Search Documents

By Leroy A. Palmer

All the domestic production of magnesite during 1925 came from two states, California and Washington. Of a total of 120,660 tons of crude ore, 64,600 tons, or 54 per cent., were produced in California.' Of this quantity California produced about 99 per cent. of the caustic calcined, but only 10 per cent. of the dead-burned. The largest producer was C. S. Maltby, of San Francisco, who operated the Red Mountain mine, in Santa Clara County, and the Sampson mine, in San Benito County, under lease. These two mines have been studied by the author, and offer interesting comparisons as to mining and treatment methods and final products. Geology The general geology of the magnesite deposits of California has been described by Hess,2 Bain3 and others4 and although a detailed discussion is not necessary here, a brief summary will assist in understanding mining conditions. California magnesite, when comparatively pure, is usually a white, fine-grained rock, with a conchoidal fracture, occurring in veins and lense-like masses in serpentine. The veins vary considerably in width, and usually occur in a series of more or less parallel veins intersected by other series or systems of veins, probably following original or secondary fissures in the enclosing serpentine. The most generally accepted theory of origin is that the magnesite was formed by the action of surface waters charged with CO2 percolating downward through fissures and changing the magnesium silicates of the serpentine into magnesium carbonate.

Jan 1, 1927

By Prakash C. Kapur

Many balling and gradation system6 generate self- similar size distributions of the agglomerates. Inspection of the experimental data shows that this is also true of the steady state distributions resulting from the granulation of coarse, partially wet powders, for example, the fertilizer feeds. This result is exploited in the derivations of a number of simple and useful relationships that are pertinent to the analysis of these agglomeration systems. The bonding liquid demand of the granulating charge is a third order polynomial function of the dimensionless ratio of feed particle size to median granule diameter in the weight-fraction distribution. The median size, in turn, is the scale factor or characteristic size parameter in the similarity distribution. The granule size distribution, therefore, is completely specified by the liquid content and the similarity function, and so are the process efficiency and the ungranulated component In the product at steady state.

Jan 1, 1977

By S. S. Clarke

THE opening of zinc-lead ore bodies in the lower chert beds of the Tri-State district, locally called sheet-ground deposits, [ ] presented several new economic operating problems to be solved before the low-grade deposits could be mined profitably. Drilling was the first high-cost problem and loading and haulage difficulties followed. At this time, the sheet-ground mines are producing about 2000 tons per day. GEOLOGY The geology and ore deposits of the Tri-State district have been covered in detail by [ ] Fowler and Lyden.* Briefly, the sheet-

Jan 1, 1942

By C. W. Goodale

I. INTRODUCTION. In the summer of 1909 the Boston & Montana reduction department of the Anaconda Copper Mining Co. completed a new flue system, at a cost of about $1,100,000, and -is this includes the largest and highest chimney in the world, and some new features of flue construction, a description will be of interest. At the Spokane meeting of the Institute in September, 1909, a brief mention was made of this flue system, in discussing Mr. Brunton's presidential paper on the Progress of Metallurgy in the West, and a promise was given that when a long enough time had elapsed, so that operating results could be given, a paper would be offered. The smelting plant includes blast furnaces, MacDougall roasters, gas-fired reverberatories, and converters.

Jan 8, 1913

By A. B. Kinzel

Precise knowledge regarding the effect of heat treatment on the properties of steel has made possible the detailed specifications and instructions covering optimum heat-treating temperatures and practices that are in current use. A distinct contrast is presented by the metallurgical treatment of steel adjacent to a fusion weld, as such steel is subjected to each temperature from room temperature to fusion temperature, and cooled at a rate that is not generally controllable but is predetermined by the nature of the assembly to be welded, the kind of welding used, and the surrounding conditions. This is true regardless of the type of fusion welding: oxyacetylene, electric arc, thermit or flash resistance. Therefore it seemed desirable to investigate the effect of this metallurgical treatment on the characteristics of carbon steels commonly used for welding, by a detailed study of metal subjected to each temperature range; i.e., each heat-affected zone. Oxyacetylene welding was chosen for the investigation because of the experimental facility of accurately segregating and studying each temperature zone. The nature of the zones produced by other types of welding is the same. The difference is primarily a matter of dimensions of each of the temperature zones involved. The advantages and disadvantages of the extent of the zone are of prime moment, and are discussed after the presentation of the detailed zone study. No mention is made of the fused metal proper, as this has been the subject of much published research and the nature of the solidified metal is fairly .ell known. General Method The scheme of procedure in the work herein reported involved the testing of the metal of each temperature zone adjacent to the weld in so

Jan 1, 1935

By A. B. Kinzel

Precise knowledge regarding the effect of heat treatment on the properties of steel has made possible the detailed specifications and instructions covering optimum heat-treating temperatures and practices that are in current use. A distinct contrast is presented by the metallurgical treatment of steel adjacent to a fusion weld, as such steel is subjected to each temperature from room temperature to fusion temperature, and cooled at a rate that is not generally controllable but is predetermined by the nature of the assembly to be welded, the kind of welding used, and the surrounding conditions. This is true regardless of the type of fusion welding: oxyacetylene, electric arc, thermit or flash resistance. Therefore it seemed desirable to investigate the effect of this metallurgical treatment on the characteristics of carbon steels commonly used for welding, by a detailed study of metal subjected to each temperature range; i.e., each heat-affected zone. Oxyacetylene welding was chosen for the investigation because of the experimental facility of accurately segregating and studying each temperature zone. The nature of the zones produced by other types of welding is the same. The difference is primarily a matter of dimensions of each of the temperature zones involved. The advantages and disadvantages of the extent of the zone are of prime moment, and are discussed after the presentation of the detailed zone study. No mention is made of the fused metal proper, as this has been the subject of much published research and the nature of the solidified metal is fairly .ell known. General Method The scheme of procedure in the work herein reported involved the testing of the metal of each temperature zone adjacent to the weld in so

Jan 1, 1935

AT the meeting of the Board of Directors held on June 25, 1926, and in response to numerous in-dividual suggestions for changes, a committee on Re-vision of the Constitution and By-Laws of the Insti-tute was appointed, consisting of C. F. Rand, Archi-bald Douglas and H. Foster Bain. Various confer-ences were held, much correspondence conducted and a preliminary draft was prepared. It proved imprac-ticable to complete the work in time to submit the matter to the membership for approval or disapproval at the annual meeting in 1927, and the Committee was continued with instructions to prepare a report as a basis of action in 1928. After Mr. Rand's death George Otis Smith was appointed in his place and the tentative draft herewith submitted has been pre-pared in its present form by Messrs. Smith, Douglas and Bain, though not differing in any material mat-ter from an earlier draft approved by Mr. Rand. In preparing this the Committee has kept in mind primarily the desirability of simplification and of making the By-Laws conform to the actual practice of the Institute as worked out through experience. The Constitution and By-Laws adopted in 1912, and which with minor amendments only still govern the Insti-tute, are full of specific provisions regarding pro-cedure; such as that laid down for guidance of the Papers and Publications Committee. Many of these have proved unworkable and in practice have not been always strictly followed. It now seems wise to write into the Constitution and By-Laws only the general fun-damental principles to he followed and to provide for such easy change in methods of following them out as will permit efficient conduct of the business. It is this thought that has guided the Committee in rewrit-ing many of the sections. With this in view also the Constitution, as such, has been shortened to the brief-est feasible statement of fundamentals. All matters relating to means of making these principles effec-tive have been put into the By-Laws or in the hands of committees whose work is subject to control and whose rules are subject to approval or disapproval by the Board of Directors. Many suggestions for changes have come to the Committee that have not been incorporated in this draft. Some of these are in themselves excellent but have not been incorporated here because the Commit-tee discovered no sentiment for them such as would be likely to secure their approval, or found them out of harmony with the general plan followed herein.

Jan 9, 1927

By Louis J. Demer, Paul A. Beck

As reported in a previous publication,1 isothermal grain growth in high purity aluminum and in an aluminum alloy with 2 pct magnesium can be adequately described by means of the empirical relation: [ ] or in some cases, by the simpler relation, [ ] Here, D is the average grain size after an annealing period t. The annealing period includes the time for complete recrystallization R, and the time for grain growth [to]. DA is the grain size as recrystallized, n is a parameter depending on the temperature and on the material. The effect of 2 pct magnesium in solid solution was to decrease D, and to increase R, A and n at a given temperature. The present work was undertaken in order to investigate the above listed effects of magnesium in solid solution, as functions of the magnesium content. The work also includes the study of certain anomalous effects observed in the recrystallization and grain growth of the 2 pct magnesium alloy at 350°C. EXPERIMENTAL PROCEDURE The method of producing the ingots used in this work was described in detail1 and need not be reproduced here. The materials used were high purity aluminum, furnished by the Aluminum Co. of America, of lot analysis shown in Table I and magnesium from a high purity distilled stock of magnesium crystals. [ ] Ingots were prepared for a series of binary aluminum-magnesium alloys of increasing alloy content. The numbers used to designate these ingots and their magnesium contents by chemical analysis are given in Table 2. [ ] The analyses showed no difference in composition between the top and the bottom of the ingots. Spectrographic analysis of the ingots for elements other than magnesium showed, within the limits of accuracy of the method, no increase in impurities over the amounts given in the lot analysis for the high purity aluminum in Table I. Careful microscopic study of ingot 21 in the as-cast condition, at magnifications up t0 1500X, revealed a cer-

Jan 1, 1948

By G. S. Ansell, J. Weertman

The creep behavior of an aluminum alloy hardened with a finely dispersed phase of aluminum oxide was investigated. The as-extruded alloy shows an approximate steady-state creep in which the creed rate depends exponentially on the applied stress. The activation energy of creeb is abbroximately 150,000 cal per mole. The recrystallized alloy shows no steady-state creep. ONE method of improving the creep resistance of a metal is to introduce a finely dispersed second phase into the metal matrix. The improvement of the creep resistance has been qualitatively explained by assuming that the dispersed second-phase particles act as obstacles to dislocation motion. If the main effect of second-phase particles is simply to hinder dislocation motion then it is possible to derive a high-temperature creep equation for a dispersion-hardened alloy in a straightforward manner. In the Appendix of this paper such an equation is derived from a creep model which works very well for pure metals. Recently, F. V. Lenel has fabricated, for the first time, powder extrusions of aluminum-aluminum oxide in a large-grained recrystallized form. This alloy, designated as MD 2100, consists of a fine dispersion of aluminum oxide plates in a matrix of commercial purity aluminum. A considerable amount of investigation has been carried out concerning the microstructure and physical properties of this alloy.&apos; ) The aluminum oxide is present in the form of flakes 130A units thick and 0.3 u on edge. They are dispersed in the aluminum matrix with an average spacing of approximately 0.5 jx. The spacing varies in the range of 0.05 to 1.5 µ. The alloy structure is extremely stable at high temperatures. For this reason the alloy offers a unique opportunity for a fundamental study of creep of a very finely dispersed two-phase alloy. Lenel supplied specimens in both the unrecrystallized and recrystallized condition. This paper reports high-temperature creep experiments carried out on these specimens. The results obtained were rather unexpected. No steady-state creep was observed in the recrys-tallized material. In fact, after some transient creep which takes place upon loading, the creep rate is essentially zero ( < 10-8per min). If the second-phase particles acted solely as obstacles to the motion of dislocations, measurable steady-state creep would be expected. Since none is observed it appears that the main effect of the fine dispersion in the recrystallized material is to inactivate the dislocation sources themselves, rather than hinder the motion of dislocation loops created at these sources. EXPERIMENTAL DETAILS Specimens were tested in wire form, 0.087 in. in diam for the as-extruded alloy, and 0.035 in. in diam for the recrystallized alloy. These samples were held in friction-type wire grips; a gage length of 2.5 cm was used for all the creep tests. The specimens were held at 600°C in the test apparatus for at least 15 hr prior to each test. The tests were run under the condition of constant loading and, since the creep strains were small, can be considered as constant stress tests. The temperature of testing was held constant within 3°C. Elongations were measured with an optical cathetometer which was capable of measuring strains as smaIl as 0.00012. This allowed the measurement of strain rates as low as l0-8&apos;per rnin. In addition to the creep tests optical micrographs were made in order to determine both the grain size and microstructure of these materials. RESULTS Fig. 1 shows a few typical creep curves obtained from the as-extruded material. The elongations were somewhat erratic, but each curve shows a region of quasi-steady-state creep from which an approximate steady-state creep rate can be obtained. In general the higher the stress at a given temperature, the greater the total elongation before fracture. The lower the applied stress, the longer is the region where the creep rate is almost constant. Summary data from the creep tests of the as-extruded material are listed in Table I. The steady-state creep data of the as-extruded material for a range of stresses at a constant temperature follow a creep equation of the type creep rate = K&apos; = A exp (&) [11 where A and B are constants, k is Boltzmann&apos;s constant, T is the absolute temperature, and a the stress. The standard error of estimate of the data received is less than one order of magnitude. As shown in Fig. 2, if one compensates the creep-rate data for the effect of temperature over the range of test temperature, the steady-state creep data roughly follow a creep equation of the type Temperature compensated creep rate = K* = A exp

Jan 1, 1960

By C. H. Mathewson

ABOUT fifty pages of Henry M. Howe&apos;s profound treatise, "The Metallography of Steel and Cast Iron," are devoted to twinning with special reference to the origin, nature and general significance of the Neu-mann bands in ferrite. Howe believed with Osmond and Cartaud1 that the Neumanns are mechanical twins and his careful observations leave no doubt that these straight-sided narrow bands habitually occur parallel to trapezohedral planes of form {211}. Attempts to develop the structure of the bands by various methods so that their identity could be established beyond question have not been conspicuously successful. Howe thought that they deflected slip bands. Some of the etching figures which have been developed within and adjacent to Neumann bands support the contention that they are twins. A good example of this effect in ferrite containing 0.6 per cent. of nickel and 1.3 per cent. of phosphorus, originally due to Harnecker and Rassow,2. was reproduced in the 1928 lecture before the Institute of Metals Division on twinning in metals.3 In this case, the sides of the figures might represent the traces of cubic planes laid bare by etching a properly oriented grain of ferrite, twinned along a plane of form 12111. Our own observations in this direction may be represented by Fig. 1 which shows in a deeply etched cavity in the boundary region between a Neumann band and the original crystal two small crystal surfaces which resemble the faces meeting at a reentrant angle in the simple cube twinned along a bisecting plane of form {211} as sketched in Fig. 2. Rosenhain and McMinn4 in 1925, after a careful study of slip bands in ferrite containing Neumanns previously produced by shock, concluded

Jan 1, 1928

By W. J. Putnam, H. F. Moore

THIS paper gives a preliminary summary of results of tests on the resistance to fatigue under reversed stresses of steel subjected to cold-working and of tests to determine the effect of rest on the endurance of steel under reversed stresses. The tests of cold-worked steel were undertaken as part of an investigation by the National Research Council Committee on Fatigue Phenomena of Metals and were made by Mr. Moore; the tests to determine the effect of rest are part of an investigation now being made by Mr. Putnam. Both series of tests were made in the Materials Testing Laboratory of the University of Illinois. The preliminary results of these tests are reported now because it is believed that test data on fatigue strength should be available at the earliest possible moment; however, it should be clearly kept in mind that this paper gives preliminary results and is intended to encourage discussion rather than to give final conclusions. Before giving the data of the tests, the writers will explain the term "fatigue strength" as used in this paper and will discuss briefly the method used in interpreting the test data of repeated-stress tests. " The term fatigue strength, as applied to a material, may be defined as that maximum fiber stress that will cause fracture of the material after the repetition of any given number of cycles of stress, each cycle involving the variation of stress from a minimum to the above maximum. The fatigue strength, then, varies with the number, of repetitions occurr,ing in the lifetime of a structural or machine member and with the range of stress for each cycle of stress. The fatigue strength will be lower for a member in which the stress is completely reversed than for one in which the stress varies from zero to a maximum. In interpreting test data from fatigue tests under reversed stress, the stresses and corresponding numbers of repetitions required for failure are plotted on logarithmic cross-section paper. In 1910, Professor

Jan 1, 1920

By R. S. Dean

THE first attempt to establish an equilibrium diagram of the lead-antimony series was made by Roland-Gosselin1 in 1896. This investigation classified the system as a purely eutectiferous one, with the eutectic at 12.5 per cent. antimony and 228° C. In the next year, Stead2 placed the eutectic temperature at 247° C. The error in temperature made by Roland-Gosselin, however, has been perpetuated in the literature with a remarkable degree of persistency; this value was accepted by Campbell (1902), and Ewen (1910),3 and will be found in the last edition of Desch&apos;s3 Metallography (1922). Gonterman&apos;s investigation, made in 1907, was the most complete one available at the time the present investigation was started. He concluded&apos; that the system was a simple eutectiferous one and placed the eutectic at 13 per cent. antimony and 247°C. Other investigations by Tammann (1907),5 Garbow (1909),6 Rudolfi (1910),7 Loebe (1911),8 and Leroux (1913)9 added little, if any-thing, to Gonterman&apos;s diagram. A number of investigations have been made of physical properties of the alloys. The electrical conductivity of the series was studied by Matthiessen (1860)10 and by A. W. Smith (1921);" the thermoforce by Rudolfi (1910),12 and Pelabon (1923);13 the specific heat by Durrer

Jan 2, 1926

By Larry G. Hayes

Development of the Bowers-Campbell zinc deposit, located in the Shenandoah Valley two miles northwest of Timberville, Va., was commenced in 1956 by the Tri-State Zinc Co. The occurrence of lead-zinc mineralization in this area has been known for many years, but the first serious exploration program was initiated in 1951 by the geologic staff of Tri-State Zinc Co. Ordovician dolomites. The deposit is approximately 700 ft long, 100 ft wide, and 475 ft thick. Its projected plan has an elongated ovoid shape, where- as the profile appears boot-shaped with the upper portion outcropping. Vertical cross sections show the lense as having been thrust-faulted along certain bedding planes. The movement along these bedding thrusts varies greatly and in one case, has offset the deposit so as to divide it into an upper and lower orebody. The breccia lense strikes parallel to the N 34" E strike of enclosing strata.

Jan 9, 1960

By L. E. Wemple

Previous to 1915, zinc refining had not become a general practice among the zinc smelters in the United States. Such refining as had been carried on was confined chiefly to remelting very high-leaded zinc, such as third-draw metal from the retort furnaces, and slab dross, and hard spelter from galvanizing pots. In this remelting operation, the lead and iron were settled out and the refined spelter obtained graded fifth class, ie., Prime Western. Owing to the presence of lead in most zinc ores, the bulk of the spelter produced by direct smelting is of this Prime Western grade. Careful selection of ores of low lead content gave purer grades of spelter, z.e., Brass Special and Intermediate; and smelters which could secure ores carrying practically no lead produced high-grade spelter. Thus, in general, the grade of spelter produced by any smelter was predetermined by the purity of the ore it could obtain. The needs of the warring nations of Europe for enormous quantities of cartridge and other high-grade brass resulted in such a demand for the purer grades of spelter that the available supply of lead-free and low-lead ores could not produce the quantity required. Prime Western grades went begging, so to speak, while high grades sold at times from 5 to 15 c. per pound over the Prime Western market. The great demand, coupled with the wide market margin, which permitted the inherent costs and losses, resulted in the conversion of the lower grades into higher grades by processes of refining. These conditions also accentuated the development and size of the electrolytic plants, which were being worked out at the time this increased demand for pure grade of metal occurred. The electrolytic process, where available, produces a higher grade of spelter from impure ores than does the fire process; a large portion of those impurities in the ore, which by the distillation process would be carried into the spelter, are removed in the leaching of the ores and the purification of the solutions. The refining process, adopted at a number of smelters for the purpose of converting low-grade spelter into grades suitable for bras4 was that of redistillation.

Jan 1, 1918

By H. Reinhardt, P. Haglund, J. Rydberg, B. Lunden

As legislation to minimize pollution in effluent streams becomes stricter, it is important to treat used acid pickling baths before discharge. This is usually achieved by neutralization of the acids and precipitation of the dissolved metals in such a way that neither acids nor metals can be re-used. A process has been designed and tested on a pilot plant scale to recover both acids and metals from a stainless steel pickling bath leaving only Na2SOs in the effluent. In this process, H2SOr is added to the spent pickling liquor and the recovery of the pickling acids HN03 and HF is achieved by solvent extraction, using TBP in kerosene as the organic solvent. The extracted acids are stripped with water, giving an acid concentration high enough for direct use in the pickling bath. Molybdenum is also extracted by TBP and is recovered in a separate step. The other metals, Fe, Cr and Ni, are precipitated from the raffinate as hydroxides, dried and recycled to the metal process. In evaluating this process, comparative experiments with mixer-settler and pulsed column have been performed. The process described is being considered for use by a Swedish company pickling 70,000 tons per annum of stainless steel.

Jan 1, 1973

By Donald H. McLaughlin

THE primary function of the mining engineer is to find mineral deposits and fuels in the accessible rocks of the earth and to recover them for the vast needs of our complicated civilization. On him has been placed the responsibility for the exploitation of the nation&apos;s and world&apos;s mineral resources. The degree to which the minerals of the earth have been utilized serves to an extent as a measure of man&apos;s material advancement, as well as an index of the relative strength of nations. The natural endowment of lands, varies greatly, but the intellectual energy of a people is revealed by the way in which they take advantage of their heritage of minerals or reach out to less developed regions by exporting their engineering skill as well as capital to secure the raw materials they need.

Jan 2, 1953

By J. A. Snyder, W. L. Finlay

SEVERAL notable studies of the effects of sub- stitutional solutes have been reported. Outstanding among these for its elucidation of general principles, is the summarized work of Hume-Rothery and coworkers.1 For a systematic study of the effects of substitutional solutes on the mechanical properties of the solvent lattice, the work of Brick, Martin, and Angier² on copper; of Frye and coworkers³,4,5 on copper and silver; and of Lacy and Gensamer6 and of Austin7 on iron may be mentioned. Titanium is one of the few elements offering the possibility of a similar study of interstitial solutes since, unlike most metallic elements, it exhibits extended solid solubility for most of the interstitial solutes—hydrogen, boron, nitrogen, oxygen, and carbon. This paper reports a survey of the effects of dilute solutions of nitrogen, oxygen, and carbon on the mechanical properties of high-purity alpha titanium. Previous Work: Van Arkel and De Boer showed" that high purity titanium was quite ductile and De Boer, Burgers and Fast established".&apos; that not only were oxygen and nitrogen very soluble in solid titanium but that, long before the limit of solid solubility of either had been reached, these interstitial solutes rendered the metal brittle. Their electrical resistance data as a function of

Jan 1, 1951

By R. T. Southin

Cast ingots of 99.99 pct purity A1 and aluminum/copper alloys containing up to 2 pct Cu have been found to contain four zones rather than the three previously accepted, i.e., chill, colummar, and equiaxed zones. The fourth zone consists of a coarse dendritic layer across the top surface of the ingot which is open to the atmosphere. It is also found that the grains in the equiaxed region have a "cornet" shape, with a head which is coarsely dendritic and a tail which grew with the same structure as the columnar grains. Experiments using mechanical barriers, and others involving the elimination of the surface dendrile layer, have indicated that nucleation of the equiaxed zone is caused by the showering of dendritic particles from this surface dendrite layer. These particles are the dendritic heads found in the comet grains. A mechanism of nucleation and growth of these comet grains is put forward. Experiments with a number of other metals and alloys suggests that these conclusions may apply generally to ingots cast without the addition of nucleating agents, and solidified under normal conditions. THE macrostructure of cast ingots may contain the following three zones: i) a peripheral zone of fine equiaxed grains, commonly called the chill zone; ii) a zone of columnar grains extending inwards from the chill zone; iii) a central zone of equiaxed grains; these are normally larger than the chill grains. All three zones are not necessarily present in any particular ingot since their existence and magnitude depend upon the casting conditions and composition of the cast material. The mode of formation of zones i and ii is fairly well understood. However, the cause of the central equiaxed zone remains a matter of conjecture. Previous theories put forward to explain the mechanism of nucleation in the equiaxed zone have been examined by Chalmers1 and Winegard.2 At the time when the present work was carried out the most re -cent hypothesis was that due to Chalmers,1 who recognized more fully than previous workers that conditions in this zone during solidification were not conducive to nucleation. In his hypothesis, he suggested that nuclei were formed near the mould wall during the very early stages of solidification, and that they can drift into the central zone by convective motion. This was supported by evidence from experiments using mechanical barriers to stop the drift of nuclei. A similar hypothesis had previously been put forward by Genders.3 More recently, Jackson et al. 4 have observed that dendrite arms in organic compounds can melt off during solidification. They have postulated that this occurs in metals and alloys, and that the dendrite arms which have been freed from the main dendrite act as nuclei for the equiaxed zone. In the present work, critical metallographic examination has shown that there is a fourth zone in the macrostructure of cast ingots which is a dendritic layer over the top surface of the ingot. It is also shown that there is a relationship between this zone and nucleation of the equiaxed zone. EXPERIMENTAL DETAILS The alloys examined were prepared from super -purity aluminum of 99.99 pct min purity (spectro-graphically detected impurities of Cu, Fe, Si, and Mg) and copper of 99.98 pct min purity (spectrographically detected impurities of Si, Zn, As, Fe, Pb, Bi, Ni, Sn, Mn, Ag, Cr, and Al). Three compositions of ingots were examined, containing 0.0, 0.1, and 2 pct Cu, respectively. The alloys were melted in an alumina-lined salamander crucible using a medium-frequency electric induction furnace; when the appropriate casting temperature was reached, the alloys were cast without degassing or fluxing treatment. The mould used was made of electrode graphite and had the following dimensions: external diameter 6 in., height 9 in., with a mould cavity 8 in. deep and a diameter tapering from 5 in. at the top to 4 in. at the bottom. Casting temperatures used were generally in the order of 70" to 90°C above the liquidus and the mould was at room temperature before casting. Inserts kere placed in the mould cavity in some experiments. These consisted of either an 18-g stainless-steel tube of 2 in. diam held axially in the mould i in. off the bottom and extending 1 in. out of the top of the mould or a "trap-door" barrier of stainless-steel gauze of 24-mesh held horizontally in the mould 31/2 in. down from the top. The construction of this insert is shown in Fig. 1. All inserts were preheated prior to casting to prevent chilling. RESULTS The macrostructures of ingots of the three compositions are described, in terms of the three generally recognized zones, in Table I, and illustrated in Figs. 2(a) to (c). The most interesting observation in this table is that relating to the shape of the equiaxed grains, which were not in fact equiaxed but of almost tear-drop shape. Closer examination of these grains showed that each consisted of a head which had a coarse dendritic structure and a tail which always grew in the opposite direction to heat flow, and which had the same structure as that of the columnar material of the ingot concerned; i.e., in the pure aluminum and 0.1 pct Cu alloy it was cellular and in the 2 pct Cu alloy it was cellular-dendritic. Identification of original cast grains was greatly hampered in the super-purity aluminum ingots, and to a lesser degree in the 0.1 pct Cu alloy,

Jan 1, 1968

By C. M. Schwartz, A. E. Austin, W. B. Wilson

High-temperature X-ray diffraction studies were conducted with Th-U alloys with up to 10 wt pet U. The solid solubility of uranium in thorium as a function of temperature was determined by the method of lattice parameters. Thorium will dissolve up to 2.5 wt pet U at 950°, 4.5 wt pet U at 1150°, and 7.5 wt pet U at 1250°C. Determinations were made of the temperature of the transition of thorium and of the effect of uranium upon the transition. The a to ß transition for thorium was observed to occur at 1330&apos; ±20°C. Mean coefficients of expansion were calculated for thorium and two alloys, and for ThO2 in contact with the thorium, using X-ray lattice-parameter data. Values obtained at 950° C for thorium and Tho2 were 12.1 and 9.40 X 10-6 per OC, respectively. Impurities obtained during the X-ray exposure were identified by diffraction and were essentially Tho2 and ThC, with two additional unknown phases being detected. The effect of the impurities upon the results is discussed. DIRECT investigation (i.e., high-temperature X-ray diffraction studies) of the phase diagram of thorium-rich uranium alloys has been shown to be necessary since recent work1 - has disclosed the presence of an allotropic transformation near 1400°C in pure thorium with the room temperature face-centered-cubic phase transforming to a body-cen-tered-cubic structure at the elevated temperature. The effect upon the transition of the addition of uranium to thorium and of the solubility of uranium in thorium at high temperatures remained unknown, yet was of interest in understanding fabrication procedures and elevated temperature use. The present work was undertaken to provide information in this area by determining the transition temperature, the effect of uranium on the transition temperature, and the solubility of uranium in thorium as a function of temperature. Experimental Work The high-temperature diffraction data were obtained using a camera especially designed for the purpose3 and capable of reaching temperatures in excess of 2000°C at pressures as low as 1 x 10." mm Hg. Temperature regulation was provided by regulating the power input to ±0.1 pet variation, and by regulating the water flow through the camera jacket to provide a constant thermal load. The X-ray sample was a rod nominally 80 mil diam, which was further turned down to 20 mil and then etched to 18 mil over 1/2 in. of one end. This was placed in the sample holder and mounted on the camera so that the smaller part was surrounded by a cylindrical tantalum-sheet radiation-type heating element. Diffraction from the sample was recorded on film after passing through a slot in the heating element and radiation-baffle shield and through beryllium vacuum windows. The X-ray film mounting was of the Straumanis type4 with a camera diameter of 114.59 mm. Since previous work of Chiotti&apos; indicated that impurities considerably alter the transition temperature, chemical analysis of the arc melted iodide crystal-bar thorium samples was obtained prior to testing. The analysis disclosed the material to contain as low as 0.001 ±0,0002 wt pet H and 0.007 ±0.001 wt pet 0. Carbon was 0.003 wt pet and nitrogen less than 0.002 wt pet. This material was sealed in mild steel in an inert atmosphere and subsequently hot rolled to 3/8-in. diam rods at a temperature of 732°C. Following removal of the jacket, the material was pickled and cold swaged to 1/8-in. rods, from which the diffraction samples were prepared. The alloys were similarly prepared, with the uranium being added during arc melting. The uranium analyses of the alloys prepared appear in Table I. The experimental procedure for diffraction examination of the three samples of high-purity thorium differed from those of the Th-U alloys. The original practice, later modified, consisted of pumping down the camera with the diffusion pump on and then admitting liquid nitrogen to the cold trap of the system. This was modified for the Th-U alloys by maintaining liquid nitrogen in the cold trap at all times before and while the diffusion pump was heated. This minor change produced a reduction in the amount of carbon pickup by the sample during exposure to the diffusion-pump vapors. The sample was brought to the desired test temperature and exposed for 21/2 hr at pressures which were usually 2 x 10-6 mm Hg, or lower. Exposures were made at

Jan 1, 1959

By William G. Kegel

Apart from a usable product and good mining conditions, the greatest asset for a profitable coal mining organization is an effective mine maintenance program. The first step in achieving this is to have good mechanics-or men who want to be mechanics and are interested in knowing ,more about the design and control of the machines in their charge. A good mechanic&apos;s knowledge and ability result from ambition, curiosity, and determination. Starting with these qualities, the aspiring mechanic can launch his career by learning all he can about mechanics, electricity, and hydraulics. Though the path is rough, the end result is rewarding. Mining machinery probably receives as much, if not more, abuse as any other heavy equipment in use today. Considering the conditions under which much of the repair work must be done, it is essential that the mine operator has the best men and tools to perform the work. Mining machines, from their inception, have utilized the electric motor ; and down through the years of mechanization, this power source has undergone many changes to better adapt it to the job. The first motors used were direct-current (d-c) motors since d-c power was the most economical power source for mining at the time of early mechanization. These motors were large open-type machines which are seldom used in modern mining. Because of the mine environment, the d-c motor has been reduced in size to better suit the application in mining machines and is now manufactured with dust-tight or explosion-proof enclosures. The d-c motor is constructed with either (or both) series and shunt fields located on the stationary part of the motor (stator) and an armature coil wound on the rotating part of the motor (rotor). Power is supplied to the armature by brushes which are held stationary and make sliding contact with the armature. The brushes requires regular and careful maintenance because worn or defective brushes will cause heat or arcing which can destroy the motor. D-c motors can be used as d-c generators when mechanical power is supplied to them by the rotating

Jan 1, 1981