By P. M. Swash

The paper describes the use of mineralogical methods in the exploration and evaluation of primary diamond occurrences. The most common methods that are used include the systematic search for kimberlitic indicator minerals, surface textural study of the indicator minerals, (garnet, spinel, ilmenite and chrome diopside) and alluvial macrodiamond studies so as to understand their provenance and guide exploration towards diamondiferous targets. The mineral chemistry of the indicator is used to positively assess the origin of the mineral grains and is also pivotal in the determination of the diamond potential of a deposit. Petrography of the primary deposit is able to identify the body to be kimberlitic and is also a support to the mineral chemistry findings. Unambiguous proof of a prospects potential to contain macrodiamond is proven by the occurrence of microdiamonds in the residues from the rock. The presence of a sufficient number of microdiamonds in the rock is enough to determine a semiquantitative grade estimate and warrant further metallurgical evaluation so as to determine its actual macrodiamond content.

Jan 1, 1991

By Art Johnston

Gas handling at Magma Copper company's, San Manuel smelter receives process gas from a flash .smelting furnace and four copper converters. The major gas handling equip11lent consists of four electrostatic precipitators and a sulfuric acid plant. Process ,vessels in gas handling are, typically confined, spaces. Lethal gases, mechanical and chemical hazards, and the difficulty of rescue, should an accident occur, makes this area a must in the safety plan. The presence': of hazardous chemicals and explosive gases in process' vessels and piping are of major concern when repairs' are required. Proper job procedures are critical to prevent injury during repairs. This includes plant employees and contractors who are likely to be unfamiliar with the hazards ,involved. The safe operation of a gas handling operation must include the functions of operations employees on a daily basis. This includes a safe working environment and involvement of all employees in the safety program. If an injury does occur quick medical response is critical to prevent serious injury. Medical responders must be adequately trained and prepared to treat the injured person without becoming victims' themselves. The methods used at Magma Copper Company to deal with these safety problems are the focus of this presentation.

Jan 1, 1992

By I. Perus, M. Fazarinc, G. Kugler, M. Tercelj

"Ledeburitic tool steels are highly alloyed steels used for specific highly loaded applications but are characterized by low and variable hot workability. In this contribution the importance of selecting the right choice of some essential process parameters, i.e. casting temperature, solidification rate and soaking temperature, needed for improving the intrinsic hot deformability of ledeburitic tool steels, is studied. An inappropriate selection of casting temperature and cooling rate results in precipitation of unusual eutectic carbides that decreases the hot workability, whereas with the selection of appropriate soaking temperature the temperature range of safe hot working can be broadened. For each initial as-cast microstructure individually determined soaking temperature should be selected.IntroductionThe surface cracking during hot deformation of ledeburitic tool steels reduces mechanical properties and their industrial yield. These tool steels have high hardness, wear resistance and high tempering resistance on one hand, and high flow stresses and low hot deformability on the other. Decreased hot deformability of the tool steels is attributed to the type, size, shape, distribution, fraction of eutectic carbides and/or other phases, grain growth, etc. at upper limit while precipitation of secondary carbides and decreased recrystallization rate at lower limit of the safe hot deformation temperature range, [1-6].The occurrence of cracks on most exposed areas of workpiece are related to the areas where similar conditions related to upper and/or lower limit of temperature working range prevail, i.e. areas with accelerated cooling, areas with higher value of accumulated strains where also decreased recrystallization rate with simultaneously presence of higher tensile stresses takes place, furthermore areas of workpiece which are due to combustion conditions in furnace heated to higher temperatures, etc. Thus the areas, where combination of previously mentioned conditions prevails, are more exposed to cracking. This additionally requires that hot deformability of ledeburitic tool steel should be considered as a complex problem. Publications in the literature with regards to hot deformability of tool steels are predominately of a partial nature thus all reasons for unexpected occurrence of cracks are not sufficiently explained in available literature so far. Furthermore modern practice proves that previous processing parameters significantly influence the hot deformability and thus this cannot be considered as a constant value. During heating, soaking and hot deformation various processes take place: decay (decomposition) of carbides, formation of new carbides, dissolution of carbides and of alloying elements, etc. Thus depending on variation of process parameters and chemical composition, that consequently influences the processes related to carbides, shifting of decreased deformability at both limits of temperature working range to higher and/or to lower temperatures can occur, [1-14]."

Jan 1, 2012

By James P. Bennett, Jasper Kwong

As concerns about the environment and the disposal of industrial wastes increase, the utilization of spent refractories from electric arc furnaces (EAF) is receiving more attention. Longer service life of refractories in an EAF can be achieved by foaming MgO saturated slag. The refractory wastes removed from a melt shop can be utilized as a part of these slags. The Albany Research Center is conducting research on recycling spent basic refractory materials as EAF slag conditioners. A good foaming slag should be a creamy, MgO saturated slag, which contains some solid particles (MgO-FeO). A computer model was developed to calculate the dual saturated slag chemistry with respect to CaO and MgO, the MgO saturated slag chemistry, and the solid content in solution. The effects of C/S ratio, AhO3 and temperature on the MgOsaturated slag as calculated by the model will be discussed.

Jan 1, 2000

By KNona Liddell

Many metal recovery processes Involve heterogeneous reactions In porous media accompanied by fluid flow and mass transfer. Modeling such systems Is difficult because of the number of rate processes Involved and is complicated even further by effects due to the structure of the porous medium. Data on even bulk properties of the medium are often severely limited or unavailable. For many such systems, a cell model may provide, an attractive alternative to models based on transport ,mechanisms in a differential volume. A cell model requires less input data and is computationally efficient. Identical residence time distributions can be obtained with models of both types, and both allow conversion and concentration profiles and histories to be calculated. The formulation and properties of cell models for metals recovery are described in detail.

Jan 1, 1996

By Shenghui Guo, Dongbo Li, Lijun Liu, Chengdong He, Jinhui Peng, Libo Zhang

In present study, partially stabilized zirconia (PSZ) was prepared by CaO doped fused zirconia heated by microwave furnace at the temperature of 1450 oC and holding time of 120 min. The XRD results showed that untreated fused zirconia mainly consists of crystalline compounds of cubic ZrO2 phase; while the roasted one mainly is composed of crystalline compounds of cubic ZrO2 phase and monoclinic ZrO2 phase. It is shown through the optimization of structures of two phases that structure of cubic ZrO2 and monoclinic ZrO2 reject each other, revealing its difficulty in forming coinciding interface and linkage of two phases being of Ca atom. Introduction Due to advantages of zirconia, such as high melting point, chemistry inertia, low heat transmission and so on. Zirconia is always taken as megathermal refractory material[1]. However, in the heating and cooling processes of pure zirconium oxide, martensitic transformation will take place associated with greater shear force and volume change, which severely limits the industrial application of pure zirconia in some areas. Such as: Refractory materials, grinding materials and high temperature insulation materials[2]. Through adding a certain amount of MgO, CaO, or Y2O3 stabilizer, etc.[3,4], the zirconia can change into fully stabilized zirconia, which exists in cubic phase. But this high purity fully stabilized zirconia cracks easily because of thermal stress. Therefore, the thermal shock resistance variation is one of the most important quality indicators of zirconia-based materials. According to the heat treatment, the fully stabilized zirconia can be changed into the partially stabilized zirconia (PSZ)[5], which exists in cubic phase and monoclinic phase and has superior mechanical properties, such as anti-heat, low thermal conductivity, large coefficient of thermal expansion and stability, as well as good wear resistance[6].

Jan 1, 2011

By Cristiän Vargas, Jaime Simpson, Gerardo Cifuentes

"This paper presents a new process for the precipitation of Sb and Bi present in copper refinery electrolytes in the presence of Pb02 (Chilean Patent No. 45,037). To establish the conditions under which the precipitating compounds form, it was necessary to evaluate the amount of PbCh consumed, antimony extraction efficiency, precipitate stability, reaction kinetics, diffraction analysis and X-ray fluorescence, separation of size, plus observation of the precipitates in the electron microscope. Preliminary tests were carried with synthetic copper refinery electrolyte, and then the final testing was done with electrolytes from Chilean refineries. This process provides a real alternative for the treatment of copper refinery electrolytes for the control of Sb and Bi in solution; it is very simple to operate and is low cost compared with competing processes.Introduction.A high quality copper cathode implies a cathode free of impurities. The electrorefining process seeks to eliminate these impurities from the copper anode (99.5% purity) by its dissolution in an acid electrolyte using chemical and electrochemical reactions. As a result of this process, a cathode (99.99% purity) is obtained. If the concentration of impurities in the electrolyte, from the dissolved anodes, begins to increase; particularly if the antimony concentration in the electrolyte increases up 500 ppm, the formation of floating slimes which are a major cause of contamination of the cathode is favoured. The most important impurities from the point of view of their effect on the quality of the cathode copper, are Ag, As, Sb, Bi, Pb, Se and Te. Silver is necessary for the control of Se and Te. To control all of these impurities, it is necessary to establish different methods or parameters of control in copper electrorefining. These parameters are anode composition, additives, purification of the electrolyte, current density, acidity, etc."

Jan 1, 2012

By K. S. Raja, M. Misra, S. K. Mohapatra

"Ordered arrays of TiO2 nanotubular photocatalysts were prepared by a simple anodization process. Band gap states of the TiO2 were altered by controlling the anodization electrolyte composition and thermal annealing conditions that resulted in enhanced photo activity. These nanotubes were used for reducing CO2 to methanol either by photochemical or photo electrochemical routes. Pd nano-particle loaded TiO2 nanotubes were employed for photochemical reduction of CO2 to methanol that showed a conversion rate of 12 x 10-3 mol m- 2h-1. Carbon modified TiO2-xCx type nanotubes were used as photo anode and Ti as cathode for photo electrochemical reduction of CO2. The potential of Ti cathode was maintained at -0.5 V SCE. The formation rate of methanol was determined as 13 x 10-3 mol.m-2h-1.1. IntroductionGlobal warming due to emission of carbon dioxide is a serious environmental concern. The atmospheric concentration of CO2 is about 384 ppm by volume and about 3 x 1012 tonnes by weight. Burning of fossil fuels and deforestation are the leading causes for increase in the anthropogenic CO2. More than 32 x 109 tonnes of CO2 are released per year (based on 2006 data) worldwide from the fossil fuel. Pumping CO2 from the fossil fuel power plants into deep ocean basin is one of the most discussed disposal options. The other potential option is converting this green house gas into valuable fuels.Carbon dioxide feed stock can be converted into fuels of solid, liquid or gas phase by chemical, electrolytic, photocatalytic and photo-electrocatalytic methods. Reduction of CO2 to fuel form of any phase requires energy. The reduction process should be energy efficient so that we do not spend more energy and emit more (indirect) CO2 in the process of converting CO2. From this point of view, conversion processes occurring at room temperature look attractive.Electrolytic conversion of CO2 into various forms such as methane1, ethane2, ethylene3, methanol4,5, ethanol6, n-propanol, formic acid7, and formaldehyde has been widely reported. The standard equilibrium potential (at pH: 0) for reduction of CO2 to methanol is 0.14 VSHE and to methane is 0.2 VSHE which is thermodynamically more favorable than hydrogen reduction. However, the gas phase reduction is kinetically complex requiring effective electrocatalyst. The major issues with electrolytic conversion of CO2 to useful products are:"

Jan 1, 2010

By Carole Read

Hydrogen is under consideration by several countries for its potential as an energy carrier for transportation applications. In order to compete with vehicles in use today, hydrogen-powered vehicles will require a driving range of greater than 300-miles in order to meet customer needs and expectations. For the overall vehicular light-duty fleet, this dictates that a range of 5 to 13 kg of hydrogen be stored on-board (assuming a fuel cell power plant) within stringent system weight, volume, and cost constraints. Vehicular hydrogen storage thus constitutes a major scientific and technological challenge. To meet this challenge, the U.S. Department of Energy (DOE) initiated a ?National Hydrogen Storage Project? with roughly 40 universities, 15 companies and 10 federal laboratories, actively engaged in hydrogen storage research. Centers of Excellence in metal hydrides, chemical hydrides, and carbon-based materials have been established, as well as independent university and industry projects in the areas of new concepts/materials, hydrogen storage testing, and storage system analysis. Recent technical progress in each of these areas is discussed, as well as collaborative hydrogen storage activities under the recently established International Partnership for the Hydrogen Economy (IPHE).

Jan 1, 2006

By Hideyuki Itou

Municipal wastes are mainly incinerated in Japan. Both bottom ash and fly ash from the incineration treatment are smelted recently to decrease the volume. Direct smelting of municipal wastes is also becoming popular. The smelting treatment generates fly ash which contains concentrated heavy metals such as Zn, Pb and Cu, and the harmfulness is causing concern. The smelter fly ash is mainly landfilled after stabilization. An effective treatment process of the smelter fly ash is required to recover the metals. For the treatment process, an application of chloridizing volatilization technique is considered. Chloridizing volatilization experiments were carried out to determine the effects of various factors on the volatilization behaviors in this study. A pretreated ash was mixed with a main raw material which mainly consists of hematite. Calcium chloride water solution was added into the mixture. The mixture was pelletized, dried and used as samples for the volatilization experiments. The sample was placed in the reaction tube heated in an electric resistance furnace. 5%02-95%N2 gas with controlled humidity was introduced into the reaction tube. Effects of humidity in the carrier gas, addition of calcium chloride and mixed ratio of the ash to the main raw material were investigated on the volatilization of Zn, Cu and Pb. To determine the volatilization behavior, samples were taken from the furnace at specified temperatures on the heating stage. In addition, experiments at specified holding temperatures for 15 minutes with shortened heating time were conducted. The two series of experiments revealed the effect of heating temperature on the volatilization behavior of Zn, Cu, Pb and Cl.

Jan 1, 2006

By Marshall Khan

The Goodfellow Expert Furnace System Optimization Process (Goodfellow EFSOP?) is a proprietary process that uses real-time and continuous off-gas analysis, along with process monitoring to optimize the operation of electric arc furnaces (EAF) for steelmaking. With the exception of off-gas composition, dynamic process measurements within the EAF are not possible due to the harsh operating environment. The Goodfellow EFSOP? system provides a dynamic indication of the operating conditions within the EAF. Continuous measurement of furnace off-gas composition, along with other furnace operating parameters is used to elucidate the fate of chemical energy usage within the EAF including: the evolution of carbon from the molten steel bath; the in-leakage of air into the furnace; the extent of combustion above the molten steel bath and the occurrence of dangerous water-leaks from the furnace cooling system. The ability to measure the process reliably and continuously enables Techint Goodfellow Technologies Inc (TGTI) to implement dynamic process control of combustion within the electric arc furnace and to optimize the overall operation through adjustments to the EAF process based on off-gas measurement. This paper discusses the methodology and results achieved from several recent Goodfellow EFSOP? installations in South East Asia.

Jan 1, 2006

By Jackson Jenkins

The second survey of world copper SXEW plants has been completed. Solvent extraction and electrowinning data published in 1996 has been updated and leach data from seventeen plants is now included. The following pages list the results of the thirty- two plants that responded to the survey. Selected information is summarized in graphical form.

Jan 1, 1999

By Mark William Kennedy

"Electric furnaces containing high quantities of slag are applied in many areas of pyrometallurgy, often for smelting or slag cleaning. A variety of ratios or rules of thumb have been employed in the industry for the dimensioning of these vessels, in most cases with no clear technical basis.In this paper, several design guidelines are presented (electrode size, spacing, vessel dimensions, energy intensity, etc.) as an attempt to provide some technical basis for optimal dimensioning.Furnace heat generation is related to side wall copper cooler heat losses, in an attempt to establish a methodical design strategy particularly for minimum electrode to wall spacing for modern furnaces with cooled linings.Issues regarding the true nature of heat production in a slag furnace are discussed with regards to the possible impact on accurate modeling and design.IntroductionSlag furnaces have passed through a number of design 'generations' characterized by increasing energy intensities, improved electrode technologies and advancing development in their physical structure or 'furnace integrity' as shown in Table I f 1]. A 3rd generation furnace using ultra-high-power (UHP) graphite electrodes is shown in Figure 1, as a generic example of the types of physical structures present in modern slag furnace designs [1]."

Jan 1, 2012

By S. V. Subramanian

The tool material and the machine design for high speed machining are well advanced over the last decade but the steel design has lagged behind. The paper examines the design of steel in order to control the sliding tribology for high speed machining under dry machining conditions. In high speed machining of steel, accelerated chemical wear of the tool occurs once atomic contact is established at the tool-chip interface, resulting in poor tool life even with high performance tools such as cubic boron nitride. Recent research has confirmed the occurrence of nanocrystalline grains in the interfacial layer of the chip at the tool-chip contact. The volume percentage of grain boundary is increased significantly (10 to 30%) as the nanocrystalline grain size is decreased well below 30 nm. The solubility of tool material into the nanocrystalline grain boundary is two or three orders of magnitude greater than in the crystal lattice. Further the kinetics of diffusion in the grain boundary is seven or eight orders of magnitude greater than in the crystal lattice. Enhanced nanocrystalline grain boundary diffusion occurring in the interfacial layer at the tool-chip contact causes the accelerated chemical wear. Significant improvement in tool life could be achieved by engineering glassy oxide inclusions in steel, designed to self-lubricate the tool-chip interface in-situ at higher cutting speeds. Thus the control of sliding tribological condition at the tool-chip interface is key to suppress nanocrystalline layer formation at the tool-chip contact and hence prevent accelerated chemical tool wear. Sulfide inclusions are designed essentially to promote chip fracture. In addition, sulfide inclusions are designed to act as a diffusion barrier at the tool-chip interface. The application of inclusion engineering concepts to enhance the tool life in high speed machining will be demonstrated with a suitable case history.

Jan 1, 2006

By T. V. Jayaraman

Fe-Ga alloys, with compositions around 27.5 at % Ga, can be heat treated to obtain ? (ordered bcc), DO19 (ordered hexagonal), and L12 (ordered fcc) ordered structures. Our earlier work using polycrystalline samples had shown that magnetostriction is strongly influenced by ordering in this alloy. Here more detailed study of the correlation between ordering and magnetostriction using single crystals of Fe 27.5 at. % Ga alloys is reported. Single crystals of Fe 27.5 at % Ga were grown using Bridgman single crystal growth technique. X-ray and electron diffraction were used to study the ordering in this alloy. Magnetostriction measurements were carried out at no load conditions. Elastic constants were measured using Resonant Ultrasound Spectroscopy.

Jan 1, 2006

By P. Chris Pistorius

"Use of coke in blast furnace ironmaking is the main origin of carbon dioxide emissions from integrated steelmaking. Use of pre-reduced iron feedstocks would reduce the coke rate and, if pre-reduction were carried out with natural gas, would decrease the overall carbon intensity of ironmaking. Blast furnace productivity would also increase, because the blast volume per unit of hot metal would decrease. This paper shows that these trends can be predicted quantitatively, by using a conceptually simple Rist-style blast furnace mass and energy balance, assuming furnace productivity to be limited by the tuyere gas flow rate. Such predictions would assist in optimizing the choice of the degree of reduction and relative amount of pre-reduced blast furnace feed.IntroductionSteelmaking is responsible for some 5% of world CO2 emissions, at a rate of approximately 1.9 tonnes of CO2 per tonne of cast steel [1]. In integrated steelmaking, the ultimate source of most of the CO2 emissions is coke, the indispensible (and expensive) fuel and reductant for blast furnaces. There are several research programs underway worldwide which seek to lower the carbon intensity of ironmaking; one of the largest is the European ULCOS program [2], in which the main proposed change to blast furnace ironmaking is to scrub CO2 from the furnace off-gas (for possible sequestration), recycling the remaining gas to the furnace. To limit the recycling nitrogen load, oxygen rather than air is used to combust coke.A conceptually simpler approach is to charge prereduced feed (direct-reduced iron) to the blast furnace. This approach has been used for some two decades at the AK Steel Middletown plant, where some 200 kg of direct-reduced iron (DRI) is charged per tonne of hot metal [3]. The Middletown blast furnace has exceptionally high productivity (rate of iron production relative to the furnace hearth area), simply because less coke is required per ton of hot metal if part of the feed is already metallic. Midrex [4] has provided some quantitative predictions of the implications of DRI use in the blast furnace, stating that for every 10% of Fe in the feedstock that is in metallic form, the fuel requirement decreases by 7% and the productivity increases by 8%."

Jan 1, 2012

By John Sakala, Jeyapandian Sasikumar, Sydney Kwalela

The Isasmelt Furnace was commissioned in September 2006 with a concentrates treatment capacity of 850,000 tonnes per annum. However, the converter section became a bottleneck to the high throughput. Over 25% of the Isasmelt Furnace down time was attributed to lack of converter space. Factors that affected converter operations were low tuyere line campaign life (an average of 150 blows), high reverts generation, low conversion rates, and high converter cycle time. As a result of efforts carried out to improve converter operation, the average campaign life has increased to over 250 blows and reverts generation has been reduced from 22% of concentrate treated to 15%. Blister copper conversion rate has increased from 15 tonnes per hour to 19 tonnes per hour and blowing time per cycle has been reduced from 5.7 hours to 4.7 hours.

Jan 1, 2012

By K. A. Lewandowski

Agglomeration of ore can be used to immobilize fine particles during heap leaching by agglomerating them into granules. Without agglomeration, the fine ore particles can migrate within the heap, clogging flow channels and producing large areas where access of solution to the ore is very poor. The benefits of agglomeration are well-known in gold heap leaching operations, which can be effectively agglomerated using binders such as Portland cement due to the alkaline leaching solutions used. However, agglomeration has not been very effective in the heap leaching of copper ores, because these ores require an acidic leaching solution. Acid destroys the effectiveness of most binders, causing the agglomerates to disintegrate as soon as the leaching solution is applied. In order to gain the benefits of agglomeration in copper heap leaching, an economical, acid-resistant binder is needed. The two issues that needed to be addressed were: 1) Lack of effective methods for evaluating binder acid resistance before performing expensive, time-consuming, full-scale heap leaching tests, and 2) The vast majority of known binders react poorly to acid conditions, and so a basis was needed for determining which binders are most likely to be acid-resistant. In this paper, the development of two new tests for evaluating binder acid resistance in the laboratory are described. The ?soak test? determines the degree to which agglomerates disintegrate and release fines on contact with acidic solution, measuring the relative quantities of fines released by agglomerates made with different binders under controlled conditions, and serves as a rapid means for comparing large numbers of binders. The ?percolation test? measures several different parameters to determine how a binder is likely to perform in heap leaching: 1) the degree of ?slump? and compaction of agglomerates as they are wetted by acidic solutions; 2) the hydraulic conductivity of the agglomerate bed; 3) the migration of fines through the bed as the solution flows through it; and 4) the quantity of liquid retained in the agglomerates after they are drained. Using these tests, a broad spectrum of binders were examined. Soak testing determined that the most acid-resistant binders were nonionic polymers. Five of these binders were further evaluated using percolation testing.

Jan 1, 2006

By Per Anders Eidem, Merete Tangstad, Jens Davidsen

"During excavations of submerged arc furnaces producing silicomanganese, silicon carbide (SiC) has been found. Contributing to the size of the inactive area of the furnace, the active area of the furnace where reactions occur will decrease, thus reducing the potential for pre-reduction in the furnace.This work studied the formation of SiC from the liquid-solid reaction between slag, metal, and metallurgical coke. Slags and metals with different levels of silica (S1O2) and silicon (Si) have been studied. The slag and metal has been heated together with coke, and the samples investigated by microprobe. The results show that SiC was formed on the coke particle through reactions with both slag and metal. For the metal, the carbon most likely diffused through the SiC to react with Si in the alloy. SiC formation with slag is likely to go through the reduction of Si02 to Si.IntroductionToday, Silicomanganese (SiMn) is produced in submerged arc furnaces (SAF) by reduction of S1O2 and manganese oxides, mainly with metallurgical cokes. Typically, the tapped metal has a silicon content of 17 - 20 wt.%. To achieve higher levels of Si, the metal can be refined by adding off-grade silicon metal, yielding low carbon SiMn. [1]. What is believed to be SiC that has been found during dig-outs of SiMn furnaces producing high silicon alloy. It is possible that excess amounts of SiC in the furnace cause operational problems, since SiC will occupy furnace volume. As SiC accumulates, the active volume of the furnace will decrease, increasing the flow of material and gas in the active areas of the furnace. Formation of SiC is inevitable, so it is desired to keep the formation as low as possible. To be able to control the formation of SiC, one has to understand the basic mechanisms."

Jan 1, 2012

By Toshiyuki Kozuka

CdTe semi-conducting materials have been expected as solar cell materials because its theoretical energy conversion ratio is very high. The actual efficiency still low, however, many research works have been done in order to improve the efficiency. And crystal orientation is one of possibilities for that. In this work, a new method using intense magnetic field for a control of texture of CdTe crystals will be proposed, where the CdTe film was electro-deposited under an intense magnetic field. CdTe is less affected by magnetic field, because of its cubic structure, but Cd or Te has hexagonal structure, which is sensitive for magnetic field. In this paper, crystal orientation of Cd or Te film, which can be utilized as basic layer for CdTe deposition, will be developed.

Jan 1, 2006