By A. L. Holley

The occurrence of this gas, in quite appreciable quantities, has been observed for many years in its escape along the creeks of Western Pennsylvania, and more recently, in much larger quantities, from the oil wells in and near Venango County. Within about five years several gas wells have been struck, from which the gas has escaped continuously in prodigious quantities and at great pressure. During the last year a systematic attempt has been made to utilize the flow of gas from one of these wells, and results have been reached which were quite unexpected. This well, near Leechburg, Armstrong County, is about twenty miles northeast of Pittsburgh, on one of the side tributaries of the Alleghany River. It had been drilled in search of oil to a depth of 1250 feet in 1871, but none was found. A great flow of gas was developed, however, accompanied by a slight spray of salt water, and this has continued with little or no diminution to the present time. The gas in its escape has been discharged through a 5-inch pipe, and at a pressure of from 60 to 80 Ibs. per square inch, but no exact determinations, either of the pressure or quantity, have been made. The rolling mill of Messrs. Rogers & Burchfield is on the opposite side of the river, and it has been for some years devoted to the production of fine grades of sheet iron from charcoal pig metal, by puddling and in knobbling fires. The usual weekly product of the mill has been 30 tons of No. 30 tin plates, and 50 tons of No. 24 to 28 sheets. The well was bought by this firm for $1000, and the gas is led across the river, a distance of about 500 feet, through a 3-inch pipe. It is distributed through half-inch pipes, and at a pressure of about 45 Ibs. per square inch, to several of the furnaces, but a large fraction of the total flow of gas is still wasted at the well. No essential alteration in any of the furnaces has been found necessary in the use of the gas fuel, except to brick up the firebridge and to put in the gas and air pipes. The old grate used for coal is loosely covered with bricks and cinder, so that a slight percolation of air may take place through them. The gas is admitted through a half-inch pipe, and blows toward the fire-bridge through 18 or 20 one-eighth inch jets. The air is blown in at about 2 lbs.

By J. H. Frye, C. P. Sun

A PRIMARY substitutional solid solution is a solution that has the same crystalline structure as the solvent metal, and in which solute atoms have replaced solvent atoms at random on the host lattice. This replacement usually results in an increase in hardness as measured by conventional penetration tests. The factors controlling this hardness increase have been investigated in some detail for copper and silver aneys.1-5 It has been shown that at least, four factors are involved: (I) concentration of solute, (2) row of the periodic table from which the solute is taken, (3) increase in lattice parameter of the solvent produced by the solute, and (4) work-hardening produced by penetration of the hardness indenter.2,4 The last factor is of the utmost importance. An investigation of the available data2.4 leads to the conclusion that the solutes that produce large hardness increases in copper or silver do so principally because they increase the rate of work-hardening. Furthermore, it is doubtful whether any solute produces appreciable hardening in the absence of plastic deformation and hence work-hardening. Thus it is clear that an understanding of the effect of solutes on rate of work hardening is essential to an understanding of the hardness of solid solutions. This effect of solutes is also important in forming operations such as rolling or deep drawing. The presence of elements that confer rapid rates of work-hardening will increase power consumption and may well decrease the amount of deformation possible between anneals. This paper is the report of an investigation of the factors that control rates of work-hardening in copper and silver solid solutions. The silver and copper alloys considered are those in which all solutes are from the B subgroups or second short period of the periodic table. Experience with hardness, with structure of alloys, and with electrical conductivity has proved that results of a fundamental nature are most likely to be obtained if alloys are made up on the basis of the positions of the constituent elements in the periodic table. In previous work, Meyer analysis data on high-purity copper and silver solid solutions were obtained through careful measurements with fully calibrated equipment and these data were corrected to correspond to a standard grain size. From these corrected Meyer analysis data rates of work-hardening have now been calculated. CALCULATION OF RATES OF WORK- HARDENING The Meyer analyses, on which this study of rates of work-hardening is based, consisted in determining impression

Jan 1, 1944

By E. S. Wheeler

The conversion plant of the Clirnax Molybdenum Co. is at Langeloth, Washington . County, Pennsylvania, approximately 30 miles west of Pittsburgh. The molybdenite concentrates converted originate in the company's mine and mill at Climax, Co1orado.l They are delivered to the Langeloth plant by rail packed in 175-lb. bags. War production of concentrates at the mill started in 1918 but it was not until about 1920 that any peacetime uses of the metal began to develop. Early conversion of Climax concentrates was mainly into ferromolybden um, produced for the company by a custom smelter. Chronology of Plant Development In 1924 a small hand-rabbled roaster was built at Langeloth, the roasted concentrates being used principally in the production of calcium molybdate by a conventional wet method. The size of the original plant is indicated by the fact that during 1925 about 400,000 lb. of molybdenum was converted. In 1925-1926, a multiple-hearth roaster was erected (12-ft. 0.d. 8-hearth Nichols-Herreshoff); also the first experimental ferromolybdenum was produced at Langeloth. At this time sa.1cium molybdate was produced in the furnace by a process to be described. With continued interest in and increased use of molybdenum, it was necessary to arrange for enlargement of plant facilities. Although only one 12-hearth 16-ft. 0.d. roaster was erected at this time (1929), plans were prepared for a duplicate unit, which was completed in 193 5, giving a potential roasting capacity of some 16,000 lb. Mo per day under the then prevailing roasting practice. Shortly after this second unit had gone into production, increased demand overtaxed the plant, and as a result two 12-hearth 18-ft. 0.d. roasters were placed in operation in 1936 and 1937. This gave the plant a potential roasting capacity of 40,000 to 50,000 lb. Mo per day, and necessitated major changes in auxiliary handling equipment as well as improved facilities for producing ferromolybdenum. Following the introduction (1938) of a new product—molybdic oxide briquets— and because of the constantly growing demand for molybdenum, plant facilities were again enlarged in 1940 and 1941 by the erection of two 16-hearth 18-ft. 0.d. roasters. These two new units, along with a change in roasting practice, brought the potential roasting capacity to 150,ooo to 190,000 Ib. Mo per day, based on about 15 lb. per sq. ft. of hearth area. Other departments of the plant have necessarily grown, until today the plant is modern throughout and completely mechanized, with equipment geared to produce marketable products as follows:

Jan 1, 1944

By R. D. Barer, M. B. Bever

Age hardening alloys are quenched from the solution treatment to room temperature in order to retain a supersaturated solid solution. Some alloys age "naturally" in this condition but in most alloys aging is induced "artificially" by heating to intermediate temperatures. Cold working of the supersaturated solid solution accelerates the aging process and quenching strains have the same effect. The investigation reported here is a study of the progress of aging in specimens quenched directly from the solution treatment to various aging temperatures. This procedure reduces the temperature interval of quenching and the resulting quenching stresses. It also eliminates any changes which would take place in the undercooled sample at room temperature prior to aging at an elevated temperature. Isothermal aging is thus approached and its kinetics may be studied. An aluminum-copper and an aluminum-silicon alloy were chosen for this investigation. The aging mechanism of aluminum-copper alloys is complex while the aging of aluminum-silicon alloys is nearly ideal. As standards of comparison for the samples directly quenched to the aging temperature, specimens were also age hardened by the usual procedure in which solution treated samples are first quenched to room temperature and then reheated to the aging temperature. Review of Previous Work The mechanism of age hardening has been the subject of a controversy which has ranged from the theory of outright precipitation of an equilibrium phase to theories based on subtle changes occurring in the matrix prior to precipitation. A detailed critical review of the literature up to 1939 is available1 and contributions to the general theory of age hardening continue to be made.2,3 Age hardening, whatever its mechanism, involves the nucleation of a second phase within a supersaturated solid solution. Theoretical considerations4,5 indicate that the rate of nucleation reaches a maximum at an intermediate temperature below the temperature at which supersaturation sets in. Studies of precipitation at various subcritical temperatures have demonstrated that the largest property changes in a given time occur at such intermediate temperatures.6,7,8 The precipitation of a phase from supersaturated solid solution is accelerated by strains which may result from quenching or cold work. Phillips and Brick9 established that quenching strains are an essential condition for the age hardening of aluminum-copper alloys at room temperature, at least for aging periods of less than 30 days. They also found that on aging at 300°C the hardness increased faster and reached a higher maximum after quenching into water than after quenching directly to the aging temperatures. Fink and Smith10 observed preferential precipitation on slip bands and grain boundaries in aluminum-

Jan 1, 1950

By Charles S. Barrett, F. W. Steadman

DEFORMATION bands of surprising regularity are found in large-grained polycrystalline copper after cold-rolling (Fig. I). Individual bands frequently are large enough to permit a determination of their orientation by means of etch pits and an optical goniometer. Measurements have been made on 21 areas in seven different grains, and these, combined with X-ray studies of nine single crystals that had been cold-rolled after mounting in a polycrystal-line block, have contributed to a better understanding of the preferred orientations in rolled copper just as similar studies have for rolled iron' and brass.2.3 Particular attention was given to determining orientations that are stable during rolling and to the manner of fragmentation and rotation of unstable grains. The possible role of twinning was also carefully investigated. The texture of polycrystalline copper after cold-rolling is well established by the pole figures that have been plotted by Schmid and Staffelbach,4 Iweronowa and Schdanow,5 and Brick and Williamson,3 all of which are in substantial agreement. There has been some divergence in the list of individual "ideal" orientations that have been used to describe the texture by these observers and others,6 although the orientation (110) [112]-that is, (110) parallel to the rolling plane and [112] parallel to the rolling direction-is generally recognized as the most prominent orientation and (I12) [111] one of the lesser orientations. Other orientations have been given by some observers as (236) [533], (100) [001], and (I 10) [001]. The texture of copper has also been described as (135) [533].6.1 The sum of these orientations provides a reasonable approximation to the complete pole figure, but it does not follow that these specific orientations are necessarily of fundamental significance, for the choice of indices is arbitrary, within limits. Furthermore, a detailed investigation of the ideal orientations in cold-rolled iron discloses continuous ranges of equally favored positions rather than definite positions of high stability,1 and similarly Brick's observations in a single crystal of a brass2 suggest that all orientations in the range between (110) [113] and (110) [117] are about equally stable. MATERIALS AND METHODS The material used was vacuum-cast electrolytic copper kindly supplied by L. L. Wyman, of the General Electric Co.* Slices 1/2 in. thick and 2 1/2 in. square, cut from the ingot, were rolled with 50 per cent reduction per pass to final thicknesses between 0.02 and 0.04 in., and etched to develop cube-face etch pits suitable for goniometric work.8 The etch was light on some strips and deep in others.

Jan 1, 1942

By Sandip K. Mukherjee, Anthony W. Laurito, Madan M. Singh, Jon C. Volkwein

In the past, little attention has been paid to the costs of ventilation, since it seldom represented a significant portion of the total mining cost. However, in recent years adverse mining conditions and increases in power charges have caused ventilation costs to rise. The federal regulations have set minimum standards for volumetric airflow rates in underground coal mines. As a mine develops, the air volume and pressure requirements increase. There are several methods by which the quantity of airflow to the mine and working faces can be increased. Some of the methods include (1) increasing main fan output or replacing the main fan by a new higher capacity fan, (2) reducing leakage across stoppings and overcasts, (3) adding a new ventilation shaft or borehole, (4) reducing resistance to airflow by reducing the resistance factor of the individual airways, increasing the number of airways (especially the parallel airways), or re- arranging the air courses by using the available entries, and (5) using auxiliary ventilation systems. This paper addresses the cost-benefit analysis of several of these alternatives as applied to a large operating coal mine located in southern Illinois. Pressure and quantity surveys were conducted under-ground, and measurements were taken at the main exhaust fans on the surface. The existing ventilation network was modeled by using the Penn State ventilation simulator. The input data included the configuration of branches, resistance of each branch (including a component for shock losses), and changes in pressure and volume. The results of the simulation were compared with the survey data to check the merits and accuracy of the model network. The net- work was designed to take into account shafts, major entries, overcasts, regulators, gob areas, working faces, and major leakage paths. The model network served as the basis for the cost analyses of networks designed for increased airflow. The applicable alternatives for increasing airflow were simulated. Performance data obtained from these simulation runs were utilized to conduct the cost-effectiveness analysis. The costs for each f the alternatives included capital, operating and maintenance costs. These costs were expressed as annual costs in terms of dollars per cfm of circulating air, taking into account the economic life associated with each of the alternatives. The benefits were expressed as increased airflow quantity in the critical sections. The result of these analyses show that for the short-range plans evaluated, the most cost-effective way of increasing airflow at this mine would be to reduce leakage through stoppings and overcasts.

Jan 1, 1982

By John M. Hartman

On May 19th, 1857, an English patent was granted to E. A. Cowper for heating air or other gases under pressure by means of a regenerator inclosed in an air-tight iron case, having between the regenerator and case a lining of brick. This patent provided for heating the stoves by a separate fireplace, or by gas direct from the blast furnace. A number of forms of interior arrangement of the brickwork are shown in the drawings; also hollow poppet valves with hollow stems, and a pipe inside of the stem for circulating the water; the valve seats have coil cast in them for water circulation to keep them cool; slide valves, with snake coil cast in the discs, are shown, and the use of cold air for cooling the valves is also described. The combustion-chamber of these stoves was central, and openings mere provided at the top and bottom to get into the stoves. These Cowper stoves are all circular in section. November loth, 1865, an English patent was granted to Thomas Whitwell for regenerative stoves for heating air or gas, provided with cleaning openings at the top and bottom capable of being closed with firebrick plugs and doors. The drawings show a rectangular stove inclosed in an iron case. The interior brickwork has numerous upand-down passages through the stove, but there is no claim on the interior construction. March 3d, 1868, an English patent was granted to Charles Cochrane for a slide valve to be subjected to high heats. The disc of this valve was hollow, and had a circulation of water through it by the two hollow stems that operated it. The valve-seat was detachable and had a coil cast in it, through which water circulated. The valve and seat were placed on an incline to the body to cause the valve-disc to lie on the valve-seat. A cap was placed on the bottom of the body to get at the interior readily. January 5th, 1870, an English patent was granted to Siemens, Cowper and Cochrane for the construction of regenerators in firebrick stoves, with numerous vertical passages of sufficient size to allow a brush to pass through and clean them. These passages had slight projections on the sides to tarn the air over and over as it passed through. A claim also covered the use of horizontal passages connected at each end alternately, and the use of blasts or jets of air,

Jan 1, 1880

By B. J. Harlan

The trying times experienced by the steel industry during the past four years have emphasized the necessity of producing pig iron at the lowest possible cost. The trend in both design and operation of blast furnaces has been toward this end rather than toward securing maximum production from a unit or group of units. In the following discussion the trend in design of stacks and auxiliary equipment will be taken up before operation is considered. Although few furnaces have been constructed in the past few years, the trend is definitely toward larger furnaces with a hearth diameter of 24 or 25 ft. Such a furnace is very flexible, being able to produce efficiently any desired daily tonnage between 500 and-1000 or more. The detail of the design of furnace stacks, with the exception of the top, has changed little in recent years. To decrease the velocity of gas through the throat of the furnaces, thereby reducing flue-dust losses, the stock-line areas are constantly being made larger. The top dimensions of the larger furnaces are usually as follows: Stock-line diameter, 19 to 20 ft.; large bell diameter, 14 to 15 ft.; straight section of throat, 5 to 10 ft. high; inwall batter, 1 to 11/4 in. Pe ft. The ratio between the area of the stock line and the area of the large. bell is usually about 1.85 to 1. The stock-line diameter of some smaller furnaces has been increased to that of the hearth diameter of the stack at the expense of the stack batter. Remarkable decreases in flue-dust production are claimed for the so-called " Venturi top," which is achieved by flaring the stock line, in the form of an inverted cone, from a diameter of 17 ft. at 10 ft. below the large bell closed to a diameter of 19 ft. 6 in. at 3 ft. below the large bell closed. Time alone will tell which of the two designs is the better. Because of differences in raw materials, one top may be better for some plants and the other top for other plants. In the search for lower costs and higher efficiencies all operators are, adopting stoves that will maintain maximum hot-blast temperatures with a minimum gas consumption. To meet these requirements, stove capacity of approximately 7 sq. ft. of heating surface and 1.8 cu. ft. of brick volume is required per cubic foot of wind blown per minute.

Jan 1, 1934

By Joan M. Hartman

ON May 19th, 1857, an English patent was granted to E. A. Cowper for heating air or other gases under pressure by means of a regenerator inclosed in an air-tight iron case, having between the regenerator and case a lining of brick. This patent provided for heating the stoves by a separate fireplace, or by gas direct from the blast furnace. A number of forms of interior arrangement of the brickwork are shown in the drawings; also hollow poppet valves with hollow stems, and a pipe inside of the stem for circulating the water; the valve seats have coil cast in them for water circulation to keep them cool; slide valves, with snake coil cast in the discs, are shown, and the use of cold air for cooling the valves is also described. The combustion-chamber of these stoves was central, and openings were provided at the top and bottom to get into the stoves. These Cowper stoves are all circular in section. November 10th, 1865, an English patent was granted to Thomas Whitwell for regenerative stoves for heating air or gas, provided with cleaning openings at the top and bottom capable of being closed with firebrick plugs and doors. The drawings show a rectangular stove inclosed in an iron case. The interior brickwork has numerous up-and-down passages through the stove, but there is no claim on the interior construction. March 3d, 1868, an English patent was granted to Charles Cochrane for a slide valve to be subjected to high heats. The disc of this valve was hollow, and had a circulation of water through it by the two hollow steins that operated it. The valve-seat was detachable and had a coil cast in it, through which water circulated. The valve and seat were placed on an incline to the body to cause the valve-disc to lie on the valve-seat. A cap was placed on the bottom of the body to get at the interior readily. January 5th, 1870, an English patent was granted to Siemens, Cowper and Cochrane for the construction of regenerators in fire-brick stoves, with numerous vertical passages of sufficient size to allow a brush to pass through and clean them. These passages had slight projections on the sides to turn the air over and over as it passed through. A claim also covered the use of horizontal passages connected at each end alternately, and the use of blasts or jets of air,

Jan 1, 1880

By Gordon G. Bentle, W. P. Fishel

GREINER, Marsh, and Stoughton1 have reviewed the literature in a monograph on the iron-silicon system. The lack of agreement among the various studies may be due to the difference in the purity of materials in some cases. The results of the X-ray method indicate only a general rather than a specific limit of the y loop. The iron-titanium system was investigated by Roe and Fishel,' whose results are used in determining the iron-silicon-titanium y loop. The literature indicates that no study has been made thus far of the iron-silicon-titanium system in the y loop region. Experimental Procedure The alloys were made from Armco iron, 99.86 pct Si, and 98.5 pct Ti. The titanium contains 1.07 pct Fe. The Armco iron contains 0.01 pct C, 0.005 pct Si, 0.02 pct Mn, 0.006 pct P, 0.01 pct S, and 0.04 pct Cu. A dilatation sample of Armco iron was prepared in the same manner as were the other samples. Several dilatation runs indicated that Ac3 begins at 905°C and ends at 910°C, which compares favorably with the study of Wells, Ackley, and Mehl' employing specially purified iron. All alloys were melted in an induction furnace in Alundum crucibles and were top poured into baked core sand molds. The ingots weighed about 600 g as cast. Dilatation samples of 4 in. by % in. diam were taken from the bottom end of the ingot, from which turnings for analysis were taken. Turnings from each end of two of the samples indicated that the alloys possessed uniform silicon content. A hole was drilled halfway through each end of a 4 in, dilatation sample. A chromel-alumel thermocouple was inserted in each hole and the surrounding metal peened in to hold the thermocouple in place. Fig. 1 represents the dilatation apparatus. The heating unit is an Alundum tube wound with resistance wire; the dilatation tube is a McDanel combustion tube; the push rod is zircon; the dial gage is graduated in 0.0001 in. and was vibrated to prevent sticking. A blank run over the temperature range of interest gave no significant dilatation. The thermocouples were attached to a multiple recording micromax which indicated the temperature at each end of the sample at 35 sec intervals. A Lindberg control unit governed the rate of heating of the furnace, and lowering or raising the

Jan 1, 1957

By R. L. Sandefur

Professor Kim's excellent review article1 on ultimate pit planning contains a statement of the apparently widely held but incorrect belief that "kriging provides information on the confidence limits around the estimate which no other extension technique is capable of supplying." If a geostatistical approach is valid, there are several good reasons for using kriging but uniquely provided confidence limits is not among them. If kriging is possible, then confidence limits can be calculated for any other linear estimate. Kriging is the procedure which finds the weighing coefficients which minimize the estimation variance [ ] is the variance of blocks like the one being estimated. wi is the covariance of the estimated block and the i-th sample. oij is the covariance of the i-th sample and the j-th sample. Ai is the weighing coefficient for the i-th sample. N is the number of samples. The formula for estimation variance can also be used to calculate confidence limits on blocks estimated by any linear combination of sample grades including: 1) Polygons a. Hole nearest block centroid is assigned weight 1. All other holes are assigned weight 0. b. Polygonal area weighing. The samples are assigned weights directly proportional to their polygonal areas of influence within the block. The weights sum to 1. 2) Inverse distance weighing. The samples are assigned weights directly proportional to the reciprocal of their distance to some power from the block centriod. The weights sum to 1. Often only holes nearer than a certain distance and/or the nearest hole in each octant is considered. If there is an antisotropy to the ore body, an elliptical transformation often gives more accurate results. The most popular inverse distance weighing function is inverse squared distances (IDS). 3) Simple average. All samples within a certain distance are assigned the same weights which sum to 1. As an example of the applicability of the above formula to any linear estimate an internal verification on copper grade of 665 blast holes on the 1040 bench at Utah's Island Copper mine is presented. Internal verification is simple and applicable to non-linear estimates as well. Any sample (drill hole, bulk, trench, or chip) is dropped out, the value of the dropped sample estimated and compared with the actual value. If this is done for all samples, a measure of confidence limits is obtained. Internal verification is used in Cominco's MEPS system4 and in the BLUEPACK system.5 Comparison of block values against estimates697 is not dissimilar to internal verification. Results of the internal verification are presented below:

Jan 1, 1980

By Richard McCaffery

THERE has been some discussion among blast-furnace operators regarding the relative merits of tuyeres of the converging type and tuyeres designed in an attempt to produce a diverging jet of air. An article1 on Progress in German Blast Furnace Practice indicates the interest in this subject abroad. This article illustrates a diverging type of tuyere which is shown here in Fig. 1A. The design appears to be rather poor as regards known properties of air flow. The adoption of this. tuyere, the article states, resulted in a decrease of blast pressure of about 4 lb. per sq. in. and an increase of the output of the furnace. If the improvements mentioned are due entirely to the change in tuyere design, the subject of tuyere design seemed worthy of investigation and this paper is a report of such work. Because of the gain in efficiency brought about by the use of a diverging tuyere in the German plant, it was thought desirable to investigate the shape of the air streams issuing from various-types of tuyeres to ascertain whether the gain was due to the tuyere itself or to the distribution of the air in the furnace. Since it is difficult to do experimental work on a full-sized furnace, or even on full-sized tuyeres, and because of the equipment available for the work, it was decided to carry out the work on scale models of tuyeres. Therefore, in this work, single tuyeres were used and the blast discharged into the atmosphere. The shape of the air stream was determined by means of a Pitot tube suitably supported in the air stream at various positions. The air was. furnished by a Roots blower driven by a 10-hp. direct-current motor having field control, and capable of discharging 250 cu. ft. per min. with a pressure on the discharge of 4 in. of mercury. A modern blast furnace with 21-ft. hearth requires about 50,000 cu. ft. per min. of free air at from 16 to 23 lb. per sq. in. pressure, depending upon the type of burden. This pressure is the total pressure required to force the air through the burden and through the tuyeres. Upon computation the pressure drop through the tuyeres is about 1 to 2 lb. per sq. in. By making the tuyeres to a one-fifth scale, and by using a pressure of 1.5 in. of mercury, the shape of the air streams should be

Jan 1, 1931

By Russell G. Wayland

This paper gives the author's personal idea of the general viewpoint of the world's largest mica consumer, the U. S. Army, toward the supply, uses, and conservation of mica. However, to cover so broad a subject in a brief paper will require the dismissal of many phases with little or no mention. For example, it will be necessary to omit further reference to phlogopite or amber mica, even though amber block and splittings for certain spark plugs and commutator segments present some supply problems. This paper will deal entirely with muscovite, or white mica. Muscovite Mica Muscovite mica is available commercially in four general forms; namely, as block mica, as splittings, as washer punch, and as scrap mica.1 No strategic importance is attached to washer punch and scrap mica, even though scrap has found some use in military construction and in electrical ceramics. The use of washer punch as such has fallen off with the non-manufacture of household electrical appliances. Some qualities of block mica are also of little or no interest, but other qualities of block mica and all splittings are considered of vital importance. Army equipment requires large amounts of muscovite mica splittings in the form of built-up mica commutator segments and coil insulation in motors and generators. Other military items using significant amounts of muscovite splittings are transformers, switchboards, and blasting apparatus. Flexible mica tape, made from bookform or loose-dusted splittings cemented to paper, linen, glass cloth, and other backing, is widely used in coil insulation in heavy electrical equipment and in aircraft generators. All muscovite mica splittings come from India, principally because of the enormous amount of hand labor required in their preparation. In this emergency, the need for them was anticipated and large industry and government stocks were on hand, while shipments have continued to come by sea in spite of wartime hazards. With the possible exception of certain bookform splittings, no trouble is anticipated in supply. Accordingly, the remainder of this paper is devoted to block (or sheet) muscovite mica, including condenser film that is split from block. The Mica Problem Block muscovite mica is commercially classified into the following general qualitie3, beginning with the best quality: 1. Clear and Slightly Stained (C & SS). 2. Fair stained (FS). 3. Good stained (GS). 4. stained (s). 5. Heavy Stained (HS). 6. Black spotted. The ratio of relative commercial abundance in the present new supply of these micas is approximately 1 C & SS to 4 FS to ro GS to 14 S to whatever the

Jan 1, 1948

By C. E. Berry

Natural stone or manufactured porcelain pebbles are used as the grinding elements in pebble mills and the mills are lined with stone or porcelain blocks. Steel balls usually form the grinding medium in ball mills, and the mills may be lined with steel. Pebble mills are used to avoid contamination by metal of the material being ground, to avoid rapid wear due to corrosion, and for other specialized reasons. Belgian silex (silica) blocks formerly were used widely for lining pebble mills, because of their good resistance to wear, light color, and low cost, but the importation of these blocks was suspended early in the war. The stocks of Belgian silex diminished so rapidly that it was found desirable to compare the properties of a number of domestic substitutes for use in critical operations. Accordingly, a study was made to determine the best substitutes for fine grinding of white pigment and for certain heavy-chemical process work such as the disintegration of phosphate rock in weak phosphoric acid solution. A comprehensive survey of substitute lining materials was not contemplated. It was stipulated at the beginning of the investigation that only materials on the market, available in large quantities, would be tested and that these should be reasonable substitutes from a a ance viewpoint as determined from known physical characteristics. Marble and limestone, for example, could be eliminated immediately. Quartzite, granite and porcelain were selected as likely substitutes for Belgian silex and were subjected to quality tests. Materials Tested 1. Belgian Si1ex.—Sample blocks of a standard grade were taken from crates in which they had been imported. The stone was light gray in color and contained inclusions of small clusters of quartz crystals as well as light colored portions that might be calcite. This was a siliceous rock which appeared to be of igneous origin. 2. Quartzite.—Samples of quartzite were obtained from a quarry in Minnesota. The blocks exhibited a crystalline fracture. The stone was pink in color and composed of fine quartz crystals bound together with a siliceous cement. 3. Granite A was a fine-grained granite quarried in South Carolina. 4. Granite B was coarse-grained granite quarried in South Carolina. 5. Granite C was a coarse-grained granite quarried in North Carolina. 6. Porcelain A.—Sample blocks of the pebble-mill lining material were obtained direct from the manufacturer. It was white in color and of lower specific gravity than the natural materials. It did not have a crystalline structure. 7. Porcelain B.—Sample pebble-mill lining blocks of the porcelain were received direct from the manufacturer. It was white

Jan 1, 1948

By Russell G. Wayland

This paper gives the author's personal idea of the general viewpoint of the world's largest mica consumer, the U. S. Army, toward the supply, uses, and conservation of mica. However, to cover so broad a subject in a brief paper will require the dismissal of many phases with little or no mention. For example, it will be necessary to omit further reference to phlogopite or amber mica, even though amber block and splittings for certain spark plugs and commutator segments present some supply problems. This paper will deal entirely with muscovite, or white mica. Muscovite Mica Muscovite mica is available commercially in four general forms; namely, as block mica, as splittings, as washer punch, and as scrap mica.1 No strategic importance is attached to washer punch and scrap mica, even though scrap has found some use in military construction and in electrical ceramics. The use of washer punch as such has fallen off with the non-manufacture of household electrical appliances. Some qualities of block mica are also of little or no interest, but other qualities of block mica and all splittings are considered of vital importance. Army equipment requires large amounts of muscovite mica splittings in the form of built-up mica commutator segments and coil insulation in motors and generators. Other military items using significant amounts of muscovite splittings are transformers, switchboards, and blasting apparatus. Flexible mica tape, made from bookform or loose-dusted splittings cemented to paper, linen, glass cloth, and other backing, is widely used in coil insulation in heavy electrical equipment and in aircraft generators. All muscovite mica splittings come from India, principally because of the enormous amount of hand labor required in their preparation. In this emergency, the need for them was anticipated and large industry and government stocks were on hand, while shipments have continued to come by sea in spite of wartime hazards. With the possible exception of certain bookform splittings, no trouble is anticipated in supply. Accordingly, the remainder of this paper is devoted to block (or sheet) muscovite mica, including condenser film that is split from block. The Mica Problem Block muscovite mica is commercially classified into the following general qualitie3, beginning with the best quality: 1. Clear and Slightly Stained (C & SS). 2. Fair stained (FS). 3. Good stained (GS). 4. stained (s). 5. Heavy Stained (HS). 6. Black spotted. The ratio of relative commercial abundance in the present new supply of these micas is approximately 1 C & SS to 4 FS to ro GS to 14 S to whatever the

Jan 1, 1948

By C. E. Berry

Natural stone or manufactured porcelain pebbles are used as the grinding elements in pebble mills and the mills are lined with stone or porcelain blocks. Steel balls usually form the grinding medium in ball mills, and the mills may be lined with steel. Pebble mills are used to avoid contamination by metal of the material being ground, to avoid rapid wear due to corrosion, and for other specialized reasons. Belgian silex (silica) blocks formerly were used widely for lining pebble mills, because of their good resistance to wear, light color, and low cost, but the importation of these blocks was suspended early in the war. The stocks of Belgian silex diminished so rapidly that it was found desirable to compare the properties of a number of domestic substitutes for use in critical operations. Accordingly, a study was made to determine the best substitutes for fine grinding of white pigment and for certain heavy-chemical process work such as the disintegration of phosphate rock in weak phosphoric acid solution. A comprehensive survey of substitute lining materials was not contemplated. It was stipulated at the beginning of the investigation that only materials on the market, available in large quantities, would be tested and that these should be reasonable substitutes from a a ance viewpoint as determined from known physical characteristics. Marble and limestone, for example, could be eliminated immediately. Quartzite, granite and porcelain were selected as likely substitutes for Belgian silex and were subjected to quality tests. Materials Tested 1. Belgian Si1ex.—Sample blocks of a standard grade were taken from crates in which they had been imported. The stone was light gray in color and contained inclusions of small clusters of quartz crystals as well as light colored portions that might be calcite. This was a siliceous rock which appeared to be of igneous origin. 2. Quartzite.—Samples of quartzite were obtained from a quarry in Minnesota. The blocks exhibited a crystalline fracture. The stone was pink in color and composed of fine quartz crystals bound together with a siliceous cement. 3. Granite A was a fine-grained granite quarried in South Carolina. 4. Granite B was coarse-grained granite quarried in South Carolina. 5. Granite C was a coarse-grained granite quarried in North Carolina. 6. Porcelain A.—Sample blocks of the pebble-mill lining material were obtained direct from the manufacturer. It was white in color and of lower specific gravity than the natural materials. It did not have a crystalline structure. 7. Porcelain B.—Sample pebble-mill lining blocks of the porcelain were received direct from the manufacturer. It was white

Jan 1, 1948

By W. T. Bishop, G. A. Crowe

While the literature in the United States on general polarographic technique is extensive, very little appears to be directly applicable to the analysis of flotation tailings. For this reason, it seemed worth while to present a few polarographic methods of ore analysis that have been in constant use in the laboratories of the Hercules Experiment Station for the past few years. At the time of our initial investigation of the polarographic method, there was little or no mention of its specific application to flotation tailings. It was therefore necessary for us to establish suitable conditions for the analysis of our flotation tailings and to consider possible interfering constituents. The polarograph, or dropping mercury electrode, method was discovered in 1925 by J. Heyrovsky and M. Shikata,1 of the Charles University, Prague. This method has since received extensive development and the literature contains many articles on the use of the polarograph for the quantitative determination of metals as well as anions, oxygen in solution, and reducible organic compounds. Kolthoff and Lingane,² by the publication of their book, "Polarography," in 1941 did much to advance the knowledge and use of the polarograph. In chapter 25 of that book, methods for the polarographic analysis of brass, steel and iron products, alloys, and zinc ore are given. Aluminum,³ cadmium,³,4 cobalt,4 cop-per,³-9 gold,10 iron,3,11 lead,³,l2,l³ molybdenum,14 nickel,4,8,9 tin," and zinc³,4,5,7 in ores have been analyzed by the polarograph. However, most of the work on tailing samples has been published in Russian journals and translations are not yet readily available. In this paper we will describe the method that was developed and used in our laboratory for the determination of copper, zinc, and lead in flotation tailings. Principle OF the Method The polarograph is an instrument for applying a potential to a mercury pool and a dropping mercury electrode separated by a solution, and for measuring the resultant electrical current. The procedure is essentially a small-scale electrolysis, in which the voltage required to reduce or oxidize the material identifies it qualitatively and the current measures the concentration quantitatively. Different constituents in a sample may often be determined simultaneously provided they reduce at sufficiently different voltages. An example is the determination of copper and zinc in the same solution. The reduction potentials are quite far apart, as shown in Fig. I. The polarographic method is particularly useful in the range of concentration between those normally determined by spectographic and chemical methods. In

Jan 1, 1947

By G. A. Crowe, W. T. Bishop

While the literature in the United States on general polarographic technique is extensive, very little appears to be directly applicable to the analysis of flotation tailings. For this reason, it seemed worth while to present a few polarographic methods of ore analysis that have been in constant use in the laboratories of the Hercules Experiment Station for the past few years. At the time of our initial investigation of the polarographic method, there was little or no mention of its specific application to flotation tailings. It was therefore necessary for us to establish suitable conditions for the analysis of our flotation tailings and to consider possible interfering constituents. The polarograph, or dropping mercury electrode, method was discovered in 1925 by J. Heyrovsky and M. Shikata,1 of the Charles University, Prague. This method has since received extensive development and the literature contains many articles on the use of the polarograph for the quantitative determination of metals as well as anions, oxygen in solution, and reducible organic compounds. Kolthoff and Lingane,² by the publication of their book, "Polarography," in 1941 did much to advance the knowledge and use of the polarograph. In chapter 25 of that book, methods for the polarographic analysis of brass, steel and iron products, alloys, and zinc ore are given. Aluminum,³ cadmium,³,4 cobalt,4 cop-per,³-9 gold,10 iron,3,11 lead,³,l2,l³ molybdenum,14 nickel,4,8,9 tin," and zinc³,4,5,7 in ores have been analyzed by the polarograph. However, most of the work on tailing samples has been published in Russian journals and translations are not yet readily available. In this paper we will describe the method that was developed and used in our laboratory for the determination of copper, zinc, and lead in flotation tailings. Principle OF the Method The polarograph is an instrument for applying a potential to a mercury pool and a dropping mercury electrode separated by a solution, and for measuring the resultant electrical current. The procedure is essentially a small-scale electrolysis, in which the voltage required to reduce or oxidize the material identifies it qualitatively and the current measures the concentration quantitatively. Different constituents in a sample may often be determined simultaneously provided they reduce at sufficiently different voltages. An example is the determination of copper and zinc in the same solution. The reduction potentials are quite far apart, as shown in Fig. I. The polarographic method is particularly useful in the range of concentration between those normally determined by spectographic and chemical methods. In

Jan 1, 1947

By William Klement

KNELLER' has recently reported that extensive metastable solid solutions may be obtained in Cu-Fe alloys by simultaneous vapor deposition. This note reports that solid solutions, apparently single -phase, can be obtained for Cu-Fe alloys containing 0 to 20 and 85 to 100 at. pct Fe by rapid quenching from the melt; the inability to extend the solid solubilities further is related to the liquid miscibility gap, Fig. 1, as for Cu-Co alloys.2'3 Accurate lattice spacings of the copper-rich fcc and iron-rich bcc solid solutions have been obtained. Homogeneous alloys were prepared by casting4'5 and sintering2 from elements of 99.9+ pct purity. The quenching techniques were as before,' except the iron-rich alloys were liberally covered with argon while at elevated temperatures. Flakes about 1 sq mm in area were obtained and investigated with the Debye-Scherrer technique, as previously described.2,4 All X-ray work was done at 25° 2°C using filtered copper and cobalt K radiation. Relative visual intensities of the diffraction lines for the phases in the quenched alloys are shown in Table I. The lattice spacings of the fcc structure for alloys containing up to 80 at. pct Fe are plotted in Fig. 2. The variation of these lattice parameters with composition is in good agreement with the re- of cementite spots usually present (all hkl reflections are allowed) and the ease of confusing them with ferrite or martensite reflections. Copies of the report can be obtained by writing to the Materials Research Department, Rocketdyne. 6633 Canoga Avenue, Canoga Park, Calif., 91304. A copy is also available at the Engineering Societies Library, 2nd floor, 345 East 47th Street, New York, N.Y., 10017. Photocopies, either full-size or microfilm, may be purchased from the Engineering Societies Library. sults6 of Andersen and Kingsbury, Fig. 2, although there is some disagreement in absolute value. This discrepancy may be due to the different temperatures at which the X-ray measurements were carried out and perhaps to the different extrapolation procedures. Also, Andersen and Kingsbury6 state that their lattice spacings were computed relative to the wavelengths given by Siegbahn in 1933; this reference has not been found and it is assumed that the well-known 1931 wavelengths were used, the lattice spacings then being in kx units which are converted into angstroms by the factor 1.00202. There is no support for the contention that solution of iron decreases the lattice parameter of copper, as con-

Jan 1, 1965

By J. H. Frye, R. M. Treco

One of the chief hindrances to an understanding of the hardness of solid solutions is the sparsity of suitable hardness data. There is great need of a large body of hardness data obtained from many different alloys of high purity by identical testing methods and corrected to correspond to a single grain size. A considerable amount of such data has been obtained by means of the Meyer analysis on copper-rich and silver-rich solid solutions. There are enough of these data to permit comparison of numerous alloys at equal solute concentration in these two solvents, but only in a few cases is it possible to construct hardness-concentration curves for any given alloy. Therefore additional hardness work on most of these alloys is desirable. The primary solid solutions of silver with cadmium, indium, tin, or antimony as solute are of special interest, since all elements are from the same period of the periodic table and since, as shown previously,l the hardening effect of equal percentages of these solutes is proportional to the lattice expansion produced by them. This paper presents the relation between hardness and concentration in the silver-antimony system from very dilute to nearly saturated solutions of antimony in silver. Experimental Procedure Alloys were made from silver, 99.99 per cent pure, and antimony, 99.975 per cent pure. Silver and antimony were placed in graphite crucibles that had an ash content of less than 0.7 5 per cent. These metals were melted and allowed to solidify in a vacuum, which, after melting was corn- . plete, was usually equivalent to 3 mm. of mercury. A high-frequency furnace was used. The ingots so obtained were worked and annealed to lessen segregation and to control grain size. Annealing was done in evacuated and sealed glass tubes. Hardness measuremeuts on specimens from these ingots were by means of the Meyer analysis.394 Using a 4-mm. ball, impressions were made under seven loads from 25 to 400 kg. The diameter of impression made under each load was measured. This enabled calculation of the constants in the well-known formula of Meyer. L = adn where L = load, d = diameter of impression, a = a constant, n = a constant The Meyer hardness is defined as P = L/i(1/4pd2) or P = 4adn-2/p Meyer hardnesses corresponding to d = I and to d = 4 are of especial interest, since the first corresponds to comparatively slight 'plastic deformation and the second to the maximum plastic deformation producible by penetration of the ball. These

Jan 1, 1945