By Lu Lin, Yanping Bao, Xiang Li, Linzhu Wang, Xiaobai Yan

The results showed the microinclusions were mainly Al2O3 and sulfide inclusions from tapping to the beginning of LF refining. Al2O3 inclusions were modificated into calcium aluminates after calcium treatment. Lots of spherical calcium aluminates composite inclusions containing MgO, TiO2 and MnS were found after soft blowing and during tundish metallurgy and left in the slab which caused the defects of beam plates. Pure Al2O3 inclusions were observed again after soft blowing 8min. Average sulfur content in inclusions decreased because of the high desulfurization ability of refining slag. Average Ca/Al ratio value in inclusions increased during LF refinging because of the reduction of CaO in slag by carbon and it increased obviously during the process of soft blowing 8min because of the dissolusion of calcium wire.

Jan 1, 2015

By Thierry De Nys

A direct leaching process of sulphidic zinc-based concentrates in aqueous sulphuric acid solutions has been developed by the V.M. R & D Department. By a very accurate control of the oxidation potential of the leach solution, this process enables a separate recovery of the zinc, copper, silver, lead and sulphur of the concentrate and makes it extremely attractive for treating more complex ores. The iron, solubilized during leaching, is eliminated out of the zinc solution by means of the V.M. goethite process. Alternative flow sheets for a conventional zinc electrolysis plant are presented.

Jan 1, 1990

By Adrian C. Deneys, David G. C. Robertson

"Fluid flow phenomena on the surface of a molten slag have been documented using video photography in a laboratory scale D.C. arc furnace. The flow on the surface of the slag appeared to be electromagnetically influenced. This was confirmed by varying the position of the anode, which changed the direction of flow on the surface of the slag. Temperature measurements in the bath also confirmed the change in the directional nature of the fluid flow induced by the arc.During some periods, solids were fed into the arc attachment zone (AAZ) down the center of the hollow graphite electrode. Significant movement of the arc around the basal annular surface of the hollow electrode takes place. The point of attachment of an arc on a hollow electrode was more variable than an arc attached to a solid graphite electrode. Video images showed that the solids were rapidly incorporated into the bulk of the slag. Temperature measurements confirmed the existence of a superheated slag layer at the slag-gas interface, which allowed the solids to be rapidly incorporated into the melt.This work has been conducted to study fluid flow, temperatures, and solid behavior during feeding, in the arc attachment zone of a D.C. arc furnace. The work also has relevance to optimizing furnace design for pyrometallurgical slag cleaning processes."

Jan 1, 1999

By Toshiaki Akahoshi

Keywords: Wasted catalyst, Hydrodesulfurization, Ammonium vanadate, Ammonium molyb-date, Hydrometallurgical process. The fundamental reactions have been investigated in order to develop a hydrometallurgical process for recovery of molybdenum and vanadium from wasted catalysts generated in the hy-drotreating desulfurization of heavy oil. The principal steps of the process are a mild oxidation roasting of the waste catalysts at temperature around 500°C, leaching of the target metal components with dilute ammoniacal aqueous leachates, selective precipitation of vanadic acid, and ammonium molybdate precipitation. The selective recovery of vanadium as vanadic acid is successfully performed using ammonium sulfate as a salting-out agent. Recovery of ammonium molybdate is based on large dependence of solubility of ammonium molybdate in ammoniacal solutions upon temperature and ammonium salt concentration. In this process, the solution after recovery of vanadium and molybdenum is recycled to the leaching stage of the roasted materials, and the ammonium salts in the process liquor is in the repeated use. Employment of am-moniacal system makes it possible to operate the roasting at much lower temperature than that for the currently operating process.

Jan 1, 2005

By N. Kanari

Kinetics of the carbochlorination of Cr2O3 has been studied with C12+CO gas mixtures between 500 °C to 900 °C using thermogravimetric analysis. The apparent activation energy is about 100 kJ/mol. Mathematical fitting of the experimental data suggests that the shrinking sphere model is the most adequate to describe the carbochlorination mechanism of chromium oxide and that is controlled by the chemical reaction. In the temperature range of 550 "C to 800 OC, the reaction order is about 1.34 and is independent of temperature. Changing the C12+CO content from 15 pct to 100 pct increases the reaction rate and does not affect the reaction mechanism. Similarly, changing the ratio of C12/(Cl2+CO) from 0.125 to 0.857 do not modify the carbochlorination mechanism of Cr203. In these conditions, the reaction rate passes through a maximum when using a chlorinating gas mixture having a Cl2/(C12+CO) ratio of about 0.5.

Jan 1, 1998

By Yuchun Wang

In principle, supported liquid membranes could be an exceedingly elegant separation process. However they tend to fail by displacement and emulsification of the organic solution in the pores, which allows mixing of the feed and strip solutions. We have stabilized supported liquid membranes comprising moctylamine in nylon and PVDF supports by covering the pores with semi-permeable polyamide films, using an in-situ polymerization technique. Scanning electron microscopy demonstrates that the polyamide films are sensitive to production conditions and the nature of the support. The transport properties of stabilized supported liquid membranes for Cr(VI) are compared with those of unstabilized membranes.

Jan 1, 1998

By H. Y. Sohn

"The nonferrous production industry has gone through a remarkable transformation in recent years in terms of developing and adopting new technologies. Technology innovations have largely been driven by the need for greatly improved environmental protection in addition to increased productivity. One of the most notable aspects of the new technologies is their ability to reduce the emission of sulfur and other pollutants to extremely low levels.The current industry trends towards more environmentally friendly technologies are bringing about additional benefits of developing more efficient, technically advanced, and continuous processes in closed reactor vessels. Key aspects of these modem trends include the use of increased oxygen enrichment in the process gas, better process control, reduced manpower requirements, and plant operations with more skilled personnel.Computer simulation and modeling of complex processes have become more reliable, realistic, and thus increasingly useful in metal production. Some of the notable examples are reviewed.Finally, the need and advantages for value-added production in the nonferrous industry are discussed.I. IntroductionMost recently commissioned technologies for nonferrous metals production have been developed largely in response to environmental concerns. One of the most remarkable improvements made by the nonferrous industry in the last decade has been the rapid increase in sulfur capture. Before the start of the last decade, 90% capture of sulfur was considered good. Since then, strict emission regulations have become the norm in advanced societies, although smelters in many parts of the world still operate with limited pollution control. Other emissions and discharges have also been substantially reduced, resulting in much improved working conditions and worker hygiene in addition to the overall environmental protection. The development of the more environmentally friendly technologies has accompanied other advantageous advances made in the nonferrous industry, i.e., the trend towards more gas-tight, continuous processes and larger plants. This has increased the competitive edge enjoyed by the industry in the industrial countries, offsetting the higher costs of labor and pollution abatement that they have to overcome in those countries. Experience has shown that clean technology often leads to a profitable business, because its adoption forces the concomitant advancement of related technologies in addition to the avoidance of penalties imposed by the public on pollution-prone industries. Needless to say, there are other driving forces for new technologies such as reduction of operating and capital costs, improved product quality, and energy considerations in terms of reduced consumption and utilization of readily available sources."

Jan 1, 2000

By J. L. Holman

The Bureau of Mines is investigating recovery of Ni, Co, Cr, and other metals from mixed contaminated supera110y scrap. The scrap is melt-refined and cast into anodes for electrodeposition of recyclable Ni-Co alloy. Melt oxidation using roasted superalloy grinding sludge as oxygen source can divert the Cr to the slag but with excessive Ni-Co loss. Melt oxidation-carburization or direct melt carburization retains -95 pct of the Ni-Co in the anode alloy. With direct carburization, -90 pct or more of the Cr and other refractory metals report to the anode alloy, largely as carbide phases insoluble in electrolysis. Electrorefining data relate parameters such as controlled cathode potential, Fe and Cr impurities, pH, and compartmented cell use, to current efficiency and Ni-Co deposit quality. Recovery of -90 pct of the Ni-Co in the scrap can be achieved. Preliminary experiments to recover Cr, W, and other metals from the anode sludge and other byproducts are discussed. 347

Jan 1, 1987

By Isabella Lancellotti, Fabrizio Passarini, Luisa Barbieri, Fernanda Andreola, Ivano Vassura, Luciano Morselli

"The techniques able to incorporate wastes by means of a heat treatment present the advantage to fix the residue with chemical bonds. Among these techniques there are vitrification and sintering which are characterised by different operating temperatures in the range of 950-1500°C and the involved raw materials develop silicatic crystalline phases and glassy matrices capable to immobilize heavy metal contents in the waste matrix. In this work incinerator bottom ash, polishing and glazing ceramic sludges have undergone to thermal treatments in order to valorise the waste as secondary raw material for the obtainment of re-products. The chemical efficiency of the process adopted has been evaluated by comparing the results of release tests applied to the as-received wastes and to the thermally treated materials in order to verify the effectiveness of the different matrices to fix the waste components.IntroductionVitrification is one of the most promising technological options for the treatment of some kinds of waste. The high temperature involved in the process (1200-1500°C) leads to the complete destruction of organic pollutants, such as dioxins, and glassy network formed can incorporate heavy metals. Some vitrification processes naturally occur: glasses produced by volcanic eruptions, such as obsidians (Na2O-K2O-Al2O3-SiO2) and basaltic (CaO-MgO-Al2O3-SiO2) rocks, are basically inert materials even when they contain toxic elements, because these are embedded in an extremely stable glassy matrix. The disadvantage of vitrification is that it is an energy-intensive process involving relatively high costs, therefore its use is better justified if a high-quality product with optimised properties can be fabricated. The most effective way to improve the properties of the vitrified material is the transformation into glass ceramic. This is a fine-grained polycrystalline material (typically from 50% to 98% of the volume may be crystalline) formed when a glass of suitable composition is heat treated and hence undergone to controlled crystallisation (phenomenon named devitrification). The three key variables in the design of a glass-ceramic are: glass composition which controls glass viscosity related to the effectiveness of nucleation and rapidity of crystallisation; glass-ceramic phase assemblage (that is, the types of crystals and the proportion of crystals to glass) which is responsible for many of the physical and chemical properties; nature of the crystalline microstructure (crystal size and morphology and the textural relationship among the crystals and glass) which is the key to many mechanical and optical properties. In particular, a partly crystalline material can be obtained by powder sintering."

Jan 1, 2008

By Joseph Goodwill

1. PURPOSE The objective of this paper is to summarize a study undertaken by the EPRI Center for Metals Production (CMP). The overall purpose of the study was to identify electrolytic opportunities that might merit consideration for joint development by industry and EPRI. 2. SCOPE The electrolytic technologies of interest to this study include: Electrorefining, Electrowinning, and Fused-salt electrolysis. Recovery from primary, secondary, and waste materials were included in this effort; however, we excluded from consideration: Plating and coating operations, such as electrogalvanizing; Mining and milling operations in which electric energy is predominantly used for comminution; Electrothermal processes in which submerged-arc, open electric-arc, and plasma-based smelting processes use electric energy largely to provide a melting or refining ("heating") capability; and Aluminum electrotechnologies since these were the subject of a separate study (CMP 86-2). We recognize that there may be some "gray areas" between these excluded areas and the electrolytic sectors of interest. For this reason, a secondary criterium was used, namely, if the major use of electric energy was to extract or refine the

Jan 1, 1990

By E. M. Weenink

A proposed alternative to the conventional zinc extraction processes is the flash reduction of zinc calcines. As part of an overall study of this process, the kinetics of single zinc oxide pellets were investigated. Pellets, compacted from Outokumpu zinc calcine (60.9% zinc, 9.6% iron), were suspended in a flow of CO/CO, mixtures and reduced at temperatures between 1000 and 1200°C and atmospheric pressure. The pellet weight loss with time was recorded and analyzed. It was found that the reduction of calcine pellets (0.9 cm height and 1.36 cm diameter) was controlled by chemical reaction. This paper includes an analysis of the experimental results of two previous investigations of ZnO reduction.

Jan 1, 1992

By Chunlin Chen

Nickel-sulfide minerals are normally associated with copper and iron sulfides and often contain a minor amount of valuable metals such as cobalt and detrimental impurities such as arsenic. Metal losses in slag vary from process to process during the pyrometallurgical production of nickel and, depend on the feed composition, slag chemistry and operating conditions. Maximiz the metal recovery is one of major considerations to optimize operating condition for nickel smelting/ converting processes. At the same time, the deportment of minor elements between various phases during nickel smelting is of great importance by smelter operators. The Multi-Phase Equilibrium (MPE) is a thermodynamic package developed by CSIRO for simulating reactions between phases in multi-component and multi-phase systems [1]. Over the years the capability of the MPE model has been extended to cover the behavior of a large number of elements in high temperature systems. The sulfide smelting module of the MPE, which covers the minor elements such as As, Bi, Sb, Pb, Se, Te, Sn, Co and Zn, is capable of modeling the deportment of major and minor elements between various phases during nickel smelting. In this article the application of the MPE model in modelling the nickel smelting process is presented. The modelling results on the majors and minors are compared with the plant data. The deportment behaviour of arsenic in nickel smelting was analysed and the impact of slag chemistry on slag properties was modelled. These results can assist process metallurgists in exploring the optimum fluxing strategy for smooth operation and the potential practices for improving arsenic removal.

By James M. Fragomeni

"The mechanical behavior of an Al-Li alloy was studied and related to the extrusion processing parameters, the plastic metal flow during defonnation, the anisotropy, and the microstructure. The extrusion temperatures, strain rates, extrusion ratios, billet temperatures, and extrusion geometries were varied during processing and correlated with the microstructure and properties. The extrusion processing variables were related to the mechariicar behavior, anisotropy, and microstructure through the ZenerHollomon parameter i.e., the temperature compensated strain rate. Based on optical and electron microscopy studies it was found that regardless of the extrusion conditions, the various microstructures for the most part were unrecrystallized for both the as-extruded and the solution heat-treated conditions. Smaller grain sizes were correlated to larger Zener-Hollomon parameters. The extrusion temperature and ratio did not significantly affect the strength or ductility as did the section geometry, which had a large affect on these mechanical properties. The anisotropy of the properties varied substantially when comparing the extruded longitudinal versus transverse grain orientations.IntroductionThe extrusion process also has a substantial influence on: the microsfructure and mechanical properties of a material that is Athens, Ohio, 45701 fonned The plastic defonnation that occurs during the extrusion process alters the grain size, crystallographic texture, anisotropy, subgrain size, dislocation density and various other microstructural features. Often the material being extruded is not homogeneous, therefore variations in the microstructure and properties occur across the cross-section of the final extruded product. The mechanical properties and microstructure can also vary with length since it is hard to maintain a constant temperature throughout the extrusion process. The extrusion temperature often varies from the heat generated during the extrusion process. The demonstration material that was extruded for this .study was an aluminum alloy containing 2.6wt, % lithium and 0.09wt.% zirconium. This alloy was strengthened by heat treatment causing nucleation, growth, and coarsening of coherent metastable o' (Al3Li) precipitates in the microstructure. The ? precipitates which are a consequence 9f artificially aging the AlLi alloy, are spherical, ordered, and coherent with the aluminum matrix and impede the dislocation glide inotion during plastic defonnation. Theo particles grow homogeneously in the matrix, and have the Cu3Au (L 12)"" superlattice crystal structure. Aluminum-lithium alloys are used primarily for aerospace structural applications since they have attractive properties such as a lower density and higher elastic modulus than conventional 2XXX and 7XXX alloys."

Jan 1, 2000

The oxidation of zinc vapour plays a very important part in the operation of the Imperial Smelting Process. The kinetics of the reoxidation of zinc vapour by carbon dioxide and water vapour onto quartz and zinc oxide substrates is qualitatively understood and this pertains to the conditions found as the gases are being transferred from the furnace to the splash condenser. However, re-oxidation also occurs in the shaft of the furnace where the solid substrates are sinter and metallurgical coke. It was found that there was a threefold increase in the rate of oxidation on sinter, compared to quartz and a 30 to 300 increase in rate on the coke. This was attributed to the high surface area offered by these materials.

Jan 1, 2003

The oxidation of zinc vapour plays a very important part in the operation of the Imperial Smelting Process. The kinetics of the reoxidation of zinc vapour by carbon dioxide and water vapour onto quartz and zinc oxide substrates is qualitatively understood and this pertains to the conditions found as the gases are being transferred from the furnace to the splash condenser. However, re-oxidation also occurs in the shaft of the furnace where the solid substrates are sinter and metallurgical coke. It was found that there was a threefold increase in the rate of oxidation on sinter, compared to quartz and a 30 to 300 increase in rate on the coke. This was attributed to the high surface area offered by these materials.

Jan 1, 2003

By Tetsuya Uda

Our recent achievements of rare earth separation technique[1,2] and new process idea for rare earth magnet recycling[3] are reviewed, (1) Binary chloride mixtures of rare earths were separated by a new selective reduction-vacuum distillation process. According to our experimental results, apparent separation factors were 8.1 for the Pr-Nd chloride mixture and 570 for the Nd-Sm chloride mixture. These values are much higher than conventional solvent extraction methods. (2) A study of recycling process of magnet sludge was carried out. The rare earths in the neodymium magnet sludge were extracted by chlorination with FeCI2, An activated carbon was used as a de-oxidation reagent Metallic iron in the sludge was not chlorinated because the iron monochloride is not stable, The extracted rare earth chlorides were easily separated from Fe-alloy and the excess of FeCh by vacuum distillation, 96 % of neodymium and 94 % of dysprosium in the sludge were extraeted into chloride phase, By the vacuum distillation, a mixture of neodymium and dysprosium trichlorides of 99.2 % purity was recovered, On the other hand, the rare earth chlorides can be converted to the corresponding oxides by a pyrohydrolysis reaction accompanied by a formation of HCl gas, The HCI gas can chlorinate metallic iron to FeCh, Therefore, a new recycling process for rare earth magnet waste can be realized as a chlorine circulation type process. During the process, only carbon and water are consumed and there are no toxic pollutants, Moreover, the obtained rare earth oxide can be directly used as raw material in the conventional oxide electrolysis process,

Jan 1, 2003

By I. Gaballah

Decontamination of synthetic solutions of copper acetate, chloride, nitrate and sulfate containing 10, 100 and 1000 ppm of copper, using chemically treated barks has been studied. Metal percent removal from solutions depends on the pH and the initial concentration and to some extent on the salt used. It varies from 40 to 99 % of the solution initial metallic ion's content. The maximum retention capacity of the treated bark varies from 31 to 43 mg of Cu per gram of dry modified bark. Bark loaded with copper had been analysed by Scanning Electron Microscopy and lnfra Red spectroscopy. Cu is uniformally distributed in the bulk of the bark. No copper segregation is observed. It seems that copper is bound to the acidic sites of the bark. Anions are not detected on the copper loaded bark neither with the SEM or with the IR spectroscopy.

Jan 1, 1993

By Francis C. Furman

Microscopic evidence indicates that the high sinterability of certain commercial dolomites is tied to specific dolomite textural characteristics. This study encompasses detailed characterization of the unprocessed dolomite and sintering doloma results. The chemical and mineralogical compositions, insoluble residue, chemistry homogeneity, crystal size, primary carbonate texture, secondary dolomite texture, deformation structure, porosity type, porosity, and density of the raw dolomite were observed. These characteristics are compared with sintering trials of <74um powder-compacts samples in which holding times were varied. The evolution of the dolomite characteristics are reviewed and related to the final sintered doloma characteristics. The critical characteristics of a single-stage sintering brick dolomite are the following: 1) primary oolitic texture, 2) dolomite purity, 3) dolomite stoichiometry 4) minimal impurities, less than 1 weight {%} Fe2O3 Al2O3 and SiO2, 5) chemical homogeneity, 6) high density, 7) very low porosity, S) very coarse homogeneous crystallinity, 9) nonplanar dolomite texture, 10) abundant strain related slip microdeformation structures, 11) minimal subsequent alteration. Even with grinding to <74um the nonplanar dolomite texture and slip deformation still have a major effect on doloma sintered density. The three newly identified characteristics of single-stage sintered refractory brick dolomite are their primary oolitic texture, secondary nonplanar texture and abundance of stress related microdeformation structures. The primary oolitic texture reflects a homogeneous pure carbonate with respect to chemistry and crystal size secondary nonplanar texture produces crystals with large surface area to volume ratio. Stress related slip deformation moves CO, groups in to the same site of another CO, group but different orientation which is very unstable. All of these characteristics may facilitate the formation of higher density dolorna sinters.

Jan 1, 1995

By P. J. Uggowitzer, H. Kaufmann

"New Rheocasting is a novel route of semi-solid casting, in which the globular semi-solid precursor material is produced by controlled cooling of only slightly superheated melts in conventional steel crucibles. The resulting semi-solid slugs are placed into the sleeve of a vertical Squeeze Casting Machine and then filled into steel dies. Solidification occurs under hydraulic pressures up to 100 MPa Due to the reduced cost of precursor material, reduced investment cost and easier recycling, the New Rheocasting process offers cost reductions of up to 25% over conventional semi-solid casting · routes. The New Rheocast products are pore free, pressure tight, weldable and heat treatable castings.In the present work the New Rheocasting Process is introduced and the influence of heat treatment on mechanical properties of the New Rheocast alloy A356 is discussed.The alloy A356 is cast under ideal New Rheocasting conditions into a step die on an UBE HVSC 350 Squeeze Casting machine. As-east, TS and T6 heat treatment conditions with variations in solutionizing and aging time/temperature parameters are applied and the samples are tested by tensile testing. Alternatively, the same heat treatment conditions are applied to conventional Squeeze Casting parts and compared with New Rheocasting.Questions of potential cost savings due to modified heat treatment conditions are also addressed in this paper."

Jan 1, 2000

By Ivo André

Sorption of copper ions from aqueous solutions by dried biomass of the aquatic plant Potamogeton luscens was studied at laboratory scale. The aquatic plant was collected in water resources in Brazil, washed, dried at 60°C and ground in a bladed mixer. Sorption experiments were conducted in agitated flasks and in a packed bed column. Maximum copper removal was obtained between pH 5.0 and 6.6 when copper was present in the ionic form Cu&apos;. Sorption followed the Langmuir isotherm with saturation attained at 35 mg/g. Free energy of sorption was found, to be of the order of -25 kJ/mol. Sorption kinetics data were better described by a second order reaction and rate constants were calculated in 0.030 1/(min.mg) for - 4.0 mm particles and 0.081 1/(min.mg) for - 0.59 mm particles. Removal of metal ions in a packed bed column showed that Potamogeton luscens biomass can be used in several sorption/dessorption cycles. After sorbent saturation, copper ions can be recovered from the loaded biomass by elution-with H2SO4, solution. Main mechanism responsible for heavy metal uptake was found to be ion exchange. Results are discussed in terms of the surface properties of the biomaterial, solution chemistry of copper ions and thermodynamics parameters.

Jan 1, 1995