By H. J. Ramey

Conventional calculation of total system isothermal compressibility for a system containing a free gas phase involves, among other things, evaluation of the change of oil and gas formation volume factors and the gas in solution with pressure. Preferably, this information should be obtained from laboratory measurements made with particular oils and gases. Often, experimental measurements are not available. In this case, it is necessary to obtain pressure-volume-temperature relationships from general correlations such as those of Standing' for California oils. In order to speed estimates of compressibility, generalized plots have been prepared of the change of both oil formation volume factors and gas in solution, with pressure from Standing's correlations. A generalized plot for estimating the change in the two-phase (oil and gas) formation volume factor with pressure is also presented. Usually, the effect of gas dissolved in reservoir water upon the total system compressibility is neglected for gas saturated systems, due to the low solubility of gas in water. Results of this study indicate that the increase in total system compressibility caused by solution of gas in water is often as large as the compressibility of wafer, and can be magnitudes larger for low pressure systems. Generalized results for estimating the change of gas in solution in water with pressure are presented in tabular and graphical form. INTRODUCTION During the past decade, pressure build-up and drawdown techniques have gained an important place in reservoir engineering. Build-up and drawdown analyses are only two special applications of the broad field of transient fluid-flow theory. All solutions of transient fluid-flow problems contain a parameter called the total system isothermal compressibility. This property of fluids and porous rock is a measure of the change in volume of the fluid content of porous rock with a change in pressure, and it may vary considerably with pressure. Evaluation of total system isothermal compressibility is not difficult, but it is tedious and time-consuming. Often compressibilities are estimated roughly, or transient flow methods are neglected completely. The benefits of using accurate system compressibility in properly-executed build-up or drawdown analyses are: 1. Better planning of pressure build-ups may be achieved to avoid unnecessary loss of revenue due to excessively long shut-in periods, or to shut-in periods too short to yield useable data. 2. Better and more reliable estimates of static formation pressures for reserves estimates and rate performance estimates. 3. Reliable information for evaluation of well completion effectiveness, and planning and interpretation of well stimulation efforts. The purpose of this paper is to clarify the nature of the total system isothermal compressibility, and to present useful methods for estimation of compressibility, particularly for systems containing a gas phase. DEVELOPMENT Numerous publications have presented solutions to transient single-phase flow of slightly compressible fluids, stressing pressure build-up applications. In transient flow, a compressibility* term arises to permit volume content of fluids in porous rock to change as pressure changes. The basic nature of the compressibility term is usually taken for granted. Problems arise in practical applications of transient fluid theory because most published works consider only one flowing fluid—in an ideal porous system containing only one fluid. In 1956, Perrine2 presented an intuitive extension of single-phase flow pressure build-up methods to multiphase flow conditions. Later, Martin- established conditions under which Perrine's multiphase build-up method had a theoretical foundation. Perrine has shown that improper use of single-phase build-up analysis in certain multiphase flow situations can lead to gross errors in estimated static formation pressure, permeability and well condition. It is likely that, much pressure build-up data for oil wells should be analyzed on the basis of multiphase flow. For both single-phase and multiphase build-up analysis, the isothermal compressibility term in dimensionless time groups often should be interpreted as the total system compressibility. All real reservoirs contain one or more compressible fluid phases. In addition, rock compressibility can contribute in an important way to the total system compressibility. The proper total system compressibility expression may contain terms for compressibility of oil, gas, water, reservoir rock and terms for the change of solubility of gas in liquid phases.

Jan 1, 1965

By E. D. Levine

A study was made to delineate the dislocation mechanistns controlling prismatic and basal slip at low temperatu.ves in titanium containing approximately 100 ppm interstitial impurities. Mechanical tests were performed on single crystals prepared from electron-beam zone-refined crystal bar by a thermal cycling technique. Measurements were made of critical shear stress and activation volume as functions of temperature. The study revealed that, for prismatic slip, two overlapping thermally activated processes aye rate-controlling below 300°K. From absolute zero to 220°K, reasonable agreement is obtained between experiment and the mechanism which involves overcoming 01. the Peierl's stress by the formation of double kinks in dislocation lines lying in close-packed directions. Between 220°and 300°K prismatic slip is controlled by a difierent thermally activated process which is characterized by a stronger temperature dependence of critical shear stress. Above 300OK, prismatic slip is controlled by an athermal process. Basal slip is controlled by a thermally activated process between 195' and 400°K. An approximate analysis suggests that it is the Peierl's mechanism that is rate-controlling in this range. Below 195°K, the occurrence of mechanical twinning obscures the features of basal slip. Above '400 X, basal slip is controlled by an athermal process. TITANIUM, an hcp metal with a less-than-ideal axial ratio of 1.587, deforms primarily by {1010}( 1210) slip at low temperatures.'-3 The critical shear stress is strongly affected by the presence of interstitial impurities. For example, churchman3 reported that a decrease in the combined nitrogen plus oxygen content from 0.1 to 0.01 pct decreased the critical shear stress for prismatic slip from 9.19 to 1.4 kg per sq mm at room temperature. Basal slip, however, is less strongly affected by interstitials; Churchman's data for {0001}( 1210) slip show a smaller decrease in critical shear stress from 10.90 to 6.3 kg per sq mm at room temperature, for the same decrease in interstitial content. In the present study, an attempt has been made to delineate the dislocation mechanisms controlling prismatic and basal slip in titanium. In view of the strong effects that impurities may have on at least some of these mechanisms, experiments were performed on material of reasonably high purity, so that comparisons could be made with investigations on material of both lower and higher impurity contents. EXPERIMENTAL PROCEDURE Single crystals were prepared from 1/4-in.-diam electron-beam zone-refined crystal bar, furnished by Materials Research Corp. The analysis of the zone-refined material is given in Table I, indicating that the interstitial content is of the same order as the purer of the two materials investigated by Churchman. The Vickers diamond pyramid hardness number of this material was 85.6. This value agrees quite well with the correlation between hardness and interstitial content proposed by Ogden and Jaffee.4 On the basis of hardness, the material investigated in this study is, therefore, intermediate in purity between that studied by Churchman (Vpn = 97) and that studied by Spangler and Herman (Vpn = 62.4).5 Single crystals were grown by thermal cycling through the a-ß transformation. Two-in.-long by 1/2-in.-diam bars were heat-treated in vacuum for 4 hr at 1160°C. The temperature of the furnace was then lowered to 865°C, and the specimens were maintained at this temperature for 7 days. This procedure was repeated several times, resulting in the growth of individual crystals up to 14 in. in length. Specimens for testing in direct shear along either {l010}(1210) or {0001}(1210) were obtained by electrical-discharge machining. The specimens were in the form of cylinders 1/4 in. in diam by approximately 1/2 in. in length, with a reduced section 1/8 in. in diam and a in. in length. All specimens were electropol-ished subsequent to electrical-discharge machining. The ends of the test specimens were cemented in stainless-steel collars. Shear tests were conducted in an Instron Tensile Tester at various temperatures from 4.2° to 508°K. Measurements were made of critical shear stress and activation volume. The latter measurements were performed by measuring the change in flow stress upon cycling the strain rate between ?1 = 2.62 x 10-3 per sec and ?2 = 2.62 x 10-4 per sec. Activation volume, I)*, is defined as u* =ßkT [11

Jan 1, 1967

By G. P. Connell, R. E. Gilmore, J. H. H. Nicolls

The purpose of this paper is to suggest a procedure for indicating the dividing line between noncaking coals and those that have weakly caking properties. A laboratory agglomerating test as an aid in classifying weakly caking coals is outlined and its merits in comparison with the standard agglutinating method advanced by the U. S. Bureau of Mines are discussed. No attempt, however, is made to discuss in detail either the different methods for determining "caking" and "agglutinating" indices or the various systems of classification. Two methods, differing somewhat in procedure, have been employed and recognized as suitable for determining the caking or agglutinating values of coals; namely, those in which an inert material such as sand, electrode carbon, etc., has been mixed with the coal before being heated, and those in which the coal is carbonized alone. In all such methods, the coal with or without the inert material is in the finely divided state and the index or value sought is derived from the examination of the residue after heating in a closed crucible or other container. The procedure outlined by Selvig, Beattie and Clellandl is the most recent representative of the method using sand as inert material, while the agglomerating test described below is representative of the method in which the coal is carbonized alone. The standard volatile-matter determination affords a means for observing the coking properties of a coal, and this has been described by Rose2 as the simplest of all coking tests. According to him, "the resulting coke button will indicate whether the coal is noncoking, feebly coking or strongly coking," despite the fact that "almost every condition in this test is at variance with large-scale carbonizing practice." Lessing,3 the

Jan 1, 1934

By J. McLaren Forbes

Geologists and engineers in charge of diamond drilling often have no practical experience in the work, yet they must direct the drillers. In discussing some of the problems that arise, the author of this paper has tried to remember the things he did not know about diamond drilling when he first came in contact with that work. The basic reason for most diamond-drill holes is to obtain information. The more thorough the understanding of the geological and engineering problems involved, the greater will be the benefit derived from a drilling program. One of the best methods to ensure some thinking before drilling is to record on the permanent drill log, before the hole is collared, the reasons for the work and the information desired from that particular hole. When the hole is finished, the information obtained should be recorded. Driller The choice of a diamond driller is very important. If no experienced driller is available, a competent miner who has a sense of responsibility and better than average mechanical ingenuity can do the work. The best answer to most practical drilling problems, from the standpoint of the person in charge of the drilling program, is the service of experienced diamond drillers or drilling firms. Equipment Drilling equipment should be adequate to put down the longest hole desired and handle the toughest ground encountered. The type of bit used depends upon the ground drilled. Experimenting with various bits and careful study of footage records are the best means of determining which to use. Under ordinary circumstances it is best to drill using an EX barrel when possible. The length of rod and core barrels that can be used depends on the size of the drill station. Also, the length of core barrel depends on the way the ground cores. In good ground as much core will be recovered with a 10-ft. barrel as with a shorter one, and with considerable saving of drilling time. A water pump is needed if the hole is so deep that the water pressure is not strong enough to wash out the cuttings, or if it is drilled at an angle that prevents full force of the water pressure. Instructions For an Inexperienced Driller 1. Never run a bit too long a time. When a bit seems to be "good for one more run," discard it. 2. Always let the rods down on bottom easily. Protect the bit from sudden shock. 3. Start the drilling slowly and easily. Do not put pressure on the bit too fast. Diamonds can break. 4. Be sure the water pressure is strong enough to clear the bit, but do not use more water than is needed, as it may wash away the core. Usually, if no core is recovered the hole is a total loss. 5. When dry-blocking, do not run without water longer than necessary as the bit may burn. 6. Be sure the rods are well caulked and tightly screwed together. If not well caulked they will lose water, and if not

Jan 1, 1946

By H. Kreye, E. Hornbogen

An increase in electrical resistivity during aging or after quenching from high temperatures is known in a large number of alloys. Plastic deformation of alloys in this condition leads to a decrease in resistivity. This anomaly has been called the K effect. This effect has been reported in Ni-A1 alloys by several authors.'-4 The nickel-rich solid solution y is in equilibrium with Ni,A1 (y') with CkAu structure. With this alloy it is therefore possible to produce a homogeneous solid solution as well as a coherent mixture of y and y. The changes in resistivity should be determined for these two conditions. In the present literature on the K effect no distinction is made between them, because of experimental difficulties to determine small coherent particles. In the present work transmission electron microscopy and image formation by (100) and (110) superlattice reflection of the y' phase was employed for a detailed determination of the temperature dependence of solubility of aluminum in nickel and the resulting microstructures with alloys up to 15 at. pct Al. The solubility line follows the equation indicating a smaller solubility than given in the literature at temperatures below 700°C. X-ray scattering was used to get evidence for short-range ordering in the homogeneous solid solutions.5 Parallel to the determination of the microstructure electrical resistivity was measured as a function of aging tempera- ture, time, and aluminum content, which led to the following results: 1) Resistivity increases slightly during aging of a homogeneous solid solution which was quenched from a high temperature as a consequence of short-range order, Fig. 1, curve c,. 2) Resistivity shows a maximum during aging of all alloys which are heterogeneous according to the phase diagram, but which were obtained as a supersaturated solid solution by quenching, Fig. 1, curve c,. The increase in resistivity is mainly due to coherent precipitation of y'. In Fig. 2 the effects due to short-range order pN and due to precipitation of particles APT are shown for an aging temperature of 450°C and different aluminum contents. 3) The increase in resistivity depends on the size !f the coherent particles. A critical diameter of 15 5A for the maximum was found for all alloys and aging treatments by extrapolating particle sizes determined by electron microscopy. 4) The maximum of resistivity of the heterogeneous conditions does not occur if particles, larger than the critical size, have formed already during quenching. 5) Plastic deformation destroys short-range order as well as small coherent particles. Therefore a decrease in resistivity is observed if the increase in resistivity caused originally by these phenomena is

Jan 1, 1967

By H. N. Eavenson

Prior to 1907 nearly all coke was made in beehive ovens, and most of the gas produced was made in the old-style gas retorts, and while there were a few coke plants in southern West Virginia, southwest Virginia and Kentucky operating on high-volatile coals the proportion of the total product made by them was small and usually was used locally. The greater part of the coke made, and the coal gas produced, came from the Pittsburgh seam of western Pennsylvania and northern West Virginia, which was then regarded as the standard coking and gas coal of the country, and the best coal available anywhere for these purposes. With the advent of the byproduct oven and the building of coke plants at the furnaces, the restriction of the use of one grade of coal for making coke was removed and the use of mixtures of low-volatile and high-volatile coals began. The change in the locations of the coke plants removed the necessity of using Connellsville coal and also made sources of gas available to the public utilities other than of their own manufacture. Most of the first oven plants were built at points distant from the Connellsville region and this afforded an opportunity for the use of coals from the southern Appalachian fields, which were then at approximately equal distances from the ovens. Since that time development has been made on a number of seams of coal of great purity in southern West Virginia, southwestern Virginia and eastern Kentucky, which have been largely used for gas, cokemaking and metallurgical purposes where low amounts of ash, sulfur and phosphorus are determining factors. These coals are much lower in the objectionable elements than most of the coal shipped from the Pittsburgh seam, or than any northern coal, and when blended with low-volntile cod produce coke in byproduct ovens that is not excelled for any purpose by any coal mined in this country, and is equaled very seldom. Coal from several of these scams is shipped in great quantities without beneficlation and is lower in ash and sulfur than any but the best washed product from the Pittsburgh seam in the north. The writer has made a study of these coals to ascertain their relative qualities and the areas and reserves of coal available in each of them. No attention has been paid to the coals of Alabama, which do not compete with any of these coals, and no coal of equivalent quality is found in

Jan 1, 1934

By F. R. Wadleigh

There are in commercial use today in the United States various classifications of coal, each based on one or more characteristics. The bases of these classifications may be described as follows: GeNeRaL Basis Examples 1. Geological By seams and basins (local). 2. Chemical By constituents, as determined by analysis—ash, volatilc, slilfur and hcating value. 3. Combustion Characteristics As frce-burning, smokeless, character of ash. 4. Carbonization Characteristics Coking, noncoking. 5. Physical Characteristics Splint, soft, hard, block. 6. Geographical States, Fields, Counties, Districts. 7. Sizes By dimension or name. 8. Company Names Producing or sales company names, as "C. C. B. Pocahontas," etc. 9. Trade Names, copyrighted or not 10. Uses Gas, steam, coking, locomotive, fuel, bunkers, etc. 11. Use Methods Stoker coal. 12. Pools (Tidewater Exchanges) Analyses Size Seams Railroads Uses Structure Districts There are also classifications founded on more than one basis, as follows: 1. Geographical and Geological. By locality of mines (State, District, County) and seam. Examples: Cambria County, Miller Seam, New River, Sewell Seam. 2. Geographical and Chemical. Alabama medium volatile. 3. Combustion Characteristics and Ash Content. Free-burning, red ash (anthra- cite). 4. Carbonization Characteristics and Analysis. Noncoking, high-volatile, low sulfur. 5. Physical and Carbonization Characteristics. Splint, noncoking. 6. Size and Use. ¾-in. gas coal; domestic sizes (prepared sizcs); stcam sizcs. 7. Company Name and Seam. Consolidation Co., Elkhorn. 8. Size and Analysis. Low-volatile run-of-mine; low-volatilc slack. 9. Sizes—size of screen and name. 6 by sin. lump. 10. Chemical and USP. High-volatile steam. 11. Geographical and Use. Youghiogheny gas. 12. District, Size and Use. Pittsburgh gas l¼-in. lump. ,

Jan 1, 1930

By B. Russell, J. R. Tuffley

The stability regions of the normal sulfate and the various basic sulfates of lead in 02-SO2 and PhS-SO2 gas atmospheres were calculated from available thermodynamic data over the temperature range 600o to 1200oC. Roasting experiments were carried out on samples of synthetic lead sulfide at various temperatures and for various roasting times. Compounds in the oxidized surface layers were identified by X-my techniques. The order in which the various reactions occurred was determined by considering the experimental results in conjunction with the thermodynamic calculations. The results of these investigations were applied to the sintering of lead sulfide concentrates, and the extent to which each of the various reactions occurred in a sinter bed was determined. PRODUCTS which may be formed during the roasting of PbS are PbS04, PbSO4. PbO, PbSO4 . 2PbO, PbSO4 . 4PbO, PbO, and Pb.1, 2 The formation of some sulfates has been studied by a number of investigators3-' whose experiments have mostly been confined to the temperature range between 500" and 850°C. Culver, Gray, and spooner3 were able to isolate the reactions which formed PbSO4 and PbSO4. PbO by carefully controlling the compositions of the roasting gases. The kinetics of these reactions were studied within the temperature range 673" to 807°C. Gardner4 and Merrick5 also studied the kinetics of oxidation of PbS. Gardner disregarded the existence of basic sulfates and, as a result, misinterpreted some of his experimental data. Merrick recognized that most of the products of oxidation were mixtures of basic sulfates, but was unable to identify the individual components. Hoschek6 oxidized PbS in air at temperatures up to 800°C. The products were analyzed after roasting had proceeded for some minutes, but no attempt was made to follow the reactions in the initial stages. Consequently, no roasting mechanism was derived. He also showed that PbSO4 and PbSO4 - 4PbO decomposed slowly in air at temperatures in the region of 800°C. The stability regions of sulfates in the temperature range 500" to 850°C have been only partially determined, while practically no information is available for higher temperatures. In the lead sintering process, PbS concentrates are roasted at temperatures within the range 1000o to 1200°C. In order to investigate sulfate formation, it is necessary to determine the effects of temperature and gas composition upon the various oxidation reactions and upon the regions of stability of the various lead sulfates. Kellogg and Basu2 introduced an equilibrium diagram similar to those in Figs. 1 to 3 which provides a convenient medium for represent-

Jan 1, 1964

By Edward D. Thimons, Richard J. Kline

Converting the energy of falling water into useful work is a well developed engineering concept. Much of the electric power consumed in the United States is generated in this manner. It is easy to conceive that the water which flows down long vertical pipelines into deep nines could be utilized in a similar manner by allowing it to operate a turbine at the bottom of the pipelines. The mines in the United States are continually descending to greater depths in search of mineable deposits. Large quantities of water are carried down long vertical pipelines in order to be used for dust suppression, motor cooling, and refrigeration. Pumping the used water back to the surface is also required. The electrical costs associated with mining are also constantly escalating due to both increased demand and rising kilowatt hour costs. To help deal with this problem, the United States Bureau of Mines (USBM) has awarded a contract to Foster-Miller, Inc. of Waltham, MA, to investigate, evaluate, and demonstrate commercially available means of energy recovery for the deep mining industry. In other words, it demonstrates an efficient system for converting the energy of water flowing down vertical pipelines into useful mechanical or electrical energy.

Jan 1, 1982

By E. G. Bailey

PLANTS that normally burn coal now able too obtain a substantial increase over their normal supply for their greater power needs, and also additional tonnage for extra storage against the uncertainties of the future. Many plants previously burning oil or gas have already been converted to coal, and those which must yet change to coal will undoubtedly be able to obtain ample tonnage of coal of standard quality at reasonable prices. What a contrast this is to the conditions of 25 years ago, when the shortage of coal and transportation led to prices of $5 to $6 per ton at the mines, and degradation of quality, until the already overburdened railroads were called upon to haul 100,000 ton per day of extra ash alone. This was the result of a runaway market and the loading of gob, slate, and sub-quality coal amounting to an estimated increase in ash of 5 per cent of the total tonnage hauled. The problem of getting increased steam output from inferior coal caused unbelievable reductions in the low normal boiler efficiency of that time and untold labor in firing the hand- and stoker-fed furnaces of that day.

Jan 1, 1942

By H. L. Couch, J. D. Lubahn

In decarburized mild steel, the strain hardening arising from 1/2 pct strain can he partly recovered by subsequent heating, even though re crystallization or grain growth does not occur. This recovery varies from 5 pct in an hour at room temperature to 70 pct at 800°C. The variation with temperature was qualitatively similar to that reported for copper, but occurred at lower temperatures. Except for the initial portion (Bazdschinger effect), the stress-strain curve following recovery can be superimposed on the original curve by shifting it to the left. In other words, the tensile behavior is essentially the same after straining and heating as if there had been less strain and no heating. The importance of this observation in understanding simultaneous deformation and recouery is explained. AN earlier investigation1 on copper showed that strengthening due to strain hardening was augmented by heating at moderate temperatures, but was diminished by heating at higher temperatures, Fig. 1. Auxiliary experiments1 indicated that recovery and strain aging are independent processes, which may proceed simultaneously, and whose effects are additive as indicated in Fig. 1. In order to study recovery by itself, similar tests were made on decarburized mild steel, where strain-aging effects are known2 to be absent. MATERIAL, TESTING PROCEDURE The specimens were made from rimmed, hot-rolled SAE 1020 steel 0.040 in. thick, by stamping out rectangular blanks and end holes, Fig. 2, and pack milling the reduced section. These were wet-hydrogen treated2 for 16 hr at 720°C to remove carbon and nitrogen completely and then heated 1 hr at 850°C in vacuum to stabilize the grain size. Auxiliary ex- periments showed that heating up to 800°C will not cause grain growth. They were prestrained 5 to 7.5 mils per in. using the special grips shown in Fig. 2. Such small strains are less than the "critical" strain for recrystallization and, therefore, will not cause recrystallization, even at high temperature. The recovery treatment after prestraining and before the retesting consisted of heating for 1 hr in wet hydrogen at the desired temperature. In one test, Huggenberger gages were used to define more accurately the loading and unloading curves. Fig. 3 illustrates the creep during the early stages of unloading, the hysteresis due to cold stretching, and removal of hysteresis by heating.3 RESULTS The load-deflection curves had ratner widely differing shapes for different specimens, both before and after the recovery treatment. Some specimens showed perfectly smooth curves, Fig. 4, while others exhibited an inflection more or less suggestive of a yield point (Fig. 4 shows all extreme case). Some curves were much steeper than others; Fig. 5 shows two extremes. Some additional ex-

Jan 1, 1960

By C. Ernest Birchenall, Robert F. Mehl

APPLICATION of diffusion laws in the customary form to experimental studies in binary metallic solid solutions has shown the diffusion coefficient to vary with concentration for all systems investigated. The factors determining this variation have not been ascertained. However, the question of whether the diffusion coefficient would become a constant, independent of concentration throughout a single phase if the concentration gradient in the diffusion equation were replaced by an activity gradient has been an attractive subject for speculation. Wagner1 derived an expression for the force acting on a diffusing particle in terms of the chemical potential. This was also the approach chosen by Jost2 in his monograph. From a somewhat different point of view, Eyring3 and his co-workers have used activity gradients when dealing with diffusion in concentrated nonideal solutions. The only actual test with experimental data is that given by Darken,4 though this is more qualitative than quantitative. Many others opposed the application in any way of thermodynamic concepts to kinetic phenomena, including diffusion processes. A rigorous examination of this principle requires good data expressing the relationship between activity and concentration for solid solutions for which reliable diffusion work has been done. The literature provides such information only for the interstitial solution of carbon in gamma iron (austenite) and for the substitutional copper-zinc solutions (alpha brass). Activity data for carbon in austenite at 800°C and 1000°C are available from the recent work of Smiths on the equilibrium of hydrogen-methane and carbon monoxide-carbon dioxide mixtures with gamma iron. Combining these with the diffusion studies of Wells and Mehl6 makes possible a quantitative test for this interstitial solid solution. The vapor-pressure determinations for zinc over brass by Hargreaves7 allowed the calculation of activities in this system over a wide range of temperatures and concentrations. Extensive investigation of diffusion in this substitutional solid solution has been carried out by Rhines and Mehl.8 ACTIVITIES IN BRASS9 If the vapor phase of zinc is assumed to behave as an ideal gas, any solid or liquid solutions that are in equilibrium with the same partial pressure of zinc at the same temperature have the same thermodynamic activity of zinc. In order to assign a numerical value to the activity azn, it is necessary to choose some standard reference state to which an activity value of unity is arbitrarily assigned. It is customary to choose the liquid or solid state of the pure material. Then azn is defined numerically by azn = Pza/Pzn° [I]

Jan 1, 1947

By C. M. Brown

Selection criteria for the instrumentation employed in semi-autogenous grinding circuits are reviewed. Instruments in use for grinding mill and related process equipment start- up, shutdown, protection, monitoring, control, and performance reporting functions are discussed with examples given of current industry practice. The quantity and type of instrumentation used vary from operation to operation, but today many semi- autogenous circuits are highly instrumentated, and employ automatic process control for both circuit stabilization and optimization of economic performance. Examples of analog and digital based control systems exist, and are described.

Jan 1, 1982

By Fred C. Bond

THEM is acute need for a method that will measure the size distribution of finely divided materials, particularly when the particle sizes are smaller than the openings of the finest screen cloth regularly available for testing. Several methods and types of apparatus are in common use, but none are entirely satisfactory for all purposes. The commonest methods are microscopic grain counts, elutriation by liquids or air, and sedimentation. Valuable results have been secured by air elutriating devices, typified by the Haultain Infra-Sizer and the Pearson Air Analyzer. These are especially useful in obtaining sized fractions that can be examined and analyzed separately. They are particularly advantageous because the sizes of the samples produced are adequate for a considerable amount of subsequent manipulation and testing. The sedimentation methods, such as the Wagner and Klein turbidimeters, and the sedimentation balance, do not deliver sized fractions, but they do provide a means for reasonably rapid comparative determinations of fineness and surface area, which are important in many industries. The sedimentation balance consists essentially of a balance pan suspended in a liquid that contains falling particles. These are weighed as they settle onto the pan, and the time rate of settling is determined. The size distribution is computed from the settling rate. The balance appears to be inherently more accurate than any of the other methods, and it has served a useful purpose in the study of numerous problems, but there have been limitations which have restricted its scope of application. Because of the essential simplicity of the method, it was felt that intensive investigation might lead to modifications that would make it a valuable tool for the operators in industries that require precise information regarding the results secured from grinding equipment. A large number of size-distribution determinations below 200 mesh were required in connection with a particular research problem in fine grinding. The sedimentation balance was used in this investigation, and a technique was gradually developed that ultimately gave good results. A serious difficulty appeared early in the work. It was discovered that less material always settled on the sedimentation pan and more on the bottom of the containing jar than could be accounted for by calculation, and also that the material that settled to the bottom of the jar outside the edges of the pan was considerably finer than that on the pan. This segregation was so great that the distribution obtained for the finer sizes was obviously very much in error; material ground to about the degree of comminution of cement might have only 60 per cent of the calculated weight actually settling on the pan, and the error increased with the fine-

Jan 1, 1939

By Lewis Reeve

As part of a program of investigation of the properties of electric arc welds carried out in the laboratories of the A. 0. Smith Corporation, considerable work has been done on the determination of the oxygen, nitrogen and hydrogen content of different types of weld metal, employing for this purpose the so-called "vacuum fusion method." It is the purpose of this paper to describe certain improvements that have been introduced in this method of determining the gas content of metals, with particular references to the steel specimens examined in this investigation. The method and apparatus used at the beginning of the investigation were essentially those of the Bureau of Standards as described by Vacher and Jordan.' Later a number of changes were introduced which resulted in more rapid evacuation of the graphite crucibles employed and which enabled larger volumes of gas to be dealt with than could be handled conveniently in the Bureau of Standards equipment. In addition, the analyzing of the gases evolved from a melt in the same apparatus as collected was abandoned in favor of analysis outside the equipment using standard methods of gas analysis. The time required for gas analysis in the apparatus itself, as described by the Bureau of Standards, was found to be considerable, and during this time the rest of the equipment was tied up, preventing its use for the analysis of further steel samples. As a result of the modifications introduced, the time required for the analysis of a steel sample for gas content was reduced from about 8 hours to less than 3 hours. Subsequently, the whole procedure of melting the sample and collecting the gases evolved was modified so as to enable a distinction to be drawn between the easily reducible oxides such as iron oxide and the more stable oxides such as silica and alumina. At the same time evidence was obtained indicating the probable existence in the steels of other nitrides than those of iron alone and making possible their quantitative etermination.

Jan 1, 1934

By G. Derge, W. Peifer, J. H. Richards

INTRODUCTION A WIDE variety of metallurgical defects in steel have commonly been attributed to the presence of excessive amounts of hydrogen. These defects include flakes in rails and forgings, cracks in welds, and blisters in enameled ware. They have been related to hydrogen largely by circumstantial evidence because the proper sampling and analysis of steel for hydrogen has been known to be difficult and because no general agreement has existed with regard to the relative suitability and accuracy of available methods. The need for a direct approach to these problems has been widely recognized. This general situation has been well described in the publications of the British Committee on the Heterogeneity of Steel Ingots,1 and current approaches to the problem were reviewed in a recent symposium of the AIME.12 The plans described by the present authors at that meeting have now matured satisfactorily and will form the basis of this paper. The principle object of this paper will be to describe the methods of sampling and analysis which have been developed and to illustrate the usefulness and limitations of these methods by citing their application to a specific problem. The first problem selected for investigation was the behavior of hydrogen in rail steel. This was chosen because the occurrence of shatter cracks in rails has received a great deal of study over a long period of time. The defect can be controlled by the expensive procedure of slow cooling. However, it may be hoped that a better understanding of the factors influencing the hydrogen content of rails will lead to a more efficient control of this problem. Rails provide a good starting point for a more general study of hydrogen in steel because they provide a cross section large enough to develop cracks, yet small enough for convenient handling and sampling. Rails were also selected because they are made from plain carbon steel and it was felt that the initial work should not be complicated by the effects introduced by alloying elements. The considerations which determined the original planning of this study should be reviewed. The inherently complex nature of most hydrogen problems requires that a large amount of data must be collected for any particular case. This in turn means that any analytical procedure should be as rapid and simple as possible. The same objective of speed is indicated by the fact that it may finally become desirable to use hydrogen analysis in process control. It is also known that hydrogen is highly fugitive and that any procedure which facilitates early analysis of the sample without prolonged or irregular storage has distinct advantages. The most important previously reported methods of analysis may be classified into three general groups: (I) Vacuum fusion. (2) Vacuum extraction (without melting). (3) Total combustion.

Jan 1, 1948

By Irving Hartmann, H. P. Greenwald

READERS of this journal are familiar with the danger of coal-dust explosions in mines and with recommended means for preventing them. The subject was treated in a paper by R. R. Sayers in the January 1943 issue, as well as in several previous articles. Similarly the danger of dust explosions is generally recognized in the handling of grain dust, flour, starch, sugar, and other carbonaceous products. However, until recently, few people realized that an analogous, real explosion hazard exists wherever dust suspensions of certain finely divided metal powders are formed. This lack of knowledge was in part due to the fact that until a few years ago only a small number of metal powders, such as aluminum, magnesium, zinc, iron, and tungsten, were produced, in comparatively small volume, and partly because information on the explosibility of metal powders was lacking.

Jan 1, 1945

By Harold Roast

THE object of this investigation was to compare the arsenical antimony-lead alloy with some of the regular bearing-metal alloys. With this end in view, the following tests were made: 1. Chemical analyses to show the composition. 2. Thermal analyses. 3. Macroscopic examination of fractures. 4. Microscopic examination. 5. Tensile tests. 6. Crushing tests. 7. Scleroscope tests. 8. Brinell tests, at temperatures from 80° to 400° F. Tests 3 to 8 were conducted on both sand-cast and chill-cast specimens. For the purposes of this paper the alloys have been numbered from 1 to 6; their composition is as follows: LEAD, ANTIMONY, TIN, COPPER, ARSENIC, NUMBER PER CENT. PER CENT. PER CENT. PER CENT. PER CENT. 1 82.64 12.95 4.40 0.01 none 2 27.54 9.94 59.87 2.65 none 3 77.65 20.75 none 0.13 1.47 4 82.95 16.85 none 0.20 none 5 83.78 15.35 none 0.05 0.82 6 0.15 7.87 84.13 7.85 none The analysis, in the case of the antimony, was made by solution in sulfuric acid and titrated with permanganate. For tin, the ferric-chloride method was used; for copper, the alkaline separations, and the thiocyanate methods; for arsenic, volatilization of arsenic and titration with iodine. The lead, with the exception of alloy 6, was taken by difference.

Jan 2, 1922

By C. S. Harloff, Frank R. Corwin

THE Nichols Copper Co., associated with the Phelps Dodge Corp. and the Calumet & Arizona Mining Co., has constructed at El Paso, Tex., and is now operating a copper refinery with a yearly capacity of 100,000 tons of anodes. Transportation facilities were perhaps the most important of the considerations that led to the selection of this site. The rapid industrial development of the Middle and Far West has increased the consumption of copper there. The advantage of local refining as against shipping the copper to the Atlantic sea- board is apparent. Copper refined in the Southwest is equally competitive for export shipment, either from the Gulf or the Pacific Coast ports. The tonnage of copper produced in the Southwest not only justifies the construction of this plant, but may warrant considerable expansion in years to come.

Jan 1, 1930

By J. W. Freeman, J. P. Rowe, R. F. Decker

HEAT-to-heat variations in properties of an alloy of constant nominal chemical composition have been a perplexing problem to the metallurgist. These heat-to-heat differences have been especially baffling in high-temperature metallurgy. In order to establish fundamental reasons for these heat-to-heat variations, the National Advisory Committee for Aeronautics has sponsored and financially assisted an extended research program on heat-resistant alloys at the University of Michigan. As part of the program to find the contribution of processing variables, Frey, Freeman, and white' studied effects of heat treating on nickel-base alloys and Ewing and reeman' investigated effects of hot-working practice on N155 alloy. To extend the program to the study of effects of melting practice on high-temperature properties, a 55 Ni-20 Cr-15 Co-4 Mo-3 Ti-3 pct A1 composition was selected for experimentation. The objective of this program was to establish the melting-practice variables which influenced the hot-working characteristics and creep-rupture properties and, at the same time, establish the metallurgical mechanisms for the effects. During the course of the investigation of practices using vacuum melting, it became increasingly evident through chemical analyses supplied by industrial concerns that a major variable was melt reaction with the crucible. This paper is devoted to the results of this phase of the melting-practice study. EXPERIMENTAL PROCEDURES Experimental 10-lb heats were induction melted in the University of Michigan vacuum-melting unit with the melting practices outlined in Table I. Aim analysis for the basic alloy, in wt pct, for all heats was as follows: Cr Co Mo Ti Al 20.0 15.0 4.0 3.1 3.1 Mn Si C Ni 0.12 0.12 0.08-0.15 Bal. Small amounts of boron and zirconium were added to certain heats as listed in Table I. These additions

Jan 1, 1959