By Christopher B. Vierrether

Reflected light microscopy, scanning electron microscopy, and electron microprobe analysis have been used to determine the mineralogy, phase percentages, grain sizes, textures, and partitioning of cobalt and nickel in two cobalt-nickel rich mattes. These mattes were prepared by submerged bath smelting from a flotation cobalt-nickel concentrate containing 4.8% cobalt and 5.1% nickel. The concentrate was derived from lead-zinc-copper ores of the Viburnum Trend, southeast Missouri. Eleven discrete phases have been distinguished in the matte samples, three of which contain significant cobalt and nickel. The phases are cobaltpentlandite ((Co,Ni,Fe)9S8), cobalt-bearing marmatite ((Co,Fe,Zn)S), shandite (Ni3Pb2S2), bornite (Cu5FeS4), galena (PbS), magnetite (Fe3O4), pyrrhotite ((Co,Ni,Cu,Fe)1_xS), chalcocite (Cu2S), CuPbS phase, metallic copper, and metallic silver. Cobaltpentlandite and cobalt-bearing marmatite- occur in coarse grains (50 µm) that would separate readily during grinding, but shandite contains small (5 - 10um), abundant inclusions of pyrrhotite and bornite.. Some mineralogical variations between the two matte samples were due to differing degrees of oxidation during smelting,

Jan 1, 1988

By A. Mezei

Samples of cobalt and bismuth concentrates produced from the NICO deposit in Northwest Territories were subjected to a comprehensive metallurgical testwork consisting of: pressure oxidation, ferric chloride leach and carbon in leach, to recover the cobalt, bismuth and gold, respectively. A specific testwork program was designed to allow for the optimization of process parameters under multiple restrictive criteria. The overall objective was to establish leaching sequences that could produce acceptable recoveries while generating environmentally disposable residues as well as solutions suitable for further processing. The recoveries for the leaching stage, under the optimum conditions, were 97% for cobalt and 95% for gold, in the case of the cobalt concentrate. The bismuth concentrate produced recoveries of 99% for bismuth, 99% for cobalt and 97% for gold, respectively

Jan 1, 1999

By Emmanuel N. Zevgolis

After the Krupp-Renn process was shown to be unsuitable for treatment of the Greek nickeliferous laterites, the LM process was developed. It involved roasting reduction up to metallic iron in a Rotary Kiln (R/K) and smelting in an Electric Furnace (E/F). Ferronickel (with 15% Ni) produced in the E/F, was upgraded to 90-95% Ni in an 02 converter. Raw Ni was then electrolyzed to pure Ni. The LM process was not applied for very long however, due to various problems. So, the Larco process was developed, i.e., pre-reduction in R/Ks, smelting of the calcine in E/Fs for ferronickel production (15% Ni) and enrichment to 20% Ni, in an O2 converter. Until now, many technological improvements have been invented and applied or adjusted to the process, which have made it a fully reliable and competitive one. sohe of the improvements were the invention and application of a new granulation process for liquid ferronickel, the modification of the existing R/Ks, E/Fs and converters and the design of new ones, and others that are described in the paper. Keywords: Ferronickel, metallurgy, laterites, LM process, Larco process

Jan 1, 2004

By Robert C. Laudon

Spectral reflectance data for 335 minerals, including 228 minimum-maximum combinations for anisotropic minerals giving a total of 563 data sets, have been collected from the literature and combined into a single database. Quantitative color values for x, y, Y, Ad , and Pe referred to ICI standard i11uminant C have been calculated from the spectral reflectance data and are included in the database. The programs plot spectral reflectance curves together with all quantitative color data for each mineral in the database. The plots and data can be directed to a dot-matrix printer such that a databook of quantitative color and spectral reflectance having one mineral per page can be generated for the ore microscopy laboratory. In addition, by sorting the database and grouping the minerals, groups or individual minerals can be plotted on the chromaticity diagram, and this plot can also be sent to a dot-matrix printer. The programs are written in compiled BASICA for an IBM-PC with graphics capabilities and at least 128KB random access memory (RAM). The databases are accessible either through the BASIC programs or through any commercial database system capable of loading and writing to an ASCII format sequential file. The programs and database are available by sending a blank diskette and self addressed, stamped envelope to the authors.

Jan 1, 1987

By Charles H. Rawlins

Reported is work done on processing of steel mill effluents in the areas of dewatering and separation. Much of the waste from these operations is in the form of sludges from scrubbers, in which the primary constituent is iron oxide. Recycling of the sludge&apos;s magnetic fraction has become economically attractive in order to reduce the overall volume placed in landfills. The objective of this research is to determine the effectiveness of combining magnetic and cyclonic forces, to recover iron oxide particles from waste water stream, while decreasing the volume to be disposed. Three different size hydrocyclones, operating within the field of a quadripole magnet, were tested using varying feed pulp densities of magnetite, magnetite/dolomite, blast furnace (BF), and basic oxygen furnace (BOF) slurries. In the first three cases, the percentage of magnetics recovered increased to greater than 95%. The limiting operational factors are; high pulp density for small cyclones, which can cause flow blockage within the magnet field, and extremely fine particle sizes (<2 microns), which cannot be recovered. The results indicate this technique can remove virtually all the magnetic particles from some steel effluents to a 40-50% weight percent solids pulp, on an in line continuous basis.

Jan 1, 1994

By Francis C. Furman

Microscopic evidence indicates that the high sinterability of certain commercial dolomites is tied to specific dolomite textural characteristics. This study encompasses detailed characterization of the unprocessed dolomite and sintering doloma results. The chemical and mineralogical compositions, insoluble residue, chemistry homogeneity, crystal size, primary carbonate texture, secondary dolomite texture, deformation structure, porosity type, porosity, and density of the raw dolomite were observed. These characteristics are compared with sintering trials of <74um powder-compacts samples in which holding times were varied. The evolution of the dolomite characteristics are reviewed and related to the final sintered doloma characteristics. The critical characteristics of a single-stage sintering brick dolomite are the following: 1) primary oolitic texture, 2) dolomite purity, 3) dolomite stoichiometry 4) minimal impurities, less than 1 weight {%} Fe2O3 Al2O3 and SiO2, 5) chemical homogeneity, 6) high density, 7) very low porosity, S) very coarse homogeneous crystallinity, 9) nonplanar dolomite texture, 10) abundant strain related slip microdeformation structures, 11) minimal subsequent alteration. Even with grinding to <74um the nonplanar dolomite texture and slip deformation still have a major effect on doloma sintered density. The three newly identified characteristics of single-stage sintered refractory brick dolomite are their primary oolitic texture, secondary nonplanar texture and abundance of stress related microdeformation structures. The primary oolitic texture reflects a homogeneous pure carbonate with respect to chemistry and crystal size secondary nonplanar texture produces crystals with large surface area to volume ratio. Stress related slip deformation moves CO, groups in to the same site of another CO, group but different orientation which is very unstable. All of these characteristics may facilitate the formation of higher density dolorna sinters.

Jan 1, 1995

By Lv Guozhi, Niu Liping, Shi Guanyong, Liu Yan, He Jicheng, Du Yanjun, Dou Zhihe

"We proposed thermit reduction-electroslag remelting method of preparing the large scale CuCr alloy. But there are pores and oxide inclusions in CuCr alloy prepared by thermit reduction process. This paper studied mainly the effects of ratio of reactant and additive on the inclusion type and their occurrences in CuCr alloy. The alloy prepared in different process conditions was characterized via XRD, SEM, OM and TEM and metallographic microscope, in which the existing state and micro-structural defects of inclusions are analyzed. The results show that there are three distinct regions: copper-rich regions, chromium-rich regions and the inclusion regions. Inclusions are mainly in the form of stomata and Alz03 phase, mainly locating in the copper-rich phase and the interface area of chromium-rich phase and the copper-rich phase. Adding Na3AlF6 and heating agent can effectively reduce the inclusion content in the alloy.1 IntroductionIn recent years, with the development ofhigh power vacuum and high-pressure technology ,the CuCr alloy contact material which has many advantages gradually replaced the traditional W-Cu and Cu-Bi series alloy contact material, and become the first choice of material in high-voltage and high-power vacuum switch contacts['-3l. The traditional powder metallurgy method, infiltration method and vacuum arc melting method[4-SJ are using metal Cu powder and Cr powder as raw material by casting molding, and have disadvantages such as high production costs, complicated process, poor product density and low yield, especially in the large size alloy ingots[9-12l. At present, the world regards CuCr alloy new preparation technologies as the first place, and how to achieve a large size the CuCr alloy ingot preparation has become a hot research of CuCr alloy[3l. Zhang Ting-an and Dou Zhihe[l-3l who are supported by national natural science fundation of china successfully successful developed new technologies and core equipment to prepare large-size copper-chromium alloy through aluminum thermal reduction-secondary refining method, and obtained two national invention patents. The method includes two key steps: one is get CuCr alloy consumable ingot by Thermit-SHS with electromagnetic stirring, the other is to refme the CuCr alloy ingot to remove the pores, inclusions and other defects by electroslag remelting technology to get dense and uniform CuCr contact material. The preliminary study results show that means of electromagnetic stirring evidently inhibit effect of alloy ingot macrosegregation during the electromagnetic casting stage, but there are still microstructure defects such as alumina inclusions and pores in the alloy ingots. Therefore, Zhang Ting-an et al refer new ideas of using the electroslag remelting to refine Cu Cr alloy ingots and effectively remove the defects of the ingots such as pores and inclusions [3l _ At present, there is no report of study on the electroslag remelting refining processes of CuCr alloy (the refining slag, remelting current). This article will research mode of occurrence and distribution law of inclusions in the large-size CuCr alloy ingots by Al Thermit-SHS under magnetic field stirring action and provide a theoretical basis for chosing refining slag to remove inclusions by electroslag refining. Meanwhile the article analyses the effect of reduction conditions of Thermit-SHS on the types of inclusions, mode of occurrence and distribution of regular inclusions in alloy ingot, and refer theory for inclusions regulation in the large-size alloy ingots."

Jan 1, 2013

By Rodney Hundermark, July Ndlovu, Lloyd Nelson, Phillimon Mukumbe, Paul van Manen, Whitey Seyanund, Bart Pieterse, Bertus de Villiers, Diale Mokwena

The 2003 redoubling in power to 68MW on the Polokwane Smelter furnace represented a significant intensification in platinum group metal (PGM) smelting. Combined with onerous ‘green’ PGM concentrate smelting requirements, this yielded conditions unusually corrosive to copper coolers and refractories. This presented unexpected operational and design challenges to reliable crucible operation and maintenance. Combined with specific operational control intervention, development of protective coatings has led to the life of water-cooled copper components improving from 9 to 40 months. The furnace matte endwall was extended in 2010 to address accelerated wear of refractories and the potential risk for contact of copper components by superheated matte. An 18 month planned endwall rebuild cycle has been demonstrated (versus catastrophic failure within 9 months). Finally, benefits including lower energy consumption, improved metal recoveries and higher productivity resulting from operational and in-house design developments will be described, that justify “Celebrating the Mega-scale” in PGM smelting.

Jan 1, 2014

By Yuanbo Zhang, Zhixiong You, Zijian Su, Bingbing Liu, Guanghui Li, Guang Yang, Tao Jiang

Sodium stannate is widely used in the electroplating and tin alloy industry. But the traditional processes for sodium stannate production are characterized by long flowsheet, high production cost and strict requirement for the equipments, etc. In this study, a novel process for sodium stannate preparation from cassiterite concentrate and sodium carbonate via roasting in CO/CO2 mixed gas then followed by leaching was developed. The effects of roasting parameters on the Sn leaching efficiency were conducted. A Sn leaching efficiency of 77.2% was obtained under the optimal conditions. Sodium stannate (Na2SnO3·3H2O) with a purity of 95.8% was produced by the new process, which is better than that specified for the industrial first-grade product.

Jan 1, 2014

By I. Goy D. Gaballah

Decontamination of synthetic K2Cr2O 7 solutions containing 10 to 1000 ppm of hexavalent chromium using chemically treated barks have been studied at a laboratory scale. Metal removal from solutions depends on the pH, the initial concentration and the bark species. The use of a pulp density of 2 % in an agitated flask at the optimum pH for 2 hours leads to a percentage chromium removal of about 95 of the initial metallic ions content. Other trials conducted by column percolation permit the determination of the maximum retention capacity of the treated bark. Depending on the bark species, oak or pine, the rate of saturation is 110 and 215 mg of Cr per gram of bark respectively. The incineration of the metal charged barks gives recyclable, ashes containing 36 and 54 % of chromium metal for the oak and pine barks respectively. Experiments, of Cr6+ removal from industrial effluents containing up to 1800 ppm have been carried out on the semi-pilot plant scale. They have lead to the elimination of about 90 % of hexavalent chromium from this industrial waste solution. Further studies are conducted in order to define the hexavalent chromium binding mechanisms on bark constituents.

Jan 1, 1992

By J. Borlée, J. P. Birat

"ULCOS is a large European program launched by a consortium of 48 partners led by arcelor and a core group of steel producers, which was started in 2004 with the support of the European Commission (RFCS and 6FP programs) to search for breakthrough process routes that could, in the future, when fully developed, demonstrate the potential of large cuts in CO2 emissions for the production of steel from iron ore.The timescale for commercial implementation is the post-Kyoto period, i.e. 15 to 20 years from today.The present paper presents the progress made in the first 2 years of this 5 year program.Several concepts are being investigated in parallel: re-engineering of the blast furnace to incorporate CCS in the core of the process, smelting reduction with CCS capabilities, massive use of natural with more CO2-lean technologies than today, hydrogen steelmaking and electrolysis of iron ore. Biomass also offers very attractive perspectives, while raising major challenges.None of these new steelmaking routes are ""no regret"", which means that the European Steel Industry has already incorporated extensive energy saving steps in its present process technology and is working as close to thermodynamics limits as is cinematically and economically feasible, and that decreasing GHG emissions further means introducing breakthrough technologies that add significant costs to the operation of the Steel Mills.They will also require much research and development before they can be proven and implemented commercially.IntroductionThe ULCOS program (Ultra Low CO2 Steelmaking) is a large research program of the European Steel Industry and its industrial and research partners launched in September 2004 to investigate steelmaking technologies that have the potential of reducing the CO2 emission of the Industry by a large amount, typically in the order of 50%. It is supported in the European Community by the 6th Framework and the RFCS programs through 3 complementary European projects [1,2].The present paper summarizes the work carried out in the phase 1 of ULCOS and in framing the program of phase 2."

Jan 1, 2008

By Shadia J. Ikhmayies

SnO2:F/CdS:In bilayers were produced by the spray pyrolysis technique on glass substrates. The structures were characterized by recording and investigating their transmittance curves, I-V plots, X-ray difractograms (XRD) and by observing their scanning electron microscope (SEM) images. From the I-V plots it was found that the SnO2:F forms an ohmic or quasi-ohmic contact with CdS:In. XRD patterns show the polycrystalline nature of the films and show that there is a small shift in the position of the (200) line of SnO2:F without the appearance of new peaks. The morphology of the structures are compared with those of SnO2:F alone and CdS:In alone on glass substrates.

Jan 1, 2009

By H. Dong, J. J. Valencia, L. Nastac

"A comprehensive computer model was developed to understand and optimize the centrifugal casting process for manufacturing TiC/Al-bronze friction drums. Performance of these components requires proper distribution of TiC particles, which is shown by dimensional analysis to be dominated by centrifugal buoyancy effects and solidification kinetics.The model addresses the following: (1) a rheology-viscosity model of the interference between moving particles, (2) engulfment (entrapment) or pushing of particles in the mushy region by the advancing solid/liquid interface, (3) nucleation and growth of equiaxed and eutectic phases, (4) effects of particle size, particle concentration, and cooling rate on the final grain size, and (5) the impingement effect of particles on the nucleation and growth kinetics of solidifying microstructure.Parametric studies were conducted using the computer model to investigate the effects of various process and material parameters on the distribution of TiC particles. The effects of the volume fraction, size, and morphology of the particles (including clusters and agglomerates) on the particle distribution were evaluated in detail. The complex interaction between the solidifying structure and insoluble ceramic particles in centrifugally-cast metal-matrix-composites was also investigated.The model predictions of particle distribution and microstructure were validated with experimental data for centrifugally-cast A356/SiC and TiC/Al-bronze alloys.This work was conducted by the National Center for Excellence in Metalworking Technology, operated by Concurrent Technologies Corporation under contract No. N00140-92- C-BC49 to the U.S. Navy as part of the U.S. Navy Manufacturing Technology Program."

Jan 1, 2000

By S. Seetharaman

In the processing of molten metals, it is extremely important to monitor continuously the concentration levels of various minor elements, In the production of common metals like copper, iron and aluminium electrochemical sensors involving solid, as well as liquid electrolytes are being increasingly used to measure the concentrations of minor elements The present paper deals with the electrochemical principles underlying these measurements and the possible errors involved. One of the major difficulties in the case of the solid electrolytes is to correct for the consequences oldie electronic contribution to the conduction of the electrolyte. The application of the electrochemical sensors for molten metals processing involves designing of these probes to withstand the industrial operating conditions. In this respect, significant achievements have been made with respect to the design of oxygen probes for liquid metals in general and liquid copper in particular. Some of the salient design features are discussed in the paper, The application of auxiliary electrodes for impurities in molten metals like phosphorus in copper and silicon in iron are taken up. The development of oxygen sensors for slags is given special attention. Recent developments&apos; in the field of sensor technology, as applied to metals processing are highlighted.

Jan 1, 1996

By Gui-fang ZHANG, Zhe SHI, Lei GAO

Secondary V-recycling slag, an industrial waste containing high gallium is being dumped continuously, which causes the loss of gallium. Thus, the alkali fusion process was employed to recover gallium from this slag. The effects factors on extraction of gallium such as roasting temperature, roasting time, alkali fusion agent concentration and CaO concentration were investigated in the paper. The experimental results indicated that excessive roasting temperature and roasting time is unfavorable to the recovery rate of gallium. The appropriate roasting temperature and duration are 1000 and 2 hours, respectively; The appropriate proportioning of Na2CO3: NaOH is 2:1 when the concentration of alkali fusion agent weighs 0.4 times the mass of the slag; In order to remove SiO2 from the leaching liquor, CaO should be used as an additive in the roasting process. The appropriate concentration of CaO should weigh 0.2 times the mass of the slag. Employing these optimal alkali fusion conditions in the roasting process, gallium recovery is above 90%

Jan 1, 2015

By Mikhail Mikhaylenko

Natural and technogenic sources of rare earth elements (REE) and other rare and scattered metals are remarkable for their chemical diversity. The pregnant solutions going to processing for the valuable metals have very complex compositions. Both targeted elements and competing impurities are present in the solutions in different chemical forms. Thus processing of such materials demands application of different technological tools addressing numerous specific tasks on the way to the final product. Screening work was undertaken to identify the best resins among developmental and commercial products addressing typical cases in the hydrometallurgy of scandium and REE. The cases outline typical sources of scandium and REE, such as streams of TiO2 production, extracted phosphoric acid, barren uranium solutions and others. Specially designed ion exchange resins can be effective tools.

By R. W. McCallum, B. Jensen, K. W. Dennis

"There are substantial challenges in the exploration of magnetic materials in the R-TM-X system (R =rare earth, TM= transition metal, X =stabilizing element) where Xis an element which has high vapor pressure, high reactivity, toxicity, or a refractory nature. This research focuses on discovering new phases with high anisotropy and high magnetization through closed diffusion couples inside high purity Fe crucibles. Either vapor-solid reactions or powder metallurgy techniques are then employed to isolate a stoichiometric sample based on a potentially magnetic phase found in the diffusion couple. For this research, X = F, Ca, Sr, Se, Zn, Bi or Cd, TM= Fe, and R = Nd. New ternary phases have been discovered with WDS and EDS, and magnetic transition temperatures have been measured with a SQUID magnetometer and VSM.IntroductionSince the discovery of the RCo5 compounds in the 1960s, rare earth- transition metal (R-TM) magnets have been the main focus of permanent magnetic research over the last five decades. Iron-based magnetic materials were studied next in attempts to avoid the unstable price of cobalt as well as the high price of Sm, the top performer in the RCos and RzC011 series. This hunt eventually led to the discovery of Nd2Fe14B with a theoretical BHmax of 64 MGOe, nearly double that of the previous samarium based magnets. The next few decades were devoted to enhancing the magnetic properties ofNd2Fe14B by the improvement of processing techniques and the additions of alloying elements. The only complete elemental substitution discovered in this system was R1Fe14C, which did not improve magnetic properties. It is probably safe to say that most ternary R-TM-X systems, where Xis any element that may stabilize a ternary phase, have been investigated if they may be prepared by conventional processes such as arc or induction melting. The present study offers a systematic approach to developing a novel diffusion couple technique in which the volatile, reactive or toxic alloying elements are laser welded inside a high purity Fe crucible. This experimental setup will prevent the oxidation of the rare earth element, as well as contain the volatile X element. As the goal of the research was to find new rare earth permanent magnets, only phases which contained greater than 60 wt% Fe were investigated. 247"

Jan 1, 2012

By S. R. Reddy, R. G. Reddy

"The Margules equation is used for interpreting excess Gibbs energy of several ternary systems. In the present study activity coefficient of a dilute solute, 2, in a binary solvent 1-3 was derived. The derived expression is used to interpret logarithmic activity coefficient of oxygen and sulfur in several metallic systems. Self interaction parameter of the solute is derived from the partial function of solute using constant compositional path. An expression for logarithmic activity coefficient and self - interaction parameter of solute is also derived using Maclaurin infinite series. The derived equation is based on Maclaurin infinite series used successfully to deduce thermodynamics of self interaction of oxygen as a interstitial atom in two metallic systems. The predicted thermodynamic parameters values using Maclaurin infinite series and Margules equations, are in excellent agreement with the experimental data and also our predictions are far more accurate than the predictions made by other models.1 IntroductionIn most of the pyrometallurgical high temperatures processes, interactions of solutes such as oxygen, nitrogen and sulfur, with the solvent atoms are most important during refining processes. There are numerous theories are developed [1-25] to interpret the thermodynamics of solutes in multicomponent alloy systems. Which are mainly developed using statistical or Quasichemical equations.Wagner [4] developed one energy parameter ideal solvent model based on activity coefficient of solutes compositional dependency. He used one energy interaction term which is not able to account for interaction energy parameters for the same solute concentration at different solvent compositions and also it is ineffective model to predict for strong interacting systems."

Jan 1, 1996

By Jiann-Yang Hwang

A study on microwave assisted chalcocite leaching was carried out with a microwave hydrothermal reactor. The leaching was conducted with thick mineral slurries (50-100 g/l). The leaching media is a mixed solution of CuCL2 and NaCL The investigation included the effect of leaching temperature, quantities of the minerals per unit slurry volume as well as the initial concentration of cupric ions were investigated. The results were discussed and compared with that using conventional leaching method.

Jan 1, 2003

By J. E. Dutrizac

The mineral forms of silver, lead and cadmium in the zinc concentrates and the various roaster products made by the Kidd Creek Division of Falconbridge Inc. have been elucidated. In the concentrates, all three elements occur mainly in sulphide form, either in solid solution in the principal ore minerals or as discrete mineral grains. During roasting, Ag, Pb and Cd are preferentially concentrated in the hot cyclone and ESP dusts of the roaster train. Silver is converted to <0.5 µm grains of silver metal and to Ag2S04 which dissolves in or impregnates silicates. Lead is converted to Pb-bearing silicates or to PbS04 and PbO which are present either as tiny free grains in ZnO or as an intergrowth with lead silicate. Lead is also a minor constituent of the ferrite phase. Cadmium occurs mostly as cadmium-bearing zno and ZnFe2o4 , but a significant amount also reports as Cd-bearing silicates or zinc sulphate.

Jan 1, 1990