By Dai Xi

In the present work, the viscosities of molten FenO-MgO-SiO2 and FenO-MgO-CaO-SiO2 semi-synthetic slags for nickel flash smelting were measured in the temperature range from 1473 to 1723K by a rotational viscometer. The ratio of Fe to Si02 was fixed at 1.2, calcium and magnesium oxide contents varied in the range from 2 to 8 mass% and 9 to 12 mass%, respectively. The results showed that silicate anions became smaller by increasing CaO content, which results in a decrease of the viscosity of the slag. In the case of MgO addition the viscosity behavior was complicated. At MgO content below II mass%, the viscosity increased with the increase of MgO at all temperatures tested. However, when the MgO content was above II mass%, the viscosity decreased slightly for FenO-MgO-CaO-SiO2 system. At higher MgO contents, low-viscosity slags can be obtained by adding CaO. At a given composition, .the viscosity decreased with increasing temperature. The higher the temperature, the more MgO can be added before saturation. The effect of Fe3O4 on the viscosity was quite significant. The viscosity of slag increased by 300mPa-s at 1573K when Fe3O4 content varied from 3 to 9 mass%. The viscosity values are presented as the functions of temperature and composition. A comparison between FenO-MgO-SiO2 and FenO-MgO-CaO-SiO2 systems is given in this study.

Jan 1, 2003

By Wantae Kim, Furnia Saito, Qiwu Zhang

"A novel mechanochemical processing technique for the preparation of zeolites from kaolinite in NaOH solution was investigated. Dry and wet mechanochemical treatments combined by subsequent moderate heat treatment could accelerate the synthetic reaction for zeolites from kaolinite. This stimulating process produced zeolite-A and zeolite-X from activated kaolinite at extremely lower reaction temperature than conventionally applied for zeolites production. Conversion to zeolite-A and zeolite-X was strongly dependent on the activated state of kaolinite. Wet mechanochemical treatment modified the chemical composition of activated solids. Rapid dissolution of AIO species rather than SiO ones in the reactant solution was accelerated by wet milling together with NaOH that promoted the formation of zeolite-X of high specific surface area.IntroductionZeolites are a family of hydrated alumina-silicate minerals contains alkali and alkaline earth metals. They have a framework structure that encloses inter-connected cavities occupied by large metal cations and water molecules. Zeolites are characterized for their ability toward ion exchange and reversible dehydration. Properties of them are exploited through commercial productions of particular structural and chemical features. Zeolites are used as commercial uses for catalysis for FCC (fluidized catalytic cracking) of petroleum refining, drying reagents of gases and liquids, and selective adsorbent for pollution control [1-3]. In such purposes, artificially synthesized zeolites are employed, although natural ones are associated with hydrothermal and hot spring alteration of volcanic materials. Commercially, a hydrothermal process has been used for the preparation of zeolite synthesis. This preparation method gives zeolites of high chemical homogeneity and purity, however, this wet-chemistry-based processing is significantly influenced by reaction temperature, pH, concentration, and composition of starting substances [4]."

Jan 1, 2000

By Banqiu Wu, Ramana G. Reddy, Robin D. Rogers

Experimental studies on aluminum recycling via electrolysis in ionic liquids were carried out at the temperature of 105°C. Impure aluminum was dissolved at the anode and pure aluminum was deposited on a copper cathode. The products were characterized using an optical microscope, micro-image analyzer, X-ray diffraction, emission spectrometer, and atomic absorption analyzer. The electrorefining process with a current density of 310 - 730 AJm2, and current efficiency of about 99% was obtained. Impurities such as Si, Cu, Zn, Fe, Mg, Cr, Ni, Mn and Pb were removed as anode residue. Impure aluminum was purified from 79.8wt% to 99.9wt%. At a cell voltage of 1 volt, the energy consumption of about 3 kWh/kg-Al was obtained. The process has advantages of low energy consumption and low pollutant emissions, compared with the current industrial refining process.

Jan 1, 2000

By Fatma Arslan

Alada (Kayseri-Turkey) lead-zinc sulfide-oxide ores contain 10.17% Pb, 10.98 %Zn, 164 g/t Cd and 57 g/t Ag. During the laboratory scale flotation tests of these ores, it was found that almost all zinc was remained in the tailings that contain 12.31% Zn, 1.35%Pb, 198.3 g/t Cd, and 22.3%Fe. Three different methods were studied such as basic (NaOH) leaching, roasting+acidic (H2SO4) leaching and direct acidic (H2SO4) leaching for recovering metals that these tailings contain. In the direct acidic leaching, which gave the best results, dissolution efficiencies of 91.5% zinc, 78.2% cadmium, and 14.3% iron were reached at the optimum leaching conditions while Pb remained in the leach residues and the acid consumption was 422.3 kg/ton of tailings.

Jan 1, 2006

By Carlos A. Nogueira

Spent Ni-Cd batteries contain in the electrode materials heavy metals like Ni, Cd and Co, which must be recycled due to environmental problems. Pyrometallurgy is normally used for recycling these end-of-life products, but alternative processes by hydrometallurgy, integrating also physical operations, can be used. Hydrometallurgy seems to be useful, because metals can be efficiently recuperated in chemical forms with commercial value. The economical viability of this recycling process can be improved increasing the treatment capacity, through the application to different types of residues with similar characteristics like Ni-MH and domestic batteries, or other residues containing Ni/Co, like sludges, dusts or spent catalysts. Spent Ni-Cd batteries were first physically processed using shredding and wet sieving operations. Best results were achieved using an output of 6 mm in the shredder and 1.4-2 mm in the physical separation by wet sieving, resulting a fine fraction containing 70% of the initial electrode material and only 6% of the initial scrap. The acid leaching of the obtained material in the previous operation was studied, being the parameters like: temperature, H2SO4 concentration and the liquid/solid ratio (L/S) optimized. The values attributed to the factors which concerned the best results obtained on the leaching process were mainly influenced by Ni recovery. In opposition, Co and Cd were easily leached in a wide range of conditions. To attain an overall recovery, with minimum costs, of the three metals, the values of T~100ºC, [H2SO4]=2.3-2.7 M and L/S=8-10 L/kg were considered the most appropriate.

Jan 1, 2006

By Emilia Visileanu, Eftalea Carpus

"Due to the demographic explosion and development without precedent of the consumer society, the capacity to destroy the ecological balance the entire planet life depends on, acquire new dimensions. In this context new approaches on society development are imposing as well as special responsibilities for stopping and preventing Earth destruction and repairing the damage already done. The zero waste is a call to action that has as an aim the changing of current mentality of human society. ”take, use, throw away”. The zero waste is a policy, a way, an aim and represents a new approach planned for the XXI century that include the resources preservation principles, pollution reducing, increasing of the opportunities to create new work places and providing the highest degree of the.1. INTRODUCTIONThe zero waste is a call to action that has as an aim the changing of current mentality of human society. ”take, use, throw away”. The zero waste is a policy, a way, an aim and represents a new approach planned for the XXI century that include the resources preservation principles, pollution reducing, increasing of the opportunities to create new work places and providing the highest degree of the economy stability.2. ECOLOGICAL CONCEPTSA long-living Romania means:The closing of the production cycles, by waste reusing and recycling; the reducing of the use of fossil fuel; the improving of the material qualities, for extending the economical life of the products made by these materials; the reducing of the transport traffic.In this context, ecology, the star science with the ability to conserving and renewal of the environment is making its way, having the following principles:•,everything is bind by everything – is referring to the importance which the environment has for a great number of allied fields;•,everything leads to somewhere – the principle of the indestructible property of material (in nature, there must not exist wastes);•,nature does it the best – ecology becomes the responsible science with the governing of the strategic laws between man and nature, man takes advantage of the natural resources which he cannot create by himself and nature must feel guarded and not destroyed by this alliance;•,nothing is for free – the polluter pays.The protection of the natural environment means:•, its strong knowledge and that of the interactions between the social economic system and the natural system, the foreseen of the most close and most distant consequences of these interactions;•,the rational usage with maximum economical character of the natural resources not depending on their origin;•,preventing and direct fighting against as well on the degradation of the environment caused by man, as on those produced by natural causes;•,the ability to harmonize immediate interest of the human society on long and permanent term, using the natural factors of the environment."

Jan 1, 2008

By Kazusuke Sato, Takahiro Uno, Koji Hoshino

"A novel Ni coating technique of Ni(OH)2 powders was developed to improve the positive-electrode performance· of the Ni-MH batteries. It was found out that Ni(OH)2 powder was reduced by N2H4 without any catalysts in an alkaline - solution at high temperatures. In result of observation of pH and potential changes in the solution during the reaction, it was found that the reduced species was HNio2- ion dissociated from Ni(OH)2 in the alkaline solution. The molar fraction of reduced Ni of the Ni(OH)2 was increased in proportion to the amount of added N2H4. At the small Ni fraction, a porous Ni layer was formed on the surface of Ni(OH)2 powder. Open cell tests were carried out with the paste type electrodes made of either the Ni coated Ni(OH)2 powder or non-coat powder, and cell performances were compared. In result, it was found that the Ni coating technique is effective on improvement in the utilization of Ni(OH); as a positive-electrode active material under high current densities.IntroductionNi-MH rechargeable battery is generally used for the power source of portable machines and electric vehicles because of its good performance at high energy density and. long term cyclical life as well as cleanness and good safety. Cell component materials have been improved respectively, and as concerns ·the positive-electrode reducing 'the internal resistance is a principal problem to improve the discharging performance at higher current densities.In recent years, improved Ni(OH)2 powders coated with conductive materials as NI. or CoOOH have been developed for the· positive-electrode active materials in order to· reduce the internal resistance of the electrode1)· 2) The Ni coated Ni(OH)2, however, is costly because it is fabricated by .the -non-electrode plate technique which needs a expensive precious ·metal catalyst as PdC12We found that Ni(OH)2 powder was reduced by N2H4 without any cryatalysts in an alkaline solution at high temperatures. After the treatment, Ni(OH)2 powder become gray color like Ni powder from light-green color; and. turned into a magnetic. In this study, the mechanism of the -reducing reaction was investigated to apply the reactions .to a novel Ni coating technique of Ni(OH)2 powders, · and the performance of the Ni coated Ni(OH)2 powder obtained by the reducing process was evaluated as an -positive-electrode active material of Ni-MH batteries."

Jan 1, 2000

By S. Goto, S. Yamashita, K. Hata

"The average consumption of zinc dust for purification of zinc leaching solution is more than 25 kg per tonne of electrolytic zinc. Authors proposed to remove impurities in zinc leaching solution by electrolysis instead of cementation by zinc dust. The effects of copper and arsenic on electrodeposition of cobalt in zinc sulfate solution were examined fundamentally using a potentiostat. It is observed that cobalt is easily deposited on a cathode at potentials under -480mV with arsenic. Mesh cathodes of stainless steel and lead anodes were used in a small electrolytic cell and the electrolyte was circulated through 'the electrodes during the electrolysis. The effect of electrolyte circulating rate , pH, cell temperature, current density, and concentration of copper and arsenious ions on removal of cobalt were studied. Removal of Cd and Ni are also examined.IntroductionCobalt is difficult to remove from a zinc leaching solution by a simple cementation reaction using zinc dust. However, it is easily precipitated by zinc dust with co-addition of arsenious or stibinous oxide and copper ion in practical operations(I), (2), (3). The consumption of zinc dust for purification is 16-152 kg per tonne of electrolytic zinc and 65% of this zinc dust consumption is used for cobalt purification. The average retention time for purification of cobalt is 4.5 hours (1). A more economical process for purification is desired instead of zinc dust. The mechanism of this acceleration effect of copper and arsenious oxide on removal of cobalt are explained by the authorsas follows; a galvanic cell is formed between zinc dust and copper which is precipitated firstly, and cobalt is reduced on copper as Co-As alloy by this galvanic current(2). This assumption was confirmed in experiments using a galvanic cell with a membrane( 4). The following galvanic reactions occur between zinc dust and copper precipitate; on copper cathode,2H+ + 2e -= Hz(g)2Coz+ + 2HAs02 + 6H ++ 10e -= 2CoAs + 4HzOand on zinc anode,Zn = Zn = 2+ 2e –This galvanic current becomes almost zero in a zinc sulfate solution which includes only cobalt and no arsenious oxide, and cobalt is weakly deposited on a copper cathode. Cobalt deposition requiers a high degree of cathodic polarization. However, the galvanic current flows almost constantly in an electrolyte, which includes arsenious oxide, and the cathode potential is kept at about -500mV. Cobalt is precipitated as Co-As on the cathode.The authors assumed that cobalt may be removed by electrolysis at a very low current density instead of zinc dust and the following experiments were carried out. In the first part of this paper, the fundamental experiments using a potentiostat on the behaviour of cobalt in zinc sulfate solution are described. In the second part, the results of the electrolysis are reported. Cobalt is removed by a new type of an electrolytic cell, which was desigoed to <Iccelerate the rate of deposition of cobalt. The removal of cadmium and nickel in a solution which includes cobalt and arsenic are also examined."

Jan 1, 1997

By Kensuke Sassa, Shigeo Asai, Norihisa Waki

"A new method for separating inclusions from a molten metal using a high magnetic field has been proposed. The principle of this method based on the magnetization force has been confirmed in experiments of separating intermetallic compounds imitating inclusions from molten Al-Si-Mn-Fe and Al-Si alloys. In order to measure a magnetic susceptibility, the Gouy's method has been so modified by using a super-conducting magnetic as to work in a high temperature up to 1473K. A theoretical expression for the magnetization force, which is indispensable to evaluate the magnetic susceptibility, has been derived. The magnetization forces acting on intermetallic compounds which were used in the magnetic separation were measured over the range of liquidous to solidous temperatures and the magnetic susceptibilities of the intermetallic compounds were obtained from measured magnetization forces by use of the theoretical expression.I. IntroductionRecent developments in the technology of super-conducting magnets have given rise to the circumstance that a high magnetic field over a relatively large space is readily available without liquid helium. Then, it has been found that a high magnetic field provides magnetic effects to nonmagnetic substances and various interesting phenomena have been reported in the broad science fields of physics, chemistry and biology1). ""A science related to a high magnetic field"" in which many fields are transversally viewed from the standpoint of a high magnetic field2 ) is going to be established. In particular, new phenomena and functions brought by the science related to a high magnetic field are also useful for Material Science and Engineering so that the creation of Materials Science and Engineering related to a high magnetic field"" has been conceived 3).Now, when a substance regardless of being magnetic or nonmagnetic is put in a magnetic field, it feels a magnetization force, which is familiar to such a force that a magnet attracts iron. The force is in proportion to the product of magnetic field strength, its gradient and susceptibility so that a precipitated substance can be separated from a molten metal based on the difference between susceptibilities of a substance and a melt. This is a basic principle of the magnetic separation. So far the application of the magnetic separation has been limited to the separation of ferromagnetic substances from a nonmagnetic medium. A high magnetic field, however, has enabled to separate nonmagnetic substances from a nonmagnetic medium.In this study, a new method to separate inclusions from a molten metal using a high magnetic field has been proposed. The principle of the method was verified by experimental works and the feasibility on the elimination of inclusions in steelmaking processes has been studied"

Jan 1, 2000

By Toshihiro Kuzuya

A hydro metallurgical process has been developed for the recovery of metal values such as Co, Ni and rare earths from the electrode materials of spent nickel metal-hydride(Ni-MH) secondary battery. MmNis_xCo. (Mm : Misch metal) intermetallic compound could be separated from the electrode materials mixture by sedimentation. A typical chemical composition of MmN5-xCox was approximately, in mass%, 56.0%Ni, 13.4%Ce, 10.6%La and 7.9%Co. The time dependency of leaching intermetallic compound with sulfuric acid solution was examined with processing factors such as sulfuric acid concentration, temperature and agitation intensity, The leaching of rare earth metals proceeded very rapidly, reaching completion in less than 1.8ks. On the other hand, the slow leaching of nickel was observed. The percent of nickel leached at 328K could only reach about 70%.

Jan 1, 2003

By Nobuhiro Ishikawa

The in-situ observation of the effect of impurities on the reduction process of iron oxides by C in TEM was carried out. A few wt% of CaO or AbO, was used as impurities in FeO was prepared. Some precipitates grew into the C layer expect for using 3.0wtCa. The reaction between FeO and carbon was much different from using pure FeO at about 800-1 lOOK. The rate of reaction became much slower including Ca and almost no reaction was happened with the concentration of CaO up to 3.0wt%. On the contrary, AbO, had ahuost no effect on the reaction. The results indicated that Ca suppressed the reaction and the effect of Al was much less. The precipitates which grew into C layer accompanied almost no Ca and AI. Only Fe was detected in the precipitates.

Jan 1, 2008

By Stella Agatzini

Column leach tests were conducted to evaluate the amenability of poor Greece nickel laterites to heap leaching with dilute sulfuric acid at ambient temperature. The ore tested was a limonitic laterite with less than 1 % nickel and it was subjected to a suitable pretreatment with water prior to it being loaded into the columns, following findings of preliminary research work. The acid solution was recycled after suitable pH adjustment. Factorial designs were used to determine the effects and interactions of the following factors: sulfuric acid concentration, ore column height, ore grain size and ratio of leach solution volume to the ore quantity. The response which were investigated included nickel and cobalt recoveries, codissolution of iron, calcium, magnesium, aluminum, chromium and silica and also sulfuric acid consumption. Experimental error was also detennined. The tests showed that a nickel recovery of 88% could be achieved in 60 days.

Jan 1, 1993

By Mark L. Dietz

The unique physicochemical properties of room-temperature ionic liquids (RTILs) have led to intense interest in these materials as alternatives to conventional organic solvents in a range of synthetic, catalytic, and electrochemical applications. Recently, there has been growing interest in their potential use in various separation processes, among them the liquid-liquid extraction of metal ions. Although certain RTIL-extractant combinations (e.g., crown ethers in 1-alkyl-3-methylimidazolium bis[(trifluoromethylsulfonyl] imides) have been shown to provide extraction efficiencies far exceeding those observed with conventional solvents, recent work suggests that the utility of RTILs may be limited by solubilization losses and difficulties in recovering extracted metal ions. In this work, we demonstrate that these limitations arise, in part, from differences in the mechanism of metal ion partitioning in RTIL systems versus conventional organic diluents and consider approaches by which they might be overcome.

Jan 1, 2003

By Thomas Schuman, Jaan Kers, Lucas N. W. Damoah, Xiangjun Zuo, Lifeng Zhang

"Rapid technological innovation has propelled the use of electronic equipment leading to the generation of more and more waste electrical and electronic equipments (WEEE). Printed wiring board (PWB) is a component made of one or more layers of insulating material with electrical conductors. To investigate an environmentally friendly process to recycle PWBs, PWB samples with and without additives were pyrolyzed. Liquid, gas and solid products were achieved with different conversion fraction. Analysis of the exhaust gases from the experiments using GC-MS and MS showed that without CaCO3 additives poisonous gases such as C6H6 and HBr were produced which were adequately controlled if CaCO3 was added.IntroductionPyrolysis is one of the best methods for treating complex mixtures of waste polymers and to recover the material and energy content. The process consists of thermal decomposition at moderate temperatures in total absence or small amount of oxygen in which the structures of polymers break down into smaller intermediate products "". The decomposition temperature of a substance is the temperature at which the substance breaks up into smaller substances or into its constituent atoms 2). Thermal treatment of PWBs were reported using DC Arc Plasma furnace 3), and fixed bed reactor 4). One drawback in dealing with thermal treatment of PWB scraps is the likely production of super-toxic halogenated dibenzodioxins and dibenzofurans from the bromine containing structures. Pyrolysis of organic materials contained in waste PWBs leads to the formation of gases, oils, and chars which can be used as chemical feedstock or fuels ""'. Dehalogenation of the pyrolysis product of electronic scraps is essential to make it commercially acceptable. It would be obviously the most advantageous solution as pyrolysis and dehalogenation are carried out simultaneously. Reported pyrolysis investigations are at experimental stage and have been carried out in vacuum, molten salt, fluidized bed, rotary kiln, entrained, stationary, and moving bed reactors 7). Comparing to the incineration and combustion of PWBs, the pyrolysis process has several characteristics: 8'"">) 1). Converting the organic solid substance into fuel gas, fuel oil and carbon-black as storage energy; 2) Emitting toxic substances such as sulfur, bromine and heavy metals in wastes; and 3) Keeping metals from being oxidized. Although many researches into the pyrolysis of PWB wastes have been reported, most of the works have been carried out using analytical pyrolysis techniques or very small batch reactors ""~'5). Also, most of the works for the pyrolysis of PWBs haves concentrated on the composition of the organic products, particularly the brominated organics. The current study is to investigate the pyrolysis of PWB powders in a small TG-DTA scale and a 50-gram tube furnace scale."

Jan 1, 2011

By F. G. Caballero, J. L. Gonzalez-Carrasco, S. Barrius, H. Carreon, M. Lieblich

"The grit blasting is a low-cost technique successfully used to enhance mechanical fixation of the implants through increasing their roughness. As a result of the severe plastic surface deformation, it produces subsurface effects such as grain refinement, hardening and compressive residual stresses which are generally evaluated with destructive techniques. In this research work, non-contacting and contacting thermoelectric power measurements are performed in blasted 316L VM and Ti-6AI-4V specimens using Ah03 and Zr02 particles which yield a coarse and a fine rough surface, respectively. This study correlates the microstructural changes induced by the grit blasting treatment and the limitations and advantages of each of the nondestructive thermoelectric techniques based on the Seebeck effect used to evaluate these biomaterials.IntroductionIt is well known that surface properties play an important role in metallic materials used in bio-medical applications. Since the biological response is correlated directly with surface properties it is comprehensible the intense activity in superficial modification by physics or chemistry methods in this field. Grit blasting, one of the most popular surface modification of metallic biomaterials, enhances the mechanical fixation of the implant through the increase in roughness [1-3]. Roughening is developed by bombarding the surface with a high-velocity jet of ceramic particles, being the final roughness a function of the processing parameters (pressure, distance, time, ... ) and blasting particles (nature, shape, size). As the plastically deformed surface layer tries to expand relatively to the intact interior of the specimen, residual compressive stress gradients develops perpendicular to the surface at shallow depths with a maximum value at a depth in the range of 5 to 60 µm. This surface treatment also may cause subtle variations in the subsurface material properties, such as increased hardness and grain size refinement, which are consequences of the significant plastic deformation through cold work. Blasted affected zones may extend to a depth of up to about 200 µm. The subsurface hardening and the near-surface compressive stress gradient playa beneficial role by retarding fatigue crack nucleation and further growth, ultimately extending the fatigue life of the metallic part [4]. In this work, two non-destructive thermoelectric techniques (NDTT), the non-contacting and contacting thermoelectric power measurements were used to analyze the subsurface induced changes on blasted Ti-6AI-4V and 316L VM specimens using Al2O3 and Zr02 particles. Detailed information on the microstructural induced effects and subsurface mechanical properties were published elsewhere [5-8]. Here the nondestructive evaluation of the involved microstructural changes is used to assess the global subsurface damage. Advantages of using nondestructive techniques during manufacturing are envisaged."

Jan 1, 2012

By Mamoru Kuwahara, Tomohito Taki, Masamichi Sano

"Theoretical basis and experimental results on ultrasonic separation of dispersed inclusions from molten metal are outlined. Transitional formation of an ultrasonic standing ·wave field in a liquid bath is numerically predicted based .on the wave equations. Numerical solution of the equation of motion of a fine particle in a standing wave field indicates that the inertia term can be neglected during conventional ultrasonic separation of fine particles: Analytical solutions for the position at which particles are coagulated the minimum power for separation, and the ultrasonic separation time are derived to incorporate such key process parameters as the density difference and the acoustic energy density exerted. Cold model experiments have been carried out to observe ·transitional coagulation of polystyrene particles in an aqueous sugar solution with the incidence of standing ultrasonic plane wave. Experimental results agree well with the theoretical predictions.IntroductionDespite of recent progress of fundamental and applied researches in metallurgical systems, advanced materials· with less inclusions and better properties may demand more innovative processing in a: molten state. It may be realized by applying electromagnetic and/or ultrasonic external fields to the systems. The present authors1)·2) have been proposing : new methods of ultrasonic processing of materials based on such phenomena as acoustic streaming, acoustic radiation pressure on dispersed phase in a standing wave field, and the cavitation in liquid associated with use of high-intensity ultrasound and so on. Taking account of common physical natures between ultrasound and sound wave, we call such · a processing assisted by acoustic wave as ""sonoprocessing"". This report ·deals with some theoretical and technological aspects on the ultrasonic separation of fine particles from liquid, which could become an important operation to produce clean materials. Fundamental theory and ·supporting experimental results will be given below to give an insight into the liquid metal sonoprocessing."

Jan 1, 2000

By M. Nilmani, J. Sofra

The transverse distributions of the solids discharge velocity and mass flux at the discharge end of vertical and inclined lances were measured in order to detennine the transverse distributions of the axial momentum flux, which is a dominant factor influencing the penetration behaviour of particles into melts during submerged injection. The effects of gas velocity (10 - 30 m/s), solids loading (5 - 10), lance length (0.15 - 1.0 m), lance inclination (vertical downward - horizontal) and particle density (2500 - 8900 kg/m3 ) were investigated, while the lance diameter and particle size were fixed at 10 mm and 220 µm respectively. The particle velocities and mass fluxes were measured by image analysis of particles illuminated in a laser-generated light sheet aligned vertically through the axis of the lance at the discharge point. The particle discharge velocity profiles for vertical downward flows were synunetrical about the centre-line of the lance, with the maximum velocities occurring at the centre-line. The velocities increased with increasing gas velocity, increasing lance length and decreasing particle density in accordance with previous observations. The transverse mass flux profiles were also synunetrical for vertical downward flows, however at the lower gas velocities the peaks in the profiles were displaced from the centre-line of the lance by a fractional diameter of about 0.15. The particle discharge velocity profiles become increasingly asynunetric as the lance orientation was changed from vertical to horizontal, with higher particle velocities present near the top wall of the lance. The mass flux profile also became asyrrunetric as the horizontal orientation was approached, however in this case, the profile became biased towards the bottom of the lance. The effect was much more pronounced for a gas velocity of 10 m/s than for 30 m/s, showing the relatively stronger gravitational influence as the velocity was reduced.

Jan 1, 1996

By JiaPeng Xu, Brian Lo, Uday B. Pal, Yihong Jiang, Soumendra N. Basu

"The Solid-Oxide Oxygen-Ion-Conducting Membrane (SOM) electrolysis process has been successfully tested on a laboratory scale, producing silicon directly from silica in a cost-effective and environmentally friendly way. A yttria-stabilized zirconia (YSZ) tube, closed at one end was employed to separate the molten salt containing dissolved silica from a liquid metal anode placed inside the YSZ tube. When the applied electric potential between the liquid tin cathode in the molten salt and the anode exceeds the dissociation potential of silica, oxygen ions are pumped out of the molten salt through the YSZ membrane and oxidized at the anode while the silicon cations in the flux are reduced to silicon at the liquid tin cathode. The presence of high-purity silicon crystals on the surface of liquid tin cathode was confirmed by scanning electron microscopy (SEM) and energy dispersive x-ray spectroscopy (EDS). Silicon crystals were extracted from tin cathode by chemical etching.IntroductionPhotovoltaics (PV) generate electrical power by using solar cells, and dramatically reduce the emissions of greenhouse gases (GHG). Through 2006 to 2011, it grew the fastest of all renewable technologies with operating capacity increasing an average of 58% annually [l]. However, the cost of manufacturing solar-grade silicon (SoG-Si) for high-efficiency solar energy production represents a major barrier to achieving the industrial goal for solar power of $1/Wp (watt at peak exposure) which would enable widespread grid parity. The current contract price of silicon to PV manufacturers is $50-$60/kg, with the spot market in 2007-2008 showing prices as high as $300/kg [2]. This makes the development of low cost and environmentally friendly manufacturing of high purity silicon very important."

Jan 1, 2013

By Biswadeep Saha, Meenakshisundaram Ramanathan, Chai Ren, Sivaraman Guruswamy

"Fe-Ga alloys have a large low-field magnetostriction and these alloys are attractive candidates in energy conversion and harvesting applications. Small additions of W also increase the magnetostriction of Fe. In this paper changes in magnetostriction by W substitution for Ga in various Fe-x at.% Ga alloys are presented. Fe-Ga-W single crystals were grown using vertical Bridgman Growth technique. [001]-orientated single crystal samples were prepared with faces within 1 degree off <100> orientation. The samples were annealed at 1150 °C in the alpha-phase region and water quenched. The magnetostriction coefficient (3/2)A-100 measurements were made on these Fe-Ga-W single crystals. The result on the effects of W substitution and annealing on the magnetostrictive behavior of these alloys are discussed.*Support of this work by NSF-DMR under the award DMR-0854166 is gratefully acknowledged.IntroductionMagnetostrictive materials changes their dimension exhibit reversible strains and changes in elastic properties in the presence of an applied magnetic field or the reciprocal effect of changes in the magnetic properties with the application of stress [IJ and are very important in sensor, actuator device, linear motor, magnetomechanical devices, microelectro- mechanical devices, active vibration dampening devices application areas. The discovery of an order of magnitude enhancement in the magnetostriction of Fe with Ga addition coupled with low saturation magnetic fields, and excellent mechanical properties opened up the possibility of obtaining larger magnetostriction values in other low-cost ductile a-Fe phase based alloys with alloying additives that are less expensive than rareearths such as Tb and Dy [2·4l_ The magnetostriction values observed in Fe-Ga single crystals are sensitive to thermal history and composition. The formation of second short range ordering phases and local defects inside crystal structure can also cause a dramatic change to this alloy's magnetostriction behavior [5-9l_"

Jan 1, 2012

By Shun Fujieda, Shigeru Suzuki, Kozo Shinoda, Tetsuo Fujita

"Dowa Metals & Mining Co. Ltd. has developed and plant-practiced a unique scorodite synthesis technology (DMSP®) for arsenic immobilization by oxidizing Fe(ll) ions in the presence of As(V) ions. Dowa has improved the DMSP® technology and has developed the process extensively for other applications. This paper focuses on the applicability of the DMSP® for various cases of copper smelting, and introduces other technologies for fixing arsenic and recycling gallium from GaAs, simultaneously processing (fixing) arsenic and thallium, and fixing and recovering arsenic from dilute arsenic solutions. The DMSP® was found to be applicable not only for various processes in nonferrous smelting, but also for other applications with a high potential for reducing environmental problems.IntroductionDowa Metals & Mining Co. Ltd. developed a method for synthesizing scorodite at ambient pressure [1], The scorodite is precipitated by oxidizing Fe(II) ion in a high-concentration As(V) solution. The scorodite produced in this way does not readily release arsenic because of its high crystallinity. Dowa built a demonstration plant for this technology at the Kosaka Smelter and established the production of scorodite at 30 t As/month by treating intermediate products from copper smelting as the starting material. The DMSP® was demonstrated to be favorably applicable to copper smelting [2]. We are engaged in further increasing the amount of arsenic fixation by the use of this process. Further improvements in productivity, cost reduction and applicability in various processes have been devised. Dowa has been endeavoring to resolve other problems as well as to improve productivity. We have gained extensive knowledge on arsenic treatment in our endeavors, enabling us to solve problems and improve productivity. This paper introduces the investigations and developments related to DMSP®."

Jan 1, 2012