LITTLE study has been made of the pressure changes and energy losses that take place when an air current is divided into splits which subse-quently unite. The discussion and the experiments that are described in this paper deal with the division of an air current into square splits of equal size, the area of each of the splits at the downstream junction being one-half the area of the main duct. APPARATUS AND SYMBOLS The duct system shown in Fig. 1 was built of Y4-in. redwood and made as smooth as possible.The section of the top over the splits and the zone of mixing was of plate glass to permit observation of the stream lines. FIG. 1-DUCT SYSTEM. Static pressures were measured by means of pinhole tubes and a precise inclined manometer. Measurements of rates of flow were .made by determining the drop in pressure through concentric square orifices in the splits. The air was supplied by a fan operated by a direct-current motor that received its current from a motor generator set. Delicate rheostats in the armature. of the motor. made possible the perfect control of the fan speed, which was indicated on an electrical tachometer. Vanes to straighten the. flow were placed at the head of the main duct.

Jan 1, 1933

By J. C. Fisher

Martensite transformations in steels and other alloys are characterized in part by the absence of composition changes during the growth of a new phase. Transformation occurs rapidly, and there is insufficient time for long range diffusion or partition of alloying elements to take place; martensite reactions in alloys thus are similar to phase transformations in single component systems. A fundamental understanding of martensite transformations in steels is impossible without knowledge of the free energy change upon transforming austenite (face centered cubic iron containing alloying elements) to ferrite (body centered cubic iron containing alloying elements) of the same chemical composition. The present paper assembles the best information available concerning the influence of temperature and composition on this free energy change. Most of the material has been taken from the work of Johansson,' Mehl and Wells,2 Zener3,4 and Smith;5 and indirectly, through these authors, from the work of Austin.6 In agreement with the generally accepted viewpoint, martensite is assumed to be an ordered solution of carbon in ferrite of the same composition as the parent austenite; only at high temperatures and low carbon concentrations is the carbon in ferrite distributed at random. The properties of the disordered solution are estimated by extrapolating the known properties of iron-carbon solid solutions into the range of supersaturation, and the free energy change associated with ordering is estimated from the theory developed by Zener. By incorporating Smith's recent thermodynamic measurements and Zener's theory of ordering, the present analysis modifies previous estimates of the free energy change associ- ated with martensite transformations. Consider a two component system consisting of a solvent A and a solute B. Let Na and Nb represent mol fractions of A and B respectively, let aa = raNa and ab = YbNb represent activities, and let superscripts 1 and 2 refer to phases 1 and 2. The partial molal free energies of A and B in phases 1 and 2 can be summarized as follows: free energy standard state Fa' - Fao1 = RT In an1 pure A' Fa2 - Fa2 = RT In aa2 pure A2 Fb1 - Fbo = RT In ab1 pure B Fs2 - FB2 = RT In aB2 pure B. The free energy of a gram atom of phase 1 is* AF1 = Na'Fa1 + Nb'Fb1 and that of phase 2 is AF2 = NA2FA2 + NB2Fb2. A martensite transformation from phase 1 to phase 2 requires Na1 = Na2 = Na and NB1 = NB2 = Nb, and the free energy change per gram atom accompanying transformation is AFi-2 = NA(Fa2 - Fa1) + Nb(Fb2 - Fb1) = NA[RT In (aA2/aA1) + AFa1?2] + Nb RT In (aB2/aB1) = Na[RT In (ra2/ra1) + AFa1?2] + Nb RT In (TaVTB1). [1] where yn2, yn1, yB2, yB1 are activity coefficients, and where Ma'+* is the free energy change upon transforming a gram atom of pure A from phase 1 to phase 2 at the temperature in question. For martensite transformations in plain carbon steels, A = iron (Fe), B = carbon (C), 1 = austenite (7). 2 = ferrite (a), and Eq 1 is AFr ?a= NFe[RT In (rf.a/rfer) + AFF.r?a] + TVc RT In (eca/rc1)- L2] Nothing is known concerning the values of yFea and yca for carbon concen- , trations in excess of 0.025 pct. However, the approximation rf.7 = 7f." = 1 cannot be appreciably in error for small carbon concentrations, and Eq 2 reduces to Afr-a = NfeFfer?a1 + NC RT In (rca/rcr)- [3] Johanssonl and Zenera have calculated MFfr?a from the specific heat measurements compiled by Austin.6* Their calculated values agree closely, and are summarized in Table 1. The activity coefficients relative to graphite for carbon dissolved in iron vary with temperature according to the relationships d In rcr/d(1/T) = AHcr-R dlnyca/d(l/T) = AHCa/R where AHc? and AHca are the heats of solution of graphite in y and a iron. Assuming the values of AH to be independent of carbon concentration and temperature, In rCr = AHcr/RT + I1 In rca = AHCa/RT + 12

Jan 1, 1950

By Leroy Palmer

ALL the domestic. production of magnesite during 1925 came from two states, California and Washington. Of a total of 120,660 tons of crude ore, 64,600 tons, or 54 per cent., were produced in California.1 Of .this quantity California produced about 99 per cent. of the caustic calcined, but only 10 per cent. of the dead-burned. The largest producer was C. S. Maltby, of San Francisco, who operated the Red Mountain mine, in Santa Clara County, and the Sampson mine, in San Benito County, under lease. These two mines have been studied by the author, and offer interesting comparisons as to mining and treatment methods and final products. GEOLOGY The general geology of the magnesite deposits of California has been described by Hess,2 Bain3 and others,4 and although a detailed discussion is not necessary here, a brief summary will assist in understanding mining conditions. California magnesite, when comparatively pure, is usually a white, fine-grained rock, with a conchoidal fracture, occurring in veins and lense-like masses in serpentine. The veins vary considerably in width, and usually occur in a series of more or less parallel veins intersected by other series or systems of veins, probably following original or secondary fissures in the enclosing serpentine. The most generally accepted theory of origin is that the magnesite was formed by the action of surface waters charged with C02 percolating downward through fissures and changing the magnesium silicates of the serpentine into magnesium carbonate.

Jan 1, 1927

By G. Derge, M. Bourgon, G. M. Pound

A STUDY of electrical conductance in molten Cu-Fe sulfide mattes' has shown that pure molten Cu,S behaves like a semi-conductor in that it is an electronic conductor and its specific conductance, of the order of 100 ohm-' cm-', increases with increase in temperature. On the other hand, pure molten FeS, another electronic conductor, behaves like a metallic conductor in that its specific conductance, about 1500 ohm-' cm-', decreases with increase in temperature. Molten solutions of Cu,S and FeS follow a roughly additive rule of mixtures with respect to both specific conductance and temperature coefficient. The behavior of molten Cu,S may be understood, by analogy to the situation in solids, in terms of semiconductor theory.' It is thought that, although the melt consists of cuprous and sulfide ions, the bond between these atoms has a certain degree of cova-lency. According to the simplest concept the electrons in the partially covalent bonds are thermally promoted to a conduction band. In another concept, small amounts of impurities (undetermined) provide donor or acceptor levels in the forbidden zone between the valence and conduction bands and thus facilitate semi-conduction in the usual way. However, the metallic behavior of molten FeS is difficult to explain, because one might expect from similar reasoning that it too should act like a semi-conductor. It was suggested that the apparent metallic behavior of molten FeS might be explained by a large negative temperature coefficient of density. Thus if molar conductance instead of specific conductance were plotted versus temperature, the slope might prove to be positive, indicating semi-conduction instead of apparent metallic conduction. Accordingly, density measurements were made in order to answer this question in regard to molten FeS and also to provide data for conversion of specific conductance to molar conductance for molten Cu,S and a molten 50-50 wt pct Cu-Fe sulfide matte. Experimental Diagrams of the apparatus are given in Figs. 1 and 2. A 3 x 8-cm dense alundum crucible containing the prefused specimen is positioned in the uniform temperature zone of an induction furnace tube and melted under a helium atmosphere. Then the cell assembly, consisting of two 3-mm spectro-graphite rods, one of which is in a 1-cm ID open

Jan 1, 1959

By T. W. Guy

IN approaching the problems of sampling coal, a brief statement of certain facts that are more or less taken for granted may be helpful: 1. The coal-mine operator needs reliable data as to the physical and chemical characteristics of his coal in order to plan and control intelligently its mining, preparation, and marketing. The consumer needs such data in order to select the equipment and the coal best suited to meet his requirements, to check the quality of fuel delivered, and the efficiency of its use. Various government control agencies require such data as a basis for classifications and establishment of limits, for use in carrying out the requirements of federal, state or municipal laws. 91. All such data must be obtained by analyses, measurements, or tests made on samples, which are taken to represent the coal tested. It is now becoming generally recognized that, in accordance with statistical laws, test results from samples are not expected to represent the exact qualities of the lot or lots from which they are taken, except within statistical, or "expected limits. Such limits are definitely specified by some present standards of the American Society for Testing Materials and the British Standards Institution. 3. Samples that give ash within satisfactory limits are usually assumed to be sufficiently accurate for other analyses, except under special condi¬tions such as meeting close specifications for coals showing wide variability in sulphur, fusibility of ash, or other quality. 4. In modern coal sampling the increment is recognized as the basis for taking samples. For a given accuracy the number and weight of increments specified are increased with: (a) the expected ash, and (b) the top size designation of the lot to be sampled. 5. It is extremely important that every sampler recognize that: the specified number and weight of increments are minimums, and that the precautions to be used in order to take them properly are also minimums; that in the reduction of the gross sample the sizes specified for the coal after each stage of the crushing are maximum; that the quantities specified to be taken after each crushing stage are minimum; that any short cuts or failures to meet the requirements specified will reduce the statistical accuracy of the results, although it is possible that one or two checks on a few results may seem to show otherwise.

Jan 1, 1943

The first record of coal anywhere in the Appalachian regions of which we now know is along the north fork of the Potomac River, above the mouth of Savage River, on a map entitled, A Plan of the upper Part of Potomack River call Cohongorooto Survey'd in the Year 1736. Benj. Winslow1 two "Cole-mines" are shown, one just above Green Island and the other just below Hopwood Run. Winslow was in charge of a surveying party to "Lay out the Bounds of the Northern Neck of Virginia," or Lord Fairfax's Grant, his party locating the liver above the mouth of the Shenandoah, while another party located it below that point, and then around Chesapeake Bay and up the Rappahannock River. The results of the two surveys were combined in a map called, The Courses of the Rivers Rappahannock and Potowmack, in Virginia, as surveyed according to Order in the Years 1736 & 1737, made by Wm. Mayo, which does not show the "cole-mines;" this map was used with the report of the boundary commission which was sent to London in the case before the Privy Council. The boundary line decided upon was surveyed on the ground in 1746, just ten years after the original one. The results of this work were shown on A Map of the Northern Neck in Virginia, According to an Actual Survey begun in the Year MDCCXXXVI, and ended in the Year MDCCXLVI, Drawn by Peter Jefferson And Robert Brooke, Surveyors, which is now in the Colonial Office in London. This map shows the "cole-mines" in the same location as on Winslow's map, and taken from his record, of course, as that part of the survey was not retraced. Faulkner, who examined all of these records in his review of the case in 1832, refers to the notes of the original survey as "No. 10. The original field notes of the survey of the Potomac River, and the mouth of the Shenandoah to the head spring of said Poto¬mac River, by Mr. Benjamin Winslow." While the notes of the 1746 survey are in the London records and photographic copies of them are in several libraries in this county, the notes of the 1736 survey cannot be found anywhere. (For Chas. J. Faulkner's report, dated Nov. 6, 1832, see Kercheval's History of the Valley of Virginia, pp. 160-173. Jas. W. Foster's Maps of the First Survey of the Potomac River, 1736-37, in Wm. and Mary College Quarterly History Mag., April, 1938, gives a complete history

Jan 1, 1942

By W. H. Howard

As the result of a series of analyses and volume determinations of gases discharged from the converters at the Garfield Smelting Co.'s smelter at Garfield, Utah, it was found that a considerable amount of lead fume was escaping from the stacks of the converter plant, and that if this lead could be recovered at a reasonable expense an attempt should be made to collect it. Two methods suggested themselves: (1) filtration through bags; (2) electrical precipitation of the condensed fume by a Cottrell plant. Filtration through Bags Tests were made in filtering converter gases through the ordinary woolen bags of lead-smelter bag houses to determine how long such material could withstand the corrosive action of the gases. While blowing on white metal only, the fabric was usually destroyed in 10 to 14 hr. In tests conducted in filtering gases when blowing on matte or slagging stage exclusively and when relatively considerable lead was being volatilizcd, bags in one instance lasted 60.5 hr. It therefore was evident that the Garfield converter gases did not contain in themselves sufficient neutralizing elements for the purpose of direct bag filtration, even during the slagging stage. Such results were more or less anticipated, but it was thus proved that under all conditions of blowing Garfield mattes a very considerable amount of neutralizing agent, zinc oxide or lime, or both combined, as in the Sprague process, would be required to render bag filtration possible. Again, owing to the constantly changing quantities of SO3 from a given battery of converters, depending on the number blowing at a given time and on the stages of the blow, it would be practically impossible to feed automatically the required amount of neutralizer. In order to safeguard the bags sufficient neutralizer would have to be continuously added to meet the maximum SO3 output, thus wasting neutralizers and giving an undesirably diluted final product. Such a condition is entirely different

Jan 1, 1915

Discussion of the papers of DAVID H. BROWNE, Louis V. BENDER, and R. E. H. POMEROY, presented at the New York meeting, February, 1915, and printed in Bulletin No. 97, January; 1915, pp. 49 to 60, 73 to 81, and No. 98, February, 1915, pp. 445 to 453, respectively. E. P. MATHEWSON, Anaconda, Mont.-After hearing about the success of D. H. Browne with his furnaces, we in Anaconda decided we might venture into the field of pulverized coal for reverberatory smelting. We sent a delegation of investigators to see Mr. Browne and his work, and they returned, filled with enthusiasm, and said they would recommend it strongly. We thereupon asked for an appropriation, and after some delay obtained the same and fitted up one furnace to use pulverized coal. We copied Mr. Browne's practice and his selection of machinery for drying and pulverizing coal; and we also copied the burner he used, which was a standard article on the market. We got an expert coal-dust machinery man to design our plant, and were very glad we did so as we avoided some of the unpleasantness that had been experienced at other plants through fires and minor explosions.

Jan 5, 1915

By H. D. Newell

Jan 1, 1938

By H. D. Newell

Jan 1, 1938

By Ursula E. Wolff

The precipitation of carbides from an alloy containing 33 pct Ni, 21 pct Cr, balance iron, was investigated electron microscopically by means of extraction replicas and thinned metal foils. Annealing temperatures ranged from 565°to 870°C and up to several thousand hours. M23C6 precipitated in pain boundaries, incoherent and coherent twin boundaries in that sequence. The orientation relationship between carbides and austenite matrix was determined and correlated with the morphology of the carbides and with the type of boundary in which precipitation occurred. In large-angle grain boundaries, as well as in coherent twin boundaries, the carbides had the same orientation as one of the adjacent pains. These carbides formed sheets of individual flakes with shapes related to the orientation of the boundary. In incoherent twin boundaries carbides precipitated in ribbons composed of pavallel rods. An unidentified subcarbide was found to precede precipitation of M23C6 in these boundaries. The M 23 C6 rods had a kind of fiber texture with (110) parallel to the long dimension of the rods and ribbon, and with orientations of both of the adjacent twin-related austenite crystals Predominant in the texture of the carbide. A hard sphere crystal model has been used to discuss orientation and morphology of the carbides in terms of free volume and vacancies available in the boundaries. A number of papers have dealt with the morphology of chromium carbide (M23 C6) precipitated in austenitic stainless steels.1"7 In all these investigations, the carbides were examined in the electron microscope by means of extraction replicas. With this technique, the carbides retain the spatial distribution they had in the bulk sample. However, since the matrix is dissolved in the process, the particles can turn in an unpredictable way; and the orientation relationship between matrix and carbides cannot be established. In this paper the results of studies on extraction replicas and on thinned metal foils are reported. These studies were undertaken to determine the matrix-to-car bide orientation relationship, and to correlate the orientation of the carbides with their morphology. PROCEDURE The material used was an austenitic alloy with 33 pct Ni, 21 pct Cr, balance iron, containing approximately 0.05 pct C. Coupons of 1.25-mm sheet were first solution-annealed at 1050°C for 15 min and air-cooled. Then, to precipitate the carbides, samples were isothermally annealed in the range from 565" to 870°C for times up to several thousand hours. All further specimen-preparation procedures were carried out after the final anneal. Carbon extraction replicas from polished and etched surfaces were made with 10 pct bromine in methyl alcohol.' Thin foils were prepared from punched-out 3-mm-diam disksg which fit into the electron-microscope holder. The disks were prethinned by grinding to approximately 0.5 mm thickness, and then electro-polished in a polytetrafluoroethylene holder1' with a solution containing 5 pct perchloric acid in acetic acid to which 10 g per 1 Cro3 and 5 g per 1 nickel chloride were added (etchant modified from that of Briers et al."). This solution dissolves neither the carbides nor the austenite around the carbides preferentially. By using extraction replicas, electron micrographs and selected-area electron-diffraction patterns were taken from the same carbide arrays. By using thin foils, electron micrographs were made from a grain boundary area containing carbides. Electron-diffraction patterns were then taken from the same area and from each of the adjacent grains separately. In this manner, the orientation of each grain could be determined without interference by the carbide pattern. A peculiarity of extraction replicas should be pointed out. After the matrix is etched away, the carbide arrays float freely in the etching and washing solutions, and are held in place only at the anchoring points in the carbon replica. When the replica is picked up with a screen the carbide arrays tend to flip to one side. Thus, while the surface features are preserved, the original arrangement of the carbides may severely and unpredictably be disturbed whenever the specimen contains large amounts of interconnected carbides. Nevertheless, it is possible to correlate the different morphologies of the carbides with the type of boundary in which they have precipitated. RESULTS 1) Extraction Replicas. Fig. 1 shows that the grain boundaries usually are curved, multicornered surfaces of random orientation. The coherent twin boundaries (which are (111) planes) cut a grain into parallel slices. Incoherent twin boundaries occur at the ends and on the steps of twins and are often narrow, parallel-sided strips which are much longer than they are wide. Different morphologies can clearly be distinguished for the M23Ce carbides precipitated in each of these types of boundaries, and agree well with those observed by kinzel.2 The kinetics of this precipitation has been investigated." The first carbides precipitate in junctions of three grain boundaries and fan out from there into the adjoining boundary surfaces, Fig. 2(a). These carbides are oriented randomly, Fig. 2(b), and become coarser and thicker as annealing time increases. The large-angle grain boundaries are next to fill

Jan 1, 1967

By Donald Barton

THE theory of gravitation is based on Newton's law that any two bodies exert a mutual attraction which is proportional to the product of their masses and inversely proportional to the square of the distance between them; i. e., A = K MM/R2 (1) where K is a constant, M and m are the respective masses of the two bodies, and R the distance between them. In the earth's gravitational system, the earth is one of the bodies; the other may be any body within or without the earth. In theoretical discussions and calculations in regard to gravity, that other body usually is taken as a unit of mass: in the C. G. S. system, a body of one gram in mass. GRAVITY AND LEVEL SURFACES Gravity is defined in geophysics as the force of attraction exerted by the earth, towards itself, on a body of unit mass. The intensity of gravity is usually expressed in dynes of force or in centimeters of acceleration. In geophysical work in America, most commonly it is expressed in dynes (per gram) with the "per gram" understood and not directly expressed. In geophysical work in Europe, most commonly it is expressed in centimeters per second per second (cm./sec 2) and less commonly merely as centimeter-gram-second units (C. G. S.). At sea level, the intensity of gravity amounts very nearly to 980 dynes. The vertical is the direction along which the attraction of gravity is exerted at any point. In most cases, it is very nearly, but not quite, perpendicular to the earth's surface. The path that would be taken by a body falling freely through space toward the earth is vertical at each point and may be spoken of also as "the vertical," or as the line of the vertical, or as a line of force of gravity. At the earth's surface it commonly is very nearly, but not quite, a straight line.

Jan 1, 1928

By Sherwin F. Kelly

THIS is intended as a simple review of the principles and practice of geophysics, so will not be of interest to the geophysicist, who is hereby warned of its elementary character. The engineers for whom it is written are those who, having glimpsed the formidable formulas and discussions of the geophysicists, give all publications on the subject a wide berth. For a few years now the geo-physicists have had a tendency to be ingrowing at their meetings, going deeper and deeper into theory and instrument construction, and forgetting to present the topics that would interest the practicing engineer who desires merely to know how geophysics can help him, not why.

Jan 1, 1934

By Jr. E. H. Dix.

In selecting the subject, "Acceleration of the Rate of Corrosion by High Constant Stresses,'' for the 1940 Institute of Metals Division Lecture, I have been influenced by its highly theoretical and speculative nature as well as by the great practical importance of the correct interpretation and appraisal of the engineering significance of the phenomenon. I lay no claim to originality in talking on this topic, since it has been the subject of discussion for over a quarter of a century. However, as our technical thinking advances, old phenomena take on new and more significant aspects. In our studies at the Aluminum Research Laboratories, we have encountered many perplexing and seemingly contradictory results and have been fascinated by the problem of dovetailing all of the many pieces of information to make a complete picture. I hope that in the brief period of this lecture I may share with you some of the enjoyment we have had in attempting to meet this challenge to metallurgical science. The emphasis generally has been placed on the spontaneous failure by cracking of a metal under the combined action of high stress and corrosion, hence the present-day use of the terms "stress corrosion" or "stress corrosion cracking." The older term "season cracking," applied more specifically to copper-base alloys, includes, by inference, the element of time. For the purpose of the discussion today I will use "stress corrosion" to cover broadly the effect of stress in accelerating the rate of corrosion of metals. To stay within the limits of allotted time the disrussiorl will cover the effect of high static stresses rather than repeated or dynamic stresses, which would take us into the related field of corrosion-fatigue. The subject is particularly appropriate for an Institute of Metals Division Lecture because much the same phenomenon has been observed in almost all metal systems. Thus, in addition to the season cracking of brass may also be mentioned the "caustic embrittlement" of steel boiler

Jan 1, 1940

By Jr. E. H. Dix.

In selecting the subject, "Acceleration of the Rate of Corrosion by High Constant Stresses,'' for the 1940 Institute of Metals Division Lecture, I have been influenced by its highly theoretical and speculative nature as well as by the great practical importance of the correct interpretation and appraisal of the engineering significance of the phenomenon. I lay no claim to originality in talking on this topic, since it has been the subject of discussion for over a quarter of a century. However, as our technical thinking advances, old phenomena take on new and more significant aspects. In our studies at the Aluminum Research Laboratories, we have encountered many perplexing and seemingly contradictory results and have been fascinated by the problem of dovetailing all of the many pieces of information to make a complete picture. I hope that in the brief period of this lecture I may share with you some of the enjoyment we have had in attempting to meet this challenge to metallurgical science. The emphasis generally has been placed on the spontaneous failure by cracking of a metal under the combined action of high stress and corrosion, hence the present-day use of the terms "stress corrosion" or "stress corrosion cracking." The older term "season cracking," applied more specifically to copper-base alloys, includes, by inference, the element of time. For the purpose of the discussion today I will use "stress corrosion" to cover broadly the effect of stress in accelerating the rate of corrosion of metals. To stay within the limits of allotted time the disrussiorl will cover the effect of high static stresses rather than repeated or dynamic stresses, which would take us into the related field of corrosion-fatigue. The subject is particularly appropriate for an Institute of Metals Division Lecture because much the same phenomenon has been observed in almost all metal systems. Thus, in addition to the season cracking of brass may also be mentioned the "caustic embrittlement" of steel boiler

Jan 1, 1940

By C. D. King

The advances in basic open-hearth practice which have occurred during the past decade have been principally in the direction of the physical development of larger units, decreased fuel consumption and increased length of furnace campaigns. However gratifying the economies which have resulted from these improvements are, it must be granted that like advances in chemical, physical-chemical and metallurgical knowledge pertaining to open-hearth practice would have added greatly to these already attained reductions in costs and it is the purpose of this paper to stimulate the discussion and study of these phases of cooperation and their relation to ingot yields. Definition and Calculation oF Losses In discussing basic open-hearth yields, the writer refers to the ingot yields obtained in the process of converting pig iron, scrap and ore to steel. In this conversion some scrap is produced. The difference between the total weight of ingots and scrap produced and the original metallic charge constitutes the loss. Basic open-hearth yields vary considerably, and while some of the divergencies can be explained metal-lurgically because of differences in slag analysis, proportion of pig charges, and character of steel made, there often remain differences that apparently do not readily disclose themselves. In reconciling yields by the usual accepted methods of calculation, one is often forced to evaluate large losses as ((unaccounted for." Such a system is prone to accept these large losses as inherent to the operat.ion and not, susceptible of appraisement and correction. It is obvious that if the ingot yield plus the scrap recovered subtracted from 100 per cent. determines the loss, a drop in yield may increase the loss or the scrap, and both contribute to a monetary loss. To be sure, one can subdivide these unaccounted for losses into various components, such as metallics in slag, free Fe in slag, spillage, etc., and thereby reduce the amount of losses considered as "unaccounted for." If empirical methods could indicate with some degree of accuracy all losses, however slight, the undetermined losses become appreciably smaller and resultant calculations will check actual

Jan 1, 1929

By Frederick Laist, Howard Aldrich

The object of the construction and operation of the 80-ton leaching plant was to test out the leaching of sand tailings on a large scale and, if possible, determine a definite method of operation, and the best construction for the larger unit which is now being built. It was also of importance to obtain some practical data as regards cost items. The 80-ton plant was not expected to be a commercial success. A leaching process on such low-grade material necessitates the treatment of a very large tonnage. Such a cost item as labor, for instance, is entirely out of proportion in such a small plant. The amounts of acid, salt, scrap iron, and fuel for roasting, however, are the same per ton in an 80-ton plant as in a 2,000-ton plant. These costs were definitely established. Also the percentages of extraction and grade of tailings were definitely determined for a large-sized unit. Following will be found the description of the plant, the method of operation and the- results obtained. A general view of the plant is given in Fig. 1. The bins consisted of one coal bin with a capacity of 30 tons, one salt bin with a capacity of 20 tons, and a "mill tailings" or feed bin which held 70 tons. The coal and salt bins were placed with their floor level even with the firing floor of the roasting furnace. The feed bin, to give it greater capacity, discharged about 12 ft. below this point, to a 12-in. conveyor belt, which in turn discharged into a pug mill. This fed another conveyor belt, which discharged into the top hearth of the furnace. The furnace was an ordinary six-hearth MacDougall roaster, 20 ft. in diameter. It was equipped with two fire boxes, on opposite sides, the flames entering on the third hearth. An induced draft was obtained with a Buffalo blower, worked as an exhaust fan. Just above the top hearth was an annular flue around the whole circumference of the furnace. Slots at intervals of about 18 in. led from this flue down into the top hearth. The slots were 2 in. wide by 6 in. long. This annular flue proved rather unsatisfactory, as it tended to fill up with flue dust and choke the dots, thus cutting down the draft. The volume of gas through

Jan 1, 1915

[Cyanidation: Fresnillo, Mexico. 112. 734, 739. Abs.. YB84. 34 gold ore: before or after amalgamation. respective merita. 118, 538 high residue avoided by milling in water, 118, 542 Homestake mill, 112,607. 614 impoverishing gold ore before cyanidation justified. 118, 539 Kirkland Lake district, 112, 648, 649. Abs., YB84.32 literature prior to 1932. See Source Book. McIntyre Porcupine mines, 118, 638 mercury as an aid to extraction of gold, 118, 53 8]

Jan 1, 1936

By L. H. Dushak

DURING the war period of quicksilver activity there were a number of departures from what may be termed the classical quicksilver metallurgy. Attempts were made to beneficiate low-grade ores by gravity concentration and flotation; mechanical furnaces began to replace the Scott furnace and the vertical coarse-ore furnaces, and condensers of sewer tile and redwood tanks were used in place of the older brick and stone condensing chambers. Other developments that have occurred during the current period of quicksilver, activity are mainly in the nature of improvement and further refinement of those started during the war period. Each period of quicksilver activity has been accompanied by the proposal of various new processes, including wet methods for the treatment of quicksilver ores and innovations in furnaces, retorts and condenser equipment. As far as the author knows, nothing of economic significance in the way of "new processes" has been developed. There is in fact no real need for any essentially new process for the treatment of quicksilver ores; the direct furnace treatment is simple and inexpensive. Moreover, with fare exceptions, the quicksilver industry has no complex or refractory ore problems corresponding to those which are receiving more and more attention from metallurgists in other branches of the nonferrous field. Under these conditions improvements in quicksilver metallurgy must be looked for through the adaptation of current developments in engineering and metallurgy generally to the particular needs of quicksilver practice rather than through the invention of new processes.

Jan 1, 1930

By Kenneth P. Katen

INTRODUCTION Though the use of continuous mining machines consolidated the operations of cutting, drilling, blasting, and loading in one machine that would theoretically provide uninterrupted production, it was soon realized that the face haulage and roof support operations remained as major impediments to continuous production. The ability to provide not only continuous cutting and loading, but also continuous haulage and roof support (see Fig. I), was the basis for the introduction of mechanized longwall systems in this country from Europe in 1951. The early systems employed friction props for roof support, but were to become obsolete shortly after introduction of the first hydraulically powered, self-advancing supports in 1960. Since then, use of the longwall technique has grown to the point where it is currently providing more than 5% of the annual output of underground coal mines in the United States. The shortwall system had its origin in Australia, but was first introduced into this country in 1962 following the development of powered roof supports. It, too, provides for continuous cutting, loading, and roof support (see Fig. 2), but has not experienced the widespread popularity of longwall due to its inherent inability to easily provide for continuous haulage. While there are in the neighborhood of 100 longwall systems currently in operation in this country, there are only a handful of short- wall operations providing production of slightly more than 907 184.7 t/a (1,000,000 stpy). Both of these systems provide uninterrupted roof support for face operations by means of hydraulically powered steel roof supports. In each case, the coal removal consists of open-end cuts made from the narrow end of a large rectangular pillar (panel) which has been blocked out by continuous miners developing entries around its perimeter. However, this is the extent of the similarities between the two systems. It is hoped

Jan 1, 1981