Search Documents

By W. F. Stowasser

A downdraft traveling grate process to agglomerate pelletized iron ore concentrates has been successfully demonstrated in a pilot plant at Carrollville, Wis. Work there followed several years of development in the Allis-Chalmers Mfg. Co. laboratories, and the pilot plant phase was carried out in co-operation with Arthur G. McKee & Co., consultants and engineers to the iron and steel industry. End result of the process is conversion of iron ore concentrates into a form which can easily be transported and smelted in the blast furnace.

Jan 5, 1955

By J. H. Westbrook

UNTIL very recently the development of high temperature alloys has been strictly empirical. It is, in fact, a great tribute to the intuition, perseverance, and industry of the practicing metallurgists of this country and abroad that the amazing increases in gas turbine service temperature over the past 15 years have been achieved with so little fundamental knowledge. The result of this development has been the realization of successful but highly complex alloys possessing five, six, or more alloying elements and correspondingly complex microstructures. Within the last few years, considerable effort has been devoted to the identification of the secondary phases in these alloys and to the correlation of the presence or absence of such phases with alloy properties. Little attention, however, has been given the problem of identification of the mechanism (s) by which such phases enhance the properties of the alloy and especially to the assessment of the particular properties of the secondary phase (either in- trinsic or relative to the matrix phase) which are basically responsible for the improvement. Conceivable mechanisms which might apply include dispersion hardening and precipitation hardening. In both cases geometrical factors—particle size, dispersion, volume fraction, etc.—and agglomeration re-

Jan 1, 1958

The Institute is custodian of funds for support of numerous gold medals and prizes and has representatives on boards awarding still others. Details regarding the Institute Awards are given below. The Institute is represented on the boards of the John Fritz Medal, the Hoover Medal, and the Alfred Noble Prize, in conjunction with the three national societies of Civil, Mechanical and Electrical engineers; and, also on the board of the Washington Award, on which the Western Society of Engineers also is represented.

Jan 1, 1940

By H. E. Rorschach

Activity in Oklahoma fields declined in 1938 from the banner year of 1937. During the year, 1768 wells were completed as compared to 2632 completed during the year 1937. The following tabulation sets out details regarding the wells completed during the year: These computations do not take into account the wells drilled for repres-sure and salt-water disposal, and other nonexploratory wells. Purchasers' reports filed with the Corporation Commission of the State of Oklahoma show a total of 168,789,229 bbl. of oil purchased from Oklahoma leases in 1938, or a daily average of 462,436, a decrease of about 25 per cent from the year 1937. The outstanding operation of the year was the further development of the Ramsey pool, in western Payne County, the producing horizon being classified as the Wilcox. This pool was discovered on the last day in the year 1937, by the Mid-Continent Petroleum Corporation drilling on a unitized block in see. 18, T. 18 N., R. 2 E. The map in Fig. 1 shows the development at the end of the year 1938. An important discovery of the year was the Champlin Refining Company's No. 1 Boehm, in Garfield County, sec. 4-24N-8W., the producing horizon being the second Wilcox found at a depth of approximately 6700 ft. This pool was assigned the name of Hillsdale. Some of the offsets to this discovery well had not come up to expectations at the end of the year, but the discovery seems to be important as indicating that the Wilcox sand is productive in the Anadarko Basin area, providing that the right structural conditions are present.

Jan 1, 1939

By H. E. Rorschach

Activity in Oklahoma fields declined in 1938 from the banner year of 1937. During the year, 1768 wells were completed as compared to 2632 completed during the year 1937. The following tabulation sets out details regarding the wells completed during the year: These computations do not take into account the wells drilled for repres-sure and salt-water disposal, and other nonexploratory wells. Purchasers' reports filed with the Corporation Commission of the State of Oklahoma show a total of 168,789,229 bbl. of oil purchased from Oklahoma leases in 1938, or a daily average of 462,436, a decrease of about 25 per cent from the year 1937. The outstanding operation of the year was the further development of the Ramsey pool, in western Payne County, the producing horizon being classified as the Wilcox. This pool was discovered on the last day in the year 1937, by the Mid-Continent Petroleum Corporation drilling on a unitized block in see. 18, T. 18 N., R. 2 E. The map in Fig. 1 shows the development at the end of the year 1938. An important discovery of the year was the Champlin Refining Company's No. 1 Boehm, in Garfield County, sec. 4-24N-8W., the producing horizon being the second Wilcox found at a depth of approximately 6700 ft. This pool was assigned the name of Hillsdale. Some of the offsets to this discovery well had not come up to expectations at the end of the year, but the discovery seems to be important as indicating that the Wilcox sand is productive in the Anadarko Basin area, providing that the right structural conditions are present.

Jan 1, 1939

By Graham Bright

Before the arrival of central-station power, all coal and metal mines generated their own power and, in many cases, these isolated power plants gave a fair continuity of service. In coal mines that produce considerable gas, it is essential that power be available at all times for operating the ventilating fan and the hoist, if the mine is of the shaft type. In the case of an isolated power plant, if trouble should develop with the fan the men can be hoisted quickly when the mine is of the shaft type. On the other hand, if trouble develops with the hoist, the fan can be kept in operation, and there will be no necessity of haste in getting the men from the mine. Now that central-station power is being used so extensively for mine service, the continuity of service with gaseous mines is very important. : Inherently, the central station is much more reliable than any isolated plant, but trouble may occur on the transmission lines which may prevent the transmission of power for a considerable time. : Some mines have kept their steam equipment intact and ready for operation in case the purchased power should fail. This is expensive procedure, for the boiler plant must be fired at all times so that the emergency power will be quickly available. In a number of instances, gasoline-engine driven generators have been installed to furnish emergency power for the service hoist. As most service hoists are of the alternating-current type, the generator of the gasoline-engine driven set is usually of the a.c. type and is arranged to drive the service hoist motor at full speed, or an extra motor that can be thrown into gear on either the main or service hoist and the hoist operated at a greatly reduced speed. This arrangement is used because it is difficult and expensive to obtain and install large gasoline-engine driven units. The author has recently developed a plan by which the main hoist and the fan can both be operated at reduced speeds, in case of loss of power from a central-station power system. In this plan a gasoline-engine

Jan 1, 1923

By Graham Bright

Before the arrival of central-station power, all coal and metal mines generated their own power and, in many cases, these isolated power plants gave a fair continuity of service. In coal mines that produce considerable gas, it is essential that power be available at all times for operating the ventilating fan and the hoist, if the mine is of the shaft type. In the case of an isolated power plant, if trouble should develop with the fan the men can be hoisted quickly when the mine is of the shaft type. On the other hand, if trouble develops with the hoist, the fan can be kept in operation, and there will be no necessity of haste in getting the men from the mine. Now that central-station power is being used so extensively for mine service, the continuity of service with gaseous mines is very important. : Inherently, the central station is much more reliable than any isolated plant, but trouble may occur on the transmission lines which may prevent the transmission of power for a considerable time. : Some mines have kept their steam equipment intact and ready for operation in case the purchased power should fail. This is expensive procedure, for the boiler plant must be fired at all times so that the emergency power will be quickly available. In a number of instances, gasoline-engine driven generators have been installed to furnish emergency power for the service hoist. As most service hoists are of the alternating-current type, the generator of the gasoline-engine driven set is usually of the a.c. type and is arranged to drive the service hoist motor at full speed, or an extra motor that can be thrown into gear on either the main or service hoist and the hoist operated at a greatly reduced speed. This arrangement is used because it is difficult and expensive to obtain and install large gasoline-engine driven units. The author has recently developed a plan by which the main hoist and the fan can both be operated at reduced speeds, in case of loss of power from a central-station power system. In this plan a gasoline-engine

Jan 1, 1923

By Hans Lundberg

IN last year's report on the progress of geophysics, the airborne magnetometer was the featured new development. At that time only a relatively small number of surveys had been made. During 1947, the airborne magnetometer was used in making many surveys and is again one of the high lights of the year in geophysics. This report is mainly concerned with geophysics as applied to the search for minerals exclusive of petroleum. In 194,5 and 1946, the use of the magnetic method reached a peak, partly because of an active period of prospecting brought on by an active mining market, particularly in Canada.

Jan 1, 1948

By F. M. Lyon, F. J. Chernosky

Research efforts have not developed techniques for the complete desulfurization of coal that is needed to reduce air pollution caused by burning coal and to reduce the sulfur in metallurgical coke. Sulfur in coal occurs in three forms and of these, the pyritic sulfur occurs as discrete mineral particles and, at least theoretically, should be subject to physical rejection. Pyrite occurring in hard rock mining is concentrated by froth flotation; therefore, the possibility of removal of pyrite from coal by flotation does exist. With this possibility in mind, the flotation and adsorption characteristics of ore and coal-pyrite were compared while using potassium ethyl xanthate as the collector.

Jan 1, 1973

By Howard N. Eavenson

TWO months ago, just after the coal code hearing in Washington, one of our leading liberal weeklies printed a study of the coal industry made by an economist in the Administration, and on the outside cover bad it featured as "Coal-A Dying Industry." There are, of course, different opinions as to the accuracy of this characterization and I want to present some of the facts about the outlook for the bituminous industry for a short time ahead. In view of what has happened in the industry within the recent past it would be futile to attempt to make any prophecy about what is likely to occur in the future. We all know that a prophet is not without honor save in his own country, but it is likely that anyone undertaking this role about this industry would soon find himself in no man's land. One can, with some slight degree of safety perhaps, outline present conditions and tendencies and draw some inferences as to what the future may hold.

Jan 1, 1933

By Jack White

W. I. Garms-—The authors state that when they added 11 tons of balls to the 45 pct volume ball load, the power needle did not budge. The question arises as to whether any increase in capacity accompanied the 11-ton addition. It is hardly conceivable that all of the balls making up the l l-ton addition were sterile. However, as the work done in the ball mill is not by kilo-watthours per se or balls per se but by kilowatthour-balls, it is possible that the kilowatthourballs in the mill before the ll-ton addition had a different amperage, voltage or robustage than those in the mill after the addition and that the overall outcome was that equal work was done before and after the addition. The authors can keep the efficiency that they got with the 45 pct volume 1-in. ball charge and get additional capacity by putting more kilowatthourballs to work in the form of the addition of 11 tons of 2-in. balls to the present ball charge, and subsequent makeup additions by weight of 20 pct 2-in. balls and 80 pct 1-in. balls. J. F. Myers (authors' reply)-—Mr. Garms points his finger at the 11 tons of "sterile" balls added to the Tri-cone mill. A fact so interesting to us that we felt it should be reported. Clearly, ball slippage at the existing mill speed prevented any further transfer of power from the shell to the ball mass. We agree that the kilowatthourballs would increase, were we charging rough 2-in. balls as suggested by Mr. Garms. The assumption is, of course, that we would get a corresponding increase in work done. Our reported data (CIME meeting, Vancouver, 1946) shows a gain of work accomplished of 7.6 pct as we decreased the ball size from 2 in. to 1% in. and a further gain of work accomplished of 2.1 pct when we went from 1 % in. to 1 in. The small ball results reported by H. R. Banks at Chapman Camp are also very convincing. In the case of 2-in. balls they would take the conventional ball path and start cascading. They would thus destroy the classifying pool over the "foot" of the

Jan 1, 1951

By Jack White

W. I. Garms-—The authors state that when they added 11 tons of balls to the 45 pct volume ball load, the power needle did not budge. The question arises as to whether any increase in capacity accompanied the 11-ton addition. It is hardly conceivable that all of the balls making up the l l-ton addition were sterile. However, as the work done in the ball mill is not by kilo-watthours per se or balls per se but by kilowatthour-balls, it is possible that the kilowatthourballs in the mill before the ll-ton addition had a different amperage, voltage or robustage than those in the mill after the addition and that the overall outcome was that equal work was done before and after the addition. The authors can keep the efficiency that they got with the 45 pct volume 1-in. ball charge and get additional capacity by putting more kilowatthourballs to work in the form of the addition of 11 tons of 2-in. balls to the present ball charge, and subsequent makeup additions by weight of 20 pct 2-in. balls and 80 pct 1-in. balls. J. F. Myers (authors' reply)-—Mr. Garms points his finger at the 11 tons of "sterile" balls added to the Tri-cone mill. A fact so interesting to us that we felt it should be reported. Clearly, ball slippage at the existing mill speed prevented any further transfer of power from the shell to the ball mass. We agree that the kilowatthourballs would increase, were we charging rough 2-in. balls as suggested by Mr. Garms. The assumption is, of course, that we would get a corresponding increase in work done. Our reported data (CIME meeting, Vancouver, 1946) shows a gain of work accomplished of 7.6 pct as we decreased the ball size from 2 in. to 1% in. and a further gain of work accomplished of 2.1 pct when we went from 1 % in. to 1 in. The small ball results reported by H. R. Banks at Chapman Camp are also very convincing. In the case of 2-in. balls they would take the conventional ball path and start cascading. They would thus destroy the classifying pool over the "foot" of the

Jan 1, 1951

By Harry H. Power

WORK of the Committee on Education of the Petroleum Division has been under way for approximately-one year. Although some progress has been made, further activities of the Committee are necessary in order to discuss mutual problems more thoroughly by a unified group interested primarily in this field of specialization.

Jan 1, 1944

By Kenneth A. Gutschick, Robert S. Boynton

Lime has become a general and loosely used term to denote almost any kind of calcareous material or finely divided form of limestone or dolomite, as well as burned forms of lime. However, according to Webster, lime is only calcined limestone (known as quicklime, unslaked lime, or calcium oxide). It also embraces the secondary product of quicklime, i.e., hydrated lime or slaked lime (calcium hydroxide). There are two basic types of limestone used for lime manufacture-high calcium and high magnesium (dolomitic). The dolomitic quicklimes and hydrated limes correspond to their "high calcium" counterparts. The only difference is that the dolomitic types are a combination of the elements calcium and magnesium, in varying percents, whereas high calicum limes contain less than 5% MgO down to 1/2%. In either case a pure form of limestone of at least 97% combined carbonate content is needed to make salable lime, barring a few exceptions. The calcination of both types is diagrammed chemically as follows: [ ] In the foregoing reversible reactions the limestone is burned (calcined) in lime kilns, with the carbon dioxide content of the stone expelled as a gas. The weight loss during calcination of pure high calcium limestone is 44%; with equimolecular dolomitic limestone, the weight loss is 48%. Since lime has a strong affinity for CO_, particularly if moisture is present, it will readily revert to its original carbonate form. This occurs when quicklime "air-slakes" and adsorbs CO.. from the air. Thus, quicklime is perishable and should be stored in dry, water-tight areas. Depending upon the type of kiln used and the physical structure of the stone, the size of the quicklime may range from sandlike granules to 8 in. lumps. However, pebble sizes ranging from 1/4 in. to 2 in. are the most common. Screened quicklime fines are also com¬pressed (pelletized) into 1 in. pellets. For some purposes ground or pulverized forms of quicklime are used, ranging from No. 10 mesh to dust. Generally a pebble of quicklime is about the same size as the pebble of limestone before calcination (perhaps shrinking slightly). A more stable form of lime is hydrated lime. This is obtained by adding water to quicklime, slaking it into a dry, fine, subsieve size white powder. Because its affinity for moisture has been satisfied, it is not vulnerable to further moisture like quicklime. However, it has the same strong affinity for CO_. The following reversible chemical reactions illustrate how hydrated lime when heated (or dehydrated) can revert to the original oxide form:

Jan 1, 1975

By Herbert Clark Hoover, Lou Henry Hoover

DIFFERENT methods of parting gold from silver, and, on the other hand, silver from gold, were discussed in the last book; also the separation of copper from the latter and further, of lead from gold as well as from silver ; and, lastly, the methods for refining the two precious metals. Now I will speak of the methods by which silver must be separated from copper, and likewise from iron.1 The officina, or the building necessary for the purposes and use of those who separate silver from copper, is constructed in this manner. First, four long walls are built, of which the first, which is parallel with the bank of a stream, and the second, are both two hundred and sixty-four feet long. The second, however, stops at one hundred and fifty-one feet, and after, as it were, a break for a length of twenty-four feet, it continues again until it is of a length equal to the first wall. The third wall is one hundred and twenty feet long, starting at a point opposite the sixty-seventh foot of the other walls, and reaching to their one hundred and eighty-sixth foot.

Jan 1, 1950

By Lane Mitchell

A ceramic product or processed material is a solid composed of materials which have been subjected to heat above 875°F. The raw materials, which are blended together (or in some cases used singly), are selected and utilized for various reasons such as ease of fabrication, aid to processing, to yield desired properties after processing, lack or controllable degree of toxicity or hazard, availability, cost, and perhaps other considerations. Almost all solid inorganic, some organic, and some liquid and gaseous materials have the potential to be used individually in some ceramic product. There are several fundamental functions to be fulfilled in every ceramic product and a number of secondary functions are desirable in specified products. These functions are generally met by the most widely occurring minerals and rocks of the earth and their debris. This fact characterizes ceramics as a field utilizing the raw materials most available to man. Of course, specified products utilize synthetics, organics, and rare inorganics to produce desired results. Any solid nonmetallic product processed by subjection to temperature above a red heat may be called a ceramic product. Widely used construction materials and units, domestic utensils and units, industrial parts to facilitate manufacture, technical components, and aesthetic creations are very often of a ceramic nature because of the durability, inertness, hardness, ease of fabrication, cost, and availability of the ingredients. Often, organics or metals cannot meet desired specifications for some of these products. The rocks and minerals and mineral debris of the earth are largely siliceous. Oxygen and silicon comprise roughly 75% of the earth's crust with aluminum, iron, calcium, and the alkalies following in abundance. Silica ( SiO, ) and silicates can be melted to form glasses. Alumina (A1,0,), present in a mineral com- pound, gives greater durability, hardness, and strength, but lessens the glass-forming property. Iron, calcium, and the other alkalies flux silica and reduce melting points. Thus, sand, which is generally almost pure SiO,, and clay, which is generally hydrated alumina silicate, are the most widely used of all ceramic raw materials-principally because of the glass-forming propensities of silicates. In ceramic formulations, clay is generally a refractory filler or skeletal material, having in the raw state a plasticity derived from its colloidal grain size and its water-loving nature. On the other hand, silica sand is a glass former or nonplastic filler. Clay and silica sand in pure forms are quite refractory, i.e., not easily melted. Clay, although siliceous, is less of a glass former than pure silica and is more refractory. Natural contaminants, such as iron oxide or limestone, adulterate many clays and some sands. These contaminants act as fluxes and reduce the fusion points of the mineral or blends. Glass is made from silica sand by fluxing the sand with strong bases, usually soda ash and limestone. Red building bricks are hard and durable because the sand and clay have been partially fused with help of natural iron oxide serving as a flux. The iron oxide per- forms a dual function, serving as a pigment as well as a flux. In a blend of clay and sand and iron oxide, the sand is more susceptible to fusion than is the clay. Although silica sand and clay are the most widely used raw materials in most ceramic products, many other minerals, and some non- minerals are utilized in products where these materials can produce or aid in achieving desired results. Limestone and dolomite, feldspars, pigmentary minerals, refractory oxides or carbides, and special property producers can

Jan 1, 1975

By G. G. Luther, C.E. Jackson

The relationship between hardenability and weldability has been mentioned many times. The ease of making a hardness survey has led to its wide use as a criterion of weldability and with a given class or series of steels for which the ductility under weld heat-treatment is known the test is entirely suitable. However, in studying a new steel the hardness survey is of less value, since it is based on the assumption that there is a correlation between hardness and ductility. Several attempts have been made to derive indices for weldabilityl and hardenability from the chemical analysis. In most of these proposals the effects of the different elements were considered to be additive, but recently Grossmann2 proposed a novel method of calculating the hardenability of a steel from its chemical composition. In the method proposed, a steel is considered as having a base hardenability due to its car- bon content and grain size, and this base hardenability is multiplied by a factor for each chemical element present. The final product is the hartlenability. The purpose of the present study is to point out the possible relationship between hardenability and the effect of welding on hardness and ductility for a number of plain carbon and low-alloy steels. The composition of the 25 steels reported in this paper as determined by chemical analysis is given in Table I. To eliminate the effect of variations in finishing temperatures, the 1/2-in. plates were normalized after heating for one hour at 1650°F. in a con-trolled-atmosphere furnace. In making comparative tests, it is essential to hold conditions as Constant as possible; hence full automatic weltling control was used. The electrodes, all supplied by

Jan 1, 1943

By G. G. Luther, C. E. Jackson

The relationship between hardenability and weldability has been mentioned many times. The ease of making a hardness survey has led to its wide use as a criterion of weldability and with a given class or series of steels for which the ductility under weld heat-treatment is known the test is entirely suitable. However, in studying a new steel the hardness survey is of less value, since it is based on the assumption that there is a correlation between hardness and ductility. Several attempts have been made to derive indices for weldabilityl and hardenability from the chemical analysis. In most of these proposals the effects of the different elements were considered to be additive, but recently Grossmann2 proposed a novel method of calculating the hardenability of a steel from its chemical composition. In the method proposed, a steel is considered as having a base hardenability due to its car- bon content and grain size, and this base hardenability is multiplied by a factor for each chemical element present. The final product is the hartlenability. The purpose of the present study is to point out the possible relationship between hardenability and the effect of welding on hardness and ductility for a number of plain carbon and low-alloy steels. The composition of the 25 steels reported in this paper as determined by chemical analysis is given in Table I. To eliminate the effect of variations in finishing temperatures, the 1/2-in. plates were normalized after heating for one hour at 1650°F. in a con-trolled-atmosphere furnace. In making comparative tests, it is essential to hold conditions as Constant as possible; hence full automatic weltling control was used. The electrodes, all supplied by

Jan 1, 1943

By S. Dinda

A series of as -quenched 4340 bars were drawn through a carbide die to various reductions. The X-ray diffraction technique of Lopata and Kula was employed to detect preferred orientation in drawn martensitic steel bars with low amounts of deformation, as lord as 0.8 pct The specimen face of each bar examined was cut at a 45-deg angle to the bar axis. The reflecting planes in the 45-deg face were varied by appropriate rotation of the sample using a spectrogonionzeter. TIE X-ray bean of a diffractometer was reflected from the center of the bar and the diffracted intensity was delected with a proportional counter and recorded. Intensity peaks were developed by cold working for 110 planes oriented at 0 and 60 deg to the bar axis. The intensity peaks increased with increasing defortnalion us a preferred orientation with a 110 texture developed parallel to the drawing direction. The intensity peaks for deformed as-quenched specimens remain unchanged after tempering at temperatures as high as 1000°F. The same amount of preferred orienlalion was observed both inferritic (hot-rolled) and martensitic (as-quenched) structures after an equivalent amount of deformation. THE deformation of martensite with medium carbon content. less than 0.5 pct, has been studied by Breyer et a1.1,2 It was reported that changes in properties such as resistivity, carbide precipitation, and the introduction of a yield point phenomenon were produced after cold reduction of as-quenched AISI 4340 steel bars. Later, Breyer and Nachtman3 studied the effect of cold reduction upon X-ray line intensity. They showed that the integrated 110 line intensity increased with increasing deformation when the planes examined were perpendicular to the die drawing direction. The integrated 110 line intensity for planes oriented at 45 deg to the die drawing direction, in contrast, were found to slightly decrease. These changes were proposed to be consistent with the previously proposed model of a stress-induced ordering of carbon atoms in the vicinity of dislocations.1,2 Objections can be raised to the above interpretation of the X-ray results on two grounds: a) Rough structure factor calculations indicate that the intensity changes are too large (50 pct observed vs 2 pct calculated4,5) to be the result of changes in the location of iron atoms produced by the stress-induced ordering of the carbon atoms. b) The results might be explained in terms of preferred orientations, although X-ray evidence of the development of texture has not been reported in the literature for deformations as slight as 1 or 2 pct. The aim of the present work was to determine if preferred orientation was present in such cold-drawn martensitic steel bars. In drawn rod or wire there is generally a certain crystallographic direction which is aligned in the direction of the wire axis, and the crystallographic planes are distributed symmetrically around this "fiber axis".6-8 This type of cylindrical specimen, with the fiber axis located at the center, will show rotational symmetry. Lopata and Kula9 proposed an experimental method utilizing a specimen cut at 45 deg, see Fig. 1. The X-ray beam is diffracted from the center of this bar cross section. The specimen is rotated around an axis perpendicular to the bar axis and lying in the 45-deg cut face. This permits the angle between the normals to the reflecting planes and the bar axis to be varied from 0 to 90 deg.9 With this arrangement the errors due to absorption and irradiated volume compensate each other.' This greatly simplifies analysis of the data and is of considerable advantage for quantitative measurements. If there is preferred orientation in the specimen, more planes are oriented in a particular direction in the bar. When the bar is rotated to the favorable Bragg condition for that particular orientation, the intensity will be higher than that for some other angle. This technique was adopted for the present investigation.

Jan 1, 1969

By L. D. Godshall

A great deal has been written of late regarding the loss of silver in assaying; very discordant results have been published by different writers, and much uncertainty exists concerning even approximate losses in a careful determination of silver, as represented by a fire-assay. In the present paper it has been the aim of the writer to determine as accurately as possible the losses sustained by silver, under certain specified conditions, during the process of cupellation. Such losses are well known to be due to absorption by the cupel and volatilization. The conditions, however, which govern these losses are not believed by the writer to be so well understood. The most important of these are : 1. The effect of variable quantities of silver used. 2. The temperature of cupellation. 3. The character and quantity of impurities in the lead button. 4. The weight of the lead button. 5. The nature of the cupel. The following experiments were made for the purpose of demonstrating, as nearly as possible, the total loss of silver in cupellation under the most favorable conditions to be obtained in commercial assaying. Chemically pure silver and pure lead were taken. The latter was obtained from test-lead, first melted into a bar, from which pieces of the desired weight were cut and accurately weighed. The experiments recorded in this paper were planned by the writer, but executed throughout by Mr. J. N. Walker, whose ability as an accurate, careful and painstaking assayer is too well known and recognized throughout the West to require any further endorsement from me.

Jan 1, 1897