By Fred Witt, Milton Schwartz

ESTABLISHED methods for obtaining quantitative pole figures for flat sheets1"5 can be extended to apply to thin films on a substrate. The mode of scanning the sample is exactly the same as described in the references? but consideration is given to the fact that the scattered X-ray intensities are due to both the thin film and its substrate with appropriate attenuation factors. The purpose of this paper is to describe a method to obtain the scattered intensities from the film alone for subsequent pole-figure determinations. Fig. 1 shows the four possible general positions of the film (f) and its substrate (s) with respect to the incident X-ray beam (I,). In this paper it will be assumed that the plane of the sample is normal to the plane of the diffractometer. In the diagrams the line jV is the normal to the flat sample and the line P is the trace of the diffracting crystallographic planes in the plane of the diffractometer. The angle of tilt, a, is the positive acute angle measured from the line N to the line P; if this angle is measured clockwise then a is said to be in the positive a region; if this angle is measured counterclockwise then a is said to be in the negative a region. For the reflection cases, the total scattered intensity, at the proper Bragg angle for a particular set of planes, is due to that scattered by the film Vf) and that scattered by the substrate. The beam incident on

Jan 1, 1967

By J. C. Sarace, S. M. Sze, C. R. Crowell

Thin films of tungsten 077 n-type germanium, silicon, and gallium arsenide were obtained by reacting tungsten hexafluoride with the semiconductor surface in an argom atmosplrere at temperatures between 325° and 400° C. Capacity-voltage, current-iloltage, and photoelectric measurements were used to investigate the characteristics of the tungsten -semiconductor diodes thus Produced. The junctions are shown to he very close to ideal Schottky barlp/ers with barrier heights measured with respect to the Fermi energy of 0.18, 0.65, and 0.78 1.1 jar W-Ge, W-Si, and W-GaAs, respectively. The electrical properties of the W-Si interface show no deterioration when heated to 1000°C in dry forming gas for 5 min. A theoretical value of the Richardson constant, A, appropriate to the semiconductor-hand structure has been used in evaluating the current-voltage characteristics. ThE W-Si surface-barrier diode was initially proposed for investigation because the eutectic temperature with silicon (1400°C) is much higher than that in the Si-Au system 1370°C).1 This would permit more flexibility in heat treatment and possibly provide greater reliability at elevated temperatures. The lower work function of tungsten (4.54 ev)2 compared with that of gold (4.78 ev)3 also suggested that a lower barrier height would be obtained with tungsten and hence a lower forward bias and lower minority carrier injection ratio for a given current density. The investigation was extended to include the characterization of W-Ge md W-GaAs surface-barrier diodes. The tungsten films have been produced by reacting WF6 with germanium, silicon, and GaAs surfaces in an argon atmosphere at temperatures from 300° to 500°C.4 This process is a very satisfactory alternative to the relatively difficult process of evaporating tungsten films in vacuo. To ensure an adequate electrical characterization of the tungsten-semiconductor interface, three types of barrier-height measurements have been performed. The mutually consistent results obtained lead to the conclusion that the tungsten-semiconductor junctions are indeed of the Schottky type. EXPERIMENTAL PROCEDURE The apparatus used for producing tungsten films is shown schematically in Fig. 1. It consists of an argon carrier gas line to which metered amounts of tungsten hexafluoride can be rapidly added. The mixture passes through a heated reaction tube containing the semiconductor slices and is exhausted to a hood. The argon is purified by passage through a 6-in. column of titanium turnings maintained at 800°C. The tungsten hexafluoride dispensing arrangement was designed by V. C. Garbarini and W. R. Bracht.4 A measured amount of liquid tungsten hexafluoride is injected into the argon stream and vaporizes. The mixture passes through a sodium fluoride absorption cell to remove traces of hydrogen fluoride, then into the nickel reaction tube. The tube is 12 in. long with an inside diameter of 1/2 in. The center section is heated by a furnace of the self-supporting wire-filament type. It was chosen for its rapid heatup and cooling. The wall thickness is 10 mils except for a 3-in. hot zone which is 30 mils thick to reduce thermal gradients along the length. The samples to be coated are placed on a sapphire plate and centered in this section. The tungsten is deposited with the following sequential steps: the loaded reaction tube is flushed with argon at a rate of 500 cu cm per min and heated to 370°C. Then 0.45 g of liquid tungsten hexafluoride is injected into the argon stream. The samples are held at this temperature for 2 min. The tube and samples are then cooled to room temperature and the samples removed. Tungsten films were grown on (111) faces of silicon and germanium polished with Linde A abrasive and lightly etched with HF-HNO3. The GaAs surfaces were (100) faces chemically polished with a H2SO4-H2O2 solution. The films have typical sheet resistances of 0.2, 8, and 15 52/0 when grown on germanium, silicon, and GaAs, respectively. After the tungsten deposition, ohmic contacts were alloyed on the back surfaces of the wafers. Ohmic contacts to the germanium and silicon were obtained by alloying Au-Sb at 370°C, ohmic con-

Jan 1, 1965

By E. J. Ripling

A NY mechanism proposed to explain hydrogen embrittlement in titanium and its alloys must, of course, be consistent with the experimental data that characterize this embrittlement. Unfortunately, however, the mechanical behavior of hydrogen-bearing titanium, at least a-ß titanium, has not been unequivocally defined. Lenning, Craighead, and Jaffee have clearly shown that hydrogen cmbrittles a-titanium by elevating its transition temperature, probably as the result of the formation of titanium hydrides. Therefore, in these alloys, hydrogen acts like at least one other interstitial contaminant, namely, nitrogen.&apos; On the other hand, ß-titanium has been shown by these same investigators to tolerate very large amounts of hydrogen without suffering severe mechanical damage.2 Mixing these two phases, however, to form the most important class of commercial alloys, the a-ß alloys, again results in severe hydrogen embrittlement, although the mechanism by which the embrittlement is produced is not of the same type as that which causes brittleness in a alloys. Ductility damage due to hydrogen increases as the strain rate is reduced in a-ß alloys, while embrittlement in a alloys increases as the strain rate is increased, since the latter is a transition temperature behavior. Steel, like the a-ß alloys, becomes more hydrogen sensitive at slow strain rates, suggesting that the mechanism producing the embrittlement in these two metals is similar. Brown and Baldwin&apos; described the hydrogen-produced ductility depression in steel as a function of testing temperature and strain rate by defining the slope of the two surfaces that produced the depression in a three dimensional chart, Fig. 1. One of these surfaces was given by the equations (de/de)4 > 0 (de/dT) < 0 [1] while the other was defined by the pair of equations Surfaces of the type given by Eq. 1 are suggested in two ways. One is an embrittlement mechanism wherein the diffusion rate of hydrogen is competitive with the rate at which the material is being deformed, as suggested by the planar pressure theory of Zapffe and his co-workers.&apos; The other is the diffusion controlled extension of Orowan&apos;s theory on delayed fracture in glass by Petch and Stables.&apos;&apos; Surfaces of the type given by Eq. 2 are also compatible with a mechanism of pressure build up in voids, according to de Kazinczy,&apos; since the solubility of hydrogen in the metal increases with testing temperature so that as the temperature is raised, the pressure in the voids is reduced. Kotfila and Erbin recently presented some data on the dependence of ductility on testing temperature and strain rate for the a-ß 3 pet Mn complex alloy at four different hydrogen levels.H Although data were presented for only three testing temperatures at three different strain rates, their results indicated that surfaces of the types defined in Eqs. 1 and 2 are produced in the alloy when the hydrogen level is sufficiently high—200 and 300 ppm—Fig. 2. Jaffee and his co-workers presented data on a number of different a-ß alloys which indicated the existence of surfaces of the type described by Eq. 2, but the ductility recovery at low temperatures as given by Eq. 1 was not found." In an attempt to aid in crystallizing this description of the ductility dependence of hydrogen-bearing a-ß alloys, tests were conducted by the author on a-ß titanium 140A with three different hydrogen contents. The tensile properties of two as-received rods and one vacuum annealed rod* were obtained over a range of testing temperatures and strain rates as shown in Figs. 3 and 4. Hydrogen analyses were made by the Battelle Memorial Institute on four pieces of the rod whose properties are shown as solid circles in Fig. 4. The hydrogen content of these pieces, taken at widely spaced intervals within the rod, were 280, 270, 289, and 270 ppm, indicating that the hydrogen content within a single as-received rod was quite uniform. One of the broken test pieces whose properties are shown in Fig. 3 as solid circles was also analyzed, and found to have a hydrogen content of 310 ppm. The analyses obtained on two of the vacuum annealed specimens were 92 and 170 ppm.

Jan 1, 1957

By Strathmore R. B. Cooke

On the basis of experiments conducted on quartz using a bubble pick-up method, it was shown in an earlier paper1 that this mineral will preferentially adsorb hydrogen, calcium, or sodium ions, depending on the relative concentrations of those ions in the solution in which the quartz is immersed. For quartz particles ranging in size from 0.2 to 1 mm, it was demonstrated that the concentration of calcium in solution (assumed present as ions) necessary to completely activate quartz for flotation is given by the expression: Ca++ = [H+] X 106 + [Na+] X 10-3 In this expression, ionic concentrations are in mols per liter. It was further shown that the pick-up method is apparently more sensitive to changes in reagent concentration than the standard captive-bubble method, and that induction times are apparently much reduced. Since completing these earlier tests, a new type of cell has been constructed; this is shown in Fig 1 and 2. In Fig 1, A is a ground joint, B is a central tube reaching to within a few millimeters of the bottom of the cell, and C is a stopper which may be removed for reagent addition, and serves the further purpose of excluding carbon dioxide from the air during the test. The entire cell is constructed of Pyrex glass, and does not give the trouble experienced with the earlier cell, in which activating ions were released from the glass at high pH values. The only critical factor in the construction of the cell is the clearance between the central tube and the bottom of the cell. This clearance should be sufficiently small that the bubble can be pressed directly on the mineral grains lying on the bottom of the cell. In the pick-up tests to be described in this paper, the reagents used were all of C. P. grade, except the sodium oleate, which was Merck&apos;s "neutral powder." The quartz employed was water-clear vein quartz, sized on screens, cleaned with both hydrochloric acid and sodium hydroxide, and given a thorough final washing with distilled water. Experimental procedures were the same as described in the earlier paper. EFFECT OF SIZE OF QUARTZ ON PICK-UP To ascertain the effect of particle size on the adsorption of calcium ions, the quartz was sized from minus 14 plus 20 mesh through the intervening screen sizes to minus 270 mesh plus 400 mesh. Each size was thoroughly cleaned, and then tested in the cell at different calcium chloride and sodium hydroxide concentrations, and at a constant sodium oleate concentration of 20 mg per liter. All particles, within the size range given, exhibited complete pick-up within the curve expressed by the equation above. This presumably means, when the conditions imposed by the equation are satisfied, that this maximum is independent of particle size. However, it was found that the range through which partial particle pick-up occurred progressively broadened as particle size decreased. This is shown in Fig 3, in which curves B, C, and D show the limits at which pick-up just commences (as the pH is increased) for particles of minus 14 plus 28 mesh, minus 65 plus 100 mesh, and minus 270 plus 400 mesh size, respectively. These results indicate that for satisfactory activation, at any given pH, a lower calcium ion concentration is required for fine particles than for coarse particles. EFFECT OF HIGH ALKALINITY ON PICK-UP At calcium concentrations of between 1 and 10 mg per liter, and at high alka-linities, it was noticed that pick-up ceased as soon as calcium hydroxide commenced to precipitate. This effect was investigated at other calcium concentrations, with the same results. Solutions of calcium chloride, containing 105, 104, l03, and l02 mg of calcium per liter were made alkaline with sodium hydroxide until calcium hydroxide just started to precipitate, according to the following equation: CaCl² + NaOH -+ Ca(OH)2 + 2NaCl The beginning of precipitation was taken as that point at which either a faint opalescence appeared in the solution, or a Tyndall cone became ap-

Jan 1, 1950

By F. W. von Batchelder

The principles of microradiography and their application practically coincided with the discovery of X-rays. These principles were first used in the metallurgy field by Heycock and Neville1 in a study of the dendrite structure of alloys of Au-Na, Au-A1, Cu-A1, and Ag-A1. The method was introduced in the USA by clark2 after a visit to France. Scores of papers have been written, and a very complete bibliography on this subject was compiled by the Eastman Kodak company. Although a number of papers have discussed X-ray

Jan 1, 1959

By A. Manganwidjoyo, W. A. Wiebenga

The aim of this paper is to disclose some of the correlations between rock parameters, hidden in Wuerker&apos;s "Annotated Tables of Strength and Elastic Properties of Rocks," 1956. The empirical relations concern dry rocks of varying porosity. Curves and equations interrelating the specific gravity, compressive strength, bar velocity, and Poisson&apos;s ratio are presented. In 1956 Wuerker published his "Annotated Tables of Strength and Elastic Properties of Rock", in which various physical properties of rocks determined by different authorities, are tabulated systematically. The tables are primarily intended for use by mining-, quarrying- and ore-dressing engineers. Since the list of measured parameters for each type of rock includes properties such as — grain size, specific gravity, porosity, compressive strength, static elastic cons:ants (moduli of elasticity, rigidity, specific damping capacity and longitudinal bar velocity) the tables are also of considerable interest to the practical geophysicist. Correlations between rock parameters may enable geophysicists, geologists and civil engineers to transiate measurements from one parameter to another. Even if these translations are of limited accuracy, or valid only within certain specified ranges, they often serve a useful parpose. The aim of this paper is to disclose some of the correlations between rock parameters concealed in wuerker&apos;s Tables. Throughout this paper the following symbols and units are used unless otherwise stated: Sg is Specific gravity, the ratio of the density of a specimen to the density of water at 4°C. P is Porosity, in %, the ratio of the volume of voids in a specimen to its total volume. CS is Compressive strength in 1000 p.s.i., the stress under which a specimen will fracture when undergoing a standard compression test. V is Bar Velocity in kilo-feet/sec, the velocity of longitudinal seismic waves measured in a slender bar type specimen. Vc is Bulk or Constraint Velocity in kilo-feet/ sec, the velocity of longitudinal seismic waves measured in a very large specimen.+is Reciprocai bar velocity in millisecs/ft (1 millisec = 10-3 sec). cis Poisson&apos;s ratio, the ratio of the lateral to longitudinal strain of a body under longitudinal stress. CORRELATIONS Specific Gravity (Sg) vs. Porosity (P) Figure 1 is a diagram illustrating the relatiooship between specific gravity and porosity for approuirr~ately 70 samples of dry rocks. A curve fitted by estimation to this data yields the empirical formula: Sg =-0.0268P + 2.67 * 0.2 (1) Considering unit volume of a porogs specimen then

Jan 1, 1961

By J. Gurland

The strength variation ofWC-Co alloys with composition and particle spacing falls into two ranges. 1) Above a critical value of the mean free path, the strength follows a dispersion hardening relation; it is proportional to the volume fraction of WC and in-versely proportional to the particle size. 2) Below a critical value of the mean free path, the strength variation is based upon the Griffith criterion of fracture and is controlled by the case of crack propagation. The maximum strength is attained when the structure and load just satisfy the critical conditions for spontaneous crack propagation. THE relation between the strength and the structure of cemented carbides is of interest not only for its own sake but also for its contribution to the understanding of composite materials in general. The cemented carbides are essentially aggregates of a brittle carbide constituent and a ductile binder phase and, at certain structures of intermediate composition, the composite alloys attain strengths far higher than those of the separate constituents in bulk. It is this variation of strength with structure which will be discussed. The experimental procedures of sample preparation, mechanical testing, and quantitative metallo-graphic analysis have been described in Ref. 1. The reported strengths are the maximum fiber-stresses in bending calculated on the basis of completely elastic behavior. The plastic contribution to the over-all deformation is small and was neglected in the calculations (the elongation at fracture of the most ductile alloy, 50 pct WC-50 pct Co, is less than 0.5 pct).2 The pertinent structural parameters are: f, the volume fraction of tungsten carbide; p, the mean free path through the binder phase; the contiguity C, defined as the average fraction of surface area shared by a particle of wc with all neighboring particles of the same phase; and d, the average equivalent spherical diameter of the WC particles. The strength variation of WC-Co alloys with composition and particle spacing is shown in Fig. 1 and Table I, which are based partly on previously published data&apos; and partly on new experimental work which extends the range to higher values of the mean free path. Each data point represents the average of five samples. For a given composition, the transverse rupture strength reaches a maximum

Jan 1, 1963

By Wallace Ralston

The East Texas district includes the northeast 38 counties of the State of Texas. It still remains one of the most important oil-and-gas-producing areas of the United States, since it includes within its boundaries the large East Texas field. Other fields of importance are: Van, Rodessa, Talco, Cayuga, Long Lake and Sulphur Bluff. Production is from the Nacatoch, Blossom, and Woodbine of the upper Cretaceous and the Paluxy and Glen Rose of the lower Cretaceous. Of these, the Woodbine is the most important, since it is the producing horizon iri the East Texas field. Fields East Texas Field.—There were 2471 oil wells, 1 gas well and 84 failures completed during the year of 1936 in the East Texas field; that is, 1565 fewer than in the year of 1935. The total number of producing wells is now 22,031, of which 50 are temporarily shut down; 18,435 wells flowing their production; 3150 pumping; 293 on gas-lift, and 82 operated by other methods. This shows an increase of 1642 wells on artificial lift over Jan. 1, 1935. The average daily salt-water production is estimated at 42,700 bbl. from 2327 wells—an increase of 1201 wells over the year of 1935. The field is now drilled to an average density of one well to 5.85 acres. Average bottom-hole pressure has dropped from 1193 Ib. to 1168 lb., approximately 1 lb. drop for each 6,600,000 bbl. of oil produced. During the month of December 1936, the estimated daily average production of illegal oil had dropped from 20,500 bbl. in December 1935 to 7500 bbl. The commercial gas production is of minor importance in the East Texas field, and figures for the amount of gas taken from the field are not available at the present time. Talco Field, Titus and Franklin Counties.—The discovery well was drilled by Housh, Thompson et al. on the C. M. Carr tract and completed in March 1936, as a pumping well making 552 bbl. per day of 24&apos; gravity oil. This well was first completed at a total depth of 4208 ft., the top of the sand being 4190 ft. Later it was deepened to 4260 ft., which increased the production from 552 to 725 bbl. per day. This field is producing

Jan 1, 1937

By R. G. Davies

WeERTMANI has shown that the high temperature steady state creep rate, i, in lead and indium-base alloys obeys an equation of the form where AH is the activation energy, o the applied stress, n the stress exponent, and R and T have their usual meanings. He observed a variation in n from 4.5 for pure metals to 3 for concentrated alloys, which he interpreted as due to Change in creep mechanism from the climb of dislocations in pure metals to a micro-creep mechanism in the alloys. The Cottrell-Jaswon microcreep mechanism of the moving dislocation taking its impurity atmosphere with it was considered to be the most likely process, although short-range order and the segregation of solute atoms to a stacking fault will also give a stress exponent of 3. Steady state creep has been investigated in a Au - 27 at. pct Cu alloy at temperatures above 1/2 TIM where TIM the absolute melting temperature. As the oxidation resistance of this alloy is excellent all tests were carried out in air with a furnace built to give a temperature variation of less than 1°C along the 60 mm gage length. A lever-arm arrangement applied the stress with a load being adjusted between each creep test to maintain a constant stress. As each test produced less than 0.5 pct creep strain, the variation in stress during the test was negligible. The creep strain was measured by a transducer at the end of one of the alloy-steel grips, with the out of balance potential being finally recorded on a variable speed chart recorder. A typical creep curve is shown in Fig. 1. The results, Fig. 2, confirm that n is nearer to 3 than to 4.5; the creep mechanism could be any of those given above. The activation energy, AH, which is independent of stress, is consistent with a diffusion controlled process; the activation energies for the self-diffusion of gold and for the diffusion of gold into Copper are both -45 kcal per ml., There is now considerable evidence, that, when the steady state creep is dependent upon diffusion, irrespective of the actual creep mechanism, the activation energy is independent of the stress. The author would like to acknowledge the financial assistance provided by the International Atomic Energy Agency, Vienna, and the Argentine Atomic Energy Commission.

Jan 1, 1962

By John Nelson

AN OUTLINE survey of the economic outlook for the United States export trade in petroleum products resolves itself broadly into two general divisions; first, a consideration of our present position in this trade, and second, a discussion of the visible factors which promise to affect appreciable changes in the immediate future in that trade. The UNITED STATES PETROLEUM EXPORTS OF MAJOR PETROLEUM PRODUCTS 1925, 1926 and 1927 Gasoline, Naphtha, and Other Light Products 1925 1926 1927* Quantity (gal.) 1,286,787,796 1,784,154,802 1,851,494,190 Value $197,491,588 $263,199,938 $214,721,652 &apos;Illuminating Oil, Kerosene 1925 1926 1927* Quantity (gal.) 885;136,041 924,680,979 827,162,280 Value $84,699,724 $100,352,877 $80,358,082 Gas and Fuel Oil 1925 1926 I 1927 Quantity (gal.) 1,365,358,988 1,449,688,394 1,815,130,464 Value.... ? $49,040,024 $45,354,108. .. $50,343,031 Lubricating. Oil 1925... ....1926 .. 1927 Quantity .(gal.) 402,572,584 388,767,055 403,369,512 Value $90,596,671 $86,414,621 $88,926,815

Jan 1, 1928

By J. F. Elliott

PRESENT knowledge of the usual metallurgical slags indicates that they are, for the most part, rather complex in behavior and as yet there is no ready means for describing, in a simple manner, the behavior of any one of them. One of the best known slag systems is the iron oxide-silica-lime ternary which is the basic "solvent" in a number of important metallurgical refining operations, the basic open hearth being one of the most important. In this operation, the slag dissolves such components as sulphur, phosphorus, manganese oxide, and magnesia. Considerable study of this slag system and the behavior of these additions has been carried out in the past by a number of authors, as has been summarized in several critical reviews.&apos;,&apos;2 However, except for determination of the activity of iron oxide, only a limited amount of effort has been directed towards developing, from these data, an understanding of the general behavior of the basic solvent. Reported here are the results from a series of calculations based on data from the literature which permit a semiquantitative evaluation of the activities of iron oxide, silica, and lime (plus magnesia) in the ternary system at 1600°C. The preliminary results, which were reported briefly at a symposium held by AIME in 1953, have been revised and are completed. The steps in the calculation are as follows:* I—establish the activity curves and the curve of the excess molar free energy of mixing at 1600°C for each of the binary systems, 2—construct the activity surface of iron oxide for the ternary from the data on the binary systems and information available in the literature for the ternary area, 3—determine the surface of excess molar free energy of mixing for the ternary system from the activity surface of iron oxide and from the molar curves obtained for the binary system, and 4—differentiate the ternary surface of the molar excess free energy of mixing to obtain the ternary surfaces for the logarithm of the activity coefficients for silica and lime (log rslo, and log rc.~). Si0,-Fe,O: Schuhmann and Ensio have measured the activity of iron oxide in simple iron oxide-silica slags when in equilibrium with y iron. Their data recalculated to 1600°C are shown in Fig. 1. Also included is a point representing a measurement by Gokcen and Chipmana of the activity of iron oxide at 1600°C at the point of saturation with solid silica. For convenience and in accordance with other treatments,&apos; the calculations are based on the hypothetical component, FelO, which is obtained by converting all the analyzed iron in the slag to FeO. In spite of Schuhmann and Ensio&apos;s conclusion that the activity of iron oxide in the system does not vary with temperature over the experimental range of 1258" to 1407"C, the data are corrected to 1600°C assuming that temperature does have an effect. It was felt to be most reasonable to assume that the term log rr.10 is a linear function of the reciprocal of the temperature. Reyu has indicated that an effect of temperature on the activities in this system is to be expected from the Schuhmann and Ensio data. In essence, the correction consists of multiplying the experimental value of log rf,,o by the ratio of the experimental temperature in Kelvin to 1873°K. The magnitude of the correction is not large, being approximately 11.5 pct of the experimental value of log rve10. A very minor correction was necessary to compensate for the fact that the slags were in equilibrium with y iron in the experiment, while at steel-making temperatures they would be in equilibrium with liquid iron. Data for the correction were obtained from Darken and Gurry. The standard states established are pure liquid iron oxide (FelO) in equilibrium with pure liquid iron (with the appropriate amount of oxygen in solution) and pure liquid silica. The method of plotting in Fig. 1 is convenient for the calculation of the activity of liquid silica and permits a reasonable extrapolation for the activity of Fe,O in the ranges where no experimental data are available. The uncertainty in the extrapolation to infinity at one terminal where Nvelo = 1 for the usual Gibbs-Duhem integration is reduced considerably by this method. The region of two coexisting liquid phases is estimated to range from 1.8 to 41.7 mol pct Fe,O. The nature of the activity curve for the single-phase region indicates that the activity of iron oxide across the two-phase region is very close to 0.39. Computation of the function log ~F,,o/(1— NF,,o)&apos; for this region (dashed line) in conjunction with the curve through the adjusted experimental data indicate the best probable value of 0.382 for alPe,o in the two-phase area. The line from 0 to 0.018 Nf~~o is obtained by assuming that the component follows Henry&apos;s law. In this range, the value for log rveto is 2.59. Appropriate mathematical manipulation of the plotted linet yields the activity curves for the The curve AF", the excess molar free energy of mixing (actual minus ideal), as shown in Fig. 3 is also computed from Fig. 1. This curve is required for subsequent calculations. CaO-Fe,O: The phase diagram for the lime-iron oxide system when in equilibrium with liquid iron is not well known but there appears to be no intermediate compound present. This fact as well as the activity values for Fe,O extrapolated to the CaO-Fe,O binary from Taylor and Chipman&apos; tend to indicate somewhat negative deviations from ideality for the activity curves for the two components. Strong indication of this is evident in Fig. 1 where are plotted the points computed from the estimated activities of Fe,O for the binary system.&apos; It appears that the best line through the data is a horizontal straight line. Because of the general indication of the slight negative departure from ideality, the line is extrapolated horizontally to NF~,o = 0. It is con-

Jan 1, 1956

By W. G. Woolf, A. Y. Bethune

Filtration of hot (60°C) supersaturated zinc sulphate solution (sp gr 1.540) from slimy leach residues at the electrolytic zinc plant of Sullivan Mining Co., Kellogg, Idaho, is described. Separation of liquids and solids in the finished leach is by Burt filters modified to meet conditions of high-acid, high-density process for electrolytic zinc. Operating characteristics of the Burt filter on this pulp are presented.

Jan 5, 1950

By J. S. Blakemore, E. O. Hall

SERRATED yielding, commonly called the Portevin-Le Chatelier effect, is known to occur in a wide range of alloys where the moving dislocations are considered to be locked by the diffusion of solute atoms to them. From the work of Cottrell,1 an approximate relationship between strain rate, E, dislocation density, p , and solute diffusion coefficient, D, giving rise to serrated yielding is: e =Dp

Jan 1, 1969

By J. A. Clum, R. W. Heins, T. D. Tiemann

The use of Na-montmorillonite clay binders (Western Bentonite) in the pelletizing of iron ore concentrates is well established as is the idea that alternative binders must be found. 1-6 This note summarizes work done7 in evaluating a Wisconsin montmorillonite clay binder. The clay occurs in irregualr beds overlying the Prairie du Chien Dolomite and the St. Peters Sandstone near Hersey, St. Croix County.

Jan 1, 1978

Sec. 1. This Division shall be known as the Institute of Metals Division of the American Institute of Mining and Metallurgical Engineers. Sec. 2. The object of the Division shall be to furnish a medium of cooperation between those interested in the metallurgy, fabrication and uses of the nonferrous metals and their alloys; to represent the A. I. M. E. in so far as nonferrous metallurgy is concerned, within the rights given in A. I. M. E. By-law XI., Sec. 1, and not inconsistent with the Constitution and By-laws of the A. I. M. E.; to hold meetings for social intercourse and the discussion of nonferrous metallurgy; to stimulate the writing, presentation and discussion of papers of high quality on nonferrous metallurgy; to reject or accept such papers for presentation before meetings of the Division. Article II—MembeRs Sec. 1. Any Member, Associate, or Junior Associate of the A. I. M. E. in good standing may become a Member, Associate or Junior Associate of this Division upon registering in writing a desire so to do, but without additional dues. Sec. 2. But no one who has been continuously indebted to the A. I. M. E. or to this Division for more than three months shall be entitled to vote or to receive publications to which, as a member of the Division, he would be entitled. Article III—Funds Sec. 1. The expenditure of the funds reccived by the Division shall be authorized by the Executive Committee of the Division. Article IV—Meetings Sec. 1. The Division shall meet at the same time and place as the annual meeting of the A. I. M. E., and at such other times and places as may be determined by the Executive Committee subject to the approval of the Board of Directors of the A. I. M. E. Sec. 2. The annual business meeting for election of officers shall be held within a few days before or after the annual business meeting of the A. I. M. E. Sec. 3. At any meeting of the Division for which notice has been sent to the members of the Division through the regular mail at least one month in advance, a business meeting may be convened by order of the Executive Committee, and any routine business transacted not inconsistent with these By-laws or with the Constitution or By-laws of the A. I. M. E. Sec. 4. For the transaction of business, the presence of a quorum of not less than 25 members of the Division shall be necessary. Article V—Officers and Government Sec. 1. The officers of the Division shall consist of a Chairman, two Vice-chairInen, Secretary and Treasurer. The office of Secretary and Treasurer may be combined in one person, if desired by the Executive Committee. Sec. 2. The government of the affairs of the Division shall rest in an Executive Committee, in so far as is consistent with the By-laws of the Division and the Constitution and By-laws of the A. I. M. E. Institute of Metals Divisiori

Jan 1, 1931

By E. Maxwell, C. J. Bechtoldt, H. C. Vacher

IN the course of an investigation of the properties of metals at low temperature there was occasion to determine the constitution of four iridium-osmium alloys. There is very little information in the literature1 on the constitution of synthetic Ir-0s alloys. Zvyagintzev&apos; s has made a comprehensive study of different natural Ir-0s alloys and concludes that alloys containing more than 32 pct 0s have the close-packed hexagonal structure of osmium, whereas those containing less than 32 pct 0s have the face-centered cubic structure of iridium. The alloys studied in this work were prepared by the American Platinum Works, Newark, N. J., and were received in the form of fragments approximately 1.5 mm average diameter. The fragments had been obtained by crushing ingots made by fusing charges of iridium and osmium under an arc and air cooling. The ingots were not given a homogenizing heat treatment. Sample fragments Table I. Results of X-Roy Diffraction and Microscopic Examinations Phases Present as Determined by X-ray Diffraction Osmium Alloy Close- Iridium Face- Packed Centered Osmium, Iridium, Hexagonal Cubic Mlcro- WtPot Wt Pct Structure Structure scope 0 99.9 None Present 1 23.6 76.4 None Present 1 38.7 61.3 Present Present 2 59.4 40.6 Present Present 2 79.0 21.0 Present Not detected 2 99.9 0 Present None 1 Note: Chemical analyses of the iridium, osmium, and alloys were furnished by the American Platinum Works. of the iridium and osmium used in making the alloys also were included. Several fragments of each metal and alloy were examined microscopically and by X-ray diffraction. For the X-ray method the fragments were crushed further to pass a 270-mesh screen, then sealed in evacuated fused-silica tubes, heated to 1100°C for 18 hr, and allowed to cool in the furnace. Powder X-ray diffraction patterns were obtained from the annealed fragments by means of a Norelco camera having a diameter of 114 mm, and unfiltered cobaIt radiation. For the microscopic examination several fragments in the as-received condition were mounted in Melmac, (American Cyanamid Co.) and ground using the conventional series of abrasive papers. The polishing was done with 0-2 diamond abrasive on a Microcloth (Buehler Ltd.) lap, wet with xylene. After polishing, the surface was etched electrolytically in a 10 pct solution of chromic acid or in a 10 pct solution of potassium cyanide. Both reagents attacked the osmium-rich constituent, whereas the iridium constituent was attacked slightly by the chromic acid reagent and not noticeably by the potassium cyanide reagent. The results of the X-ray diffraction and microscopic examinations are summarized in Table I. Fig. 1 shows the microstructure of a 21 pct Ir-79 pct 0s alloy. The results indicate an appreciable solid-solu-bility range of osmium in iridium as was reported by Zvyagintzev.&apos; The solid-solubility range of iridium in osmium is more restricted, apparently less than 21 pct Ir. This implies a large range of composition in which two phases can coexist that was not reported by Zvyagintzev.

Jan 1, 1955

Now producing 35,000 tpd of coal from a deposit whose estimated reserves total 1.1 billion t, the Navajo mine of Utah International Inc. near Farmington, N. M., is the largest open-pit coal operation in the US. The history of this mine began in 1953 when, foreseeing the growing need for electrical power in the southwest, Utah International obtained a prospecting permit from the Navajo tribe. The lease, now covering 31,000 acres of the 12-million acre New Mexico-Utah-Arizona Navajo Indian reservation, was entered in 1957; in the next 3 years, Utah International negotiated with the State of New Mexico for water rights on the San Juan River, and finalized an agreement with the Arizona Public Service Co. to provide coal for the proposed Four Corners power-generating plant near Farmington.

Jan 10, 1974

By David Turnbull

IN isothermal recrystallization processes, new crystals generally grow into the matrix until they impinge upon other new crystals or an external surface, at constant linear rates G. Before impingement the perceptible course of growth can be described by the equation: 1 = G(t-7) C1I where, G = dl/dt, 1 is a crystal dimension measured in a constant direction, t is the time, and 7, the nucleation period, is a positive intercept on the time axis. Fig. 1 is a schematic representation of I as a function of time for a recrystallizing grain. G is dependent upon temperature, driving energy (strain or surface energy), relative grain and boundary orientations, but is generally independent of time. The frequency of nucleation, fi, (time" volume") can be defined by the equation: N = 1/fV [2] where ? is the mean nucleation period and V is the volume of the specimen that has not recrystallized. The kinetics of primary and secondary recrystallization generally can be described satisfactorily in terms of the parameters N and G only.&apos;-" After recrystallization is complete the average grain size 7 increases with time by "normal grain growth;" didt, the average rate of grain growth, is strongly time dependent and has not yet been precisely related to G for the motion of the individual grain boundaries constituting the system. It has been suggested4* " that the elementary act in grain boundary migration is closely related to the elementary act in grain boundary self-diffusion. Although the distance of atom movement in the two processes may be somewhat different, there is reason to expect that the activated states may be very similar, so that the free energy of activation for grain boundary migration should be of the same order of magnitude as for grain boundary self-diffusion. Therefore, it is desirable to develop a satisfactory basis for comparing data on self-diffusion and grain boundary migration and to make such comparisons where possible. Theory The formal theory of grain boundary migration rates is analogous to the theory for the rate of growth of crystals into supercooled liquids reviewed elsewhere 6-8. Boreliuss has shown that the latter theory describes, within the theoretical uncertainty, the growth of selenium crystals into supercooled liquid selenium. Motto and more recently Smolu-chowski" have derived expressions for the rate of boundary migration in recrystallization. The treatment to be presented is similar to Mott&apos;s excepting that the formalism of the absolute reaction rate theory will be used. The atomic mobility, M, in grain boundary migration is defined by: G = -M6p/6x where p is the chemical potential per atom and x is the coordinate measured in the direction of grain boundary movement. Let AF be the free energy difference per gram atom on the two sides of the boundary and k the thickness of the boundary. For RT>>AF the potential gradient across the boundary (6p/6x) is essentially linear and it follows that: SF/8x = - aF/N\ [4] where N is Avogadro&apos;s number. According to the Nernst-Einstein equation, M is related to a diffusion coefficient, Do, for matter transport in grain boundary migration by the equation: M = Da/kT [5] Substituting eqs 4 and 5 into eq 3 gives the basic relation between Do and G: G = DoaF/\RT [6] Do values may be calculated from experimental values of G from eq 6 and directly compared with the coefficient of self-diffusion within the crystal, DL, or the grain boundary self-diffusion coefficient D,. However, a more convenient, though equivalent, basis for comparing atomic mobility in grain boundary migration and self-diffusion is through the constants of the absolute reaction rate theory. According to this theory diffusion coefficients may be written:" D = k2(kT/h) exp [-AF,/RT] 171 aFa, the free energy of activation, is related to the measured energy of activation, Q, by the equation: AFA = Q - T aSx - RT [8] where aSa is the entropy of activation. Substituting eqs 8 and 7 into eq 6 gives: G = ek(kT/h) (aF/RT) exp [(AS,,)C/R] exp C-Qc/RTI C91 where the subscript G refers to boundary migration. The relationship between the driving free energy and the free energy of activation in boundary migration is indicated schematically in Fig. 2. Experience indicates that the variation of G with temperature can be described by: G= Go exp [- Qc/RT] [10] where Go and Qc are generally temperature independent over wide ranges of temperature. Comparison of eq 9 with eq 10 gives:

Jan 1, 1952

[ARTICLE I. NAME AND OBJECT Section 1. This Society shall be known as the Society of Petroleum Engineers of the American Institute of Mining, Metallurgical, and Petroleum Engineers, Inc. Section 2. The object of the Society of Petroleum Engineers shall be to furnish a medium of cooperation among those interested in the petroleum-natural gas industry an to promote the advancement of this branch of mineral technology through meetings to stimulate the preparation, reading, discussion and circulation of papers connected therewith. ARTICLE II. MEMBERS Section 1. Any person who is a member of AIME may become a member of this Society by the specified process. Section 2. Local organizations may be formed by the Society of Petroleum Engineers as subsidiary units, the membership of which shall be subject to and in accordance with the by-laws of the Institute.]

Jan 1, 1961

By N. S. Bornstein, M. A. DeCrescente

ThE nickel and cobalt base superalloys employed in gas turbine engines under some conditions&apos; oxidize at an accelerated rate when exposed at elevated temperatures to atmospheres containing minor quantities of sea salt. It is generally agreed by investigators in the field that the major steps comprising this phenomena of accelerated oxidation, also called hot corrosion or more commonly, sulfidation, are a) a slag composed primarily of Na2S04 is formed on turbine components, b) the protective oxide scale is rendered ineffectual, c) the slag reacts with. the substrate to form metal sulfides, and d) the substrate is rapidly oxidized. Sodium sulfate, a minor constituent of sea salt, is formed within the gas turbine engine from the reactions between NaC1, the major constituent of sea salt, and the oxides of sulfur.&apos; Depending upon concentration, engine compression ratio, and temperature, the Na2S04 will be present in the gaseous or condensed state. It has been determined that in order for sulfi-dation to occur the Na2S04 must be present in the condensed state.&apos; Although a number of sulfidation mechanisms have been postulated, there is no consistent explanation of oxide scale breakdown and subsequent catastrophic oxidation. Some investigators believe that after oxide scale breakdown, the Na2SO4 reacts with the substrate to form lower-valent sulfur compounds. The accelerated rate of oxidation is due to oxidation of a nickel-sulfide phase." Other investigators believe that sulfur from the fused salt reacts with chromium in the alloy to form chromium-rich sulfides; thereby depleting the alloy of an element which imparts oxidation resistance.3,4 This publication will demonstrate that the accelerated rate of oxidation associated with sul-fidation is due to interactions between Na20, a con-stituent of NazSO.,, ancl the substrate. The aim of this study was to separate and determine the effect of compounds of sulfur and sodium on the oxidation kinetics of various nickel-base superalloys, in order to elucidate the sulfidation mechanism. The work reported herein is sponsored in part by the Naval Ship and Development Center-Investigation of EXPERIMENTAL PROCEDURE The nickel base alloys B-1900, U-700, and Waspaloy were chosen for this study. The nominal compositions are presented in Table I. The specimens, approximately 1 in. by 1 in. by 0.060 in. received in the "as cast" condition were polished with 600 grit emery, washed, and rinsed with acetone immediately prior to oxidation experiments. Sulfida-tion attack was duplicated in the laboratory by apply-ing a saturated aqueous solution of Na2S04 onto the al loy substrate and subsequently exposing the specimens in oxygen at elevated temperature. The method of Na2S04 application is described elsewhere in detail.6 In another set of experiments the affected substrate microstructure associated with sulfidation was reproduced free of the normal oxide scale, by reacting and diffusing elemental sulfur into the alloy. The experimental procedure is also described elsewhere in detail. All oxidation studies were performed using an Ainsworth thermobalance type RV-AU-1, which is readable to 0.01 mg and is reproducible to ±0.03 mg. The specimens, introduced into a heated furnace, were exposed in the temperature range 800" to 1000°C

Jan 1, 1970