Search Documents

By B. W. Levinger

THE system Ti-CI- has been studied by several investigators." ' Though titanium and chromium are completely miscible at high temperatures, an intermediate phase of the approximate atomic proportions TiCr, has been identified at various compositions between 60 and 68 wt pct Cr. The structure of this phase was established as the cubic C15 (MgCu2) type with 24 atoms per unit cell and a lattice parameter 6.929 kX.2 During a study of the ternary system, Ti-Mo-Cr,5 the existence of a high temperature modification of the TiCr, phase was discovered. In a series of alloys annealed at 1300°C and containing from 60 to 70 wt pct Cr and 5 pct Mo, a new phase was present which did not correspond to either ß solid solution or TiCr,. By trial, the new phase was identified to be of the hexagonal C14 (MgZn2) structure with 12 atoms per unit cell. Further work showed that the hexagonal structure was. in fact, also present in binary Ti-Cr alloys quenched from high temperatures. To make the identification more certain, the intensities of the various reflections were calculated assuming a composition TiCr2 and C14 structure. Table I lists reflection planes, interplanar distances, calculated intensities, and a comparison of these values with the lines of a binary Ti-Cr alloy (66 pct Cr) annealed for 20 min at 1385°C and water quenched. Since high angle lines were more diffuse, the correspondence between visually observed and calculated intensities was not as good at these angles. Lattice parameters were computed to be a = 4.922 kX, c = 7.945, c/a :- 1.614. The corresponding interatomic distances are: titanium to titanium distance, 3.00:, kx, chromium to chromium distance, 2.43, kX, titanium to chromium distance, 2.88,, kX. These compare to 3.00, 2.45, and 2.87 kX in the cubic phase, respectively.' The atomic positions in the C14 structure are as follows: Titanium 1/3, 2/3, Z; 1/3, 2/3, 1/2: 2/3, 1/3, i; 2/3, 1/3, (1/2-z); Chromium 0, 0, 0: 0, 0, 1/2; 2x, 2, 1/4; 232, x, %; X, 22, 1/4; X, 2x, 3/4; x. x, 1/4; x, x, 3/4; The values of x and z were calculated for the alloy mentioned and found as follows: z — 0.061, x = 0.165. The values assumed in the intensity calculations were those for an ideal close-packed lattice or z = 1/16, x = 1/6. Work in the Ti-Mo-Cr system indicates that y2 the hexagonal modification of TiCr2, is the stable phase above 1300°C, while y1 with the cubic structure is stable below 1000°C. X-ray examination of a number of alloys annealed at intermediate temperatures showed that the hexagonal and cubic phases can coexist. Alloys quenched from 1000°C and annealed at 1100" and 1200°C showed small amounts of y2 at the higher temperature. A considerable amount of y, seemed present, however, in cast alloys annealed at 1100°C. It further appears that there is a small but definite solubility range for both phases in the ternary system. Acknowledgment The results of this paper represent work carried out in conjunction with a project sponsored by Watertown Arsenal, Contract No. DA-11-022-ORD-272. References 'M. K. McQuillan: Journal Inst. Metals (1951) 79, p. 379. 2 P. Duwez and J. L. Taylor: Trans. ASM (1952) 44, p. 495. W. J. Van Thyne,. H.. D. Kessler, and M. Hansen: Trans. ASM (1952) 44, p. 974. 1 F. B. Cuff, N. J. Grant, and C. F. Floe: Trans. AIME (1952) 194, p. 848; Journal of Metals (August 1952). Unpublished Research, Armour Research Foundation. "H. J. Wallbaum: Ztsch. Krist. 103, p. 391.

Jan 1, 1954

By N. J. Grant, B. C. Giessen, U. Wolff

With the aid of the splat-cooling technique of rapid quenching, metastable alloy phases based on antimony ad bismuth have been prepared. At room temperature, simple cubic phases were found in the Sb + Au, 56 + Yd, and Sb + Ni systems. Another phase was retained in the Au-Bi system at -190°C; in this systent, a microcrystalline phase and a rhombohedrally distorted phase were also observed. The crystal chemistry of these phases is discussed in terms of their valence electron concentration range. A remarkable five-step Phase sequence was found upon heating and equilibration of certain metastable Au-Bi alloys. USING the splat- cooling technique of rapid quenching from the liquid,' a large number of metastable intermediate alloy phases have been prepared in recent years. Thus, Hume-Rothery phases of the hexagonal type based on the valence electron concentration have been produced in systems where they are missing in equilibrium, e.g., Ag-Ge 1 or AU-Sb. 3 In a comprehensive study of metastable alloys based on tin, simple hexagonal metastable y phases were found, raising the total of stable and metastable y phases from 3 to 13. 4 In the In-Bi system, five new metastable intermediate phases were retained.' In most cases, the new metastable phases have some crystal chemical characteristics in common: a) They have rather simple, elementlike structures with few atoms per unit cell, e.g., y phase,4'5 or the metastable primitive cubic phases in the Ag-Te and and Au-Te systems.= b) Their structures are often related to those of the terminal phases, or to elements that are straddled in their position in the periodic table by the constituent elements; this is the case for metastable ß (In-Bi) with the structure of white ß Sn,' or metastable a (Cd-sn). 4 c) They seem to represent the crystal structures appropriate to certain average group number (AGN) ranges in which no or few single-phase structures exist in equilibrium. These average group number ranges can probably be equated in the case of many elements of the Ba(Zn)-Bs(As) groups with the averaged valence electron concentration. In the present work, the splat-cooling technique has been applied to the alloys of antimony and bismuth. In equilibrium, neither element forms intermediate alloy phases with other B elements from groups Bl(Cu) to B4(Si) that contain more than 66.7 at. pct of Sb or Bi, respectively, e.g., AUSb 2. 7 Thus, antimony- or bismuth-rich phases, which might be closely related to antimony or bismuth, and which would reflect struc- tural changes occurring on alloying with small amounts of addition elements, do not exist. Also, the terminal solubility of antimony and bismuth for all B metals is very small. It was therefore of interest to investigate the influence of enforced, nonequilibrium solid solution of addition elements in antimony and bismuth on their crystal structures. It was found that additions of group B 2-B4 metals act distinctly differently than additions of group T 10 and B1 metals. The latter set of additives will be treated here. EXPERIMENTAL TECHNIQUES Alloy preparation and splat-quenching followed closely the procedures described in Refs. 1, 4, and 5; they consisted of the preparation of master alloys from high-purity starting materials (99.99+ pct) and blast-atomizing of 20-mg quantities onto copper sheets. The resulting approximately 1 to 5 u thick foils were investigated by X-ray diffraction. The cooling rates obtained are of the order of 107 to 10 8 C per set,'" causing solidification to proceed at a rat; of approximately 100 cm per sec.' Powder patterns of the resulting fine-crystalline materials were taken with filtered CuK, radiation. For antimony alloys the substrates were held at room temperature and for bismuth alloys at -190°C both during splat foil deposition and X-ray investigation. Annealing treatments at several

Jan 1, 1969

By George C. Lipsey

FOR many years the mining of coal and other minerals occurring in sedimentary formation has been planned according to information obtained by diamond drilling. Placer mines have used churn drills for sampling and estimating deposits, and some metal mines have used the method either wholly or in part. The diamond drill method, therefore, although not entirely new, has come into more prominence in the last few years. Several large-scale developments now being planned or in the production stage have used this method in varying degree. This paper will describe the operations of the Howe Sound Exploration Co., Ltd. at Snow Lake, Manitoba, where a gold mine was developed and equipped for mining and milling wholly on the basis of diamond drilling results. The property has been in operation nearly 3 years, so that results can be compared with the estimates and assumptions made from the diamond drilling. In developing the subject it is necessary to outline as briefly as possible the normal method of mining, from discovery to production stage. Table I sets forth these various stages, the methods of financing, the percentage of total cost, and the relative time interval required for each section of the work. The plan presented in this table cannot be applied to all mining developments, but it gives a basis on which to work. In Stages 2 and 3 the investment is moderate, and if the property does not respond favorably the options or interests can be terminated. Stage 4 represents a sizeable investment, and it is more difficult to drop the property after this part of the operation is completed. Stages 2, 3, and 4 may be repeated several times by different groups or companies before Stage 5 is reached, but when Stage 5 has been started the total capital investment must be provided and there can be no turning back. It will be noted that there is a total of 116 units of investment in the overall cost if one company proceeds with Stages 2, 3, 4, and 5 in order. Stage 4, however, consumes time which is important when markets are being considered. Bringing a property into production when metal prices are low is much more difficult than when the prices are high, and if this stage can be set aside production is attained more quickly. When Stage 4 is eliminated the total becomes 86 units of cost for Stages 2, 3, and 5, but an adjustment of 14 units must be added to Stage 5. These 14 units represent the useable value of Stage 4. Thus Stage 4 represents an investment of 30 units if carried on before Stage 5, but 14 units if included with Stage 5. This is accounted for by the fact that development work can be accomplished more cheaply under Stage 5, since everything that is done is planned on a production basis with permanent services. Stage 4 must of necessity be governed by expenditures, and a great many temporary services, including housing and power plants, must be provided. The prospect shaft is a small one, and drifts,

Jan 1, 1952

By N. B. Davis

I. Introduction. II. Definition of Plasticity. III. Theories of Plasticity. A. Structure of the clay particles. (1) Fineness of grain. (2) Plate structure. (3) Interlocking particles. (4) Sponge structure of particles. B. Presence of hydrous aluminum silicates. C. Molecular attraction between particles. D. Presence of colloidal gelatinous matter. (1) Review of theory of colloids. (a) Suspension colloids. (b) Emulsion colloids. (2) Experiments. IV. The Formation of Clays. A. Residual clays. B. Transported clays. V. Summary. VI. Conclusion. I. IntRodUction While working with a number of very sticky cracking clays from western Canada the writer became interested in a study of the cause of the excessive plasticity. This led to a review of the rather bulky literature on the subject and the finding that plasticity still remains to be satisfactorily explained. Most of these investigations seem to have been carried on solely from the chemical viewpoint, the geologic aspects having been ignored. In nearly every case, the investigators have worked with the higher-grade clays of low to medium plasticity, such as the kaolins, the excessively plastic ones having generally been neglected, partly because of their limited application, yet the author believes that these are

Jan 1, 1915

By William R. Webster

I have continued the investigation of the Pottstown Iron Com pany's basic Bessemer keel plates on the line referred to in my paper of last October (Trans., xxi., 766)) and have added a study of the hardening effects of sulphur, which were not taken into account at that time. The results are so encouraging that I now give them in full. For some months we have graded all the steel at these works by the table given in my former paper, and checked the grading by the forging-tests as described in the paper of Mr. Joseph Hartshorne, read at the same meeting (Trans., xxi., 748). The steel thus graded was bloomed for the plate orders. Then one slab was rolled into a plate for the order, and a tension-test was made of this plate. By the result of this tension-test we were guided in rolling the balance of the heat. Out of several hundred heats graded in this manner, 95 per cent. met the requirements of the orders in every respect, and were accepted; but these results will no doubt be improved upon, when the influence of sulphur is also considered.. The hardening effect of sulphur seems to be about 500 pounds per each .01 per cent. of increase. In the table accompanying the pres ent paper, the ultimate strength with .06.5 per cent. sulphur agrees with the old table where sulphur was not considered; that is, for all steels with less than .065 per cent. sulphur we now get lower re sults, and for those with more sulphur, higher results. Making this allowance for sulphur, the assumed ultimate strength of a 3/8-inch plate of pure iron is reduced from 38,000 pounds per square inch to 34,750 pounds. With this as a basis, I have constructed my new table, giving each of the elements, carbon, phosphorus and manganese the same hardening effect as before, to wit : Carbon is credited with a constant effect of 800 pounds per each, 0.01 per cent. Phosphorus shows greater effect in high-carbon than in low-carbon steels. For 0.07 and 0.08 C, it has about the same effect as carbon, that is, 800 pounds for each .01 P. This increases to 1500 pounds per .01 P in 0.15 C steel, or nearly twice the effect of carbon. This

Jan 1, 1894

By C. C. Harris

The 3-parameter equation* was introduced1 as having the necessary form and flexibility for describing the major features of size distribution curves. Also, Eq. 1 was shown to contain most of the widely used 2-parameter equations as special cases. Special methods are necessary in order to determine the parameters of 3-parameter equations by graphical means. The procedure given previously required double graphical interpolation followed by regraphing the interpolated data. The theoretical basis of the method was a difference equation eliminating y. Several other methods for obtaining the parameters have been under development and one method appears to overcome the disadvantages of the earlier method and satisfies several procedural requirements. The points in favor of the new method as compared to the earlier method are as follows: 1. Estimation of the quality of fit is direct, and is in fact an essential part of the procedure. 2. The data is plotted directly without the necessity of interpolation from a graph. 3. The method makes use of Rosin-Rammler2 paper which because of expanded scaling in the coarse sizes leads to improved accuracy1 as compared with the log-log plot for the Gates3-Gaudin4-Schubann5 representation. 4. There is a gain over the earlier method in overall accuracy and in simplicity.

Jan 1, 1970

By H. E. Wheeler

THE work described was carried out during 1917 and 1918 at the testing laboratory of Watertown Arsenal at the instigation of the Nitrate Division and later with the concurrence of the Cannon Section of, the Ordnance Department, U. S. A. The experiments follow three principal lines of work: First, the effect of nitrogen under pressure on steel containers of various compositions at a red heat; second, the effect of decomposing ammonia on various alloy steels, iron, and non-ferrous alloys; third, a new theory of the erosion of guns in respect to the effect of nitrogen in steel. PART I In the Haber process for the manufacture of ammonia from its elements, it is necessary to have nitrogen and hydrogen of 1500 lb. per sq. in. (105.5 kg. per sq. cm.) at a temperature of 500 to 600° C. The steel containers for these gases gave trouble by failing without apparent cause. When the General Chemical Co. began to develop its method for the production of ammonia, it experienced the same difficulty and, knowing that the Haber process had solved the difficulty by the use of alloy steels, it made several small steel bottles of different compositions and kept them filled with these gases at this pressure and temperature until they failed. The time of service varied from a few days, for the plain steel casting, to two years for a chrome-vanadium forging. Four of these steel bottles were sent to this laboratory for investigation; they were a plain carbon-steel forging, a nickel-steel forging, a chrome-vanadium steel forging, and a chrome-steel forging. The time of service was as follows: plain carbon steel, 4 mo.; nickel steel, 6 mo.; chrome-vanadium steel, over 2 yr.; chrome steel, 4 mo. When these containers were cut open and the cross-section surface polished, they showed an inside zone with a different luster from the rest of the metal. Upon etching, this zone was almost unaffected while the rest of the steel etched normally.

Jan 4, 1920

Mining and Metallurgy of Lead and Zinc, AIME Vol. 121, edited by Dr. C. R. Hayward in 1936, remains a document of importance today even though 34 years have passed in the meantime. Since nothing in this world seems to be permanent, however, and progress brings new and better ways to do things, a two-volume set has just been published to bring the state of the art of 1936 up to date. This two-volume set, Mining and Concentrating of Lead and Zinc and Extractive Metallurgy of Lead and zinc, incorporates the papers to be presented during the Proceedings of the 1970 World Symposium on the Mining and Metallurgy of Lead and Zinc. The Symposium is being held October 20-24, 1970, in St. Louis, a site near to the famous Lead Belt of southeast Missouri. Some eighty papers are bound in these two volumes covering exploration, geology, mining, concentrating, roasting, smelting, electrolytic processing, residue fuming, refining, etc. All of this is laced with data on tonnages, processes, assays and efficiencies obtained, and the man-hours and equipment needed to achieve these performances.

Jan 1, 1970

By Philip B. Bucky

[ ] FOREWORD THIS symposium brings together points of view, experiences and ideas on rock bursts from a goodly portion of the globe. Some conceptions, particularly those regarding the necessity of depth, have been fairly well shattered, as we find that they are present in the water tunnels of New York, on the surface at marble quarries in Vermont, and in the coal mines of the United States, as well as in the deep mines of the South African and Kolar gold fields, and in the nickel, copper and gold mines of Canada. Their occurrence under such a variety of conditions is, therefore, a challenge,

Jan 1, 1942

By F. X. Tartaron

This article is a continuation of a previous paper by the writer in which Kick's Law was stated to be a part of comminution theory. ln the present paper, a broadening of ideas is attempted in order to state a general theory. The word "general" is employed because the new theory includes all previous laws and generalizations which are considered to be essentially correct. These ideas are combined into a coherent whole and the general theory can be expressed by the equation In the author's previous paper on comminution, ' the equations developed were based on Charles' equation of exponents a-n +1 = 0. 2 This paper is divided into two parts, designated as First Approach and Second Approach. In the First Approach, the equations of the previous paper are utilized, with Charles' equation of exponents being necessary. In the Second Approach, a separate and independent method is used to derive the same conclusions as in the First Approach, but without the use of Charles' equation of exponents. Holmes accepts the theoretical foundation of Kick's Law as sound but denies that the law as such operates in comminution. His idea is that Kick's Law requires homogenous matter whereas the presence of cracks, flaws and cleavage planes, which predominate in the coarser particles, makes matter unhomogene-ous. This explains why there is no experimental evidence to support Kick's Law. However, since the basis of the law is theoretically sound, all experimental evidence must be viewed as emanating from it. This requires modification of current comminution equations to fit this concept. Holmes makes the modification by changing the constant exponent n in the general energy equation used by Charles (E = - JCdx/xn) to a variable exponent r. The writer asserts that Kick's Law operates in comminution without modification but it does not

Jan 1, 1963

By W. P. Heineken, A. T. Child

This paper presents the results of a series of experiments made in the metallurgical laboratory of Columbia University, New Pork City. The object of the investigation was to determine, as far as possible, the changes in micro-structure and physical properties caused by short periods of heat-treatment and the longer malleable cast-iron process. It was proposed to do this by means of micro-photographs, heating- and cooling-curves, and tensile tests after the various heat-treatments. I. Micro-Constituents of Iron and Steel. The list of the micro-constituents of iron and steel has grown till now it includes seven different substances, called ferrite, cementite, pearlite,* martensite, austenite, sorbite and troosite. Only the first five of these are mentioned in this paper, to facilitate the understanding of which, the following brief definitions are given: 1. Ferrite (named by Prof. Howe) is, chemically, iron free from carbon. It is the softest of the constituents, and is not colored by etching, except when long-continued. Under the microscope it is easily determined by its regular polygonal etructure; or, if structureless, as in malleable cast-iron, by the ease with which it is scratched. Ferrite appears in mild steel in small amount, in grey cast-iron, and in malleable cast-iron. 2. Cementite (also named by Prof. Howe) is now generally conceded to have the formula Fe3C. It is the hardest of the micro-constituents, having the hardness indicated by 7 of the mineralogical scale; and hence it is always left in relief after

Jan 1, 1901

Aalde, Kaare. ('40) Gen'I Del., Bisbee. Ariz. Aase, Glenn D., ('40) Univ. of North Dakota. Grand Forks. N. D. Abadesco, Enrique A., ('39) College of Engrg.. Univ. of the Philippines. Manila, P. I. Abbott. John L., ('40) Colorado School of Mines. Golden. Colo. Abdul-Ahad, A., ('39) Montana School of Mines. Residence Hall, Butte. Mont. Abreu, Ovidio M., ('38) Univ. of Nevada, Reno, Nev. Acomb, Allen. ('41) Louisiana State Univ., Box 1970, University. La. Acosta S., Gonzalo. ('40) Univ. of Texas, Univ. Sta., Box 1785. Austin, Tex. Adam, Howard W., ('41) Montana School of Mines. Butte, Mont. Adams, Albert, ('381 New Mexico School of Mines, Socorro. N. M. Adams. Charles W., ('39) Michigan College of Min. & Tech., Houghton, Mich. Adams. H. Travis, ('39) 316 South -5th St., Bur¬bank. Calif. Adams, Jack L., ('39) Univ. of Oklahoma, Nor¬man. Okla. Adams. John W., ('41) Colorado School of Mines, Golden. Colo. Adams. Lewis J.. ('39) 402 Del Mar Blvd., Corpus Christi, Tex. Adams, Rob L., ('40) Agricultural & Mech. Col¬ lege of Texas. Box 600, College Sta., Tex. Adamson. Charles R., ('41) Univ. of Utah, Salt Lake City. Utah.

Jan 1, 1941

By Sylvain J. Pirson

The number of seismograph field crews employed in the active survey of potential oil territories is still on the increase, owing to the ever pending threat of a shortage in the supply of crude oil. It is to be expected that for years to come the seismograph will be responsible for discovering many new oil fields, both in wildcat territories and in deeper formations, and that the seismographic campaign will go on unabated. Yet improvements in instrumental design, in the field and interpretative techniques, are brought about year after year, and lead to the reshooting of areas many times surveyed previously. Notwithstanding the experience gained by the past eight years of active work in reflection seismographic surveys, the results given by this method of mapping deep formations have in many instances been at variance with the information subsequently obtained by the drill. To overcome this shortcoming, geophysicists have used closer spacing of the shot points and closer control of the depth points. The method discussed here is being used actively in the Mid-Continent region and endeavors to reduce the interpretation work to a mere mechanical technique, leaving as little as possible to the opinion of the interpreter. The New Method Field Technique.—In sectionized territory where country roads are available every mile, shot points are preferably located every 1/4 mile when six detectors are available or every % mile when eight detectors are at hand. The disposition of individual spreads is represented on Fig. I; in each case a shot point is located at the section corners. Fig. 2a represents the layout of a spread between shot points, the vibration detectors being preferably equidistantly located. Normally in the 1/4-mile control, the distance between shot points is 1320 ft. and the distance between detectors 220 ft. When shooting from shot point S.P. I, detectors 1 to 6 are connected to the recording galvanometers and detector 0 (which indicates the vertical travel time of the wave corre-

Jan 1, 1940

By Sylvain J. Pirson

The number of seismograph field crews employed in the active survey of potential oil territories is still on the increase, owing to the ever pending threat of a shortage in the supply of crude oil. It is to be expected that for years to come the seismograph will be responsible for discovering many new oil fields, both in wildcat territories and in deeper formations, and that the seismographic campaign will go on unabated. Yet improvements in instrumental design, in the field and interpretative techniques, are brought about year after year, and lead to the reshooting of areas many times surveyed previously. Notwithstanding the experience gained by the past eight years of active work in reflection seismographic surveys, the results given by this method of mapping deep formations have in many instances been at variance with the information subsequently obtained by the drill. To overcome this shortcoming, geophysicists have used closer spacing of the shot points and closer control of the depth points. The method discussed here is being used actively in the Mid-Continent region and endeavors to reduce the interpretation work to a mere mechanical technique, leaving as little as possible to the opinion of the interpreter. The New Method Field Technique.—In sectionized territory where country roads are available every mile, shot points are preferably located every 1/4 mile when six detectors are available or every % mile when eight detectors are at hand. The disposition of individual spreads is represented on Fig. I; in each case a shot point is located at the section corners. Fig. 2a represents the layout of a spread between shot points, the vibration detectors being preferably equidistantly located. Normally in the 1/4-mile control, the distance between shot points is 1320 ft. and the distance between detectors 220 ft. When shooting from shot point S.P. I, detectors 1 to 6 are connected to the recording galvanometers and detector 0 (which indicates the vertical travel time of the wave corre-

Jan 1, 1940

By Zay Jeffries

This paper will include a brief discussion of Prof. Howe's paper on The Supposed Reversal of Inheritance of Ferrite Grain Size from that of Austenite.l The general subject of grain refining in steel and iron will also be treated. The conclusions reached are stated in the following hypotheses which are discussed more in detail below. 1. The ferrite grain size in pure iron, the ferrite and pearlite grain size in hypoeutectoid steel, the pearlite grain size in eutectoid steel and the cementite and pearlite grain size of hypereutectoid steel are not inherited from the grain size of the mother austenite. 2. The only structural feature that is generally inherited from the austenite of hypo- and hypereutectoid steels on cooling through their transformation ranges is the position of the excess ferrite or cementite at the austenite grain boundaries, sometimes causing complete and sometimes incomplete networks which outline the old austenite grain boundaries. Rapid cooling through the transformation range will cause the non-inheritance of this structural (network) feature. 3. The austenite grain boundaries themselves are nearly always effaced in all steels and also in pure iron during the At transformations. 4. The grain-size refining of steel and iron is brought about by the combined effect of non-inheritance of the transformation products on either heating or cooling, i.e., the austenite transformation products do cst inherit their grain size from the austenite on cooling through the transformation range nor does austenite inherit its grain size from the products which form austenite on heating. 5. In general, in both iron and carbon steel the larger the austenite grain size, the larger will be the grain size of the transformation products on cooling. This, of course, assumes all other conditions constant except the austenite grain size. An exception is found to this general rule in very pure iron such as electrolytic iron. In this instance small austenite grains may form very large ferrite grains on cooling through Arg.

Jan 1, 1918

By George Rice

THE A.I.M.E. Ground Movement and Subsidence Committee, pro-posed in 1920, held its first technical meeting in February 1923, under the able chairmanship of Mr. H. G. Moulton. The following list of papers and discussions, indicating the scope of the problems and relation to various conditions and method of mining, were given at that meeting by the distinguished mining engineers: J. Parke Channing, on Subsidence at Miami, Arizona; Howard N. Eavenson, on Mining an Upper Bitu-minous Seam after a Lower Seam Has Been Extracted; J. J. Rutledge, on Subsidence in Two Oklahoma Coal Mines; Benjamin F. Tillson, on Caving Cracks at the Franklin Mine, New Jersey; Dr. F. W. McNair, on the Dome Theory; William Kelly, on disadvantageous effects in Mining and Back-filling Working Upward a Steep-Pitching Iron-ore Bed; Eli T. Conner, on the good results of Back-Filling by Hydraulic Means in Preventing Destructive Subsidence in the Anthracite District; Thomas H. Claggett, on the merit of Systematic Pillar Drawing in Preventing Cracks in an Upper Seam; Henry H. Otto, successful results in the anthracite district in Mining Lower Seams before Upper Seams; Douglas Bunting, on Leading Factors Incident to Successful Mining of an Overlying Seam; Edwin Ludlow, on there being "less damage to buildings when there was complete removal of coal with complete packing than when room and pillar is used without extracting the pillars"; Edward O'Toole on "bumps" in eastern Kentucky mines, which he thought were the result of geologic stresses: H. A. Buehler, on Upheaval of Surface in an Illinois Case in Advance of the Face; and R. Dawson Hall, on The Mechanics of Subsidence from Mining. The author of this paper discussed various kinds of problems of ground movement and subsidence in both metal mining and coal mining; the production of great landslides by workings near an outcrop, as at Turtle Mountain, Alberta, Canada; and general

Jan 1, 1939

By Norman Goss

IT is generally agreed that cold-working mechanically refines the grains into smaller fragments and with continued working these are oriented with certain crystallographic directions bearing a relation to the direction in which the metal is worked. Some of the energy expended on the metal during plastic deformation appears in the form of heat, but a very small portion remains in the metal as stored energy. The entropy, specific heat capacity, temperature at which recrystallization will just begin, density, ductility, elasticity, tensile strength, and resistance to corrosion are affected. These properties have been studied extensively and some of the changes in the physical properties due to cold-working were attributed to lattice distortion.1-8 The broadening of the K. lines on the X-ray diffraction diagrams of plastically deformed metals is believed to indicate lattice distortion, and consequently the existence of internal stresses. The evidence supporting this theory rests solely upon the observed experimental fact that the dif-fraction lines are broadened and the K a doublets are completely diffused. Elam9 has reviewed the matter of lattice distortion in relationship to the hardening of metals by plastic deformation. The X-ray diagrams of plastically deformed metals differ in general from annealed metals. The hardening of a metal was believed due to lattice distortion.9 The resolu-tion of the doublet is lost when a metal is cold-worked and the Lane spots are elongated. At one time this elongation was thought to indicate the elastic bending of the crystal planes. However, more careful work showed that the asterism was due to new orientations developed within the fragmented grains during plastic deformation. Some theories attrib-uted the hardening to fragmentation of the grains into smaller units.

Jan 1, 1940

By A. Matsubara

Jan 1, 1922

By A. Matsubara

Jan 1, 1922

By Royal Jackman

Two comprehensive papers have appeared regarding the forms of copper that occur in smelter slags, one by Frank E. Lathe1 and the other by C. G. Maier and G. D. Van Arsdale.2 These authors comment on other published results and draw conclusions from their own investiga-tions. The development of X-ray examination of minerals and improve-ment in high-power microscopic methods make it possible today to get additional evidence by means that were not available to earlier investi-gators. The present work was confined to reverberatory slags obtained from five different plants. Some definite conclusions were reached regarding the forms of copper present in these slags. In most cases these agree with some of the findings of Maier and Van Arsdale but new methods of attack were used in the investigation.

Jan 1, 1933