Examination of tensile bar surfaces shortly after destructive testing was conducted to search for clues that would aid in optimization of mechanical properties, especially tensile strength, yield strength and elongation to fracture. Cu-Ni-Si-Cr alloy bars in the as-cast, forged, rolled and extruded conditions were examined. Low ductility bars (<4% Elongation) showed dramatically different features than the fracture surfaces of high strength - high ductility bars (7 to 10% Elongation). Analysis of the fracture surfaces at 15X to 2000X and use of Energy-Dispersive X-Ray Spectroscopy (EDS) identified Ni-Si and Ni-Si-Cr precipitates of varying sizes and morphologies. Thermo-mechanical processing techniques to control the size and distribution of these precipitates show promise in improving the properties and performance of this alloy system and appear to correlate with improvements in the fracture surface morphology.

Jan 1, 2008

By B. Mishra

Several reactive metal purification processes using molten salts generate effluent from which significant quantities of metal can be recovered prior to discardinglrecycling the salt. A Salt-scrub [SS] process has been applied where the reactive metals are recovered as a metal-gallium alloy by calciothermic reduction of the metal compounds. The SS alloy compositions were produced by mixing, pressing and sintering the metal-powders. Measurement of metal recovery has been studied for cerium, silver, tin and lead. The process has been optimized for variables such as the metal quantity per kg of effluent salt, amount of excess calcium over stoichiometry, stirring rate and time and holding time at reduction temperature. Over ninety-seven percent metal recovery has been obtained under optimized conditions. The development of an alloy for efficient Salt Scrub processing reduces a major contaminated waste disposal problem as well as recovering the valuable reactive metal. Surrogate metals have been used in this work to study the behavior of plutonium.

Jan 1, 1994

By Y. Ono

In lightweight metal processing such as aluminum (AI) and magnesium (Mg), metal cleanliness is a crucial process parameter for refining, part manufacturing and recycling in order to obtain high quality parts and products. In this paper, techniques for cleanliness evaluation of molten AI and Mg using ultrasonic probes with clad steel buffer rods having high signal-to-noise ratio (SNR) are presented. Due to the high SNR of the ultrasonic probes used, backscattered ultrasonic signals from inclusions, which may be oxide films and/or particles, in molten Mg and those from silicon carbide particles, having an average size of 50f.Ull, added in molten AI are successfully detected with reflection configurations of pulse-echo and/or pitch-catch modes at an ultrasonic frequency of 10 MHz. In addition, relative cleanliness evaluation of molten Al and Mg is demonstrated. In order to establish the procedure and to investigate the optimum system configurations for cleanliness evaluation of molten metals, particle flow simulation system using water and polyvinyl chloride (PVC) particles has been constructed. Counting the number and measuring the size distribution of the PVC particles, having an average diameter of 128um, suspended in water with the PVC volume concentrations of 5ppm and 10ppm are performed with ultrasonic pitch-catch mode. The counted numbers of particles by the presented method and system have good agreement with the calculated results with a count error of less than 10% or two counts. Based on the results obtained with water simulation experiments, the prototype system for cleanliness evaluation of molten Mg by counting and sizing inclusions has been developed. Keywords: Ultrasound, Clad buffer rod, Molten metal, Aluminum, Magnesium, Inclusion detection, Cleanliness measurement, Counting, Sizing

Jan 1, 2003

By M. Waladan

The top submerged lancing Sirosmelt system has been developed through laborator.y scale testwork and pilot plant trials for recovery of zinc from ISF slag. The effects of the process variables of gas injection rate, method of coal feeding, and temperature on zinc fuming rates were studied in the laboratory. It was found that the rate of zinc elimination was dependent on all of these variabl.es. The rate of zinc removal from slag was independent of zinc content of slag down to approximately 1.5% Zn, below which the rate was proportional to zinc content in slag. Pilot plant trials were carried out to evaluate a proposed process and results followed predictions from the laboratory scale tests. A comparison of the proposed process with conventional slag fuming operations is made and it is shown that the process has a number of advantages which have a significant impact on the economics of zinc slag fuming.

Jan 1, 1990

By Nathanael Hudson, Ruel A. Overfelt, Sushil H. Bhavnani

"In the aerospace and automotive industries, complex shapes exist which require casting. The problem with these cast parts is the empiricism required to develop the casting process and the accompanying time and expense to develop that process.There has been an interest in using fluidized beds to allow molding sand to better encapsulate the complicated surface geometries of lost foam patterns. Fluidization coupled with a mixing jet helps to homogenize the sand through stirring and may improve the integrity of the casting.At issue is the hydrodynamics of the sand and air around the foam pattern. The commercial package PHOENlCSTM is used to simulate the flow around the pre-casting foam geometry. Employing a two fluid approach, each component is considered a fluid that interpenetrates the other phase. To this end, the kinetic theory of granular 'flow for the sand phase was incorporated into the re-compilable PHOENlCSTM code.The results of this study consist of time-averaged void fraction patterns, with voidage being defined as the fraction of air in the mixture, around the foam pattern submerged in a two-dimensional fluidized bed. The model was benchmarked against past fluidized bed experiments. In order to better understand the dependence of the void fraction pattern around the lost foam pattern, certain physical parameters are varied and the resultant void fraction maps are predicted with the model. Physical parameters such as the aspect ratio of length to width, the placement of the mixing jet, and different mixing jet velocities are varied to illustrate the dependence of the time-averaged void fraction on those variables.Results consistently indicate the presence of channeling around the lost foam pattern, with the extent of the channeling and void formation reliant to a greater degree upon the placement of the mixing jet, and to a lesser degree on mixing jet velocity and aspect ratio.The increase in radial position of the mixing jet from the bed centerline had the desirable effect of granting the churning benefits of a penetrating jet, while at the same time minimizing the formation of excess void fraction at the top of the pattern."

Jan 1, 2001

By C. D. Adams, R. T. Tuenge, C. N. King, J. A. Samuels, B. F. Espinoza, R. C. Dye, C. F. Schaus, D. C. Smith, N. M. Peachey

"Recently, doped calcium thiogallate (CaGa2S4) phosphors have been investigated for use in electroluminescent flat panel displays. The current technique used for the deposition of thin film calcium thiogallate is sputtering. Unfortunately, this requires a high temperature annealing process to provide the desired crystallinity of the phosphor. Recent efforts have focused on the possible use of metal-organic chemical vapor deposition (MOCVD) to produce the CaGa2S4 layer. The use of MOCVD provides an attractive alternative to sputtering since it does not require heating above the strain point temperatures of the glass substrates used for the display panels. To accomplish this, the deposition of both Ga2S3 and CaS is investigated as these compounds are intermediate steps in the development of the phosphor deposition. Uniform, crystalline films of both Ga2S3 and CaS were deposited and the process shows promise for successful deposition of the CaGa2S4 phosphor.IntroductionThe lack of a satisfactory blue phosphor having sufficiently high luminances at low power has hampered the development of high resolution flat panel displays. Recently, a new series of blue emitting materials have been investigated for use in thin film electroluminescent (TFEL) devices. l ,2,3 These phosphors are based on a series of alkaline earth thiogallate host materials of the form MGa2S4:RE where M can be either calcium, strontium, zinc, or barium and RE is a rare earth ion. A full-color VGA TFEL panel using CaGa2S4:Ce as the blue phosphor has recently been fabricated and tested. l This FPD provided a luminance of 10 cdlm2 at 60 Hz. The enhanced blue in this display allowed its color capabilities to approach those of the conventional CRT.The method of depositing the phosphor onto the display panels in these test devices has been sputtering. Unfortunately the phosphor as deposited does not possess the crystalline properties required for optimum luminance. The crystalline structure is achieved by subsequent annealing of the deposited material. Although this post deposition anneal provides the desired crystal structure, it occurs above the strain point temperature of ordinary glass. Consequently, the implementation of these phosphors requires the use of glasses capable of withstanding high temperatures, adding to the cost of the final display unit."

Jan 1, 1994

By Dirk Verhulst

The Altair process employs digestion of ilmenite ore in concentrated hydrochloric acid, solvent extraction to concentrate Ti in a purified stream and spray hydrolysis to produce a TiO2 hydrate, followed by final calcining and milling. HCl gas is regenerated by pressure-swing distillation and reinjected in the leaching solution. All chloride streams are recycled. Chromium compounds generally remain in the residue. Solvent extraction provides flexibility for the removal of naturally occurring radioactive elements (NORMs) present in some ilmenites. The process was previously tested at a 5 t/day feed scale. Recent work at pilot scale (40 liter reactor) led to further improvements. Recovery of Ti in solution is now at least 90% with ilmenite ores, while crystallization at lower temperature lowers the amount of Fe in solution to about 5 g/l and improves solvent extraction, which is now conducted in columns. Higher Ti and lower Fe concentrations in the SX eluate improve the economics. A new formula for pigment production via spray hydrolysis produces a pigmentary base with a narrow particle size distribution.

Jan 1, 2003

By J. J. Kim

In a study of buildup in a green-feed reverberatory furnace, it was determined that approximately half of the crucible area has a moderate buildup of 25 in. or less, and that the area extending 45 f t from the burner end of the furnace has only a slight buildup. The false bottom, averaging 6 in. in thickness, was found to cover the entire crucible area. The stratification of Cr2O3, A12O3, and SiO2 occurs throughout the slag layer; this phenomenon is the principal reason for the formation of the false bottom in the green-feed reverberatory furnace. The false bottom is caused primarily by the settling of FeO*(A1,Cr),03 aggregates, which are derived mainly from returned converter slag. The false bottom can be transformed to a solid permanent buildup in the furnace, particularly when the matte is completely withdrawn. From the material balance of Al2O3 and Cr2O3 around the furnace, It is estimated that the average rate of aluminum chromite accumulation is approximately 0.3 ton per day or less.

Jan 1, 1976

By William Petruk

The mineralogy of the primary and oxidized ores from the Malanjkhand porphyry copper deposit in India was studied to determine ore characteristics that affect metallurgy, and to assess applicable processes for recovering the copper. Three mineral assemblages were found. One occurs in primary ore, another in moderately oxidized ore, and a thir:d in intensely oxidized ore. Chalcopyrite, the main mineral in the primary ore, is relatively coarse-grained, with grain size increasing as the ore grade increases. High chalcopyrite liberations should be achieved at a relatively coarse grind, and good chalcopyrite recoveries should be obtained. The chalcopyrite, however, tarnishes readily and oXidizes to chalcocite in a relatively short time (several months). The presence of both the tarnished chalcopyrite and chalcocite may affect chalcopyrite flotation and reduce copper recoveries, The moderately oxidized ore occurs in an oxidized cap immediately above the primary ore, and stockpiled primary ore alters quickly to a moderately oxidized ore. Chalcocite is a major copper-bearing mineral in moderately OXidized ore. The concentrator processing this ore should be capable of handling a chalcocite-rich ore. The intensely OXidized ore contains a wide variety of acid-soluble copper-bearing minerals. Leaching may be required to recover the copper from them.

Jan 1, 1987

By A. Van den Steen

In the early fifties Professor Breckpot of the Louvain University in Belgium in collaboration with the Research Laboratory of Metallurgie Hoboken, discovered the possibility to separate nickel from cobalt sulfate solutions by a nickel sulfide depolarized cementation. This reaction, completed later with a zinc precipitation, was developed into purification processes for the Shituru and Luilu Gécamines cobalt plants in Zaíre. Due to increasing demand for higher quality products and the necessity of lowering the production costs, more laboratory and pilot plant investigations concerning the key parameters for the nickel and zinc sulfides precipitation were under- taken. Especially the relative stabilities of cobalt, nickel and zinc sulfides, precipitated with elemental sulfur or sodium hydrosulfide, were examined in relatlon with the pH and with the redox potential. These investigations have led to better plant practice and new development possibilities. The valorisation of the precipitated sulfides has also been considered.

Jan 1, 1988

By Chunyang Guan, Jilai Xue, Jun Zhu, Qiaochu Liu

"Al-Sc Alloys have showed many advanced properties for a wide range of industrial application, which is usually produced using thermal reduction process. This work is aimed to develop an electrochemical process to make Al-Sc alloy using industrial Hall aluminum reduction cells. The experiments have been carried out in a lab cell where NaF/AlF3-Al2O3-LiF as electrolyte, Sc2O3 as raw material, and liquid aluminum as cathode were used at operating temperature of 950 °C. The resulting Al contained 0.2 - 0.5 wt.% Sc that is the common range in its content for advanced applications. However, a small fraction of Sc was found from thermal reduction at Al melts interface. SEM-EDS and ICP-AES analysis showed a uniformed distribution of Sc at varying locations of the Al-Sc alloy sample. In addition, a higher Sc content in Al-Sc alloy can be obtained with introducing ultrasound through the cathode than that without it.IntroductionIn recent years, scandium has been investigated as an alloying element for aluminum alloys. With addition of a small amount of Sc, Al alloys can improve the strength, weld ability, resistance to re-crystallization and corrosion resistance [1-3]. Due to their advanced properties and potential applications, the demand for Al-Sc alloys will increase in the future. However, the difficulties in reduction technologies and the high costs in production process may limit their expansion in application areas.The current major method of producing Al-Sc alloys is to mix Sc into Al by melting Al-Sc master alloy. This alloying process has several technical problems, such as easy segregating and heavy burning loss, etc. The price of Sc metal or starting material is also high, so the mixing process is an expensive alloying method. Molten salt electrolysis is alternative method to prepare RE metal and RE alloys [4, 5]. It also can reduce the segregation of alloying elements. Sc2O3 is an ideal material as raw material with low price and decomposition voltage. Some work has proved that Al-Sc alloys can be obtained by electrolysis Sc2O3 directly in cryolite [6-8], or CaCl2 molten salt [9]."

Jan 1, 2012

By Batric Pesic

The interactions of mineral-pyrite with T. ferrooxidans were studied by using a cyclic voltametry technique. The interactions with bacteria were carefully examined during the entire growth stage of bacteria (fermentation). Several very important discoveries were made. For example, the pyrite surface invariably drastically changed its properties at the second day of fermentation. Beyond two days of fermentation, the cyclic voltamograms were insensitive to convective diffusion produced by stirring. The SEM study revealed that bacteria populated the pyrite surface at an extremely high density levels. The high density of bacteria, and the solid reaction products formed on the pyrite surface created conditions for pore diffusion which explained why the CVs became insensitive to convective diffusion in solution (stirring).

Jan 1, 1990

By Yin Zhang, Xiaoyu Huang, Mi Wang, Bencheng Du, Youduo He

"Burners are important facilities for blast furnace stoves to raise hot-blast temperature up to 1200°C. Common types of two-ring ceramic burners have very long flames so that part of combustion occurs in the upper part of the chequers and will cause damage to the refractory materials. Using computer simulation to analyze the turbulent diffusion flame in the combustion chamber, some good results were obtained. A new type of ceramic burner will be installed by Anshan Steel Complex in stoves of blast furnace number 4. A pilot experiment was done on the new burner. The experimental data have shown that the mixing condition was improved and the length of flame was shorter with the new type of ceramic burner.IntroductionPulverized-coal injection can give significant operating saving, reducing coke rate in blast furnace(BF) operation. However, during high rates of coal injection, extra heat must be compensated in hearth to maintain certain raceway adiabatic flame temperature. One of the effective methods for heat compensation is to raise hot-blast (HB) temperature up to 1200°C. Nowadays, since the fuel being combusted in stoves is BF gas only, in which the calorific value is down to round 3000 kJ/m3 , to increase the combustion ability and to provide a suitable length of flame in combustion chambers of stoves becomes more important. In other words, designing a good ceramic burner which will affect to HB temperature and stove lifetime is drawing more attention."

Jan 1, 1999

By A. H. Rhoades

The modern polarizing microscope with such accessories as cameras, infrared devices, reflectance and/or transmission photometers, indention hardness, and heating stage is used to characterize coal, coke, and other carbon forms. It allows characterization of coke by-products, such as tars and pitches and their insoluble residues. A useful product of the microscopic approach is the coal petrographic analysis which permits the prediction of coke strength carbonization pressure and volume change. Carbonization tests are expensive, time-consuming and require large amounts of coal. Tests on the coke show it to be strong or weak but give no indication of why. Petrographic analysis requires grams of coal and yields data that indicates why the coal produces coke of a given quality. Small samples from drill cores are sufficient for petrographic analysis. These data are also used to optimize blends for coke production. When coke-plant problems occur, ~he microscope can be used to check the coal blend proportions, as well as for weathered coal. Microscopy is useful in spore correlation work which may be a prerequisite to sound coal reserve estimates. Dispersed vitrinoid reflectance studies are used to determine the degree of organic metamorphism which serves to establish oil and gas deadlines. Tars and pitches are examined microscopically for the amount of normal solids as well as the size of undesirable carry-over solids resulting from pollution abatement practices in coke works. The microscope is also used to study coals for gasification and liquefaction.

Jan 1, 1981

By Saeid Pournaderi, Ahmet Geveci, Ender Keskinkilic, Yavuz A. Topkaya

There are mainly three commercial nickel laterites in Turkey: Gordes, Caldag and Sivrihisar. The first two appear in Western Anatolia. The third one, Sivrihisar (Yunusemre) laterites have been found in the first decade of the millennium, in the Central Anatolia region of Turkey. Since then, mining facilities have been continued in Yunusemre. Calcination, prereduction and smelting of Sivrihisar laterites have been extensively studied and published. In the current work, some results of the studies related to characterization of Sivrihisar laterites will be presented.

Jan 1, 2016

By John W. Lund

The Geo-Heat Center has been investigating the utilization of waste silica from the Cerro Prieto geothermal field for several years. The main objectives of the research were to com-bine silica with various additives to (1) form bricks for low cost housing, and (2) to produce a suitable road surfacing material. The various additives that were tested included hydrated lime, portland cement, plastic fibers, asphalt cement and emulsified asphalt. The silica-cement combination produced the strongest bricks and had the best weather resistance, whereas, the silica-lime combination produced the bricks with the lowest thermal conductivity and specific gravity density. The addition of plastic fibers to the silica-lime mixture improved both strength and weather resistance. The combination of asphalt and silica is not suitable as a road surfacing material, however, silica-cement appears promising.

Jan 1, 2006

By S. Ozbilen

"Al-Li binary alloys with nominal Li contents of0.15, 1.1and2.8 (in wt%) were aged naturally at room temperature for two months, aged at low temperatures ( 65 and 1 OOEC) for up to 2 months and aged artificially at 190EC for 4 days after water quenching to 25EC following solutionizing at 530EC for 20 minutes. Ageing behavior of these binary alloys were studied by Vicker's Hardness measurements and DSC thermal analysis. Thermal analysis results indicate the formation of GP zones of Al-Li system in Al-2.8wt%Li binary alloy. In the same alloy, rapid quenching from one phase region (a) gives rise to precipitation of small o' particles in a matrix (a) with still high supersaturation. During ageing of this alloy below lOOEC an additional transformation, i.e., GP zone formation occurs proceeding at a very high rate which is described on the basis of the theoretical analysis for the quenched Al-Li system proposed by Khachaturyan et al [6]. Ageing at temperatures below 11 OEC takes place slowly by the formation of small d' particles of lower thermal stability than the quenched-in d precipitates in addition to GP zones resulting in an increase in hardness compared to water quenched samples. During artificial ageing, GP zones transform by dissolution to d' precipitates while d' particles already in the microstructure coarsen during under aged condition at which hardness increases with time till peak aged condition.IntroductionIn binary Al-Li alloys the d' (Al3Li) fully coherent internally ordered inetastable phase of Li2 structure with a=0.4038d [1-5] forms homogeneously between 120 and 190EC before the formation of stable d' (A!Li) phase and cause the superior mechanical properties. This is due to an appreciable age hardening effect resulting because of the d' precipitation during ageing [1]. The response of d' to decomposition and its formation kinetics have been studied previously and it is believed that the decomposition of the a-supersaturated solid solution occurs in a two stage process; i.e., a 6 d' (Al3Li) 6 d(A!Li). Khachturyan et al [6] theoretically investigated precipitation of the d' phase and gave an interpretation of the transformation paths of the quenched Al-Li alloys. They predict that the disordered supersaturated solid solution congruently orders, and then the uniformly ordered solution decomposes into ordered regions that differ in Li-content. Finally, ordered d' phase forms in the disordered matrix."

Jan 1, 1998

By Joo Hyun Park, Soo Sang Park

The distribution behavior of Pb between molten copper and FetO-SiO2 (-CaO, Al2O3) slags was investigated at 1473 K (1200 oC) and p(O2)=10-10 atm in view of the reaction mechanism of Pb dissolution into the slag. The distribution ratio of Pb (LPb) decreases with increasing CaO content (~6 mass pct) irrespective of Fe/SiO2 ratio (1.4~1.7). However, the addition of alumina into a slag with Fe/SiO2=1.5 linearly decreases the LPb, whereas a minimum value is observed at about 4 mass pct Al2O3 at Fe/SiO2=1.3. The log LPb continuously decreases with increasing Fe/SiO2 ratio, and the addition of Al2O3 (5 to 15 mass pct) into the silica-saturated iron silicate slag (Fe/SiO2 < 1.0) yields the highest Pb distribution ratio. The log LPb linearly decreases by increasing the log (Fe3+/Fe2+) value. The Pb distribution ratio increases and the excess free energy of PbO decreases with increasing Cu2O content in the slag. However, from the viewpoint of copper loss into the slag, the silica-saturated system containing small amounts of alumina is strongly recommended to stabilize PbO in the slag phase at a low Cu2O content.

Jan 1, 2014

By U. Lauwers

The influence of different waste materials in sinter blends on the quality and mineralogical composition of a sinter is described. As a result of partial preservation of the original textures of waste materials in the final product the degree of assimilation of the original material in the sinter product can be ascertained. Recycling of waste materials such as dolo char , arc-furnace slag, scrap fmes, mill scale and BOF-mud via the sintering process a saving on costs of raw materials such as flux and fuels, and a reduction on pollution can be achieved. A comparison of a typical sinter with a sinter produced through the utilization of waste materials showed a distinct correlation between certain types of waste material and some metallurgical properties. Dolochar in a sinter blend acts as part of the fuel and flux that are normally added to a sinter mix. Generally dolochar improves the quality of the sinter and decreases the consumption of coke. Other waste materials adversely influence the quality of the sinter. The glass and calcium ferrite content of a sinter when dolochar is used in the blend is similar to that of a sinter produced with only coke as a fuel in the sinter mix. The glass content is lower and the calcium ferrite content is higher, in a sinter produced from dolo char in the blend compared to a sinter produced with additions of other waste materials. Changes in the mineralogical composition are related directly to the metallurgical properties of the sinter product.

Jan 1, 1991

By J. L. Jambor

Sulfide-rich tailings accumulated in a 4l-hectare impoundment at the Waite Amulet minesite near Noranda, Quebec, have undergone partial oxidation and destruction of the principal sulfides (pyrite and pyrrhotite) in the vadose zone. Mineralogical studies and whole-rock chemical analyses of 18 samples from 3 boreholes along a cross-section of the tailings pile indicate that the principal chemical manifestations of the alteration are a pronounced depletion in sulfide-sulfur, and an enrichment in total Fe as Fe203&apos; Other elements such as Al, Mn, Mg, Ca, Na, and K in the solids show erratic or inconsistent variations, but a trend to Si enrichment in the oxidation zone is clear. The trend is interpreted to be a relative enrichment whereby the proportion of the stable silicate minerals has increased as a consequence of the consumption of pyrite and pyrrhotite in the oxide zone.

Jan 1, 1989