By W. H. Bassett

ALTHOUGH brasses and bronzes have been made for ages, a systematic study of their physical properties has been carried out only during the years of the present century. Among these properties may be included those which are to be detected by means of microscopic examination; in other words by the science of metallography. The earlier workers in this field, both in this country and abroad, gave their attention to steel. When the senior author explored the situation in 1902, there was little encouragement to be found in undertaking the study of the non-ferrous alloys. A start was made, and the metallography of the brasses and bronzes, as well as of the copper-nickel- zinc alloys developed materially under his direction. Annealing experiments were begun in 1902, and in the succeeding years the effect of temperature, and the influence of previous working, on the grain size of brass were studied. The conclusions so well known and widely published today were largely reached during those earlier years. In 1905 the first complete annealing series were made. By this it is meant that brass and copper sheet, 5 B & S Nos. hard, was machined into tensile test specimens, then annealed under accurate control for 30 min. at temperatures up to the melting point of the material. Various determinations were made, including tensile strength and elongation in 2 in. There rapidly followed similar series on all of the copper-zinc alloys from 100 to 60 per cent. copper, on the bronzes, cupronickels, and on copper-zinc-nickel alloys. At this point there was published by Grard, in October, 1909,1 the very comprehensive and complete work on the tensile properties of cartridge brass, 90-10 copper-zinc, and electrolytic copper. The excellent photomicrographs in that paper illustrated the changes in structure produced by cold rolling as well as by annealing at different temperatures, but where Grard's work was confined to copper and to two alloys, the investigations in this laboratory have been over the entire fields of the commercial copper-zinc alloys, copper-tin alloys, representative copper-nickel and copper-nickel-zinc alloys as well as aluminum bronzes and others of a more special nature.

Jan 1, 1927

By W. H. Bassett, C. Davis

Although brasses and bronzes have been made for ages, a systematic study of their physical properties has been carried out only during the years of the present century. Among these properties may be included those which are to be detected by means of microscopic examination; in other words by the science of metallography. The earlier workers in this field, both in this country and abroad, gave their attention to steel. When the senior author explored the situation in 1902, there was little encouragement to be found in undertaking the study of the non-ferrous alloys. A start was made, and the metallography of the brasses and bronzes, as well as of the copper-nickel-zinc alloys developed materially under his direction. Annealing experiments were begun in 1902, and in the succeeding years the effect of temperature, and the influence of previous working, on the grain size of brass were studied. The conclusions so well known and widely published today were largely reached during those earlier years. In 1905 the first complete annealing series were made. By this it is meant that brass and copper sheet, 5 B & S Nos. hard, was machined into tensile test specimens, then annealed under accurate control for 30 min. at temperatures up to the melting point of the material. Various determinations were made, including tensile strength and elongation in 2 in. There rapidly followed similar series on all of the copper-zinc alloys from 100 to 60 per cent, copper, on the bronzes, cupronickels, and on copper-zinc-nickel alloys. At this point there was published by Grard, in October, 1909,' the very comprehensive and complete work on the tensile properties of cartridge brass, 90-10 copper-zinc, and electrolytic copper. The excellent photomicrographs in that paper illustrated the changes in structure produced by cold rolling as well as by annealing at different temperatures, but where Grard's work was confined to copper and to two alloys, the investigations in this laboratory have been over the entire fields of the commercial copper-zinc alloys, copper-tin alloys, representative copper-nickel and copper-nickel-zinc alloys as well as aluminum bronzes and others of a more special nature.

[A session of the Institute of Metals held during the February, 1926, meeting of the Institute, was devoted to a symposium on ''gas" in copper. S. Skowronski, Perth Amboy, N. J., was chairman. On the program were papers by T. S. Fuller; W. H. Bassett and J. C. Bradley; Susan B. Leiter, and W. H. Bassett and H. A. Redworth. These papers follow the chairman's introductory discussion.] S. Skowronski, Perth Amboy, N. J.—There are today two groups of metallurgists, one group who believe in oxygen-free copper and another group who believe that oxygen is absolutely essential in copper; not that the two groups disagree, but that a certain grade of work calls for oxygen-free copper, while another grade of work does not. I can sum up the problem by reading the abstract of an article by Frederick Johnson of Great Britain in The Metal Industry of Sept. 4, 1925. Few, who have watched the trend of things during the last two decades, can have failed to notice the steady growth of opposition to the prevalent use of copper in the "tough-pitch" condition, which for many ages enjoyed an unchallenged supremacy. Broadly speaking, there are two schools of thought in the metallurgical world, one holding the view that copper containing a small proportion of oxygen is an eminently suitable material for users, the other expressing its preference, in no hesitating or uncertain manner, for copper from which oxygen has been removed by means of a deoxidizer. In the old days, before the advent of the converter and the electrolytic refining process, the copper of commerce was so impure that the presence of oxygen was imperative in order to neutralize the influence of impurities which militated against the hot-working properties of the metal. For electrical purposes, oxygen must be present, because sound bars and billets cannot be produced without it, except at the expense of electrical conductivity. For most engineering purposes, however, electro-deposited copper may be used either by itself or with the addition of alloying elements, e. g., arsenic and nickel, which experience has proved to be beneficial, such copper being freed from oxygen by the aid of a deoxidizer, e. g., phosphorus. Such material has positive advantages over "tough-pitch" copper as at present produced from refinery furnaces. It has greater toughness and malleability, and is immune from the action of reducing gases at high temperatures, the destructive action of which, in the case of "tough-pitch" copper, is well known. The reasons why there has been no wholesale replacement of "tough-pitch" copper by deoxidized copper are commercial in nature; copper can be more economically melted in large-capacity furnaces which lend themselves to the poling process and are not so suitable for control of uniformity of action of deoxidizers as the smaller electric or crucible furnaces, whilst they are also more convenient for the production of very large castings. Moreover, the equipment of most large copper manufacturing plants is designed for casting "tough-pitch " copper in open moulds, e. g., wire bars and cakes, and these could not be used for deoxidized copper, which must be cast in vertical moulds as in brass-shop practice. Further, there are still certain impure brands and

Jan 1, 1926

By A. S. Malicsi, R. J. Lipp, I. Iwasaki

A loch-grade copper-nickel deposit, with an estimated 4.6 Gt (5 billion st) and average analyses of 0.6% copper, 0.2% nickel, occurs in northeastern Minnesota. In addition to copper, nickel, cobalt, and precious metals, the Duluth gabbro contains magnetite, ilmenite, olivine, plagioclase, and biotite. It u estimated that flotation tailings that would be produced by a concentrator of optimal size to sustain a smelter would amount to 20 Mt/a (22 million stpy). The flotation tailings, having already been ground, warrant a closer examination for recovery and use of potential byproducts. Residual sulfide minerals and fibrous minerals may also be isolated and treated separately for useful purposes or for disposal in an environmentally acceptable manner. Two flowsheets were developed; one involving preconcentration by low- and high-intensity magnetic separation and another involving preconcentration by gravity concentration. Concentration methods for recovering and purifying individual byproduct minerals were investigated. From their chemical, physical, and mineralogical characteristics, the potential areas of application and marketabilities of each product fraction were surveyed.

Jan 1, 1985

By AIME AIME

In the uniform of his country for the second time, Harry Phillip Stolz. Chairman of the A.I.M.E. Petroleum Division, holds a commission as Lieutenant-Commander in the Naval Reserve and is attached to the office of Inspector of Naval Petroleum Reserves in California. During World War I he left his studies at Stanford University to join the Army and was granted a commission as Second Lieutenant of Infantry. He remained in the Army Reserve until 1938 when he resigned to accept a commission as a member of the Naval Petroleum Reserves Advisory Board. Born in San Francisco Jan. 29,1899, where his father had lived since 1880, he was in that city during the turbulent year of 1906 where the city was ravaged by fire and earthquake.

Jan 1, 1942

By G. Sachs, E. J. Ripling, J. J. Lynch

It is general practice to evaluate the strength properties of a particular metal from its stress-strain (s1 — el) curve obtained by means of a conventional tension test. Such a stress-strain curve, Fig I, illustrates two important properties of a metal, its ability to strain harden, and its ability to withstand a certain limiting stress, the "fracture stress," (s), and a certain limiting strain, the "ductility" (es), before it fails by separation. These two fracturing characteristics are the coordinates of the point of fracture in Fig I. In the case of a metal which necks in a tension test, both the fracture stress and the ductility (measured in a tension test) are dependent upon (I) the shape of the neck and (2) average values of the stresses and strains over the cross-section at the moment of fracture. However, for the pur. pose of this investigation, these average quantities, rather than the actual values, may be considered for reasons of simplicity. It appears that the conclusiom also hold true if the analysis were carried out for actual values of fracture stress and ductility at the locos of failure. In this paper, the effects of straining (at room temperature) by various methods on the above metal characteristics, which were determined by subsequent tension tests will be discussed. According to Our present knowledge, any such prestrainitlg results in a stress-strain curve (in subsequent testing by tension), Fig 2, the general shape, or flow characteristics, of which can be derived from the original stress-strain curve of the unstrained metal minus a certain portion exhausted by the initial straining. This phenomenon is called strain hardening, and may be measured by the magnitude of the cut-off, or the "effective strain,'' from which the new curve must start in order to coincide in its plastic branch with the original stress-strain curve.

Jan 1, 1949

By J. A. Faucher

The mining industry has undergone significant technological advances in metallurgical process methods in recent years. The 1000 tpd concentrator of St. Lawrence Colum-bium Metals Corp. portrays the continuing effort made by the industry to achieve economical concentration of new and difficult ores. During the active search for sources of uranium in the early fifties, radioactive minerals were found in the Oka district near Montreal. The compatatively small quantities of uranium which were found occurred in association with widespread columbium (niobium) mineralization which included perovskite, a calcium titanate containing roughly 40% Cb2O5; niocalite, a silicate containing some 20% Cb2O5; and pyrochlore, a calcium niobate containing 45 -70% Cb2O5 as well as fluorine and some water. An idealized formula for one type of pyrochlore is: A typical chemical analysis of pyrochlore is shown in Table I. An important feature of this analysis is the lack of tin, lead, sulphur and P2O5 which conforms with the requirements of most consumers. In general the cerium content varies with sodium content and any increase in Ta2O5 lowers the Cb2O5 content of the concentrate. However, Ta2O5 rarely exceeds 0.5%. The carbonatite host rock of the columbium mineralization has the average mineral composition shown in Table 11. In Table 11, the term "diopside" is used to cover all silicates except mica which is shown separately because of the problems involved with its separation during the concentration process. In some ore zones, small quantities of rare earth minerals, such as monazite are present.

Jan 1, 1964

By John Bonar

A switch to refractory-type slurry pump linings has significantly reduced maintenance costs arising from liner failure at a Missouri lead mill. The pumps routinely handle a slurry consisting of 79 to 81% solids with occasional tramp iron, and are subjected to intense abrasion which previously wore out rubber liners in anywhere from three days to two months. Average liner life at the 1.5-million-t/y (1.6-million-stpy) operation was 30 days. Experimentation with mild steel liners and even manganese steel liners failed to extend liner life beyond two months.

Jan 3, 1978

By Victor A. Phillips

A series of specimens of a Cu- 3.23 pct Co alloy were prepared with particle diameters from zero to 590A. The samples were then cold-rolled 95 pct and the effects of the particle size on the behavior on annealing for hr at temperatures between 100" and 900°C were studied (by hardness, light, and electron metallography). Particles, particularly for d r 105 to 590A, greatly impeded softening and vecvystallizn-tion, and tended to give elongated grains. Particles deformed fairly homogeneously with the ,matrix, be- IN a previous study by the author,' the growth of cobalt-rich precipitates was followed electron microscopically in Cu-3.12 Co alloy as a function of aging, typically at 650°C. The coherent spherical precipitates grew to 520 + lOOA average diam before spontaneously losing coherency and developing (111) facets. Stretching a few percent after precipitation 2aused loss of coherency to occur sooner at about 220A average particle diam. The particles apparently retained their fcc structure after loss of coherency. coming lau2ellae. For d = 55 to 180A, these lamellae gave streak-contrast effects apparently due to coherency strains , and spheroidized on annealing at 600" to 650°C, forming coherent particles. Particles of d = 250 ov 320A lost coherency during t-olling, giving incoherent lamellae. Recrystallization apparently occured by growth of new grains into unrecrystallized (recovered) material at temperatures below that at which cobalt atoms had much mobility. The present study was undertaken to explore the effect of cobalt-rjch particles of various average sizes from 50 to 600A diam on the isochronal annealing behavior of copper after heavy cold rolling. The previous work' was used as a guide in preparing the two-phase series of prerolling structures. The solution-treated alloy was also rolled for comparison. A further question of interest in the present study was whether dislocation and particle hardening were additive, since the prerolling structures covered the full range unaged - peak aged — overaged, and further precipitation might occur on annealing after cold rolling. Although there have been exhaustive studies of the isothermal2"6 and is~chronal annealing behavior of

Jan 1, 1967

By E. D. Gardner, E. M. Sipprelle

The Synthetic Liquid Fuels Act (58 Stat., 190; 30 U.S.C. Sup., Secs. 321-325) was approved by Congress April 5, 1944; it directed the Bureau of Mines to build demonstration plants to produce synthetic liquid fuels from coal, oil shale, and agricultural products. The most important oil-shale deposits in the United States are in the Green River formation of Colorado, Utah, and Wyoming. The oil shale of western Colorado generally is more amenable to exploitation, more persistent, and apparently richer than elsewhere in the Rocky Mountain Region. It occurs at the top of a high plateau surrounded by bold, nearly vertical escarpments 500 to 600 ft in height. The top 400 to 500 ft of these escarpments comprises an oil-shale measure that averages 15 gal of shale oil per ton; the bottom 70 90 100 ft of the measure, called the Mahogany Ledge, averages over 30 gal per ton. The full measure in a 1000-square-mile area is estimated to contain 300 billion barrels of shale oil;' the Mahogany Ledge is estimated to contain 100 billion barrels of oil. These estimates are based on numerous surfac,e samples and on core-drill holes drilled by the Government and by private enterprise. The oil-shale beds are undisturbed and lie nearly horizontal. The name "oil shale" is unfortunate, as the rock is a tough, strong marlstone. Organic matter named "kerogen" is a constituent of the rock. The oil-shale demonstration mine is on Naval Oil-Shale Reserve No. 1; it is about 5 1/2miles by mountain road from the plant site, which, in turn, is 2 miles from U.S. Highway 6 and 10 miles west from Rifle, Colo. The highway parallels the Colorado River, the Denver and Rio Grande Western Railroad, and a 66,000-volt public-utility power line. Early in the program it was realized that an oil-shale enterprise would have to be on a large scale to be commercial, and that unusually low mining costs would be necessary. The physical characteristics of the Mahogany Ledge and an overlying roof stone are unusually favorable both for large-scale operation and low mining costs. Quarry practices largely will be followed underground to mine the Mahogany Ledge. The aim has been toward complete mechanization of all mining operations. A mining unit would comprise a square mile containing 100,000,000 tons of oil shale with allowance for mining losses. An investment of $1,000,000 would be $0.01 a ton; such an expenditure, therefore, could be made to save, say, $0.015 per ton daily operating cost. A goal of a mining cost of $0.50 per ton was set up in 1945. Open-cut mining costs then were about $0.25 per ton of material handled; it was hoped that a cost double this amount could be obtained in mining the Mahogany Ledge. Costs of labor and supplies have increased since 1945 and so has the selling price of petroleum products. To those unacquainted with the character of the Green River deposits, the name "shale" suggested high mining costs. Others assumed that coalmining costs of $2 to $5 per ton would apply. To many, the expected mining costs appeared the principal handicap to the establishment of an oil-shale industry. The purpose of the Bureau of Mines is to demonstrate methods and to establish costs for mining the oil shale on a large scale. It is hoped this work will lead to the establishment of a large-scale, commercial oil-shale enterprise.

Jan 1, 1950

By M. S. Azun

I do not at all agree with the basic points of the author's conclusion. The use of lognormal or normal model to respond to the attribute distribution function should be carefully questioned. If fitting a distribution function of regionalized variables is the main purpose, one may employ one of certain well-known families of distributions, such as Tukey's lambda functions. For instance, the distribution function of gold assay values studied by Krige (Krige, 1978) may fit the lognormal model well, but one should not exclude that the basic idea of using the distribution function of observed data is to have insight of the physical mechanism that gives rise to the regionalized variables. In Applied Geostatistics, there are many examples considering only lognormal or normal model for the distribution function of geostatistical data even if the observed distribution function has more than one mode. Of course, using lognormal or normal model always brings easy computation for the statistical properties of attribute under investigation. Still, I object to adopting any of those models without having any "statistical inference." As seen from the author's paper, lognormal and normal model produce the same average grade (0.746% copper) and almost the same sample variance. Therefore, which model explains the probabilistic behavior of ore deposit is always an important question that should be replied by the geostatistician using not the common sense but the statistical and probabilistic methods. For kriging procedures, such as linear kriging, one should describe either second order stationary properties or bivariate properties of regionalized variables. Second order properties, such as correlogram function or semivariogram function, are the inputs of the so-called kriging equations. Selecting one of any useable models for the observed second order properties, such as spherical model, is not easy since the models are not based on the correlations structure of the regionalized variables. How those models being used in Applied Geostatistics can be distinguished is another important problem. One may develop many fitting models to respond to the observed second order properties of regionalized variables. However, I suggest that the model should be based on the probabilistic behavior of geologic process. The author used spherical model for copper, wolfram, and silver grades from isotropic sector (Fig. 2, 4, 3b) and exponential model for silver grades obtained along raises in isotropic sector (Fig. 3a). It seems that those semivariograms given in Fig. 3b for isotropic sector and Fig. 4 may be described by the random model implying that regionalized variables do belong to renewal process (Azun, 1983). If I knew the total number of data points used in estimation, may prove that my conclusion is correct. Recalling the test for the first order sample correlogram value, the test procedure is introduced such that the independence is rejected if [Ir(1) I > Za/2 N1/2] where Za/2 is the a/2 percentile of standard normal random variable and N is the total number of samples used in estimation (Azun, 1983). For the other observed semivariogram functions I suggest the author might try to use the so-called "Markovian model" describing not only the correlation structure of regionalized variables, but also the physical mechanism that produces the regionalized variables. The Markovian model for correlogram function is, [p (h) = T 1ih , h>1 ,] The Markovian model for the other second order properties of ReV are also derived. [T veß], in the above equation, show, for example, structural change and mineralizational variation in a considered deposit, respectively (Azun, 1983). In selecting any model, it is not easy to search for the "best" response to the observed second order properties of ReV's. The Markovian model, based on a theoretical understanding of underlying mechanism, gives more information about the occurrence of regionalized variables and respond to all properties. Random model and the so-called hole effect structure can be easily defined as a special form of the Markovian model (Azun, 1983). An estimation of any second order properties of regionalized variables may be computed through (N-1) lag. However, the dependency between the regionalized variables may be deemed to have "died out" after the so-called stationarity width (range). In practice, the estimation is carried out through 25% of the total number samples available. Therefore, the large fluctuations around the zero level and variance for correlogram or covariogram function and semivariogram function, respectively, cannot be observed. Since the number of pairs involved in the estimation of higher second order properties is small, the estimation variance at those lags is large. There is no need to show higher order estimated second order properties. After using one of any kriging procedure for block estimation, the distribution function of average grades has the same mean as the drilling sample grades but

Jan 1, 1986

By L. G. Austin, P. T. Luckie, R. R. Klimpel

Application of the Charles and Bond Laws to batch grinding can be deduced as a special case of solution of the first-order batch grinding equation. With additional limitations on the feed size distribution, this special case also gives Rosin-Rammler distributions of constant slope, with the 36.79% retained point a simple function of time. In general, the assumptions concerning the breakage parameters S and B which are necessary to get Charles' and Bond's laws, are not valid except as a crude approximation. With less restrictive assumptions, it is still possible to get approximate Rosin-Rammler distributions, but the slopes change with time of grinding, and the 36.79% retained point is a more complicated function of time. An alternative form to Charles' law is suggested, which accomplishes the same result and has the same errors, but avoids the use of energy of grinding and deals with specific rate of grinding.

Jan 1, 1973

By Yang Tsang Woo

The method of making coke that has been adopted at the Kaiping and other collieries in northern China resembles, to some extent, the familiar bee-hive oven process of the United States, except that a kiln with permanent sides is used instead of a closed oven, and the products of combustion are drawn off at the bottom. In building coke-kilns in China, two circular holes, 8 ft. 6 in. in diameter at the bottom and 13 ft. in diameter at the top, are excavated in the ground, and connected at the bottom by a flue, as shown in Figs. 1 and 2. The sides and bottom of the kiln are lined with fire-bricks, and covered with a lager of fireclay, and a rectangular opening, 6 in. by 8 in., connects the bottom of each kiln with the main flue. Around the edge of the hole, and overlapping the lining, is a wall of fire-brick extending 2 ft. 6 in. above the level of the ground. An open space 5 ft. wide is left in this wall, through which the coal is carried into the kiln and the resultant coke removed. This space, of course, is bricked up during the time that the coking-operation is being carried on. The wall is pierced with nine flue-openings uniformly placed around the circumference, each interverliilg space in the wall being strengthened with a brick buttress, as is shown in Figs. 2 and 4. The floor of the kiln, as well as the main flue, is lined with fire-brick. Before charging the coal, it is first placed in shallow bamboo sieves, 2 ft. in diameter, and immersed in a trough 10 ft. long, and 3 ft. wide, fed with pit-water, in which it is washed by hand. Fig. 3 shows the manner in which the washing is done. From 25 tons of good "dust" coal, 22.5 tons of washed coal are obtained. When ready to charge the coal into the kiln, a temporary cone-shaped flue of fire-wood and lump coal is first built to a

Jan 1, 1906

By G. R. Speich

The interlarnmelm spacing, growth rate, and degree of segregation that accompany cellular precipitation in four Fe-Zn alloys containing 9.7, 15.2, 23.5, and 30.5 at. pct Zn have been determined in the temperature range 400" to 600°C. The chemical free-energy change for the reaction was calculated from the available thermodynamic data and the known compositions of the phases. The fraction of the chemical free-energy change for equilibrium segregation that is converted into interfacial free energy decreases from 0.43 to 0.08 as the magnitude of this free-energy change increases from 35 to 270 cal per mole. At constant temperature the cellular growth rate is proportional to the cube of the dissipated free energy. At 600°C newly 100 pct of the equilibrium segregation is achieved during cellulm precipitation whereas at 400°C only 85 pct of the equilibrium segregation is attained. During cellular growth, mass transport of zinc occurs by grain boundary diffusion; excess zinc remaining in the a! phase after the completion of growth is removed slowly by volume diffusion. A modified Cahn theory of cellular precipitation predicts the observed interlamellar spacing within a factor of two. In cellular precipitation reactions such as pearlite formation or discontinuous precipitation, the basic problem is to predict the variation of growth rate G, interlamellar spacing S, and degree of segregation P with composition and temperature. To accomplish this we need three independent equations relating these quantities. One of these equations comes from the diffusion solution. To obtain two additional independent equations, some assumptions must be made. cahnl has suggested recently that two plausible assumptions are 1) that growth rate is proportional to the dissipated free energy and 2) that the spacing which occurs is that which maximizes the dissipated free energy. According to the first assumption, this spacing also maximizes the growth rate and the rate of decrease of free energy per unit area of cell boundary. The present work was undertaken to test these assumptions. To test the first assumption it is necessary to study a cellular reaction over a wide range of supersatura-tions to establish a relationship between G and the dissipated free energy at constant temperature. This is possible only in discontinuous precipitation reactions since in pearlite reactions constituents other than pearlite form if the composition of the parent phase deviates even slightly from the eutectoid composition. The Fe-Zn system was chosen for study because 1) discontinuous precipitation proceeds to completion over a wide temperature and concentration range, 2) the degree of segregation within the cell can be measured by lattice parameter measurements,2 and 3) the thermodynamics of this system have recently been determined by Wriedt.3 In this system the cells consisting d alternate lamellae of a and r phases form from supercooled iron-rich a phase. The a phase within the cells is bcc as is the original a phase, cia, but has a different orientation and a slightly lower zinc content than the original a phase. The r phase has a zinc content of about 70 at. pct and a crystal structure isomor-phous with T brass. EXPERIMENTAL PROCEDURE Four Fe-Zn alloys with 9.7, 15.2, 23.5, and 30.5 at. pct Zn were prepared from carbonyl-iron powder (400 mesh, 99.8 wt pct Fe) and zinc powder (200 mesh, 99.99 wt pct Zn). The powders were ball-milled together and cold-pressed under 60,000 psi to discs $ in. thick by $ in. diam. The cold-pressed discs of the alloys with 9.7 and 15.2 at. pct Zn were sealed in evacuated silica capsules and heated slowly to 1100°C over a period of 1 week (3 days at 600°C, then 3 days at 80O°C, then 1 day at 1100°C). The alloys with 23.5 and 30.5 at. pct Zn were treated similarly except that the final homogenization temperatures were 1000" and 85O°C, respectively, to prevent melting. The alloys were quenched in iced brine from the final homogenization temperature. Specimens of each alloy were subsequently aged in salt pots at temperatures of 400°, 450°, 500°, 550°, 600°, and 650°C for times that varied from a few minutes to several hundred hours. At a late stage of this work, an alloy containing 11.2 at. pct Zn was prepared by vapor-impregnation of iron foil with zinc vapor at 890°C. This alloy proved useful for electron microscope studies because it was free of porosity. The homogenization and aging conditions were based on the recent Fe-Zn phase diagram of Stadelmaier and Bridgers4 rather than the earlier diagram of ansen.5 They consist of a homogenization heat treatment in the homogeneous a field followed by an aging treatment in the two-phase a + r field. The aged specimens were metallographically polished and etched in 2 pct nital and the radius of the largest cell in the microstructure determined. This radius plotted vs time gave a straight line whose slope is the boundary migration rate or growth rate G of the cell. To determine the interlamellar spacing, specimens were examined by surface-replica and thin-section electron microscope techniques. Because of the irregular nature of the lamellae within the cell, the average interlamellar spacing S .of the cell was measured by the method of Cahn and Hagel,6 where S is defined by:

Jan 1, 1969

By H. K. Shearer

Drilling for oil and gas in Arkansas in 1934 showed more activity than in any year since 1929; with a total of 96 completions, including 36 oil wells, 1 gas well and 59 dry holes. Of the producers, the lone gas well and 35 oil wells were in old fields, and one wildcat producer opened a new pool. Of the dry holes, 16 were in or near fields and 43 were wildcats. The total reported initial daily production of the oil wells was 9013 bbl., averaging 252 bbl. per well. Active drilling operations numbered 65 at the close of the year, compared with 26 at the beginning.

Jan 1, 1935

By YANG TSANQ WOO

THE method of making coke that has been adopted at the Kaiping and other collieries in northern China resembles, to some extent, the familiar bee-hive oven process of the United States, except that a kiln with permanent sides is used instead of a closed oven, and the products of combustion are drawn off at the bottom, In building coke-kilns in China, two circular holes, 8 ft. 6 in. in diameter at the bottom and 13 ft. in diameter at the top, are excavated in the ground, both being .connected at the bottom by a flue as shown in Fig. 1. The sides and bottom of the kiln are lined with fire-bricks, and covered with a layer of fire-clay, and a rectangular opening, 6 in. by 8 in., connects the bottom of each kiln with the main flue. Around the edge of the hole, and overlapping the lining, is a wall of fire-brick extending .2 ft. 6 in. above the level of the ground. An open space 5 ft. wide is left in this wall, through which the coal is carried into the kiln and the resultant coke removed. This space, of course, is bricked up during the time that the coking operation is being carried on. The wall is pierced with nine flue-openings uniformly placed around the circumference, each intervening space in the wall being strengthened with a brick buttress, as is shown in Figs. 2 and 4. The floor of the kiln, as well as the main flue, is lined with fire-brick. Before charging the coal, it is first placed in shallow bamboo sieves, 2 ft. in diameter, and immersed in a trough 10 ft. long, and 3 ft. wide, fed with pit-water; in which it is washed by hand. Fig. 3 shows the manner in which the washing is done. From 25 tons of good " dust" coal, 22.5 tons of washed coal are obtained. When ready to charge the coal into the kiln a temporary cone-shaped flue of fire-wood and lump coal is first built to a

Nov 1, 1905

By P. S. Rudman

Laves phases, AB2, are considered as Izerrzisub-stitutional solutions m1hich are defined by a one-for-truo replacement scheme. Atomic-size tnisfit is considered in terms of deviations of the ratio 2V°b/V°A from unity, where v° = atomic volume. A simple elastic model has been used to calculated deviations from "Vegard&apos;s law of atomic vol-umes". Comparison has been made between calculated and observed atomic-volume deviations fov 222 Laves phases. Agreement is generally very good although there ave some few exceptions which appear to be excusable in terms of electronic changes that ore beyond the scope of the present model. We can consider the formation of a binary sub-stitutional solution A-B from an A solvent as one-for-one replacements of A atoms by B atoms. As the atomic-size ratio deviates from unity, the solution becomes thermodynamically less stable and hence more restricted because of atomic-misfit strain energy. In accordance with our previously presented conclusion1 that the atomic volume, v, is in general the most appropriate measure of atomic size, the ideal size ratio for a binary sub-stitutional solution is vg/vA = 1. The Laves phases have been described by Berry and Raynor2 in terms of various stacking sequences of hexagonal layers of B atoms for the three structures MgZn2(C14), MgCu2(C15), and MgNi2(C36). To form the Laves phase of ideal composition AB, we start with complete hexagonal layers of B atoms in the appropriate stacking sequence and we remove, according to an appropriate scheme for each structure, two out of every four B atoms and replace the two removed atoms by one A atom. We thus might expect to find that the ideal size ratio for the Laves phases is 2v/B/ VA= 1. From this point of view, then, we call Laves phases hemi-substitutional solutions since we employ one-for-two replacements. By analogy with substitutional solutions we can expect for Laves phases that as the ratio 2VB/Va deviates from unity the phase occurrence will be more restricted. Laves3 has plotted the distribution of Laves phases as a function of the radius ratio, ?A/rB, and found that, while the distribution extended from 1.05 < rA/B < 1.50, the

Jan 1, 1965

By Thomas B. Douglas

INSTRUMENTATION in the process industries can no longer be regarded as a convenience, but rather an absolute necessity. Although many chemical processes must already be conducted with instruments, every properly designed application of automatic process control will improve operation: 1) the product will be more uniform and of higher quality; 2) the manual labor saved will reduce cost; 3) uniformity of flow and uniform control of process will increase production; and 4) surges will be eliminated, making it possible to operate equipment near ultimate capacity at all times. Industrial instruments fall into two general classifications-those that measure and those that measure and control. The cement industry has been using instruments for a number of years, particularly in the burning process, primarily for indicating and recording. Automatic process control makes additional use of these instruments, and others, to control variables. Assisted by the instrument manufacturers, engineers at Ideal Cement CO. achieved considerable progress in determining how well the usual recording instruments could be made to control various phases of cement-making. The results of these experiments were used to make the new plant at Houston as wholly automatic as possible.

Jan 2, 1958

By David B. Reger

Extensive drilling for gas and increased pipe-line building were the major petroleum activities in West Virginia during 1937. According to the West Virginia Department of Mines, 1034 permits to drill were issued. A running account of operations from trade journals and other reports shows that 1041 wells were drilled, resulting in 193 oil wells with 1238 bbl. of daily production; 680 gas wells with 1,048,057,000 cu. ft. of daily open flow; and 168 dry holes. The new oil-well average is 6.4 bbl. per well per day; the gas-well average is 1,541,260 cu. ft. per well per day; the ratio of dry holes to completions is 16.13 per cent. Very little attempt was made to develop new supplies of oil. Because of the continued low price, operators evidently considered it good business to leave oil in the ground rather than to produce it at a loss or on a small profit basis. The principal oil wells completed, by counties, are: Calhoun, 16; Clay, 10; Pleasants, 17; Ritchie, 42; Roane, 16; Tyler, 13; Wetzel, 11; Wirt, 14; Wood, 13. The leading counties in gas, with the number of successful wells in each, are: Boone, 54; Braxton, 31; Cabell, 48; Calhoun, 46; Gilmer, 82; Kanawha, 134; Lincoln, 44; Ritchie, 56; and Wayne, 26. General State of the Industry In Table 1 will be found an approximate summary of oil and gas territory and reserves, oil and gas production and number of oil and gas wells. The amount of land under lease is an approximation, because the exact figures are not available through any public or private agency. The proved land and reserves represent the opinion of the writer. The oil production for 1937 is subject to revision, and the gas production for the same year is only an estimate, based on demand and supply. The number of oil and gas wells now active is also an approximation, based on previous studies, and revised for completions and abandonments. Principal, Areas of Activity In Boone County, 62 wells were drilled in various localities, resulting in 4 oil wells and 54 gas wells with 18,170,000 cu. ft. of new production.

Jan 1, 1938

By A. A. Smith, J. S. Smart

THE controlled amounts of phosphorus, arsenic, sulphur or selenium found in commercial coppers perform a variety of highly useful functions. Indeed, a large segment of modem copper technology is essentially dependent upon the presence of one or more of these elements. Consequently, the literature contains many references to their effects but the scope is broad and has been only partly covered. New data are presented herewith directed toward a better understanding of the basic behavior of these elements in copper, with particular emphasis on the composition range 0 to 0.05 per cent. These data are a part of a general program of research on the effects of impurities on the properties of oxygen-bearing and oxygen-free copper, other portions of which have been reported previously.1-2-3 Schematically, the behavior of individual elements is determined from measurements of conductivity and softening temperature,1, 2 and the binary alloys employed are synthesized from high-purity copper in order to eliminate interference from the effects of extraneous impurities. Alloys of selected composition were first prepared in the oxygen-free form by continuously casting the melts in the form of 3/8-in. diameter rod. Oxygen was added subsequently to portions of the alloys, either by remelting or by diffusion at 850°C. from a surface scale. Test wires were drawn one B. and S. number per pass, using four 30-min. 600°C. anneals at o.3125, 0.257, o.204 and o.162 in., and a final cold reduction of 95 per cent t0 0.081 in. Oxygen-bearing slugs made by remelting were hot-rolled to 5/16 in., drawn to 0.162 in., annealed for 30 min. at 600°C. and cold-drawn 95 per cent to 0.081inch. The alloys containing phosphorus, having been compounded very early in the program, were prepared in the form of 5/16-in. rod, and processed to wire with only the last three intermediate anneals listed above, all of these having been conducted in commercial nitrogen. In addition, the conductivity anneals on these alloys were also performed in the same atmosphere, and the small amount of oxygen present as an impurity in the gas resulted in some loss of accuracy at temperatures of 700° to 800°C., as will be shown later. Subsequently, the anneals for all oxygen-free alloys were conducted in hydrogen to prevent oxidation, and purified nitrogen was employed only for oxygen-bearing samples. All conductivity anneals were of one hour duration followed by a rapid quench in 10 per cent H2SO4. EFFECT OF PHOSPHORUS The widespread use of phosphorus as a deoxidant has resulted in universal appreci-

Jan 1, 1945