By G. L. Fisher, R. H. Geils

The effect of small amounts of columbium (<0.01 to 0.10 pct) on the ?-a transformation occurring during the continuous cooling of a low carbon Ni-Cu steel was investigated. Dilatometer specimens were aus-tenitized at 950" and 1068?C and cooled at 17? and 375 C° per min. Columbium caused a marked depression in the ?-a transformation temperature except when cooling at the slower rate from 950°C. The effec of columbium on the transformation temperature was greater the higher the austenitizing temperature and rate of cooling. A maximum depression of 92 C" was observed. Metallographic examination of specimens of <0.01 and 0.07pct Cb steels heated at 1200°C for 1 hr and cooled at various rates showed that columbium had a major effect on the ferrite morphology. The fer rite in the columbium -free steel remained equiaxed at cooling rates as high as 440 C? per min while the columbium-bearing steel exhibited mixed structures o equiaxed and bainitic ferrite at cooling rates as low as 130 C° per min. The ? grain boundaries in the columbium -free steel provided the ferrite nucleation sites in rapidly cooled specimens. There was a complete absence of nucleation at these sites in the colum bium-bearing steel. It is concluded that columbium depresses the transformation temperature by suppressing ferrite nucleation at the austenite grain bound-aries. In this respect the effects of columbium are analogous to those of boron in low C-Mo steels. It is well known that small columbium additions can substantially strengthen plain carbon steels. As little as 0.02 pct Cb can increase the yield strength of mild steels by 10,000 psi.1 A fine precipitate of CbC has been observed in columbium-bearing steels2 and is generally thought to be responsible for the strengthening. Little attention has been devoted to the effect of columbium on the ?-a transformation. Webster and woodhead3 have studied the effect of columbium on the isothermal proeutectoid ferrite reaction in mild steels. They found similar transformation behavior in steels both with and without columbium additions. However, as the austenitizing temperature increased, the incubation time for the start of the ferrite transformation became longer in the columbium-containing steel. Morrison1 found that the addition of 0.03 pct Cb to a C-Mn steel lowered the transformation temperature by 50 C° during cooling from 1200°C at a rate of 80 C" per min. The strengthening effect of columbium has recently been utilized in an age-hardenable, low-alloy steel containing copper and nickel.4 A small amount of columbium has a substantial effect on the as-rolled strength of this steel. By increasing the columbium level from <0.01 to 0.13 pct the as-rolled yield strength is increased by 15,000 psi. Columbium also significantly lowers the ?-to-a transformation temperature of this steel during continuous cooling from the austenitizing temperature. Because of the low carbon level in this steel (0.05 pct max), it is almost entirely ferritic. Thus, it offers the opportunity of studying the effect of small columbium additions on the proeutectoid ferrite reaction. Of particular interest in this study was the reason for the marked lowering of the transformation temperature by columbium during continuous cooling. EXPERIMENTAL PROCEDURE Materials. The compositions of the steels used in this investigation are shown in Table I. The steels were 30-lb air induction melts. They were forged to 4 by 8 by 1 in. plate at 1230°C, air cooled, and then reheated to 1230°C and cross-rolled in two passes to in. plates. Dilatometry. A Leitz Bollenrath dilatometer was used to record the transformation during continuous cooling from two different austenitizing temperatures. The dilatometer specimens were + in. in diam and 2 in. long. Oxidation and decarburization of the specimens was prevented by maintaining a small positive pressure of dry argon in the dilatometer furnace and by plating the specimens with 1 mil of Cu. For the lowest cooling rate, 17 C" per min, the temperature of the specimen was measured with a Pt-Pt 10 pct Rh thermocouple placed in a & in. diam well in the center of the specimen. During air cooling, 375 C° per min, this method of measuring the temperature interfered with the operation of the dilatometer. However, it was found that the temperature of the specimen could be measured accurately by placing a thermocouple in an identical specimen in a holder adjacent to the one being used to operate the dilatometer mechanism. The dilation-temperature curves were recorded on photographic film and then converted to volume percent ferrite-vs-temper-ature curves. The cooling rates obtained with the dilatometer are shown in Table 11. Cooling rates of

Jan 1, 1970

By D. V. Edmonds, C. J. Beevers

Tensile tests were carried out on a! titanium containing 850, 1250, and 2700 ppm 0, and up to -500 ppm H. The tests were performed at -196", -78", 20°, 150°, and 300°C at a strain rate of -1.0 x 10??3 sec-1. Increasing oxygen content, increasing grain size, and decreasing test temperature resulted in enhanced embrittlement of the a titanium by the hydrogen additions. Metallographic observations showed that this can be correlated with the influence of these parameters on the introduction of cracks into the a! titanium by fracture of titanium hydride precipitates. CRAIGHEAD et al.1 reported that the hydrogen content normally found in commercial-purity a! titanium (60 to 100 ppm) was sufficient to cause a substantial lowering of the impact strength, and they attributed this embrittling effect of hydrogen to the precipitation of titanium hydride. Lenning et al.&apos; found that in commercial-purity a titanium there is an almost complete loss of impact strength at about 200 pprn H, which is approximately half the value needed to eliminate the impact strength of high-purity a titanium. They also showed that the presence of 3000 ppm hydrogen reduces the room-temperature tensile ductility of commercial-purity material to a value of the order of 10 pct; the corresponding hydrogen concentration for high-purity titanium is over 9000 ppm. It thus appears that the detrimental effect of hydrogen on the mechanical properties of commercial-purity titanium becomes evident at much lower hydrogen contents than for high-purity titanium. The main difference between the two types of a titanium might be expected to be the higher level of interstitial impurity in the commercial-purity grade. Jaffee et a1.3 studied the influence of temperature and strain rate on the hydrogen embrittlement of high-purity and commercial-purity ! titanium. In general, the behavior was the same for both materials; embrittlement was enhanced by decreasing temperature and increasing strain rate. Recent results from tests on commercial-purity a titanium containing 850 ppm O and varying amounts of hydrogen up to -500 ppm showed that the degree of embrittlement by hydrogen is intimately related to the fracture characteristics of titanium hydride precipitates.4 The present paper considers the interrelationship between the mechanical properties and micro-structural features of commercial-purity a! titanium containing 850, 1250, and 2700 ppm 0 and varying amounts of hydrogen up to -500 ppm. 1. EXPERIMENTAL PROCEDURE Three types of commercial-purity titanium supplied by IMI* were used in the investigation, and for the *Address: Witton, Birmingham 6, United Kingdom. purpose of this paper are designated Ti 115, Ti 130, and Ti 160. The principal impurity elements are given in Table I. The material was received in the form of 12.7 mm diam bars having a fully recrystallized structure. Tensile specimens with a round cross-section of 4.5 mm diam and a gage length of 15.2 mm were machined from the bars. In order to develop the same grain size (mean linear intercept of grain boundaries) in each of the three types the specimens were annealed under a dynamic vacuum of <10?5 mm Hg, Table 11. Specimen hydriding was carried out in a modified Sieverts apparatus;&apos; hydrogen was taken into solution at 450°C and after holding the specimens at this temperature for 24 hr they were furnace-cooled to room temperature at an average rate of -100 C deg per hr. By this method nominal hydrogen contents of 0, 50, 100, 250, and 500 ppm were introduced into specimens of Ti 115, Ti 130, and Ti 160 (100 ppm (wt) -0.5 at. pct). The actual hydrogen contents were calculated from the weight differences obtained by weighing the specimens before and after the hydriding treatment. Tensile tests were carried out at temperatures of -196", -78", 20°, 150°, and 300°C on a 10,000 kg In-stron machine at a nominal strain rate of -1.0 x 10-3 sec-1. Fractured specimens were sectioned in planes parallel to the tensile axis, mechanically polished to 0.25 µm grade of diamond paste, and then attack polished using a solution containing by volume 99 parts H2O, 1 part HF, and 1 part HNO3. Although the latter treatment unavoidably opened out cracks and voids visible after mechanical polishing, it did reveal the grain structure, titanium hydride morphology, and deformation twinning structure.

Jan 1, 1970

By V. F. Zackay, W. A. Goering

ALLOYS of iron and aluminum up to 35 wt pct aluminum are single-phase solid solutions, and are of potentially wide applicability.1-3 In spite of early and continued interest1-4 little progress has been made until recently in the preparation and evaluation of sound alloys containing more than 6 wt pct aluminum. Vacuum-melting techniques for the production of ductile Fe-A1 alloys have been described recently.1-7 A. procedure for air melting these alloys is presented here. Low-carbon iron is induction melted without a slag in a rammed magnesia crucible. At the beginning of melt-down, aluminum pig (99.95 pct Al), charged in a clay-graphite bottom-pouring crucible is placed in a pot furnace at 1800°F. The primary deoxidation of the molten iron after melt-down is effected by the addition of 0.1 pct aluminum and 0.5 pct manganese. (Hilty and Crafts" have reported a significant increase in the deoxidation efficiency of the aluminum and manganese combination over that of the aluminum alone.) A more drastic deoxidation designed to reduce the oxyen content to the lowest possible level is accomplished by plunging metallic calcium to the bottom of the melt. This is done by wiring small cubes of the metal to a steel rod. A circular shield larger than the diameter of the crucible opening is attached to the rod so that any spa&apos;ttering of the molten metal will not endanger the operator. Since the temperature of the molten metal is above the boiling point of calcium, the bath is vigclrously purged by calcium vapor. It is believed that the calcium-vapor treatment permits a homogeneous distribution of calcium in the melt. Owing to the vigor of the reaction the temperature of the molten metal should be kept below 2900°F prior to the calcium addition. A total of 0.05 pct calcium is added in two stages in this manner. The second calcium deoxidation is made just before charging the molten aluminum into the iron, in order that an excess of calcium be present for the remainder of the melt. The aluminum, which has been removed from the holding furnace, is then hydrogen degassed by bubbling chlorine through a quartz tube immersed in the molten aluminum. The hydrogen-chlorine reaction is an exothermic one preventing the solidification of the aluminum during the 5-min chlorination. Approximately 0.1 pct calcium, based on the amount of aluminum, is then added to the aluminum. A further excess of calcium is introduced into the melt in this manner. The oxide dross is removed, fluorspar is added to the molten iron, and the molten aluminum is poured through the fluorspar slag. The fluorspar should be dried thoroughly prior to its use, as any water present will react with the aluminum. Aluminum oxide formed during the pouring operation reacts with the fluorspar slag to form gaseous aluminum fluoride and calcium oxide. A forced-draft ventilating system is required for this operation as aluminum fluoride is toxic. As soon as the molten aluminum has been added, vigorous manual stirring of the melt is required because the slag-aluminum oxide reaction is highly exothermic and tends to take place near the top of the melt. The combination of high temperature and the slagging action of the fluorspar quickly erodes the crucible at the slag line if the aluminum is not stirred uniformly into the melt. It has been found that at least 4 min of manual stirring combined with induction stirring are necessary to ensure homogeneity. The power is shut off 1 min prior to pouring to allow metal and slag to separate. As much slag as possible is removed from the melt, which is then poured directly into cast-iron molds. A mold wash of aluminum oxide is used to prevent ingot sticking. For slab ingots which are to be rolled into sheet, a carbon-tetrachloride vapor atmosphere or a chlorinated-pitch mold wash is desirable, as the aluminum oxide formed in the pouring operation is subsequently removed by the chlorine in the presence of carbon." As in vacuum melting, a pouring temperature of about 2900°F is recommended. Adequate hot-topping is important as iron-aluminum ingots are subject to very deep piping. Ingots are removed from the molds and buried in vermiculite, where they are allowed to cool slowly to room temperature. The ingots are radiographed,

Jan 1, 1959

By E. Teghtsoonian, E. M. Schulson

The tensile behavior of bcc ordered P&apos; AuZn single crystals (CsCl structure) has been investigated under varying conditions of temperature, composition, and orientation. Between -0.2 and 0.4 T, multi-stage hardening occurs fm stoichiometric and nonstoichio-metric crystals oriented near the middle of the primary stereographic triangle. At higher and lower temperatures, parabolic type hardening occurs, followed by work - softening at the higher temperatwes. Deviations from stoichiometry give rise to increased flow stresses. Multi-stage hardening was observed for most orientations, except along the [loll-[lll] boundary and near the [001] corner of the stereo -graphic triangle, where parabolic type hardening occurs. Along two slip systems, (hk0)[001] and (, operate simultaneously while in the [001] comer, slip occurs mainly on the system. Electron microscopy of deformed crystals revealed bundles of edge dislocations forming walls approximately Perpendicular to the glide plane. In general the plasticity of 4&apos; AuZn closely resembles the plasticity of bcc crystals. In recent years, considerable interest has arisen concerning the mechanical properties of the CsCl type intermetallic compounds Ag Mg,&apos;- Fe co,&apos; and Ni Al.&apos;-&apos; The compound P&apos;AuZn is structurally similar. It has a low and congruent melting point of 725"~,&apos;" remains ordered up to the melting point,16 and pos-esses a range of solid solubility from 47.5 to 52.0 at. pct Au at room temperature.15 The present paper reports the results of an investigation on the general tensile behavior of material in single crystal form. Some dislocation configurations characteristic of the deformed state are also reported. The results of a detailed study of the slip geometry in AuZn are presented in a separate paper.17 PROCEDURE Alloy preparation, crystal growing techniques, and the procedure followed in selecting specimens of minimum composition variation are reported elsewhere.17 Dumb-bell shaped tensile specimens were prepared by carefully machining single crystals in a jewellers&apos; lathe to a gage length of 0.80 in. and diam of 0.090 in. Back-reflection Laue X-ray patterns and room temperature tensile tests revealed that machining damage could be eliminated by electrochemically polishing 0.005 in. from the machined surface followed by annealing at 300°C for 1 hr. Specimens were polished in fresh 5 pct KCN solution (40°C, 12 v). Experiments were performed by gripping specimens in a self-aligning pin-chuck and threaded collet system, then straining in a floor model Instron tensile machine. All tests were performed in duplicate. Experimental variables included temperature, composition, and orientation. Unless otherwise stated the strain rate was 2.5 x 10"3 per sec. Liquid testing environments included nitrogen (WOK), nitrogen cooled petroleum ether (133" to 293"K), and silicone oil (293" to 488°K). Resolved shear stress-shear strain curves were electronically computed from autographically recorded load-elongation curves. Stress and strain were resolved on the macroscopic noncrystallographic (hkO) [001] system operative under the specific test conditions of temperature, strain rate, and orientation reported earlier.17 RESULTS The temperature dependence of the work-hardening curves is shown in Fig. 1 for gold-rich crystals of 51.0 at. pct Au oriented near the center of the stereo-graphic triangle. Over the range of intermediate temperatures from -200" to 400°K, they are very similar to those classically observed for fcc metals (reviewed by Nabarro et al.).&apos;&apos; The beginning of deformation is characterized by a region of decreasing hardening rate, stage 0, which is followed by a region of low linear hardening, stage I, and then a region of higher linear hardening, stage 11. At the higher temperatures, stage 111 is observed, a region of decreasing hardening rate. Over the intermediate temperature range, the extent of stage 0 and of the slow transition between stages I and I1 decreases with increasing temperature. Total ductility is large, often greater than 300 pct shear. As the temperature is either increased or decreased, the extent of stage I is decreased, giving rise to parabolic type flow and reduced ductility. Similar temperature effects have been reported for bcc ~r~stals.~~-~~ Below -14O°K, hardening is terminated in brittle fracture while above -400°K. initial hardening is followed first by work-softening and then by chisel-edge type ductile fracture. Stoichiometric (50.0 at. pct Au) and Zn-rich (51.0 at. pct Zn) crystals were also tested from 77" to -500°K. The effect of composition on the flow behavior is illus-

Jan 1, 1970

By A. S. Grove, C. T. Sah, E. H. Snow, B. E. Deal

A summary of- several recent investigations in to the properties of the metal-oxide-silicon system is presented. A major portion of these studies makes use of the MOS capacitance-z)oltage method of&apos; analysis. The particular areas of investigation which are reported include: 1) a general survey of the electvical properties of thermally oxidized silicon surjbccs; 2) a study of ion migration through silicon dioxide films ; 3) measurements of electron and hole mobilities in surface inversion layers; 4) a study of impurity redistribution due to thermal o.ridatiotz; and 5) measurements of the rates of oxidation oj-heavily doper7. silicon. THE importance of the metal-oxide-semiconductor (MOS) system in the semiconductor industry is well-known. In addition to its importance in the "planar" device technology,&apos; the MOS structure is now also used in the fabrication of active solid-state devices. Consequently, extensive efforts have been made recently to obtain a better understanding of the characteristics of this system. A summary of some studies of the MOS system conducted in our laboratories during the past year is presented. For the most part these studies used silicon as the semiconductor, along with silicon dioxide and aluminum as the other two components of the system. Since the MOS capacitance-voltage method of analysis was used extensively in these studies, we will first briefly describe its nature and consider some of the possible causes of deviation of experimental observations from the simple theory. We will then outline the various related areas of investigation carried out in our laboratories and will briefly indicate some of the results. It should be noted that the purpose of this paper is merely to provide a brief summary of MOS studies. More detailed discussions of the various areas of investigation are given in the references cited. PRINCIPLES OF THE MOS C-V METHOD OF ANALYSIS&apos; A sketch of the MOS structure is shown in the upper portion of Fig. 1. In this case the insulating film is Si02 and the semiconductor p-type silicon. If a large negative bias is applied to the metal field plate, holes are attracted to the silicon surface. The silicon then behaves much like a metal and the capacitance measured is that of the oxide layer alone, Co. If a small positive bias is applied to the aluminum, holes are repelled and a region depleted of majority carriers is formed at the silicon surface. This depletion I-egion adds to the width of the dielectric and the measured capacitance begins to drop. With increasing positive bias, the width of the electrical depletion region increases. At some large positive bias an inzevsion regiotr is formed at the surface and additional charges induced in the silicon appear in the form of electrons in this narrow inversion region. Thus the depletion-region width approaches a maximum value and, consequently, the capacitance reaches a minimum value and then either levels off or rises again depending on the measurement frequency and the rate of equilibration of the minority carriers in the inversion layer.3 Band diagrams, along with the corresponding charge distributions, are shown in Fig. 1 for the above bias conditions. If minority carriers cannot accumulate at the surface to form an inversion region, the depletion-region width continues to increase with increased positive bias and the capacitance drops toward zero as in a reverse biased p-n junction. The effect of a work-function difference $hs between the metal and the silicon, and of surface charges per unit area Qss located at the oxide-silicon interface, is simply to attract charges in the silicon much like the applied bias. It can be shown that this results in a parallel shift of the capacitance-voltage characteristic along the voltage axis by an amount corresponding to AV = -$bIs + Qss/Co. Theoretical curves have been calculated4 giving the capacitance of the MOS structure C normalized to the oxide capacitance Co vs the quantity VG here VG is the voltage applied to the metal field plate. In Fig. 2 such calculations are shown as points for a particular oxide thickness and bulk impurity concentration for a p-type semiconductor. (For an n-type semiconductor the curves would be mirror images of these.) All three cases, i.e., low frequency. high frequency, and depletion, are indicated. Also shown in the figure are recorder tracings of the characteristics of actual devices. These characteristics have been shifted along the voltage axis to compensate the effect of surface charges and work-function difference. It is evident that agreement between experiment and theory is good. The nature of this shift along the voltage axis is

Jan 1, 1965

By R. W. Raymond

(Pittsburg Meeting, March,1910.) THE Giroux Consolidated Mines Co. is equipping a five-compartment shaft at Kimberly, Nev., which will serve the Alpha mice. The depth of this shaft, January, 1910, is 963 ft., and of this depth 948 ft. was opened by raising, 15 ft. of sinking was done so that the bearers, collar-set, and three shaft-sets might be installed and concreted, and with this done it was possible to erect the necessary surface-equipment for resuming shaft-timbering on the completion of the raise. The arrangement of the shaft-timbering is shown in Fig. 1. At the 1,000-ft. level of the Alpha, and 750 ft. SW. from the Alpha shaft, a 14- by 18-ft. station was cut, and a 25-h-p. air-hoist *as installed. From here the raising commenced on July 5, 1909. The raise was cut approximately 13 by 21. ft. in area, and supported by timbering with square sets, illustrated in Fig. 2, which shows the division into four compartments. The end compartments, which were used as chutes, had the center girts heavier than in the others on account of the wear from falling rock. The chute-lining was braced by inserting 8- by 8-in. stiffeners parallel to and half way between successive caps. Similarly, the lagging on the wall sides of the cage-way and the compartment for pipes and ladder was stiffened with 4- by 6-in. timbers. In the pipe-and-ladder compartment the chute-stiffeners were reinforced with 8- by 8-in, struts, and as the cage-way was partitioned off by braced lining, there was practically no chance of rock entering the ladder-way in case a chute burst into the cage-way. Over the two center compartments the last two, sets were always bulkheaded with 8- by 12-in. timbers, shown in Fig. 3, and from the lower bulkhead the cage sheave-wheel was suspended. After a round of holes had been blasted and the loose

Jun 1, 1910

By Robert Anderson

ROUGHLY, a crack in a casting may be considered, for the moment, to be due to fracture of the alloy resulting from the stress set up by the contraction in volume on passing from the liquid to the solid state. Cracks may be external or surface, internal or deep-seated, or incipient or so-called strain cracks. Draws may appear as depressions, unevenness, and "pinching in" of the surface of a casting. Roughly, draws are due to contraction in volume and are governed largely by the same factors as cracks. A casting may be cracked, however, without being drawn. Shrinkage is a foundry term; it connotes the contraction in volume of a metal or alloy on passing from the liquid to the solid state. Pattern-makers&apos; shrinkage is the total contraction in volume (including liquid, solidification, and solid shrinkage) that occurs when an alloy is poured into a mold. The contraction in volume of aluminum is one of the principal factors affecting the occurrence of cracks, as will be shown later, and the question of shrinkage and its control requires careful study in any treatment of cracking in castings. In the case of, sand and die castings, cracks have been attributed to a number of causes, but in the case of most light aluminum alloys, they are due to the large contraction in volume on freezing and the lack of its regulation or control. The most important factors are: (1) Contraction in volume; (2) composition of alloy; (3) quality of melting charge; (4) design of casting; (5) method of molding; (6) hardness of ramming; (7) method of gating; (8) hardness and characteristics of cores; (9) chills; (10) risers; (11) melting temperatures; (12) furnace used for melting; (13) pouring tempera-tures; (14) inclusions in alloys; (15) hot shortness of alloys; and (16) physical properties of alloys at high temperatures. Of these, the first, second, third, and eleventh to sixteenth involve ascertainable metallurgical facts; the remainder are largely matters of opinion, judgment and technical knowledge of men experienced in the production of castings.

Jan 10, 1921

By G. L. F. Powell

Bulk samples of silver have beat undercooled lo a large degree in contact with crystalline siliceous and ceramic oxide materials, indicating lhat stable oxides and oxide compounds are not the heterogeneous nucleants which normally catalyze cryslallization within a feu degrees of the equilibrium freezing point. Since 400-g samples were undercooled 250°C in contact with cristobalite, it is concluded that the undercooling required for homogeneous nucleation of sil11er is greater than 250°C. Undercooling was Jacilitated by precleaning the crucibles with a high-fires -sure blast of gas. IN numerous experiments on the undercooling of metal melts it has been assumed that a solid glassy surface, being non crystal line, will have no effect in catalyzing crystal nucleation from the melt. Conversely, it is usually accepted that any crystalline surface, in contact with a metal melt, will catalyze nucleation of metal crystals from the melt at degrees of undercooling less than that at which homogeneous nucleation will occur. Both these assumptions were implicit in the claim that homogeneous nucleation was observed in experiments1&apos;2 on the undercooling of small metal droplets (10 to 100 mp diam). The droplets were thought to be freed of suspended crystalline particles which would otherwise catalyze heterogeneous nucleation. They were supported on flakes of silica glass which were assumed to be amorphous, and therefore incapable of acting as substrates for heterogeneous nucleation. In later experiments, large samples of molten metal were undercooled to temperatures similar to those achieved by the droplet technique by melting in a fused-silica crucible3 or a boro-silicate glass slag.4 Since these samples were usually fully enclosed in glass at the moment of freezing, it seemed possible that nucleation was homogeneous when maximum degrees of undercooling were achieved, despite the large size of the samples (up to 500 g). In experiments on the undercooling of silver5 the metal was contained in vitreous silica crucibles, the

Jan 1, 1968

By W. A. Wood, W. H. Reimann

A study is made of the creep that can be induced in armco iron at room temperature by superposing small amplitudes of alternating torsion on a tensile creep load. It is shown that the creep differs from that in comparable tests on copper in being trmsient only. At the same time, though transient, the creep can produce extensions of some 10 pct under creep loads less than the tensile yield stress of the material. The creep can be largely suppressed b$ applying cyclic strain of suitable amplitude before applying the creep load and the metal thereby stabilized. At room temperature, plastic flow in a metal under steady load is normally limited by strain-hardening processes. However, if a small cyclic stress is superposed on the steady load these processes may be more or less neutralized and, as shown in recent investigations,&apos;-4 plastic flow may continue. In this way annealed copper, for example, can be induced to creep continuously to fracture under loads as small as 1 tsi. Dislocation mechanisms possibly responsible for this room-temperature creep have been usefully reviewed by Feltner.But discussion so far has been based mainly on creep as it is found in close-packed metals initially in the annealed state, and their behavior may not be general. In fact, recent work shows that the form of creep in annealed copper is different from that even in cold-worked copper;7 the creep thus depends on the dislocation pattern already in a metal as well as on the metal itself. This paper describes the creep in annealed armco iron, tested in the same way as the above-mentioned copper. One object was to see how creep in a typical bcc metal compared with that in the annealed close-packed metals. Another object was to utilize the fact that a bcc metal like iron has a more pronounced elastic range than close-packed metals like copper and to find to what extent the creep load or superposed cyclic stress had to exceed their re-

Jan 1, 1964

By B. Tani, K. Anderson, I. Johnson, R. Schablaske

INVESTIGATION of the various rare earth-cadmium binary systems discloses the existence of a compound corresponding to the composition MCd6 in all systems save the La-Cd system. Lattice constants for all of the MCde compounds, except LaCd6 which apparently does not form, and PmCd6 whose synthesis was not attempted, are also recorded herein. Iandelli and Ferro 1 report the existence of the compound CeCd6. No additional information, structural details, and so forth are given. Elliott and Lemons2,3&apos; have measured the vapor pressure of cadmium over CeCd6 and have calculated the activity of cadmium in solid CeCd6. These authors find that CeCd6 exists over a composition range from 5.967 to 6.098 (Cd:Ce ratio) at 584oC, and from 5.971 to 6.118 at 639°C. The following is an excerpt from the paper by Elliott and Lemons: 2 "Recently Mr. F. H. Ellinger of this laboratory has indexed an X-ray diffraction powder pattern of CeCd6.00 which we had prepared by gas phase reaction. The compound has a primitive cubic unit cell with a = 15.783 + 0.001A Based on the volume of the cubes surrounding an elemental cerium or an elemental cadmium atom, Mr. Ellinger finds room for 24.10 CeCd6 formula units in the CeCd6 unit cell; similar calculations based on CeCd2 and CeCd11 yield 24.18 formula units per unit cell. The presence of 24 CeCd6 units per unit cell seems probable with an X-ray density of 8.255 grams per cubic centimeter. The most one can say about in-terstitial~ is that there appears to be room in the crystal even at room temperature." Measurements of the solubility of the rare earths in liquid cadmium4 led to the discovery of GdCd6,

Jan 1, 1964

By Arthur Winslow

Introductory.—The following paper is based upon a report on the lead- and zinc- deposits of Missouri, prepared for the State Geological Survey, which is now being printed. This report is the outcome of work prosecuted by the writer, assisted by Mr. J. D. Robertson, during the past five years. The studies in the State were supplemented by examinations of the similar ore deposits in Wisconsin and Arkan- sas. The report will contain in all about 800 pages, and the aim has been to make it complete and exhaustive, especially in descriptive matter. Naturally, only a brief outline can be presented here, and the reader is referred to the report itself for further details. Contents. I.—History and Statistics, . . 636 II.—Topography of the Region, . 639 III.—General Geology, . . .639 The Archean, . . .639 The Algonkian, . . 640 The Silurian, . . .640 The Devonian, . . 640 The Lower Carboniferous, 641 Tie Coal Measures, . 641 The Tertiary, . . .641 Structural Geology,. . 642 IV.—The Ore-Deposits, . . .643 Geologic Distribution, . 643 The Forms of the Ore-Bodies, . . .641 The Composition if the Ore-Bodies, . . .645 Gangues, . . . 645 Minerals, . . .618 Paragenesis of Minerals, . . . 651 The Structure of the Ore-Bodies, .... 651 V.—Descriptions of Types, . . 652 The Eagle Mines, . . 652 Shaft No. 23, . . 652 The Western Zinc Company or Oswego Lands, 651 The Gobar and Tomlinson Shaft, . 655 The Alba Company&apos;s Mine, 656 The Victor Mine, . . 658 The Bonne Terre Mines, . 660 General Geology, . 660 The Ore-Bodies, . 661 The Vallé Mines, . . 664 The Garatee Mines, . 664 The Corn-Stalk Diggings, . . .665 The Virginia Mine, . 666 The Conlogue Mine, . 667 VI.—The Mode of Formation of the Ore-Bodies, . . 670 The Formation of the Cavities. . . . 670 The Filling of the Cavities, . . . .675 The Formation of the Breccia Deposits, . . 673 The Formation of Circle Deposits, . . .674 The Impregnated Deposits of the Southeast, . 676 VII.—The Origin of the Metalliferous and Other Minerals, 676 1. Originally Deposited in Concentrated Condition, 676 2. Derived from Great Depths, . . .677 3. Original Diffusion, Supplemented by Lateral Secretion, . . . 678 4. Concentrated Through Surface Decomposition, 681

Jan 1, 1895

By R. W. Moore, A. B. Kinzel

Although the iron-carbon diagram has undergone many changes in the last 20 years, the region below the eutectoid line and up to approximately 1.7 per cent carbon has been little affected. This region is generally considered to consist of cenlentite and ferrite. Graphite has been noted occasionally in the hypereutectoid steel region, and the ready formation of graphite nodules in malleable cast iron is a phenomenon difficult to interpret in the light of cementite, supposedly stable at sub-eutectoid temperatures. In this case the graphite formation has been partly explained by the presence of silicon, and many have believed that silicon acts to change the stable state rather than to accelerate reactions so as to arrive at the stable state in a briefer period of time. Consideration of this phenomenon indicates that cementite is not the stable phase in the temperature composition zone referred to. In the course of examining a low-carbon steel tube taken from a petroleum cracking still, which had been in service for approximately three years at temperatures somewhat below the eutectoid temperature, observations were made that shed light on this entire subject. The tube in question analyzed:&apos; C, 0.15 per cent; Mn, 0.49; Si, 0.02; S, 0.023; P, 0.015. The microstructure of the tube after service is shown In Figs. 1 and 2. From these it is evident that cementite as such is absent, and that in its place nodular graphite has been formed. In order to check this observation further, samples taken from the tube were heated at 850" C. for varying periods of time. The small samples were put into a large hot furnace, and the total time is recorded. The structure of the sample after 5 min. at 850" C. is shown in Figs. 3 and 4, and the nest of pearlite surrounding the graphite nodules is most satisfactory evidence of the character of the nodules. As the length of time of heating at this temperature increases, the pearlitic zone increases, with final restoration

Jan 1, 1935

By R. W. Moore, A. B. Kinzel

Although the iron-carbon diagram has undergone many changes in the last 20 years, the region below the eutectoid line and up to approximately 1.7 per cent carbon has been little affected. This region is generally considered to consist of cenlentite and ferrite. Graphite has been noted occasionally in the hypereutectoid steel region, and the ready formation of graphite nodules in malleable cast iron is a phenomenon difficult to interpret in the light of cementite, supposedly stable at sub-eutectoid temperatures. In this case the graphite formation has been partly explained by the presence of silicon, and many have believed that silicon acts to change the stable state rather than to accelerate reactions so as to arrive at the stable state in a briefer period of time. Consideration of this phenomenon indicates that cementite is not the stable phase in the temperature composition zone referred to. In the course of examining a low-carbon steel tube taken from a petroleum cracking still, which had been in service for approximately three years at temperatures somewhat below the eutectoid temperature, observations were made that shed light on this entire subject. The tube in question analyzed:&apos; C, 0.15 per cent; Mn, 0.49; Si, 0.02; S, 0.023; P, 0.015. The microstructure of the tube after service is shown In Figs. 1 and 2. From these it is evident that cementite as such is absent, and that in its place nodular graphite has been formed. In order to check this observation further, samples taken from the tube were heated at 850" C. for varying periods of time. The small samples were put into a large hot furnace, and the total time is recorded. The structure of the sample after 5 min. at 850" C. is shown in Figs. 3 and 4, and the nest of pearlite surrounding the graphite nodules is most satisfactory evidence of the character of the nodules. As the length of time of heating at this temperature increases, the pearlitic zone increases, with final restoration

Jan 1, 1935

By D. I. Bardos

The occurrence of Laves phases (AB,) in various binary alloy systems has been reviewed in recent papers.13 Iron forms Laves phases with Sc-, Ti-, V- and Cr-group elements. However, two of the corresponding Laves phases with cobalt, namely MoCo, and WCo,, are missing. Nickel forms binary Laves phases with Sc and Y, but not with any Ti-, V-, or Cr-group element. These conditions are schematically illustrated in Table I. That electron concentration is a significant factor in determining which type of Laves phase is formed in a given case was recognized long ago by Laves and Witte,4 This concept has been more recently applied to Laves phases formed by transition ele-ments. It now appears that the average electron concentration (average number of electrons per atom outside of the closed shells of the component atoms) may be an important factor also in determining whether or not a Laves phase can occur at all in a given system. As shown in Table I, in the transition element systems considered Laves phases are absent at electron concentrations of 8, or larger (to the right and below the double line in Table I). These absences clearly cannot be accounted for on atomic size considerations, as evidenced by the many inconsistencies apparent in Table 11. While the ideal radius ratio for Laves phases is 1.222, in the systems which do have Laves phases the ratios of CN 12 radii range from 1.10 to 1.46. The consistent absence of Laves phases at RA/RB< 1.10 might be attributed to the low values of these radius ratios. However, Table II shows that absences also occur irregularly throughout the radius ratio range covered. In a previous paper7 it was concluded that, in transition element systems forming u-phases, silicon may act as an acceptor of electrons, thus stabilizing the u-phase at electron concentrations higher than

Jan 1, 1962

By F. E. Smith, David R. Mitchell, B. M. Bird

DENSE-MEDIA processes utilize the familiar laboratory float-and¬-sink procedure on a commercial scale. Just as wood chips float on water and sand sinks, so coal floats and refuse sinks when placed in a medium intermediate in specific gravity between the coal and refuse. Liquids intermediate in specific gravity between coal and refuse used in commercial plants are of four types: (1) Organic liquids of high specific gravity-halogenated hydrocarbons; (2) dissolved salts in water; (3) pseudo liquids obtained by suspending solids, such as sand, in water, and (4) fluidizing a mass of sand or other solids by air currents. Those most widely used for cleaning coal are solutions of calcium chloride in water and a suspended-sand pseudo liquid. Laboratory float-and-sink testing is an intermittent operation during which every opportunity is given for particles lighter than the medium to float and particles heavier to sink. Commercial processes are con¬tinuous, vertical and horizontal currents of the separating medium occur as either part of the process or unavoidedly produced by the intro¬duction of feed and withdrawal of products, so that the exact separation of the laboratory technique is not duplicated by commercial processes. However, separations close to the theoretical are obtained in commercial machines by careful technical control of the process. Most machines in commercial installations are crowded to get as much out of the equipment as possible, so that careful technical control is necessary to get the recoveries and grade of product desired. Sizes usually cleaned are plus %6-in. or plus 3-in. in the United States and plus 36-in. in Great Britain. Coal as small as 1 mm. has been cleaned in some experimental installations. The separation of coal from refuse in sizes finer than about % in. is made difficult by viscosity effects and hence at the present time cleaning is confined to the coarser . sizes. Technical advances in the art of cleaning coal by dense-media

Jan 1, 1943

By D. K. Crampton

INTERNAL stress and season cracking in brass have been studied for many years and the technical literature contains many data on various phases of the subject. A résumé of the literature shows certain fairly well established points upon which various authors are mostly agreed: 1. Season cracking is primarily caused by the presence of relatively high internal stresses, or possibly in some cases by external stresses, or both. 2. A specific corrosion is also essential to season cracking: Certain agents, particularly mercurous salts, mercuric salts and ammonia salts; have such a specific corrosive effect. 3. The tendency to season crack under given conditions increases with increasing zinc content, brass containing less than 20 per cent zinc being relatively immune. 4. In alpha brass the season cracks are intercrystalline; in alphabeta brass they lie between the two constituents; and in beta brass they are transcrystalline. 5. The ordinary impurities or added elements in special brasses have little or no effect on the tendency to season crack. 6. Internal stresses can be eliminated, or at least reduced to a safe &apos;limit by annealing treatments at temperatures that do not produce visible microstructural changes or appreciable softening of the worked brasses. There are, however, some points in connection with the phenomenon of season cracking which have not been thoroughly investigated, or wherein different authors and investigators are not entirely in agreement. The investigations described in this paper were undertaken to determine: 1. The correlation between mercurous nitrate tests and actual season cracking on long-time atmospheric exposure. 2. The quantitative effect of type and degree of drawing operations on the intensity of internal stress and on the tendency to season crack in brass tubes. 3. The possibility of drawing high-brass tubes in such a manner as to prevent the occurrence of harmful stresses rather than to find a remedy for such stresses once having obtained them.

Jan 1, 1930

By J. Gordon Parr, A. J. Goldak

OgdEN et al.1 and Bumps et al.2 suggested that the solubility of aluminum in a titanium extended to 30 pct.* Sagcl,3 Clark and Terry,4 Anderko et al.,5 Ence and Margolin6 and Saulnier and croutzelles,7 subsequently proposed the existence of an intermetallic compound in the region of 25 pct Al. Although Anderko et al.5 suggested that the structure of this phase, Ti3Al, was of the DO,, (Ni3Sn) type, their conclusion was based only upon the results of a powder photograph that included reflections from ? = 0 to ?= 27° (CuK),some of which were reported to be indistinct. Ence and Margolin,6 referring to a 25 pct alloy (but without indicating whether the figure referred to weight or atomic pct) stated: "The structure of Ti2Al is isomorphous with Ti3Sn DO19, as pointed out by Pietrokowsky". But the point was not proven, because Ence and Margolin did not report values of calculated intensities of Ti2Al with the DO,, structure. In fact, the observed intensities they reported are in poor agreement with the values we calculate for DO19 (see Table I). Saulnier and croutzelle7 concluded, on the basis of electron micrography and microdiffraction studies, that the structure of the 25 pct A1 alloy was ordered hexagonal. Our purpose has been to unequivocally determine the Ti3Al structure. Alloys containing 25 pct Al were prepared from iodide titanium and spectrographic standard aluminum by levitation melting. The levitation chamber was evacuated to 10-6 mm Hg before filling with 99.999 + pct A. After casting, the alloy was chilled to liquid air temperature and crushed to -200 mesh in a percussion mortar. The powder, wrapped in molybdenum foil, was annealed (by induction heating) at 1000 "C for 2 hr in the argon atmosphere of the levitation chamber. No sublimate was seen on the foil or elsewhere, and therefore the assumption is

Jan 1, 1962

By Hans Conrad, W. D. Robertson

FORMAL theories of yielding and flow have been developed to describe thermally activated plastic flow in metal crystals.&apos;-" hey are all based on Becker&apos;s&apos; original idea that thermal fluctuations aid the applied stress in overcoming internal barriers to flow and lead to the following relation. where j is the strain rate; C is a constant which includes a frequency factor, the entropy, the number of flow units, and the amount of strain associated with each successful fluctuation; E(T) is the activation energy associated with flow, and is a decreasing function of the applied stress, 7; k is Boltzmann&apos;s constant; and T is the temperature in OK. The various theories differ mainly in the model chosen and in the nature of the relationship between the applied stress and the activation energy. Beckerl and Orowan&apos; suggest a relationship of the form E a(Ti — t)2, where .ri represents the stress required for flow without the aid of thermal fluctuations; Kauzmann,3 Cottrel1,5 and Seeger6,7 suggest E a(t — t) ; Fisher8 suggests E while Cottrell and Bilby4 suggest a more complex relationship between E and 7. Additional data are needed to test these various theories., esweciallv- in view of Dorn&apos;s9 ork. which indicates that the activation energy for creep is independent of the stress and strain. The present paper presents the stress-strain data derived from incremental loading of magnesium single crystals in tension and direct shear, in the temperature range of 78" to 364°K. Incremental loading was employed in order that the creep component of the strain could be determined. Stress-strain curves of aluminum10-13 and copper" single crvstals. derived from incremental loading tests, have been found to be in agreement with those obtained by the more conventional constant strain rate or loading rate tests. Two types of tests were conducted in the present investigation: 1) tests in which the temperature was maintained constant throughout the entire

Jan 1, 1958

By John B. Baker, Bernard B. Betty, H. F. Moore

Fox several years there has been in progress in the Materials Testing Laboratory of the University of Illinois an investigation of creep and fracture of lead and lead alloys. In the course of this investigation it has been shown that the phenomenon of creep occurs in part at the grain boundaries of lead and lead alloys. To study the occurrence of creep and the development of fracture within crystalline grains, two series of tests of single crystals of lead have been carried out. The first of these, a preliminary series, by Mr. Betty, has been described.1,2 The second, pursued by Mr. Baker for his doctoral dissertation, was carried out under the direction of Professor Moore, with the assistance of Prof. G. L. Clark in the X-ray work, and the cooperation and advice of Mr. Betty. This paper is based on the test data obtained in this second series. Single crystals of a very pure commercial lead have been prepared, some of them tested to measure creep, others tested to fracture under long-continued steady load, and still others tested under cycles of repeated tension. An interpretation of the test data of these single-crystal tests is offered, which is a combination of parts of several well-known theories. SPECIMENS The single-crystal specimens were made from a piece of very pure commercial lead sheathing. A spectroscopic analysis of one of the single crystals showed the presence of 0.005 per cent Bi, 0.0001 per cent Cu and 0.0003 per cent Ag. Preparation.-The Bridgman method of casting single-crystal speci¬mens was used.3 The specimens were cast to the shape and size shown in Fig. I (dimensions in Fig. 4c) in a duralumin mold. Molten lead does not stick to duralumin. Fig. 1 shows the mold and the blast flames for heating. After the mold had been heated to the temperature of molten

Jan 1, 1938

By F. E. Smith, David R. Mitchell, B. M. Bird

DENSE-MEDIA processes utilize the familiar laboratory float-and- sink procedure on a commercial scale. Just as wood chips float on water and sand sinks, ,so coal floats and refuse sinks when placed in a medium intermediate in specific gravity between the coal and refuse. Liquids intermediate in specific gravity between coal and refuse used in commercial plants are of four types: (1) Organic liquids of high specific gravity-halogenated hydrocarbons; (2) dissolved, salts in water; (3) pseudo liquids obtained by suspending solids, such as sand, in water, and (4) fluidizing a mass of sand or other solids by air currents. Those most widely used for cleaning coal are solutions of calcium chloride in water and a suspended-sand pseudo liquid. Laboratory float-and-sink testing is an intermittent operation during which every opportunity is given for particles lighter than the medium to float and particles heavier to sink. Commercial processes are continuous, vertical and horizontal currents of the separating medium occur as either part of the process or unavoidably produced by the introduction of feed and withdrawal of products, so that the exact separation of the laboratory technique is not duplicated by commercial processes. However, separations close to the theoretical are obtained in commercial machines by careful technical control of the process. Most machines in commercial installations are crowded to get as much out of the equipment as possible, so that careful technical control is necessary to get the recoveries and grade of product desired. Sizes usually cleaned are plus 3/16-in. or plus 1/8-in. in the United States and plus 1/16-in. in Great Britain: Coal as small as 1 mm. has been cleaned in some experimental installations. The separation of coal from refuse in sizes finer than about in. is made difficult by viscosity&apos; effects and hence at the present time cleaning is confined to the coarser sizes. Technical advances in the art of cleaning coal by dense-media

Jan 1, 1943