By G. F. Fix, R. E. Esarey

During 1939, Indiana experienced a grcat increase in prospecting and drilling for oil and gas. Major activity, as during the preceding year, was in the southwestern part of the state, the Indiana portion of the Eastern Interior Coal Basin. An increasing interest was evident during the year, however, in the entire state, chiefly in northern Indiana (on the south flanks of the Michigan Basin) and in the old Trenton field of east central Indiana. In the latter area several tests to deeper horizons in the Trenton and to the underlying St. Peter sandstone were completed. Results in this area have been discouraging, however, since these deeper horizons are very erratic. The regional structure in the Indiana portion of the Michigan Basin is generally favorable to oil accumulation, but the picture is complicated by a uniform mantle of glacial drift and a lack of subsurface information. Several wells were started during the last half of 1939 to test the Devonian and Trenton formations in this area. Production from these formations was found at several localities many years ago, hut, no sustained effort has been made to locate pools in this area, which covers perhaps 20 counties. There were 377 wells completed in Indiana during 1939, and 77 others were in various stages of drilling at the close of the year. Of the 377 completed, 255 were classed as field locations and 122 as wildcats. The field wells were divided as follows: 156 oil wells, 39 gas wells, and 60 dry holes; the wildcats: 98 dry holes, 19 oil wells and 5 gas wells (wildcat oil and gas wells include deeper production in oil fields and field extensions as well as new field discoveries). During the year 218 more wells were completed than during 1938. Outstanding developments for 1939 include the discovery of several new oil and gas fields. In the Griffin field, which was discovered during the closing days of the previous year, 103 wells were drilled, including field extensions. Of these, 97 were productive oil wells. This field now covers more than 2000 acres of productive area and has not as yet been defined. There are five producing horizons in the field, including the Waltersburg, Tar Springs, Elwren, and Aux Vases sandstones of Chester age and the McClosky horizon of the Ste. Genevieve limestone. Produe-

Jan 1, 1940

By G. F. Fix, R. E. Esarey

During 1939, Indiana experienced a grcat increase in prospecting and drilling for oil and gas. Major activity, as during the preceding year, was in the southwestern part of the state, the Indiana portion of the Eastern Interior Coal Basin. An increasing interest was evident during the year, however, in the entire state, chiefly in northern Indiana (on the south flanks of the Michigan Basin) and in the old Trenton field of east central Indiana. In the latter area several tests to deeper horizons in the Trenton and to the underlying St. Peter sandstone were completed. Results in this area have been discouraging, however, since these deeper horizons are very erratic. The regional structure in the Indiana portion of the Michigan Basin is generally favorable to oil accumulation, but the picture is complicated by a uniform mantle of glacial drift and a lack of subsurface information. Several wells were started during the last half of 1939 to test the Devonian and Trenton formations in this area. Production from these formations was found at several localities many years ago, hut, no sustained effort has been made to locate pools in this area, which covers perhaps 20 counties. There were 377 wells completed in Indiana during 1939, and 77 others were in various stages of drilling at the close of the year. Of the 377 completed, 255 were classed as field locations and 122 as wildcats. The field wells were divided as follows: 156 oil wells, 39 gas wells, and 60 dry holes; the wildcats: 98 dry holes, 19 oil wells and 5 gas wells (wildcat oil and gas wells include deeper production in oil fields and field extensions as well as new field discoveries). During the year 218 more wells were completed than during 1938. Outstanding developments for 1939 include the discovery of several new oil and gas fields. In the Griffin field, which was discovered during the closing days of the previous year, 103 wells were drilled, including field extensions. Of these, 97 were productive oil wells. This field now covers more than 2000 acres of productive area and has not as yet been defined. There are five producing horizons in the field, including the Waltersburg, Tar Springs, Elwren, and Aux Vases sandstones of Chester age and the McClosky horizon of the Ste. Genevieve limestone. Produe-

Jan 1, 1940

John A. Church, New York City: It requires some courage to appear as a critic of a theory which is not only the fashion among American geologists but is usually presented by them in terms which imply that any other views are an exhibition of ignorance. Still, I am obliged to say that the theory of lateral secretion as it is stated in this and other writings of Mr. Emmons and other geologists has not added much to our real knowledge or clearness of view. In the earlier and less developed stages of the theory, when it was used as Sandberger used it, to show that certain veins were probably derived from the rocks in which they lie, or which are adjacent, it was valuable in pointing us to an immediate source of ore-deposition. When we are driven to assume the existence of undiscoverable rocks at an unknown but certainly a considerable distance and in an unknown direction from the vein, I do not see that we have improved upon the despised " unknown source in depth " with which our ignorance has been covered so long. The new theory may suffer from adolescence, and these points map be cleared up by further study, but I speak of it as it is. Differentiation in a magma, by which a metal is concentrated in one member of a series of outflows, may explain why certain ores have favored a given locality with their presence; but it is not a necessary precedent to ore-formation. Concentration in the source of supply cannot be a requirement, for the forces that have been able to take up four or five tons of gold from an extensive body of rock must be able to collect four or five thousand tons of lead, copper or nickel from a proportionately more extended body of rock. That is to say, concentration is no more essential for these metals than it is for gold. In fact, differentiation, as it is now explained, is not an advance upon old ideas, but a retreat from them. It was noticed long ago that violent eruptive phenomena, however long continued, died away in solfataras; and when a vein came to be looked upon as an extinct solfatara the inference was ready that veins are eruptive in the sense that the solfataric waters collected the metals from the unerupted residue of the magma and carried them to the veins. The early views carried differentiation further than the modern school.

Jan 1, 1894

By R. C. Hyslop

The object of this experiment was to obtain a usable set of field curves for determining the susceptibility of rocks with the vertical magnetometer. The need often arises for determining the susceptibility of rocks in the field in order to interpret magnetic anomalies obtained. This is particularly true when diamond drilling has been done and the relation to the surface rocks of the samples taken is desired. Many methods of measuring rock susceptibility have been developed, but in general they require careful shaping of the sample or pulverizing it in addition to delicate laboratory measuring instruments designed for the purpose. The requirements for a practical method for the determination of susceptibilities are as follows: 1. There should be as little alteration as possible of the specimen. 2. A minimum of time should be required in the preparation of the specimen and the calibration of the equipment. 3. Theequipment used should be portable. 4. An accuracy within the limits of the survey at hand should be obtainable. 5. A means of measuring the remnant magnetism should be available. Laboratory Procedure With these ideas in mind, the problem was approached in the manner in which Koenigsbergerl developed his method using the principle of the electrical theory of images of Lord Kelvin and applying it to the magnetic case. This solution of the problem states that the apparent change in the magnetic field intensity AZ due to the proximity of a specimen is given by: mk AZ = 2a2 Where k is the susceptibility of the specimen, m the strength of the pole of the needle, and a its distance from the surface of the specimen, as shown in Fig. r.2 This relation is true only for an infinite body and corrections are necessary for a finite body. Koenigsberger used in his work a variometer of special design. He suggested that a Schmidt vertical balance or horizontal magnetometer, as well as some other instrument, might be used. The Colorado School of Mines horizontal torsion magnetometer operates on this principle. In the

Jan 1, 1946

By R. C. Hyslop

The object of this experiment was to obtain a usable set of field curves for determining the susceptibility of rocks with the vertical magnetometer. The need often arises for determining the susceptibility of rocks in the field in order to interpret magnetic anomalies obtained. This is particularly true when diamond drilling has been done and the relation to the surface rocks of the samples taken is desired. Many methods of measuring rock susceptibility have been developed, but in general they require careful shaping of the sample or pulverizing it in addition to delicate laboratory measuring instruments designed for the purpose. The requirements for a practical method for the determination of susceptibilities are as follows: 1. There should be as little alteration as possible of the specimen. 2. A minimum of time should be required in the preparation of the specimen and the calibration of the equipment. 3. Theequipment used should be portable. 4. An accuracy within the limits of the survey at hand should be obtainable. 5. A means of measuring the remnant magnetism should be available. Laboratory Procedure With these ideas in mind, the problem was approached in the manner in which Koenigsbergerl developed his method using the principle of the electrical theory of images of Lord Kelvin and applying it to the magnetic case. This solution of the problem states that the apparent change in the magnetic field intensity AZ due to the proximity of a specimen is given by: mk AZ = 2a2 Where k is the susceptibility of the specimen, m the strength of the pole of the needle, and a its distance from the surface of the specimen, as shown in Fig. r.2 This relation is true only for an infinite body and corrections are necessary for a finite body. Koenigsberger used in his work a variometer of special design. He suggested that a Schmidt vertical balance or horizontal magnetometer, as well as some other instrument, might be used. The Colorado School of Mines horizontal torsion magnetometer operates on this principle. In the

Jan 1, 1946

By W. B. Humes

The use of high vacuum on a large industrial scale in the ferrosilicon process for the production of magnesium marks the coming of age of an important new metallurgical technique. The economical production of reactive metals, such as magnesium, which combine with all the well-known furnace atmospheres, has until recently been successfully carried out only by electrolytic methods. It is now apparent that, through the use of high vacuum, the distillation or sublimation of many metals can be done industrially at much lower temperatures, and hence in much simpler equipment, than heretofore has been thought possible. At the beginning of the present emergency, when the ferrosilicon process of producing magnesium was brought to the fore, little was generally known about vacuum engineering, practices, and techniques. In a comparatively short time, the available equipment has been adapted, new equipment designed and built, and a fund of know-how evolved to make possible the production of thousands of pounds of magnesium per day at pressures less than 1/ r0,000 of an atmosphere. Pilot-plant operations have been consistently maintained at pressures even as low 2s one micron (0.001 mm.). These low pressures, which previously were regarded as prohibitively costly or impossible to attain, have been demonstrated as economically feasible on an industrial scale. Necessity for Vacuum The main function of vacuum in the ferrosilicon process, and hence in most vacuum smelting processes, is to lower the temperature at which the metal may be distilled or sublimed from the reduction mixture. A secondary function is to protect the distilled metal from attack by the furnace atmosphere and to permit the formation of a dense condensate. In the ferrosilicon process, magnesium is formed by the reaction between dolomite and ferrosilicon: 2(Mg0-Ca0) -\- HFeSU / t=> aMg + MFe + (CaO)2-SiO2 The metal is distilled from the pelleted charge at a free air pressure of about 0.100 mm. of mercury (100 microns). This low pressure is not needed for the reaction, but rather serves to protect the metal vapor from the oxygen or nitrogen of the atmosphere and permits the formation of a condensate free of pyrophoric material. The reaction proceeds at air pressures as high as several millimeters of mercury, and evidence has been offered to show that the actual equilibrium pressure of magnesium at operating temperatures of 2I50°F. is somewhat higher. Experimentation indicates that the yield begins to decrease at pressures above 500 microns. While no real operating data are yet available on the relationship between

Jan 1, 1944

By James A. Barr

Prospecting methods used in Tennessee have gradually improved with the years, as required by depletion of the easily accessible and shallow deposits and the universal trend toward mechanization, and as necessitated by exploring deeper beds, often occurring under limestone and flinty overburden. In the early days it was a very simple matter to dig pits by hand, using a plentiful supply of local farm labor to expose relatively shallow deposits of "brown rock" under shallow clayey overburden that would stand up without timbering. Visual inspection of the exposed phosphate and expert judgment of the "grade" analysis, aided by a "biting" test to reveal presence of unwanted silica, furnished most of the information required. All this might be helped by a few samples sent to the local chemist† who supplemented his income by judicious trading or tanning a few bear skins. The extra curricula activities did not affect the accuracy of the analysis which hold up even under present day standards. Some shot and core drilling was done in Hickman County, mostly for the limestone-like blue Phosphate deposits. The next step was the use of a 4-in. posthole auger, hand operated as described by Guenther, followed by a completely mechanized rig, as described by Pickard. Both these methods are practically adapted to the prospecting of the relatively soft brown rock deposits at moderate depths of clay overburden. For prospecting in areas of deeper overburden, such as are often found in Hickman County, up to 150 or even 200-ft depths, a modified core-drilling method is described by Guenther. Johnston describes a special diamond-drilling technique, developed by TVA, to penetrate flint horizons, which was adopted by the International Minerals in chemical corporation to prospect in Hickman County where deposits had previously been prospected at considerable expense and with difficulty, by small, temporary, hand-dug shafts.

Jan 1, 1948

By James A. Barr

Prospecting methods used in Tennessee have gradually improved with the years, as required by depletion of the easily accessible and shallow deposits and the universal trend toward mechanization, and as necessitated by exploring deeper beds, often occurring under limestone and flinty overburden. In the early days it was a very simple matter to dig pits by hand, using a plentiful supply of local farm labor to expose relatively shallow deposits of "brown rock" under shallow clayey overburden that would stand up without timbering. Visual inspection of the exposed phosphate and expert judgment of the "grade" analysis, aided by a "biting" test to reveal presence of unwanted silica, furnished most of the information required. All this might be helped by a few samples sent to the local chemist† who supplemented his income by judicious trading or tanning a few bear skins. The extra curricula activities did not affect the accuracy of the analysis which hold up even under present day standards. Some shot and core drilling was done in Hickman County, mostly for the limestone-like blue Phosphate deposits. The next step was the use of a 4-in. posthole auger, hand operated as described by Guenther, followed by a completely mechanized rig, as described by Pickard. Both these methods are practically adapted to the prospecting of the relatively soft brown rock deposits at moderate depths of clay overburden. For prospecting in areas of deeper overburden, such as are often found in Hickman County, up to 150 or even 200-ft depths, a modified core-drilling method is described by Guenther. Johnston describes a special diamond-drilling technique, developed by TVA, to penetrate flint horizons, which was adopted by the International Minerals in chemical corporation to prospect in Hickman County where deposits had previously been prospected at considerable expense and with difficulty, by small, temporary, hand-dug shafts.

Jan 1, 1948

By R. N. Singh, A. S. Atkins

One of the most difficult problems associated with modern mechanised longwall mining is the lack of system flexibility to deal with local changes in geology, seam thickness and the face design parameters. As a consequence of system rigidity and the quest for increasing the coal face performance, the percentage extraction in the U.K. is currently below 52%. The paper outlines the current guidelines used in face design which permit coal to be left in situ for various purposes and discusses the strata control implications in extracting subsequent panels in the same and adjacent coal seams. The paper examines the application of strata mechanics to the design of longwall layouts for maximizing .the percentage of coal extraction. Remedial measures include optimizing pillar dimensions, reduction in roof coal left for support purposes by improving the use of available powered support technology and application of thick seam mining methods including sub-level caving and techniques of extracting coal from odd shaped pillars. Case studies are described where coal extraction has been maximized by adopting a new single heading retreat mining system; a shallow seam partial extraction system utilizing, existing heading machines and minimisin8 coal sterilization in pillars by replacing longwall access roadways by goaf scour.

Jan 1, 1984

By J. Nagy, D. W. Mitchell, E. M. Murphy

In 1957 research was initiated in the U.S. Bureau of Mines experimental coal mine near Pittsburgh, Pa., to study factors affecting foam generation and transport, to evaluate the effectiveness of high-expansion foam for controlling mine fires, and to develop techniques for applying the method under U.S. mining conditions. These investigations showed that high-expansion foam containing at least 0.2 oz of water per cu ft of foam is effective in controlling experimental underground fires burning coal, wood, and oil. Sometimes the fire was completely extinguished, but more often, it was brought under sufficient control to permit either a direct attack on the fire with a stream of water or loading of the hot material into cars. A progress report' prepared in July 1958 summarized the initial achievements of the USBM experiments. Since then other phases of the foam-plug method for attacking fires have been studied in the laboratory and in the mine. Previous studies by British engineers' of the foam-plug method for fighting mine fires indicated that high-expansion foam was effective in controlling experimental timber fires in an underground passageway. Their subsequent workx-1 pertained to the practical aspects of fighting large fires within a mining area with a foam-plug. CONTROLLING EXPERIMENTAL FIRES In the USBM tests foam was formed by spraying a dilute solution of a foaming agent on a metal or cotton net of 1/8 to 1/4-in. mesh. Air passing through the continuously wetted net forms bubbles of 1/2 to 11/2-in. diam and produces a honeycomb of foam that fills the passageway. Under the ventilating-air pressure, this light-weight plug moves forward through the passageways, around sharp corners, and over obstacles. as illustrated in Fig. 1. High-expansion foam was transported to a wood fire, an oil fire, and 13 coal fires. Figs. 3 and 4 show a typical coal fire before and after attack with foam. In 12 of the 15 experiments the fire was brought under control when the water content of foam was 0.2 oz or more per cu ft. A fire was considered controlled when the flames were quenched and observers could cross the area without wearing breathing apparatus or protective clothing. In the other three experiments, conducted when the water content was less than 0.2 oz per cu ft of foam, the flames were retarded but the fire was not controlled. Coal fires have been attacked successfully by foam introduced at points varying from 155 to 1010 ft from the fire. The time of burning in coal beds 10 in. thick ranged from 11/2 to 5 hrs or more. Most of the experimental fire beds were 15 ft in length. However, in one experiment a floor fire 25 ft long and 5 ft wide was constructed $5 upwind from another fire 15 ft in length; in another instance, the fire was 100 ft long and 5 ft wide. Foam was applied to the fires for periods ranging from 7 to 36 min. The time required for foam application depends on the extent of the fire, time of burning, water content of foam, foam velocity, and degree of fire control desired. In addition to the coal fires, foam was transported to a fire covering 45 sq ft, produced by 15 gal of oil burning in metal trays on the floor. The foam extinguished the oil fire in about 1 min. In one other test, the burning of 1100 lb of dry sawmill slabs stacked in open cribs 4 ft high and 16 ft long was brought under control by foam in 2 min. Composition of Gases in Return Air: In several of the experiments samples of the return air from fire zones were collected; composition of the atmosphere before, during, and after foam application was then determined. Because of condensation in the relatively cool sampling tube, the amount of water vapor was not determined. Analyses showed that concentration of carbon dioxide and combustible gases increased as the foam began passing over the fire. This resulted from the decrease in the volume of air when foam generation started and from the formation of gases when water reached the fire.* The quantity of gases generated would not be greater than that from an equivalent amount of water applied directly to the fire. The highest total concentration of combustibles (CO, CH1, and H2 mixture) obtained during the experiment was about 2 pct; this occurred 6 min after foam reached the fire. This atmosphere was nonex-plosive, but calculations show that if the air flow were reduced to about 5 fpm and if the rate of gas liberation from the fire remained constant, the mixture would be explosive. The use of foam on a fire in all probability would affect the normal ventilation of a mine. If the mine is gassy, this factor must be carefully considered before the foam is applied. APPLICATION OF THE FOAM-PLUG TECHNIQUE IN MINES Equipment and procedures for applying the foam-plug methods must be adapted to the prevailing conditions at a particular mine. Some factors to be considered in developing equipment are: size or extent of the mine, dimensions and number of entries, ventilation system, mining methods, haulage facilities, availability of water, amount of methane liberated, and existing fire-control apparatus. • In most experiments the initial air velocity of 200 fpm decreased to 50 to 100 fpm as the foam plug increased In length.

Jan 1, 1961

High-type research metallurgist with approximately following qualifications: American, 30 to 45 years old. Mind-Analytical. Education-college graduate. Practical shop experience-not less than 5 years. Metallurgical experience in steel making-at least 5 years. Chemical experience-should have some chemical training. Research ability -should be the type of man who is interested in new developments or research work. No. 337. Engineer with some underground, experience who is physically able to spend a large portion of his time underground, to act as general efficiency engineer. He will have cost keeping on special work, charge of contracts, labor distribution, etc. No. 338. The services of a man experienced in flotation and familiar with the Callow apparatus are required for a short engagement in South America. No. 339. A position as surveyor and draftsman for mines in Mexico is open. Opportunity for advancement. Climate pleasant and healthful. Knowledge of Spanish required. No. 340. The Bureau of Construction and Repair, Navy Department, Washington; D. C., is in need of a few draftsmen of experience for work in connection with the development of industrial yards and shops of the Navy, under the cognizance of the Shore Establishment Division of the Bureau of Construction and Repair. Training in one of the following courses would be considered a requisite qualification:

Jan 9, 1918

By William P. McConnell

At the dawning of the first century of AIME, mechanical handling of bulk materials was largely confined to movement of grain and light mill products by belt and screw conveyors, but grain handling experience inevitably led to the use of the belt conveyor for coal, ore and other heavier materials. In 1891, the first major U.S. conveyor installation for heavy minerals was completed at the Edison, N.J., plant of the New Jersey & Pennsylvania Concentrating Co. Functionally, this plant revealed its grain elevator heritage. Overlooked at the time of design or, perhaps more accurately, not fully recognized, were the dramatic differences between grain and minerals in both operating conditions of the system and the physical characteristics of the material to be conveyed. This inevitably caused problems, but from the ashes of these problems rose solutions. The Edison plant became a proving ground from which came two significant developments by Thomas Robins-the first conveyor belt designed specifically for impact loading and abrasive materials and the three-roll conveyor idler. As an installation with more than 50 conveyors in widths of 20-30 in. and belt centers of up to 500 ft, the plant was a landmark, for it established the belt conveyor as a vital method of trans- porting heavy, abrasive materials.

Jan 1, 1971

By T. S. Fuller

Various phases of the embrittlement of solid copper containing oxygen by the action of reducing gases at high temperatures are familiar to readers of metallurgical literature through the work of many experimenters. In 1900, Heynl recorded observations of copper being heated in hydrogen with the development of fine cracks, the result of the formation of steam within the metal through the action of hydrogen on the copper oxide usually found in copper. Archbutt,2 in 1905, published the results of experiments, showing that all oxygen can be removed from copper by heating to redness, for several hours, in hydrogen. Intercrystalline cracks and extreme brittle-ness developed. Archbutt attributed the brittleness to the reduction of oxides present in the copper. Bengough and Hil1,3 in 1910, encountered the now well-known embrittlement at the outset of their investigation and stated in their paper: It soon became evident that the effect of any heat treatment depended largely on the presence or absence of reducing gases in the atmosphere of the furnace, as well as on its temperature. Hence it became necessary to adopt a somewhat elaborate scheme of heat treatment. The authors found embrittlement in separate experiments due to both hydrogen and carbon monoxide and concluded that: "The gases ruin the alloys after being heated to about 650" C. in their presence." Ruder,4 in 1916, reported the results of a series of experiments made by heating commercial and deoxidized copper in hydrogen, carbon monoxide, carbon dioxide, and steam. In agreement with other writers, he found that copper containing oxygen was made brittle by reducing gases, while the deoxidized metal remained unaffected. In the case of

Jan 1, 1926

By C. H. G. Bushell, M. Malnarich

Reagent control in flotation is more an art than a science. Operators vary the amount of re- agents used according to the metallurgy obtained. The amount of collector may be increased, for example, if tailings losses are high and decreased if concentrate grades are low. Often control decisions are based on only one assay, such as the tailings analysis by microscopic or quick assaying techniques. This method of control has given reasonably satisfactory results but is clearly far from perfect. No adjustment in reagent addition can be made until information is received that metallurgy has deteriorated, that is, until the optimum time for adjustment has already passed. The first adjustment probably will be an overcorrection or an undercorrection, and time will be required to establish the best new addition rates. The seriousness of the problem depends on variability of the ore. In ore of continually shifting composition and complexity, mill results will shift back and forth from excessively high concentrate grades and high tailings losses to excessively low concentrate grades and low tailings losses. Economic incentive for improved control also increases with increasing size of mill. Even a small improvement in percentage recovery in a large mill pays for expensive control equipment.

Jul 1, 1956

By N. P. Goss

Asterism appearing in X-ray Laue diagrams is an extremely sensitive index of changes in the internal structures of individual grains of polycrystalline metals. It indicates the existence of various forms of subboundary structure or subdivision within the grain. The present viewpoint is that the grain is made up of lattice blocks having substantially the same size and shape.l-4 When these blocks all assume exactly the same orientation, the crystal is perfect and asterism is absent. Cleaves and Thompson5 observed that the hardness of iron is virtually constant over a range of grain sizes. It is quite possible that the subboundary structure caused this, and that the latter is just as important as grain size itself. While the experiments reported here are not conclusive, they do support this viewpoint. Metals can, under certain conditions, be prepared entirely free from asterism, but this preparation does not necessarily require long heating or slow cooling, as will be shown here. In this paper a distinction is made between mosaic and distorted grain structures but the difference is only a matter of degree. In a previous paper9 it was shown that the grains can become distorted even during heat-treatment. The block structure exists inherently, even in a perfect crystal; the size and shape of these crystallites, or lattice blocks, varies, depending upon a number of factors. Goetz, for example: has shown that a metal before crystallizing from the molten state must go through a paracrystalline phase with oriented groups of atoms about 10-l4 to 10-l5 c.c., or 10-15 cm. in size. These crystallites, or blocks, appear to survive the most drastic cold-working, for it has been shown, and more elaborately by Wood's recent work," that cold-working cannot reduce the size of these crystallites smaller than of the order 10-5 cm. The interesting correlation brought out by the experiments of Goetz and Wood is that the block size after severe cold-working is of the same order of magnitude as the groups that formed in the metal just before crystallizing from the molten state. The work of Ewald and Rennenger17 and the now classical experiments of Darwin and James12,13 all strongly suggest the existence of a periodic structure of crystal. lites smaller than the grain itself. Related to this effect is the appearance of veinlike markings in the microstructures. Ammer-man and Kornfeld,16 in their experiments, did not observe any evidence of veining in specimens of alpha iron annealed below A3 and believed that veining was not due to impurities in the iron, as Northcott16 suggested; veining was observed by them only in specimens annealed above A3. Hanemann,16 Schrader and Tangerding found that annealing in hydrogen did not diminish veining and so it could not be caused by oxides. They concluded that veining was due to a slight difference in the orientation of ferrite lattice blocks. This viewpoint is well supported by the evidence presented here.

Jan 1, 1941

By N. P. Goss

Asterism appearing in X-ray Laue diagrams is an extremely sensitive index of changes in the internal structures of individual grains of polycrystalline metals. It indicates the existence of various forms of subboundary structure or subdivision within the grain. The present viewpoint is that the grain is made up of lattice blocks having substantially the same size and shape.l-4 When these blocks all assume exactly the same orientation, the crystal is perfect and asterism is absent. Cleaves and Thompson5 observed that the hardness of iron is virtually constant over a range of grain sizes. It is quite possible that the subboundary structure caused this, and that the latter is just as important as grain size itself. While the experiments reported here are not conclusive, they do support this viewpoint. Metals can, under certain conditions, be prepared entirely free from asterism, but this preparation does not necessarily require long heating or slow cooling, as will be shown here. In this paper a distinction is made between mosaic and distorted grain structures but the difference is only a matter of degree. In a previous paper9 it was shown that the grains can become distorted even during heat-treatment. The block structure exists inherently, even in a perfect crystal; the size and shape of these crystallites, or lattice blocks, varies, depending upon a number of factors. Goetz, for example: has shown that a metal before crystallizing from the molten state must go through a paracrystalline phase with oriented groups of atoms about 10-l4 to 10-l5 c.c., or 10-15 cm. in size. These crystallites, or blocks, appear to survive the most drastic cold-working, for it has been shown, and more elaborately by Wood's recent work," that cold-working cannot reduce the size of these crystallites smaller than of the order 10-5 cm. The interesting correlation brought out by the experiments of Goetz and Wood is that the block size after severe cold-working is of the same order of magnitude as the groups that formed in the metal just before crystallizing from the molten state. The work of Ewald and Rennenger17 and the now classical experiments of Darwin and James12,13 all strongly suggest the existence of a periodic structure of crystal. lites smaller than the grain itself. Related to this effect is the appearance of veinlike markings in the microstructures. Ammer-man and Kornfeld,16 in their experiments, did not observe any evidence of veining in specimens of alpha iron annealed below A3 and believed that veining was not due to impurities in the iron, as Northcott16 suggested; veining was observed by them only in specimens annealed above A3. Hanemann,16 Schrader and Tangerding found that annealing in hydrogen did not diminish veining and so it could not be caused by oxides. They concluded that veining was due to a slight difference in the orientation of ferrite lattice blocks. This viewpoint is well supported by the evidence presented here.

Jan 1, 1941

By Louis A. Panek

THE purpose of this paper is to present a method of designing safe and economical arch structures that are to be constructed of concrete or directly of original earth materials. The experimental data used to illustrate the design method are taken from Bucky and Fentress,1,2 and the application of the ideas presented by them is extended by obtaining an additional set of curves from which arch structures may be designed. This design method is based upon the following principles of similitude: A scalar model made of the same material as that of the full sized structure will behave similarly to its prototype if the density of the model is increased in the same proportion as its linear scale is decreased. Let R represent the scale or model ratio, namely, the ratio of a prototype linear dimension to the corresponding model linear dimension. The effect of increased density may be obtained by rotating the model in a centrifuge at a speed such that the centrifugal field exerts on the model an accelerative force R times the accelerative force of gravity. Under these conditions; (I) model unit stresses are equal to corresponding prototype unit stresses, (2) the ratio of the prototype deformation at a given point to the model deformation at a similar point is equal to the scale ratio, R, and (3) the model and the prototype will behave similarly within and beyond the elastic limits of strain. According to the above relations, such models can be used to solve the following problems: I. The dimensions of the most economical safe arch structure for a given load. 2. The maximum safe roof span underground for given geologic conditions. The procedure is described briefly as follows. Tests are made by rotating in a centrifuge a number of models that repIesent a variety of prototype loads and dimensions. From the experimental data, curves are plotted to show the relations between these loads and dimensions. The curves are used to solve directly the problems stated above. Structural design is based upon the working (safe) stress of the material of construction, which is established by applying a factor of safety to the experimentally determined ultimate strength of the material. In conformity with this principle, each model is gradually loaded until failure occurs. A safety factor is then applied to the results. If a safety factor of 4 is used, a given model at failure represents a safe prototype, the linear dimensions of which are equal to one-fourth the model ratio at failure times the corresponding model dimensions. The safe model ratio is computed from the following formula: [Safe R = (rl 47r2n2r _ 7r2n2r~r~ \4/ gg in which: n = centrifuge revolutions per second at model failure; r = radius of rotation of the model in feet; g = 32.2 ft/sect.]

Jan 1, 1947

By J. T. Norton, J. G. McMullin

An 1820°C isothermal cross section of the Ti-Ta-C ternary diagram was prepared from X-ray diffraction and metallographic data. No phases other than those appearing in the three binary diagrams were observed. At temperatures above the titanium transition temperature titanium and tantalum form a complete series of solid solutions containing up to 2 atomic pct C. The phases Tic and TaC also form a continuous series of solid solutions extending across the diagram. PREVIOUS work on this alloy system was very limited. Of the three binary constitution diagrams involved, only one, the Ta-C system was available in the literature. Preliminary data on the other two systems was received from the investigators during the course of the investigation and both have been published in recent months. It had been shown that Tic and TaC formed a continuous series of solid solutions, but the range of carbon content in this phase was not known. While Ta2C had been described, its solubility for or reactions with other carbides had not been reported. It was not known whether or not any ternary compounds occurred in the system. The present program was undertaken to determine experimentally the general form of the ternary diagram. It is hoped that the results will be of value in furthering the development of sintered carbide cutting materials and high temperature ceramets, many of which contain combinations of Tic and TaC. The Binary Systems Of the three binary diagrams involved only that of Ta-C was available at the time this project was started. The diagram of Ellinger¹ redrawn in Fig. 1, shows a hexagonal phase Ta2C having a very small composition range and a cubic TaC phase having a composition range of from 40 to 50 atomic pct C. The authors made a separate determination of the composition range of TaC using lattice constant values and found the range to extend from 40 to 49.7 atomic pct C in good agreement with Ellinger's diagram. Two determinations of the Ti-Ta system have appeared recently.2,3 These two diagrams are in good agreement and show that ß titanium and tantalum form a complete series of solid solutions. The Ti-C diagram by Cadoff and Nielsen4 shows a very limited solubility of carbon in both a and ß titanium. The single carbide formed persists over a wide range of carbon contents. Several values for the upper limit of carbon content of this phase have been reported."' The highest value obtained in the M.I.T. Laboratory was 47.5 atomic pct C with a lattice constant of 4.328?.5 Fattinger7 describes a gas carburization method which he claims produces stoichiometric Tic although he does not present any data showing that he actually had 50 atomic pct combined carbon. Several complete analyses on

Jan 1, 1954

By Reed W. Hyde

SOME information has been published on the sulphur dioxide concentration of gases from Dwight-Lloyd machines sintering lead ores but most of this relates to the customary practice in which the charge is relatively high in lead and is sintered in two passes over the machine. It is thought, therefore, that the following observations on sintering in one pass a low-lead, low-sulphur charge may be of interest. The data were obtained in sintering lead sulphide flotation concentrates mixed with minus 20-mesh oxide ore, the mixture carrying 16.8 per cent Pb and 5.3 per cent S. No returns were used because of the limited amount of sulphur available as fuel, but the mixture pelletized readily to make a satisfactorily permeable bed on the sintering machine. As there was a possibility that the SO2 might be utilized, a series of runs was made to determine the concentration of SO2 in the gases at different points along the wind box, and the effect on this concentration of changes in the wind-box vacuum. Several runs each were made with vacuums (as measured in inches of water at the wind box) of (1) 2 to 1 3/4 in., (2) 4 to 3 1/2 in. and (3) 6 to 5 1/8 in. The averages of the determinations from each series are platted on the graph (Fig. I). The vertical scale shows the percentage by volume of SO2 (as determined by the Reich method), and the horizontal scale shows the time expressed as percentage of the total sintering time. Sintering was considered to be complete when no SO2 could be detected in the gases. In all cases the depth of bed was 4 1/2 in. and the weight of dry charge per square foot of hearth area was 45.2 lb. Other data are given in the table. The volume of gases corresponding to the several points along the wind box at which SO2 determinations were made could not be measured, but has been calculated from the SO2 content and sulphur elimination on the assumption that the volume is uniform throughout the sintering period. This is not strictly true, as with a given vacuum the volume will usually drop slightly toward the middle of the period and increase toward the end. However, this assumption is a reasonable approximation. Several interesting features are brought out by these data. In general, the published data on SO2 concentration in sintering under ordinary conditions show a high SO2 concentration in the early stages followed by a rapid decrease in concentration and with relatively little SO2 in the gases from the last half or third of the operation. In other words, the greater part of the sulphur elimination is obtained in the first third or half of the period. In these runs, the 6-in. vacuum, which approximates the usual operating condition, gives a curve that follows this customary pattern. Maximum SO2 concentration is obtained 2 ½ min. after

Jan 1, 1942

By M. E. Glicksman, G. S. Ansel

It has been shown by Walton and Chalmers,&apos; that the mechanism of the development of solidification textures in castings involves the preferential growth of dendrites along certain crystallographic directions as determined by the influence of prevailing heat-transfer conditions. Specifically, this growth is parallel to the direction of heat flow. The purpose of the present investigation was to determine the applicability of this mechanism to: 1) commercially pure aluminum (99.75 pct) solidified to coarse columnar crystals, 2) an aluminum-silicon casting alloy (5.25 Si, 0.38 Fe, 0.02 Cu, 0.10 Ti, 0.002 S) cast to a fine-grained structure under complex and reproducible heat transfer conditions. PROCEDURE AND RESULTS 1) Specimen Preparation—Using a technique similar to that employed by Northcott and Thomas,2 samples were melted in the directional solidification mold, Fig. 1, by heating the entire assembly to 670° C. The mold was then end cooled using a water jet. From considerations of harmonic analysis, the likely distribution of isotherm normals encountered by the growing crystals is shown in Fig. 1. 2) Orientation Analysis—The pure aluminum sample froze to large columnar crystals, nucleated close to the metal diaphragm, with the growth direction parallel to the mold axis. Using the back-reflection Laue technique, the growth direction of these crystals was determined to be a <100>, which coincided within 53 deg to the mold axis. Metallographic examination of the relatively fine-grained aluminum-silicon sample revealed a dendritic mode of growth having its primary dendrite arms along isotherm normals. Back-reflection Debye-Scherrer patterns, taken with the specimen rotating about its cylinder axis, yielded rings displaying symmetrical arcing, thus proving that the sample did, indeed, possess the solidification texture inferred from the preliminary metallographic examination. To determine the extent and orientation of the texture in the aluminum-silicon alloy, a density distribution of the (111) poles of the sample was plotted using the transmission Debge-Scherrer

Jan 1, 1960