Search Documents

By Xuewei Lv, Guibao Qiu, Jiaqing Yin, Chenguang Bai

"The iron ore sinter is one of the main raw materials for the blast furnace (BF) process. In the production of iron ore sinter, the cooling speed of the sinter determines its quality. In addition, the heat recovery devices are installed in the cooling machine for energy saving. The cooling parameters like gas flow rate and the size of sinter should be optimized for getting the gas with a higher temperature and a good quality of sinter simultaneously. In this study, the commercial simulation software COMSOL was used to establish a model for simulating the cooling process of the iron ore sinter. Moreover, three different gas flow rate (1.5, 3, 5m/s) and three different diameter of sintered particles (50, 70, 100mm) were investigated with the model. As a result, in certain porosity, a higher cooling speed was achieved when smaller size or larger gas flow rate was used. And lower gas flow rate was beneficial for the heat recovery. The model could intuitively present the exchange of heat between the sinters and air, as well as the flow and temperature fields during the cooling process.IntroductionIron ore sinter plays a great role in iron and steel industry for many Asian countries such as China, Japan and India. As a part of the sintering procedure, the impact of cooling process on the quality of iron ore sinter couldn't be neglected. On the other hand, the massive iron ore sinters which were at high temperature contain extremely large amount of heat. However, it was reported that there's very few of them recovered in China with an average recovery rate of nearly 10.5% at 2004 [1]. Thus, more reasonable cooling procedure should be developed to get high quality product and heat recovery rate simultaneously."

Jan 1, 2011

By B. Erik Ydstie, Dimitrios I. Gerogiorgis, Sridhar S. Seetharaman

"Carbothermic production of aluminium is an important alternative to electrolytic processes and has in fact been identified several decades ago as a potentially feasible and profitable process. The cornerstone principle is to take advantage of the endothermic reduction reaction between carbon and alumina instead of resorting to extreme amounts of electric energy to ionize and reduce aluminium oxide to aluminium. Electric energy is necessary only for heating purposes.The present study focuses on constructing and solving a steady-state electrothermic model for obtaining the spatial distributions for electric potential, electric field intensity and temperature. The complex issues of reaction kinetics and multiphase flow are handled by an approximation and are not addressed at the present stage, due to the lack of complete validated models. Because of its inherent complexity, the reaction slag is considered a pseudohomogeneous layer.An electrothermic simulation encompasses important research challenges, due to the limited knowledge of thermophysical properties for high-temperature multi component molten slags. Therefore, thermophysical property modeling and a systematic compilation of published data is a necessary and major first step towards enhancing understanding of the process fundamentals. Models are obtained by analyzing measurement data from numerous literature references for the density, viscosity, thermal and electrical conductivity and specific heat capacity of the slag.The electric potential, field intensity and temperature distributions obtained reveal interesting maxima which indicate localized superheating and lead to important engineering conclusions. The temperature profile calculated will serve as the foundation for the flow problem solution. This computational study will form a basis for future research towards combining the scopes of microscale CFD modeling and mesoscale process modeling into a unified modeling approach."

Jan 1, 2001

By S. N. Monteiro, C. M. F. Vieira, M. M. Ribeiro

"This work has as its objective to evaluate the effect of incorporation of the powder waste retained in the eletrostatic precipitator of the sintering stage from an integrated steel making plant on the physical and mechanical properties of a red ceramic. Formulations were prepared with incorporation of the waste in amounts up to 20 wt.% into a kaolinitic clay. Rectangular specimens were prepared by uniaxial mold-press at 20 MPa and then fired at 750, 900 and 1050°C. The evaluated physical and mechanical properties were: linear shrinkage, water absorption and flexural rupture strength. The results showed that the waste has a potential to be used into red ceramics. The incorporation of the waste enhanced the properties of the ceramic, decreasing the water absorption and increasing the mechanical strength at all investigated temperatures.IntroductionThe sintering stage of an integrated steel-making plant is dedicated to the agglomeration of a mixture of iron ore, coke or coal, fluxes and water [1]. It is a common practice in this stage to use of solid wastes with great amounts of iron in the form of sludge and powder. One of the atmospheric pollutants generated during the sintering process is the particulate material, which is normally retained in an equipment denote as electrostatic precipitator. This equipment retains very small particulates, present in the gaseous emissions by application of an electrical potential difference in between the plates that the fluid is forced to go through. [2]."

Jan 1, 2011

By Yuan-bo Zhang, Gui-hong Han, Yan-fang Huang, Tao Jiang, Guang-hui Li

"Under isothermal conditions, the reduction behavior of oxidized pellets balled with bentonite was investigated with CO-CO2gas mixers in the temperature range from 900°C to 1100°C. The whole reduction of oxidized pellets was followed up by means of weight-loss technique. And the swelling index of pellets was examined by visualizing physical changes of pellet in a horizontal tube furnace. The results present that the reduction rate of oxidized pellets is increased with the increase of reduction temperature. While the swelling index is firstly increased and then decreased with the increase of reduction time and reduction extent, which can be ascribed to the disruptive stresses induced during the transformation of hematite to magnetite. The maximum swelling index is gradually increased with the increase of reduction temperature and CO content.IntroductionWith the rapidly development of iron and steel industry, direct reduction iron has been considered as one kind of high quality burdens in electric furnace steelmaking [1]. At present, ""Two-step"" coal-based direct reduction process, which employs oxidized pellets as raw materials, has been used in industrial production [2]. The reduction behavior of iron ore oxidized pellets has been becoming one of the most frequently studied topics in extractive metallurgy[3]. The heat and mass transfer in direct reduction processes results in a series of stepwise reduction reaction (hematite--magnetite--wustite--iron), accompany with the volumetric swelling of pellets[4]. A lot of literatures have been reported on the reduction model of ferrous oxides and swelling behavior of pellets. A. A. El-Geassy K, et.al [5-7] revealed that the reduction process was controlled by chemical reaction at early stage by employing pure Fe203 as raw materials and CO as reduction gas. Chen Y [8] made research on the reduction kinetics of porous oxidized pellets and obtained the rate constant and activation energy of at different reduction stage. In addition, the swelling and disintegration of iron ore pellets was affected by chemical composition of pellet and reducing parameters, which have been studied by numerous investigators [3,9, 1O]."

Jan 1, 2013

By Artur R. P. Junior Sergio, Pedro A. Netto, N. Monteiro, Foluke S. de Assis, Frederico M. Margem

Synthetic fibers are being replaced gradually by natural materials such as lignocellulosic fibers. Compared to synthetic fibers, natural fibers have shown advantages in technical aspects such as environmental and economic. So there is a growing international interest in the use of those fibers. The banana fiber presents significant properties to be studied, but until now few thermal properties on banana fiber as reinforcement of polyester matrix were performed. The present work had as its objective to investigate, by photoacoustic spectroscopy and photothermal techniques the thermal properties of diffusivity, specific heat capacity and conductivity for polyester composites reinforced with banana fibers. In the polyester matrix will be added up to 30% in volume of continuous and aligned banana fibers. These values show that the incorporation of banana fibers in the polyester matrix changes its thermal properties.

Jan 1, 2015

By M. Y. Mohassab-Ahmed

In an effort to develop a novel flash ironmaking process, the chemistry of selected slags was investigated. In different ironmaking processes, the molten bath (iron-slag bath) is expected to be in contact with gas atmospheres of H2/H2O, CO/CO2/H2/H2O, and CO/CO2. The latter was investigated to allow comparison with the blast-furnace conditions. The slag composition was selected to resemble that of the blast furnace with CaO/SiO2 in the range 0.8 to 1.4. The temperature range was 1550 to 1650°C. The oxygen partial pressure was maintained in the range 10-10 to10-9 atm. The effect of water vapor on the chemistry of the slag as well as the equilibrium reactions involving the slag has been studied for the first time. H2O dramatically affects the chemistry of the slag and strongly affect the phase equilibria in the slag as well as the equilibrium distribution of elements between slag and molten metal.

Jan 1, 2014

By Jinliang Zhang, Jian Pan, Deqing Zhu

"Limestone and burnt magnesite were added to vary MgO content and basicity (CaO/SiO2 ratio) of pellets for investigating their influences on the properties of specularite pellets. At fixed MgO content, the addition of limestone does not affect on the properties of green balls significantly. The addition of burnt magnesite has obvious influence on the quality of green balls, especially on the thermal shock temperature. Without burnt magnesite, the thermal shock temperatures are about 400°C, and, the thermal shock temperature increases to 600~630°C by adding burnt magnesite. For preheated pellets, when the burnt magnesite is added, the compressive strength will be decreased. For roasted pellets without burnt magnesite, the calcium additives can form binding phase of calcium-ferrite, and suitable liquid phase will improve recrystallization of hematite, but excessive liquid will destroy the structure of pellets, so the compressive strength of pellet increases firstly and then decreases. When adding burnt magnesite, the compressive strength will increase as the basicity increases. When the basicity is more than 0.2, the compressive strength of the pellets various MgO content and basicity is above 2500N/pellet and then MgO-bearing fluxes can be added to prepare pellets with good high temperature properties.IntroductionWith the rapid development of the steel industry in China, oxidized pellets, possessing good mechanical and metallurgical properties, are becoming indispensable burdens for blast furnace ironmaking [1-3]. However, this has resulted in the shortage of domestic iron concentrates, so many Chinese steel plants begin to use imported hematite concentrate to prepare pellets. Compared with magnetite pellets, the hematite pellets require high roasting temperature and narrow roasting temperature range (1300–1350°C) and possess low compressive strength [4,5].1"

Jan 1, 2012

By L. J. Davies

Refractories usage in furnaces for the extraction of nickel from both sulphides and lateritic ores is reviewed. Recent changes in raw materials and basic brick qualities developed to meet the increasing demands of existing and new processes are outlined. Examples of used brick examinations to establish mechanisms of wear are given. The importance of physical and chemical properties are discussed. The use of simulative laboratory testing to aid in refractories development and selection is described.

Jan 1, 1988

By Y. K. Rao

In the carbonyl process for the refining of crude nickel CO(g) reacts with nickel in the 310-370K range producing nickel tetracarbonyl, Ni(C0)4(g). Iron and cobalt impurities also form gaseous carbonyls but their partial pressures are low. The carbonyl is led to a decomposer plant wherein the gas disproportionates in the 500-600K range depositing pure metal on nickel pellets that move countercurrent to the gas-flow. This system serves to illustrate the fundamental principles involved in the vapor phase mass transport of elements, against temperature-gradient, under the influence of chemical potential gradient. Unlike in the crystal growth, the source is at a lower temperature (say 350K) whereas the seed is in the hot-zone (say 550K) of the closed ampoule-type reactor. By assuming virtual gas-solid equilibria in the end zones, with diffusion of gaseous species between them acting as a slight perturbation, the quasi-steady- state mass-transport rates are computed for a range of CO-pressures and temperatures.

Jan 1, 1993

Sanes are utilized to make molds for metal castings in the foundry industry. Approximately a half ton of sand is disposed of for each ton of metal cast in this country. The purpose of this investigation was to study and develop a process to separate chromite sand and silica sand from reclaimed sands for a steel foundry. Physical separations were utilized to yield silica and chromite sands with desirable molding properties. Several different separation methods, including electrostatic, magnetic, and various gravitational approaches were examined. Experimental results are presented. A method was developed to separate chromite sand from silica sand after mechanical or thermal reclamation. The reclaimed sands are passed through a rare earth magnetic separator to separate chromite sand and magnetic impurities from non-magnetic silica sand. Chromite sand can be recovered from magnetic silica sand or magnetic impurities very effectively using a wet concentrating table. The applicabilities of the separation methods are discussed.

Jan 1, 1995

By Robert Vidal

The performance of a laboratory-scale cell for the electrolysis of an aqueous chrome alum solution was studied. Electrode potentials, pH, and Eh were recorded. An optimum catholyte pH of about 2.5, consistent with information from the literature was observed. Values exceeding this range resulted in a precipitate formation and are detected by wavering cathode potentials. The role of anodically produced dichromate ions was investigated by chemical analysis. It was found that the steady state concentration of dichromate ions varies inversely with fluid flow from catholyte to anolyte. This concentration was also reduced with the use of precious metal coated titanium anodes.

Jan 1, 1994

By F. H. (Sam) Froes, C. Suryanarayana, K. C. Russell, C. M. Ward-Close

"Far from equilibrium synthesis allows development of novel crystal structures and microstructures, leading to achievement of enhanced physical and mechanical properties. A number of ""far from equilibrium"" techniques are reviewed with emphasis on the amount of departure from equilibrium. The ability of two such techniques, mechanical alloying (MAl, and physical vapor deposition (PVD) to develop novel structures are discussed in detail. For the MA process emphasis is placed on intermetallic compound compositions. Solubility extension, beyond rapid solidification (RS) levels, is found in terminal compositions but not for the intermetallics. Nanostructure-sized grains (< 100nm) form which can be retained after ""low temperature"" compaction. On continued milling in many cases the nanometer-sized grains transform to an amorphous structure. Ordering is destroyed by MA, except in those intermetallics with large negative enthalpies of formation. For the PVD process, a review of application to terminal light alloy compositions is presented. This includes a new high-temperature aluminum alloy, layered materials with nanometer spacing, corrosion-resistant magnesium alloys and low-density titanium compositions. IntroductionTo enhance the mechanical property combinations of advanced structural materials innovations in process/synthesis are required [1-6]. In this paper the capability of various ""far from equilibrium"" synthesis techniques [7,8] to produce novel constitutional and microstructural effects, and hence potentially enhanced physical and mechanical properties, in advanced materials is presented. The application of two such methods, mechanical alloying (MA) and physical vapor deposition (PVD) is discussed in detail. For the MA process emphasis is on intermetallic compositions with consideration given to solid solubility extension, microstructural refinement, amorphization, and formation of intermetallic compounds. For the PVD process application to terminal light alloy compositions is discussed."

Jan 1, 1994

By Djona M. Gaballah I.

Selective chlorination of unroasted and roasted spent hydrorefming catalysts was studied between 300 and 600°C using the following gas mixtures : C12+CO, C12+N2 and CI2+air. Such materials contain Co, Ni and Mo compounds supported by alumina and/ or silica. They also contain variable amounts of V compounds, C, S, etc., accumulated during the life time of the catalyst. Direct oxychlorination of the C+S rich sample allows higher extraction rates than those obtained by the carbochlorination of the same roasted one. It seems that the roasting step doesn&apos;t favor the economic metals&apos; recovery. Results of the chlorination of C+S poor spent catalysts, in the presence of CO, in the chlorinating gas mixture, or of carbon added to the sample, were comparable. Cobalt and nickel chlorides were .extracted from the chlorination residues by their dissolution with acidified water, whereas molybdenum and vanadium chlorinated compounds were recovered by selective condensation from the vapor phase. The recovery rates of valuable metals as well as the selectivity were higher for the chlorination of spent catalysts than results obtained by the hydrometallurgical processing of the same sample. Results of the scale-up of the oxychlorination of the unroasted sample confirmed those of the laboratory scale. The global recovery rates were about 88 pct of cobalt, 93 pct of molybdenum and 76 pct of vanadium. The carbochlorination was applied to the recovery of W and Ti from Denox catalyst that is a carbon and sulfur free one. Recovery rates higher than 99 pct at temperatures lower than 500 °C could be obtained. This may indicate that the chlorination process can be applied to the treatment of various industrial wastes or by-product containing transition and/or refractory metal compounds A flow - sheet for the pretreatment of these materials is proposed.

Jan 1, 1995

By Huimin Lu, Shi Zhou, Lisha Yang

"The Zeolitic imidazolate frameworks (ZIFs) were successfully synthesized by applying a combination of ionothermal synthesis and microwave energies for rapid synthesis. The synthesis was proceeded under various conditions including different raw materials, reaction temperature as well as microwave irradiation time. Zeolitic imidazolate frameworks (ZIFs), also known as coordination polymers, are new type of porous materials formed by inerratic polyhedral in three-dimensional. They are the ideal crystalline substances for gas separation and storage. The assynthesized samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), thermal gravimetric analysis (TGA) and C02 adsorption test. Results illustrated that the synthesized samples had stable structure, high thermal stability (up to 530 °C) and C02 adsorption capacity (10.2 cm3/g at 0°C under ambient pressure). This novel method also showed great advantage with high energy efficiency, safe synthesis conditions, and rapid crystallization time (60 minutes).IntroductionNowadays, carbon dioxide capture has become imperative due to the global warming caused by the increase of C02 in the atmosphere, especially produced by the concentrated sources such as power plants [1]. Zeolitic imidazolate frameworks (ZIFs), also known as coordination polymers, are ideal crystalline substances for gas separation and storage due to their structure diversity, high thermal and chemical stability [2-5]. They are formed by inerratic polyhedra in threedimensional with large cages and small apertures. Traditionally, ZIFs are synthesized by solvothermal method in a sealed autoclave under autogenous pressure [6-9]. However, in order to generate the products, the solvothermal temperature should not be lower than 100°C according to the sovlothermal mechanism. Moreover, at such a temperature, molecules with a low boiling point (such as water) may generate high pressure in reactor which might cause danger [9]. Thus the synthesis requires the equipment to possess resistance to autogenous pressure and corrosion. Further, conventional solvothermal methods need a long time to prepare products, usually a few days, which is a large energy consumption and inefficiency. So it is interesting to synthesis ZIFs through other ways under mild reaction condition with high energy efficiency."

Jan 1, 2012

By William Petruk, J. H. Gilles Laflamme, Jean Robitaille, Louis J. Cabri

"A quantitative mineralogical study using ore microscopy, electron microscopy, proton-microprobe, image analysis, and material balances was done on samples from the circuit of a concentrator in Quebec, with particular emphasis on the Cu concentrate. The ore contains many different minerals, of which the principal ones, in decreasing order of abundance, are pyrite, sphalerite, chalcopyrite, bornite, galena, tennantite, and pyrrhotite. Minor to trace amounts of covellite, chalcocite, stannoidite, mawsonite, colusite, wittichenite, miharaite, hessite, petzite, electrum, and an unidentified Cu-Pb-Bi-sulfide also occur.Liberation of pyrite is very high in all size fractions for all samples (ranging from 80-91 %). Liberation of chalcopyrite, bomite, sphalerite, and tennantite is relatively high, on average, in the head .sample and Cu concentrate (55-78% and 66-88%, respectively). Most of the chalcopyrite in the flotation tails is not liberated, whereas about one half of the tennantite and sphalerite are liberated in both the flotation and :final tails. Recoveries calculated for the Cu concentrate (on the basis of assays, mineralogy, and image analysis) are chalcopyrite 72. 5%, bornite 73. 7%, sphalerite 41.0%, tennantite 70.9 %, and galena (together with some trace minerals) 34.2%. It was also calculated that the Cu concentrate contains 10.0 % of the pyrrhotite and i.4 % of the pyrite.Materials balance calculations were done on the five major sulfide minerals to determine the mineralogical distribution of 13 major, minor, and trace elements (as determined by protonmicroprobe analyses). It was determined that tennantite is the principal carrier of Bi (67%), As (90%), and Te (86%) in the Cu concentrate. Therefore, removal oftennantite, which is mostly liberated in the Cu concentrate would significantly reduce these three contaminant elements, but at a loss of9% of the Cu, 2.0% of the Zn, and 0.7% of the Ag. The precious metals (Au, Ag) occur as discrete minerals (electrum, petzite, hessite). Some of the Ag also occurs in solid solution in bornite (23.1% of Ag in Cu concentrate), tennantite, and sphalerite. Four of the major sulfides (chalcopyrite, bomite, sphalerite, tennantite) in the ore also contain measurable concentrations of the following trace elements: Se, Cd, In, Sn, and Sb, occurring mostly as solid solutions. Some of these elements are also concentrated (up to about 18%) in minor and trace minerals such as colusite, stannoidite, and mawsonite."

Jan 1, 1999

By José Brant, Douglas Torres, Rogério Navarro, Rodrigo Souza, Eduardo Brocchi

The steelmaking process requires the input of ferro-alloys to implement the adjustment of some elements composition in the final product. In the particular case of stainless steel production, the high carbon FeCr alloy stands out as one important precursor. However in the production of this material a certain quantity of fine powder with remarkable chromium and carbon content is also generated, which, in turn, could be processed through alkaline roasting in order to selectively recovery this element in a subsequent aqueous route. In the present work, this process is investigated, using excess of NaOH as oxidizing agent, and H2O2 for precipitating chromium as Cr(OH)3, which is next calcinated to Cr2O3. According to the results, the global achieved recovery has shown to be around 98%, suggesting that the proposed route can be seen as a potential process for chromium oxide production from the mentioned fine powder.

Jan 1, 2015

By Qian Li, Li-chen Hou, Yong-bin Yang, Tao Jiang, Jian-jun Hu, Bing Xu

Extraction of gold from refractory gold concentrates usually requires an oxidation step to remove arsenides、sulphides and carbonaceous matter. In this investigation, the gold concentrates were two-stage roasted under different atmospheres and temperatures. Results indicated that at the first stage, under neutral atmosphere, the removal rate of arsenic increases as the temperature rises. Under the oxidizing atmosphere, with the increase of temperature, arsenic content in the residued calcine increases, in addition, the volatilization of arsenic is also affected by the oxidation of carbon that generated CO, which is advantageous to the decomposition of arsenate decomposition. At the second stage of roasting, it is the higher temperature and stronger oxidizing atmosphere, the faster sulfur and carbon oxidated rate is, but at the same time, the calcine appears the phenomenon of consolidation because of the phase of silicate compounds generate.

Jan 1, 2015

By L. Lü, M. O. Lai

"Mechanical alloying is a dry, high energy ball milling process which has been used to synthesize metallic powders in the solid state. The present study use this technique to synthesize Cu-base shape memory alloy powder from commercial Cu70Zn30, Cu86Zn14 and element AI powders. The evolution and formation of shape memory alloy powder were monitored using X-ray diffraction and microscopy. It was observed that shape memory alloy powder started to form after 1.8 ks of mechanical alloying. ? phase was clearly detected after 3.6 ks of mechanical alloying. The intensity of X-ray diffraction of the y phase increased when mechanical alloying duration was prolonged indicating an increase in the amount of y phase. Microstructure observation showed different stages of formation of alloyed powders: welding between powders and formation of layered structure, deformation and fracturing of layered structure, and finally the formation of alloyed powders.IntroductionMechanical alloying (MA) is a process used for producing powders with controlled and extremely fine microstructure. It was original developed in 1966 (1) to produce aNi-based superalloy combining oxide dispersion strengthening with gamma prime precipitation hardening. In recent years this technique has been used in producing a wide range of materials including intermetallic compounds (2, 3), amorphous materials (4-6) and other materials (7-9). In MA, a blend of powders is subjected to highly energetic compressive collision. The powder panicles are welded and fractured during ball milling. Therefore, it is essential that at least one of powders should be ductile to act as combiner. It has however been found that brittle components without soft element can also be mechanically alloyed (10), even ceramic powders (11).The present work aims to study the mechanism of formation of shape memory alloy powder during MA."

Jan 1, 1994

By Eva B. Kisvarsanyi

An Early Proterozoic orogenic terrane of metasedimentary and metaigneous rocks underlies Nebraska, Kansas, and Missouri. Middle Proterozoic epizonal terranes of anorogenic granite and rhyolite, a known metallogenic province partly exposed in southeastern Missouri, overlap the orogenic terrane on the south. These Proterozoic terranes, covered by less than 1,000 meters of Phanerozoic strata, contain a virtually untapped source of mineral wealth and are one of the last frontiers for geologic exploration in the continen-tal United States. Petrographic study of subsurface samples is a powerful tool in the identification of favorable host rocks for a variety of ore deposits.

Jan 1, 1987

By Jose Bengoa

Low metal prices and environmental restrictions are always a challenge for copper smelters operation and its productivity. Thus, in order to reduce production costs and control gas emissions, improvements of the Teniente Converter (CT) operation were made at 110 Smelter Plant of Southern Peru Copper Co., 110, Peru, and the main objective was to increase its capacity for smelting copper concentrates without affecting normal operation. The present work corresponds to a recent study conducted during the normal industrial operation of the Teniente Converter in this plant and, it shows the effect of increasing air oxygen enrichment from 28 to 34% on its productivity. The results show an increasing of concentrate smelting rate from 800 to 1370 tpd and hence a notorious improving in copper production, and practically no effect on the refractory consumption. The increment of the concentrate throughput, increases also the SO2 concentration and the sulfuric acid production, showing the effort done by this operation in order to accomplish the environmental Peruvian regulation.

Jan 1, 2003