IRON-COBALT alloys in the range of 35-50 pct cobalt are of interest in the electrical industry because they possess the highest magnetic saturation of any magnetic material known.1,2 The magnetic saturation induction of the 35 pct alloy is 24,200 gausses, compared to 21,600 for pure iron (Fig I). This difference is significant in electrical apparatus, where weight or space is at a premium. Saturation values higher than that for iron can be attained up to about 70 pct Co but economics restrict the use to as low a cobalt content as possible without sacrifice of saturation. Fig 2 shows the iron-cobalt equilibrium diagram. Up to the present time, two factors have retarded the use of iron-cobalt alloys in the electrical industry for magnetic purposes.† One is the high cost of cobalt ($1.50 per pound) and the other is the inherent brittleness of the binary iron-cobalt alloys. Straight iron-cobalt alloys up to 25 pct cobalt are ductile and easy to process to thin sheet or strip by conventional methods of hot and cold rolling, but the alloys containing higher percentages of cobalt, including those for which the saturation magnetization is a maximum (35 to 40 pct), are increasingly brittle with increasing cobalt, at least up to 50 pct, and are consequently difficult to process, either hot or cold. Work by White and Wah13 indicated that iron-cobalt alloys could be made ductile by alloying with vanadium, and after quenching the alloys (vanadium up to about 4 pct) were found to be cold rollable to very thin gauges. With this as a background, we resumed our work on these alloys with the objective of developing methods for economical commercial production of wide strip. For this purpose we have concentrated on the 35 pct alloy in order to obtain the highest possible saturation value. Experiments were carried out on many alloy additions to the iron-cobalt alloys and on the response of these compositions to heat treatments. This work finally culminated in a commercially producible iron-cobalt alloy which has been named Hiperco. * MATERIALS STUDIED AND PROCEDURE Binary alloys of iron and cobalt in the range of 35 pct cobalt are difficult to hot work (by forging or rolling) without such additions as C, Mn, Si, V, Cr, Mo, W or perhaps others. Another beneficial effect of such additions is that they in-crease to a greater or less extent the strangely low electrical resistivity of these alloys (about 10 microohms per cm3

Jan 1, 1947

By J. B. Cohen

In an investigation of the microstructure of shock-loaded metal specimens1 C. S. Smith found that there was little distortion of grain boundaries or change in external dimensions, although the hardness corresponded to that produced by severe rolling. Furthermore, the hardness of individual grains was independent of the deformation structures present; grains with no markings were as hard as those heavily populated with markings. These markings which resemble twins do not appear in copper until high shock-loads of the order of 200 kb are applied. It appears that due to the high velocity of a shock wave and its sharp front, heavy deformation takes place on a submicroscopic scale. In this work an attempt was made to examine this deformation, particularly at a load below which macroecopic markings appear. The broadening of 200 and 400 diffraction peaks was examined from the face of a poly crystalline sample normal to the direction of the shock wave. These peaks were chosen because the elastic constants in copper are such that residual strains would be greatest in the <100> directions; hence, the strain-broadening contribution to these peaks would be large in comparison to other sets. Also the broadening due to stacking faults and microtwins would be greatest with this set.2 A complete Fourier analysis of these peaks was made, as described by warren,&apos; using the Stokes correction with peaks from an annealed sample.3 With the aid of the U. S. Army Ordnance Corps EDVAC computer and a curve matching program, sixty sine and sixty cosine coefficients were obtained for each peak. The last of these was about 1.5 pct or less of the largest coefficient, indicating good representation. Transverse sections from a 1.5 in. rod of as-drawn electrolytic tough-pitch copper were reduced in cross-sectional area about 50 pct by cross rolling. Disks 1.5 in. in diam were recrystallized at 275 °C for 30 min and then at 300°C for the same time. The faces were polished and deeply etched in nitric acid to remove 25 mils. The grain size was 0.02 mm. Laue back-reflection patterns indicated the sample was well recrystallized. The two diffraction peaks from this sample were recorded on a Norelco diffractometer using filtered copper radiation. Peak intensities were kept less than 600 cps to assure linearity of the counter and circuitry. This sample was then placed between two rods of the same material and diameter. The top rod was 2.25 in. long and the bottom rod 1 in. long. (In

Jan 1, 1961

By V. J. Sikora, T. S. Hutchinson

This paper presents a method for making a water-rlrive ana1gsis without prior knowledge of aquifer geometry and uniformity using a standard desk calculator. Although it is necessary to know the initial oil in place to use this method, this is a minor limitation to the scope of (he method since in most reservoirs it is possible to obtain reasonably accurate volumetric oil-in-place estimates. An equation is developed which relates pressure at the water-oil contact to the water influx rate as a function of time by a factor called the resistance function. The resistance function introduces the composite effect of the aquifer geometry and flow resistance disrribution. It is pointed out that the characteristic shape of this function makes it possible to start with on approximation of the function and successively improve the approximation until the correct resistance function curve is obtained. In this fashion water-drive estimates can be made without the limitation of assuming simplifed aquifer shapes and flow distributions. This is the novel feature of this development. Methods are given for extrapolating the final curve to calculate future aquifer behavior. Equations are developed for adjusting the pressures and water influx rates where it appears that possible errors in these quantities make it difficult or impossible to obtain a useuble resistance function curve without this adjustment. Application of the pressure build-up analysis techiiique to estimate. some of the aquifer properties is also presented INTRODUCTION A great many oil pools are the result of oil accumulation in some type of trap in an otherwise large and continuous porous stratum. The void space of this stratum outside of the oil pool itself is filled with water or brine. In analyzing performance of the oil pool surrounded by this water aquifer, it is quite necessary. in most cases, to include behavior of the water. When the pressure at any point in a fluid system is lowered, such as by opening a well in an oil sand, fluids in the immediate neighborhood of this point will begin flowing towards this lower pressure sink. As pressure in this area drops due to flow towards the sink, fluids from farther out will start to flow towards the lower pressure. As more and more fluid is removed from the system, the distance from the sink or well within which flow is occurring will continually increase; that is, thc region of disturbance will grow. If some rigid boundary such as a fault is reached by the disturbance, this area will cease to grow; but if some movable boundary is reached, such as a water-oil contact, the area will grow on out into the water, although rate of growth may and almost always does change. The relation between amount of pressure drop and amount of fluid flowing at any point and at any time in an aquifer depends on such factors as compressibility and viscosity of the fluids, the porosity and permeability of the rock, geometry of the whole system and withdrawal rate or pressure drop. With these factors known, it is theoretically possible to calculate the pressure-flow behavior of the system, However, in practice true solutions to the problem are next to impossible due to complexity of reservoir systems. A number of approximate methods of solution have been developed based on various simplifying assumptions. One frequent assumption is that the water-oil contact can be located and equations defining oil reservoir and aquifer solved separately by assigning values to various parameters so as to match past pressure and production history. Usually the properties of the aquifer are not known, since few, if any, wells are drilled through the aquifer; but the water influx and the pressure at the reservoir boundary are known over some time. If it can now be assumed that the aquifer is circular, pie-shaped, or linear, and that it has uniform properties, it is possible to fit a theoretical dimensionless curve to the past aquifer performance history and therefore calculate future water drive. These theoretical curves are available in the literature,1,2,3 Of course, the assumption of uniform aquifer properties is almost always somewhat in error. Fortunately, however, moderate variations from the average have little effect on behavior of the system; and, hence, the best fit of a theoretical curve is frequently satisfactory. In other cases variations in aquifer properties and geometry are large enough that none of the available theoretical curves will give an acceptable fit of the data. In these cases, methods of fitting the data with various electrical analyzers have been developed.1,2&apos; It is the purpose of this paper to present an approach

By Arthur F. Taggart

The major portion of the work described in this paper was performed by R. W. Young, † a graduate student in the department of Mining and Metallurgy, Sheffield Scientific School, Yale University, working under a cooperative agreement between the Hardinge Conical Mill Co., the Sheffield Scientific School, and himself. Since this cooperative scheme is at present in effect in the case of a considerable number of other students in the department and since it is the hope of the school that the privilege thus extended may be utilized even more freely in the future by mining and manufacturing companies, it may not be amiss at this point to give a summary of the general plan. Briefly it is as follows: A graduate student, whose undergraduate work in this or other universities shows promise of ability to handle research work, is chosen by conference between the company and instructor involved. The aim of the company in the agreement then entered into is to obtain the solution of one or more of the technical problems with which it may be confronted, or, at the end of 1 or 2 years, to obtain as an employee a man especially trained in its work. As a means to accomplish one or both of these ends, the company furnishes the machine, apparatus, or material to be tested and pays the student during his graduate work a small salary, usually just sufficient to cover his living expenses, tuition and fees. The aim of the student is special training along a line in which he is particularly interested, the attainment of his advanced degree, and the chance to show to his future employer ability to handle such problems as may be presented to him. In return for the financial aid which he receives he agrees to devote at least half of his working time to the special problem submitted by his company. The other half is devoted to study of the collateral subjects required by the department for the granting of the degree which the student seeks. The student further agrees to enter the employ of the company in question at a wage not greater than that paid in like positions to recent graduates not specially trained and to remain with his employer at such wage for at east 1 year. If the student is to obtain a degree, the special work forming the basis of his investigation must be such as will involve real research and not mere routine manipulation. The subject is chosen by conference between the three parties to the agreement. The work is carried on under the direct supervision of the instructor involved. The school furnishes the general laboratory and library equipment essential to the pursuit of any extended investigation. In

Jan 1, 1918

By W. F. Carew, F. A. Crossley

Tensile, creep-rupture, and stability tests were employed to evaluate the effect of a-strengthening and ß-complexing additions on the base composition Ti-6Al-3Mo. The ultimate objective was to produce an alloy of greater strength than the Ti-7A1-3Mo alloy. Strengthening of a was accomplished by additions of 2 and 4 pct Ge, 4 pct Sn, 4 pct Zr, and 2 pct Sn-2 pct Zr. Making the ß more complex while keeping the total of ß-stabilizing additions constant at 3 pct resulted in higher tensile strengths but lower creep and rwpture strengths, especially at 1000°F. None of the more complex versions of the base alloy offers greater promise than the Ti-7A1-3Mo alloy. However, some improvement in the strength of the latter may follow from additions of zirconium perhaps up to 4 pct. PREVIOUS work directed at the development of titanium-base alloys with: 1) minimum room-temperature tensile elongation of 10 pct in 1 in., 2) high creep resistance at elevated temperature, and 3) the ability to retain original room temperature tensile ductility following exposure to creep conditions at elevated temperatures, demonstrated Ti-Al-Mo ternary compositions in the range 5 to 7 pct Al-3 to 6 pct Mo to be the most promising. Of this group the Ti-7Al-3Mo alloy was the strongest.&apos;-= The objective of the present work was to determine if alloys of this type could be further strengthened by making additions which dissolve preferentially in the a-phase and by making the ß-phase more complex. For this study the base composition Ti-6Al-3Mo was selected rather than Ti-7Al-3Mo in order to minimize the possibility that in a more complex alloy with a-strengthening additions, low ductility might obscure the strength contribution. The metals

Jan 1, 1959

By A. S. Learoyd

The Anthracite Division, Bureau of Distribution, of the United atates Fuel Administration, came into existence about Oct. 20, 1917. There had been no definite policy determined upon and the distribution had been carried out by the producers and distributors of this fuel as under normal conditions. The domestic sizes had been shipped from the beginning of the coal year on Apr. 1 in about their usual proportions to the various sections of the anthracite consuming territory of this country, which, in a general way, extended as far west as Nebraska and Montana, and in the south along the Atlantic seaboard to Florida. With the advent of cold weather, about the middle of November, acute shortages commenced to develop all over the northeastern section of the country, due to largely increased demand by the public in general, to enormously increased population in centers where industrial war activity was concentrated, and by the needs of the war industries themselves. Commencing with the early part of December, this demand was aggravated by extreme low temperatures and heavy snow; and the production decreased for the same reasons. From that date until the change in the weather, about the latter part of February, it was simply a question of getting coal into communities as emergencies occurred, to take care of individual cases. No definite plan of distribution could be followed. The coal mined between Apr. 1 and Nov. 1 had been distributed as mined and therefore only current production was available for distribution. The Anthracite Division, during this period, consisted of a Director, two assistants, together with an office force .of seven or eight clerks and stenographers. The trying experiences of the winter of 1917-18 had, however, shown a ready willingness on the part of the anthracite operators and distributors to cooperate in every way with the United States Fuel Administration. It was realized that if a definite and comprehensive plan of distribution could be formulated to become effective Apr. 1, 1918, determined on the actual needs of each state and community, the producers

Jan 1, 1920

By H. l. Burghoff, D. E. Lawson

The presence of tellurium in copper and, by inference, in copper alloys, has been considered seriously detrimental and has been avoided. In particular, very small amounts of tellurium have been found to produce red-shortness, although the effects on cold-working and ordinary physical and mechanical properties have not been known so definitely. References in the literature are few, but as long ago as 1881, Eglestonl reported that 0.083 per cent tellurium in fire-refined copper rendered the copper red-short and therefore worthless for hot-rolling. In hot-rolling copper cakes containing this amount of tellurium, he found that fine cracks appeared in the cakes on the first pass through the rolls, the cracks opening further in successive passes. When cold, the metal was said to be tough and malleable. A few years ago, during the course of an investigation in our laboratory on copper-base alloys, it was found that tellurium-bearing alloys could be machined much more freely than similar alloys not containing tellurium. The study was pursued further in this direction, and considerable data were obtained, which indicated that certain tellurium-bearing alloys might have properties of commercial interest. The work eventually led to patent protection,2 a wide range of tellurium-bearing copper-base alloys being covered. This article presents results obtained on the effect of tellurium on the mechanical properties of three copper-base alloys: commercial bronze (90 Cu, 10 Zn), 1.5 per cent tin bronze (98.5 Cu, 1.5 Sn), and silicon bronze (96 Cu, 3Si, 1 Zn). Several alloys were cast in each series, with tellurium content ranging from 0 up to about 1 per cent. The alloys were melted under charcoal in a clay-graphite crucible, using a high-frequency induction furnace, and were cast without undue difficulty in rod form, 15/8 in. in diameter. Charges for the zinc and tin series were made up from the following materials: cathode copper, electrolytic zinc, tin, and tellurium in slab

Jan 1, 1938

By H. l. Burghoff, D. E. Lawson

The presence of tellurium in copper and, by inference, in copper alloys, has been considered seriously detrimental and has been avoided. In particular, very small amounts of tellurium have been found to produce red-shortness, although the effects on cold-working and ordinary physical and mechanical properties have not been known so definitely. References in the literature are few, but as long ago as 1881, Eglestonl reported that 0.083 per cent tellurium in fire-refined copper rendered the copper red-short and therefore worthless for hot-rolling. In hot-rolling copper cakes containing this amount of tellurium, he found that fine cracks appeared in the cakes on the first pass through the rolls, the cracks opening further in successive passes. When cold, the metal was said to be tough and malleable. A few years ago, during the course of an investigation in our laboratory on copper-base alloys, it was found that tellurium-bearing alloys could be machined much more freely than similar alloys not containing tellurium. The study was pursued further in this direction, and considerable data were obtained, which indicated that certain tellurium-bearing alloys might have properties of commercial interest. The work eventually led to patent protection,2 a wide range of tellurium-bearing copper-base alloys being covered. This article presents results obtained on the effect of tellurium on the mechanical properties of three copper-base alloys: commercial bronze (90 Cu, 10 Zn), 1.5 per cent tin bronze (98.5 Cu, 1.5 Sn), and silicon bronze (96 Cu, 3Si, 1 Zn). Several alloys were cast in each series, with tellurium content ranging from 0 up to about 1 per cent. The alloys were melted under charcoal in a clay-graphite crucible, using a high-frequency induction furnace, and were cast without undue difficulty in rod form, 15/8 in. in diameter. Charges for the zinc and tin series were made up from the following materials: cathode copper, electrolytic zinc, tin, and tellurium in slab

Jan 1, 1938

By J. B. Cheatham

An analysis of indexing is given for an idealized plastic rock. Indexing refers to chipping from a bit tooth to a previously formed crater. A method is indicated for computing the dependence of chip size and shape as well as force on the tooth for various tooth shapes as a function of crater configuration and distance to the previous crater. Pressure on the tooth is found to vary with depth of penetration after a critical depth has been reached. Damp sand model experiments indicate that simple solutions using linear and logarithmic spiral slip-line fields for Coulomb plastic materials give reasonable approximations to the failure patterns. Both idealized roller cone bits and fixed blade or drag bits are considered, and methods are presented for approximating the force on the bit and the chip volume when the rock is subjected to sufficiently high pressure to behave plastically. One of the primary objectives of drilling research investigations is to develop theoretical equations which can be used to predict the behavior of rock under drilling loading conditions. Since rocks usually fail in a brittle manner at atmospheric conditions, much current research is directed to studies of the brittle failure of rock under the action of drilling too1s. 1,2 The results of triaxial test on rocks indicate that both rock strength and ductility increase at high confining pressures.3 Recent results from single bit-tooth indentation experiments on dry rocks indicate that the transition from brittle to ductile failure under a bit tooth can occur at pressures sufficiently low to be of interest in oil well drilling.4 Single bit tooth experiments and analyses are not directly applicable to the drilling process since one of the important facets in drilling is the interaction between a bit-tooth and the previously formed crater. This interaction is referred to as indexing.&apos; The purpose of the present paper is to indicate how plasticity theory can be applied to the analysis of indexing for plastic rock. Drag bit or fixed-blade drilling is considered and a discussion is given of the drilling action of an idealized roller cone bit. Results of simple experimental studies using a damp sand model are given as a method of visualizing the failure patterns in rocks under high confining pressures. These results are compared with plasticity theory using simple solutions based on linear and logarithmic spiral slip-lines. Discontinuous stress fields are proposed for drag bit drilling based upon the soil mechanics analysis of Shields. SINGLE BIT TOOTH RESULTS Single bit tooth indentation experiments using dry rocks under pressures from 0 to 5000 psi have indicated a correlation between the shape of a force-displacement curve and the nature of the rock failure beneath the tool.4 Continuous linear curves are in-

Jan 1, 1965

By P. Wynblatt, J. E. Dorn

The effect of strain rate, temperature, and interstitial impurity concentration on the flow stress was investigated in a poly crystalline Fe-2 pct Mn alloy. The temperature dependence of the flow stress was found to be independent of the interstitial impurity concentration, removal of interstitials merely decreasing the atherma1 stress level. Below 160%, the large temperature dependence of the flow stress was interpreted in terms of the Dorn-Rajnak theory of the Peierls mechanism of plastic deformation. Above 160"K, some other thermally activated intrinsic meckanisln seems to be operating. The strong temperature dependence of the flow stress of bcc iron at low temperatures has been studied by numerous investigators and interpreted in terms of several different thermally activated dislocation mechanisms. The following mechanisms have been proposed: a) interaction of dislocations with interstitial impurity atoms1 or with solute atoms in general; b) interaction of dislocations with clusters of impurity atoms;3 c) resistance to the motion of dislocations due to jogs on screw dislocations;* d) resistance to the motion of dislocations due to the Snoeck effect;&apos; and e) interaction of dislocations with the intrinsic resistance of the bcc lattice or Peierls "hills". In previous work: it was found that the plastic behavior of polycrystalline iron containing 2 wt pct Mn (and 100 ppm C + N) is in good agreement with predictions based on the Peierls mechanismlo from 77" to 160°K whereas from 160" to about 370°K another as yet unidentified thermally activated mechanism is operative. The purpose of the present investigation was to determine the effect of interstitial impurities on the temperature dependence of the flow stress, by purifying the previously investigated alloy with respect to interstitial impurities. The investigation revealed that removal of the interstitial impurities to a level that eliminated Cottrell locking and the Portevin-LeChatelier effect (i.e., serrations in the stress-strain curve due to dynamic strain aging) affects neither the strong temperature dependence of the flow stress at low temperatures nor the general characteristics of the higher-temperature behavior. Such purification, however, lowered the athermal yield stress. I) EXPERIMENTAL PROCEDURE AND RESULTS The material used in this investigation consisted of an Fe-2 wt pct Mn alloy having the following additional elements present: 0.004 pct C, 0.006 pct N, 0.05 pct 0, 0.004 pct S, 0.003 pct P, and 0.001 pct Si. This was the same material as that studied in the previous investigation and will henceforth be referred to as the "impure material". The as received -jr by 2 in. hot-rolled bars were cold-rolled to 0.08-in. thickness, recrys-tallized under argon for 30 min at 80O0C, and further cold-rolled to 0.053-in. thickness. Flat tensile specimens 3 in. wide having a 1.625-in.-long gage section were machined from the sheet and then purified. The first stage of purification consisted of holding the specimens at 850°C for 24 hr in a stream of hydrogen saturated with water vapor at room temperature. Material prepared in this fashion will subsequently be referred to as "wet hydrogen purified material". It has been estimated that this type of treatment reduces the carbon content of iron to less than 5 ppm.&apos; The second stage of purification consisted of holding the specimens in a closed system through which hydrogen was circulated past the heated specimens as well as a zirconium hydride getter. The specimens were held at 850°C and the getter at 800°C. The process was continued for 212 hr. The starting material for this process was wet hydrogen purified material. Material prepared in this manner will be referred to as "ZrHz purified material". The technique used was substantially the same as that described by Stein et al.&apos; who have shown that the carbon level at the end of the process is reduced to about 5 parts per billion. The mean grain size of the three materials was found to be -60 C( for the impure material and -160p for the wet hydrogen and ZrHz purified materials. All tensile testing was carried out on an Instron Testing Machine either in controlled-temperature baths or at fixed-point baths such as boiling liquid nitrogen, and so forth. When fixed points were used the temperature was kept constant to better than *1°C whereas in all other tests the temperature variation was less than *2°C. Test of Purity. It was not possible to determine the purity achieved at each stage of the purification because the resulting level of interstitial impurities was near or below the limit of sensitivity of standard analytical techniques. It was possible, however, to obtain a qualitative measure of the extent of purification from the appearance of the stress-strain curves for the three materials. Fig. 1 shows the stress-strain curves for the three different materials tested at 300°K. It can be seen that the effect of wet hydrogen

Jan 1, 1967

By Edward Martinez

The reactions occurring in the copper segregation process were studied by heating mixtures of chryso-colla, salt, and a reducing agent. The techniques used in this investigation were differential thermal analysis (DTA) and thermal gravimetric analysis (TGA). The initial chloridizing of the oxide copper occurs below 500°C and cupric chloride may be the compound formed. Volatilization and reduction of the copper chloride take place above 550°C, although these reactions do occur to some extent below 550°C. A difference in the distribution of the metallic copper in the reducing agent was found when sodium chloride was used compared to magnesium or calcium chloride. Segregation was obtained with mixtures of cupric oxide, salt, and charcoal with no quartz or silicate present. Preliminary tests indicate that segregation may occur even in the absence of water vapor. The DTA and TGA techniques were found to be of great value in studying these reactions. The copper segregation process is a method for treating oxide copper ores. The ore is heated, most commonly in a kiln, with a reducing agent and a halide salt, generally sodium chloride, to approximately 700°-750°C and held for 30 to 60 min. The addition of the salt results in the migration and reduction of the oxide copper to metallic copper on the surface of the reducing agent rather than in the original mineral structure. The metallic copper can then be recovered by a subsequent leaching or flotation step.1-4 Experimental work in 1923 on oxide copper ores from the Sagasca mines in Chile led to the discovery of the reduction process. It was found that during the reduction of the copper mineral with coal, at about 700°C, the copper migrated to the surface of the coal instead of remaining disseminated in the ore. The unusual behavior of the copper, which caused it to migrate from the ore particles to the coal, was traced to the presence of a small quantity of sodium chloride occurring in the ore. Further experiments with oxide copper ores proved that the presence of a halide, either occurring naturally or admixed with the ore, caused the copper to migrate from the ore particles and to segregate in the charge. The ratio of salt to reducing agent may vary somewhat, but in general 0.5% to 1.5% sodium chloride and 0.5% to 1.0% coal or coke have been mixed with the ore. Less than stoichiometric amounts of salt are required to convert all the oxide copper to a chloride, so that a cycle of reactions appears to be occurring. Several investigations reported in the literature have proposed reactions to explain the mechanism of the process.5-10 There appears to be general agreement that water is necessary for the reactions to occur; that once the sodium chloride reacts with silica or silicates in the ore, the hydrochloric acid formed will convert the cupric oxide in the mineral structure to cuprous chloride. However, there appears to be a conflict of opinion on the reactions involved in the reduction of the cuprous chloride to metallic copper on the surface of the carbon. Rey has indicated that salt, water vapor, and

Jan 1, 1968

By V. A. Phillips, M. Safdar Ali

The tensile properties of Cu-0.20 pct Al, Cu-0.45 pct Mg, Cu-0.27 pct Cr, and Cu-0.22 pct Be solid-solution alloys were studied at -196°, 18°, 2509 and 500°C on wires internally oxidized at 900°and 1000°C. Internal oxidation produced marked increases in yield strength relative to pure copper, particularly at low temperature. The yield strength decreased with increase in temperature to a much greater extent than predicted by current theories of dispersion hardening. The strengthening effect of internal oxidation persisted throughout the entire stress-strain curve, but since a marked loss of ductility occurred at all test temperatures, only modest increases in tensile strength were realized. INTERNAL oxidation involves the preferential oxidation of a baser solute in a relatively noble solvent by diffusion of oxygen into the solid. Since the process is diffusion controlled, it is expedient to carry it out at a high temperature often approaching the melting point. The amount of solute is limited and the oxidation conditions adjusted so that oxygen diffuses inwards to meet the solute causing reaction to progress inwards and form subscale instead of only sur face scale. The reaction can be made to occur throughout the thickness of thin material producing a fine dispersion of oxide inside the metal. C. S. Smith1"3 appears to have been the first to recognize the true nature of the process of internal oxidation. Although extensive kinetic and metal-lographic studies followed by Rhines and coworkers,4-5 Chaston7 andMeijering and Druyvesteyn8 working independently were the first to report hardening effects due to internal oxidation. These results prompted detailed studies of the effects of internal oxidation on the hardness, tensile, creep, and fatigue properties of a number of alloys by G. C. Smith and coworkers9-12 in England, on hardness by Gottardi13 in Italy, and on hardness and tensile properties by wood14 in the U.S.A. Publications dealing with other aspects of internal oxidation will not be reviewed here. Internal oxidation of solutes having a high affinity for oxygen provides a means of obtaining very fine dispersions stable in a suitable atmosphere at temperatures well above those at which most age harden ing precipitates coalesce. The process therefore offers a method of producing thin sheet and wire of possibly outstanding creep resistance. The size limitation might be overcome by internally oxidizing porous powder compacts made from alloy powder before final sintering. PREPARATION OF ALLOYS The alloy ingots, which were approximately 5 1/2 in. long by 1 in. diam, were made up in a high-frequency furnace, using as raw materials OFHC copper, 99.99 + pct Al, high-purity magnesium, and master alloys of Cu-4.19 pct Be and Cu-10 pct Cr. The alloys containing aluminum and magnesium were melted ii closed high-purity graphite crucibles and solidified in the crucible which was lowered partly Out of the coil to give a hot-top effect. The alloys containing beryllium and chromium were made by melting in vacuo in alumina-lined sillimanite crucibles. The magnesium, chromium, and beryllium

Jan 1, 1960

By E. W. Hart, W. R. Hibbard

The room temperature flow characteristics of a series of Cu-Cr alloys are found to be related to the amount and characteristics of the chromium-rich precipitate. The results are consistent with the theory of Fisher, Hart, and Pry, which considers the trapping to dislocation loops around precipitate particles. THE use of dispersed phases for hardening metals, particularly high temperature alloys, has been practiced for several years. Current theories describing the effects of dispersions on the basis of dislocation theory have been proposed by Mott and Nabarro.l-4 rowan," and Fisher, Hart, and Pry.8 These theories recently have been discussed by Hart,&apos; who pointed out that the experimental data available for comparison with theoretical calculations for overaged alloys are confined to studies by Gensamer, Pearsall, Pellini, and Low,8 Shaw, Sher-by, Starr, and Dorn,9 and some hitherto unpublished data on Cu-Cr alloys which will be described herein. Certain difficulties were associated with the interpretation of the first two studies. Gensamer, Pearsall, Pellini, and Low were concerned principally with interparticle spacing and did not document particle sizes. Shaw, Sherby, Starr, and Dorn included all the data in their report which was necessary for the theoretical evaluation, but their study is subject to some question1" due to difference in prior history of various specimens and due to systematic differences in particle characteristics" which appeared to be associated with differences in the magnification of their microscopic examination. The current study was undertaken to obtain critical data in a manner which avoids some of these limitations. Specimens of eight Cu-Cr alloys remaining from a previous investigation&apos;&apos; were available in the form of 100 mil sheet of the compositions shown in Table I. At 200 mil this material had been previously an- nealed ½ hr at 1000°C, water quenched, and cold rolled 50 pct. Samples were further cold rolled to a thickness of 20 mil for a total reduction of 90 pct. Sheet tensile specimens of standard geometry with a gage length 2½ in. long and 0.20 in. wide were machined from this sheet. These specimens were then annealed in a dried N2-H2 atmosphere for the times and temperatures indicated in Table I. This anneal served two purposes: 1—to obtain a fairly uniform and nearly constant grain size of 0.015 to 0.022 mm average diameter, and 2—to precipitate a fairly uniform, nearly spherical over-aged dispersion of essentially pure chromium. A typical microstructure illustrating the grain size and the uniformity of the dispersion is shown in Fig. 1. A typical dispersion illustrating the range of sizes and shapes of the particles is shown in Fig. 2. The tensile specimens were tested in the Instron equipment described in ref. 11 at room temperature at a strain rate of 0.04 in. per in. per min. Three tests were run on each alloy with sufficient repro-ducibility that a single true stress-true plastic strain curve could be drawn through the three sets of data for each alloy. Typical curves are shown in Fig. 3.

Jan 1, 1956

By Mehl, Robert F.

IT has been shown by numerous studies that the orientations of new metal crystals are determined by the orientations of the crystals in the original matrix, whether these new crystals are formed by recrystalliza-tion, by precipitation from solid solutions, or by transitions in the solid state. The orientations of crystals formed by recrystallization of cold-worked worked metals that bear preferred orientations are occasionally simply related to the initial preferred orientation; often, however, the relation-ship is not simple, but complicated and obscure in origin.1 The orientations of crystals formed by precipitation from solid solu-tions have been shown by many studies in this and other countries to be determined by the orientation of the crystals of the solid solution stable at the higher temperatures, though here again complicated cases have been found and no general theory is available .2 Related to this latter class

Jan 1, 1934

By C. H. Chou, A. Sauveur

The senior author of this paper has expressed the belief that when gamma iron transforms into alpha iron on reaching the A3 point, each gamma grain does not change bodily into one or more alpha grains but that the alpha phase forms first at the boundaries and along the crystallo-graphic planes of the austenite grains.1 To quote: On cooling through the point As, at about 900° C, iron passes from the gamma condition to a new allotropic form generally designated as alpha. This transformation, however, is not instantaneous. There are good reasons for believing that it begins at the grain boundaries and along the octahedral planes of the crystals and that it progresses until each grain of gamma iron is changed into a grain of alpha iron, the resulting structure being similar to that of gamma iron. Were it possible to retain

Jan 1, 1929

By A. J. Ardell

SASS and cohenl (S-C) have recently reported some transmission electron microscope observations of an interesting effect which they call "veining". They observed veining in thin foils of solution-treated and (in certain cases) aged samples of a Ni-10.3 at. pct Ti-0.6 at. pct A1 alloy (assumed equal to 10.9 at. pct Ti). S-C suggest that veining in solution-treated samples is due to the selective electrolytic etching of titanium-rich regions in alloys which are otherwise homogeneous. They associate the veins with the discrete titanium-rich regions detected in a magnetic study of aging in this system by Ben Israel and Fine,&apos; and they also suggest that the initial strengthening of aged Ni-Ti alloys is due to these titanium-rich regions, rather than the formation of the coherent precipitate (Ni3Ti, L12 crystal structure).

Jan 1, 1970

By Joseph Singewald

AMONG the genetically interesting iron ores of the United States are those of the St. Francis Mountains near Ironton and Iron Mountain, Missouri. They are specular hematite in porphyry. The Iron Mountain and Shepherd Mountain deposits are generally spoken of as veins and those of Pilot Knob, Cedar Hill, and Russell Mountain as bedded deposits. Iron Mountain has produced nearly 4,000,000 tons of ore and Pilot Knob about 1,500,000 tons. The output of the other three localities has been insignificant. Pilot Knob is no longer worked as an iron mine, but the rock is now being crushed for use as road metal. Iron Mountain has continued as an active producer. In 1927, the property was acquired by the M. A. Hanna Co. and an extensive prospecting and exploration campaign was undertaken, so that the ultimate production of Iron Mountain will doubtless greatly exceed the figures mentioned.

Jan 1, 1929

By Albert F. J. Bordeaux

INTRODUCTION. THE following general survey of the character and present condition of the silver-mines of Mexico, though not offered as a detailed treatise, has been prepared with care, is believed to he generally up-to-date, and is offered as a summary which may be found useful by mining engineers. Mexico has ranked for several centuries first among the silver-producing countries. It is now second as copper-producer, and seventh as gold-producer, with a fast-increasing output every year. The total amount of capital invested in its mining- and smelting-works is more than $250,000,000, while the yearly metallic production is $160,000,000. There are more than 20,000 recorded mining properties. The silver-mines of Mexico represent deposits of three principal classes: (1) veins and stock-works in eruptive rocks; (2) fissure-veins crossing the crystalline schists, granite, diorite, etc. ; and (3) veins and replacement-deposits in limestone. The true fissure-veins in some districts contain (in value) more gold than silver. In other deposits, the silver is decreasing in depth, leaving galena and zinc-blende as the principal ores.

Jan 9, 1908

By C. Chiou, M. E. Fine

While Gunier-Preston zones are growing in Al-4.2 pct Cu at room temperature, Young&apos;s modulus, measured dynamically, increases about 0.4 pct. From the change in modulus with time the exponent of time in the rate equation for growth of the zones was deduced to be %. From a comparison of the rates of increase of modulus at 1, 28, and 42°C an activation energy of 12 to 14 Kcal per mole is computed. These findings support the idea that copper atoms are supplied along dislocation channels to growing zones. In alloys the elastic constants will be functions of the distributions of the atoms. If the degree of ordering or clustering is changed, one expects a corresponding change in the elastic constants. During age-hardening of aluminum-copper alloys at room temperature, the copper atoms cluster on 100-type planes in the aluminum lattice forming

Jan 1, 1959

By C. W. Kempton

IF New England were located in some distant and almost inaccessible region, there is no doubt that its mineral resources would have been ere this well developed and generally acknowledged, but laboring under the disadvantage of nearness, it has been neglected. Its surface, moreover, is not cut up by mountains and canons, and the remnants of many of the old ridges are extensively covered by glacial drift. Having for the past ten months been engaged in the development of a. mineral district in Southeastern Maine, I would take this opportunity to lay before the Institute sketches of results, and try to give some idea of the formations as found. The Sullivan Mining District extends from the town of Franklin, through Hancock, Sullivan, and Gouldsborough, from northwest to southeast, about sixteen miles. A general idea of this locality may be gathered from the map accompanying. (Fig. 1).

Jan 1, 1879