By Dmitri Goljandin, Jaan Kers, Xiangjun Zuo, Lifeng Zhang, Priidu Peetsalu

"In this paper, the mechanical milling of the electronic wastes was carried out. The metal parts and plastic parts were roughly separated. The final plastic powder size could be as small as ~100 µm. Then the pyrometallurgical recycling Printed Circuit Boards (PCB) was executed. The mechanisms of thermal degradation and combustion are investigated using TG/DTA and MS. Some chemical powders, such as Na2CO3, NaHCO3, NaOH and CaCO3 are used to control the exhausted toxic gas such as Br2. Introduction Waste electric and electronic equipment (WEEE), or electronic wastes (E-wastes), has been taken into consideration not only by the government but also by the public due to their hazardous material components [1-3]. From the point of material composition, electronic wastes can be defined as a mixture of various metals, particularly copper, aluminum, and steel, attached to, covered with, or mixed with various types of plastics and ceramics [4]. Precious metals have a wide application in the manufacture of electronic appliances, serving as contact materials due to their high chemical stability and their good conducting properties. Platinum group metals are used among other things in switching contacts (relays, switches) or as sensors to ascertain the electrical measurand as a function of the temperature [5]. Table 1 [6] gives examples of the metal composition of different electronic scraps from literatures. Additionally, non-ferrous metals and precious metals content have gradually decreased in concentration in scraps. The value distributions for different electronic scrap samples are shown in Table 2 [6], where the metal price data are from London Metal Exchange (LME) (Octoebr 2007). It can be seen that for cell phones, calculators, and printed circuit board scraps, the precious metals make up more than 70% of the value, for TV boards and the DVD player they still contribute to about 40%. This indicates that the major economic driver for recycling of electronic waste in industry is from the recovery of precious metals. Behind the precious metals come copper and zinc, while Al, Pb, and Fe are less value. Recycling of electronic waste is an important subject not only from the point of waste treatment but also from the recovery aspect of valuable materials."

Jan 1, 2008

By Anurag Tripathi, J. K. Saha, S. K. Ajmani, J. B. Singh

"The quality of steel is a major concern in the metallurgical industry. The control of liquid steel temperature can enhance the level of cleanliness in steel. Ladle is one of the major vessels used to transfer liquid steel between different stations. The heat transfer phenomenon taking place in this vessel needs to be monitored for controlling the liquid steel temperature. A CFD model was developed for prediction of liquid steel temperature during complete process cycle of ladles in direct heats. The model was validated with liquid steel temperature measured at on-line purging station and tundish during teeming from one of the actual steel plant. The accuracy of model was 96 %. The results obtained show insignificant effect of slag thickness, tapping temperature and ladle life on liquid steel temperature in the ladle. However, the importance of initial refractory temperature was noticed. The CFD model developed in present work can generate the thermal history of liquid steel and refractory walls of any ladle at any stage.1. IntroductionThe control of liquid steel temperature is desired to achieve required steel quality. The low casting temperature is detrimental and may result in nozzle blockages due to premature solidification in the tundish. The phenomenon of heat losses taking place in ladles needs to be understood for prediction of liquid steel temperature. The assessment of thermal profile of liquid steel from BOF converter to caster can be done through consideration of heat losses at all points. Hlinka and Miller [1] showed that the ladle pouring temperature varies due to heat losses from molten steel into surrounding refractory layers. The phenomenon of thermal stratification was numerically simulated by Ilegbusi and Szekeley [2]. The effects of slag cover on heat loss and liquid steel flow in ladle before and during teeming to a continuous casting tundish was numerically simulated by Chakraborty and Sahai [3]. Investigators also developed some simple models to predict the steel temperature for some of the processes taking place in ladles [4-9].The present work is an effort to generate the full information about the temperature drop taking place in any ladle throughout its process cycle. This information can be used to predict liquid steel temperature and to take decisions to minimize heat losses."

Jan 1, 2012

By Wayne Bell, Xiaodi Huang, Matthew Andriese, Jiann-Yang Hwang, Zhiwei Peng

"The equations for determining microwave field attenuation length and half-power depth in magnetic materials were derived from Maxwell’s equations. The microwave field attenuation length and the half-power depth for a magnetite concentrate were calculated and the temperature dependence of them was determined. It is demonstrated the microwave field attenuation length and the half-power depth highly depend on temperature and decrease with increasing temperature up to 900 °C. The variations of field attenuation length and the half-power depth with temperature indicate the microwave power attenuates much faster than the field strength in materials. The evaluations of field attenuation length and microwave half-power depth can be used to characterize the microwave dissipation behaviors in the sample and optimize the dimensions of the material in microwave heating.IntroductionMicrowave has been applied in materials processing for its distinguished advantages including rapid heat transfer, volumetric and selective heating [1,2]. However, most research work involving microwave heating are confined to non-magnetic materials (e.g. ceramics), with limited attention paid to the heating of mixed property materials (e.g. magnetite and other ferrites) under microwave irradiation [3-5]. Since many magnetic materials exhibit good and even better microwave absorption capability than non-magnetic counterparts, it is quite necessary and deserved to take advantage of this property and then improve the heating efficiency. To achieve this aim, further understanding on the microwave heating mechanism, especially the microwave propagation/dissipation behaviors in magnetic materials is required.The dissipation behavior of microwave in materials has been identified as one of the key factors that affect the efficiency of heating under microwave irradiation and this behavior can be characterized by several parameters. Apart from traditional penetration depth (TEM power penetration depth, Dp = 1/(2*a), where a is the TEM field attenuation factor), two other parameters, field attenuation length (Df) and half-power depth (Dh), are also applied to indicate the microwave dissipation in materials [6].The accurate determination of such parameters can help in optimizing the dimensions of the load in a microwave furnace, producing more uniform heating under microwave irradiation and avoiding thermal runaway."

Jan 1, 2011

By Tadafumi Adschiri

"Supercritical water can provide an unique reaction atmosphere for synthesizing metal oxide nanoparticles. Due to the drastic change of properties of water around the critical point, including density, dielectric constant and ionic product, the reaction phase with O 2 or H2 gas and the reaction rate and equilibrium can be varied to synthesize new materials or define particle morphologies. In this work, hydrothermal crystallization experiments are performed with several types of flow apparatus that allow convenient manipulation of variables such as temperature, pressure, and residence time. Key features in the flow modes and material preparation are discussed. The proposed supercritical hydrothermal synthesis method has the following desirable features: i) nanoparticles can be produced, ii) morphology of the produced particles can be controlled with small changes in pressure or temperature, and iii) a reducing or oxidizing atmosphere can be applied by introducing oxygen or hydrogen or other gases. An overview of this method is given for functional material synthesis of significant industrial interest including barium hexaferrite magnetic particles, YAO/Tb phosphor fine particles and lithium cobalt fine crystals.IntroductionHydrothermal crystallization, a method of metal oxide formation from metal salt solutions, is typically used at temperatures ranging from 373 K to 473 K. We are developing a new process for hydrothermal crystallizations that uses temperatures in the range of 673 K to 723 K, which is just above the critical temperature of water1 • 8 • In this work, we refer to this process as supercritical hydrothermal synthesis. The supercritical state of water allows one to vary reaction rate and reaction equilibrium by shifting the dielectric constant and solvent density with pressure and temperature. From of our research on material production in supercritical water, we have identified the following specific features of the supercritical hydrothermal synthesis method: (i) ultrafine particles can be produced, (ii) morphology of the produced particles can be controlled to some extent with pressure and/or temperature, and (iii) a homogeneous reducing or oxidizing atmospheres can be provided by introducing gases, such as O 2, H2, H2O 2• and so on.1"

Jan 1, 2000

By M. Rockandel

"Universal Dynamics Ltd. of Vancouver, Canada has developed, patented and commercialized the ""REMERC"" process for the treatment of mercury contaminated sludges and soils. Mercury is extracted into an acidified and oxidizing, sodium chloride brine solution. REMERC was initially developed to treat mercury contaminated EPA listed wastes (K106) generated by the chlor-alkali industry. More recent work has expanded the capability;' of REMERC to include remediation of mercury contaminated sites, equipment and building materials.In the process mercury is currently recovered from solution by cementation on iron powder in an agitated reactor. The process recovers high purity elemental mercury (99.9% purity). Cementation typically recovers about 90-95% of the mercury in 30 minutes. Higher recovery is not necessary because of the recirculation of the leach solution. When treating highly contaminated chloralkali wastes (5-13% mercury content), REMERC will reduce the mercury laden solutions from 400-1,000 mg/L mercury to 50-100 mg/L. In the treatment of less concentrated wastes «1,000 mg/kg mercury) such as those encountered in site remediation, the treated solutions will generally contain 10-20 mg/L mercury. Cementation while being simple and able to achieve the required recovery has the. undesirable properties of; requiring a solid-liquid separation and adding iron to solution which must be precipitated, ultimately increasing the weight of residue to landfill. .The potential advantages of electrolysis were recognized early in the development of REMERC. Mercury electrolysis is well known in gold and chloralkali processing. Initial testwork utilized a liquid mercury cathode and a coated titanium anode both common to chloralkali producers. The mercury cathode appeared susceptible to polarization and solution impurities significantly affected performance. Agitation of the mercury pool improved performance but it was still not possible to achieve the reduction objectives. Current efficiencies were low, near 10%, and it was apparent that a relatively large cathode pool would be required to limit the current density. A number of electrode combinations with and without a membrane were then tested in a vertical electrode' configuration but the desired performance was not obtained."

Jan 1, 1997

By R. Winand, M. Degrez, C. Temmerman

"The influence of the copper electro crystallization inhibitors (mainly thiourea, gelatin and chloride ions) is studied in a new fully automatic pilot plan. This paper describes the conception and the building of this plan. The new approach is to reproduce the experimental conditions observed in the industry with the three additives present simultaneously in the electrolyte and secondly to study the influence of a slight modification of the concentration of one inhibitor, the others being present in the electrolyte with their industrial nominalconcentrations.1. INTRODUCTIONDespite the fact that gelatine, thiourea and chloride ions have been used in copper electrorefining for a long time, precise knowledge concerning their influence on the cathode deposit, metallographic structure and associated properties is still lacking.Many authors studied the influence of each additive separately, or of two added at a time. Only a few authors studied the combined influence of the three additives added simultaneously. The general conclusion that can be drawn is that the combined influence is far from that forseen from the influence of each additive separately, or even from two additives used at a time. Moreover most of the experiments described in the literature were performed by adding all additives at once initially. It is however, well known that gelatine looses a great part of its activity during the first half hour due to degradation by sulfuric acid (as shown by the cathode overpotential drop). Thiourea is rapidly replaced by a number of degradation mole,cules and complex ions including cations from the solution, changing even the equilibrium between Cu, Cu(I) and Cu(II).Chloride ions are consumed by precipitation.A number of successive research projects [1-9] led pregressively to the concept that, in order to obtain reproducible results representative of industrial cathodes, it was necessary to simulate as far as possible industrial conditions. It was essential that all additives were added continuously during the electrolysis, with, as consequence, a continuous bleed.The purpose of this paper is to describe the concept of a new fully automatic pilot plan for copper electrorefining and to present the first results."

Jan 1, 1997

By Michal Rehor, Vladimir Cablik, Peter Fecko, Tomas Lang

"1. Introduction The North-Bohemian Basin area is known for its largest Czech brown coal deposit. About 50% brown coal reserves have been exploited in the North-Bohemian Basin by the mining company of Severoceske doly, a.s. (North Bohemian Mines, j.s.c.) today. The opencast mining of brown coal naturally led to vast landscape damages. Therefore reclamation work has acquired great significance. The specific feature of Severoceske doly, a.s. mining is the fact that the mining has been realized in two geologically absolutely different localities. This fact demands even rather different methods of reclamations. The main problem at Doly Bilina localities is the occurrence of overburden rocks from the series of rocks of coal seams. These rocks are texturally light but large amounts of coal (cca 5 %) and sulphur (cca below 3 %) which makes the soil reaction extremely acid. If they appear on the surface of the dump, they create a phytotoxic area, reclamation of which requires special methods. Rocks from Doly Nastup Tusimice localities are more suitable to reclamation use, but texturally extremely heavy rocks with large fraction of physical clays appear there that can generate a sterile soil area. Their reclamation requirements are completely different from those on Doly Bilina phytotoxic areas. That is the reason of the application of some non – traditional restoration methods. This report briefly summarises the experience in application of fertilizable soils, power plant stabilizer, power plant ash and aerial sowing of charlock. The results are documented by the monitoring of the physical, mineralogical and pedological parameters of rocks in testing areas.2. Properties of Overburden Rocks in Opencast Mines Bilina and Libous The reclamation work methodology in the North Bohemian Basin is above all determined by the properties of overburden rocks which occur in the top horizon of the reclaimed sites. The research of the rocks reclamation properties dealt with four current mining localities in the central part of the basin. It concerned the Bilina and Libous mines. This chapter states the stratigraphic status properties of these sites with respect to reclamation availability. The total status of the area of interest is shown in the figure No. 1."

Jan 1, 2008

By Vladimir Lobanov, Pritchinm Alexander, Nikifor Ageev

"Sulfuric anhydride is one of the most voluminous technological emissions. The possibility of high-temperature SO2 oxidations without catalyst in presence of calcium-bearing filling materials (CaO, Ca(OH)2 and CaCO3) with obtaining of binding material on the basis of waterless calcium sulfate is studied. Due to application package HSC-4 the thermodynamic analysis of the specified interactions is made and following conclusions are drawn: 1) Reactions are feasible in the all range of investigated temperatures (400 – 1000 °?); 2) The best results should be expected at use of ???; 3) The heat of reaction does possible autogenous behavior of process. The researches have shown: 1) Practical possibility of the process; 2) SO2 oxidation without the catalyst is feasible in presence of ???, Ca(OH)2 and CaCO3; 3) The optimum temperature range is 600-800 °?; 4) The content of waterless calcium sulfate in a product reaches 48% that makes it possible to use as the binding material; 5) At excess of ??? the degree of SO2 collection is nearer to 100%. Introduction At processing of sulfide raw materials in metallurgical furnaces the significant amount of sulfur, mainly in the form of sulfuric anhydride is escaped. Rich gases (SO2>3 %) are used for the sulfuric acid or element sulfur production. Chemism of sulfuric acid manufacturing is based on catalytic high-temperature oxidation of anhydride. Poor gases of metal works (SO2 =2,5 %) and power combustion units (SO2 =0,5 %) after clearing discharge into the atmosphere. Commonly, to recovery of weak sulfuric anhydride the chemical and physicochemical methods are applied. A few chemical ways of recycling sulfur dioxide are applied practically. In a number of methods for SO2 recovery a pulp of metals oxides (magnesium, zinc, etc.) with formation of sulfites is used. In other case sulfuric anhydride is catch by weak sulfuric acid in the presence of an oxidizer (pyrolusite ore). Methods of absorption SO2 by solid sorbents, (carbon fibers, silica gels, zeolites) are known and put into practice. Regeneration of the saturated sorbents is realized by thermal decomposition or extraction. Obtained as a result high-concentrated solutions are a commercial product."

Jan 1, 2008

By Arvind Thekdi, Cynthia Belt2

"Waste heat from industrial operations in metals industry represents 20% to 50% of the total energy used in most manufacturing plants. Reduction and recovery of waste heat offers the most attractive and cost effective method of reducing energy intensity for an industrial plant to meet corporate energy saving goals. It is possible to reduce or recover 30% to 60% of the available waste heat by using conventional and readily available technologies. Projects to reduce or recovery waste heat may offer less than 3 years payback to as short as a few months. This paper presents information on most commonly used methods for waste heat reduction and recovery in the metals industry operations. It describes the methods and use of analysis tools that would allow a user to estimate energy savings, CO2 or GHG reduction potential, and economic benefit and includes appropriate case histories.Waste Heat SourcesSources of waste heat abound with the metals industry. While the overall quantity of energy is high, the sources are distributed throughout a plant. The largest source within the metals industry is within furnace exhaust / flue gases. This includes the high temperature gases from burners in process heating such melting, calcining, and sintering operations. It also includes lower temperature gases from heat treat, dryers, and heaters. Lower temperatures are also found after post processed hot gases. This could include heat left after heat exchangers, regenerative systems, thermal oxidizers, and emission control systems. Other hot gases include air used in direct and indirect cooling.While waste heat in form of exhaust gases is readily recognized, waste heat can also be found within liquids and solids. Waste heat within liquids includes things such as cooling water, heated wash water, and blow down water. Solids can be hot product at discharge after processing or reactions are complete. Indeed, not only is energy wasted in the hot metal that slowly air-cools, but additional energy may be used in providing air or water-cooling to increase the speed of cooling. Other waste heat sources are not as apparent and include things like hot surfaces, steam leaks, boiler blow down water, etc. Table 1 and Figure 1 show several major sources along with the temperature range and characteristics of the source."

Jan 1, 2011

By Xiping Chen, Wangxing Li, Jiemi Zhou

"Desulfurization methods suitable for anode-grade petroleum coke (coke for short) used in primary aluminum industry are coke desulfurization during calcination, desulfurization in soakage and desulfurization in mediums. Coke desulfurization during calcination is discussed in this paper. Influences of calcination temperature, holding time and coke granularity on coke desulfurization were discussed. Experimental results show that calcination temperature has a remarkable influence on coke desulfurization. When the temperature is high enough desulfurization ratio of coke can reach 85% only by calcination. Holding time has a definite influence on coke desulfurization, but desulfurization ratio is low at the temperature of 900~1300°C. The influence of holding time is obvious when calcination temperature surpasses 1400°C. The influence of coke granularity is smaller compared with calcination temperature and holding time.IntroductionPetroleum coke is main raw material for carbon anode in primary aluminum industry, and its weight percentage in carbon anode is about seven percent. Green coke can not be directly used for anode production because of its immanent moisture and volatiles. Green coke must be calcined in order to meet the request of anode production. Calcination is a heat-treatment process during which green coke is heated to a given temperature to remove volatiles, moisture and some sulfur. Real density, strength, electrical conductivity and anti-oxidation ability of petroleum coke can be improved by calcination and calcined coke can be received [1, 3, 4]. Sulfur in calcined coke finally goes into carbon anode. During baking or aluminum smelting, the sulfur in anode ultimately changes into SO2 and emits from anode into the atmosphere. Excess SO2 easily leads to acid rain which brings heavy pollution to the environment [1, 2]. With the development of Chinese aluminum industry, consumption of anode-grade petroleum coke increases year by year, the total consumption in 2007 surpassed 4.5 million tones and the yearly emission of SO2 from aluminum smelters has exceeded 270 kilotones. From 2005 Chinese government began to limit the emission of SO2 from primary aluminum industry, so desulfurization of anode-grade petroleum coke becomes more and more urgent. Some relationship need to be found and used to guide desulfurization of petroleum coke."

Jan 1, 2008

By Magdelinka Padenkova-Yaneva, Emilia Christova Kostakeva

"One of the methods for waste treatment is composting during which as a result of controlled biological decomposition of organic waste in aerobic conditions harmless materials are received. Composting takes place in suitably designed premises which ensure the optimal conditions for biochemical decomposition of the waste. A usual way to process composting is the spreading of the waste on a base made from reinforced concrete.In the paper the phases and basic technical features of the process of composting, the requirements and properties of the base and the ways of protection of concrete base against corrosion are revealed. Technical decisions for a specific construction site in Bulgaria are shown and the advantage of achieving durability of the concrete constructions in the plant while achieving simultaneous environment protection from pollution is discussed.IntroductionComposting is the process of controlled biochemical decomposition of vegetable and animal organic waste in aerobic conditions as a result of which harmless materials are obtained. The latter have better stability and are rich in humus substances which are useful for agricultural crops and can be used for restoring the soil fertility [1, 2, 3, 4].In modern waste treatment plants a composting technology is adopted in which the waste is spread on a concrete base as piles with certain dimensions [1, 3]. These piles are periodically stirred or air is blown through them in order to ensure the quantity of oxygen required for the process of aerobic decomposition of the organic matter. The fluids and gases formed in the course of the composting are take away in order not to pollute the environment – air, water, and soils. For this purpose the base on which the waste is spread must satisfy certain requirements, and the gases must be taken away and rendered harmless in order to protect the atmospheric air from pollution. This paper discusses the need for protecting the concrete base from corrosion and characterizes the stages and main parameters of the composting process and the possibilities for primary and secondary protection of the concrete base from corrosion. Specific technical decisions applied in a composting facility in the area of the town of Plovdiv are presented."

Jan 1, 2008

By Rzyman Michal, Nakamura Takashi, Shibata Etsuro, Grabda Mariusz, Oleszek-Kudlak Sylwia

"Tetrabromobisphenol A (TBBPA) and many systems based on the synergistic effect of brominated organic compounds with Sb2O3 are extensively used as effective brominated flame retardants (BFRs) in many materials such as plastics and textiles. Thermal degradation of BFR containing plastics leads to the formation of hydrocarbons and gaseous compounds such as HBr and SbBr3. Our thermodynamic considerations indicate that these gases can act as bromination agents for metallic oxides such as ZnO, Cu2O, CuO, PbO and FeO. Moreover, these metallic oxides have the thermodynamic tendency to brominate easier than does Sb2O3. The aim of this study was to investigate experimentally the reactivity of ZnO with 1) HBr originating from the thermal decomposition of TBBPA and 2) SbBr3, which is formed during thermal degradation of brominated flame retardant plastics. The thermal treatments of the mixture of compounds of interest were investigated by thermogravimetry coupled with mass spectrometry.IntroductionTetrabromobisphenol A (TBBPA) and many systems based on the synergistic effect of brominated organic compounds with Sb2O3 are extensively used as effective brominated flame retardants (BFRs) in materials such as plastics and textiles. For instance, 4.5 million tons of flame retardant plastics containing BFRs are produced in Japan each year. Thus, in thermal treatments such as the incineration and melting of solid wastes, BFR containing plastics are intentionally or unintentionally included in the wastes. Thermal degradation of BFR-containing plastics leads to the formation of hydrocarbons and gaseous compounds such as HBr and SbBr3 [1-5]. Our thermodynamic considerations [6] indicate that heavy metal oxides such as ZnO, Cu2O, CuO, PbO and FeO should easily react with HBr prior to Sb2O3 and also with SbBr3, the main gaseous product in the thermal decomposition of TBBPA, forming low boiling point metallic bromides suitable for the volatile separation of heavy metals. The metal oxides are also expected to qualitatively and quantitatively affect debromination and decomposition of the flame retardant."

Jan 1, 2008

By Kenji Monden

"In order to obtain basic data for the development of highly thermally conductive composite materials, the thermal conductivity of a resin composite material with an Aluminum Nitride filler was assessed. Several different measurement techniques such as the xenon flash and the temperature wave thermometric analysis method were employed to gather data on these composites. An excellent match between theoretical and experimental data was achieved by employing a predictive expression that takes into account the effect of percolation on thermal conductivity.IntroductionA thermal solution composite is made by incorporating dense inorganic fillers with high thermal conductivity into a resin. Because the composite materials have high thermal conductivities, they have been used in electrical products that generate excessive thermal energy during operation, such as inverters, amplifiers and motor drivers. They function as electrically insulating and thermally conducting parts of the electric modules. As the uses of thermal solutions are expanded, composites of higher thermal conductivities will be required. The aim of this work was to investigate, evaluate, and try to predict the influence of key parameters on thermal conductivity and diffusivity. This was achieved by analyzing the effect of both volume fraction and shape of Aluminum Nitride ceramic fillers and measuring the thermal conductivity. In addition, the influence of percolation on thermal conductivity is considered. The thermal conductivity of the composites is discussed by employing a predictive equation using literature data of thermal conductivities for both the filler and resin. As well as thermal conductivity measurements the effect of volume fraction of the filler was also explored.ExperimentalSpecimen PreparationThe composite samples were prepared from silicone resin and Aluminum Nitride (AlN) fillers. The AlN fillers with an average particle size of 20 µm are shown in Figure 1. The mean diameters of the AlN particles used are given in Table I. For comparison the AlN fillers with an average particle size of 5 µm are shown in Figure 2. A planetary centrifugal mixer was used for simultaneously dispersing the components uniformly and de-aerating the mixture. After mixing, these materials were placed in a silicone rubber case and cured at 150 °C for 1 hour."

Jan 1, 2013

By Dirce H. Jacomo, Jaciele G. Teixeira, Anibal Y. Abreu Castillo, EsperidianaA. B. Moura, Yalquiria A. Silva, Rene R. Oliveira, Michelle G. Gomes

"Composites consisting of poly(vinyl alcohol), starch and sugarcane bagasse ashes, using glycerol as plasticizer agent, were prepared by solution casting method. Composites prepared were subjected to electron-beam radiation treatments, at radiation dose of 50 and 80 kGy using a Dynamitron electron beam accelerator, at room temperature in the presence of air. The composite samples obtained were evaluated for their water absorption, mechanical and morphological properties.1. IntroductionThe potential of biodegradable polymers and more specifically of biocomposites obtained from agro-resources have long been well established [1-3]. Starch, derivate from variety of botanical sources (cereals, legumes, and tubers) is widely available raw material and one of the most studied and promising agro-resources for the production of biodegradable polymers as matrices for biocomposite applications. However, starch itself is very brittle, hydrophilic and its mechanical properties are very poor for many applications [3 - 5]. The blending of starch with conventional polymers is a promising approach to improve its drawbacks. Recently, many efforts have been made to blend starch with biodegradable synthetic polymers [5, 6]. Polyvinyl alcohol (PYA) is a particularly well-suited synthetic polymer for the formulation of blends with natural polymers, as it is highly polar and can also be manipulated in water solutions, and depending upon its grade, in functional organic solvents as well [3, 7]. PY A has been reported to be an option to blend with starch. Most of the starch/PY A composites have been prepared by casting. However, it is well known that starch/PY A composites has poor in water resistance and mechanical properties after absorbing water [3,8]. Attempts to improve the mechanical properties and to decrease the water absorption property of the starch/PY A composites are made by adding the cross-linkers and plasticizers. Park et al. prepared starch/PY A/citric acid films by the casting method. They also studied the effect of (spell out) citric acid on the mechanical properties and water resistance of composites [9]. Zhai et al. prepared the starch/PY A hydrogels using electron-beam radiation [10]. Different kinds of lignocellulosic fibers have been investigated in blends for formulation of biocomposites."

Jan 1, 2013

By Ledjane Barreto, Tulio Flávio Accioly de Lima e Moura, Wilson Acchar, Antonio Carlos Silva da Costal

"Clays are common ingredients in pharmaceutical products both as exclplents and active substances. Clay minerals are naturally cationic exchangers and they may undergo ion exchange with basic drugs in solution. Smectites, and montmorillonite have been studied due their high cation exchange capacity as compared to other silicates. Recently a patented study reports the use of attapulgite as the encapsulating agents both for the protecting the active substance and modulating release into the body. Some clays such as kaolinite, smectites, talc, etc are also used as dermatological protectors. Sepiolite and smectites have the ability to form complexes with organic compounds with absorb ultra-violet radiation, enabling them to be used in sun screens with protection factors. The objective of this work is to characterize the attapulgite in order to study the potential use of this clay material in the human health.IntroductionSince the begimling of time, nature has served humanity as a source of various raw materials. Among these, clays such as kaolinite and ilitte are common ingredients in the tile production. Recently, special clay materials have been investigated in order to identifY new potential uses of these class of materials. Clay materials are natural raw material and have excellent properties such as low toxicity, good biocompatibility, making them a good material to be used in biological applications. Attapulgite (paligorskite) and sepiolite is so called special clays. These special clay materials are very sin1ilar and have a great potential to be used in some technological areas due their special catalytic, sorptive and colloidal-rheological properties [1-8]. Recently some works have reported the use of these special clays materials for many applications such as drug delivery, wound dressing, oil absorbent, pesticides, fertilizers [9-12]. Brazil has a significant reserve of attapulgite located in Piaui state, making the study of the potential of this mineral in special areas, very attractive. Attapulgite is classified a fibrous alluminous silicate material and shows the presence of micro pores and channels, fine particle size and high surface area making this material a good candidate alternative material to be used in many industrial applications [6,8,9,11,12]. The objective of this work is to characterize the physical and microstructure of attapulgite."

Jan 1, 2012

By Carl C. Nesbitt

A study was conducted to investigate the claims of early observers who noted an increase in the rate of gold dissolution when chlorine was chemically produced in the leach vessel compared to sparging with chlorine gas. This "nascent" chlorine was presumed to be an active intermediate in the production of chlorine (C1,l from chloride ions. The study used UV light to produce an activated chlorine atom intended to recreate the observed increase in the gold dissolution rate. Although no change in the kinetic rate was observed, the reaction mechanism by which chlorine reacts with particulate gold was instead determined. Various concentrations of multivalent cationic chloride salts were added to the leach solution to demonstrate that the increased dissolution rate was due to the increased concentration of the chloride ion and ionic strength of the solution.

Jan 1, 1992

By Chai Li-yuan

The anodic behavior of AZ31 magnesium alloy in NaOH alkaline solution was investigated in this paper. The effects of anodizing parameters, such as applied current density, concentration of NaOH and temperature of the solution on the formation, structure and surface morphology of the anodic films were also studied. The formation of the anodic film was analyzed by analyzing the anodic polarization curves, the potential-time curves and XRD, SEM graphs of samples obtained at different anodizing time. The results of corrosion resistance tests, XRD and SEM observation showed that the temperature greatly affected the formation and anti-corrosion property of the anodic film, but the concentration of NaOH not. The film with best anti-corrosion resistance was obtained at applied current density of 10mA/cm2, 353k in 1mol/l NaOH solution.

Jan 1, 2006

By Antonio Martin, Jesus Hurtado, Francisco Jimenez

"Atlantic Copper is one of the largest copper producers in Europe. Its production facilities, including a primary copper smelter and an electrolytic refinery, are located in Huelva, on the southwest coast of Spain. These installations enable the smelting of over 1 million tpy concentrates to produce up to 260,000 tons per year of cathodes and 900 ktpy of sulphuric acid.Since 1970, several improvements have been made at the Converters Area such as modifications of primary hoods, operations with an OPC system, installation of scrap chargers, the recent installation of the secondary hoods and other environmental projects. All these modifications have been aimed at increasing the capacity of our smelter while keeping our continuous environmental commitment.This paper describes the modifications and improvements carried out at the converters area and our proposals for future developments."

Jan 1, 2012

By S. Ferlay

"The main purpose of the ZIMA VAL project (Label EUREKA EU1367 and LIFE ENV/F/000278) is to demonstrate industrial scale recovery and recycling of the main components of used dry batteries (zinc, manganese dioxide, mercury, and stainless steel) into high added value products. The originality of the ZIMA VAL process resides in:1- the use of hydrometallurgy2- alkaline treatment implementation (highly selective) for zinc and mercury3- electrochemical recovery of high quality products.4- the recycling of all the battery components (zinc, mercury, manganese dioxide, stainless steel) ·5- low operating and investment costs.The process consists of physical classification, mechanical dismantling, hydrometallurgy and electrochemistry. The purpose of the demonstration plant in FALAISE (Calvados - France) is to define the technical and technological parameters of an industrial unit for the treatment of 2400 tonnes per year of used batteries."

Jan 1, 2000

By Wan Entong, Xie Junlin, Jiann YangHwang, Yang Chengwei, Chen Junfu, Zhang Jianjun, Cao Tongyou, He Feng, Peng Zhugang, Fang De

During the solidification process of peritectic steel (PS), the peritectic reaction often causes volume contraction which associated with surface longitudinal cracks, and using mould flux with low heat flux density help for alleviating surface longitudinal cracks. New peritectic steel mold flux with Co2O3 doping reduced the heat flux density, and the optimal content was found to be 2.0 wt %. Furthermore, basicity and Na2O addition were designed, and the minimum heat flux density required basicity of 1.4 and 10.0 wt %. Na2O content. As a result, the optimal peritectic composition was CaO(35.67wt% ), SiO2(25.48 wt %)，Al2O3(3.7 wt %)， MgO(2.53 wt %)，Na2O(10 wt %)，CaF2(14 wt %)，Co2O3(2 wt %).

Jan 1, 2015