By G. M. Ritcey

The concentration of metals in the solution, the .value of the metal being recovered, together with the flow through- put, may singly or in combination conbribute to the decision on the possible use of solvent extraction. Also, as noted earlier, the upstream and downstream aspects of the overall process have to be considered. The economic considerations may be divided into: 1. Capital investments 2. Operating costs Capital Cost The capital costs can be influenced by the following: 1. number of stages; 2. kinetics; 3. coalescence; 4. entrainment; 5. flow rates and ratios; 6. building requirements; 7. ancillary equipment; 8. environment constraints or requirements; 9. engineering design.

Jan 1, 1978

US 4,185,996 -- Removal of arsenic and sulfur Impurities from arsenic-containing cobalt sulfide ore. The ore is oxidized In air at a temperature of 700 to 800°C for 3 to 8 hr to drive off the bulk of the sulfur The oxidized ore 1s heated with a reducing gas at a temperature of 700 to 800°C for 2 to 6 hr to volatilize arsenic, and the final calcine 1s leached with an acid to eliminate substantially all of the remaining arsenic. A.R. Zambrano, assigned to Hanna Mining Co Jan. 29, 1980. 3 pp. (75-2). Filed. 2-13-78 (877,002).

Jan 1, 1982

By J. C. Jr. Vaughan

ALTHOUGH a considerable amount of practical importance attaches to systems involving gases and molten metals, little is known regarding the effects of alloy elements upon the solubility of gases in liquid iron. The solubilities of hydrogen1 and nitrogen2,3 in pure liquid iron are known and it has been shown that small amounts of silicon and aluminum3 exert only a small effect upon the solubility of nitrogen but greatly increase its rate of solution. This paper presents the results of a study of the Solubility Of nitrogen, at pressures approximately one atmosphere, in molten iron containing up to 1.5.5 per cent silicon.

Jan 1, 1939

West Virginia University, Engineering Experiment Station, Morgantown, W Va C E Lawall, Director. For copies of Bulletins or other information address the Director Two classes of the Bulletins published by the Engineering Experiment Station are of particular interest in this directory- Research Bulletins, and Extension Bulletins, or bulletins published for use in extension work They are. Research Bulletin 1, The conservation of natural gas in West Virginia (1918), 2, Acceleration stresses in hoisting ropes (1927), 3, Classification of gas wells for operation (1927), 4, Mining methods in West Virginia (1929), 5, The whiteware industry of West Virginia, Extension Bulletin 1, Electricity in mines, series

Jan 1, 1933

For the year ending February, 1920 PRESIDENT HORACE V. WINCHELL.. . MINNEAPOLIS, MINN. PAST PRESIDENTS PHILIP N. MOORE ST. Louis, Mo. SIDNEY J. JENNINGS NEW YORK, N. Y. FIRST VICE-PRESIDENT A. R. LEDOUX NEW YORK, N. Y. TREASURER GEORGE D. BARRON NEW YORK, N. Y SECRETARY BRADLEY STOUGHTON NEW YORK, N. Y VICE-PRESIDENTS CHARLES W. GOODALE,1 . . . . District 5 BUTTE, MONT. MARK L. REQUA,1 District 6 SAN FRANCISCO, CAL. HENRY S. DRINKER, District 2 So. BETHLEHEM, PA. ROBERT M. RAYMOND,2 . . . . District 0 NEW YORK, N. Y. EDWIN LUDLOW,3 District 2 LANSFORD, PA. A. R. LEDOUX,3 District.0 NEW YORK, N. Y.

Jan 11, 1919

By Walter Kauenhowen

The production of crude oil in Germany during 1933 totaled about 1,669,521 bbl., a slight increase over the 1,608,558 bbl. produced in 1932. This is an extension of a yearly increase which has continued uninterruptedly since 1928. The 1933 increase in production is due chiefly to developments in the Nienhagen field. The production of the Wietze and Oberg fields remained rather stable, while the Oelheim-Eddesse and Volkenroda fields showed decreases. Nienhagen Field.—This field furnished about 61 per cent of the total German oil production in 1933. Most of the drilling activity centered the north district near the village of Nienhagen, where the trend of

Jan 1, 1934

By O. N. Carlson, E. D. Gibson, D. W. Bare

SEVERAL investigators have recently contributed to a clarification of the controversy concerning the allotropy of chromium. Ross and Hume-Rothery1 and Vasyutinskii et a1.2 have reported high-temperature X-ray data on unalloyed chromium from which they have concluded that no allotropic transformation occurs in this metal. Bechtoldt and vacher3 in their investigation of the Cr-Ni alloy system found no evidence for a transformation in chromium and Smart and Haynes4 in critically analyzing the data presented to date concerning this system could find no evidence for a eutectoid reaction in this system. Wyder and Hoch5 in research concurrent with our

Jan 1, 1964

By J. H. Kittel

THE properties of the metal molybdenum have been the subject of recent investigations1,2 = which have included studies of the changes that occur in the metal when it is annealed after having been cold worked. Most of the data which have been reported have pertained to only one aspect of annealing, that is, the conditions under which recrys-tallization has been observecl. The process of recovery which may precede recrystallization docs not appear to have been investigated, and it is the purpose of this note to report observations on the recovery process in cold-worked molybdenum as determined by changes ill the thermoelectric power which occur as the metal is annealed. The measurements were made on commercially pure molybdenum wires which, after annealing at 1035°C in dried hydrogen for 1 hr, were swaged to give a series of reductions up to a maximum of 84.5 pct. The variously cold-worked wires were then annea1c.d in dried hydrogen for periods of 16 hr at progrc:ssively highel. temperatures from 200" to 1000 c with a final annealing treatment of 70 hr at. 1100°C. After each annealing treatment the ther.ma1 emf's were determined against a length of original unwo~,ked material that had received the initial hydrogen anrit,aling treatment. The difference in temperature between the hot and cold junctions was maintained at about 75'C. and. the thermal emf's were measured with a potentiometer that could be read. to 0.01 microvolt. Fig. 1 shows the thermoelectric power. (dE/dT) in microvolts per C between annclalcd and cold-worked molybdenum as a function of the degree of cold work. The effect of annealing is shown in Fig. 2. The general shape of the curves in both figures is similar to results which have been obtained for copper." It was observed that after annealing at temperatures as low as 200°C recovery was well under way. The rapid changes irt thermoelectric power observed near 900 C are probably associated with recrystallization, since such a relation has been observed with copper. Beyond 900°C the thermal emf's changed in polarity. indicating that from this point or1 the specimens were more highly annealed than the standard. Annealing treatments could not be given at temperatures higher than 1100°C due to limitations of the furnace, and it is evident that, since equilibrium values of thermoelectric powers were far from having been attained, temperatures considerably higher are required to fully anneal molybdenum. References Robert M. Parke: Molybdenum, A New High-Temperature Material. Metal Progress (1951) 60, pp. 81-96. * R. A. Long, K. C. Dike, and H. R. Bear: Some Properties of High-Purity Sintered Wrought Molybdenum Metal at Temperatures up to 2400 °F. NACA TN 2319 (March 1951): G. W. Brindley: A Thern-io-Electric Study of the Cold-Rolling and Heat-Treatment of Copper, Report of a Conference on the Strength of Solids. Physical Society, London (1948) pp. 95-106.

Jan 1, 1953

By Pradeep K. Rohatgi, David N. French, Surendar M. Jain, Clyde M. Adams

The effect of solute concentration and diffussivity on dendritic solidification of dilute binary aqueous solutions has been investigated; chlorides of sodium, potassium, lithiurn, and hydrogen were used as solutes. Dendrite spacings were measured in spherical droplets and in unidirectionally solidified specimens. In the droplets, the freezing rate is uniform over the entire specimen and remains constant from the beginning to the end of solidification. In the unidirec-tionally frozen specimens the freezing rate varies within a given volume of liquid during the solidification cycle; in addition, it varies with location uithin the specimen. Mass transport analysis has been used to calculate the supersaturation, AC, supercooling, AT, and transcerse growth velocity, V , of ice dendrites during solidijication from the dendrite spacings measured in the droplels. The ice dendrite spacing in a given solute increases lineary with the solule concentralion at a fixed freezing rate. The ualues of AC, AT, and V increase with an increase in solule concentration. The value of AT in the aqueous solution is of the same order of magnitude as in Al-Cu alloys of the same concentration; the dendrite spacings in Al-Cu alloys also increase with an increase in solute concentralion. For the jamily of aqueozrs solulions incestigaled, the dendrite spacing increases linearly with solute diffusivity at fixed values of concertralion and freezing ,rate. The values of ?C and ?T decrease, whereas the value of V increases with an increase in solule diffusicity. The measured dendrite spacings , L, can be expressed by the relatiun: L = K;(dfa/db) 4 K2C +K3D - K4 where dfs/d? is-change in fraction solid with time (freezing rate), C is solute concentration, D is solute diffusivit K1 = (14 * 4)pmin1'2, K2 = (70 ± 10) pl (moles)- K3 = (24 r 3) . l05 psec (cm)-~. K. = -132 ± 10) 1. FREEZING of solutions is almost always an ehunmix-ing" process because the composition of crystallizing solid generally differs from that of the parent liquid. " Solute concentration and transport are therefore in]portant considerations in solidification of solutions. The influence of these factors on the dendritic solutions produced from metallic solutions is of practical significance since the properties of the solid aggre-gate are often strongly influenced by dendrite spacing.''' Alexander and Fthines3 found that dendrite spac- ings generally increase with solute concentration in several metallic systems. Michael and Bever1 have observed an increase in a aluminum dendrite spacings in dilute A1-Cu alloys. Rohatgi and AdamsJ have reported a linear increase in a aluminum dendrite spacings with increasing copper contents up to 28 pct in A1-Cu alloys. Bolling and Tiller"' have theoretically examined the effects of solute concentration and diffusivity on the growth of cells and dendrites. Their analysis of dendritic growth assumes a steady-state growth and the maximum possible velocity for dendrite propagation. In addition, the quantitative analysis is restricted to dendrites of rotational symmetry and is therefore not directly applicable to the plate-shaped dendrites of ice obtained in the present study. There are practically no experimental observations of the effect of solute diffusivity on dendrite spacings in metallic systems. The reason appears to be the lack of experimental data on solute diffusion coefficients in liquid metallic solutions. The present work is concerned with the effect of solute concentration and diffusivity on dendritic solidification of dilute aqueous solutions: the solutes examined are potassium chloride. sodium chloride, lithium chloride. and hydrogen chloride. There were several reasons for selecting these solutes. The variation of dendrite spacing with freezing rate in these solutiolls is similar to that observed in A1-Cu alloys.8 These aqueous solutions have almost identical phase diagrams at dilute concentrations. Fig. 1. and the diffusion coefficients show very little variation with solute Concentration.9,10 Dendrite spacings were measured as a function of freezing rate. solute concentration. and solute diffusivity. Dendrite spacings were measured in two different types of freezing systems. droplet and unidirectional, respectively. In the droplet freezing system

Jan 1, 1970

By H. R. Gardner

The heat treatmmt of plutonium was studied using the Jominy end-quenching technique commonly used for determining the hardenability of steel. Plutonium specimens were end-guenched from temperatures in each of the ß, y, d, d') and E phases. One series of specimens with a low-iron content, 165 pprn Fe, and another gvoup with a high-iron content, 678 pprn Fe, were used in order to study the effect of a Pu-Pu,Fe eutectic network on the hardness and micro-structure. Hardness traverses indicated no significant variations in hardness with either cooling rate or quench temperature. Metallographic studies indicated major effects on microstructure. Grain size was found to vary markedly with quenching temperature and cooling rate. It was determined that the Pu-PueFe eutectic network could be modified extensively by heat treatment, including spheroi -dization in the y phase and 6 phase below 413°C. An unidentified spheroidal inclusion was observed to go into solution in the delta and higher temperature phases. 1 HE element plutonium is unique among metals in that it has six allotropic forms in the solid state.' These have been designated' as the a, ß, y, d, d', and phases. The respective phase transformations occur at approximate temperatures of 122", 210°, 319°, 450°, and 480°C with a melting point at 640°C. With this number of phase transformations it becomes pertinent to consider the effect of heat treatment and cooling rate in the various phases on the microstructure and hardness of plutonium. To determine; the effect of a wide range of cooling rates, the Jominy end-quenching technique was applied to cylindrical plutonium specimens. In addition, since the presence of iron in amounts greater than 500 pprn is common in plutonium and results in a network of the Pu-Pu6Fe eutectic, it was decided to study heat treatment effects on two bomb reduced plutonium buttons with different iron contents. A low iron button containing 165 ppm Fe and a high iron button containing 678 ppm Fe were selected for this comparison. EXPERIMENTAL PROCEDURE Experimental Material. The cylindrical bars for Jominy quenching were cast from button stock in vacuo in MgO coated graphite molds. Metal pouring temperature was approximately 950°C and the molds were preheated to 300°C. The castings were machined to 0.5 in. diam. by 2.5 in. long cylinders. Chemical analysis and density data for the two groups of Jominy specimens containing different iron contents are presented in Table I. Except for iron, heats 19-12-1 and 20-2-1 are comparable within the limits of analytical accuracy. Representative specimens from the low-iron and high-iron bars were taken for metallographic examination. The low iron specimen was found to have extensive microcracking, Fig. 1. In addition, numerous unidentified spheroidal inclusions were present, Fig. 17. The average grain size of the low-iron plutonium is 0.068 mm, Fig. 4. In the high-iron plutonium, a Pu-Pu6Fe eutectic network is prominent, Fig. 7. The average size of the network is 0.100 mm. Unidentified spheroidal inclusions were also common in the high-iron plutonium. The average grain size of the high-iron plutonium is 0.036 mm. Experimental Technique. A Jominy end-quenching fixture was fabricated for glove box use. A 2.5 in. water height was used with an orifice of 0.250 in. ID. The orifice to specimen distance was maintained at 0.5 in. Annealing temperatures of 160°, 265°, 400°, 465°, and 535°c were chosen for the study of the effect of quenching from ß, y, d, d', and e phases on microstructure and hardness. During quenching, cooling curves were obtained from the Jominy specimens at distances from the quenched end of 1/16, 1/8, 3/8, 3/4, 1-1/4, and 2 in. Cooling rate calculations were made from the cooling curves for temperature intervals of 100° to 110° 160" to 170°, 330" to 340°, 420° to 430°, and 490° to 500°c. These temperature intervals were chosen

Jan 1, 1962

By F. S. Pettit

The oxidation of Ni-3 to 25 wt pd Al alloys has been studied in 0. 1 atm of oxygen at temperatures between 900° and 1300°C. These alloys have been found to oxidize by three different mechanisms which depend on the temperature of- oxidation and the alloy composition. Two of the three mechanisms do not permit a continuous layer of Al,0, to be formed on the alloy surface and the oxidation rates are greater than that for pure nickel. The third mechanism results in the formation of an external A1203 scale and lke oxidation rates are about three orders of magnitude smaller than those for pure nickel. The minimum amount of aluminum required for the formation of external scales of A L,0, has been determined. NICKEL-base alloys are currently the main source of materials for use at elevated temperatures in gas turbine engines. These alloys are usually coated to obtain oxidation resistance. Coatings on nickel-base alloys are frequently formed by reaction of the alloy with aluminum whereby alloyed nickel aluminides are formed. The alloyed nickel aluminides provide protection to the nickel base alloy because external scales of A1203 (alumina) are formed during oxidation and mass transport through A120, is slow in comparison to mass transport through most other oxides. In view of the protective properties of A1203, it is important to know how much aluminum is required in these alloys in order to form external scales of AlzO,. The present paper is concerned with the oxidation kinetics and the oxidation mechanisms of Ni-A1 alloys and the minimum amount of aluminum required in these alloys for the formation of external scales of Alz03. THEORETICAL CONSIDERATIONS When a Ni-A1 alloy is heated in oxygen at elevated temperatures, the following reactions can take place on the surface of the alloy where the oxide phases are assumed to be virtually pure: These oxide phases are in the form of nuclei scattered over the surface of the alloy and, in view of their rapid formation, they need not be in equilibrium with the alloy. As the oxidation process continues, equilibrium between the alloy surface and the oxide phases is approached and the stability of the oxide nuclei is determined by the composition of the alloy at the alloy/oxide interface because of the following reactions: 3NiA1204 + 2A1 (alloy) = 4AlzO3 + 3Ni (alloy) [41 4Ni0 + 2Al (alloy) = NiA120, + 3Ni (alloy) [ 5 1 Application of the mass-action law to Eqs. [4J and [5J yields the following equilibrium conditions for these reactions: where aA1 and aNi are the activities of aluminum and nickel, are the standard free energies of formation of NiO, A1203, and NA1204, respectively, R is the gas constant, and T is the absolute temperature. If the composition of the alloy at the alloy/oxide interface is such that (akl/ahi) is greater than the equilibrium values defined by Eqs. [6] and [7], then Reactions (41 and [5] will go to the right as written. Conversely, if the alloy composition is such that the activity ratio (aLl,/aki) at the alloy/oxide interface is less than the equilibrium values, then Reactions [4] and [5] will proceed to the left. The equilibrium activity ratios in Eqs. [6] and 171 can be calculated since values for the standard free energies of formation of the oxide phases are available. Standard free energies of formation for NiO and A1203 have been tabulated by Elliott and ~leiser.' The standard free energy of formation for NiA1204 can be obtained from the data of Tretjakow and Schmalzried.' The results of these calculations are tabulated in Table I. Table I shows that the following inequality is valid over the temperature interval 900" to 1300°C: (Reaction [5]) (Reaction [4]) « 1and therefore the aluminum activity for these compositions can be taken as equal to the square root of the activity ratios (i.e., aNi = 1). If equilibrium is estab-

Jan 1, 1968

By R. E. Ogilvie, E. T. Peters

The X-ray Kossel-line method has been used preaioz~sly for measuring lattice parameters to accuracies of 1 part in 100,000.5 A second application of this method is described for determining the crystallographic orientation of a randomly positioned single-crysta1 spherical volume that can he as small as 50 µ in diameter, within accuracy limits of ±1/2 deg. The theory, experimental procedure, and interpretation of Kossel-line patterns and an experimenta1 verification of the predicted orientation relationship of the cph k and fee a Cu-Si phases are presented. This orientation relationship can be described as (111)a, (00.1)k; [110]a [11.0]k. In addition, the lattice parameter of the a phase was found to he a. = 3.62154 ± 0.00014Å. The Kossel-line method when used in conjunction with electron microanalysis is shown to he capable of providing a complete chemical and structural analysis of a given crystal. THE most easily accomplished methods for determining the orientation of a single crystal are variations of the Laue X-ray diffraction method. Although certain materials can be oriented to within ± 1 deg accuracy by observation of exterior macroscopic features, such as etch pits, cleavage faces, or growth features, the Laue method is generally preferred for routine laboratory application. Both back-reflection and transmission patterns are coordinated by appropriate reference charts and are plotted in terms of reflection plane poles (normals) on a stereographic projection. Orientation is deduced by relating the pole distribution (which is fixed by the crystallographic symmetry of the specimen) to two specified external reference directions. The Laue method has several limitations. 1) Orientation can rarely be determined to better than ±l deg accuracy. Principal errors involve inaccuracy in specimen-to-film distance, measurement confidence of individual Laue spots, and stereographic plotting. 2) Because of the indeterminacy of the X-ray wave length diffracted to a given spot, it is not possible to determine supplementary crystallographic data, such as interplanar spacings and lattice parameters. 3) The method is generally limited to specimens of cubic symmetry or to specimens of high symmetry and known structure. 4) The relatively large cross-sectional area of the incident X-ray beam generally precludes the measurement of relative grain orientation in a polycrystalline material.* _____ Several of these limitations can be overcome by application of the Kossel-line method, which has been previously employed for precision lattice-parameter determinations.'-= For this method, a point source of divergent monochromatic X-rays is generated within the crystal by means of an incident electron beam. The divergent X-rays which fulfill the Bragg law are diffracted by the specimen and are recorded on a film placed either in transmission or back reflection. Analysis of the film yields a direct measurement of orientation and lattice-spacing values to an accuracy of ±1/2 pct. As analyses can be obtained from spherical specimen volumes as small as 50 µ in diameter, the method provides a means for structural analysis of second-phase or impurity precipitates within a given matrix. The primary limitation of the Kossel-line method is the requirement for an electron microanalyzer or similar apparatus capable of producing a finely focused electron beam. This paper is designed to present the theory, experimental procedure, and geometrical interpretation of Kossel patterns. The experimentally determined orientation relationship between the k and a phases occurring in the Cu-Si system and a precision measurement of the a lattice parameter are presented as a practical application of the method. THEORY OF KOSSEL LINES Divergent X-ray beam photography utilizes an effective point source of characteristic X-rays which, when diffracted from a single crystal, form numerous diffraction and absorption cones that are recorded on film.7 The cones generated from a source lying within the crystal are called Kossel lines.' Although the X-ray scattering from a divergent point source contained within a crystal is described in terms of Laue dynamical theory,9 the directions of the diffracted spectra can be ade-

Jan 1, 1965

By B. C. Allen

Surface free energy and surface self-diffusion of solid molybdenum were studied in the temperature range 1600" to 2400°C using pressure-sintered bi-crystals. Comparison of groove angles formed in various surfaces perpendicular to the grain boundary indicate a maximum of 1 pct variation in surface free energy with crystallographic mientation. This anisotropy tends to decrease with increasing temperature. The surface diffusion of the bicrystals is equivalent to that of sheet with a mild (100) Preferred orientation. Anomalously low values found for bi-crystals with surface orientations of (OOl), (012), and (011) are rationalized in terms of anisotropy in surface free energy. THE effect of crystallographic orientation on surface free energy1,' and surface self-diffusion3,4 has been primarily studied in fcc metals. The object of this work was to study the effect of orientation on surface diffusion and surface free energy of bcc molybdenum using pressure-sintered bicrystals. EXPERIMENTAL WORK Materials and Crystal Preparation. Arc-melted molybdenum rod was obtained commercially and electron beam zone refined at 50 cm per hr at 10- 5 torr to form single crystals about 8 cm long and 0.65 cm diam. Three crystals were prepared with axial orientations about 1 deg from [001.], [011], and. [111]. To reduce the carbon content, the crystals were annealed 2 hr in 1.4 atm flowing wet hydrogen at 2050°C. Then the oxygen content was reduced by annealing for 2 hr in -30°C dewpoint hydrogen at 2020°C. The resulting impurity analysis is given in Table I. Bicrystal Preparation. The single crystal rods were cut into transverse slices with a thin silicon carbide abrasive wheel to produce specimens about 0.6 cm long. They were mounted in epoxy and surrounded by stainless steel washers. Cutting in half was done longitudinally at various angles to known crystallographic planes containing the cylinder axis according to Fig. 1. To reduce surface deformation resulting from the cutoff wheel and thus reduce parasitic grain boundary formation on subsequent annealing, about 0.003 cm was manually ground off each cut surface with 600 grit paper. Care was taken to keep the surface flat. After removal from the mounts, one half was generally ro-tated 180 deg with respect to the other to give a po- tential symmetrical tilt grain boundary between the two halves. In the other cases when low misorienta-tion angles were desired, the crystals were not rotated. On the basis of symmetry, sufficient bicrystals were prepared to cover the entire range of misorientations for symmetrical tilt boundaries. The misorientations, +, ranged from 0 to 45, 0 to 90, and 0 to 60 deg for [001], [011], and [111] bicrystals, respectively. One [Ill] twist bicrystal was prepared from 2 single crystal discs rotated 17 deg relative to each other. Each specimen consisted of two pieces which were placed in a cylindrical tantalum can. Sharp edges were rounded and the fit was made as snug as possible to reduce subsequent deformation during bonding. The assembly and crystals generally were vicuum outgassed at 900" or 1700°C and then electron beam welded in the can at l x 10-4 torr. After being leak checked, the samples were placed in an autoclave and hydrostatically gas-pressure bonded5 in four batches under helium at 10,000 to 18,000 psi at 1650°C for 3 hr. Satisfactory bonds were obtained in many cases, and most of the crystals bonded after two exposures. The results did not appear to be affected by the various pressures used, preannealing conditions, crystal orientation, or time-pressure-temperature route taken to the final bonding condition. After bonding, the tantalum cans were selectively removed in cold concentrated HF. Measurements indicated overall deformation was under 1 pct. The bicrystals were metallographically ground and polished flat and perpendicular to the axis. Examination showed the boundaries were straight and almost free of parasitic grains caused by extraneous local deformation. Annealing. In preparation for thermal grooving, the bicrystals were cleaned and annealed by outgassing at 10-5 torr at 1900°C and heating at 2300°C under 1 atm 99.996 Ar for 0.5 hr. The crystals were held in a closed 4-deck box made of molybdenum sheet, and were heated in a Ta-1OW resistance furnace. The ar-

Jan 1, 1970

By W. A. Tiller

The conventional techniques1 for determining the liquidus and solidus surfaces of an alloy system containing more than two components are extremely tedious to use and do not provide a complete picture of the equilibrium relations between solid and liquid alloys. These techniques are unable to yield "tie-line" information concerning solid and liquid phase equilibrium, a very important parameter in the solidification description of the liquid alloy and a very necessary parameter in the preparation of "zone-levelled" alloy crystals. The tie-line in a polycomponent system is analogous to the partition coefficient, k, in a binary system, it gives the composition of the solid, Cs, in equilibrium with a liquid of composition CL. That is, CS = kCL, where CL = [CO, c1,...Cn] denotes the concentrations of the n + 1 constituents, and k = [ko, kb ,...kon] denotes the gross partition coefficient for the elements between the two phases; thus, k is the tie-line in this system. To provide complete information concerning the two-phase equilibrium in a polycomponent system it is necessary to know both the liquidus surface and the gross partition coefficient. From these two the solidus surface is obtainable. The conventional techniques are unable to provide this information in other than a binary system so we must look elsewhere. In recent years considerable insight has been gained into the correct description of the liquid-solid transformation, 2,3 and controlled solidification experiments may now be designed to both facilitate and enhance equilibrium diagram studies. In the present paper consideration is given to two methods for obtaining the liquidus surface and the tie-lines in polycomponent systems. The methods to be described below deal with the solidification of an n + 1 constituent liquid alloy of initial composition [co, Co ,...Con], where the superscripts refer to the elements present and the Oth element is considered as the solvent in which the n solutes are dissolved. The general assumptions made in the treatment are the following: (i) the solid and the liquid at their interface are in equilibrium during the growth of the solid phase, (ii) there is no diffusion in the solid phase, and (iii) the liquid phase is completely mixed and is therefore homogeneous in concentration. METHOD I In this section a general experimental method will be described which, in principle, is capable of giving an exact description of the liquidus surface and tie-lines. Consider the unidirectional solidification of the liquid alloy specimens L cm in length (freezing either horizontally or vertically). Allow the sample to be frozen very slowly from one end, as indicated in Fig. 1, with complete mixing in the liquid, and then analyze the solid bar to determine its chemical constitution as a function of position, x, along the bar. Let Fig. 2 represent a possible distribution of the ith constituent along the bar. At the point x' the concentration of the ith constituent is C1/5(x'), and the average concentration of the rest of the bar between x' and L is given by C:(X' - L) where [ A(x) c1s(x)dx c1/s(x'-L) = f A(x) dx x * and A(X) is the cross-sectional area at x. In a similar manner. all the Cf(x' - L) may be determined. Thus, the gross artition coefficient k for liquid of composition [Cs(x - L),...Cs(X' - L)] is given by -ko= CUs')/Cos(x' - L)" k0 = csn{x')/cs(x'- L) During the freezing of a charge of length L, the liquid composition may vary over a wide segment of the phase diagram and the gross partition coefficient over this segment of the phase diagram may be determined from one, bar. Fig. 3 illustrates the magnitude of Cs(g)/C,' as a function of the fraction g of the bar which has Solidified.2 We can see that the concentration in the bar will vary over a range of about 15 wt pct for C,' = 10 wt pct and k0 = 0.5. It appears that 4 or 5 specimens would be adequate to study a simple binary eutectic phase diagram.

Jan 1, 1960

By R. W. Armstrong, P. C. Jindal

The hardness dependence on grain size for polycrys-talline cartridge brass and a leaded brass has been measured by Brine11 and Rockwell B testing. In each case, the hardness, H, depends on the average grain diameter, 1, according to: H =Ho + kHl-1/2 where Ho and kH are experimental constants. Diamond pyramid hardness values have also been measured as a function of the indentation size and grain size to give additional information on the nature of the hardness test and the dependence of hardness on micro-structure. The hardness of polycrystalline brass depends on its grain size. Bassett and Davis' demonstrated this as early as 1919 by making Brinell hardness measurements on cartridge brass. Since then, the hardness of this type of material has been measured as a function of grain size by making Rockwell,2'3 Vickers,4 and Brinell5 tests. he hardness dependence on grain size has also been measured for other materials. Angus and summers6 investigated the grain size dependence of the Brinell hardness of polycrystalline copper and a Cu-4.5 pct Sn bronze. In other studies, nickel,? Armco iron,Big an Fe-0.07 pct C alloy,I0 and an 0.39 pct C-12.45 pct Cr stainless steel" have been investigated. In some of the preceding cases, the hardness results have been analyzed to show that the hardness varies with the average grain diameter, 1, according to an l-l\4, l-1/4 or I-2 dependence,11-13 The studies of the influence of grain size on hardness have not been based on any theoretical model. This may be because the hardness of a material is itself a complicated property. However, attempts have been made to correlate, experimentally and theoretically, the hardness of a material with its unidirectional stress-strain behavior.14-l6 On this basis, Hall" proposed that the polycrystal hardness dependence on grain size might follow directly from the Hall-Petch18,19 relation for the grain size dependence of the yield stress. Thus, the hardness-grain size relation was given as: H = Ho + kHl-1/2 [1] where Ho and kH were taken as experimental constants. The relation was applied to the measurements on brass,' copper,6 bronze,= and Armco iron.' More recently, this relation was shown by Armstrong and jindal20 to adequately describe the measurements on cartridge brass made by Bassett and Davis' and Babyak and Rhines.5 In this case, the relationship was taken a step further by independently relating the values of Ho and kH to the values of oyand ky, previously reported by Armstrong, Codd, Douthwaite, and petch21 from measurements of the yield stress dependence on grain size for this type of material. In the present investigation, new Brinell and Rockwell B hardness measurements have been made as a function of grain size for a cartridge brass and a leaded brass. In addition, diamond pyramid hardness values were measured as a function of the indentation size. All these results are applied to a further analysis of the hardness dependence on grain size. MATERIALS AND EXPERIMENTAL METHODS Cartridge brass and a leaded brass were selected for this investigation for two main reasons: it was anticipated 1) that these materials could be cold-worked and recrystallized to a wide range in grain size and 2) that the results to be obtained on these typical industrial materials could be usefully compared with previous investigations. The chemical analyses of the actual materials which were employed are given in Table I. The as-received 1/2- and 3/4-in.-thick plates were given various reductions in thickness by cold rolling. The rolled material was heat-treated at various temperatures between 330" and 850°C for differing time periods from 5 min to 9 hr to achieve a variation in the average grain diameter between 0.0339 and 0.000543 cm.22 During heat treatment, the brass was protected from zinc loss by packing it in chips or foils of the same composition material. Reasonably equi-axed grain structures were obtained in each case. The metallurgical grain sizes of the specimens were determined from measurements of the average linear intercept on a random line. Annealing twin interfaces were not counted along with grain boundaries. The

Jan 1, 1970

By K. E. Beu

IN the measurement of retained austenite concentrations in steels using the integrated intensity method,1 Averbach has pointed out" that the absorption factor A(0) for a flat sample making a glancing angle 4 with the incident X-ray beam can be combined with his constant factor R to obtain our constant factor" G provided that "1—There is no preferred orientation in the sample, and 2—The geometric requirements [for the sample, film, and X-ray beam] have been met precisely."' If A(0) can be combined with R to give G according to the equation G = R . A(0) [14] then the possibility for making non-compensating errors in the austenite determination has been eliminated. This has been described previously in a technical note." Because of the brevity of the previous note,3 it was impossible to emphasize the fact that the two conditions on preferred orientation and geometry can be easily met experimentally, contrary to Aver-bach's statement that: ". . . the necessary conditions must be tested experimentally for each determination, and this is done most easily by observing whether the apparent absorption has the form of Eq. 2 [the theoretical equation for A(0)]."" he way in which these two conditions can be met experimentally will be discussed briefly to help clear up this point. In addition to these two conditions, other factors such as sample shape, homogeneity, and grain size which also affect A will be included in this discussion. A (0) depends on sample shape. The theoretical function for A was derived originally for a flat surface.' In general we have found that a flat sample surface is readily obtainable." If such a surface can * The effect of surfaces which are not flat on the measurement of retained austenite will be discussed later. be obtained, it has the following advantages: 1—it is easily reproducible from sample to sample, 2—it is the form required for metallurgical examination —this type of examination being frequently desirable for this work, and 3—it is an efficient shape for diffraction purposes. Perhaps the most important of these features is that a flat sample surface is easily reproducible; hence, this requirement on the repro-ducibility of A from sample to sample is met for all such samples. Fig. 1—Schematic diagram of the quartz crystal monochromator diffraction unit. The centerline of the main beam is at 6' to the target face. The tangent to the crystal face is at 16.8' to the moin beam. The centerline of the monochromatic beam is at 33.6 to the main beam. The sample surface can be rotated in its own plane. The angle of the sample surface and the monochromatic beam can be adjusted by rotating about the vertical axis, The film holder can also be rotated about B so that the film can be exposed over the desired angular range. For Fe K, X = 1.932A. 1011 planes of quartz have d = 3.35A. A(0) depends on homogeneity and grain size. If the sample is badly segregated or the grain size is large, the effect of micro-absorption and primary extinction1. ' must be considered. It has been shown, however, that for most plain carbon or low alloy hardened steels, neither micro-absorption nor primary extinction effects are present.' A (0) depends on camera geometry. For a given angle 0, A remains theoretically constant from a geometrical viewpoint only if the following factors are kept constant: 1—the angle of inclination .+ of the sample to the X-ray beam, and 2—the centering of the sample with respect to the film cylinder. These are mechanical problems which can be solved readily if the facilities of a good machine shop are available. The arrangement used to insure that the angle 4 remains constant and the centering of the sample is reproducible is indicated schematically in Fig. 1. The sample is clamped against a thin plate with a hole in it by means of a spring-loaded pres-

Jan 1, 1954

By N. J. Grant, R. Nordheim

An extensive study was made of the aging characteristics of alloys based on the 80 pct Ni-20 pct Cr composition hardened with aluminum and/or titanium, each up to 4 pct. Aging was followed by means of hardness and hot electrical resistance measurements as well as by X-ray and microscopy. Stress rupture tests at 1500°F were utilized as a check on the predicted behavior. THE titanium and aluminum hardened Ni-Cr alloys, exemplified by Nimonic 80 and Inconel X, constitute one of the more important groups of alloys developed to meet the demand for materials retaining their strength at elevated temperatures. For service in the temperature range 1200" to 1500°F, these alloys offer high creep resistance. With increasing service temperature, however, the strength of the simpler Ni-Cr base alloys falls off rapidly so that above 1500°F there is a significant loss of strength. The present investigation was undertaken with the hope that a better understanding of the factors controlling the precipitation hardening of these alloys would make it possible to increase the useful service temperature range. Primarily this investigation involved the study of the effects of titanium and aluminum on the hardening and the subsequent softening at elevated temperatures. The titanium and aluminum contents were each varied between 0 and 4 pct by weight at a constant nickel to chromium weight ratio of about 4:1. (Except when otherwise stated, all compositions are expressed on a weight basis.) The major part of the investigation was confined to alloys with less than 0.06 pct C. Recently several papers dealing with the identity of the microconstituents in the titanium and aluminum hardened Ni-Cr alloys have been published. Using X-ray analysis of the residues from anodic dissolution, Rosenbauml was only able to identify carbides and nitrides in Nimonic 80 and Inconel X. However, since Rosenbaum worked with alloys in the hot rolled rather than in the aged condition, his results are inconclusive. Recently Hignett' reported that the hardening of Nimonic 80 was due to the controlled precipitation of Ni,(TiAl) having the cubic Ni3A1 structure. Taylor and Floydv-" published the results of an investigation of the nickel-rich corner of the Ni-Cr-Ti, Ni-Cr-Al, and Ni-Ti-A1 systems. In the Ni-Ti and the Ni-A1 systems the hexagonal Ni,Ti phase, 7, and the cubic Ni3A1 phase, -y', respectively, exist in equilibrium with the nickel-rich solid solution. The interatomic distances in the basal plane of Ni,Ti and the octahedral planes of the matrix are almost equal, thus explaining the Wid-manstaetten type structure formed when Ni,Ti precipitates from solid solution. When Ni:,Al precipitates from solid solution, it appears usually in globular form, often dispersed along rows corresponding to definite crystallographic directions. The 7 and phases are also the only intermetallic compounds which occur in the nickel ternary alloys with up to 25 pct Cr and 10 pct Ti or Al. Taylor and Floyd found that Ni,Ti takes practically no nickel, chromium, or aluminum into solution. Nial, on the other hand, dissolves a considerable amount of chromium and titanium and some nickel. Up to three out of every five aluminum atoms could be replaced by titanium in Ni,Al. This substitution caused a slight increase (less than 1 pct) in the lattice parameter. With respect to the effect of variation in the titanium and aluminum contents on the high temperature strength of Nimonic 80 type alloys, Pfeil, Allen, and Conway" reported that an 80 pct Ni-20 pct Cr alloy containing 0.20 to 0.30 pct A1 had the highest creep resistance when the titanium content was kept between 1.65 and 2.75 pct. Experimental Procedure The materials used for this investigation were electrolytic nickel, electrolytic or low carbon chromium, sponge titanium and 2s aluminum. The alloys were melted in an indirect carbon arc furnace under

Jan 1, 1955

By Luckie. Peter T., Deurbouck. A. W., Harold L. Lovell, E. R. Palowitch, James K. Kindig

PART 1: DENSE MEDIUM SEPARATION by E. R. PALOWITCH and A. W. DEURBROUK INTRODUCTION During 1974, 43.9% of the 603,406,000 tons (549,099,000 mt) of bituminous coal and lignite produced was cleaned mechanically, of which 82,280,000 tons (74,875,000 mt) was cleaned by dense medium processes.l The percentage of bituminous coal and lignite cleaned mechanically by dense medium processes increased from 7 to 31 % between 1938 and 1974. Dense medium separations include those coal preparation processes which clean raw coal by immersing it in a fluid having a density inter- mediate between clean coal and reject. As there is a general correlation between ash content and specific gravity, it is possible to achieve the required degree of removal of ash-forming impurities from a raw coal by regulating the specific gravity of the separating fluid. Dense medium processes offer the following advantages over other coal cleaning processes: 1) Ability to make sharp separations at any specific gravity within the range normally required even in the presence of high percentages of the feed in the range of 2 0.1 sp gr units. 2) Ability to maintain a separating gravity that can be controlled with ± 0.005 sp gr units.

Jan 1, 1979

By C. A. Heiland

THE investigations described were made on a portion of Clear Creek basin near Golden, Colo. (A portion of the area under survey is shown in Fig. 1. The photograph was taken in the vicinity of station No. 2 of Line II.) Three principal purposes were in the minds of the investigators: 1. To repeat with modern, more sensitive and more reliable instruments magnetometric placer investigations previously made. 2. To disprove the recently advanced theory that deposits of the glacial period have no pronounced magnetic effects. 3. To develop in detail the theory of the magnetic effects produced by placer deposits. Six years ago, the first magnetic observations were published, which proved that it is possible to locate gold-bearing channels with relatively crude instruments.1 Two years ago, K. C. Laylander published results obtained with similar instruments.2 The measurements of the latter were discussed by the senior author of this paper.3 At that time, however, the material available for such a discussion was somewhat scarce and not made with the most modern magnetic instruments, although very brilliant results were obtained. Therefore, the senior author felt that magnetic investigations should be made on very clear geologic conditions with the most modern instruments.

Jan 1, 1928

By F. W. Bremmer

THE drilling of constantly deeper oil wells has made it imperative that the manufacturer of casing be ever searching for new methods and new materials to meet the increased demands. One phase of this search constitutes the subject matter of the present paper. Starting from the original Drake well in 1859, the depth of wells has advanced by leaps and bounds, until today depths of 6000 to 8000 ft. are common. Conditions point to the necessity for drilling to greater depths, and it is not at all improbable that much of the future oil produc- FIG. 1.-TREND IN DEPTH OF OIL WELLS. tion will be from, wells around 10,000 ft. deep. The trend to deeper wells is nicely illustrated by the curve in Fig. 1.1 The points plotted are the maximum depths attained in the various pools which were at their peak for the years given. It may be of some interest to observe the change that has taken place in the tensile and collapsing stresses over the last 25 years. The pressure at the bottom of a 900-ft. hole, equivalent to the pressure caused by an equal column of water, is only 450 lb. per sq. in. The equivalent

Jan 1, 1930