By J. D. Edwards, C. S. Taylor, A. S. Russell

Solubilities and densities are reported for alumina hydrates in NaOH solutions under the conditions of the Bayer process employed to purify alumina for aluminum production. The equilibrium constants for reactions to form A102- accurately correlate the effects of NaOH concentration on the solubilities; the temperature coefficients of the equilibria lead to heats of solution of 7.34, 4.76, and 5.24 kcal for the a trihydrate, a monohydrate, and ß trihydrate, respectively. Moderate calcination does not change the solubility of the a trihydrate but increases that of the a monohydrate. At solution temperatures above 100°C, the trihydrates transform rapidly to a monohydrate. Hydro-thermally produced a monohydrate is the stable phase above 20°C. CORNERSTONE of the aluminum industry, the Bayer process for alumina production is based on the difference in solubility of hydrated alumina in NaOH solutions between 170" and 40°C. Solubilities and densities in this system were determined thirty years ago by M. Tosterudl under the direction of J. D. Edwards and C. S. Taylor. The solubility data, which still appear more concordant than those in the literature, are employed to sort out the complex equilibria in this system. The nomenclature for the alumina hydrates is that presented in The Aluminum Industry' and more recently summarized in Alumina Properties.3 a trihydrate is the purified phase analogous to gibbsite, a monohydrate is similarly akin to boehmite, and ß trihydrate is sometimes known as bayerite. Literature Goudriaan4 reviewed the early literature on alumina in NaOH solutions and presented data on the solubility at 30°C of several forms. The gel precipitated from aluminum sulphate or chloride with ammonia and dried at 130" to 140°C had the highest solubility but was unstable, its solubility being cut to one-tenth on standing in NaOH. The solubility of the gel was decreased one-third on calcination at 300" to 400°C, while that of the gel transformed in NaOH at room temperature to a crystalline trihydrate was unchanged on calcination. The preparation produced by slow hydrolysis of sodium aluminate solution with CO, in the air gave solubilities in rough agreement with later values for a trihydrate. The solubility of this form was increased slightly by the calcination. Fricke and Jucaitis5 extended the work to 30" and 60°C with a trihydrate. They also gave solubilities for ß trihydrate (bayerite b), although the residue belonging to the left branch of the solubility curve corresponded to a trihydrate. The residues at high NaOH concentrations were mono and trisodium aluminates, the latter being 3Na2O . AL2O3 • 6H2O. Solubilities of a trihydrate at 95°C and of a monohydrate at 150" and 200 °C come from the work of Magarchak.6 a trihydrate transformed to a monohydrate above 95°C. A few measurements on the solubility at 25°C of an alumina trihydrate prepared by slow hydrolysis of NaAIO, solutions were presented by Sprauer and pearce.? Their analyses showed the monosodium aluminate to have the composition Na2O.Al2O3-2.5H2O.

Jan 1, 1956

By M. C. Flemings, P. J. Ahearn

Dendvite morphology of unidirectionally solidified Sn-12 pct Bi alloy was determined with the aid of X-ray and macroetch techniques. Columnar growth direction (growth direction of primary arms) in this alloy is [110]; secondary arms grow in the [lii], [111), and [112] directions. Interstices between [112] dendrite arms fill in during early stages of solidification so that well-defined (110) planes are seen in the final structure (parallel to the heat-flozo direction). Similarly, interslices betweex the [111] secondary arrlls fill in to form (112) planes, and interstices between [1111 ] arms fill in to form (112) planes. DENDRITE morphology in alloys is conveniently studied in unidirectionally solidified castings. In this type of solidification, heat is extracted from a single chill surface of the casting while other surfaces are insulated. Solidification progresses from the chill and results in cast grains that are columnar with the long axis of the grain perpendicular to the chill. Dendrite morphology is conveniently studied by examination of etched surfaces parallel and perpendicular to the chill, as previously described.'" Experimental studies on the growth direction for tin are in general agreement. The major growth direction is [110]:-' although this is altered somewhat by supercooling. In one study, tin dendrites pulled from a supercooled melt had a growth orientation 12 deg away from the [110] direction toward the [002] direction.' This orientation could be changed back to the [110] or close to the [110] direction by changing the tempera- ture gradient in the melt. In a study using autoradio-graphic techniques, (111) directions were shown to be directions of preferred growth in addition to the [110) direction.7 PROCEDURE The samples employed in this study were cut from 12 pct Bi-88 pct Sn castings, 1.5 in. in diam and 3.5 in. tall. The casting procedure consisted of heating the charge to 390°C and then pouring the molten alloy directly into a gypsum sleeve mounted on a massive copper chill. Specimens were cut from the ingot, mounted, polished, and etched with Taffs reagent [FeC13 .6H2O, 2 g; HC1, 5 cu cm;H20, 30 cu cm; CzHaOH (95 pct), 60 cu cm].' The dendritic pattern was clearly visible after etching. Photomicrographs at about 8 and 35 times were taken on surfaces parallel and perpendicular to the chill. Laue back-reflection patterns were obtained from three different columnar grains in a singIe polished face 2 in. from the chill. The cut face was polished and positioned in the beam of a Laue camera, so that diffraction occurred from a single dendritic grain. The resulting diffraction pattern was interpreted to determine crystal log raphic orientation in relation to the heat-flow direction and in relation to microstruc-ture of the given grain. RESULTS Fig. 1 shows a horizontal and vertical section of the columnar structure, at low magnification. Light regions are rich in tin, and darker regions tin-poor; the primary phase is tin-rich a phase. The two sections shown were taken orthogonally from the same metallographic specimen. It is readily seen from Fig. 1 that the dendrites have

Jan 1, 1968

By M. Herman, G. J. London

A series of dilute Fe-Co alloy specimens were prepared from zone-melted iron. The iron used was given ten floating-zone passes in purified hydrogen. Alloying was accomplished by plating a gradient of metallic cobalt onto a 1/4-in.-diam bar of material from a pure plating bath. The deposit was radioac-tively tagged by a small addition of co80 to the plating bath. Alloy homogenization was accomplished by passing an additional floating-zone pass through the plated section of the bar. The final concentration gradient achieved was from residual to about 1000 ppm (0.1 pct) added Co. After homogenization, the bar was swaged to 0.057 in. wire and cut to tensile specimen blanks 1-1/16 in. long. Each specimen was counted in a well-type scintillation counter. The concentration of cobalt was computed by combining the normalized specimen counting rate with the known weight (measured to the nearest 0.01 mg) of cobalt added during plating. Fig. 1 shows the cobalt gradient obtained, exclusive of residual cobalt which was estimated by neutron-activation analysis to be approximately 50 ppm. Results of recrystallization for 1 hr at 750°, 700°, 650°, and 600°C with specimens containing 40, 170, 470, and 870 ppm added Co are shown in Figs. 2, 3, 4, and 5. Recrystallization was accomplished in a dynamic vacuum of less than 1 x 10 torr. The specimens were mounted and polished parallel to the swaging direction. The recrystallization re- sults show a radical coarsening of structure with increasing cobalt concentration. The coarsest structure obtained was at the 470-ppm level (at all recrystallization temperatures) with a slight grain refinement at the 870-ppm level shown. A more normal solid-solution effect is seen in Fig. 5 (60OoC, 1 hr) where the only specimen completely recrystallized is the one containing 47 ppm Co. Since the possibility existed that some atmosphere-contamination phenomenon might be responsible for the observed results the recrystallization series was repeated using sealed quartz capsules. These were filled with purified argon which was gettered during heat treatment on metallic titanium included in the capsules. The results obtained were essentially the same as shown. Another identical alloy was made using a 5-mm-diam bar of Westinghouse Puron. Specimen preparation and recrystallization treatment were also as described. The results obtained (see Table I) were somewhat erratic. Some coarsening in structure does appear at the highest cobalt concentrations. There is no apparent relationship between the coarse, columnar, directionally solidified structure of the as-melted bars and any of the recrystallized grain structures observed, all of which are much finer than the former structure. A recrystallization process can be most simply described as one of homogeneous nucleation of recrystallized grains in a cold-worked matrix followed by more or less uniform growth of the strain free grain into the cold-worked material.' An impurity element may influence one or both of these processes. Aust and utter' have shown that impurities strongly influence grain boundary mobility in lead. Moreover, definite recrystallization textures are produced by small concentrations of tin,3 while additions of silver or gold4 produce large boundary in-

Jan 1, 1964

By K. A. Johnson, F. H. Ellinger, C. C. Land

The Pu-In phase diagram has been determined by thevmal, filtvation, micrographic, and X-ray diffraction methods. This alloy system is characterized by 1) limited solubility of indium (-2 at. pet) in 6 and e plutonium, 2) one eutectic, and 3) fizte intermediate phases. Of the latter, PuIn and PuIn3 melt con-gruently, and Pu31n, Pu31n5, and the high-temperatuve 7 solid solution are formed peritectically. The n phase decomposes eutectoidally into Pu3In and PuIn at 865°C. Although the 6 phase can readily be retained to room temperature, it is not thermo-dynamically stable below 300°C. The Pu-In system has been investigated at Los Alamos as part of a study of the alloys of plutonium with the group 111-B elements. Constitutional studies of the Pu-A1 and Pu-Ga systems have been reported earlier.'9' To date, published information on the constitution of Pu-In alloys covers only the identification of the intermediate phases Pu3In and PuIn3.3,4 EXPERIMENTAL The alloys were prepared from five different lots of plutonium and three different lots of indium. The principal impurities in the plutonium differed from lot to lot within the following limits (in ppm): iron, 30 to 80; nickel, 30 to 60; aluminum, 15 to 30; silicon, 20 to 145: thorium, 50 to 300; carbon, 75 to 335; and oxygen, 20 to 135. Spectroanalysis of the indium showed that two of the lots were 99.9 wt pct pure, and the third was 99.98 wt pct pure. The alloys, in the form of about 5-g buttons, were prepared by arc melting in conventional equipment. The components for each alloy were weighed to the nearest 0.1 mg. In most instances the weight losses during melting were negligible; therefore confirmatory chemical analyses were usually not made. A few results are given in Table I. Density measurements of the arc-cast buttons were made by the liquid displacement of bromoben-zene. Heat treating was done in muffle furnaces controlled to +2°C. The alloy buttons were wrapped in tantalum foil before being enclosed in evacuated clear silica capsules. As a precaution against breakage, each capsule was in turn placed in a silica tube closed with a refractory wool plug prior to being charged into the furnace. For a moderately fast quench of the alloys, the outer protection tubes containing the capsules were plunged into cold water. Differential thermal analyses (DTA) in racuo were performed at heating and cooling rates of about 1.5°C per min. Tantalum crucibles having inverted thermocouple wells were used for most of the analyses. It was found micrographically, however, that the liquid alloys containing more than about 35 at. pct In reacted with the tantalum, resulting in contamination of the surface of the alloy. A search for a more satisfactory crucible material was not successful: tungsten and yttria behaved comparably to tantalum; thoria, vitrified magnesia, and vitrified alumina severely contaminated the alloys. So as to minimize the contamination by the crucible mater-

Jan 1, 1965

By AIME AIME

As already announced in the January Bulletin, this publication will be issued during the coming year monthly instead of bi-monthly as heretofore. Among other reasons for this change, it is desired to effect thereby the earlier transmission to members of important papers, lists of candidates for membership, and other items of timely information. Spokane Meeting and Excursions. Further details of the' 97th meeting of the Institute have been sent to members in the Circular of May 8, 1909. For, convenience of the members a summary of the additional in¬formation is here presented. A special train of Pullman cars will leave Chicago about September 15. This train will be side-tracked at all places visited, and the sleepers will be available for lodging and the dining-car for meals during the entire trip, except during the Yellowstone Park tour. The general. cost of the trip per member will be $300, which includes transportation, berth, and meals for the entire trip from Chicago back to Chicago, almost 6,000 miles, and the tour through Yellowstone Park, occupying in all about 30 days. Special accommodations on the train will be furnished at the following, rates

May 1, 1909

By Strathmore R. B. Cooke, Marcus Digre

That calcium will activate quartz for flotation with anionic collectors such as soaps has been known for a number of years,12'3 and the method has been applied to the concentration of various iron ores4 5 6 as well as to other materials. Clemmer gives the permissible pH range for the activation of quartz by calcium as between 9.5 and 12.5 with an optimum value of 11.0, and Hertzog7 has determined the calcium abstraction of iron ores and of Ottawa sand, but otherwise little quantitative data are available. The purpose of the present investigation was to determine those conditions under which dilute solutions of calcium chloride will activate quartz for anionic flotation and to determine the amount of calcium ion adsorbed by quartz. Those variables, the influence of which was primary, such as calcium, sodium, and hydrogen ion concentrations, were studied. Other factors which influenced the results are discussed in the description of the experiments. Three different experimental methods were used to determine the activation of the quartz. The first method was to treat a sample of ground, deslimed quartz with solutions of calcium chloride and sodium hydroxide, and to determine the calcium adsorbed by chemical analysis of the solution. Advantages are that a direct value for the amount of calcium adsorbed is obtained, and introduction of a collector which may affect the adsorption is avoided. The difficulty is to determine the extremely small differences in the calcium concentrations before and after the abstraction. The second method was to determine the activation of the quartz by observing the contact angle obtained on pressing an air bubble against the polished surface of a piece of quartz immersed in a solution of calcium chloride, sodium hydroxide, and sodium oleate. This is the well-known "contact angle" method. The third method was to determine those conditions under which an air bubble will pick up quartz particles immersed in a solution of the desired reagents. Disadvantages common to the sec- ond and third methods are that introduction of a collector is necessary to obtain bubble contact with the mineral; very small quantities of contaminant can give erroneous results; and no information is obtainable concerning the amount of calcium adsorbed. Advantages are that tedious analyses, which at best give approximate results, are avoided, and the conditions, especially for the third method, closely simulate those of actual flotation. Although the most consistent results were obtained with the third method, this paper describes the techniques used and the results obtained from each of the three methods. Distilled water and analytical grade reagents were used throughout except where otherwise stated. Between tests all glass articles were cleaned with a chromic-sulphuric acid mixture and sodium hydroxide. Abstraction Method The raw material for the tests was Ottawa sand sized between 14 and 28 mesh. Batches of 500 g of this sand were dry ground for 1 hr in an Abbe porcelain mill with 2700 g of quartz pebbles. The batches were split down to samples weighing approximately 30 g, and the weight of each sample was adjusted to exactly this value.

Jan 1, 1950

By W. R. Davis

This paper presents a sunimary of the results of a study of the Dornick Hills-Springer sand reservoir of the Velma Pool. Stephens County, Oklahoma. The data are of interest because this type of reservoir is unusual in the mid-continent area. The reservoir is characterized by very steep dips and a relatively thick producing section. Its up-dip productive limit is defined by truncation of the productive sands, and the down-dip limit is defined by deterioration of sand quality rather than by the presence of an oil-water contact. The crude oil is of 29" API gravity, is relatively viscous and was saturated with dissolved gas at the original reservoir pressure. Consideratiqn of the physical characteristics of the reservoir indicates that natural water encroachment will be negligible, and that the producing mechanism will be a dissolved gas drive augmented by gravity drainage. Performance to date tends to confirm this. INTRODUCTION It is the purpose of this paper to present some of the features of the Dor-nick Hills - Springer sand reservoir which are unusual in mid-continent operations. The study was undertaken in an attempt to define the producing mechanism or mechanisms that will control reservoir performance, as an aid in determining well completion and production practices. GEOLOGY The reservoir under consideration is a series of sand bodies of Pennsylva-nian age found in the Lower Dornick Hills and/or Springer formations. For the purpose of this paper, the sand series is referred to as the Dornick Hills-Springer sand. This sand series lies on the northeast flank of the Velma anticline, and dips very sharply to the northeast in TWP 1S-5W, the average dip being about 45º. However, as shown in Fig. 1. the trend of the pool swings eastward in TWP 1S-4W with a coincident de- crease in dip angle. In this portion of the pool the average dip is about 25". Faults in Sections 30-1S-4W and 32-1S-4W are shown in Fig. 1. These faults show only minor displacements for the horizon contoured in Fig. 1, but they do show a pronounced displacement of the immediately overlying beds. Similar faults are thought to exist in TWP 1S-5W; however, since the detailed geological studies necessary to properly define these faults were not available to the author, no attempt to show them in Fig. 1 has been made. The up-dip productive limit throughout the pool is determined by the truncation of the Lower Dornick Hills-Springer sand. The down-dip productive limit does not appear to be defined by edge water, but by a gradual reduction in permeability of the sands. No dry hole has produced a significant volume of water from this sand section. There was a small gas cap in TWP 1S-5W. Most of the wells in TWP 1S-SW encountered an oil sand 70 ft to 150 ft thick, a shale 20 ft to 80 ft thick, and another oil sand 50 ft to 130 ft thick. A few scattered wells in this area encountered other and bodies below these

Jan 1, 1951

By W. R. Davis

This paper presents a sunimary of the results of a study of the Dornick Hills-Springer sand reservoir of the Velma Pool. Stephens County, Oklahoma. The data are of interest because this type of reservoir is unusual in the mid-continent area. The reservoir is characterized by very steep dips and a relatively thick producing section. Its up-dip productive limit is defined by truncation of the productive sands, and the down-dip limit is defined by deterioration of sand quality rather than by the presence of an oil-water contact. The crude oil is of 29" API gravity, is relatively viscous and was saturated with dissolved gas at the original reservoir pressure. Consideratiqn of the physical characteristics of the reservoir indicates that natural water encroachment will be negligible, and that the producing mechanism will be a dissolved gas drive augmented by gravity drainage. Performance to date tends to confirm this. INTRODUCTION It is the purpose of this paper to present some of the features of the Dor-nick Hills - Springer sand reservoir which are unusual in mid-continent operations. The study was undertaken in an attempt to define the producing mechanism or mechanisms that will control reservoir performance, as an aid in determining well completion and production practices. GEOLOGY The reservoir under consideration is a series of sand bodies of Pennsylva-nian age found in the Lower Dornick Hills and/or Springer formations. For the purpose of this paper, the sand series is referred to as the Dornick Hills-Springer sand. This sand series lies on the northeast flank of the Velma anticline, and dips very sharply to the northeast in TWP 1S-5W, the average dip being about 45º. However, as shown in Fig. 1. the trend of the pool swings eastward in TWP 1S-4W with a coincident de- crease in dip angle. In this portion of the pool the average dip is about 25". Faults in Sections 30-1S-4W and 32-1S-4W are shown in Fig. 1. These faults show only minor displacements for the horizon contoured in Fig. 1, but they do show a pronounced displacement of the immediately overlying beds. Similar faults are thought to exist in TWP 1S-5W; however, since the detailed geological studies necessary to properly define these faults were not available to the author, no attempt to show them in Fig. 1 has been made. The up-dip productive limit throughout the pool is determined by the truncation of the Lower Dornick Hills-Springer sand. The down-dip productive limit does not appear to be defined by edge water, but by a gradual reduction in permeability of the sands. No dry hole has produced a significant volume of water from this sand section. There was a small gas cap in TWP 1S-5W. Most of the wells in TWP 1S-SW encountered an oil sand 70 ft to 150 ft thick, a shale 20 ft to 80 ft thick, and another oil sand 50 ft to 130 ft thick. A few scattered wells in this area encountered other and bodies below these

Jan 1, 1951

By T. K. Prentice

ABSTRACTED AND REVIEWED BY E. W. DAVIS,* MEMBER A.I.M.E. THE January-February number of the Journal of the Chemical Metallurgical and Mining Society of South Africa is made up entirely of a discussion of Ball Wear in Cylindrical Mills. Following the principal paper by T. K. Prentice are several remarkably pertinent and carefully prepared discussions. Few persons in this country would be likely to see this publication, and since the information presented is new and of current interest, it seems desirable to abstract and review this publication for the benefit of the members of the A.I.M.E. The purpose of the investigation is stated in the first two paragraphs of Prentice's paper, as follows: Early in 1941, The Chamber of Mines Steel Products, Limited, initiated a series of tests under semi-working scale conditions to determine, if possible, those physical and chemical properties of a ball which make it resistant to wear when used in a cylindrical mill as a grinding medium, with the primary object of incorporating those beneficial qualities in the balls being produced at their works. This paper describes the tests carried out and discusses the results obtained. From these results it was possible to formulate a new theory relating to ball wear in cylindrical mills. This theory is presented in the second portion of this paper. PRACTICAL BALL-MILL TESTS IN A CYLINDRICAL MILL Part I of the paper begins with a discussion of the methods used for the manufacture of grinding balls in South Africa. The following paragraph is of particular interest. The cast steel ingots, 4 ¼ - in. square by 3 ft. 6 in. long, are re-heated in a gas-fired sloping stationary-hearth furnace and then rolled in a six-pass continuous mill into 2 5/8 in. round billets. Some of these billets are then removed and cut into suitable lengths for forging into 4 in., 3 ½ in., 3 in. or 2 ½ in. balls by means of three Drop and two Beché hammers, but the greater number, whilst still at about 1,000 ºC., pass directly into a set of scroll rolls which produce, in an ingenious manner, finished 3 in. balls direct from the 2 5/8 in. billets. Except in special cases, all balls are allowed to cool in the atmosphere and are not water quenched. Details of the Tests In order to enable the reader to evaluate properly the results and conclusions in the rest of the paper and in the discussions following the paper, most of the information presented by the author under this heading is quoted: ….. The testing unit was a nominal 30 in. diameter and 18 in. long centre discharge Denver Ball Mill. The ore pulp to the ball mill comprised a small portion of the normal feed to one of the fourteen City Deep 5 ft. 6 in. X 22 ft. tube mills, and the grinding media consisted of the balls under test plus other balls to give the desired load. The running time of the test-mill was divided into approximately equal periods of five days 13 ½ hours each. The usual procedure was to examine and make up the load

Jan 1, 1944

Agnico-Eagle Mines Ltd. comprises a Gold Division at Joutel, Quebec, and a Silver Division at Cobalt, Ontario. In 1979 the Silver Division milled 41,700 mt (46,000 st) of ore at a recovered grade of 139 g per mt (4.06 oz per st) for a production of 5,816 kg (187,000 oz) of silver. The 100 -year -old mining, camp of Cobalt has long been noted for its high-grade silver ores, and now seems to be on the threshold of being revived with several companies operating in the area. In 1979, the Gold Division milled at the rate of 27,200 mt per month (30,000 st) and processed 333,000 mt (367,000 st) at a grade of 6.58 g per mt (0.192 oz per st) with a mill recovery of 91.670 to produce 2,013 kg (64,700 oz) of gold. The average total cost per ton milled was $22.10 per mt ($20.05 per st) which was $3.66 per g ($1 13.90 per 0s). These figures make Agnico-Eagle one of the lowest cost producers in North America. Gold occurrence in the Joutel ore is fine-grained and contained within sulfide facies composed mainly of pyrite with minor pyrrhotite. Two underground mining methods are employed with long hole stoping accounting for about 75% of the ore mined and shrinkage stoping the remainder. Ore from underground is hoisted into a 545 mt (600 st) coarse ore bin from where it is conveyed to a 45 mt (50 st) surge bin ahead of the 10-51 Hydrocone crusher. Crushed ore is then screened to make a 13 mm (112 in.) product with the oversize being recrushed in a 7-60 Hydrocone. Mill feed is conveyed to two 900 mt (1,000 st) fine ore bins. The Hydrocones were installed as part of a new crushing plant in March of 1980 and have contributed substantially to an increase in mill capacity. Space has been left to install a third crusher in the future. The fine ore bins discharge to a 2.75 m by 3.66 m (9 ft by 12 ft) rod mill, followed by a 3. 7 m by 5.5 m (12 ft by 18 ft) ball mill in closed circuit with a Krebs 380 mm (15 in.) cyclone to produce a 7070 minus 37 micron (400 mesh) .flotation feed. This pulp is first treated in a 34 cu m (1, 200 cu ft) Maxwell flotation cell and then in an additional twelve 2.8 cu m (100 cu ft) cells. Combined flotation concentrates are reground to 9070 minus 37 microns (400 mesh) in a 1.8 m by 4.9 m (6 ft by 16 ft) ball mill in closed circuit with a single Krebs 254 mrn (10 in.) cyclone. Flotation tailings are sent to the tailings dam. Reground concentrates are then aerated with lime to a single Pachuca and thickened in a 16.75 m (55 ft) diameter thickener with the addition of diesel fuel to render any activated graphite inert to adsorption of

Jan 1, 1981

By Jaakko Kajamaa

Neutron diffraction was applied to determine sheet textures by the transmission method. Cold-rolled and recrystallized copper sheets were investigated. The amount of cube texture was determined for three compositions, in which the phosphorus content was, respectively, 0, 0.005, and 0.03 wt pct. The heat treatment was in every case 8 sec at 650°C. In the two latter cases the cube texture was prevented. In addition a comparison with the X-ray diffraction transmission method was made with the 96 pct cold-rolled copper sheet. Outer parts of both (111) pole figures can be considered to be rather identical. This is seen from the fact that the intensity ratio ITD/120" was 0.45 for neutron diffraction and 0.40 for X-ray diffraction. Differences between the methods were discussed in detail. Features peculiar to neutron and X-ray diffraction in texture studies were listed and compared. In this work neutron diffraction was applied to determine sheet textures. Specifically, it was desired to ascertain whether this method can be used to reveal differences when compared to other methods. In addition, the amount of the cube texture in copper sheets was determined as a function of phosphorus content. Previous applications of neutron diffraction to texture problems include the following: nickel wires,' wire of some bcc metals,' and uranium bars.3 In the neutron diffraction technique the greatest difference is in the sample—its method of production and its volume. A sample needs no treatment and its volume is roughly 105 times larger than the volume of an X-ray diffraction sample. The cold-rolled sheet was investigated both by neutron diffraction and by X-ray diffraction, because it is expected that, due to large number of defects, possible differences in the results of the two methods would be revealed. It is a well-known fact that X-ray lines show broadening when cold-worked. Analysis has shown that this is based chiefly on small crystalline size, micro-stresses, and/or faults.4'5 Neutrons are sensitive to the above-mentioned disturbing factors as well, but circumstances in diffraction are different from the X-ray case. Because the sample represents a larger volume, the result is an average over that volume. In addition, it can be assumed that the sample has preserved its original structure, because it needs no special preparation. The particular limitation of neutrons is the relatively low neutron intensity available from nuclear reactors. This decreases the resolution as compared to the X-ray diffraction methods. Furthermore, absorption mainly reduces diffracted X-ray intensity, while multiple scattering effects, i.e., secondary extinction, disturb neutron diffraction. SO neutrons and X-rays behave in a different way when interacting with matter. As in other structural investigations, one can utilize this difference in texture studies as well. One cold-rolled and three recrystallization textures in copper sheets were investigated by neutron diffraction. The samples were produced at the Outokumpu copper factory to the specifications shown in Table I. The paper is divided into five parts. The first deals with the theory of the measurement. In the second, experimental procedures are described. Results are presented in the third part. Both cold-rolled and re-crystallized samples are studied. Discussion is in the fourth part, and finally in the fifth part some conclusions are drawn. 1) THEORETICAL CONSIDERATIONS Properties peculiar to neutron diffraction are the following: a) the scattering length varies greatly between one element and another; b) many of the elements do not absorb neutrons appreciably. In this connection it is of primary interest to know the interaction of neutrons with lattice imperfections. As with X-rays this problem leads to diffraction analysis of deformed and recrystallized metals. From the physical point of view the main difference is that neutrons are scattered by nuclei (magnetic scattering is not considered here), whereas X-rays are scattered by electrons. The features peculiar to neutron and X-ray diffraction methods in texture studies are listed in Table 11. Pole figures are an important tool in performing structural analysis of deformed or recrystallized metal. Present texture research technology requires pole figures which are as precise as possible. The choice between these two methods depends on the technical information which is required. The X-ray diffraction transmission technique may give results which are not necessarily representative of the average physical state of the sample. Although foil samples normally contain enough crystallites for diffraction, they may not necessarily represent the whole structure. An example of this problem is the frequently observed difference between the "surface" and the "inside" texture of a sample. The production of foil samples may disturb the original structure of the parent material. The selection and orientation of the foil from the sample is quite arbitrary. Normally, a highly deformed piece of metal has several texture components. Different components are deformed in a slightly different manner. This is a re-

Jan 1, 1969

By J. Moore Samuel

THE CHAIRMAN (WALTER DOUGLAS, NEW YORK, N. Y.).-Perhaps there is no problem that causes the modern metallurgist more worry than the question of unaccounted for loss. He has not the advantage of the metallurgist of the early days here, who could sleep peaceably with the settled conviction that there were certain copper mineral constituents of the ore which were volatile, and there was therefore nothing to worry about. The slag contents and volatilization accounted for the balance of the copper that went in the top of the furnace after the weighing of the bullion. There have been great strides in recent years toward reducing this loss. Perhaps the Anaconda company is the one we have to thank for the original pioneer work along the lines which we are all today following. We would be glad to hear from some gentlemen present with reference to their experience with this question of dust losses. E. P. MATHEWSON, Anaconda, Mont.-You mentioned the Anaconda company, Mr. Chairman. I would like to say something about what we have been doing there, and the troubles we have been having. We have a tremendous volume of .gas to handle. We adopted the system of large chambers, lessening the velocity of gases, and incidentally cooling the gases. Unfortunately in one sense and fortunately in another, we were compelled to increase the amount of gas handled in the flue system, and the results were then not so good. Still, we get a very good recovery. Our system of taking a sample is similar to the one described by the writer of the paper. We have tried all kinds of apparatus for getting a fair sample. We divided the area of the flue into imaginary squares, and have taken samples for a certain period of time from each square; and have used the asbestos bags. At present, there is a large unit of the Cottrell apparatus almost ready to connect up on the roaster flue to catch the dust from flotation concentrates. The worst things smelters have to handle at the present clay, they are coming in the Southwest as well as the Northwest, are of material much of which is as small as 500 mesh, and the ordinary methods of catching dust will not apply to flotation concentrates. The Cottrell process is going to be tried out at our plant for this material. We have devised special forms, with a view to preventing the formation of dust from this material, and we are pleased with the results so far obtained. There is another point in connection with this subject that I want to put before the members here, so they will be thinking about it. You know there has been a great deal of litigation between the farmers

Jan 12, 1916

By M. R. Geer, H. F. Yancey

Coal washing assumed an important role in the mining industry of the Pacific Northwest long before washing practice became firmly established in the Appalachian field. A Scaife washer was operated in the state of Washington in 1887; and by 1927, the fist year for which complete statistics were compiled, nearly a third of the state's coal production was washed, in comparison with only about 5 pct for the country as a whole. Mechanical preparation was adopted in Alaska in 1922 in a plant constructed by the United States Navy at Chickaloon to provide bunker coal for naval forces operating in northern waters. Many of the coal beds mined in Washington and Alaska contained more impurities than those mined elsewhere, and this circumstance contributed to the early interest in mechanical cleaning. A much more important factor, however, was the inclination of the coal beds. With steeply pitching beds, hand sorting by the miner at the face is impossible; consequently, all material must be loaded and dealt with on the surface, just as is now proving the case with mechanical mining of flat beds. Thus "full-seam" mining afforded the same stimulus to the early development of coal washing in the Northwest that it is providing under mechanization in the rest of the country today. Objeet and Scope ' This report is intended to provide a general summary of the status of coal-washing practice in Washington, Oregon, and Alaska—an area in which some of the coals mined are more difficult to wash than those mined elsewhere in the country. Detailed flowsheets of plants, statistical data on production, and cost figures have been omitted, largely for the sake of brevity but also because such information is principally of only local interest. On the other hand, considerable washability data have been included because they are Washington At present Washington leads all other states in the percentage of its total production that is cleaned mechanically, 82.1 pct in comparison with the national average of 25.6 pct in 1945.' The washing problems encountered in this state are highly variable because the mountain-building forces that created the Cascade Range caused such intense folding and faulting of the beds in some fields that the rank of the coal was increased to anthracitic, while in other fields more distant from the mountains the beds were relatively undisturbed, and the rank of the coal ranges down through subbituminous to lignitic. The complicated and burdensome schedule of sizes prepared in most coal fields has never been required by the Washington market. With but few exceptions, lump is prepared on a round-hole screen of about 3 in. size, egg is about 3 to 1 5/8 or 1½ in., and nut is 1 5/8 or 1½ in. to either 1 or ¾ in. Some mines screen no finer than ¾ in. and market a slack coal of that top size, but generally the coal is screened at about ¼ in. to give a stoker coal of ¾ or 1 to ¼ in., and a ¼ in. to 0 "buckwheat." During recent years the market for lump coal has largely disappeared, and lump is crushed to supplement the pro-

Jan 1, 1950

By R. A. Swalin, B. W. Roberts

ONSIDERABLE controversy has centered about the existence of an order-disorder transformation in alloys in the composition vicinity of 75 atomic pct Ni and 25 atomic pct Cr. All the evidence to date for such a transformation is of a rather indirect nature, since direct X-ray confirmation is difficult to obtain as a result of the small difference in X-ray scattering factors between nickel and chromium. As a result, superlattice lines would be very faint if present. Several investigators1-5 have observed anomalies in the electrical resistivity vs temperature curves of alloys in the vicinity of 25 atomic pct Cr. The observed change is characterized by a rather broad resistivity peak at about 540°C. A discontinuous drop in resistivity is normally associated with ordering. However, Taylor and Hin-ton4 have rationalized that the discrepancy could conceivably be caused by changes in the Brillouin zones upon ordering. The same investigators measured the specific heat as a function of temperature and have also observed anomalies in the vicinity of 540°C. Nordheim and Grant5 have proposed, because of the absence of superlattice lines and the absence of a discontinuity in the resistivity vs temperature curve, that long-range order is improbable and that the results could be better explained by short-range ordering. To date, however, the question has not been resolved satisfactorily. Neutron diffraction techniques provide a method for partially resolving the question since nickel and chromium have considerably different atomic scattering factors in the case of neutrons and, therefore, superlattice peaks, if ordering occurs, should be readily discernable. The results of a neutron diffraction investigation* coupled with a dilatometric in- vestigation are reported here. An alloy containing 28.0 atomic pct Cr was prepared from carbonyl nickel and electrolytic chromium in the form of a 1-in. diam x 10-in. ingot. Melting was done in an alumina crucible and casting in a graphite mold. The ingot was homogenized at 1250°C for seven days, after which a 5-in. long piece was cut into shavings in order to obtain a suitable neutron diffraction sample. Hardness samples and samples suitable for dilatometric analysis (% in. diam x 2 in.) were prepared from the remainlng piece. The neutron diffraction sample, along with a hardness sample, was annealed at 501°C for seven days, at which time the temperature was lowered to 479°C and held at this temperature for twenty-four more days. The hardness was observed to increase from 133 to 147 Vhn during the course of the annealing treatment, in qualitative agreement with Nordheim and Grant." Neutron diffraction traces taken at room temperature and at 42 °K are shown in Fig. 1. The insert shows the trace taken at room temperature with short counting times and thus only fair statistical accuracy. No evidence for superstructure reflections of Cu3Au-type ordering is observed. The statistical accuracy of the 4.2°K trace was improved by using longer counting periods. Several weak intensities are observed at small angles, including an aluminum reflection from the cryostat assembly and a very

Jan 1, 1958

By R. A. Stauffer

The chief ore of lithium is spodumene, a lithium-aluminum silicate containing up to 3 pct lithium. The preparation of lithium salts from spodumene is costly because of the low concentration of the metal and the difficulty of separating it from the other alkali metals present. Dr. Kroll's and Dr. Schlecten's recent paper1 has reviewed various methods proposed for preparation of lithium. It will be seen from this paper that the methods proposed to date have required one or another of the lithium salts as a raw material. The high cost of these salts has been the chief item of expense in the lithium metal produced. This situation has made it interesting to investigate the possibility of producing the metal directly from spodumene. When spodumene is calcined at 1000ºC in the presence of lime, lithium oxide is replaced in the ore as is evidenced by the fact that it may be leached from the reaction mixture with water.2 Free energy calculations suggested that lithium oxide might be reduced with aluminum or silicon and the lithium produced distilled from the reaction mixture by heating-to about 1000ºC in a vacuum. These facts taken together suggested that it might be possible to prepare lithium metal directly from spodumene by heating a mixture of the ore, lime, and a suitable reducing agent in vacuum and distilling off the lithium metal as formed. The Replacement of Li2O in Spodumene A series of experiments were undertaken to determine the ratio of lime to spodumene necessary to free substantially all the lithium oxide Present in the Ore. The spodumene used in these experiments was supplied by Foote Mineral Co. in the form of powder of about 200 mesh' Analysis of the spodumene was as follows: PCT SiO2......................... 62.7 Al2O3........................ 29.9 Li2o......................... 4.9 Na2O........................ 0.89 CaO......................... 0.75 MgO........................ 0.49 K2O......................... 0.44 Lime (cp —200 mesh) was added in various ratios to spodumene and thoroughly mixed in a ball mill. Two hundred gram samples of spodumene-lime mixtures were charged loosely in fireclay crucibles and held at 1000ºC in a gas-fired furnace for 5 hrs. The product in each case was ground to pass 140 mesh and then placed in a thimble in a soxhlet extractor. Extraction with water was carried on for 6 hrs. After this period the extract was reduced in volume by evaporation in order to precipitate dissolved lime and was then filtered and titrated with 1/4 normal hydrochloric acid. After correcting for residual calcium oxide in solution, the alkali present was calculated as lithium oxide. The results of these experiments are shown in Table I and Fig I. At lime-spodumene ratios less than 1.5, the products were invariably fused. At the ratio of 1.5 and above, the product was loosely sintered with little evidence of fusion. When the ratio of lime to spodumene was three, replacement of alkali oxides in the

Jan 1, 1949

By Howard H. Fields

Any mining engineer with a desire to operate independently, with some financial backing, and with no fear of heavy responsibility and long hours, should be able to make a comfortable living in Mexico. Barring a few inconveniences such as a lack of satisfactory liability or accident insurance, the difficulty of obtaining repair parts or vehicles, and the length of time required to receive returns from shipments, the operation of small mine is not at all difficult. It is, in fact, a little easier to find a good prospect in Mexico than in the U.S.

Jan 1, 1950

By Ralph Sweetser

PROGRESS in blast-furnace practice during 1922 has been in the direction pointed out in my article in the March, 1922, issue of MINING AND METAL-LURGY; this advance has been very satisfactory in spite of the difficulties caused by the great coal strike and the railroad strike. The progress, especially in increased tonnage, has been brought about, not by increasing the size of the furnaces, not by improved mechanical devices, but through the application of better blast-furnace practice; the advance has been metallurgical rather than mechanical. The increase in production per stack, has been more pronounced than in any period since the time that James Gayley began to break blast-furnace records in Pittsburgh. These big tonnages have been made in furnaces designed to make 550 to 600 tons of pig iron per day; but several such furnaces have had monthly averages of between 700 and 800 tons per day with a corresponding reduction of cost, and a reduction in the number of man-hours of labor per ton of pig iron. During this period there has been a wider acceptance of the fact that satisfactory blast-furnace results are more dependent on coke quality than on any other factor. There has always been much rivalry among blast-furnace men in making new tonnage records, and many schemes have been used for getting out big pro-duction, but the blast-furnace man cannot make the high records all by himself; it is necessary for him to have the cooperation of the entire management, and also the help of the organization that makes his blast-furnace coke. Herman Brassert has said that "there is no blast-furnace practice possible that can wholly overcome the effects of bad coke." In the past; the blast-furnace superintendent has often been under suspicion if he complained about the quality of the coke in times of unsatisfactory blast-furnace results, but it is now conceded that if the quality of the coke is not right, complaints are not necessarily made as an alibi.

Jan 5, 1923

By George S. Rice

DEFINITE data on the amplitude and effect of ground movement in specific mineral formations, caused by various methods used in the mining of ores, coal, and nonmetals, or in the extraction through wells of petroleum, sulphur, and soluble salts, are increasingly needed because of legal liabilities from damage to overlying or adjacent properties, and growing concern as to the conservation of national mineral resources. Not since the committee was established in 1923 has it been so difficult to get technical papers giving ground movement and subsidence data from specific mine operators. The reasons given, as above indicated, are pending or threatening lawsuits. There are three major objectives in ground movement and subsidence studies : (1) Maximum recovery of a mineral resource. (2) Minimizing damage to surface structures, highways, railroads, and agricultural lands caused by caving or subsidence, which may in some situations, as along the Gulf of Mexico shore, cause flooding by surface waters. (3) Lessening damage to overlying or adjacent mineral by back-filling of mine excavations as completely as possible.

Jan 1, 1940

By Sheldon P. Wimpfen

EVERYWHERE in mining circles the talk is of this new development of hard faced or insert bits which hints of many changes to come in mining practice and rock drill equipment. In the past fifteen years new equipment has appeared in rapid succession which brought one change after another in rock breaking practice. Detachable bits were an innovation which met with wide success. Blasthole diamond drilling has proven itself. Only recently, fusion piercing was announced as a possible solution to the problem of breaking taconite ores. For several years this interest in new methods has been growing and various experimental usages of tungsten carbides in rotary type rock drilling bits have been partially successful. American experts in rock drilling have been concerned with the subject for ten years but actual commercial practice was begun by European manufacturers and mining companies. At this time nearly every manufacturer of rock drilling bits is working on some type of an insert bit. On the Rand, European manufacturers are testing out various types of insert bits. The problems relating to rock drilling in South Africa vary greatly from ours. The bulk of the drilling there is limited to the 31/2-ft holes that are drilled for breaking the gold bearing reef ore. Rock drilling in most mines is far more diversified. Both drifting and ore breaking call for holes varying in length from 4 ft up to as much as 50 ft and more.

Jan 1, 1947

By Jacob T. Wainwright

AS a means for increasing the efficiency in modern blast-furnaces by supplying to them blast of a much higher temperature than is now possible, the writer offers as a suggestion a modification in the construction of regenerative hot-blast stoves. Stated briefly, the plan proposed is to pre-heat both the gas and the air for its combustion in a manner similar to that generally adopted in Siemens openhearth furnaces. After thus carrying the temperature of the stove to a point much higher than that common in hot-hlast stoves, the cold blast passes through it. Without entering into the details relating to the reversing valves and the system of flues, the general plan may be outlined as follows, referring to the accompanying drawings: The valves are so placed in heating up the stove that the blast-furnace gas enters at B, Fig. 1, and the cold air for combustion at A. Ascending in flues, F and E, respectively, combustible gas and air meet and mix in the combustion-chamber, I. Flowing through K, they descend through the flues, G and H, escaping through the chimney. In this manner the walls of the combustion. chambers, I and L, are highly heated, and the right-hand side of the stove is carried to a higher temperature. By reversing the valves, blast-furnace gas enters at C and cold air for combustion at D. Both are pre-heated in their ascent through the flues, G and H. They burn in the combustion-chamber, L, and the hot gases of combustion, flowing through K, I, E and F to A and B, heat the left-hand side of the stove. In this manner the stove is carried to a temperature greater than that of those now generally in use, in which air and gas are burned without preliminary pre-heating. In the plan proposed, that side of the stove will, of course, be relatively cooler through which cold air and furnace-gas last passed in its ascent to its combustion-chamber. After having sufficiently heated the stove in the manner outlined, the cold blast is admitted through all the flues, A, B, C and D. It ascends through the highly-heated regenerative material to the chambers at the top and descends through the flue, P, Fig. 2 (dotted

Jan 1, 1889