This symposium is dedicated to the lifetime achievements of Professor H.Y. Sohn. It covers the scientific fields, processing routes and investigation techniques in which Prof. Sohn has worked during his career and is based in the equally important three topical areas: Principles, Technologies, and Industrial practice. Professor Sohn was General Chair of the very first TMS Fall Extraction and Processing Symposium in 1983 in San Francisco which led to the Annual such symposia as this International symposium. Furthermore, the theme of that symposium was sulfide smelting, which is also included in this symposium. [ ] Professor Sohn was born in a beautiful dynastic capital Kaesung, Korea on August 21, 1941. He received his B.S. degree in 1962 from Seoul National University, M.Sc. in 1966 from the University of New Brunswick, Fredericton, N.B., Canada, and his Ph.D. degree in 1970 from the University of California at Berkeley all in Chemical Engineering. After working as a Research Associate at the State University of New York at Buffalo and as a Research Engineer at Du Pont?s Engineering Technology Laboratory, Dr. Sohn joined the Department of Metallurgical Engineering at the University of Utah in 1974 and currently holds the ranks of Professor of Metallurgical Engineering and Adjunct Professor of Chemical Engineering.

Jan 1, 2006

This symposium is dedicated to the lifetime achievements of Professor H.Y. Sohn. It covers the scientific fields, processing routes and investigation techniques in which Prof. Sohn has worked during his career and is based in the equally important three topical areas: Principles, Technologies, and Industrial practice. Professor Sohn was General Chair of the very first TMS Fall Extraction and Processing Symposium in 1983 in San Francisco which led to the Annual such symposia as this International symposium. Furthermore, the theme of that symposium was sulfide smelting, which is also included in this symposium. [ ] Professor Sohn was born in a beautiful dynastic capital Kaesung, Korea on August 21, 1941. He received his B.S. degree in 1962 from Seoul National University, M.Sc. in 1966 from the University of New Brunswick, Fredericton, N.B., Canada, and his Ph.D. degree in 1970 from theUniversity of California at Berkeley all in Chemical Engineering. After working as a Research Associate at the State University of New York at Buffalo and as a Research Engineer at Du Pont?s Engineering Technology Laboratory, Dr. Sohn joined the Department of Metallurgical Engineering at the University of Utah in 1974 and currently holds the ranks of Professor of Metallurgical Engineering and Adjunct Professor of Chemical Engineering.

Jan 1, 2006

By John B. Cocanour

The U.S. Bureau of Mines (USBM) has developed a laboratory-scale on-line analysis and process control system for a decopperization electrolytic circuit. This system is software driven, running on a 486DX-33 personal computer (PC) utilizing a portable energy- dispersive x-ray fluorescence (XRF) spectrometer as the sample analyzer. The XRF copper reading obtained was used as the control variable through an RS-232 serial interface to the PC for software-based control of feed flowrates. When the copper concentration in the electrolytic cell (as measured by the XRF) deviated from the set point, the feed flowrate to the cell was automatically altered using software-based proportional-integral-differential (PID) computer control to yield the desired copper concentration at the electrolytic cell outlet.

Jan 1, 1994

This symposium is dedicated to the lifetime achievements of Professor H.Y. Sohn. It covers the scientific fields, processing routes and investigation techniques in which Prof. Sohn has worked during his career and is based in the equally important three topical areas: Principles, Technologies, and Industrial practice. Professor Sohn was General Chair of the very first TMS Fall Extraction and Processing Symposium in 1983 in San Francisco which led to the Annual such symposia as this International symposium. Furthermore, the theme of that symposium was sulfide smelting, which is also included in this symposium. [ ] Professor Sohn was born in a beautiful dynastic capital Kaesung, Korea on August 21, 1941. He received his B.S. degree in 1962 from Seoul National University, M.Sc. in 1966 from the University of New Brunswick, Fredericton, N.B., Canada, and his Ph.D. degree in 1970 from theUniversity of California at Berkeley all in Chemical Engineering. After working as a Research Associate at the State University of New York at Buffalo and as a Research Engineer at Du Pont?s Engineering Technology Laboratory, Dr. Sohn joined the Department of Metallurgical Engineering at the University of Utah in 1974 and currently holds the ranks of Professor of Metallurgical Engineering and Adjunct Professor of Chemical Engineering.

Jan 1, 2006

By R. L. Nyirenda

An investigation of the reducibility of a cassiterite concentrate with charcoal was made in the temperature range of 1123-1373 K. The course of the reaction was monitored by a combination of sample weight loss measurements, product gas analysis, and chemical analysis of the reaction product. It was found that the cassiterite could be best reduced by a combination? of high temperature, reasonably high charcoal proportions, high charge poroslty, and the addition of a small percentage of lime. Analysis of kinetic data obtained from isothermal experiments using theory from the oxidation of carbon by carbon dioxide gave an activation energy value of 255 lci/mole for the consumption of carbon by reaction with cassiterite.

Jan 1, 1990

By Xiaodi Huang, Matthew Andriese, Zheng Zhang, Jiann-Yang Hwang, Zhiwei Peng

"A simplified finite-difference time-domain (FDTD) algorithm for modeling microwave propagation in magnetic dielectric materials was developed and employed to study the microwave dissipation in magnetite. Heat transfer during microwave heating of magnetite was subsequently investigated by solving heat transfer differential equation using explicit finite-difference (EFD) method. It is observed that temperature of magnetite surface increases rapidly in the first minute due to the rapid strength decays in both electric and magnetic fields within a short distance along the path of microwave dissipation. A temperature peak, initially formed at the surface of the sample slab, migrates inward as heating time extends and microwave power increases.IntroductionAs one of primary materials in iron and steel industry, magnetite exhibits excellent microwave absorption capability, which leads to great energy conservation in microwave assisted steelmaking [1,2]. The fast temperature increase in microwave heating of magnetite can be attributed to both dielectric and magnetic losses [2]. Although much experimental work has confirmed this observation, detailed computational studies for modeling of microwave field dissipation in magnetite at commonly used frequencies, such as 915 MHz, has not been well addressed [1,3].Finite-difference time-domain (FDTD) method is widely used in computational electrodynamics modeling to simulate the dynamics of electromagnetic wave scattering from various media [4,5]. This approach requires modeling algorithm to be formulated with integration of specific characteristics of each medium. An extensive literature survey indicates that current formulations are only suitable for modeling electromagnetic waves propagating in normal dielectric lossy materials [5,6]. Since magnetite is a magnetic dielectric material in which both dielectric and magnetic properties contribute to the heating process under microwave irradiation, a specific algorithm should be developed for the simulation."

Jan 1, 2012

By J. R. Donald

Surface and interfacial phenomena play a significant role in refractory performance. For example, the wettability of the refractory material with slag, matte, and metal influences infiltration and interfacial reactions. Yet, very little fundamental information regarding the surface properties of refractory materials and slag is available. Thus, in the present work, the sessile drop technique incorporating a high temperature furnace equipped with X-ray fluorescope was employed to investigate the surface and interfacial phenomena of fayalite-type slags on solid alumina at 1200?C. The iron to silica (Fe/SiO,) ratios employed were 1.4 and 2.0, and the oxygen potentials used were log p02 =-11 and log p02=-9 atmospheres. The contact angle between the fayalite-type slags and the alumina were determined to be relatively low, at about 16.9 to 19.6 degrees under the experimental conditions. The surface tension of fayalite slag (Fe/SiO2=1.4) at an oxygen potential of log -11 was 0.298, which agreed with the work of previous researchers. The surface tension of the fayalite was observed to increase with time. The spinel FeAl2O4. was determined to be the product of the interfacial reaction, and 8.8 to 15.8 mass percent alumina was dissolved into the slag after 40 minutes.

Jan 1, 1996

By Dirk Verhulst, V. I. Lakshmanan

Why Chloride Hydrometallurgy?The most available, cheapest and best known reagent for treating ores and other raw materials for the metallurgical industry is sulfuric acid. Hydrochloric acid is second in line. What often happens is that a process is developed on the basis of sulfuric acid, and that at some point the question arises: wouldn't hydrochloric acid do this better?Considering hydrochloric acid immediately opens a very interesting field of research. To summarize a few comments from another paper presented at this symposium [1]: chlorides are far more soluble than sulfates (with a few interesting exceptions); the hydrogen ion activity is greater in chloride than in comparable sulfate solutions; higher oxidative conditions are possible; regeneration is more straightforward; more diversity is possible and better conditions for the separation of species can be found for solvent extraction and ion exchange; sulfur in the ore can be separated as elemental S; higher metal concentrations in solution and more flexibility in the chosen oxidation state means significantly lower energy costs.Also, the volatility of many chlorides at higher temperature allows further separation without the need to go to a different system. Chlorides also form molten salts with a low melting point, providing another means of separation and purification in the same chloride medium.

Jan 1, 2011

By F. E. Pawlek

Copper concentrates can be comminuted in an attritor within a very short time to a particle size of 1 - 0.1 um. Addition of sodium hydroxide enhances commninution. The concentrates, suspended only in water, can be completely dissolved under oxygen over pressure and temperatures ranging from 120 - 180°C (248 - 356°F), because the surface area of the concentrate has been significantly increased by the ultra fine grinding. Addi¬tion of a small amount of silver ions to leach liquor containing sulfuric acid acted as a catalyst for the dissolution of chalcopyrite, because of the formation of local elements on the surface. The addition of C1- ions was also catalytically very effective. With this method it is possible to completely dissolve the copper contained in chalcopyrite concentrates after ultra fine grinding within 30 min at 110°C (230°F) under an oxygen partial pressure of 1 atm (14 psig). Several flowsheets demonstrate the industrial feasibility.

Jan 1, 1976

By I. Gaballah

The chalcopyrite ore's anodic and cathodic electrodissolution are studied using a Porous Pulsed Percolated Electrode (3PE) reactor. Stationary solid electrode experiments are also performed to explore the mechanism of electrochemical dissolution of chalcopyrite. Experiments with a low - grade natural ore have been carried out at 25 "C in solutions containing 1 M NaCl and 1 M HCl. Galvanostatic and potentiostatic conditions are employed. The influences of current and potential on selectivity of the chalcopyrite ore dissolution are assessed. Anodic oxidation of this ore leads to a preferential dissolution of iron bearing minerals, whereas cathodic reduction is more selective with respect to chalcopyrite. However, in both cases the electrochemical dissolution is incomplete and the current efficiency is low. Design of the actual reactor has to be modified to increase the bed conductivity and to allow continuous experimentations.

Jan 1, 1994

By Fuqiang Zheng, Shuai Wang, Ting Duan, Yufeng Guo, Tao Jiang, Andrew Yakovlevich Travyanov

Organic compound binder can effectively enhance the strength of green pellet and reduce the addition amount of binder during pelletizing. However, compared with traditional bentonite binder pellet, the compressive strength of the preheated and roasted pellets significantly declined. It is of significance to resolve this problem for the application of organic compound binder. In this paper, magnetite concentrate was used as raw material, carboxymethyl cellulose (CMC)- bentonite compound was used as binder, characteristics of preheated and roasted pellets and the effects of additives on that were systematically studied, The results show that sodium acetate can effectively improve the characteristics of the finished compound binder pellets. The compressive strength of the preheated and roasted pellets were increased by 52/N·p-1 and 342/N·p-1 respectively when the addition amount of sodium acetate is 2.2%wt of compound binder. Moreover, sodium acetate has no adverse effect on pelletizing process and drying characteristics of green balls.

Jan 1, 2015

By Kazuya Koyama

We are studying the hydrometallurgical recycling process of indium from an Indium-Tin-Oxide(ITO) target. For this process, it is necessary to remove Sn(IV) ions from the aqueous hydrochloric acid solutions containing In(III). In this study, the removal of Sn(IV) ions by a potentiostatic electrolysis method was examined. The polarization measurements and potentiostatic electrolyses were carried out under a nitrogen atmosphere. In the Sn(IV) solution, current begins to rise at the cathode potential of -0.26 V vs. SHE, and increases with a reduction in the cathode potential. In the In(III) solution, current begins to rise at a cathode potential of -0.43 V vs. SHE. Metallic tin was electrodeposited without indium electrodeposition at the cathode potentials of -0.30 and -0.40V vs. SHE. More than 98% of the Sn(IV) was removed at the cathode potential of -0.40 V after the electrolysis for 3hrs. Both tin and indium were electrodeposited at the cathode potential of -0.50V vs. SHE.

Jan 1, 2006

By M. Demuth, B. Holleis, M. Potesser, D. Spoljaric

"In 2005, Messer Group established a technology competence centre for metallurgy in Gumpoldskirchen (Austria), with the aim to develop oxygen burners which satisfy today's and upcoming standards of legislation as well as customer requirements. With the assistance of the Development Sponsorship Fund (FFF) of Austria, cooperation with the University of Leoben was agreed on. With the long term experience of the Gas-Warme-Institut ""GWI"" in Essen (Germany) and the University of Leoben, different new burners have been developed.The efficiency of industrial combustion processes can be increased in two ways (which can be seen in Figure 1 ), either by preheating the fuel and combustion air or by adding oxygen. Due to the high 79 % Nz ballast in air combustion, only low flame temperatures can be reached. This results in high heat loss in the exhaust gas, caused by the low combustion efficiency. Oxygen can be introduced into the combustion chamber using different techniques:• Oxygen fuel burners• Direct oxygen injection into the fuel air flame• Underlaying of the fuel air flame• Enrichment of the combustion airIn Figure 2, the theoretical flame temperature for the stoichiometrical combustion of natural gas is plotted as a function of oxygen enrichment. Therefore, it can be concluded that even low enrichment values produce higher flame temperatures and result in higher combustion efficiency."

Jan 1, 2012

By Jim Hardy, Tim McKnight

"The thermal mass flow controller, or MFC, has become an instrument of choice for the monitoring and controlling of process gas flow throughout the materials processing industry. In the semiconductor industry, these MFCs are used on over 70% of the processing tools. Reliability and accuracy are major concerns for the users of the MFCs. Calibration and characterization technologies for the development and implementation of mass flow devices are described. Sources of inaccuracy in process gas handling are described, and a model to correct for these inaccuracies is outlined. A gravimetric calibrator is described that allows flow sensors to be calibrated in corrosive, reactive gases to an accuracy of 0.3% of reading, at least an order of magnitude better than previously possible. All described capabilities are implemented in a Department of Energy User Facility which is available to industry and universities to test and develop gas flow sensors and controllers and evaluate their performance related to environmental effects, reliability, reproducibility, and accuracy.IntroductionMaterials processing is at the heart of semiconductor manufacturing. To make today's advanced integrated circuits, silicon wafers are subjected to over 200 process steps. Most of these steps involve processes such as etching, implanting, diffusion, annealing, deposition, and lithography (resist deposition and hardening). Often one or more process gases are used to complete the process step. To achieve the quality and performance required in the micro devices, accurate measurement and control of these gases is essential. The Oak Ridge National Laboratory (ORNL), in conjunction with the semiconductor industry, has been working to improve process gas measurement and control accuracy and reliability. Standardized test methods have been developed to characterize and benchmark the performance of mass flow controllers (MFCs), the method of choice for monitoring and controlling gas delivery. Testbeds have been designed and fabricated to produce repeatable and accurate data using these standards. Baseline testing was performed along with development of a unique mass flow instrument, the gravimetric calibrator."

Jan 1, 1997

By Chao Li, Shuai Wang, Hongxu Li, Lifeng Zhang, Xie Yang

The method of chloride-hypochlorite leaching has the advantages of short process, low pollution and higher in reaction rate compared with the traditional leaching method. In this research, NaCl - NaClO solution is used to leaching gold from a refractory gold concentrate, and the influence of NaCl and NaClO concentration, reaction time to the leaching rate were investigated in this experiment. The raw materials and the leaching residue were characterized by a series of analysis methods such as XRD, XRF, SEM and EDS. Results indicate that the leaching rate and the desulfurization rate can be achieved at 96.26% and 98% with most optimum conditions as follows: NaCl concentration 50g/L, NaClO concentration 200g/L, Liquid-solid ratio 10:1, the best reaction time was 150 mins. And these conditions should be guaranteed pH<8.0, ORP>900mV.

Jan 1, 2015

By Norimasa Yamasaki, Masao Kurosaki

"The effects of plating conditions on the crystal orientation of electrodeposited zinc were investigated by varying elecyrolyte flow rate and current density. Precipitation of the Zn (00 • 2) basal plane is promoted at lower current density and higher flow velocity. Effect of the flow velocity on the mass transport was evaluated based on the polarization measurement in which Cu was used as the tracer. As a result, it has been clarified that the crystal orientation of electrodeposited zinc can be uniquely arranged by the overvoltage (iU0.5) that can be simply calculated by considering -the current density and boundary layer thickness. At the same time, the electrode potential during electrodeposition that can be calculated by using a model based on the competitive reactions of hydrogen reduction 'and zinc reduction exhibits an extremely good correlation with the crystal orientation of electrodeposited zinc.Introduction Electrogalvanized steel sheet has better surface properties than hot-dip galvanized steel sheet, and is used in home electric appliance and automobile applications. Factors such as crystal morphology, crystal orientation and surface roughness have a large influence on its appliance, formability and corrosion resistance [1-3].Electrolysis, condition, bath composition and alloying elements are reported as factors that affect the crystal orientation of the electrogalvanized coating. Factors that can be controlled on time in the production site are electrolysis condition that-is current density and plating solution flow velocity.Some studies[4-6] report that the crystal- orientation of the Zn(00 • 2) plane is increased by promoting, the mass transfer of zinc ions in the plating solution or decreasing the concentration overvoltage, but did not investigate in detail the plating solution flow conditions in the plating cell nor quantitatively determine the effects of both current density and plating solution flow conditions on the crystal orientation of ' electrodeposited zinc."

Jan 1, 2000

By Jose Hector Figueroa P.

Mexicana de Cananea, S.A de C.V. is a major copper producer mining a large deposit of the disseminated porphyry type considered one of the largest copper resources of the world with 2.7 billion tons of 0.60% copper for the mill plus 4.1 billion tons of averaging 0.26% copper for leaching. Mining of low grade sulfide leach ore, has been an important part of the overall production of the open pit mine which started in 1944. Before this time all the mining in Cananea was by underground methods. The leaching process in Cananea began on the 1920&apos;s with in situ operations in the underground mine and small dumps up to the 1950&apos;s. Large scale leaching operations began in 1960 and the copper solutions produced were treated in precipitation plants until 1,980 when the first SX/EW Plant was put in operation in Cananea. Leaching action is essentially ferric-bacterial, with no fiesh acid added to the leaching solutions. Traditionally, 5540% copper extraction is recovered fiom ROM, 70- 120 meter high leach dumps in 80 months of leaching. Cananea has successfully improved copper recoveries by implementing several actions that include: 1. Stripping of old dumps. 2. Leaching of old dumps through slotted casing. 3. Crushing conveying leach ore to minus 8 inch and stacking it in 30 meter lifts. As result of these actions, copper recovery has been increased&apos; to about 70% of total copper with actions 1 and 2 and up to 85% in half the time by crushing-conveying the leach ore, based on the same solubility index of the run-of-mine ore. This paper describes the above actions that were implemented to enhance the leaching recoveries from. sulfide leach dumps and the economics of such actions.

Jan 1, 1999

By Wenbo Luo, Kang Liu, Jilai Xue

"Coal fly-ash(CFA) from thermal power plants is rich in Al2O3, which has great potential as an alternative resource for alumina production. In this work, Alz03 contained in the coal fly-ash was extracted using an acid sintering-leaching process. This process was enhanced by aid of power ultrasound during the leaching. The recovery rate of Al2O3 was increased with ultrasound, compared with the similar process without ultrasound under the identical operation conditions. Leaching temperature can be lowered by about 10-l5°C and the processing time reduced by about 50%. The process kinetics were investigated in details for a better understanding of the fundamentals on the effects of power ultrasound. The obtained results demonstrate the potential application in reducing processing energy and increasing production rate.Introduction Coal fly ash is a typical solid waste generated from coal combustion in thermal power station. Vast amount of CF A accumulation lead to serious environmental problems such as air and water pollution, cropland occupation, radioactive contamination, etc. However, CFA is rich in Al2O3 and SiO2 content, so that it has a potential use as recourses for alumina and silica production [1]. Aluminum industry, especially in China, has made a rapid expansion in recent years accompanying with a large amount of bauxite consumption, resulting a urgent demand to develop secondary alumina resources like CF A to maintain a sustainable development of aluminum industry that faces grim challenge [2].Acid leaching is an efficient technology to use in alumina extraction from CF A. Since the particle of CF A is not naturally existed mineral but was formed in molten state at high temperature, the internal Al-O-Si bonds are so strong to separate alumina from the ash particle. Because of this reason, the direct acid leaching [3-6] operated at ambient temperature has low extraction efficiency, approximate 30% to 40%, which is attributed to self inhibition effect from CaS04 generated by reaction between CaO and H2S04 [7-8]. High pressure leaching can efficiently decompose mullite to release A12O 3 content in the fly ash particles, but this requires autoclave material having strong acid corrosion resistance, high temperature (100°C-300°C) and pressure (1.0MPa-2.SMPa) resistance while its operating security is low and its acid consumption is large [9]. Concentrated acid boil process is conducted at near acid boiling point (200 °C - 300 °C) in 4 mouth flask wrapped by electric heating jacket with high mass ratio of acid and ash to achieve high Al203 recovery rate from CFA. Its disadvantages are similar to the high pressure leaching technology except no-pressure, and also the operating solution at nearly boiling point acid may easily spill and splash with additional acid loss and potential safety hazard [10]."

Jan 1, 2014

By Scott R. Giese, Lucas Dix

"Recently, there is a growing trend in the aluminum foundry industry to develop· improved melting and casting processes to produce lightweight, high-strength, and thin-wall castings for the aerospace and transportation industry. One casting method that has demonstrated industrial potential for producing clean, thinwall castings is vacuum-assisted, counter gravity casting. This process has the benefit of expeditiously and quiescently filling the casting cavity with a dramatic reduction of furnace related and reoxidation inclusions. Additionally, lower casting temperatures can be utilized because the application of vacuum during filling overcomes the resistive internal cavity pressure resulting in a finer, as-cast microstructure. The paper explores and discusses the processing and design conditions in improving the mechanical properties of A206 casting alloy using the vacuum assisted, counter gravity casting process.IntroductionThe process of metal casting has been, over the centuries, the chief production technique for components used in everyday life. However, the casting process has certain inherent problems that can adversely effect the properties of a finished product. These problems are directly attributable to the gravity pouring technique used to transfer molten metal to the mold and to fill the mold cavity.A recent study for the American Metalcasting Consortium demonstrated reoxidation products created during the casting process are five times more likely to cause product rejects than entrapped molding aggregates, melt slag, or furnace lining materials1. Formation of nonmetallic and intennetallic compounds are more prevalent in aluminum and titanium alloys because of their reactiveness to furnace lining materials and their high affinity for oxygen. The incorporation of undesirable compounds can be attributed to four areas of the casting operation. The sources are charge materials, melting technique, pouring methodology, and casting cavity filling. Aluminum foundry men have addressed the first three areas by selecting high quality melt stock, non-stirring melting equipment, and the use of porous ceramic filters. Unfortunately, little consideration is given to the last, but yet tl.1e most important part of the casting operation, the actual fill mg of the casting cavity.The generation of inclusion defects during the casting process can be described by two methods. As the liquid metal flows in the gating network and casting cavity, abrupt changes in flow d1rect10n cause the metal to become agitated. This mechanism liquid metal splashing, is generated by instability of the advancing liquid metal interface from turbulence effects as schematically illustrated in figure 1a2 . The surface oxide film bursts under high velocity conditions, folds over, and becomes dispersed and incorporated in the bulk liquid. Additionally, fragmented liquid droplets ejected from the disturbed interface oxidize and become dispersed in the metal stream."

Jan 1, 2000

By W. G. Davenport

The remainder of this book develops and uses mass and heat balances to describe steady"state flash smelting. Its objectives are to: a) describe the many ways a flash furnace operator can produce specified products, e,g. 65% eu matte, 35% SiOz slag, 1500 K (b) determine the oxygen, air, flux and hydrocarbon fuel requirements of each method (c) show how the flash furnace can be controlled to give specified products with varying feed compositions (d) suggest how the flash furnace operator can maximize profitability while producing specified products. This chapter develops the basiC heat and mass balance equations of steady-state ?flash smelting. It then adapts the equations to industrial feed materials .and products. Lastly it determines the amounts of oxygen and flux needed to produce molten matte and 35% SiOz slag from chalcopyrite concentrate in an Inco oxygen flash furnace,

Jan 1, 2001