By O. George Specht, Carl A. Zapffe

In recent print, some remarkably contradictory statements have appeared regarding the importance to be attached to sponge Iron,1-6 a metallurgical commodity whose history goes back at least to the time of Diodorus Siculus in the fourth century B.C. This disagreement, however, expresses the lack of a satisfactory method for producing sponge iron rather than defection in the commodity. The blast furnace is admitted to have certain inherent disadvantages, such as a general unsuitability for magnetite and the heating and blowing of vast quantities of undesirable nitrogen, so that a workable sponge-iron process remains attractive. In this respect, low-temperature gaseous reduction shows especial promise; but confusion persists regarding the factors involved. The present paper, therefore, has three principal divisions: (I) an exhaustive examination of all previous work on low-temperature gaseous reduction, (2) experi- mentation on the reduction of a magnetite with hydrogen, and (3) development of certain thermodynamic relationships in reduction, with a summarized depiction of the factors in the general process. PREVIOUS INVESTIGATIONS Gaseous media used in the reduction processes under discussion can be classified in three types: (I) H2, (2) CO, and (3) other gases. In the second, the CO is often admixed with H2. The third principally comprises hydrogeniferous gases, such as natural gas and producer gas, and in addition includes chlorine. Because hydrogen therefore features in all three, a study of hydrogen reduction based on investigations using pure hydrogen alone may be incomplete. The present paper reviews the three groups of investigations in the listed order, paying particular attention to hydrogen reduction. For the benefit of future workers, an exhaustive bibliography has been prepared and similarly classified. Group I: Reduction with Hydrogen Equilibria Although the present problem is specifically one of kinetics, a first consideration is the equilibrium of the system, since the reactions to be studied comprise that equilibrium, and their direction and end points are defined by it. The historic development of these researches is interesting and informative.

Jan 1, 1947

By O. George Specht, Carl A. Zapffe

In recent print, some remarkably contradictory statements have appeared regarding the importance to be attached to sponge Iron,1-6 a metallurgical commodity whose history goes back at least to the time of Diodorus Siculus in the fourth century B.C. This disagreement, however, expresses the lack of a satisfactory method for producing sponge iron rather than defection in the commodity. The blast furnace is admitted to have certain inherent disadvantages, such as a general unsuitability for magnetite and the heating and blowing of vast quantities of undesirable nitrogen, so that a workable sponge-iron process remains attractive. In this respect, low-temperature gaseous reduction shows especial promise; but confusion persists regarding the factors involved. The present paper, therefore, has three principal divisions: (I) an exhaustive examination of all previous work on low-temperature gaseous reduction, (2) experi- mentation on the reduction of a magnetite with hydrogen, and (3) development of certain thermodynamic relationships in reduction, with a summarized depiction of the factors in the general process. PREVIOUS INVESTIGATIONS Gaseous media used in the reduction processes under discussion can be classified in three types: (I) H2, (2) CO, and (3) other gases. In the second, the CO is often admixed with H2. The third principally comprises hydrogeniferous gases, such as natural gas and producer gas, and in addition includes chlorine. Because hydrogen therefore features in all three, a study of hydrogen reduction based on investigations using pure hydrogen alone may be incomplete. The present paper reviews the three groups of investigations in the listed order, paying particular attention to hydrogen reduction. For the benefit of future workers, an exhaustive bibliography has been prepared and similarly classified. Group I: Reduction with Hydrogen Equilibria Although the present problem is specifically one of kinetics, a first consideration is the equilibrium of the system, since the reactions to be studied comprise that equilibrium, and their direction and end points are defined by it. The historic development of these researches is interesting and informative.

Jan 1, 1947

By O. George Specht, Carl A. Zapffe

IN recent print, some remarkably contradictory statements have appeared regarding the importance to be attached to sponge iron,1-6 a metallurgical commodity whose history goes back at least to the time of Diodorus Siculus in the fourth century B.C. This disagreement, however, expresses the lack of a satisfactory method for producing sponge iron rather than defection in the commodity. The blast furnace is admitted to have certain inherent disadvantages, such as a general unsuitability for magnetite and the heating and blowing of vast quantities of undesirable nitrogen, so that a workable sponge-iron process remains attractive. In this respect, low-temperature gaseous reduction shows especial promise; but confusion persists regarding the factors involved. The present paper, therefore, has three principal divisions: (I) an exhaustive examination of all previous work on low-temperature gaseous reduction, (2) experimentation on the reduction of a magnetite with hydrogen, and (3) development of certain thermodynamic relationships in reduction, with a summarized depiction of the factors in the general process. PREVIOUS INVESTIGATIONS Gaseous media used in the reduction processes under discussion can be classified in three types: (I) H2, (2) CO, and (3) other gases. In the second, the CO is often admixed with H2. The third principally comprises hydrogeniferous gases, such as natural gas and producer gas, and in addition includes chlorine. Because hydrogen therefore features in all three, a study of hydrogen reduction based on investigations using pure hydrogen alone may be incomplete. The present paper reviews the three groups of investigations in the listed order, paying particular attention to hydrogen reduction. For the benefit of future workers, an exhaustive bibliography has been prepared and similarly classified. GROUP I: REDUCTION WITH HYDROGEN Equilibria Although the present problem is specifically one of kinetics, a first consideration is the equilibrium of the system, since the reactions to be studied comprise that equilibrium, and their direction and end points are defined by it. The historic development of these researches is interesting and informative.

Jan 1, 1946

By W. Hume-Rothery

IN recent interesting papers,1,2 Bardos et al. have described ternary Laves phases of the type A2(BsSi) and A4(B5Si3) where A = titanium vanadium, niobium, and so forth, and B = manganese, iron, cobalt, or nickel; other more complex formulae have also been established. In these phases, silicon plays the part of the smaller B atom of a Laves phase AB2, and the interatomic distances show that the effec- tive silicon radii lie between 1.16 and 1.21Å, and are thus very much smaller than the metallic radius of silicon for CN = 12. It does not seem to have been pointed out that these small atomic radii are almost the sape as the normal covalent radius of silicon (1.174Å). If, therefore, silicon acts as an acceptor of electrons as suggested by Bardos et al.,1 it appears to do so, not by the building up of a negatively charged silicon ion which would be large, but by the formation of what are very nearly or may be actually normal covalent bonds. Since a covalent bond contains two electrons, its formation would reduce the number of electrons available for bonding in other parts of the structure, and in this way the effect of silicon in stabilizing the o phase at high electron concentrations might be understood.

Jan 1, 1965

By Jay R. Burns

Two magnesium sand-casting alloys are commonly favored in the United States. These are referred to as H and C alloys (Dow Chemical Co.) or AM265 and AM260 alloys (American Magnesium Corporation). Both are of an aluminum-zinc-manganese type. H alloy contains 6 per cent aluminum and 3 per cent zinc and is characterized by relatively good toughness. C alloy contains g per cent aluminum and 2 per cent zinc and is employed where high yield strength and pressure tightness are required. Examination of magnesium castings poured in Europe and England,1,2 however, demonstrates that H and C alloys are replaced by A8 and AZ91, respectively. That is, A8 represents a magnesium alloy having superior toughness while AZ91 is suitable for high yield strength and pressure-tight applications. The basic difference between the American and European alloys is that the foreign alloys employ a somewhat higher aluminum content and less zinc than is found in H and C alloys. The mechanical properties of the alloys, when divided into high and low-aluminum groups, are quite similar, as determined from separately cast foundry-control type test bars.3 In this paper the decrease of mechanical properties caused by any given amount of microporosity is measured for H, C, A8, and AZ91 alloys. The relative susceptibility of each of the four alloys to microporosity is also determined. Typical mechanical properties and nominal chemical analyses are reported in Table I. [ ] The apparent similarities between the two alloys in each group have led to considerable discussion as to the relative merits of each of the compositions.2 Popular points for comparison between the alloys have been the relative susceptibility of each of the four alloys to microporosity5 and the effect of this microporosity on their mechanical properties. It is primarily intended, in this paper, to show the

Jan 1, 1946

By Hannu Penttila, Harrison R. Cooper, Olli Mattila

Two approaches to automated operation in metallurgical processes involve the conventional analog control or, more recently, digital control. The expanding use of digital controls applied to process automation is a comparatively new development. Several current technical reports describe digital control systems in concentrator grinding control, 1, 2, flotation, 3 and smelter operations. 4,5 The principle factors influencing trends to digital control are:

Jan 10, 1976

By J. L. McK. Yardley

There are two general classes of problems in connection with electric furnaces. First, those relating to the best utilization of the electrical power inside the furnace; second, those connected with the bringing of the electrical power to the point where it is to be utilized. Referring particularly to the latter class of problems, many calculations have been made, covering a wide variety of furnaces, to check the electrical capacity and power factor found from test. The following analysis, made for the purpose of determining the maximum capacity and approximate performance of a new furnace, to operate at 160 volts on a 60-cycle circuit, may be of interest. The first characteristic necessary to determine is the inductance, since this is the factor that limits the amount of power which can be put into the furnace. Inductance is calculated from the dimensions of the furnace, according to formulas of the U. S. Bureau of Standardsll as follows. Formula 99, for mutual inductance, is: M = 2l [log 2l/d-1 +d/l] Formula 103, for self-inductance, is: Both of these formulas are approximations which are nearly correct when 1 is great compared to d or R. 1 = length of circuit, in centimeters, d = separation between the conductors, in centimeters, R = geometric mean radius of conductors. For a circular tube, R = the radius of the circle. For a solid circular conductor, R = 0.7788 X the radius of the conductor. For a rectangular conductor, R = 0.2235 X (a + b), a being the length, and b being the width of the rectangle. To calculate the inductance of a three-phase circuit, it is customary to figure the inductance of one leg. In circuits where the three conductors

Jan 1, 1920

By John S. Brown

AT opposite ends of a mineralized belt of northeast-southwest trend, and ten miles apart, are the Edwards and Balmat zinc minas, in St. Lawrence County, New York, west of the Adirondacks. The principal town is Gouverneur, fifteen miles west of Edwards, eight miles northwest of Balmat, and the area is often referred to as the Gouverneur district. (See Fig. 1.) At various times the district has been noted for its hematite mines, pyrite mines, and marble quarries, all now abandoned. At present, in addition to zinc, it is the country's largest source of industrial talc. A short distance to the east important magnetite mines are operating. Geologically the district lies at the southern margin of the Canadian shield, where this great expanse of Pre-Cambrian igneous and metamorphic rocks merges into the foothills of the Adirondacks. The rock formations in approximate order of areal extent and importance are as follows:

Jan 1, 1947

Jan 1, 1929

By L. L. Swift

AT the present time there are four base metals being used for automotive bearing alloys. Of course there are numerous variations in the amounts of alloying elements added to each base metal and nearly all of these alloys have the conventional, if not classical, duplex structure; that is, they are composed of a hard constituent embedded in a soft matrix. The well-known theory is that the former will wear well, while the latter will be plastic enough to allow the bearing to be broken in and conform to the contours of the shaft. The requirements of the modern bearing have been most aptly described by W. M. Corse: In order to meet the engineering demands of today a good bearing metal must be able to carry the weight of the shaft and stand up under steady or suddenly applied loads, or even blows in some types of service. A certain amount of plasticity is desired to compensate for minute irregularities in the shaft or bearing surface, and to permit yielding, thereby avoiding dangerous stresses in bearing and shaft and preventing overheating and rapid wear of parts. Less plasticity is required in a bearing metal if the surfaces of bearings and journals are machined accurately, aligned, and kept in alignment. It is desirable, of course, that a bearing metal have a low coefficient of friction. Under most operating conditions the friction depends on the unit pressure of the bearing, the speed, the temperature, and the properties of the lubricant. A good bearing metal must have a low rate of wear to reduce the necessity for frequent replacements, and adjustment of the bearings. It must wear more rapidly, however, than the journal or shaft running on it, because replacement of the journal or shaft is more difficult and costly than replacement of the hearing., The hardness of, the bearing alloy is a property closely related to several of the foregoing. With a duplex microstructure, the measurement of hardness with any of the usual commercial devices means little. The Bierbaum method of measuring the hardness of the individual constituents was developed to, fill this need. MICROCHARACTER The Bierbaum microcharacter2.3 measures the scratch-hardness of a solid by pulling a weighted diamond point over the surface. The diamond point is ground. so that it is the corner of a cube, and mounted

Jan 1, 1938

By R. S. Wagner, C. E. Miller, H. Brown

A dc field was applied to liquid BI-Sx or Au-Ge alloys of eutectic composition. The liquid alloys were kept at a temperature slightly above the eutectic. The concentration changes due to electrodijfusion are large enough to cause nuclcation and growth of the primary phases at the respective electrodes. Nearly complete separation of Bi-Sn eutectic was obtained as well as substantial separation of Au-Ge eutectic. The effect of an electric field on the solute distrihn-tion was itluestignted itt tlirectiortally solidified rods of a dilute Bi-Sn (0.5 al. pc,t Bi) alloy. Field-freezing was carried out in small-diameter cupillay tubes to avoid cotuectice mixing -of the liquid. The relative sollcte corzcentratioi, Cs/Co , was rneusred by n radioac1il.e tracer netlod. Cs/Co can be made both largev than unity or srialler than the equilibiuwz distvibrrlion c.oejyicienl, k, , oiler a substattiul portion of the soliclifi&apos;erl rocls. A direct current, passed through a liquid-metal solution, can cause substantial concentration changes by electrodiffusion. The magnitude of the change depends on the difference in ionic mobilities of the atomic species in solution. Electrodiffusion has been studied in many binary and ternary liquid alloys.&apos;y2 It was found that the rate of material transport decreases with time for a constant applied field, as a concentration gradient is established in the solution. A steady-state concentration profile is achieved when electro-diffusion is compensated by chemical diffusion. This may seem to limit the use of electrodif fusion for metallurgical application. However, a way of utilizing the effect of electrodiffusion is to combine it with crystallization or controlled freezing. rakin was first to propose this as a new method of separating metal alloys of eutectic composition at temperatures slightly above the eutectic temperature. It was possible by this method to separate Bi-Sn and Bi-Cd eutectics into their component phases. Angus et al discussed the possibility that the effective distribution coefficient, keff, could be varied by proper application of an electric field during solidification. The combination of electrodiffusion and solidification, called field-freezing, was discussed in detail by Pfann and aner. It was shown that field-freezing can be used as a crystal-growth process, an efficient method for eutectic separation, and a new means of changing the effective distribution coefficient. k,ff, beyond the usual range of ko < k,ff < 1. The liquid layer adjacent to the solid-liquid interface can be either increased or depleted in solute due to

Jan 1, 1967

By D. J. McAdam

In a recent survey of the literature, the author has found evidence incompatible with prevalent views regarding the technical cohesive strength and yield strength of metals. Some of the evidence regarding the technical cohesive strength was presented in a previous paper,21 and views were presented that are believed to be in better accord with the evidence. In that paper, it was shown that the technical cohesion limit (contrary to prevalent views) varies with the combination of principal stresses,t and that the influence of plastic deformation on the technical cohesive strength is not in accordance with prevalent views. In this paper, consideration will be given to both the technical cohesion limit and the yield stress as affected by the combination of principal stresses. Evidence will be presented that the variations of the yield stress and the technical cohesion limit with the combination of principal stresses are not in accordance with prevalent views. Consideration will also be given to ductility and work-hardening capacity, which depend on the initial difference between the technical cohesion limit and the yield stress. By the "technical cohesion limit" is meant the mean stress at actual or poten- tial* fracture. An example of a rechnlcal cohesion limit is the "true" breaking stress of a tension-test specimen, the breaking load divided by the sectional area at fracture. The cohesion limit thus obtained for a ductile metal, however, has been greatly altered by the plastic deformation. It is important to consider the cohesion limit of the metal prior to this deformation, and the variation of the cohesive strength with plastic deformation. The relation between the cohesion limit and the corresponding flow stresst determines the ductility of a metal and the energy that it will absorb before fracture. In this paper, as in the previous paper,21 tensile stresses will be viewed as positive and compressive stresses as negative. The algebraically greatest principal stress will be designated S1, the least principal stress will be designated S3, and the intermediate principal stress will be designated Sz In the previous paper, attention was confined to stress combinations with two of the principal stresses equal (with the intermediate principal stress S2 equal eithel to S3 or 31). In this paper, consideration will also be given to the effect of stress combinations with all three principal stresses unequal. In the earlier sections of the paper (pp. 3I I to 324), attention will be confined to stress combinations with

Jan 1, 1942

By D. J. McAdam

In a recent survey of the literature, the author has found evidence incompatible with prevalent views regarding the technical cohesive strength and yield strength of metals. Some of the evidence regarding the technical cohesive strength was presented in a previous paper,21 and views were presented that are believed to be in better accord with the evidence. In that paper, it was shown that the technical cohesion limit (contrary to prevalent views) varies with the combination of principal stresses,t and that the influence of plastic deformation on the technical cohesive strength is not in accordance with prevalent views. In this paper, consideration will be given to both the technical cohesion limit and the yield stress as affected by the combination of principal stresses. Evidence will be presented that the variations of the yield stress and the technical cohesion limit with the combination of principal stresses are not in accordance with prevalent views. Consideration will also be given to ductility and work-hardening capacity, which depend on the initial difference between the technical cohesion limit and the yield stress. By the "technical cohesion limit" is meant the mean stress at actual or poten- tial* fracture. An example of a rechnlcal cohesion limit is the "true" breaking stress of a tension-test specimen, the breaking load divided by the sectional area at fracture. The cohesion limit thus obtained for a ductile metal, however, has been greatly altered by the plastic deformation. It is important to consider the cohesion limit of the metal prior to this deformation, and the variation of the cohesive strength with plastic deformation. The relation between the cohesion limit and the corresponding flow stresst determines the ductility of a metal and the energy that it will absorb before fracture. In this paper, as in the previous paper,21 tensile stresses will be viewed as positive and compressive stresses as negative. The algebraically greatest principal stress will be designated S1, the least principal stress will be designated S3, and the intermediate principal stress will be designated Sz In the previous paper, attention was confined to stress combinations with two of the principal stresses equal (with the intermediate principal stress S2 equal eithel to S3 or 31). In this paper, consideration will also be given to the effect of stress combinations with all three principal stresses unequal. In the earlier sections of the paper (pp. 3I I to 324), attention will be confined to stress combinations with

Jan 1, 1942

By Max Roesler

W. L. CUMINGS,* Bethlehem, Pa. (communication to the Secretary+). -In this discussion of Mr. Roesler&apos;s paper, I shall follow Kemp in using the term "granite" to refer to the acid rock called syenite by Kimball. Diorite, as I understand it, is the dark basic rock invariably closely associated with the orebodies. The types of rock of intermediate composition, mainly intrusives, are not under discussion. It is difficult for me to conceive that this granite is the ore-bearing agent, for the following reasons: 1. No isolated orebodies in the granite are known. It would seem that if this rock is the mineralizer, some small bodies, or at least patches and small masses of ore so situated would exist. 2. In 1909 the writer conducted explorations on the Pequena and Grande claims about 1 mile north of West Mine No. 5. This work was done after a very careful magnetic survey had shown a large and uniform area of attraction. As exploration progressed, it became evident that in this case the magnetic attraction was due to disseminated magnetite. Much ore of 40 per cent. Fe was found, but very little commercial ore was shown up. This ore was entirely in the diorite and no granite outcrops are near. The occurrence could easily have been described as "ore formation but very little ore." I cannot conceive how a remote granite intrusion could impregnate a diorite mountain with 40 per cent. of Fe, and prefer to believe that this 40 per cent. of iron was in its real home, rather than in a sort of dioritic "boarding house" after having been evicted by granitic parents. 3. The Ocaña mine, which has produced nearly 500,000 tons, shows no evidence that the granite is the mineralizer. This is admitted by Mr. Roesler on p. 1827. 4. I believe it will not be disputed that all the iron-ore deposits extending along the south coast for 60 or 70 miles are of a similar origin. Evidence available at other points might properly be referred to in discussing the article under review. At the La Plata mines, about 60 miles west of Santiago, the writer has also made explorations. No granite is in evidence. At one point in the bed of a creek is a small body of magnetite about 10 ft. long, entirely surrounded by a hard fresh diorite. To me

Jan 3, 1917

RECEIPTS [Magazine Advertising $ 62,564.83 Magazine Sales 3,591.44 Totalm 66,156.27 Dues, Arrears7,032.88 Dues. Current96,839.74 Dues, New Members6,525.00 Dues, in advance 1,907.02 Initiation Fees7,584.00. Sale of Transactions3,909.03 Sale of Binding7,845.05 Sale of Special Editions 338.20 Sale of Year Book76.20 Sale of Pamphlets1,189.06 Sale of Authors&apos; Reprints867.54 Miscellaneous Receipts62.93 Interest on Bank Balances1,712.89 Interest on General Reserve Fund337.50 Interest on Life Membership Fund557.84 Interest on James Douglas Library Fund....5,491.89 Total Receipts$208,433.04] [ ]

Jan 1, 1925

By W. J. Taylor

Some eight years ago I became interested to a considerable extent in one of the well-known deposits of sulphury iron ore in New Jersey, and, as a consequence, soon became interested in the subject of the elimination of the sulphur. On investigation I found that no department of pig-iron manufacture had received less attention than that of roasting or calcining ores for the elimination of sulphur, carbonic acid, water, etc. My first devices to eliminate sulphur mere naturally in the limekiln line, with solid fuel mixed with the ore, in the same way = common lime is burnt with small coal. While this process will succeed tolerably well for carbonates or calcareous ores, even though they contain sulphur as sulphates, I soon found it would not answer for our magnetites, which are very hard and dense, carrying from 2 to 5 per cent. of sulphur as pyrites, and become very sticky as soon as any attempt is made to roast them at a high heat. Some laboratory experiments developed the fact that the nearer the gaseous current surrounding the hot ore approached in composition pure atmospheric air the more rapidly the sulphur was oxidized, while in an atmosphere composed largely of carbonic oxide, carbonic acid, and nitrogen, it seemed almost impossible to reduce the sulphur more than one-half, which was a confirmation of the well-known Pact that just one-half of the sulphur in pyrites volatilizes very easily, and that the trouble is mainly to remove the remainder. It was thus apparent that the atmosphere surrounding the ore was of as much importance as the temperature..• This led to the trial of a kiln to heat the ore by conduction through the brick. It was divided into ore-chambers, which were surrounded with flues, through which the products of combustion of gaseoua fuel passed without coming in contact with the ore. We did not, however, succeed by this arrangement in getting more than a cherry-red heat, which, of course, was too low to accomplish anything. I had at this point become convinced— 1st. That gaseous fuel only would accomplish the work successfully. 2d. That since a high temperature was required to insure a rapid oxidation of the sulphur, and also to make the ore open and porous,

Jan 1, 1881

The Telfer Project, one of the world&apos;s newest gold mines, is located about 300 km (190 miles) northeast of the Mt. Newman iron ore project in the northern part of Western Australia. The first mineral claims were staked in 1972; and by mid-1975 ore reserves of 3. 8 million mt (4. 19 million st) of 9.6 g per mt (0. 28 oz per st) ore had been indicated. It is interesting to note that Newmont spent more than 10 years and A$10 million in Australia for extensive mineral exploration before finding the Telfer deposit, and then spent approximately A$3 million in exploration and feasibility engineering on Telfer. Including this A$3 million, a total of A$27 million was spent to complete construction of the mine, village, gold treatment plant and associated roads, airport, water and services. Over 50% of the capital cost is in the metallurgical facility, or approximately A$10, 000 per ton per day. All economically significant gold mineralization at Telfer occurs in a series of layered quartz-limonite reefs in which the former pyrite has been oxidized to limonite to a depth of 100 m (330 ft). The most important gold reef occurs at the base of the siltstone-shale horizon within the enclosing sandstone dome -like structure. At the Main Dome structure the dipping ore horizons will be mined to a vertical depth of about 60 m (200 ft) by open-cut methods. The waste-to-ore ratio is approximately 12:1. Eventually 44 million mt (48. 5 million st) of ore and waste will be mined. Mining of the waste is by contract; however, the ore and a thin layer of waste is company-mined. Dilution from mining the geological ore reserve is about 10%. The ore is completely oxidized and the gold occurs free within the reef, material as discrete particles of varying but mainly fine grain size. Most of the gold is "free milling"; that is, over 50% of the gold is coarse enough to be recoverable by gravity concentration. Two duplex mineral jigs receive the two cyclone underflows from the grinding circuit. The rougher jig concentrate is up-graded on a continuous strake from which the concentrate is tabled to produce a final free gold product. Jig tailings are returned to the ball mill and the concentrates are amalgamated. Gold amalgam is pressed, retorted, and melted into gold bars. The gravity gold recovery circuit is the same as was used in many of the gold mills in California in the 1930s.

Jan 1, 1981

By N. J. Grant, D. S. Bloom

N recent reports, Sully&apos; and Beck and coworkers&apos; I have advanced hypotheses concerning the formation of the phase. Both of these hypotheses are based on Pauling&apos;s theories of the electronic configuration of the elements of the first transition group. Sully considered that the number of electrons which can be absorbed in filling electron "holes" is the factor which determines whether or not the structure can form. Beck suggested that the presence of a certain concentration of electron "holes" is the controlling value. It can be shown that a similar criterion can be developed without making reference to Pauling&apos;s theories. Table I shows the elements of the first transition group and the incidence of the a structure in the binary systems of these elements according to the data presently available. Also appended is the number of electrons considered to exist in the 3d-4s levels of these elements. If the atomic percentages for the phase are listed as shown in Table 11, and if the number of electrons in the 3d-4s levels per atom is calculated for the a boundary values, the results are as shown in the last column. It can be seen that the numerical values are all in the vicinity of 7 electrons per atom. This is true also for the ternary Cr-Mo-Ni IT phase, which occurs in a system in which none of the binary compositions are known to develop the phase. In the Fe-Mo binary, the high temperature a phase, which occurs at a composition of 50 atomic pct of each element, also yields a ,;1 e of 7 electrons per atom. From inspection of Tables I and 11, it develops that any series of sequential numbers which is assigned to the elements under consideration will result in the numbers pertaining to a compositions grouping themselves around one specific number. It does not follow, however, that this random number necessarily has physical significance. Such a point has already been discussed by Hume-Rothery." One interesting point develops from this study, however, and that is the position of manganese with reference to the other elements and to the phase. In the system used here, the formation of phase is associated approximately with the value of 7 electrons per atom, which is also the number of electrons per atom that manganese has. Manganese, it will be recalled, exists in three different crystal forms, none of which are the usual, simpler metallic forms; on the other hand, elements just to the left of manganese (in Table I) generally have lower coordination-number structures (body-centered cubic) than do elements to the right of manganese (face-centered cubic). The contribution to a complex crystal structure by the interalloying of elements from opposite sides of manganese is significant in that the a phase is formed in binary systems including one element from each side of manganese, with manganese capable of participating with both sides. It is indeed an interesting coincidence that manganese, with 7 electrons per atom, solidifies in complex crystal forms, and that when alloys of the transition elements are made which have seven 3d-4s electrons per atom, they, too, tend to assume a complex crystal form. From the above, it might be deduced that the study of the a phase might be advanced by a critical examination of the element manganese and how its structure is affected by small additions of elements which change the 3d-4s electrons per atom number. The role of atom size would also be of interest in formation. References &apos; A. H. Sully: The Sigma Phase in Binary Alloys of the Transition Elements. Journal Inst. Metals (1951) 80, Part 4, p. 173. 2 S. Rideout, W. D. Manly, E. L. Kamen, B. S. Lement, and P. A. Beck: Intermediate Phases in Ternary Alloy Systems of Transition Elements. Trans. AIME (1951) 191, p. 872; Journal of Metals (October 1951). "W. Hume-Rothery, H. M. Irving, and R. J. P. Williams: The Valencies of the Transition Elements in the Metallic State. Proc. Royal Soc. (September 1951) 208A. p. 431.

Jan 1, 1954

By George A. Hill

WE of the oil industry, devoted to freedom of initiative, free competitive enter- prise, and free American institutions, applaud, with one voice, affirmation by the President of the national will and purpose to preserve and to protect, against all aggressors, "our American way of life with our individual and national freedom." We subscribe utterly and completely to this guiding declaration and seek its further definition as applied to the oil industry. Fortunately for all, the policy of the Government, after adequate study and deliberation, has been given precise definition. The National Defense Advisory Commission, with its patriotic, highly qualified, and distinguished personnel, has unanimously agreed to and adopted twelve general principles governing national defense contracts and also fair labor standard requirements. The President of the

Jan 1, 1940

By W. W. Coblentz

THE constants in question pertain to the total radiation and the spectral radiation of a uniformly heated enclosure, or so-called black body. These constants have been determined for the range within which temperatures can be measured with thermocouples. Conversely, using these constants and suitable instruments, such as an optical pyrometer, for example, it is possible to determine temperatures far above the range attainable with the most refractory thermocouples. The formula of Stefan Boltzmann for expressing the total radiation of a black body is R = kT4 in which k is the coefficient or "constant" under discussion. In view of the fact that total radiation pyrometers are usually calibrated on an arbitrary scale, there is no great demand for an exact value of the coefficient of total radiation in absolute value. However, it is intimately connected with the constant of spectral radiation; hence, an accurate determination of the constant k gives a check on the constant of spectral radiation. The distribution of radiation in the spectrum of a black body is represented by Planck&apos;s equation, E? = C1?-5 (e c/?T - 1)-&apos;. The spectral radiation constant c, in this formula, is useful in optical pyrometry and in establishing a high temperature scale. The numerical value of the constant c has been determined in the range of temperatures measurable with thermocouples and, also, by extending the temperature scale to higher temperatures by means of total radiation measurements.

Jan 8, 1919