measurably influence flotation selectivity, often to the point of spelling success or failure. Water hardness is particularly troublesome in flotation systems employing fatty acids, but other unrecognized constituents may also contribute to peculiarities in flotation behavior. Furthermore, a given water source may be entirely satisfactory in one flotation system, but entirely inappropriate in another. In recent years, society has given more attention than formerly to water use, even in areas where water is plentiful. However, both the demands of a growing population, with increased per capita needs, and also those of industry must be met. As a result, riparian rights must be negotiated with the appropriate government agency or agencies so that consumption of water is often allocated or otherwise controlled. Furthermore, the disposal of off-process industrial and domestic water is coming under the increasing scrutiny of these same governmental units. In these respects, the mineral industry is no exception, so that conservation, water reclamation, and reuse may be expected to assume increasing importance. In 1932, it was stated that, "water reclamation is generally more expensive than the economy in water and reagents resulting from its use. It is employed only if it is urgent to save water."' The economic aspects of this statement may still be true, but the unrestricted use of water is becoming less and less an option of the user. The purpose of this paper is to discuss an investigation conducted by the U.S. Bureau of Mines (USBM), in which water reclamation and treatment were undertaken to develop procedures for, and to assess the effects of, water reuse on the flotation treatment of nonmagnetic taconites. This investigation is a logical extension of previous work described by the author and associates at the Twin Cities Metallurgy Research Center employing selective flocculation-desliming and anionic flotation of silica from low-grade, nonmagnetic iron ores2,8 The requirements for the selective flocculation-de-sliming and the anionic flotation of silica processes determined the direction of the investigation. Previous studies had indicated that pH levels of about 11.0 and 11.8 were required for selective flocculation and flota-tlon, respectively. The calcium content of the water was believed to be of importance in both of these operations, and since Minneapolis tap water with a Ca(I1) content of about 16 ppm had been successfully used, an attempt was made to reclaim the process water at an equal level of dissolved calcium. Additionally, the objective was to nullify or effectively limit the effects of dispersants and fatty acid residuals from prior stages of processing. Last but not least, the system of water treatment had to have the capability of reducing turbidities to workable levels. With about half of the effluent being derived from the selective flocculation-desliming step and carrying about 25,000 ppm of highly dispersed, suspended fines, this last objective appeared formidable at the outset. Procedures for water reclamation were derived, in part, from well-known mineral dressing practices, from past observations and investigations, and from concepts contained in various pertinent publications on water treatment."c These procedures involved: 1) flocculation with lime and poly electrolyte-type flocculants, 2) lime-soda-ash softening, 3) chemical precipitation, and 4) mineral surface adsorption. Control was exercised at various stages of water reclamation by frequent measurements of Ca(11), pH, and turbidity.

Jan 1, 1971

By Henry R. Linden

The demand for natural gas continues to increase at higher than anticipated rates, partly because of its widening price advantage over most other fossil fuels when the cost of air-pollution control is included. However, there are clear indications that the natural gas supply from the conliguous 48 states and continental shelves will not keep up with this rapid growth in demand indefinitely. Projections are presented which define the extent of potential deficiencies from the 1970's to the year 2000. Among the sources of supplemental gas - imported pipeline natural gas from Canada and Mexico, tanker import of liquefied natural gas, and synthetic pipeline gas from coal and oil shale -by far the most abundant at potentially competitive costs is pipeline gas from coal. The state of development and relative economics of the various coal gasification processes are reviewed. It is shown that synthetic pipeline gas could become a very substantial market for bituminous coal and lignite at current mine-mouth prices - 60-70 million tons of coal for each trillion cubic feet of synthetic pipeline gas produced. This corresponds to only slightly more than the current annual increase in gas demand. Although annual discoveries (gross additions to proved reserves) of natural gas in the United States are still on a general upward trend from the current level of 22 trillion cu ft annually, most forecasters do not expect this to increase substantially in the foreseeable future. For example, the updated (to include 1966 and 1967 data) mathematical model of natural gas discovery and production in the U.S. developed by the Institute of Gas Technology (IGT)' projects that discoveries will level out at about 25 trillion cu ft annually in the late 1970's and during the 1980's and then decline to about 21 trillion cu ft by the year 2000 (Fig. 1). This adds up to a new supply for the period 1968-2000 of about 790 trillion cu ft. Experts who usually reflect the producers' viewpoint, such as Radford L. Schantz of Foster Associates,* are relatively more pessimistic. In contrast, a forecast just made by the U.S. Dept. of the Interior is much more optimistic.3 It assumes an increase in gas discoveries of 2.2% per year over the period 1965-80, reaching about 30 trillion cu ft in 1980. If this rate of increase were extended to the year 2000, annual discoveries would reach 46 trillion cu ft at that time, for a total over the period 1968-2000 of about 1100 trillion cu ft. To these forecasts of new gas discoveries must be added proved reserves of roughly 290 trillion cu ft,4 bringing total U.S. supplies for the rest of the century to nearly 1100 trillion cu ft (IGT) and possibly as high as 1400 trillion cu ft (U.S. Dept. of the Interior). This is approximately the same range as that of two estimates of total remaining recoverable natural gas supply: Potential Gas Committee, 980 trillion cu ft5 and IGT, 1450 trillion cu ft.6 Only the 1965 estimate by the U.S. Geological Survey7 suggests that economically recoverable natural gas supplies will not be exhausted around the end of the century. These forecasts are, naturally, based on the assumption that changes in technological, economic, and regulatory environment as they affect the gas industry will be of an evolutionary, not revolutionary, nature. The various forecasts of potential natural gas supply must now be compared to forecasts of natural gas demand (Table I). The general consensus is that the recent Future Requirements Committee projection to 1990' (extended to the year 2000 by the most recent U.S. Bureau of Mines (USBM) projection9) represents the minimum gas requirements (Table 11). They add up to a total of 1030 trillion cu ft for the period 1968-2000. Even this minimum anticipated gas demand exceeds the total remaining supply estimate by the Potential Gas Committee and would nearly exhaust the proved reserves plus new discoveries projected by IGT. The supply situation would appear much tighter if the demand projections of the Texas Eastern Transmission Gorp.10 and the American Gas Assn.(A.GA.)'' were used (Table I). Yet, these higher forecasts probably do not include the effects of such new markets as gas fuel cells, use of liquefied natural gas as a transport fuel, etc. They also may not fully reflect the impact of air quality control on the fuel market. Obviously, the probable discrepancy between projected supply and demand can only be accommodated in four ways. 1) Rapid increase in exploration and drilling activity to provide new supplies in the amount projected by the optimistic U.S. Dept. of the Interior forecast, coupled with an increase in net pipeline imports from Canada and Mexico from the present 0.5 trillion cu ft per year

Jan 1, 1970

R. W. Raymond, New Pork, N. Y.:—I think Mr. Bache has put his finger on the chief source of the danger of dust-, or gas-and-dust, explosions in collieries. 1 mean the persistent determination of the miners' unions to increase their weekly wages by the excessive use of explosives. This would not be feasible if coal-miners were paid by the day; but this form of payment is, for many reasons, not economically practicable; and the universal practice is to pay for the winning of coal according to the quantity produced. If the miner, by using a large amount of powder, can throw down a large amount of coal without corresponding labor on his own part in undercutting and drilling, he will receive more money for less work, provided he is paid for everything—merchantable coal, worth-less dust, slate, and " bone "—resulting from such a method. My attention was called to this matter many years ago by an admirable report of Prof. W. B. Potter, a past- President of the Institute, on the conditions obtaining in this respect in the Illinois coal-field. It was made very clear in that report that considerations of danger to workmen or loyalty to employers could not be relied upon to prevent miners from employing this perilous and wasteful method of increasing their own immediate receipts. So far as I know, only three remedies have been attempted, namely: the enforcement of discipline as to the methods of mining; the refusal to pay for dust, etc., produced by the miners'methods; and restriction upon the use of explosives, effected by requiring the miner to purchase them from the employer, at a price so high as to make it unprofitable for him to use them in excess. All of these attempted remedies have encountered the bitter opposition of the miners' unions. The enforcement of discipline has become almost impossible, if discipline be (as it should be) understood to involve punishment for the violation of rules when no disaster has followed. I

Jan 1, 1910

By C. C. Martin, M. C. Fuerstenau, R. B. Bhappu

Experiments revealed that quartz could not be floated in conductivity water at any pH with a long-chained sulfonate as collector. Various cations, Fe+++, Al+++, Pb++, Mn++, Mg++, Ca++, are shown to function as activators when the pH is such that the cation hydrolyzes. As the solubility product of the various cation-sulfonates was exceeded at the concentrations involved, precipitated cation-hydroxy-sulfonates, e.g. Fe (RSO3)2OH must be functioning as the collector in these systems. A number of interesting and important phenomena were revealed during a study of the response of beryl to sulfonate flotation.' Perhaps the most important observation is the effect of various cations on flotation response. Experiments showed that in the vicinity of pH 3.0, about three ppm Fe+++ increased recovery of leached beryl from about 60 pct to 100 pct, whereas about four ppm Ca+ + reduced the recovery from 60 pct to 2 pct. With the exception of ferric iron, all of the other cations investigated reduced flotation recoveries drastically at this pH. As postulated in the paper Sulfonate Flotation of Beryl,' even with low concentrations of polyvalent cations and sulfonate (on the order of one ppm), cation-sulfonates are precipitated immediately in solution. That is, blueish-white clouds were noted to form after given additions of salts to known solutions of sulfonate. Furthermore, it was also shown that one-hundred-fold more ferric iron than necessary to form the precipitated cloud had to be added to effect complete flotation. In other words, some form of solid ferric sulfonate was found to function as the collector in these systems. The form of the compound was suggested to be Fe(RCO3)2OH and that bonding to the surface occurs through the hydrogen of the hy-droxyl. As the form of this compound was shown to be dependent on the extent of hydrolysis of ferric iron, it is to be expected that ferric iron will be unique in some pH region. Further, if the presence of hydroxyl in the neutral precipitated compound is of primary importance, then other cations should function similarly but at different values of pH, since they will hydrolyze at different concentrations of hydroxyl ion. To determine whether the premise of hydrolysis is correct, the study was extended to quartz systems in the presence of various cations at various values of pH. EXPERIMENTAL MATERIALS AND METHOD Sodium alkyl aryl sulfonate was chosen as the collector for the experimental work. The reagent, sup plied as a courtesy sample by the Shell Chemical Co., has the following physical properties: Physical form Solid — Finely ground Sulfonate content, pct wt 95 to 97 Molecular Weight 450 to 470 Number of carbon atoms in hydrocarbon chain 25 to 30 Melting Point, OF 250 to 260 Solubility Soluble in water with gel formation at concentrations higher than 25 pct by weight sulfonate This particular reagent was chosen because of its high active sulfonate content, long-chain length, and solid form. With the exception of the frother and sulfonate, all other chemicals were of reagent grade quality. Conductivity water was used in the experimental work. This water, made by passing distilled water through an ion exchange column, had an average measured conductivity of one micromho. Experiments were conducted at room temperature in a small glass flotation cell with the following procedure: 1) A redetermined amount of water and salt solution (e.g. CaC12 . 2H2O) were combined and the pH adjusted to a given value. 2) A given amount of sulfonate was added so that final solution volume was 130 cc. 3) One drop of Dow 250 frother was added. 4) Five g of quartz were added and the system conditioned for five minutes. 5) The pH of the system was measured (termed flotation pH).

Jan 1, 1963

By L. L. Handy

The most common method of identifying hydrocarbon-bearing strata in a well that penetrates many different formations involves measurement and interpretation of the electrical properties of the formations as determined by electrical logs. Even though this method is used extensively, and even though in a great many instances it is capable of indicating presence of oil or gas, situations arise for which it is extremely difficult, if not impossible, to deduce the presence of hydrocarbons. These situations may involve the following. 1. A thin formation, bounded by highly resistive formations, in which it is impossible to obtain the actual resistivity of the uninvaded zone with existing logging devices. 2. A formation in which invasion has been so extensive that a value for the uninvaded zone resistivity cannot be obtained. 3. A very shaly formation in which the resistivity index, I, is lower than that usually associated with productive formations. 4. Laminated formations comprised of thin productive sands separated by thin shale streaks in which the individual sand and shale streaks are too thin to permit measurement of uninvaded-zone resistivity with existing logging devices. 5. Productive formations in which the water saturation is high. To extend the utility of electric log interpretation to identification of hydrocarbons in all types of formations, there is strong incentive to find a method not subject to these limitations. Some time ago, in connection with research on the wettability of reservoir rock, an investigation was conducted in which the resistivities of cores were measured shortly after they were removed from a core barrel, and again after they had been extracted and restored to their original oil and brine saturation.' The resistivities after extraction were generally lower. Other tests made on the cores indicated that they were more nearly water wet after they were extracted; thus, it was assumed that the observed changes in resistivities were due to a change in wettability of the cores. Other experiments'," have shown that resistivities of rock samples are sharply dependent on wettability. These experiments have shown that oil-wet samples are more resistive than water-wet samples. To obtain an understanding of how the wetting properties of the surfaces of core material affect electrical resistivity, a series of experiments was conducted. Two groups of core samples were prepared for testing. One group contained brine, but no residual oil. The other group was saturated with brine, flooded with oil to a low water saturation, then flooded with brine to a final residual oil saturation. Resistivity measurements were made on each group. Both groups were then flooded with the original brine to which a chemical had been added that renders sand and clay surfaces preferentially oil wet, a so-called reverse-wetting agent. very little change in resistivity was observed in cores containing only water. The group containing residual oil, however, showed resistivity increases of 100 to 200 per cent. These experiments showed that the resistivity of a core containing oil could be altered by changing wet-tability of the core. Moreover, the possibility was introduced that reverse-wetting agents might be employed as the basis for a logging method for identification of oil-bearing strata. Since behavior of a porous rock containing gas and water might be expected to be similar to that of a rock containing oil and water, such a method should also be applicable to identification of gas-bearing zones. In principle the wettability of the invaded zone could be reversed without altering conductivity of the interstitial water or the hydrocarbon saturation therein. Those strata showing significantly increased invaded-zone resistivities would, therefore, contain hydrocarbons; those with no significant change would be filled only with water. Addition of a reverse-wetting agent to a hydro carbon -bearing zone which is, by nature, already preferentially oil wet would not result in an enhancement of its resistivity. It is generally believed, however, that most hydrocarbon-bearing strata are preferentially water wet.

By F. D. Rosi

The slip and twinning behavior in extended titanium crystals were studied in some detail. The formation and appearance of coarse kink bands are discussed. Their crystallographic geometry was determined by X-ray analysis. A phenomenological interpretation of the complexities in kink band development is also presented. The critical resolved shear stress, coefficient of shear hardening, and plane of fracture were determined for several crystals extended at room temperature. THE slip and twinning elements observed in the room-temperature deformation of titanium were enumerated in a previous paper1 in which considerations were advanced regarding the nature and selection of these elements and their effect on the known mechanical properties of this metal. The present study concerns the crystallographic, microscopic, and mechanical aspects of flow in relation to the slip and twinning elements, and includes a prediction of slip systems, nature of slip and twin markings, inhomogeneities of plastic flow, and stress-strain characteristics. Unless otherwise noted, arc-melted titanium sponge (99.77 pct) was used in these experiments. The method of production of crystals, their dimensions, and the surface preparation for micrographic examination have been reported.&apos; For obtaining stress-strain characteristics, only those crystals which traversed the entire width of the specimen and were at least 8 mm in length were used. Tensile deformation of the crystals was performed with conventional grips for sheet specimens and a constant-stress loading beam, designed after the method of Andrade and Chalmers.&apos; The specimens were loaded by allowing sand to flow from a reservoir into a bucket suspended from the longer end of a balanced 6:1 lever arm at a rate controlled to load the specimen approximately 2 kg per min. Strain measurements were made using the Baldwin SR-4, bonded, resistance-wire strain gage, Type A-8, which permitted a reading accuracy of 2 microinches per inch. The formulas used in the evaluation of shear stress and shear strain, as in deriving the coefficient of shear hardening, are given by Schmid and Boasv n terms of the original orientation and change in length of the crystal. For calculating the critical resolved shear stress, the standard equation was used. The crystallographic nature of the unpredictable slip observed in a number of specimens was determined by the single-surface X-ray method of analysis as described in ref. 1. Experimental Results Prediction of Slip System: It was reported&apos; that room temperature slip in titanium takes place predominantly on {10i0} and in a <1120> direction, giving three potential slip systems. Hence, it should be possible to predict the operative primary system in the manner used by Taylor and Elam&apos; for alu- minum (i.e., the one with the greatest component of shear stress in the direction of slip). The stereo-graphic construction in Fig. 1 shows that this is true. In all cases, slip was found to occur initially on the (0110) plane and, in a number of cases, in the [21f0] direction. (The direction of slip was not determined for all orientations.) It follows that duplex slip can be expected when two slip systems are geometrically equally favorable for slip, as demonstrated in Fig. 2. In both crystals slip took place simultaneously on the (1700) and (olio) prismatic planes, as indicated by Fig. 2a and b. In the case of crystal B the movement of the specimen axis with increasing extension was toward the (10i0) direction, which represents the stable end orientation resulting from alternate slip on the [2ii0] and [1120] directions. This is analogous to the duplex slip process in face-centered cubic metals." Unpredictable Slip: In a number of crystals whose orientations were well within the operation of a single slip system, secondary slip occurred on planes not predicted by the criterion of maximum shear stress. Examples are shown in Fig. 3. In addition to

Jan 1, 1955

By K. E. Brown, A. R. Hagedorn

Continuous, two phase flow tests have been conducted during which four liquids of widely differing viscosities were produced by means of air-lift through 1%-in. tubing in a 1,500-ft. experimental well. The purpose of these tests was to determine the effect of liquid viscosity on two-phase flowing pressure gradients. The experimental test well was equipped with two gas-lift valves and four Maihak electronic pressure transmitters as well as instruments to accurately measure the liquid production, air injection rate, temperatures, and surface pressures. The tests were conducted for liquid flow rates ranging from 30 to 1,680 BID at gas-liquid ratios from 0 to 3,-270 scf/bbl. From these data, accurate pressure-depth traverses have been constructed for a wide range of test conditions. As a result of these tests, it is concluded that viscous effects are negligible for liquid viscosities less than 12 cp, but must be taken into account when the liquid viscosity is greater than this value. A correlation based on the method proposed by Poettmann and Carpenter and extended by Fan-cher and Brown has been developed for 1¼-in. tubing, which accounts for the effects of liquid viscosity where these effects are important. INTRODUCTION Numerous attempts have been made to determine the effect of viscosity in two-phase vertical flow. Previous attempts have all utilized laboratory experimeneal models of relatively short length. One of the initial investigators of viscous effects was Uren1 with later work being done by Moore et al.2,3 and more recently by Ros.4 However, the present investigation represents the fist attempt to study the influence of liquid viscosity on the pressure gradients occurring in two-phase vertical flow through a 1¼-in., 1,500 ft vertical tube. The approach of some authors has been to assume that all vertical two-phase flow occurs in a highly turbulent manner with the result that viscous effects are negligible. This has been a logical approach since most practical oil-well flow problems have liquid flow rates and gas-liquid ratios of such magnitudes that both phases will be in turbulent flow. It has also been noted, however, that in cases where this assumption has been made, serious discrepancies occur when the resulting correlation is applied to low production wells or wells producing very viscous crudes. Both conditions suggest that perhaps viscous effects may be the cause of these discrepancies. In the first case, the increased energy losses may be due to increased slippage between the gas and liquid phases as the liquid viscosity increases. This is contrary to what one might expect from Stokes law of friction,&apos; but the same observations were made by ROS4 who attributed this behavior to the velocity distribution in the liquid as affected by the presence of the pipe wall. In the second case, the increased energy losses may be due to increased friction within the liquid itself as a result of the higher viscosities. The problem of determining the li- quid viscosity at which viscous effects becomes significant is a difficult one. Ros4 has indicated that liquid viscosity has no noticeable effect on the pressure gradient so long as it remains less than 6 cstk. Our tests have shown that viscous effects are practically negligible for liquid viscosities less than approximately 12 cp. Actually there is no single viscosity at which these effects become important. These effects are not only a function of the viscosities of the liquids and of the gas but are also a function of the velocities of the two phases. The velocities in turn are a function of the in situ gas-liquid ratio and liquid flow rate. Furthermore, the role of fluid viscosities in either slippage or friction losses will depend on the mechanism of flow of the gas and liquid, i.e., whether the flow is annular. as a mist, or as bubbles of gas through the liquid. These mechanisms are also a function of the in situ gas-liquid ratios and the flow rates. It would thus seem that the best one could hope for is to determine a transition region wherein the viscous effects may become significant for gas-liquid ratios and liquid production rates normally encountered in the field. The viscous effects might then be neglected for liquid viscosities less than those in the transition region but would have to be taken into account when higher viscosities are encountered. There are numerous instances where crude oils of high viscosity must be produced. The purpose of this study has been to evaluate the effects of liquid viscosities on twephase vertical flow by producing four liquids of widely differing viscosities through a 1 % -in. tube by means of air-lift. The approach used in this study was as follows:

Jan 1, 1965

By W. J. Helfrich, R. A. Dodd

Binary aluminum solid-solution alloys containing various amounts of silver, magnesium, and zinc were prepared by careful directional solidification, and the hydrostatic and X-ray densities were compared. With the exception of the Al(Ag) alloys, the X-ray densities were consistently greater than the hydrostatic measurements, in agreement with earlier observations by Ellwood. In contrast to Ell-wood&apos;s interpretation in terms of vacant lattice sites associated with Brillouin zone effects, a tentative explanation based on the existence of solidification microshrinkage was favored. This hypothesis was confirmed by an examination of Al(Zn) alloys prepared by vapor diffusion of zinc into aluminum. The hydrostatic and X-ray densities were now in very close agreement, and it was concluded that the filling of Brillouin zones in aluminum solid-solution alloys does not necessarily result in the formation of defect structures containing an excess of vacant lattice sites. ThE existence of defect structures of the vacancy type in alloys in which the excess vacancies have an electronic rather than a thermal or mechanical, and so forth, origin is well recognized. Examples of incomplete lattices of this type are to be found in the Ni-Al,1-3 Fe-Ni-A1,4 c~-Ni-Al,5 Fe-Cu-Al,= and Co-A17 systems. These defect structures are of a special kind in that the intermediate phases possess an ordered atomic arrangement or superlattice, and in some instances the vacancy concentration may be unusually large, e.g., at 45.25 at. pet Ni in NiA1, approximately 8.8 pet of the lattice sites are unoccupied. Ellwood8-10 has reported similar defect structures in the aluminum solid solution alloys of the Al-Zn and A1-Mg systems and in alloys of the Au-Ni system." In Al(Zn) the (apparent) vacancy concentration rose, somewhat irregularly, to a maximum of about 2 pet vacant sites at 25 at. pet Zn, while in Al(Mg) the (apparent) vacancy concentration increased continuously to 1.7 pet at 15 at. pet Mg. An explanation in terms of Brillouin zone overlap was attempted, although Pearson12 has pointed out the difficulty of reconciling the observations with zone theory. However, the possibility of the effect being caused by the Fermi surface just touching a plane of energy discontinuity inside a prominent Brillouin zone has, in general, been accepted. In fact, Massal-ski13 has interpreted Ellwood&apos;s8 observations as confirmation of Leigh&apos;s14 theoretically predicted zone overlap occurring at approximately 2.67 electrons per atom. Unfortunately, Massalski was apparently unaware that Ellwood9 had revised his earlier results considerably, and the revised data did not confirm Leigh&apos;s analysis. Ellwood&apos;s clata were reexamined by the present authors who noted a possible correlation between the percentage defects as a function of alloy composition and the temperature interval of solidification measured from the respective equilibrium diagrams. This suggested an explanation in terms of shrinkage porosity rather than vacant lattice sites, and pointed to the desirability of reexamining appropriate alloy systems using: both Ellwood&apos;s method of specimen preparation (casting followed by wrought fabrication) and alternativ&apos;e methods, i.e., diffusion, which might be expected to minimize, or even completely obviate, microporosity. ALLOY PREPARATION 1) Cast Allolys and Aluminum Single Crystals. Al(Ag), Al(Mg;l, and Al(Zn) alloys of various compositions up to 20 at. pet silver, 13.5 at. pet mg, and 30 at. pet Zn were prepared by melting under helium and casting into graphite molds. In the first two systems, the maximum alloying addition was quite close to the limit of solid solubility, but the possibility of transformation to a&apos; during quenching somewhat restricted the suitable Al(Zn) composition range. The alloys were prepared from high-purity aluminum, a lot analysis showing 0.002 wt pet Cu, 0.002 wt pet Fe, and 99.996 wt pet A1 by difference. The silver, magnesium, and zinc were of 99.99+, 99.98+, and 99.998 wt pet respectively. Each composition was analyzed chemically. The as-cast ingots measured 7/16 in. diam and 5 in. length. One in. was removed from the top of the ingot, and the bottom 3 in. was machined to 0.275 in. diam; a point was also machined on the smaller diameter end. The remainder of the original ingot served as a top riser during subsequent remelting and controlled solidification. The machined ingots were now remelted using a Bridgman soft-mold technique to ensure directional solidification and, therefore, a minimum of micro-shrinkage. Alumina powder was used as mold material contained in an alundum thimble, and this crucible was placed in a helium-filled Vycor tube. The assembly was lowered through a suitable temperature gradient at approximately 0.5 in. min-l, and the risered portion of the casting was subsequently removed by sawing.

Jan 1, 1962

By Orville Lyons

CENTRIFUGAL force has been utilized for the dewatering of fine coal for over 50 years by means of machines commonly called centrifugal dryers. In any centrifuge the coal and water are subjected to a spinning action which usually increases in intensity as the coal progresses through the machine. This spinning action, or the centrifugal force that it induces, tears water away from coal particles and produces a dewatered coal. The effectiveness of the dewatering action for any particular machine is governed by the size-consist of the coal and the centrifugal force imparted to the water on the coal.

Jan 5, 1951