By Luben Xie, Lin Hu, Qiang Wang, Min Gan, Tao Jiang, Wenqi Li, Xiaohui Fan, Zhiyuan Yu

"Crystal precipitation behavior of calcium ferrite (CF) during iron ore sintering process along with the effect of cooling rate, SiO2 and Al2O3 on crystalline condensation were studied. The results show that CF, has strong ability of precipitation. The precipitation is barely affected by extenal factors. It begins to precipitate when the liquid phase cools down to about 1200oC. CF could crystallize rapidly at the cooling speed of 150 °C /min. Furthermore, decreasing of the cooling rate favors the development of crystal. Binder phase transformed from CF system to silicate system when SiO2 content was increased to 5~6%, with a constant basicity (R) 2.0. Increasing Al2O3 content could promote the precipitation of CF and the development of crystal.IntroductionCrystalline condensation is the last stage of sinter mineralization. It includes the processes that crystalline substance and amorphous substance precipitate from high temperature solution phase and the consolidation of material when melt cools down. During the crystallization process, minerals precipitate following the order from high to low melting point coupled with the decreases of free energy. Most of binder phase minerals and part of iron oxides crystallize in this process, which have an important influence on mineral composition and microstructure of sinter. They finally determine the sinter strength and metallurgical properties."

Jan 1, 2011

By Vadym Drozd, Yongzhou Sun, Shah Najiba, Jiuhua Chen, Andriy Durygin

"Phase transitions of the potential hydrogen storage compound, ammonia borane (NH3.BH3), was investigated using Raman spectroscopy and a diamond anvil cell at high pressures up to 9.5 GPa and low temperatures down to 90K. At room temperature, ammonia borane has three phase transitions in this pressure range. Upon cooling, four new phases were discovered through changes in characteristic Raman spectra. This result provides information about the stability of new bonding characteristics of this potential hydrogen storage material at low temperature and high pressure region.IntroductionDevelopment of hydrogen technology requires the safe, efficient and environmental friendly materials for hydrogen storage and hydrides have attracted much attention as hydrogen storage media. Among chemical hydrides, ammonia borane (BH3NH3) stands out due to its high gravimetric and volumetric hydrogen density ' "". Despite high hydrogen content, this compound is very stable. It releases hydrogen in several steps by thermal decomposition in the temperature range of 100°C to 500°C. Direct thermal decomposition also causes toxic borazine emission. Recent research interests on ammonia borane include destabilizing this compound to lower the dehydrogenation temperature with an enhanced hydrogen release rate using different techniques, e.g. the nanoscaffolds'', ionic liquids"" and acid'"" or transition metal catalysts' ""'. As a molecule of ammonia borane consists of protonic (NH) and hydritic (BH) hydrogens bonded by the polarized dative bond, thermal or catalyzed decomposition requires breaking of N-H and B-H bonding. Still now, the detailed information about the bonding characteristics of ammonia borane is not sufficient to understand details about its phases and structures. The development of methods to enhance hydrogen discharge rate from ammonia borane requires a detailed study about the structural and dynamical properties that control the stability and the intermolecular interactions of this material. This study is motivated to investigate the stability of the existing phases and also to explore the existence of any new phases at different temperatures and pressures which may have enhanced hydrogen release and uptake properties."

Jan 1, 2012

By Ximena Diaz

Mercury is one of the most undesirable contaminants in gold bearing ores. During cyanidation mercury cyanide compounds accompany gold in all the extraction and recovery processes. Of course mercury in the carbon eluates creates environmental problems in subsequent refining steps. One possible process alternative for the separation of gold from mercury in such concentrated alkaline cyanide solutions is the selective solvent extraction of gold by undiluted Dibutyl Butyl Phosphonate (DBBP). In order to describe the behavior of mercury during extraction by DBBP, the results from a preliminary research program are presented. In this study, temperature and cyanide concentration have been found to be the most significant variables which influence the separation of gold from mercury by solvent extraction using DBBP. It was found, using plant eluate from a carbon strip, that excellent separation of gold from mercury can be obtained at 60' C with 98% gold recovery and complete mercury rejection in a single stage of extraction. The influence of pH is also discussed in terms of the extraction chemistry. These results complement previous research which described the DBBP solvation extraction of an aurocyanide ion pair. In addition, these results extend our understanding of the alkyl phosphorous ester extraction systems by illustrating that neutral ionic species such as Hg(cN)02sq, can be extracted at low cyanide concentrations, a phenomenon which had not been observed previously for other cyanoanions.

Jan 1, 1993

By lchiro Aoi, Hideo Nakae, Makoto Yoshida, Makoto Ishino

"The influence 6f gravity on the microstructure of unidirectionally solidified Cu-Pb monotectic, Ag-Si and Fe-C eutectic alloys is studied. In order to examine the influence of gravity in a lg environment, both the upward (opposite to direction of gravity) and downward (direction of gravity) unidirectional solidifications are carried out. The results are as follows: (1) For the upward solidified Ag-Si eutectic alloy, the eutectic Si continuously grows. On the other hand, in the downward solidified Ag-Si alloy, the Si grows discontinuously and disperses into the ex-Ag matrix. (2) No morphological difference in the eutectic growth is observed between the upward and downward solidified Fe-C eutectic alloys. (3) In the case of the upward solidified Cu-Pb monotectic alloy, a banded structure, which consists of Pb-rich layers and Cu-rich layers, is observed. However, such a banded structure -is not observed in the downward specimen. (4) The banded structure is not found in the upward solidified Cu-Pb-0.05 mass % Al and Cu-Pb-0.1 mass % Al alloys. In the Cu-Pb-0.05 mass% Al alloy, a fibrous -L 2 phase grows continuously parallel to the growth direction at low growth rate. Only 500 mass ppm addition of aluminum induces the morphological change of the monotectic L2 phase.IntroductionThe influence of gravity on the solidification of eutectic and monotectic alloys has been investigated in microgravity environments [l-9]. The purpose of these studies was to obtain a homogeneous microstructure of eutectic or monotectic alloys, most of which alloys tend to solidify with macro-segregation under gravity. However, in most of the previous experiments, e.g., in free fall systems, in aircraft or in space laboratories, the growth rate was too high to realize a planar solid/liquid interface. This would be due to the limited time for solidification. Thus, it was difficult to examine the influence of gravity on the planar coupled growth of the eutectic or monotectic alloy. In this study, both the downward U.D.S. (unidirectional solidification by gravity) and upward U.D.S. (opposite direction to gravity) are carried out in order to examine the influence of gravity on the coupled growth in a lg environment [l0, 11]. In the case of the downward U.D.S. using the current Bridgman method, the molten alloy must be confined between the crucible and the solid."

Jan 1, 2000

By I. A. Ibrahim, A. K. Ismail, A. A. I. Afifi

"Synthetic rutile for paints industry is conventionally produced by a combined smelting and leaching process. Smelting process is an energy intensive step and represents economic burden in view of the increasing energy costs. Egyptian ilmenite ore containing 40% TiO2 and 38% total Fe was thus directly leached with sulphuric acid to produce eventually synthetic rutile. The process-involves digestion of the ore with sulphuric acid whereby both TiO2 and Fe are dissolved. The solution was then treated with iron powder to convert Fe3+ to Fe2+ to avoid co-precipitation of iron during the hydrolysis step. After solid/liquid separation and clarification, Fe was crystallized as ferrous sulphate hydrate by chilling. The titanium pregnant liquor was concentrated by evaporation and then hydrolyzed to precipitate hydrated titanium dioxide which was then calcined to produce synthetic rutile containing 98.6 TiO2 and 0.58% Fe2O 3. The optimum conditions of all the processing stages were determined.IntroductionSynthetic rutile for paints, welding rods and other industries could be produced from ilmenite ore by sulfuric acid leaching process. This process is a batch process and nearly 80% of all TiO2 produced in the world is made by this process [1]. Figure l shows simple block flowsheet of the process. The process involves the following stages.Digestion: In this stage, ilmenite ore is treated with concentrated sulfuric acid where both iron and titanium are converted to their respective sulfates according to the following equations:"

Jan 1, 2000

By I. Perus, M. Fazarinc, G. Kugler, M. Tercelj

"Ledeburitic tool steels are highly alloyed steels used for specific highly loaded applications but are characterized by low and variable hot workability. In this contribution the importance of selecting the right choice of some essential process parameters, i.e. casting temperature, solidification rate and soaking temperature, needed for improving the intrinsic hot deformability of ledeburitic tool steels, is studied. An inappropriate selection of casting temperature and cooling rate results in precipitation of unusual eutectic carbides that decreases the hot workability, whereas with the selection of appropriate soaking temperature the temperature range of safe hot working can be broadened. For each initial as-cast microstructure individually determined soaking temperature should be selected.IntroductionThe surface cracking during hot deformation of ledeburitic tool steels reduces mechanical properties and their industrial yield. These tool steels have high hardness, wear resistance and high tempering resistance on one hand, and high flow stresses and low hot deformability on the other. Decreased hot deformability of the tool steels is attributed to the type, size, shape, distribution, fraction of eutectic carbides and/or other phases, grain growth, etc. at upper limit while precipitation of secondary carbides and decreased recrystallization rate at lower limit of the safe hot deformation temperature range, [1-6].The occurrence of cracks on most exposed areas of workpiece are related to the areas where similar conditions related to upper and/or lower limit of temperature working range prevail, i.e. areas with accelerated cooling, areas with higher value of accumulated strains where also decreased recrystallization rate with simultaneously presence of higher tensile stresses takes place, furthermore areas of workpiece which are due to combustion conditions in furnace heated to higher temperatures, etc. Thus the areas, where combination of previously mentioned conditions prevails, are more exposed to cracking. This additionally requires that hot deformability of ledeburitic tool steel should be considered as a complex problem. Publications in the literature with regards to hot deformability of tool steels are predominately of a partial nature thus all reasons for unexpected occurrence of cracks are not sufficiently explained in available literature so far. Furthermore modern practice proves that previous processing parameters significantly influence the hot deformability and thus this cannot be considered as a constant value. During heating, soaking and hot deformation various processes take place: decay (decomposition) of carbides, formation of new carbides, dissolution of carbides and of alloying elements, etc. Thus depending on variation of process parameters and chemical composition, that consequently influences the processes related to carbides, shifting of decreased deformability at both limits of temperature working range to higher and/or to lower temperatures can occur, [1-14]."

Jan 1, 2012

By Jewel Gomes

Green rust is an important intermediate in oxidative transformation of Fe(II) phase. This unstable compound contains a mixture of ferrous and ferric hydroxides that belong to a family of minerals known as layered double hydroxides (LDH). Its general formula is [FeII(6-x) FeIIIx (OH)12]x+[Ax/n-*yH2O] x-, where A is an n-valent anion mainly Cl-, CO3-2 and SO4-2, and in which either the bivalent or the trivalent iron can be replaced for other trivalent or bivalent metal ions. It was first identified as corrosion product, later in soils as a product of interactions between microbes and metals in soils. Due to its high reactivity, it is used in the reduction of organic and inorganic compounds, As removal, and the treatment of acid mine drainage. In this paper, we described the method of electrochemical generation of green rust, its characterization by XRD, SEM and FT-IR, and its implications to electrocoagulation.

Jan 1, 2009

By D. W. Collins

Several organic and inorganic substances are widely used to control deposit structure and morphology during the electroprocessing of copper. Methods for monitoring the levels of thiourea, glue and guar gum during electrorefining and electrowinning have been successfully developed under the trade names of Reatrol and CollaMat. Other instrumental methods have been developed for additives and decomposition products associated with the electroplating of copper and other metals. Generally, these methods have been found to be either insufficiently sensitive or lacking in the desired selectivity for some or all of the additives. These procedures have mostly employed DC techniques; i.e., cyclic voltammetry, Tafel analysis, etc. In this work, chronopotentiometry (CP) and AC voltammetry were used to examine the interaction of glue, guar gum, thiourea and chloride during the electroplating of copper onto a platinum electrode. In addition, the interactions between the additives have been explored. It was found that glue in pure electrolyte (H2S04 and CuS04 only) had no effect on the chronopotentiogram. Glue was only active if chloride ions were present. The addition of thiourea resulted in several different chronopotentiograms depending on the presence of either chloride or chloride and glue. Thiourea used in conjunction with glue and chloride showed a significant increase in the polarization during copper deposition when compared to the electrolyte containing only glue and chloride. The use of a modified channel electrode further increased the sensitivity of CP. The use of AC voltammetry was explored as a technique to monitor some of the additives. AC voltammograms have more spectral detail then their DC counterparts and it is possible to monitor some of the additives at very low concentrations with AC techniques.

Jan 1, 1999

By S. C. Dhara

The recovery of Platinum Group Elements from various industrial scraps and spent materials in the form of high and low grade, such as, impure metals, matte, catalysts and other ceramic substrates, etc., has .been described by using high pressure reaction method. Nickel, Stainless Steel, Titanium and glass lined reaction vessels? are used in the reaction process. Primarily, the method involves either direct leaching of the substrates from the metal value or dissolving the precious metal from the substrate. Both acids and alkalies are used along with other reagents in the reaction process. The temperature and pressure of the leaching process are the main criteria for the reaction kinetics.

Jan 1, 1989

By Mikio Kobayashi

Extraction of valuable metals from sulfide ores continues to be a very important, process and so the strict control of discharge of harmful metals in effluents from refineries becomes more important in the future. The recovery methods for heavy metals have been developed. Some metals such as Se and As are still difficult to be removed to very low concentration, although the techniques for recovery and removal for many kinds of heavy metals have already been developed. Especially, in case of Se the recovery system from water with low concentration has not be developed yet, although the WHO decided Se to be harmful for human beings and then the discharge control is under obligation now. In general Se exists as selenite ion and/or selenate ion in aqueous phase and selenite ion is able to be recovered by coprecipitation with ferric hydroxide or by reduction to solid selenium by general reductants. Selenate ion, however, has a strong resistance to conventional treatments. Therefore the new technique for the recovery of Se from water including selenate ion has to be developed. In this presentation the new approach for removal of selenate ion using the reaction in which ferrous ion is oxidized to ferric ion is presented. Selenate ion is reduced to selenite ion during the reaction and then to solid selenium, while ferrous ion is oxidized to ferric ion. The coexistence of activated carbon is very useful to increase the reaction rate. The use of iron powder is also effective and very useful for reducing gel-like precipitates mainly consisted of ferric hydroxide. The concentration of the residual selenate ion is probably under 0.1 ppm after recovering Se by the mentioned-above approach. In addition to the mechanisms of these reactions, the effects of pH, coexistent positive and negative ions, and reaction temperature are also presented. Furthermore the investigation of the behavior of selenosulfate is presented.

Jan 1, 1998

By C. A. Pickles

At the present time, pyrometallurgical processes are employed for the recovery of lead from battery scrap. These processes have serious pollution problems, primarily due to the emfssion of sulphur dioxide and airborne lead in the form of dust and fume. In addition it is necessary to dispose of solid wastes and liquid effluents which contain lead and in some cases sodium sulfide-containing compounds. In this work an improved process was investigated for the recovery of lead from battery residue. This involved pelletization of the residue with sodium carbonate and moisture. Then, the pellets were melted without carbon and the .sodium sulphate salt was removed. Subsequently, the molten lead oxide was reduced with carbon. This process minimizes the sulphur dioxide emissions and leads to very low sulfide contents of the sodium sulfate salt

Jan 1, 1992

By Yan Fu, Chuanlin Fan, Xiujing Zhai, Yongfeng Chang, Binchuan Li

"The mechanism of the selective chlorination of nickel and cobalt in reduced limonitic laterite was investigated. Reduced ores were obtained from the reduction roasting of a limonitic nickel laterite. The thermal decomposition of related chlorides and the selective chlorination of the reduced ore were carefully studied using Differential Thermal analysis - Thermogravimetry (DTA-TG), X-Ray Diffraction and chemical leaching methods. In the temperature range of 300 - 500 °C, aluminum chloride hexahydrate was chosen as chloride agent. During the selective chlorination, reduced ore was partly chlorinated by hydrogen chloride generated from the thermal decomposition of chloride agent. Then the oxydrolysis of ferrous chloride re-generated hydrogen chloride was used to further the chlorination. Finally, iron was mostly rejected as hematite, while nickel and cobalt were selectively chlorinated. More than 91 %Ni , 90%Co and about 4%Fe in the chlorinated ore was extracted using a water leaching method.IntroductionLimonitic nickel laterite is an important nickel reserve, which is rich in iron in the form of goethite and has low contents of magnesium, aluminum, silicon, and other elements. Goethite is the main nickel-bearing mineral in the laterite [1]. Nickel is generally present in goethite in three modes: (a) associated with amorphous or poorly crystalline goethite, (b) weakly adsorbed to the crystalline goethite surface, and ( c) as lattice substituents [2]. In addition, cobalt in limonite was found to be associated with a manganese phase rich also in nickel [3]. These results indicate that the extractions of nickel and cobalt are highly dependent upon the degree of the decomposition of the nickel, cobalt-bearing minerals.For the selective extraction of nickel and cobalt from limonitic laterite, the ore is usually processed by hydrometallurgical methods, including high pressure acid leaching (HPAL) [4] or reductive roasting - ammonia leaching (Caron process). However, there are still some disadvantages in these processes, such as the expense of autoclaves and scaling problems in HP AL [ 4, 5], and relatively low overall metal recovery, large energy and reagent requirements for the Caron process."

Jan 1, 2011

By Brian R. Green

Resin-in-pulp (RIP) technology has been developed for recovery of gold. It is now time to look forward to the potential for application of the technology to other situations. Some cases have been identified and have merited preliminary testwork. Four examples, which illustrate the potential of RIP, are dealt with in this paper. These include removal of metal-cyanides from pulps, recovery of manganese that is difficult to wash from filter cakes, recovery of nickel from low grade pulps, and recovery of zinc from process residues. The discussion includes descriptions of the problems, factors that affect the choice of resin, and factors that will affect the economics of the process.

Jan 1, 1998

By Bo Jiang, Lianyun Liu, Hongmin Zhu, Kai Huang

"Watermelon peel is selected as a novel adsorbent to remove Pb(II) from aqueous solution. A simple saponification process is proposed to modify the peel and the adsorbent is characterized by SEM and FTIR. The effects of pH, contact time, initial concentration of Pb(ll), biosorbent dosage and temperature on adsorption of Pb(II) are investigated. Different models are used to fit experimental data. These models indicate that the adsorption process follows the Langmuir model and pseudo-second-order model. The maximum adsorption capacity obtained from Langmuir model is 1.05mol kg-1 for the prepared sorbent. Equilibrium time is attained in 5-10 min for the studied concentrations. The watermelon peel can be used as an effective and low-cost biosorbent for removal of Pb(ll) from aqueous solution.IntroductionRecently, removal of heavy metal ions from industrial effluents by biosorption has become a very attractive topic, since the more serious pollution issues caused by heavy metals emerge frequently, and more strict requirements for its control are called upon by society [1,2]. In this case, most conventional purification technologies are not suitable due to poor cost-effectiveness [3]. For example, chemical precipitation by alkaline reagents usually can not decrease the metal ion concentration below the permissive levels, and also it will produce a large amount of sludge containing toxic metals. Membrane separation techniques can realize deep purification of wastewater easily, although its operating cost is usually high. Thus, considering the high effectiveness, low cost and free-sludge operation, bisorption has become a promising technique in water treatment [4]. The most important thing for this technology is the synthesis of a suitable biosorbent, whose adsorption properties will determine the removal efficiency and economic cost for the whole process. Watermelon is one of the most popular fruits for mankind for its delicious flavor. Usually, the watermelon is consumed mainly for its edible pulp, and its peel is discarded or only used as feed for livestock. Considering the pectin contained in the watermelon peel, just like that in orange wastes in the reported literatures [3], the idea of using it as the raw material to prepare the biosorbents for heavy metal ions removal from the aqueous solution was evaluated in this study."

Jan 1, 2012

By Dinesh P. Amalnerkar, Nagegownivari Munirathnam, Tirthalli Prakash, Katia Vutova, Vania Vassileva, Veliko Donchev

"A time-dependent model for electron beam melting and refining (EBMR) of different metals and alloys is developed. The model is 3D axi-symmetrical and an adapted numerical scheme of Pismen-Rekftord type is applied. The developed computer program computes the thermal fields in the metal ingots during EBMR process as well as the dynamics of the thermal streams and the geometry of the molten metal pools. Calculated results for different regimes of EBMR of titanium are obtained and discussed in the paper. Experiments are performed and impurities' concentration data are presented. Simulation results are compared with experimental data and are used for optimization of the EBMR process in the case of Ti.IntroductionElectron beam melting and refining (EBMR) has an important role in the special electrometallurgy[ 1-6] and it is approved for obtaining of pure titanium [7]. EBMR of metals and alloys is being recognized as a competitive and even the single method for obtaining new materials for all areas of human activity.The principal scheme of the EBMR drip process is shown in Fig.1. A thin layer of molten metal is formed on the front part of the feeding rod during the e-beam processing and generated droplets fall into the molten pool in the crucible where the ingot is formed. The refining is mainly realized at the boundary liquid metal - vacuum. There are three zones in EBMR (Fig.1) - on the front part of the feeding rod (zone I in Fig.1 ), on the surface of the generated droplets (zone II in Fig.1) and the surface of the molten pool in the water-cooled copper crucible (zone III in Fig.1)."

Jan 1, 2013

By Antoine Allanore, Luis A. Ortiz, Donald R. Sadoway

"The steelmaking industry has drastically reduced its energy consumption in the last fifty years, and today’s technologies are considered to operate at their optimal efficiency with respect to energy needs. To cope with new constraints related to greenhouse gas (GHG) emissions, a change of paradigm is necessary. One of the promising technologies that could be deployed to help reach CO2 mitigation targets relies on the intensive use of electricity: molten oxide electrolysis (MOE). This paper presents the key process parameters that need to be tuned to address the practical needs for both high productivity in a steelmaking reactor and for an energy efficient process. Herein we show that contrary to common perception, the electrolysis process for ironmaking requires less energy than today’s chemical reduction route. Furthermore, we prove that most of the energy that must be provided to operate the electrolytic iron production cell is thermal energy which is readily generated by joule heating during electrolysis due to large currents being passed through the electrolyte. The energy consumption of the electrolysis cell is therefore shown to be highly dependent on the cell configuration and the chemistry of the electrolyte. As a consequence, the CO2-impact of the technology strongly depends on both the power production mode and the technological choices for design of the process, including cell configuration. Surprisingly enough, even when the electricity generation is not carbon-free, MOE still appears to be viable from the perspective of reducing GHG emissions providing sound reactor design considerations are made.IntroductionIn the context of greenhouse gas (GHG) emissions mitigation, the steelmaking industry is considering several techniques that could sustain the efforts and progress achieved by this sector in the last decades [1]. A recent report [2] on potential routes for low-CO2 steelmaking highlighted for all techniques both the strong dependency of CO2 emissions on electric power production mode and the need for a decrease in energy consumption per tonne of steel. Incited to innovate with respect to this last criterion, the steel industry considers electrolysis to be a promising technological solution, and in particular the molten oxide electrolysis (MOE) process. This process conducts electrolysis in a mixture of oxides that dissolve the iron oxide feed, which by the action of electric current is decomposed into liquid iron and oxygen gas. The opportunity for reduction in energy consumption during steelmaking by MOE is commonly attributed to the “direct” pathway from iron oxide to liquid metal offered by the use of a molten oxide melt and operation at a temperature above the melting point of iron, ideally 1600°C, to provide enough superheat for tapping the molten iron product:"

Jan 1, 2011

By Batric Pesic

Gold dissolution with bromine was studied by using the rotating disc technique. Geobram TM 3400 was used as a source of bromine. The parameters studied were: rotating speed, Geobrom 3400 concentration, pH, temperature, sulfuric and hydrochloric acid concentration, and the concentration of various cations (copper, iron, zinc, aluminum, manganese, potassium and sodium) and anions (chloride, bromide, sulfate, nitrate, and iodide) According to the Levich plot and activation energy, gold dissolution was controlled by a chemical reaction rate. Copper, iron, and manganese in their highest oxidation states, aluminum, zinc, sodium and potassium did not have any effect on gold dissolution rate. The presence of manganous ion dramatically decreased the gold dissolution rate. Kinetic performance of bromine, in the form of Geobram TM 3400, was compared with performance of cyanide and thiourea.

Jan 1, 1990

By Ehsan Vahidi, Fereshteh Rashchi, Ataollah Babakhani, Alireza Zakeri

"The synergistic effect of Cyanex 302 on solvent extraction of nickel and cadmium from sulfate solution with D2EHPA diluted in kerosene was investigated with the aim of increasing separation efficiency. Experiments were carried out within a pH range of 0.1-5.0 using sole D2EHPA and D2EHPA-Cyanex 302 mixtures in different ratios. Increasing Cyanex 302 to D2EHPA ratios in the organic phase caused a left shifting of the extraction isotherm of cadmium and a right shifting of the extraction isotherm of nickel. As a result, optimum separation was found with a Cyanex 302 to D2EHPA ratio of 0.1M:0.5M. In the present system, effect of a modifying reagent such as TBP was studied. The influence of various diluents including kerosene and carbon tetrachloride was also investigated.IntroductionBatteries are popular sources of portable energy. Ni-Cd batteries are manufactured in two main groups of small domestic cells and large industrial batteries with 80% being in domestic use. Ni-Cd cells have various uses, for example in cordless electric utensils, cordless telephones, airplane engine starters, and communicational distribution systems [1].Depleted Ni-Cd batteries are classified as hazardous waste since nickel and cadmium are heavy metals and suspected carcinogens. Given the risk associated with uncontrolled disposal, directions for issuing legislation on disposal and recycling of used batteries have been made in industrialized countries [2]. Recycling of Ni-Cd batteries is important from both economic and environmental points of view. Different methods have been used for recycling these wastes through pyrometallurgy [3], biotechnology [4,5], and hydrometallurgy [1,2].Due to the advantages of hydrometallurgical processes, several studies have been implemented on leaching and solvent extraction (SX) of the used Ni-Cd batteries. Leaching of batteries is usually done in sulfate or chloride media; while solvent extraction has been used in different extractants: two-stage solvent extraction by D2EHPA and Cyanex 272 [6]. Solvent extraction of Cd from leach solutions has been studied using various extractants; Cyanex 301 [1], D2EHPA [7], Cyanex 302 [8], Cyanex 923 [9], Cyanex 272, Tops 99, PC88A [10]. Application of phosphorus based extractants for the solvent extraction studies of Ni such as TOPS 99 [11], D2EHPA [12], Cyanex 272 [2], has been investigated. Separation of Cd(ll), Ni(II), and Co(ll) from chloride leach liquor of spent batteries [13], were explored in the earlier studies. Cd extraction with D2EHPA involves co-extraction of both Ni and Co [14], which causes issues in the separation process efficiency."

Jan 1, 2012

By Patrick R. Taylor

Iron phosphate glasses are promising host matrices for vitrifying actinide rich nuclear wastes materials because of their high solubility of actinide oxides, high chemical durability, and relatively low melting temperatures. An iron phosphate waste form was developed at the University of Missouri-Rolla. The structure and property of the waste form were well characterized by materials techniques. However, to scale the process and advance it to commercial viability, it is necessary to understand the processing parameters, such as the partitioning of waste elements and the viscosity as a function of temperature. Viscosity of 40 Fe203 - 60 P205 mole % iron phosphate melts (prepared with phosphorous pentoxide and ferric oxide) at 1000-1200 C was measured by the rotating-spindle method. It was discovered that this fluid has non-Newtonian behavior. Experiments were performed to study flow properties following the Standard Test methods for Rheological Properties of Non-Newtonian Materials by Rotational (Brookfield) Viscometer (ASTM D 2196-86). Samples prepared using ammonium phosphate and ferric oxide showed Newtonian behavior and the temperature dependence of the viscosity was studied over the range of 1000 to 1200 degrees C. The difference in flow behavior between the two fluids was analyzed in terms of preparation conditions and variation in the final composition and phases. The partitioning behavior of waste elements in the iron phosphate glass was studied by melting in a high temperature furnace and JCP analysis. The experimental results show that the solubility of Ce and Sr in phosphate glasses is significantly higher than the solubility associated with borosilicate glasses. This strengthens the conclusion that iron phosphate may be a viable alternative to borosilicate glass for immobilization of high heavy-metal-content wastes and actinide rich wastes.

Jan 1, 2002

By G. T. Lapidus, O. J. Solis-Marcial

"The oxidative dissolution of copper from refractory minerals, such as chalcopynte, represents a technological challenge that has occupied hydrometallurgists for more than half a century. Innumerable processes have been suggested, but the majority operates at high temperatures or employs corrosive media. The origin of this refractory nature is the formation of passivating phases of iron(III) or copper. One option is to add non-corrosive ligands that complex these metal ions, thereby facilitating their dissolution. In the present work, the effect of acetone in sulfuric acid solutions was studied. The initial experiments were on chalcopynte carbon paste electrodes using cyclic voltammetry, where greater reactivity was observed. Later, leaching tests with hydrogen peroxide, cupric sulfate and ozone and, as oxidants, were performed. High extractions were achieved in three hours at 50°C. The solid residues contained the iron in the form of Fe203 and FeOOH.IntroductionChalcopyrite is the most important mineral of polysulfide copper ores [1] and accounts for approximately 70% of the world's copper reserves [2]. Currently, the copper present in chalcopyrite is extracted mainly by pyrometallurgical processes, which generate environmental concerns because of the formation of SO2 gas and submicron particulates [3]. The development of a less aggressive hydrometallurgical process for the extraction of copper would constitute a possible solution to these problems. For that reason, studies of the dissolution behavior of chalcopyrite are of great technological importance [4], However, the proposed oxidative leaching routes for chalcopyrite, generally at high pressures and temperatures, have not been implemented on an industrial scale, because of the elevated costs required to equal the high copper extractions obtained in thermal processes. These extreme leaching conditions are required because of the refractory nature of chalcopyrite. Passivation has been used to explain this phenomenon, although researchers have disagreed on the composition of the layer, which is various have assumed to be sulfur, copper sulfides, and iron-bearing jarosites or hydroxides [5]. If the latter compounds are the cause, an alternative solution would be the use of polar organic solvents in the oxidative leach to decrease the formation of the passivating iron layer. In this work, the influence of acetone on the oxidative leaching of a chalcopyrite concentrate at room conditions is explored."

Jan 1, 2012