By G. Sandoz, D. A. Meyn

The fracture surfaces of specimens of titanium a1loys which exhibited susceptibility to subcritical crack growth in a wide variety of environments, including aqueous solutions, alcohols, hydrocarbon gases, carbm tetrachloride, and dry air, were examined. The dominant and characteristic fracture mode was cleavage. which became mixed with an increasing porportion of ductile fracture modes (dimples. and so forth) as the applied KI was increased. The cleavage plane in all the alloys was oriented at 15 deg from (0001) of the a phase. No indices could be assigned to the 15 deg cleavage Plane because of uncertainty as to which zone it belonged to. SLOW crack growth and delayed fracture take place in certain titanium alloys at stress intensity (KI) lower than the critical values for complete fracture (KIc) found in short-time tests for plane strain fracture toughness.' Such crack growth may take place in very dry air on sustained loading if the alloy contains a sufficient amount of hydrogen and if the stress intensity factor is higher than a threshold value designated KIH.2 Similarly, a number of environments such as water, alcohols, and hydrocarbons may cause slow crack growth provided the stress intensity factor exceeds the threshold value KISCC. In this paper it is intended to examine some fracto-graphic and crystallographic details of this subcritical crack propagation process as related to alloy composition, environment, and stress intensity. It has been previously reported that subcritical crack growth takes place in titanium alloys in aqueous environments by cleavage.2"6 The observations to be described here indicate that in the alloys investigated the mode of subcritical crack propagation is more dependent on the stress intensity during cracking than on the environment. The fracture mode is illustrated with photographs of the fracture surfaces at a wide range of magnifications. The crystallographic character of the cleavage mode is also presented and the results discussed. EXPERIMENTAL APPROACH The studies were made on four titanium alloys— Ti-8A1-1Mo-lV, Ti-5A1-2.5Sn, Ti-7Al-1Mo-lV, and Ti-0.350. Of these four alloys the first two were mill annealed and fine grained. The latter two were noncommercial and coarse grained, having been prepared for other experimental purposes. The crystallographic studies required a large-grain size. Consequently the fine-grained alloys were an- nealed in a vacuum at 1950°F and furnace cooled to produce samples for these studies. This treatment did not alter the microstructure significantly except for grain size. All the aluminum-containing alloys showed primary a with a network of ß-phase particles within the a grains; Figs. 1 and 2 show this microstructure for the specific case of fine-grained Ti-8A1-1Mo-1V. The cracks in the figures will be discussed later. Fractographic studies were made on all the alloys, but the electron fractographs displayed herein are from the Ti-8A1-1Mo-1V alloy in the fine-grained condition. Emphasis was placed on this commercial alloy because considerable information was available on the stress-corrosion cracking characteristics in a variety of environments. Sufficient supplementary studies of the alloy after the anneal to produce large grains were conducted to establish that the stress-corrosion cracking susceptibility and fractographic characteristics were not changed significantly. Thus it could be inferred that the crystallographic data obtained exclusively on large-grained specimens would apply also to fine-grained specimens. Fracture surfaces for study were obtained using precracked cantilever beam specimens loaded as described by Brown. The precracked section of a specimen was immersed in the environment of interest. Values of initial stress intensity factor Kli were chosen slightly higher than KISCC in order to obtain a fairly extensive region of slow crack growth. Fracture surfaces representative of a variety of stress intensity levels could then be examined because in the cantilever beam test KI increases as the crack propagates.

Jan 1, 1970

SULPHUR is a very well known mineral and apparently is produced in many places. It is engendered from an unctuous earthy and powerfully hot substance so that it is considered among experienced workers to bear a resemblance to the element of fire. This is called by these same men the masculine seed and the prime agent of Nature in the composition of metals. Because of its great dryness and heat it has, as experience shows, affinity with fire, which is easily introduced in it when brought near. And once introduced the fire is quenched only with difficulty before its unctuousness is wholly consumed. Although it shows itself to us of such a hot and dry nature, we must not think that sulphur is a substance so pure that it can stand by itself or that in order to attain its form it has no need of its portion and part of moisture like every other mixture. This is shown to us by its easy fusion, in which it resembles the metals. This thing is found in many places and in many varieties of color; some are white, others yellow and orange, and some others between gray and black. They also say that some red is found. It does not occur in that arrangement of veins like other minerals, but most liberal Nature makes whole mountains of it as is seen in the Aeolian islands, [26] near Sicily, in Etna or Moncibello which is the island of Sicily, at Pozzuoli, in the territory of Rome, in the Sienese domain at San Filippo, and in many other similar places. It is a substance that has a very strong odor and is most unpleasant to smell. It is very fixed in its substance so that it is never corrupted by time, by boiling, or by the moisture of water. For although it may stand in water a long time it never becomes soft nor does it ever decrease or increase in weight. It is brittle and easily crushed very fine. It is said that a trace of garlic rubbed on the mortar helps anyone who wishes to reduce it to impalpability. Its ores have a form more like earth than like stone although they some¬times have the color of a certain soft rock. The places where it is found are easily recognized by the great odor that they give out and by the very hot baths that often spring forth near it. What I have already told you about quicksilver that is contrary to the

Jan 1, 1942

By R. G. Hudson, H. W. Paxton

The activities of iron and chromium in their binary system have been measured by the Knudsen orifice technique. The system is close to ideal at 1200- 1250 C with slight positive deviations. The effect of this on the liquidus and solidus is discussed and these are calculated for two limiting assumptions. The vapor pressure of pure iron, pure chromium, and one alloy is compared with that obtained by the Langmuir free-evaporation technique. The results agree, indicating a vaporization coefficient close to 1. HERE are no reported data on the thermody-A namic activity of iron and chromium in the solid portions of the phase diagram. It is generally assumed'.' that the liquid solutions of iron and chromium obey Raoult's law. Chen and Chipman" have inferred that the liquid solution obeys Raoult's law. The minimum' in the solidus-liquidus curves for the iron-chromium system shows that there are deviations from ideality in either the solid or liquid or both. Because of the importance of developing reliable techniques for obtaining activity data in alloy systems at high temperatures and of the data so obtained, an investigation of the activity of iron and chromium in the binary at 1200-1250 C was undertaken using the Knudsen cell. Experimental The apparatus and experimental procedures used in this investigation were described in a previous paper." The various materials used for the construction of the Knudsen cell are listed in Table I. The metal used for the determination of the vapor pressure of chromium was 99.9 pet pure, obtained from A. D. Mackay, Inc. The iron was obtained as electrolytic grade from Fisher Scientific Company. The Fe-Cr alloys used are shown in Table 11. The largest error and controlling factor in the accuracy in the experiments reported here are introduced because of temperature uncertainty, which is estimated to be ±3 deg C. This introduces an uncertainty of 26 pet in the measured pressure. Experimental Results and Calculations The vapor pressures of pure iron and pure chromium were calculated from the measurements by the Knudsen equation3 on the assumption that only Cr or Fe atoms were present in the gas phase. For metal vapors, at the high temperatures and low pressures involved in these measurements this should be a reasonable assumption. Whitman" corrections for the cells were made. The data and results of pressure calculations are presented in Table I, and are plotted in Fig. 1. In addition the heat of vaporization at the absolute zero, ?E°°, has been calculated for chromium. These calculations are summarized in Table 111. The data used in these calculations are as follows kelley13 (F° - E°°/T ) Speiser, et al H (F° - E°°/T ) 010 where F" — standard free energy at temperature T It was necessary to calculate the total pressure above the alloys from the total weight loss W of the cell during a run, because of the fact that all attempts to collect and analyze the chromium and iron vapor effusing from the cell in the apparatus available failed. The failure resulted from the re-

Jan 1, 1959

By John M. Kelly

New Mexico produced 39,475,388 bbl. of oil in 1944, the greatest amount in one year in the oil history of the state. This production was 593,046 bbl. or 1.25 per cent more than in 1943. New Mexico retained its position as the seventh largest oil-producing state. The maximum per well allowable on Jan. I, 1944 was 48 bbl. daily and at the end of the year it was 45 bbl. daily. Allocations as set by the New Mexico Oil Conservation Commission closely followed the recommendations made by the' Petroleum Administrator for War. The average daily pipe-line runs were within 4 per cent of the allocation. Production by counties was as fol1ows;Lea County, 33,509,548 bbl.; Eddy County, 5,504,498; Northwestern New Mexico 461, 342. Drilling activity for New Mexico in 1944 was well above that of 1943, with 362 completions. Of these, 283 were oil wells, 12 gas wells and 67 dry holes. The ratio of dry holes to producers, about I to 4, was an improvement over 1943. Wildcat drilling during 1944 was responsible for the discovery of six new fields and the extension of two present producing areas. Drilling records were established in New Mexico during 1944 with the deepest producer ever completed, the Humble Leonard Oil Company's No. I at 11,969 ft., in the Ellenburger section of Ordovician age near Jal, Lea County. The discoveries in Lea County during 1944 were as follows: West Lovington field, where Fred Turner, Jr. drilled his No. I State B .in C SE SW sec. 4-17-36 and completed it for 122 bbl. of oil in 8 1/2 hr., in the San Andreas section of Permian age. The Tonto field, where the T-exas Company completed its No. I Baskin at a total depth of 3586 ft. in Seven Rivers lime of Permian age, with an initial production of 254 bbl. of oil in 21 hours. The Drinkard area, where the Gulf Oil Corporation's Drinkard No. I flowed 782 bbl. of oil in 14 hr. from the Yeso section of lower Permian age, thus opening the first lower Permian production in the state. The total depth of this discovery was 6508 ft. and oil was 38.8" A.P.I. gravity. The Dublin area, where the Humble Oil and Refining Co. established a drilling depth record of 11,969 ft. drilling and completing its No. I Leonard Oil Co. well in the Ellenburger lime of Ordovician age. This well flowed 221 bbl. of oil per day, of 48.9º A.P.I. gravity oil. It is in sec. 12-26-37. The new pay horizon discovery of the Continental Oil Co. in the Skaggs area, where the company completed its Skaggs B-23 No. 2 in sec. 23-20-37 for 236 bbl. of oil in 21 hr. from the Wolfcamp section of lower Permian age, at a total depth of 7725 ft. This well was drilled to granite at 10,465 ft. and plugged back to the Wolf-camp for a new pay zone completion.

Jan 1, 1945

By C. W. Allen, L. C. Moore

The Mather mine, of the Negaunee Mine Co., is within the limits of the City of Ishpeming. on the Marquette iron range in Michigan's Upper Peninsula. It is named for William G. Mather, who has served as President, and Chairman of the Board, of The Cleveland-Cliffs Iron Co. for well over 50 years. The property comprises nearly the square mile of section 2, T.47 N. R.27 W., which, except for 20 acres in the northeast corner, was leased by The Cleve-land-cliffs Iron Co. to the Negaunee company. The latter is a partnership of Cleveland-Cliffs and the Bethlehem Steel Co., organized to equip the property, retaining Cliffs in charge as operator. Shipments of ore from this area are mainly through Marquette, which is 16 miles to the northeast on Lake Superior, or through Escanaba, a Lake Michigan port, 65 miles to the south. Cleveland-Cliffs, in 1943, operated 12 mines in the Lake Superior district, with shipments of 6,635,576 tons for the year. Geology The north footwall of the Marquette Range synclinorium outcrops near the north line of set. 2, the iron formation dipping to the south at an angle of about 40. The south side of the trough reappears at a distance of 4J5 miles on sec. 26 and the surface geology between shows iron forma- tion or intrusive diorites. The latter are harder than most phases of the iron formation and, as a result of glacial action, appear as buttes or low-lying hills. The general elevation of sec. 2 is about 1450 ft. above sea level, or 850 ft. above Lake Superior, and the higher diorite outcroppings about 1600 ft. above sea level. The geological structure has been complicated by a series of major and minor faults, one of which may be illustrated by the diorite sheet, which tilts south with the iron formation in the north half of the section and then reappears near the center to repeat this sequence. Sectionally the geological series includes a nearly eroded capping of Goodrich quartzite followed by the considerable thickness of Negaunee iron formation, which is cut by intrusive dikes or diorite sheets, and underlain by the Siamo slates grading into quartzites. The ore deposits occur mainly in troughs formed by the intersection of impervious dikes and the footwall slate, but include locally enriched lenses or bands in the iron formation and also interbedded with the Siamo slate. The ore is a soft red hematite with an indicated dried analysis from the surface drilling to date of 61.50 per cent Fe, 0.134 Per cent P, 5.40 per cent Si, 2-87 Per cent A1 and 0.015 per cent S. Exploration A diamond-drilling campaign started in 1937 actually had its inception in 1917, when a number of shallow test holes were put down for the purpose of locating ore that might be quickly developed and mined

Jan 1, 1946

By E. Peters

As in other fields of Extractive Metallurgy, Hydrometallurgy is preoccupied with separation processes and with oxidation-reduction processes. The physical chemistry of each type of process can be described in terms of thermodynamic equilibria and in terms of reaction kinetics. Reaction kinetics are much more important at the low temperatures limiting hydrometallurgical processes than in com- parable pyrometallurgical operations and the number of cases in which the kinetics can be described by simple liquid-phase mass-transfer models are sharply limited. It is convenient to subdivide the applicable rate phenomena into processes in which (a) interface reactions control the rate,(b) mass transfer processes control the rate, (c) solid state process affect the rate, (d) thermodynamically predicted phase changes or molecular reactions fail to take place, (d) metastable substances or supersaturated phases persist, and (elchomogeneous reactions in solution affect the chemistry and the kinetics. Examples are drawn from the unit steps of leaching, cementation, hydrogen reduction, and electrowinning.

Jan 1, 1973

By Eugene A. Mizikar

A mathetnatical model of heal transfer in continuously cast steel slabs is described. The model, consisting of a unidimensional transient conduction equation and boundary condition equations, has been pvogrammed for computer solution. Temperatuve and solidification profiles calculated for a 6-in. slab, being cast under several conditions of secondary cooling, are presented and compared. Calculated solidification profiles are in agreement with reported expevinle~ztal values. For the mold zone, the predicted slab shell thickness can be described by: Resuilts of the study indicate that multibank spray cooling followed by radiant cooling should be employed when solidifying thick slabs with minimum surface temperature of 1600°F. Under these conditions, a 6-in. slab can be expected to solidify in about 8.3 min. Computer results also indicate that radiant cooling can replace spray cooling during solidification of the final 30 pct of slab with little increase in overall solidification time. CONTINUOUS casting has come to the forefront of the steel industry in recent years because of economic advantages resulting from increased yields and elimination of several processing steps. Considerable work, however, remains to be done regarding modifications to the process and operating procedures. Both a lack of operating plants in this country and the experimental difficulties associated with direct measurements on moving castings have made determination of solidification rates and temperature distributions difficult. An alternate approach is to mathematically simulate heat transfer in a continuously cast section, and then calculate the temperature distributions as a function of the controllable variables of the process. Simulation of heat transfer during solidification requires that a nonlinear mathematical problem be solved. As pointed out by Ruddle,' there are two mathematical approaches to the problem- the analytical approach and the numerical approach. While the analytical approach is certainly the more elegant of the two, it does require a number of inexact assumptions because of the complexity of the problem. For example, noteworthy analytical treatments of heat transfer in continuous casting have been developed by Savage Hills,3 and pehlke4 only by making one or more simplifying assumptions such as invariant thermophysical properties, constant heat-transfer coefficients in the mold, and linear temperature profiles in the shell. Simplifying assumptions such as these can introduce considerable uncertainty in the validity of results calculated with analytical solutions. Numerical solutions, which are considerably more versatile, appear to be better suited for solving solidification problems. Complex variations in the boundary conditions and variable thermophysical properties can be handled readily with this technique. Whereas numerical computations can be long and tedious when done by hand, results can now be obtained quite rapidly with the use of either the digital or analog computer. Several numerical models of heat transfer in continuous casting have been published. In 1963, Adenis, Coats, and Ragones published a numerical model used to calculate temperature distributions in direct-chill-cast magnesium billets. More recently, Donaldson and Hess 6 presented results obtained with a numerical computer model of heat transfer in continuously cast steel billets. In the present study, a model of unidimensional heat transfer in continuously cast slabs is presented. The method of solution on a digital computer is also included. Calculated temperature distributions and solidification profiles for various schemes of secondary cooling along with attempts to verify the model are also discussed. MATHEMATICAL MODEL The schematic representation of the slab continuous casting process in Fig. 1 illustrates that the slab passes through three distinct zones of cooling. Accordingly, the mathematical model consists of three parts: 1) solidification in the mold; 2) solidification in the spray cooling zone ; 3) solidification in the radiant cooling zone. Heat-Transfer Equations. The model was developed bymaking a heat balance on a horizontal slice of slab over the time period required for the slice to proceed from the liquid metal meniscus in the mold to the cutoff station. As shown in Fig. 2, the imaginary slice extends from the center line to the surface of the slab. As the slice moves downward, heat is conducted from the center line to the surface of the slab at a rate governed by the surface boundary condition and thermophysical properties of the metal in the slice. The following partial differential equation describes the conduction of heat in a medium moving at velocity U in direction Z:

Jan 1, 1968

By Charles Wert

THE diffusion and precipitation of carbon and nitrogen in a iron have previously been investigated using the internal friction as a measuring tool.' Most of this work has been done on rather pure iron; no effect was observed which would indicate that either of these phenomena is affected by the rather small amounts of impurity found in these samples of iron. Fastz observed, however, that both the diffusion rate and the aging properties of nitrogen in iron were sensibly changed by the addition of Vz pet Mn. The diffusion rate at a given temperature is reduced and the nucleation of nitrides is apparently changed somewhat. He observed no such changes for carbon in this alloy. Later Dijkstra and Sladek" extended these observations on nitrogen to other alloys of iron. They found that metals other than manganese also influence the behavior of nitrogen in iron; chromium, molybdenum and especially vanadium affect the diffusion and precipitation of nitrogen even more than manganese does. Their results have been verified in all essential details by this author, who finds in addition that small additions of nickel have about the same effect on the diffusion of nitrogen as the same amount of manganese. The present work was undertaken to study the effect on carbon in iron of these alloying elements. The alloys used had two sources. The material used as a "standard" (designated Fe in this paper) in the measurements was some iron supplied by J. K. Stanley, of Westinghouse Electric Corp., who reported 0.01 pct 0, as the only major impurity. He also made up an alloy of 0.26 pct Ni and one of 0.9 pct Mo using this same iron as a base. They were supplied by him in 2 lb billets, which were sawed into rods and cold formed into 0.030 in. wires for measurement. The alloys of chromium, manganese, and vanadium were prepared by the metallurgy section of the Institute for the Study of Metals, University of Chicago, by adding these metals in turn to vacuum melts of National Research Corp. iron. The small castings prepared in this way were also cold formed into 0.030 in. wires. After these wires had been prepared they were decarburized for 30 min at 730°C in wet Hz. After this treatment, no trace of carbon (as measured by internal friction) could be found. All specimens were then carburized for about 15 min at 710°C and water quenched. By this treatment the internal friction at 40°C was raised to a Q-' ~ 0.015. The diffusion of carbon in these alloys was studied by observing the shape and position of the internal friction peak at 0.9 cycles per sec. These measurements were made using a torsional pendulum in a manner described earlier.' The data are plotted in Fig. 1. It is seen that there is no apparent difference in internal friction between the various alloys. This is in marked distinction to the broadening and shift-

Jan 1, 1953

By J. Rogers, K. L. Sutherland

THE relationships between collector and mineral, activator and mineral, and activator, collector and mineral will be considered herein. We propose to criticize current theories of flotation but we will not repeat the many pertinent arguments presented by Wark and Cox28 in 1937 in which the "chemical" or more strictly the "solubility" theory proposed by Taggart and co-workers22 is shown to be untenable. Recently Taggart, Arbiter and Kellogg24 have studied the long-chain aliphatic amines as collectors and have attempted to resuscitate the solubility theory for these particular collectors. Dean and Ambrose3 have felt that "we stumble over words" when we distinguish different mechanisms of adsorption. Our view is that nothing is more stultifying to the development of a science than attempts to force widely different phenomena into one classification. This oversimplification leads immediately to difficulties in the interpretation of results. EXPERIMENTAL PROCEDURE The response of minerals to activator and collector was determined by "captive-bubble" tests. The methods of preparation of specimens26 and of testing18 have been previously described. Results from captive-bubble tests were confirmed by flotation tests in glass-stoppered cylinders.25 The full lines shown in the figures relating solution composition to contact (flotation) distinguish solutions in which contact (flotation) is possible from those in which it is not. The curve is derived by successive approximation and the accuracy is ±0.2 pH units and ± 5 mg. per liter of collector or depressant. Solution compositions for which it was shown experimentally that contact or flotation is possible are marked by a circle, those for which it is not possible by a cross and those for which it is doubtful by a cross within a circle. It is assumed that at all other solution compositions within (without) the curve, contact or flotation is possible (not possible). After testing in the collector solution, the mineral was removed, washed, and tested by the captive-bubble method in water, or floated in a cylinder with frother only. In this way the composition of solutions in which a mineral was conditioned but in which properties of the collector solution prevented contact or flotation can be defined. The composition of solutions in which conditioning was possible lie between the full and broken curve, the experimental results being indicated on the figures by a square. The curves show the limits of composition of solution in which flotation in a cell would be possible. Many factors other than those considered in these tests determine recovery or grade of a given mineral in practice.

Jan 1, 1947

By R. B. Walker, R. Palmer, L. C. Bryner

The purpose of this investigation was to further study some of the factors affecting the air oxidation of sulfide minerals. Data obtained from laboratory studies on the effect of temperature, concentration of iron salts, pH, and other catalysts on the biological and nonbiological oxidation of sulfide minerals are presented. The oxidation of copper sulfide minerals and subsequent leaching of the soluble copper has long been a profitable operation. The chief oxidizing agent is oxygen from the air. This reaction is influenced by a number of different factors such as temperature, light, hydrogen ion concentration, oxidizing agents, and various catalysts. Sullivan1 found that copper sulfide minerals are slowly oxidized by the air and that dilute sulfuric acid and iron (111) increased their solubility. At that time it was not known that bacteria were involved in the oxidation of the sulfide minerals. It has been shown that pyrite, molybdenite, free sulfur, and the copper sulfide minerals found in the waste rock dumps in Bingham Canyon, Utah, are largely oxidized by chemosynthetic autotrophic microorganisms found in the leaching streams.2-6 Similar organisms have been isolated in other mining areas7,8 and from the effluents from coal rnines.9 The following are some of the questions that have arisen regarding the mechanisms of the reactions involved in the leaching process. How dependent is the leaching operation upon the biological reactions? How does the temperature effect the biological and non-biological reactions? How does the concentration of iron (II) and (111) effect the rate of oxidation of copper (II) sulfide? Does the iron act as a catalyst? Does activated carbon act as a catalyst on the oxidation of sulfide minerals? What effect does the hydrogen ion concentration (pH) have on the above reactions? The purpose of this paper is to report the results of laboratory studies on these problems. EXPERIMENTAL The apparatus used in this investigation was an air lift percolator described in our earlier work.' The percolator consisted essentially of an air lift which enabled the leaching solution and microorganisms to pass freely through a suspension of mineral (substrate) in Ottawa sand. The air lift served the additional purpose of maintaining an ample concentration of oxygen and carbon dioxide in the nutrient (leaching) solution. (See Fig. 1.) The percolators were so constructed that they could be immersed in liquid constant temperature baths for temperature studies. The thermostats were controlled to +0.5°C. The reactions were all run in the dark. The percolators were charged with one to three g of mineral, dispersed in 100 g of Ottawa sand and 100 ml of nutrient or leaching solution. The sand was purified to remove traces of iron by digesting with concentrated hydrochloric acid and washng with distilled water until free from chloride. After drying, the sand was ready for use. The compressed air supply was regulated to 5 psi and bubbled through an aerator containing distilled water, which was maintained at the same temperature as the bath used. The air was filtered through cotton plugs to maintain sterile conditions. The tops of the

Jan 1, 1968

By J. P. Smith

Permian salt measures carry extensive lenses of soluble potash salts in north central Germany. Potash deposits of Oligocene age are found in the Upper Rhine Graben of Alsace (France), and in the Catalonian Basin of Spain. These deposits are found in a wide range of structural settings. Reserves are large, and the production of potash salts is an important phase in the economy of each of these countries.

Jan 1, 1950

By M. J. Pool, with Appendix by Larry Kaufman, R. W. Krenzer

Thermodynmic properties of the Cu-Mn system have been deterrrzined in the temperature range 973" to 1273°K by measuring the vapor pressure of manganese in equilibrium with alloys of compositions varying from 0.13 to 0.91 rnole fraction manganese using the Knudsen effusion technique. Activities of manganese calculated from the measured vapor pressures show large positive deviations. Calculated heats and entropies of mixing are positive with a maximum occurring at approximately 0. 7 mole fraction manganese. ThE investigation of thermodynamic properties of binary systems involving transition metals is of considerable interest at the present time. The incomplete subvalency electron levels of transition metals lead to unusual behavior in some alloys, and considerable information can be obtained by determining the thermodynamic characteristics of these systems and relating the thermodynamic behavior to observed physical properties. The Cu-Mn system, shown in Fig. 1,' provides an example of an alloy system in which the determination of the equilibrium phase diagram and various physical properties has received considerable attention, but very little work has been done on measurement of the thermodynamic properties. Elemental copper and manganese have comparable electronegatives, atomic sizes, and cohesive energies, but differ in crystal structure. They form a continuous series of solid solutions only at high temperatures and the structure varies in a continuous manner from fcc at the copper-rich end to fct at the manganese-rich end.' The purpose of this investigation was to measure the vapor pressure of manganese over a series of Cu-Mn alloys and from these values determine the thermodynamic properties of the binary system. Vapor pressure measurements were made in the temperature range 973" to 1273"K, remaining within the solid-solution region for each alloy studied. EXPERIMENTAL PROCEDURE The relative thermodynamic properties of solid Cu-Mn alloys were determined from vapor pressure measurements by means of the Knudsen effusion tech- nique. Several discussions of the theory can be found in the literature. In the case of copper and manganese, it is assumed that manganese is the only component subliming, so the vapor pressure of manganese over the various alloys can be determined directly by measuring the weight loss of the effusion cell. This is a valid assumption since the vapor pressure of manganese is about four orders of magnitude higher than the vapor pressure of copper in the temperature region of interest. The vapor pressure of manganese over the alloys at any given temperature is then related to the weight loss of the effusion cell per unit area per unit time. An upper limit of 1.5 x 10"s has been measured for the ratio of polyatomic to monoatomic molecules for manganese vapor in equilibrium with solid manganese at 1180°K, so it was assumed that manganese vapor is monoatomic. The effusion cells, fabricated from high-purity alumina, are 26 mm high, 18 mm OD, and have a wall thickness of 1 mm. Three different sized holes of 2.03, 2.54, and 3.18 mm diam were drilled in the lids from the inside face to minimize chipping, and the lids were then slip-cast onto the cells to provide a gas-tight seal. Alumina was selected for this particular application both because of its resistance to thermal shock and reaction with manganese vapor. In the ideal case, the orifice of the effusion cell should have a knife edge so that effusion through the orifice

Jan 1, 1970

By John B. Cook

Most of today's open pits take the form of conical-shaped excavations in the relatively flat or undulating terrain surrounding them. Ore is usually hauled uphill from the pit bottom by truck, rail, or skip to crushing, beneficiation, railroad loading, and stockpiling facilities near the edge of the pit. There are, however, a few orebodies whose locations in mountainous terrain causes special problems that generate different technical solutions. LAMCO's 10.5 million metric tons per year high-grade iron mine in the Nimba Range in tropical Liberia is probably one of the most extreme of these exceptions (Fig. 1). At Nimba there is a 2,000-ft difference in elevation between the upper- most levels of the orebodies and the start of the railroad below at the foot of the mountain. Haulage to the crusher is usually downhill at grades of up to 12% dictated by the topography of the rugged terrain. Ore is transported from the crusher down the mountainside by a conveyor sys- tem 10,096 ft long, whose average grade is 18%. The belt is braked by asynchronous generators, feeding power into the local network. The original crusher must be relocated at a lower elevation outside the final pit limit to allow that part of the mountain on which it now stands to be excavated. HISTORY The LAMCO Joint Venture is owned 75% by the Liberian-American- Swedish Minerals Co. (LAMCO) and 25% by Bethlehem Steel Corp. LAMCO is comprised of a 50% interest by the Liberian Government and 50% interest by Liberian Iron Ore Ltd (Fig. 2). This joint venture was launched to develop the high-grade iron ore deposits of the Nimba Range.

Jan 1, 1969

By Michael B. Bever, John R. Anderson

Carbon may affect the alloys of copper in several ways. Provided an alloying element does not oxidize preferentially, even minute quantities of carbon dissolved in liquid alloys of high copper content will form insoluble carbon oxide gases under oxidizing conditions. Gas porosity in castings of high-copper alloys can originate in this way. In certain alloys of low copper content carbon may have considerable solubility and may be an effective deoxidizer. In these alloys carbon will tend to suppress porosity. Carbon that is dissolved in the molten alloy is likely to be retained in the solidified metal. The effects of carbon on the physical properties of the metal are determined by the form in which it is present. Depending on the alloying elements and also on the cooling rate, carbon may precipitate as graphite, may form a carbide or may remain in solid solution on cooling. As solid copper does not dissolve a measurable amount of carbon, a carbon-bearing solid solution can occur only if the copper is alloyed with a large excess of an element that forms such a solution. The effect of graphite or of carbides on the properties of an alloy will depend on the size and distribution of the precipitated particles. As Hensel pointed out in discussion,' the formation of an alloy carbide may interfere with the age-hardening properties of a copper alloy. One would also expect that the presence of carbides or of graphite will under certain conditions promote corrosion or high-temperature failure in nonferrous alloys. Since carbon has an effect on the soundness of castings and affects the structure and behavior of solid copper alloys, its solubility in the liquid alloys is of practical importance. The isothermal change of carbon solubility with alloy composition is of interest from a theoretical standpoint. The binary alloys of copper with manganese and with nickel are used industrially and serve as a base for more complex alloys. The solubility of carbon in each of these metals is known, but its solubility in their alloys has not been determined. Earlier Data The solubility of carbon in molten pure copper is about o.oooi pct at II00°C and 0.0004 pct at 1475°C.l Various authors2""6 have published data on the solubility of carbon in molten manganese. There is agreement on a value of about 6.7 pct in the temperature range r2170 to 1245°c This solubility value corresponds to the formula Mn3C. It increases very little with increasing temperature. Corson7 states that carbon is soluble in copper-manganese alloys and that the

Jan 1, 1947

By John R. Anderson, Michael B. Bever

Carbon may affect the alloys of copper in several ways. Provided an alloying element does not oxidize preferentially, even minute quantities of carbon dissolved in liquid alloys of high copper content will form insoluble carbon oxide gases under oxidizing conditions. Gas porosity in castings of high-copper alloys can originate in this way. In certain alloys of low copper content carbon may have considerable solubility and may be an effective deoxidizer. In these alloys carbon will tend to suppress porosity. Carbon that is dissolved in the molten alloy is likely to be retained in the solidified metal. The effects of carbon on the physical properties of the metal are determined by the form in which it is present. Depending on the alloying elements and also on the cooling rate, carbon may precipitate as graphite, may form a carbide or may remain in solid solution on cooling. As solid copper does not dissolve a measurable amount of carbon, a carbon-bearing solid solution can occur only if the copper is alloyed with a large excess of an element that forms such a solution. The effect of graphite or of carbides on the properties of an alloy will depend on the size and distribution of the precipitated particles. As Hensel pointed out in discussion,' the formation of an alloy carbide may interfere with the age-hardening properties of a copper alloy. One would also expect that the presence of carbides or of graphite will under certain conditions promote corrosion or high-temperature failure in nonferrous alloys. Since carbon has an effect on the soundness of castings and affects the structure and behavior of solid copper alloys, its solubility in the liquid alloys is of practical importance. The isothermal change of carbon solubility with alloy composition is of interest from a theoretical standpoint. The binary alloys of copper with manganese and with nickel are used industrially and serve as a base for more complex alloys. The solubility of carbon in each of these metals is known, but its solubility in their alloys has not been determined. Earlier Data The solubility of carbon in molten pure copper is about o.oooi pct at II00°C and 0.0004 pct at 1475°C.l Various authors2""6 have published data on the solubility of carbon in molten manganese. There is agreement on a value of about 6.7 pct in the temperature range r2170 to 1245°c This solubility value corresponds to the formula Mn3C. It increases very little with increasing temperature. Corson7 states that carbon is soluble in copper-manganese alloys and that the

Jan 1, 1947

By J. J. Beeson

For the past fifty years or more, the structural features of the Cordil-leran mountain system of western United States have presented some most interesting problems. Any geologist or engineer living in this region, or even making occasional examinations of the mines, will lose much of interest and importance if he is not familiar with the literature. Some of the greatest works on geology have been the result of studies carried on in sections of this region. Among the more important of the earlier works are those of Dutton,l King,2 Gilbert3 and Powell;4 of the more recent Lindgren,5 Ransome,6 Spurr,7 Butler8 and others have contributed much. Many of the papers are largely of scientific interest but even these lay the foundation for the commercial application of the broader features of the geology. I have read many of these works with the keenest interest and pleasure; in fact, some have been read until some of the more important findings seem to be my own. In this paper, however, it is my aim to accept credit for little more than the labor of assembling some of the ideas of others. This is done with the hope that an interesting and valuable discussion will be the result. If some of the ideas presented should

Jan 1, 1927

By A. D. Hughes

C. W. MERRILL*-Mr. Hughes' paper not only is very well presented but is most timely in that it covers a subject of vital interest to the United States. Tin is one of the strategic metals which has not been found here in appreciable quantities. The total United States tin output since the first recorded production over 100 years ago would not supply current consumption for a fortnight. On the consumption side, tin is extremely important in national defense because of its use in tin plate which, in the form of tin cans, makes it possible to feed properly the armies that the United States recruits from its civilian population in emergencies. Moreover, the internal combustion engines so important in powering tanks, planes, and other war machines, require large quantities of tin alloys for bearings and for soldering. These considerations, along with the fact that Malaya, historically, has been the leading source of tin to the United States, make the kind of information that Mr. Hughes has presented so ably, a matter of vital interest.

Jan 1, 1949

By M. G. Corson

THE iron-silicon alloy series has always been one of the most puzzling among the binary alloys. Examining the well known mechanical properties of the iron-rich alloys only we meet the following situation: The ultimate strength and yield point of alloys worked and annealed under the usual conditions represent nearly a straight line function of the silicon content up to 4.5 per cent. silicon (Fig. 1). Starting at the ultimate strength of 35,000 lb. and at a yield point of 16,000 lb. for pure electrolytic iron, one reaches a maximum strength of 93,000 lb. and a maximum yield point of 74,000 lb. at 4.5 per cent. silicon. This corresponds to an increase in ultimate strength by 13,000 lb. per each per cent. of silicon added and nearly the same rate applies to the yield point. The data mentioned are taken from the investigation by T. D. Yensen,1 and while they do not exactly corroborate the results obtained by earlier investigators, they seem to be the most correct. Plastic properties of the alloys are controlled by a much more complicated relationship. Up to 2.5 per cent. Si, the elongation stays close to 50 per cent. (in 2 in.) and the area reduction amounts to 85 per cent;, a situation that forms the usual feature of all alloys representing strictly solid solutions. The plasticity of the latter is always nearly equal to that of their base metal. Beyond 2.5 per cent. silicon, the situation becomes much more complicated. Yensen observed an enormous drop in elongation and area reduction at about 2.65 per cent. silicon, where the first hardly reaches 10 per cent. and the second is still lower; he found, however, a considerable recovery in plasticity at about 2.8 per cent. Si and up to 4.5 per cent. Si it is represented by 20 per cent. for the elongation and 30 per cent. for area reduction.

Jan 1, 1928

By Paul E. Rosten

Introduction This papers describes some of the latest improvements that have been incorporated or planned by the Cleveland-Cliffs Iron Co. to reduce operating costs and improve pellet quality. The Cleveland-Cliffs Iron Co. operates and manages mining, beneficiation, and pelletizing operations in Michigan, Canada, and western Australia. This paper deals with the grate-kiln pelletizing operations at Republic, Humboldt, Tilden, Empire, and Pioneer in Michigan, and the Adams and Sherman in Ontario, Canada. Table I characterizes each operation in regard to location, ore type, pellet capacity and date that pellets were first produced. All of the operations with the exception of Pioneer and Tilden, utilize downdraft-two-pass grate cycles of drying followed by preheating. Pioneer utilizes an all-downdraft, three-pass grate cycle which consists of three drying zones followed by the preheat zone. The Pioneer and Tilden cycles have been described previously (Lindroos and Koski, 1966; Villar and Dawe, 1975; Koski, 1977). Tilden utilizes a three-pass grate cycle with a stage of updraft drying, followed by two downdraft drying stages. Recuperation systems which supply hot gases to a drying zone from second stage cooling were designed and fur¬nished for Tilden I. Tilden II will be identical. Empire IV will also be furnished with a recuperation system. The Adams grate¬kiln system was retrofitted with a recuperation system. This paper will summarize some of the efforts that are in effect or planned for grate-kiln pelletizing systems to: (1) reduce operating and maintenance costs, (2) reduce energy requirements, (3) improve product quality, and (4) meet environmental standards.

Jan 1, 1981

By C. Scala, F. Bernstein

General expressions are derived relating the streaming potential to the electrochemical potential of a permeable junction separating two electrolytic solutions. By the methods of irreversible thermodynamics, these potentials are related to the flux of mobile species arising from differences in pressure and chemical composition. The flux is conveniently expressed as a transference number, the equivalents of a mobile species transferred through the junction per faraday of electricity. At constant pressure, the flux equation gives the electrochemical potential across the permeable junction. The streaming potential across the junction is obtained by imposing the condition of constant chemical composition. The familiar expression for the borehole SP is shown to be a particular solution of the general flux equation. The derived exprersions were verified in experiments with seven shale samples. Both the theory and experimental data provide additional proof of the presence and magniturle of the streaming potential in shales. INTRODUCTION In the interpretation of electric logs, there has been much concern over the correction to be made to the recorded SP for an electrokinetic or streaming potential originating from the difference in pressure between the mud column and the formation. It was long recognized by M. R. J. Wyllie that such an electrokinetic potential source mas in the mud cake opposite permeable sands.' More recently, M. Gondouin and C. Scala2 showed an additional but opposing electrokinetic source of potential to be in shale beds. Their work was supported by the very extensive and excellent work of Hill and Anderson.3 n the present contribution, the general relationships between the electrochemical potential and the corresponding streaming or electrokinetic potential are examined and clarified. A notable advance towards understanding the relation between the various sources of electrical potential in a borehole has been the application of the now common methods of irreversible thermodynamics to describe the passage of ions and water through charged electrolyte junctions such as in shales.' The advantages of these methods are twofold. Unlike classical thermodynamics, they can be applied to non-equilibrium sys- tems, i.e., systems in which flow takes place, provided the flow processes have reached a steady state. They also permit conventional thermodynamic properties to be related to the steady-state dynamic properties. These methods arc used here specifically to derive expressions relating the potential behavior of shales in terms of ion and water transport. Experimental verification of the expression for the shale streaming potential is given which in turn offers theoretical support to the existence of a streaming potential in shales.' Importantly, the relative contribution of transport parameters to the SP is clarified. The theoretical treatment is essentially that of Lori-mer, Boterenbrood and Hermans3 ut has been extended to derive the general expression for the SP.