Search Documents

By John W. Lane, Richard A. Ronzio, Frederick N. Bender

Climax Molybdenum Co. operated a hydrometallurgical plant at Climax, Colo., from August 1966 to August 1968 to recover molybdenum from an oxidized ore. The feed, tailings from sulfide flotation, was first upgraded by cycloning. The concentration plant handled 6000 tpd of feed and produced 2000 tpd of slime concentrate. The concentrate was leached by a sulfuric-sulfurous acid solution at 65°C. The molybdenum was solubilized in the form of "molybdenum blue." Activated charcoal was added to the leach tailings in a resin-in-pulp type circuit. Molybdenum was adsorbed on the charcoal. The charcoal was screened from the pulp and washed. The washed charcoal was pumped to columns where it was ammoniated and air-blown. The oxidized molybdate then was washed from the charcoal. The eluate was evaporated until ammonium dimolybdate crystallized out. The ammonium dimolybdate was calcined to molybdenum trioxide.

Jan 1, 1973

By W. J. Reagan

All of the material described in the following paper is within the following specifications: carbon, 0.50 to 0.85 per cent; phosphorus and sulfur, 0.04 per cent max.; manganese, 0.60 to 0.85 per cent; silicon, 0.20 to 0.30 per cent. Steels with much lower carbon contents can be handled in exactly the same manner. One of the first things necessary to basic open-hearth slag control is uniformity of charge, particularly as to the silicon content and the percentage of lime charged. Our past work has shown that the silicon content of the charge is more important than the carbon content in determining the carbon at which a heat will melt. We have found that by keeping the silicon content of the charge about 0.60 to 0.65 per cent, and with a lime charge of about 7 per cent (limestone equivalent), our heats melt sufficiently high in carbon to allow a moderate feed of ore and the slag will be of low iron oxide content. In making a heat of 0.75 carbon steel we endeavor to have the heat melt at about 1.20 per cent carbon. The iron oxide content of the finishing slag depends upon the final phosphorus desired; for a given ratio of lime-silica in the slag, the lower the phosphorus desired in the final steel, the higher the iron oxide content of the finishing slag must be. By reducing the lime charge to a minimum, the heats melt faster, and by keeping the silicon content at the desired figure the heats melt with a high SiO2 slag, which has been shown in previous work to give a low iron oxide slag. In most of our work, using a 180,000-lb. charge and with basic pig containing about 1.20 per cent silicon, we use a lime charge of 8500 lb. of limestone and 2000 lb. of burnt lime. The pig charge is about 48 per cent of cold pig, and the charge contains a large percentage of works scrap. This causes a heat to melt with about 1.20 to 1.30 per cent carbon, for a heat that will finish about 0.75 per cent carbon. This gives a heat that will need a feed of about 2000 lb. of ore, and also a slag with an FeO content of about 4 to 5 per cent at melting. The additional FeO obtained from the ore addition will bring the FeO in the slag at tapping to about 6 to 7 per cent. It is necessary to carry quite a fluid slag to prevent pickup of FeO, as a too heavy slag causes FeO to build up in it, giving a finishing slag with a greater FeO than is desired. By adjusting the lime charge of a basic open-hearth heat, a very sensitive adjustment of the slag may be obtained. The figures in Table 1

Jan 1, 1935

By W. J. Reagan

All of the material described in the following paper is within the following specifications: carbon, 0.50 to 0.85 per cent; phosphorus and sulfur, 0.04 per cent max.; manganese, 0.60 to 0.85 per cent; silicon, 0.20 to 0.30 per cent. Steels with much lower carbon contents can be handled in exactly the same manner. One of the first things necessary to basic open-hearth slag control is uniformity of charge, particularly as to the silicon content and the percentage of lime charged. Our past work has shown that the silicon content of the charge is more important than the carbon content in determining the carbon at which a heat will melt. We have found that by keeping the silicon content of the charge about 0.60 to 0.65 per cent, and with a lime charge of about 7 per cent (limestone equivalent), our heats melt sufficiently high in carbon to allow a moderate feed of ore and the slag will be of low iron oxide content. In making a heat of 0.75 carbon steel we endeavor to have the heat melt at about 1.20 per cent carbon. The iron oxide content of the finishing slag depends upon the final phosphorus desired; for a given ratio of lime-silica in the slag, the lower the phosphorus desired in the final steel, the higher the iron oxide content of the finishing slag must be. By reducing the lime charge to a minimum, the heats melt faster, and by keeping the silicon content at the desired figure the heats melt with a high SiO2 slag, which has been shown in previous work to give a low iron oxide slag. In most of our work, using a 180,000-lb. charge and with basic pig containing about 1.20 per cent silicon, we use a lime charge of 8500 lb. of limestone and 2000 lb. of burnt lime. The pig charge is about 48 per cent of cold pig, and the charge contains a large percentage of works scrap. This causes a heat to melt with about 1.20 to 1.30 per cent carbon, for a heat that will finish about 0.75 per cent carbon. This gives a heat that will need a feed of about 2000 lb. of ore, and also a slag with an FeO content of about 4 to 5 per cent at melting. The additional FeO obtained from the ore addition will bring the FeO in the slag at tapping to about 6 to 7 per cent. It is necessary to carry quite a fluid slag to prevent pickup of FeO, as a too heavy slag causes FeO to build up in it, giving a finishing slag with a greater FeO than is desired. By adjusting the lime charge of a basic open-hearth heat, a very sensitive adjustment of the slag may be obtained. The figures in Table 1

Jan 1, 1935

By E. S. Machlin

RECENTLY, there has been much activity in the field of nucleation of martensitic transformations.'- One of the problems in this field is the calculation of the rate of nucleation (number of plates nucleated per unit untransformed volume per unit time) in terms of observable parameters. Two such observable parameters are the fraction of the length of a straight line which corresponds to the portion of the total length of the line that lies in the martensitic phase and the number of plates intersected by this straight line per unit length of line. Because of the necessity of a valid answer to this problem, the following investigation was undertaken. Although this problem has been treated in the past, a derivation of the relation between the volume and linear fractions of martensite will be described to illustrate the method used in the succeeding analyses. It is assumed that the martensitic plates are in the form of a right circular cylinder having a small height relative to the radius of the base. The volume fraction of martensite is then: fr = lXNl,hjAl [1] where f, is the volume fraction of martensite, and Nij is the number of plates per unit total volume having the area Ai and the height hi. The linear fraction of martensite is obtained as follows. For the plates having the particular area A, and height h,, the fraction sin 0 dB* will have their cylinder axes between the angles 0 and 0 + d0 to the straight line along which the linear fraction of mar-

Jan 1, 1953

By D. J. McAdam

IN a recent survey of the literature, the author has found evidence incompatible with prevalent views regarding the technical cohesive strength and yield strength of metals. Some of the evidence regarding the technical cohesive strength was presented in a previous paper,21 and views were presented that are believed to be in better accord with the evidence. In that paper, it was shown that the technical cohesion limit (contrary to prevalent views) varies with the combination of principal stresses,† and that the influence of plastic deformation on the technical cohesive strength is not in accordance with prevalent views. In this paper, consideration will be given to both the technical cohesion limit and the yield stress as affected by the combination of principal stresses. Evidence will be presented that the variations of the yield stress and the technical cohesion limit with the combination of principal stresses are not in accordance with prevalent views. Consideration will also be given to ductility and work-hardening capacity, which depend on the initial difference between the technical cohesion limit and the yield stress. By the "technical cohesion limit" is meant the mean stress at actual or potential* fracture. An example of a technical cohesion limit is the "true" breaking stress of a tension-test specimen, the breaking load divided by the sectional area at fracture. The cohesion limit thus obtained for a ductile metal, however, has been greatly altered by the plastic deformation. It is important to consider the cohesion limit of the metal prior to this deformation, and the variation of the cohesive strength with plastic deformation. The relation between the cohesion limit and the corresponding flow stress† determines the ductility of a metal and the energy that it will absorb before fracture. In this paper, as in the previous paper,21 tensile stresses will be viewed as positive and compressive stresses as negative. The algebraically greatest principal stress will be designated S1, the least principal stress will be designated S3, and the intermediate principal stress will be designated S2. In the previous paper, attention was confined to stress combinations with two of the principal stresses equal (with the intermediate principal stress S2 equal either to S3 or S1). In this paper, consideration will also be given to the effect of stress combinations with all three principal stresses unequal. In the earlier sections of the paper (pp. 1 to 14), attention will be confined to stress combinations with

Jan 1, 1942

By F. D. Mahone

Much crude oil, as produced from the well, carries varying amounts of water, which may be present as free water in globules sufficiently large to settle out, in time, if the fluid is allowed to stand, or as an emulsion formed by myriads of minute water particles, each surrounded and entrapped by a film of oil through which it cannot break under the action of gravity alone. Such an emulsified mixture of oil and water is commonly termed "cut oil." When such an emulsion is subjected, under proper conditions, to the influence of a high-potential alternating-current field, the minute water particles rupture the enveloping oil films and coalesce into larger water droplets this procedure continuing until all the water is freed into drops of such size that they readily settle out. This action has been photographed by the micro-moving-picture camera; under the microscope, the breaking-up of the emulsion, as described, is seen to be accomplished in a few seconds. The low power requirements of the process, from records of commercial plants, substantiate the theory that the action is that of a multitude of electrical condensers in series, rather than that of a number of conducting paths. The minute water particles serve as the metallic elements, or plates, of the condensers and the separating oil acts as the dielectric. Such surface charges as the particles may have are removed, and the intervening oil is broken, probably electrically by the voltage and mechanically by the attractive force between adjacent oppositely electrified particles. The principle of breaking up an emulsion under the influence of an alternating electric field was discovered by F. G. Cottrell and Buckner Speed, through experiments conducted, at the University of California, which resulted in a plant being installed on the property of the Lucile Oil Co. in the Coalinga field, California, early in 1909. This plant was able to reduce 14-per cent. emulsion to less than Pper cent. with commercial success. Standard Cottrell Apparatus The present standard Cottrell apparatus consists essentially of the electric treater and a settling or trap tank. The treater is a galvanized-iron tank approximately 3 ft. in diameter and 10 ft. high, which con-

Jan 1, 1924

By P. Schwarzkopf, J. H. Brophy

A modification of the Mendenhall wedge blackbody1 has been used to determine solidus temperatures and to anneal alloys in the tantalum-rhenium binary system. The technique has proven to be simple and accurate with modest power requirements. For temperatures up to 2800° C a piece of 10-mil tantalum sheet was folded double and formed as shown in Fig. 1. The middle of the resulting ribbon filament was a cylindrical-shaped crucible with less than a 1/8-in. opening. After inserting a specimen in the cavity, the filament was clamped between molybdenum electrodes in a high vacuum chamber. A representative filament 2 in. long and % in. deep was heated to 2800°C with a current of 700 amp at 4 v. The specimen temperature was determined by sighting into the cavity with a Leeds and Northrup optical pyrometer. The twisted filament shape was necessary to avoid serious geometric changes during thermal expansion. For temperatures between 2800" and 3000°C a 4-mil tungsten filament was employed. To facilitate fabrication it was warm-folded, and a twisted segment of 10-mil tantalum was used to support one end to absorb thermal expansion. This element assembly required about 700 amp at 10 v to reach 3000°C. Two geometric modifications of the filament were helpful for solidus temperature determinations. A shallow chamber, with depth to opening ratio of 3 to 1, permitted direct observation of the specimen through the optical pyrometer. The fact that the specimen was visible permitted the melting point to be determined when sharp features on the specimen surface became rounded; it also indicated that blackbody conditions did not prevail. By standardizing against the melting point of molybdenum, the observed melting temperature was corrected by the following form of Wien's Law: in which T is the true temperature, To is the observed temperature, and K is a constant characteristic of the filament geometry and determined experimentally for the molybdenum standard. The resulting corrected melting point for each alloy served as a reference temperature for the second more precise filament geometry. With a 6 to 1 depth to opening ratio, the specimen was indistinguishable from the filament interior, indicating good blackbody conditions. Using this technique, a series of specimens was isothermally treated at temperatures above and below the corrected direct reading. Incipient melting was detected by visual or micrographic examination of the specimen after cooling. This procedure was checked with specimens of pure chromium, molybdenum, and tantalum. Table I represents the values obtained, together with the solidus temperatures in the tantalum-rhenium binary system determined by the same technique. The alloy specimens were approximately 1/8 in. in diam. They were pieces of 10-g buttons melted four times in a nonconsumable tungsten electrode arc furnace on a water cooled copper hearth in 2/3 atmos of titanium gettered helium. Several sources of error are possible in such temperature measurements. Within the accuracy of the pyrometer no gradients were detectable near the specimen, and element distortion was virtually eliminated by twisting the tantalum. Compensation was made for the 1/8-in. sight glass by inserting several identical thicknesses and extrapolating to zero thickness. As a result an additional 10°C correction was added to all observations in the temperature range of 2500" to 3000°C. The principal source of error was then in the operation of the

Jan 1, 1961

By A. P. Young, F. C. Holden

IN many of the early investigations of the aging of titanium alloys, it was observed that the retained beta phase could be aged to a high hardness without an apparent change in microstructure; moreover, in some alloys it was found that even a very rapid quench produced beta having an anomalously high hardness. What appeared to be hard beta phase was designated as "beta prime," to distinguish it from the softer normal retained beta phase. Frost and co-workers'.' demonstrated that the increased hardness is caused by the formation of a metastable phase, omega, which can be identified from its X-ray diffraction pattern. This reaction also has been studied by Brotzen, et a1.,3 and the structure of the omega phase has been published by Silcock, et al.," and by Austin and Doig.3 The X-ray diffraction analysis by Austin and Doig indicated that omega is low in alloy content, approaching the composition of the stable alpha. The aging process proceeds by the path Thus, overaging results in the formation of alpha and the ultimate disappearance of omega. This is accompanied by a decrease in hardness and a recovery of ductility. The present work represents a study of the aging process in a high-purity Ti-6.4 Mn alloy, in which optical and electron microscopy, X-ray diffraction, and hardness data were correlated. The specimens, 1/8-in. sections cut from 1/4-in.-diam rod, were heated in argon to a temperature just into the beta field (810°C), held for 1 hr, and water-quenched. The aging samples were heated in air for 1 hr at 300 to 500°C. The specimens were ground and mechanically polished, finishing with alternate etching and polishing on a slow-speed wheel to remove disturbed metal from the surface. The surface finally was swab-etched, rinsed with tap water, and air-dried. The etchant used was an aqueous solution containing 1 1/2 pct HF and 3 1/2 pct HNO3. This procedure is identical with that used for preparing metallographic specimens, except that the optimum degree of final etching required for electron microscopy may vary from that used for light microscopy. Metal replicas, backed with silica, were prepared from plastic strip-pings for examination with the electron microscope. Complete details of the procedures used for preparing these replicas are available elsewhere." Fig. 1 shows a comparison between the structures revealed by the electron microscope and those obtained by conventional light microscopy. Hardness and X-ray diffraction data are listed in Table I. No evidence of a second phase is apparent in the optical micrographs for the as-quenched sample, or for the specimens aged at 300 or 400°C; fine alpha particles can be seen in the specimen aged at 500°C. In the electron micrographs, visible equiaxed pocks appear in the as-quenched specimen, and, with increasing density, in the samples aged at 300 and 400°C. After aging at 500°C, the structure becomes markedly coarser and develops an oriented appearance of a second phase, coincident with the appearance of visible alpha particles in the light micrographs. These observations are confirmed by X-ray diffraction and hardness data. In these specimens, aged for 1 hr, the intensity of the omega pattern increases to a maximum at the 400°C aging temperature, corresponding to maximum hardness and the maximum density of pocks in the electron micrographs. At this point the beta phase shows a definite enrichment in Mn. At 500°C, little or no omega re-

Jan 1, 1959

By Charles P. Williams

The lead-bearing area of Missouri has been subdivided, geographically, into the Southeastern, the Central, and the Southwestern

By R. Maddin, R. Pond

THERE have been many recent studies of nonequi-librium alloy structures using specimens which have been formed by rapid solidification.' The general methods for achieving nonequilibrium structure utilize high velocity impingement of a liquid metallic droplet(s) and one or more substrates of relatively high heat conductivity. Specimens formed by current popular techniques are small and have various forms of irregular geometry which severely limit their use for many measurements of physical or mechanical properties. As a result of geometric limitations most research has been restricted to X-ray diffraction, electron microscopy, and to a small degree, electrical resistivity. Recently several attempts in mechanical property evaluation have been reported.2,3 A technique for casting large quantities of regular, rectilinear, continuous metallic fibers has existed for a number of years.4 We have utilized this technique with some slight modifications to produce nonequi- librium alloy structures. The apparatus is composed of a small open tube furnace, a pneumatic cage which raises and lowers a graphite ejection mold, and a

Jan 1, 1970

By Leonard Obert

The structural stability of any mine or under- ground opening in rock is dependent on the stress field, that is, the state of stress in rock before mining, the stress distribution in the rock created by the opening, and the in situ strength of the rock. In the past mine design problems have been considered by assuming that the stress field is due only to the weight of the overlying rock, the stress around the opening can be calculated from elastic theory using laboratory-determined elastic constants, and the in situ strength of the rock can be determined from laboratory tests on small specimens. Solutions to hypothetical problems using this procedure are given in a report by Obert, Duvall, and Merrill.' Because of the uncertainties of these assumptions, this method can give only a rough approximation to the solution of actual structural problems. Obviously, this approach to determining the stability of underground openings would be greatly improved if the rock stress could be measured in situ, and it is undoubtedly for this reason that in recent years many investigators have spent considerable effort on the development of procedures for measuring rock stress. In this report a method is described for determining in situ the absolute stress in rock. The method requires the measurement of the deformation of a borehole before and after the rock is stress-relieved. The magnitude and direction of the applied stresses are calculated from the borehole deformation and modulus of elasticity of the rock. Also, the results of absolute stress determination made in the walls and pillars of underground openings in five rock types are presented. From these results a number of conclusions are drawn regarding the accuracy and limitations of this method and the problem of stress measurements in general.

Jan 8, 1962

The Engineers Society of Western Pennsylvania, William Penn Hotel, Pittsburgh, Pa. K. F. Treschow, Secretary Since 1880 this society has been publishing Proceedings containing papers on a wide variety of engineering and related subjects The Proceedings are issued monthly throughout the year (except for the months of August and September each year) and the monthly Proceedings from February of one year to and including January of the next are also collected in volumes The latest is vol 47, for 1931 The rate of subscription for the monthly Proceedings is $5 per year throughout the Postal Union, single copies (monthly), 50 cents each The price of the yearly volumes from vol 17 to date is $5 each, unbound. The Secretary will quote prices for

Jan 1, 1933

This brief resume of events, transpiring in Mexico, culled front the daily New York newspapers, since the last Bulletin-went to press, does not indicate any degree of improvement in the situation. RECORDS OF 217 MEXICO KILLINGS SUBMITTED BY AMBASSADOR FLETCHER Henry P. Fletcher, the American Ambassador to Mexico, called as the first witness before the Rules Committee of the House which has begun a preliminary inquiry into conditions in Mexico, which, it, is believed, will lead to a thorough and far-reaching investigation by a joint Senate and House Committee of the entire Mexican problem, submitted a list of the names of Americans officially known to have been killed in Mexico, a majority of them murdered in cold blood, since the overthrow of Porfirio Diaz by Maderoin 1911. The list contains 217 names and in comparatively few instances do the records show that arrests were made by the particular Mexican faction that happened to be in power where the crime was committed. In only one instance, that of John B. McManus, who was killed in March, 1915, was reparation made. It is significant that McManus was killed by Zapatistas, and Zapata officials apologized for the crime and paid to Mrs. McManus a voluntary indemnity of $20,000 in gold. Of the 217 persons listed as victims of the Mexicans, .137 perished since Carranza came into power. The list, it was admitted, is not complete. It was evident, says the New York Times, that the Ambassador considered the situation very serious.

Jan 9, 1919

By W. C. Winegard, C. Elbaum, T. Ojala

NONOCTAHEDRAL slip was observed in poly- crystalline aggregates of aluminum by Boas and Ogilvie.&apos; These authors indicate that the non-octahedral slip takes place on (100) or (110) planes. Ogilvie2 studied the continuity of slip lines across grain boundaries in polycrystalline aluminum. Non-octahedral slip was observed by him, but it was not reported to occur in the continuous slip lines across the grain boundaries, which were identified as octahedral slip in all cases. The present note reports the observation of non-octahedral slip in the grain boundary region of an aluminum bicrystal and tricrystal, both deformed in tension at room temperature. An analysis is made, which leads to a probable identification of the non-octahedral slip planes as (110) and (331). The specimens used were of rectangular cross section, approximately 5x10x200 mm. They were prepared by growth from the melt, using aluminum reported by the manufacturer to be 99.994 pct pure. The grain boundaries were in a plane perpendicular to the wider face and parallel to the long dimension of the specimens. The axis of tension was also parallel to the long dimension of the specimen. The orientations of the specimens studied were determined by the Laue back-reflection method and are given in Fig. 1. The nonoctahedral slip was first observed after about 6 pct extension in the bicrystal, and after about 2 pct extension in the tricrystal. The micrograph, Fig. 2, of the grain boundary region of the bicrystal shows two active slip planes throughout each of the two crystals, with a third plane active at the grain boundary in each crystal. Two major sets of slip traces observed in grain No. 1 are consistent with the operation of the slip systems (ill) [oil] and (111) [011]. The nonoctahedral slip takes place on a plane belonging to a <111> zone, as determined by drawing trace normals. Assuming that slip will take place only in the <110> direction, the planes in the <111> zone, which do not contain that direction, need not be considered. Among the remaining prominent planes of that zone, the (011) plane has a common slip direction—the [011]—with the (111) plane, which acts as one of the octahedral slip planes. In grain No. 2, a similar situation to that in grain No. 1 is observed. As indicated previously, the (oil) plane in the <111> zone, to which the nonoctahedral slip plane belongs, has a common [Oil] slip direction with the acting (ill) slip plane. Also, the orientation of the (oil) plane in grain No. 2 almost coincides with the orientation of the acting (111) slip plane in grain No. 1. Similarly, the orientation of the (oil) plane in grain No. 1 almost coincides with the orientation of the acting (111) slip plane in grain No. 2. It is, therefore, possible that the nonoctahedral slip was induced, in both cases, by octahedral slip in the neighboring grain. It is important

Jan 1, 1957

By Peter Soo

Pvestrained Ferrovac E iron has been neutron-irradiated at approximately 90°C to an integrated flux of 1020 nut (E > 0.82 mev]. The irradiation was found to produce an incveased temperature dependence of the flow stress in addition to a greatly increased athemal stress. Measurements of the flow stress and stress relaxation, from which the activation volume and activation energy for slip were deduced, show that neutron irradiation changes the rate -controlling slip process to one based on dislocation interactions with tetragonal distortions which are Produced around submicroscopic interstitial loops in the lattice. The study indicates that without prestraining prior to irradiation the chances of detecting a change in the rate -controlling slip process are greatly reduced because in the initial stages of slip a substantial fraction of the radiation defects are swept out of the slip plane by gliding dislocations. Thus, activation parameters which are subsequently measured are representative of a greatly reduced defect density and would not differ appreciably from those for unirradi-ated material. The large increase in the athermal component of the flow stress is probably connected with the presence of depleted zones in the lattice which are introduced by irradiation. ALTHOUGH fast neutron-irradiation has not been observed to markedly alter the activation parameters for slip in bcc metals,&apos; small but significant changes do occur. Most experimenters agree that irradiation predominantly increases the athermal component of the yield stress.&apos;-= In addition to this, Laidler and smidt7 have shown that in iron irradiated to 5 X 10" nvt and molybdenum irradiated to 10" nvt, changes occur in the activation volumes for slip. A similar conclusion has been reached by Milasin and Malkin8 for irradiated iron. Work by Ohr et a1.5 shows that for Ferrovac E iron, irradiated to 1.2 X 1016 nvt, small increases in the activation energy for slip also occur. So far these changes in the activation parameters have not been explained on a firm theoretical basis. One important factor which would minimize the chances of detecting a change in the slip mechanism upon irradiation is the presence of "channeling" which has been observed in molybdenum,9 niobium,10 and iron.11These channels are formed by gliding dislocations which sweep irradiation defects out of the active slip planes and thereby create zones in which continued dislocation motion is encouraged. The activation parameters for the dislocations gliding in the defect-free channels would, therefore, be similar to those for unirradiated iron and a change in the rate-controlling slip process would be difficult to detect. In the present work, an attempt has been made to reduce the effect of uneven deformation on the measured activation parameters for slip in neutron-irradiated Ferrovac E iron polycrystals, so that a more realistic assessment of the effects of neutron-irradiation could be made. Primarily, the experiments involve the irradiation of specimens which had been prestrained to 9 pct elongation at room temperature prior to insertion into the reactor. It was hoped that the introduction of a large number of evenly distributed dislocations would substantially decrease any channeling effect which might otherwise occur. MATERIAL AND EXPERIMENTAL PROCEDURE The starting material was vacuum-melted Ferrovac E iron, an analysis of which is given in Table I. The standard tensile specimen had a gage length of 1.125 in., a cross-sectional diameter of 0.120 in., and a re-crystallized grain size of 1.2 x 10-3 in. All tensile tests were conducted on a floor model "Instron" tensile machine at a strain rate of 3 x 10-4 per sec. The irradiation of the prestrained specimens was performed in the Brookhaven High Flux Beam Reactor to an integrated flux of 1020 nvt (E > 0.82 mev) at a temperature of about 90°C. All specimens were excap-sulated in high-purity aluminum sheaths which were lightly swaged around the samples to ensure good thermal contact. Subsequent measurements on the irradiated specimens showed that within experimental accuracy the swaging had not deformed them. EXPERIMENTAL RESULTS Fig. 1 shows the flow stresses for a series of unirradiated control samples. In order to produce a comparable dislocation substructure throughout the test sm range, all specimens were prestrained

Jan 1, 1970

By J. A. Coll, R. W. Cahn, A. Lawley

WHILE the creep properties of pure face-centered-cubic and close-packed-hexagonal metals have been thoroughly investigated and are well established, body-centered-cubic metals have been studied less extensively. Moreover, very few fundamental studies on the creep of solid solutions, irrespective of crystal structure, have been reported. The present study is concerned with the creep of a series of body-centered-cubic solid solutions. The present position concerning creep of pure metals is, briefly, as follows.1"3 Creep at first takes place at a steadily decreasing rate; this is the stage termed primary or transient creep. Except at the lowest temperatures this is succeeded by a stage of secondary or steady-state creep. At high temperatures and stresses, this may be succeeded by an accelerating stage, termed tertiary creep, with which we shall not here be concerned. There is no well-defined physical model at present for the transient stage; in general terms, transient creep is best regarded simply as a manifestation of work-harden ing. Steady-stage creep can certainly take place by several different mechanisms: the choice of dominant mechanism depends primarily on temperature. We shall here be concerned only with high-temperature steady-state creep, a term usually reserved for creep at absolute temperatures higher than 0.5 Tm, where T, is the melting point. In this range, the activation energy for creep is, for many metals, equal to the activation energy for self-diffusion, and this is generally interpreted in terms of a "climb mechanism.1-4 The creep rate is determined by the speed at which dislocations, impeded by obstacles the nature of which is disputed but which are probably established during transient creep, can climb by means of a diffusion process, until they are able to by-pass the obstacle. In solid solutions, the intrinsic resistance to the slip motion of dislocations may be much larger than in the solvent, to the extent that the motion of dislocations in the glide plane, rather than their escape by climb out of this plane, may become the rate-controlling factor. weertman5 has considered this possibility from a theoretical point of view, and concluded that some form of "viscous slip" is likely to be rate-controlling at comparatively low stresses. The resistance to slip may arise from "atmospheres" of impurities forming around dislocations; a high Peierls force in materials of high cohesion; or some structural peculiarity such as clustering or ordering of solute atoms.= We shall be concerned here with the case of ordering. The only published investigations concerned explicitly with the effect of order on creep refer to creep in ß-brass by Herman and Brown,7 and in Ni-Fe alloys, by Kornilov and panasyuk8 and by Suzuki and Yamamoto.9 Recently, Herman and Brown&apos;s paper has been supplemented by a determination of the tensile yield point of ß-brass as a function of temperature.10 Both studies showed a sharp drop in resistance to deformation of ß-brass over a range of a few degrees just above the critical temperature Tc at which order finally disappears. These observations are especially noteworthy, because in ß brass the degree of order diminishes steadzly to zero as the temperature approaches Tc. It is, therefore, the disappearance of the last traces of long-range order which has the largest effect on the resistance of the alloy to plastic deformation. In the Ni/Fe alloys of various compositions, resistance to creep at a given temperature and stress is maximum at the stoichiometric composition, both below Tc, (long-range order), and above T,. (short-range order).&apos; Near Tc, the creep resistance of an ordered alloy is much higher than that of the same alloy in the disordered condition.9 The aim of the present investigation was to study the creep behavior in the neighborhood of Tc, of another system of ordering alloys. The iron-aluminum alloys were considered the most suitable. because: i) The order again diminishes steadily to zero as the temperature approaches Tc; there is no sudden drop in order at Tc, and it therefore is

Jan 1, 1961

By S. Feuerstein, L. Rice

The effect of low pressures on the flow and fracture behavior of molybdenum is described. For poly crystalline samples, room-temperature tensile tests indicate greater ductility under 10 Torr than under intermediate pressures up to and including atmospheric pressure (760 Torr). In addition, tests conducted at 760 Torr under atmospheres of air, dry nitrogen, and purified argon exhibited no apparent difference in mechanical properties. Critical tests involving baking in situ as well as those involving single-crystal deformation further imply that the ductility effect is a pressure-dependent phenomenon related only to the fracture process. This dependency is discussed in terms of adsorption and diffusion contributions. THE effect of very low pressures on material properties has heretofore been presumed to be important only for substances possessing relatively high vapor pressures at ambient temperatures. Research has therefore been concentrated primarily on organic solids and liquids, and in some instances on metals such as zinc and cadmium. Most vacuum-effect studies&apos; on the mechanical behavior of metals have been performed under conditions of either cyclic loading or creep rupture at elevated temperatures, i.e., over extended time periods. These studies were not restricted to high vapor pressure materials but also encompassed such metals as gold, copper, and nickel. Very little concern, however, was placed upon the importance of a vacuum environment on the mechanical behavior of metals subjected to a simple unidirectional deformation at ambient temperatures. A tension test is generally of short duration as compared to a creep test, and at room temperature vacuum effects if any would be expected to be surface-limited. In early 1963, Kramer and podlaseck2 reported a change in the bulk flow behavior of aluminum single crystals during room-temperature tension tests. The deformations were performed under pressure conditions of 760 to 3.4 X 10-8 Torr and indicated for the first time a vacuum surface effect contributing to the bulk tensile behavior of metal specimens. As a consequence, an experimental program was initiated in this Laboratory to study the effects of ultrahigh-vacuum conditions on the mechanical behavior of metals. The results of a preliminary study on poly-crystalline molybdenum3 revealed, unlike Kramer&apos;s observations of changes in the stress-strain behavior, only an increased ductility under ultrahigh vacuum. Flow behaviors were nearly identical for all tests re- gardless of pressure. This paper presents comprehensive results obtained in this area of research. 1) EXPERIMENTAL PROCEDURE Three material categories were used in this study: sintered and are-cast polycrystalline molybdenum of nominal purity 99.93+ pct and single-pass electron-beam zone-refined molybdenum single crystals having a nominal purity level of 99.99+ pct. The interstitial levels (weight percent) as determined by the Materials Testing Laboratories, Division of Magnaflux Corp., were as follows: sintered molybdenum (C— 0.005, H—0.0004, O—0.015, N—0.008); and arc-cast molybdenum (C-0.0038, H-0.0003, O-0.015, N-0.023). Single-crystal molybdenum obtained from Materials Research Corp. had a typical interstitial analysis of C-0.0015, H-0.00007, O—0.00045, and N-0.0001. Tensile specimens having a 5 mm diam by 50.8 mm length were prepared from these materials. An average grain diameter of 0.059 mm was obtained for the sintered specimens following a 4-hr, 1600°C heat treatment. Grain sizes from 0.019 to 0.149 mm were obtained in the arc-cast specimens following heat treatments from 1100° to 1600°C for 1 hr. This series of specimens was used exclusively for the grain-size effect studies. All samples were electrolytically polished in 97 pct sulfuric acid solution prior to testing. Experiments were performed at room temperature in an ion-pumped ultrahigh-vacuum system positioned in an Instron tensile machine, Fig. 1. A constant strain rate of 4.2 x 10-4 sec-1 as derived from crosshead displacement was assumed for the deformations. Starting vacuums ranged from 2 to 0.5 X 10-10 Torr. These pressure measurements were made using corrected values4 of an NRC Redhead gage. Comparative readings were also made against a G.E. triggered dis-

Jan 1, 1967

By M. M. Rao, P. G. Winchell

The growth rates of bainitic plates were measured at 400°C in Fe-Ni-C alloys containing 0.10 atom-fract~on nickel and 0.0012 to 0.0075 atonz-fraction carbon. The growth rates are adequately represented by where xc is nearly the atom fraction carbon of the bulk austenite and PXCy is nearly the carbon atom fractlon in the ferrlte of radiids p In equilibrium with austetzite. The form of the equation is that predicted by a model in which carbon diffusion in austernite controls the gvowth, but the numerical constatnt is two orders of magnitude below that suggested by the model. THE growth of bainitic plates in steel is often assumed to be controlled by the diffusion of carbon away from the advancing plate tip. This hypothesis predicts that the growth rate will increase as the carbon content of the austenite, xCz, is reduced toward the carbon content of the saturated ferrite comprising the plate tip, PxCY The growth rate should vary approximately as (xCg- pxCy)-1. Experimental observation of the growth behavior at low carbon levels should provide a significant test of this model. An alloying element in addition to carbon is required so that low-carbon austenite can be experimentally observed while undergoing bainitic transformation. Nickel was selected. The presence of nickel complicates the interpretation of the data in two ways: First, diffusion of nickel during the transformation would make analysis very difficult. Nickel is assumed immobile during the transformation. Second, nickel affects the solubility of carbon in ferrite and austenite in equilibrium. This effect has been evaluated.&apos; At the completion of our experimental work Goode-now et al.2 published data in essential agreement with the observations to be reported here. Since their discussion is abbreviated and their data are scanty in the region of interest, we believe the present work is of significance. I) THE MODEL OF BAINITIC PLATE GROWTH The rate of lengthening of a plate is assumed to be controlled by the diffusion of carbon from the advancing ferrite-austenite interface into the surrounding austenite. The precipitation of carbides is assumed to be a secondary process. For ease of analysis the carbon-atom ratio,* pxCy, of austenite in equilibrium with ferrite which is convex with minimum curvature radius p, and the carbon-atom ratio, PxCY, of that ferrite in equilibrium with austenite are assumed independent of location on the ferrite-austenite interface. Since these carbon contents vary with the radius of curvature of the ferrite, p, their assumed positional independence must be held as an approximation. The consequences of these assumptions have been developed approximately by zener3 and Hillert,4 and the resulting equation for a platelet has been applied to bainite by Speich and cohen5 and Kaufman, Radcliffe, and Cohen.8 The Zener-Hillert equation* for plates is: The analysis of Hillert is supported by that of Hor-vay and cahn7 which involves no mathematical approximations but does include the assumption that the a/y interface coincides with an isoconcentration line. The solutions of Horvay and Cahn for elliptic paraboloids are replotted in Fig. 1. The shape of the paraboloid is expressed in terms of the ratio of the principal radii of curvature at its tip, A =p1/p2, which is also the ratio of the minor to the major axis of the elliptic cross section. The Zener-Hillert equation for plates is also plotted. The agreement is within a factor of two for (pxyaCr - xyC )/(xyC - PxCaY) between 0.5 and 100. This is the range of interest here and in most other work on bainite. The original form of the Zener-Hillert equation was the form given above with the right-hand side replaced by (pxCya -xCy)/(PxCya). This replacement is not appropriate here. 11) THE EXPERIMENTAL PROCEDURE Alloys were prepared and three kinds of experiments carried out. Continuous-cooling-transformation experiments were carried out on wires by measuring temperature and resistance during continuous cooling. Isothermal-transformation experiments were carried out on wires by measuring electrical resistance as a

Jan 1, 1968

By W. Rostoker, A. Siede

THE venerable problem of hydrogen embrittlement of ferritic iron lacks as yet a complete explanation. Possibly part of the difficulty has been the exclusive preoccupation with the total ductility prior to fracture. In the past few years it has been noted at least twice1,2 that hydrogen charged into iron has the ability to depress the upper yield point and, at room temperature, to eliminate completely the discontinuous yield phenomenon. Cracknell and Petchl rationalize that the depression of the yield stress is an example of the behavior of inhomogeneous stresses. Their explanation requires that microcracks exist in the annealed metal, and that hydrogen collect in these cavities under high hydrostatic pressure. The hydrostatic pressure of hydrogen generates localized tensile stresses in the iron which, with external loading, reach the critical stress for yield prematurely. The local plastic zones will spread across the specimen before the Lüders bands can be generated, and the yield-point elongation phenomenon is eliminated. This viewpoint will be discussed in succeeding paragraphs. Rogers,2 on the other hand, represents the depression of the initial flow stress as a result of the interaction of hydrogen with dislocations. He submits two alternative modes of interaction. In the

Jan 1, 1959

By J. W. Snavely

A practical mathematical treatment is presented for the determination and control of conveyor belt acceleration, particularly for conditions of starting where vertical curves are involved. A typical sample problem is analyzed, with required calculations, to clarify the procedure. THE part that acceleration plays in starting a belt conveyor and its effect on belt conveyor design are well understood in a general way. Its practical importance is easily overlooked, however, and under some conditions, it is absolutely necessary to give the problem of acceleration detailed study. Most handbooks on conveyor belting design adequately present basic data for the determination of acceleration values. This paper will only attempt to present practical thinking and a convenient method of treatment of acceleration in belt conveyor design. Mathematical Analysis In working out the various problems of conveyor belt acceleration, the starting point, as presented by the handbooks, is the familiar formula of "force of acceleration is equal to the mass times acceleration." By expressing these fundamental quantities in terms of belt conveyor design, it is possible to arrive at the unsuspected conclusion that the acceleration time for horizontal belt conveyors is independent of the load, and instead, dependent upon the belt speed, the type of drive arrangement and drive pulley, and the idler coefficient of friction. The mathematics leading to this conclusion are shown in Table I, which has been prepared to show this derivation. While at first the conclusion just given may not seem to be reasonable, further reflection indicates that obviously the type of drive pulley and the type of drive do affect materially the tension in the conveyor belt, and thus, as clearly shown, the time of acceleration is dependent upon the factors mentioned. Inasmuch as all of the factors except time are predetermined by the belt conveyor design, it becomes relatively easy to establish the accelerating time and to reduce further this time determination to a simple graph from which the time in seconds can be read directly. Such a graph is given in Fig. 1. The table appearing on Fig. 1 should be explained further. For a given belt speed, the time of acceleration can be expressed as a percentage of the belt speed. The time of acceleration is also dependent on the drive arrangement, and changes in the drive arrangement consequently change the time of acceleration. It further follows that for a given belt speed, the time expressed as a percentage of that belt speed also changes with the type of drive. Obviously then, it becomes possible to graph the percentage of speed for .each type of drive against the belt speed and accelerating time, after which, for a given belt speed and type of drive, the time can be read directly in seconds. Two constants were established for Fig. 1, the first one being the limiting of the maximum acceleration tension to 35 pct of the full load operating tension in the belt. The purpose of this is to limit the total tension imposed upon the belt during the acceleration period to 135 pct of the full load operating tension, &apos;which is the amount required to start or breakaway the fully loaded belt conveyor from rest. The other constant is the friction factor used for the idler equipment, which has been established as 0.022. For installations where it is necessary to establish the values of acceleration, invariably high grade idler equipment is used, and it has been established from field experience that 0.022 for the idler friction factor is amply conservative. The use of this friction factor for idlers must be tempered with judgment, of course, for occasions will arise where more power than indicated is required to start, even with the very best of equipment, such as low temperature operations that tend to congeal the grease in the bearings and thus produce additional friction drag. An inspection of the table in Fig. 1 affords a convenient rule of thumb method for determining the acceleration time, which conveniently can be 5 pct of the belt speed in seconds. The 5 pct of belt speed figure is close to the average for most types of drives. In using Fig. 1 it must be emphasized that it applies accurately to horizontal belt conveyors only.

Jan 1, 1953