(This list includes only those who have entered military service within the past month, or whose entry has only recently become known to us; it also includes a few names of those whose titles or assignments have been changed within the month. The last complete list was printed in Bulletin No. 131, November, 1917. A complete Honor List is maintained in the reception room at the office of the Institute.) BANKS, HAROLD P., 2d Lieutenant, Ammunition Train, 2d Division, U. S. A. BARKER, L. M., Co. B., 62d Infantry. BENHAM, W. M., Sergeant, Co. H, 158th Infantry. BOUDWIN, WALKER J., Co. C., 25th Engineers, Camp Devens, Ayer, Mass. BOWLES, MARTIN F., 2d Lieutenant, Co. B., 355th Infantry. BURG, ROBERT S., Instrument Sergeant, Headquarters Co., 340th Field Artillery, N. A. CHALMERS, JOHN W. P.; Signal Depot, Royal Engineers. CHETNEY, P. C., Corporal, 340th Field Artillery, Headquarters Co. CLARK,. WILL L., Federal Fuel Administrator for Arizona. COFFEY, George W., Lieutenant, Engineer Section, Officers' Reserve Corps.

Jan 1, 1918

By R. A. Nadler and

Specimens of Ti-155A (Ti-5Al-1.3Fe-1.3Cr-1.2Mo), Ti-6Al-4V and Ti-4Al-3Mo-1V were hydrogenated, aged to high strength levels, and subjected to notched stress-rupture tests and tensile tests at two strain rates. Both Ti-6Al-4V and Ti-155A were relatively unaffected by hydrogen in amounts exceeding those found in commercially -produced material. Inconsistencies in the data and a relatively low initial level of ductility prevented an accurate determination of the hydrogen tolerance for aged Ti-4Al-3Mo-1V, but there was no evidence that this alloy was any more susceptible to hydrogen embrittlement than Ti-155A and Ti-6A1-4V. THE metallurgical literature has been considerably enriched in the past five years by the publication of the results of many investigations which were concerned with the effects of hydrogen on titanium and its alloys. Although it is not the authors' intention to provide a complete literature survey of this vast field, it is worthwhile to summarize briefly some of the important factors which influence the embrittling phenomenon in a - B alloys. Some of the influencing factors are those of strain rate, temperature, and composition. Hydrogen embrittlement in a - B titanium alloys is now believed to be a strain-induced phenomenon, and whether or not embrittlement occurs at high hydrogen levels depends largely upon whether sufficient time is available for hydride precipitation. This condition is fulfilled by tensile testing at very slow strain rates or by rupture testing smooth or, preferably, notched specimens over relatively long periods. Conveniently, maximum embrittlement occurs at or near room temperature. The presence B - stabilizing elements, in amounts sufficiently small to prevent an all -B or nearly all -P condition, promotes hydrogen embrittlement and this tendency is believed to be related to the amount of a - B interfacial area present. Aluminum, by increasing the solubility of hydrogen in A titanium, greatly reduces the danger of hydrogen embrittlement, while oxygen has been shown to have detrimental effects.' The preceding discussion is based on experimental work performed on annealed a - P alloys. This early work has shown that annealed Ti-6A1-4V and Ti-155A are relatively insensitive to the embrittling effects of hydrogen.' Although no work has been reported on annealed Ti-4A1-3Mo-lV, the alloy would be expected to exhibit somewhat the same insensitiv-ity as Ti-155A. In sharp contrast to the voluminous literature on annealed titanium alloys is the paucity of reported investigations on materials receiving commercial heat-treatment cycles. To date, the most notable contributions in this field have arisen from two separate investigations on Ti-3Mn-1Fe-1Cr-1V-lMo, the so-called 3Mn comple~. These investigations

Jan 1, 1961

By W. B. Potter

THERE is probably no more interesting group of mineral fuels to be found in any country than that occurring within the limits of the new State of Colorado. The supplies are so abundant, and the occurrence and distribution are so favorable for easy development and transportation to the future manufacturing centres of the State, that they are destined to play a very important part in the material growth and prosperity of the region, the more so because of the rich and varied stores of ores awaiting metallurgical treatment, and the comparative scarcity of timber for fuel. From a purely scientific point, also, these lignitic coals form an interesting and important series. An examination of their geological occurrence and relations opens up new and important questions regarding the comparative value of various kinds of geological evidence, while a study of the character and composition of this class of fuels, which forms a connecting link, as it were, between the lignites and the true bituminous coals, may lead to a more thorough and accurate classification of mineral fuels. The analyses here presented are from samples, of not less than fifty pounds each, obtained by myself during the summer of 1875, and may be regarded as representing very fairly the average run of

Jan 1, 1877

By J. P. Hirth, A. H. Clauer

A simple graphical method is presented for the determination of climb forces on dislocations exerted by uniaxial stresses. In conjunction with standard stereographic projections, the technique is applicable for any crystal system. Climb forces on glide dislocations in bcc crystals are determined as an application. In connection with a study1 of elevated temperature creep of molybdenum single crystals, a detailed analysis of the climb force on a dislocation was necessary. In general, such forces can be calculated for an arbitrary dislocation segment from the Peach-Koehler equation2 (or one of its variants3"6) where Fk are the components of the force per unit length of dislocation line, ?i of the unit sense vector tangent to the line, ojl of the stress tensor, bl of the dislocation Burgers vector, and is the Einstein permutation operator with components ?123 = ?231 = ?321 = —?132 = — ?321 = —?—213 = unity, and all other components zero. It is understood in the suffix notation of Eq. [I.] that repeated indices are to be summed over 1, 2, and 3. For the most general coordinate system, the matrix manipulations required to solve Eq. [I] are fairly complex. However, a simplification can be achieved by specifying a coordinate system based on the dislocation in question. The pertinent system involves cartesian coordinates xi, x;, xi, with attendant unit vectors e'i; ei being parallel to the Burgers vector b, and e'3; being parallel to the climb directions (b x ?), i.e., normal to the slip plane. In this coordnate system b = (bi, 0, 0) and ? = (?'1,?'2, 0). Hence, Eq. [I] yields for the climb force per unit length F3 = ?'2s'11b'1—?'1s'12b'1 [2] The first term on the right side of Eq. [2] is the climb force on the edge component of the dislocation, while the second is the (cross-slip) force normal to the glide plane acting on the screw component. Thus, the problem of determining the climb force reduces to that of resolving the stress components —il and s'12 in the xi coordinate system. Several authors7- l0 have shown, for the glide case, that such stress resolution can be performed most readily by graphical methods. Therefore, we present a similar method for the climb case. Of the suggested methods, we follow that of Hartley and Hirth,9 which can be performed directly with a standard stereographic projection for the crystal system in question. We treat the case of simple tension, or compression, this being the most common creep test in which climb is important. A set of cartesian coordinates (x1, x2, x3) is fixed with x3 parallel to the specimen axis. This set is connected to the x'i set by the factors defined in Table I. A perspective view of the coordinate systems relating them to the glide ellipse, is given in Fig. 1, while a stereographic projection of the coordinate systems is presented in Fig. 2. The transformation matrix connecting the xi and xi coordinates is x'i =aijXj [3] where an a11 a13 aij = a21 a22 a23 a31 a23 [4] s The corresponding transformation for the stresses is i [5] The only nonzero component of okl for the simple tension case is s33,. Hence, using Eqs. [4] and 151, we find that Eq. [2] becomes F3 = b'1s33 sin2 cos ?[cos ? sin a - sin ? cos a] [6] = m1b'1s033 sin a- rn2b's33 cos a where sin a = 5: and cos a = ?i, with a the angle measured from b to ?, i.e., a polar angle in the x1, x2 plane. The same equation with a sign change applies for compression. A graphical plot of the "Schmid" factor m1, relating to the climb force on the edge component, is presented in the stereographic projection of Fig. 3. In this projection the glide plane normal points toward the top of the page and the glide direction points normal to the plane of the page. To use the graph, one

Jan 1, 1970

By A. Satter, J. M. Campbell

Reported herein are the results of a careful and detailed study of the non-ideal behavior of pure gases and their mixtures. Included are: (1) new data on five ternary systems composed of methane, ethane and H2 S; (2) a simple compressibility factor correlation that is inherently superior to present correlations, particularly for gases containing H2S and CO2; and(3) a detailed study of combination rules and the effect of system composition on the choice thereof. This study makes use of the rather large mass of data already available in the literature. A complete re-examination of the data and ideas presented in the last 25 years was considered desirable as a prelude to our basic concern — the effect of diluents on gas behavior. A consideration of both the macroscopic and microscopic properties of gases provides a better insight which, in turn, gives a firmer basis for improved correlation techniques. Such a study has shown that expressing the compressibility factor Z as a function of acentric factor w, as well as reduced temperature and pressure, yields a correlation that is broader in scope. The study of various combination rules has shown that better results are obtained by "tailoring" the rule used to the system composition. To do so improves the basic reality of results by overcoming some of the anomalies often found when using Kay's rule alone. Tentative recommendations are made regarding the most reliable combination rule for use with a given class of gas. The data presented are useful for estimating the direction and magnitude of the expected deviation when using a given rule. Although more work is needed, particularly around the critical region and with CO2 mixtures, the advantage of the classification scheme proposed is apparent. INTRODUCTION When one attempts to write a PVT equation to fit the data for actual gases, greater precision is obtained by the use of a multiple number of empirical constants. This has lead to multiple-constant equations such as Benedict-Webb-Rubin, Beattie-Bridgman, Keyes, etc., which are capable of yielding very precise results for pure gases in a range for which data to get the constants are available. As a matter of practicality, though, the use of such equations for gas mixtures is limited. Because of the infinite number of gas analyses available, any attempt to compile the constants needed requires a prohibitive amount of experimental data. This could be overcome by the use of a combination rule, but there is no real advantage in doing so because the end result offers no practical impovement over the Z factor correlation. The most widely used method of predicting the volumetric properties of pure gases is based upon the "theorem of corresponding states". According to this theorem, "all pure substances have corresponding molal volume at corresponding temperature and pressure if the reference point of correspondence is the critical point". Generalized compressibility charts for gases were prepared first by Cope and associates1 in 1931 and later by Brown and co-workers2 in 1932. However, the most commonly used charts are those of Dodge,3 Nelson and Obert,4 Hougen and atsson: and Standing and Katz.6 The work of Katz and co-workers has provided us with basic data for the hydrocarbons most widely used today. Their original chart6 was compared with a relatively large amount of multi-component data for gases consisting almost entirely of normal paraffin hydrocarbons. A deviation of only + 1.2 per cent was obtained.39 In the 20 years following publication of this work it has been found that the behavior of most mixtures of paraffin hydrocarbons could be predicted by this correlation within at least 5 per cent. Where difficulty has been encountered it has largely involved one or more of the following circumstances: pressures above 4,000 psig, mixtures containing large amounts of heavy ends and/or aromatics, systems in the critical region and mixtures containing polar compounds and/or CO2. The abnormal error sometimes found with such gases, not too unexpected for this method, is

By R. Simon, D. J. Graue

This paper presents correlations for predicting the solu-lility, swelling and viscosity behavior of CO2-crude oil sys8i.m~. The correlations were developed from experimental data obtained by the authors. These data are also presented. The data were determined by measuring the properties of mixtures of CO, and nine different oils. Experiinental conditions covered a range of 100 to 250°F and pressures up to 2,300 psia. Properties predicted by the correlations have average deviations, expressed as per cent of experimental value, of 2 per cent for solubility, 0.5 per cent for swelling and 12 per cent for viscosity. INTRODUCTION Interest in CO2 injection as an oil recovery process has led to the development of performance prediction methods which can be applied to specific reservoirs.1 iS To use these performance prediction methods, it is necessary to know the solubility, swelling and viscosity properties of CO2-crude oil mixtures at reservoir conditions. Some information on these properties has appeared in the literature; however, this information did not cover the range of different oils and conditions needed to prepare generalized correlations for reservoir engineering purposes. Consequently, an experimental program was undertaken to collect the data needed. The data obtained and the correlations developed from the data are described in the following sections of this paper. SOLUBILITY OF CO2 IN CRUDE OILS CO2 solubility data in the literature come from six principal sources. The solubility prediction method of Welker and Dunlop3 is limited to 80F. The information in Ref. 4 is of two types: the first includes binary and ternary mixtures of CO, and light hydrocarbons (C1 to C6), and the second gives data for CO1 and heavy hydrocarbons for a temperature range of 40 to 90F. Ref. 5 contains a KCO2 chart for systems whose convergence pressure is 4,000 psia. The KCO2's are based mainly on CO2-natural gas mixtures. Poettmann's work covered CO2 solubility in one condensate and one crude oil6,7 Ja-coby and Rzasa measured CO? solubilities as a function of pressure and temperature for two natural gas-absorber oil mixtures and two natural gas-crude oil mixtures.'8 CO, concentration in these four systems was fixed at 5 mol per cent. The work reported in this paper extends CO, solubility data to a variety of different crude oil types in a temperature range from 110 to 250F and pressures up to 2,300 psia. The experimental procedure used by the authors to obtain the solubility data consisted of combining known amounts of pure CO, and crude oil in a visual cell at a fixed temperature and measuring the bubble point of the mixture. Measurements were made for a total of 40 different CO2-oil mixtures and the results are shown in Table 2. The mixtures included nine different oils (seven crude oils and two refined oils) whose properties are listed in Table 1. All nine oils had vapor pressures less than 1 atm at the experimental temperatures. Consequently, analysis of the bubble-point vapor showed a CO, concentration over 99 mol per cent. At no time during these experiments was a second, more dense, liquid phase observed. The solubility correlation which was developed from the data in Table 2 is presented in Figs. 1, 2 and 3. In these figures, solubility is expressed as xco2 the mol fraction of CO, in the CO2-oil mixture. Fig. 1 shows solubility as a function of CO2 fugacity6 and temperature. Fig. 2 shows the same solubility data expressed as a function of saturation pressure and temperature. The solubility shown in Figs. 1 and 2 is for an oil whose UOP characterization factor is 11.7. UOP characterization factors of crude oils can be determined from Ref. 10 if the viscosity and APT gravity of the oil are known. Fig. 3 gives the solubility correction factor for oils whose UOP characterization factors differ from 11.7. The solubility correlation in Figs. 1, 2 and 3 predicted

Jan 1, 1966

By J. L. Walter, W. R. Hibbard

A GREAT deal of work has been done on the rolling of single crystals of iron. Barrett and evensoon studied end orientations of heavily cold-rolled iron crystals and found that some crystals maintained a sharp single orientation during rolling. Others rotated into two or more orientations, and some fragmented and approached the entire polycrystalline texture depending on the original orientation of both the normal and rolling directions. Barrett, Ansel, and Mehl2 studied iron-silicon alloys and found that the addition of silicon to the iron had little effect on heavily rolled polycrystalline material. Dunn3 has extensively studied the cold-rolling and recrystallization of silicon-iron single crystals. Dunn found that for single crystals having initial orientation between (110) [001] and (111) [112], the principalcomponent of the cold-rolled texture is (111) [112]. Koh and Dunn4 studied the cold-rolled textures of single crystals having initial orientations in the range (001) [110] to (111) [IT01 and found that these are stable end orientations. They also found that all orientations having a [110] direction parallel to the transverse direction rotate to either the (001) [110] or the (111) [112] stable end orientation except for orientations near (112) [11], which divide and produce a final texture consisting of (001) [110]and (111) [112] components. Crystals having a (111) <112>-type texture re-crystallized to a (120) [001] or (110) [001]-type texture. Crystals having orientations with a range of (001) to (335) in the rolling plane and [110] in the rolling direction recrystallized5 to a wide spread of the initial orientations resulting from a multiplicity of 30-deg rotations about several (110) poles. The present study was undertaken to relate other orientations of crystals of silicon-iron to their cold-rolling and recrystallization textures, so that one might rationalize polycrystalline recrystallization data on the basis of the known deformation texture and the behavior of single crystals in these orientations. PROCEDURE Samples were obtained from a cylindrical ingot of 3 pct silicon iron prepared as follows: Armco iron was melted with high-purity silicon flakes under an atmosphere of argon to minimize oxidation. The alloy was poured into a special mold to form an ingot which consisted partially of large columnar crystals. Plates were cut from the columnar portions of the ingot with the longitudinal direction parallel to the columnar axes and ground to 0.040 in. thick. The plates were heavily etched to a thickness of 0.032 in. to remove the cold-worked surface. Orientations of seventeen crystals were determined by Laue back-reflection techniques keeping the mean columnar axis as the reference direction. The plate was then cut in two, parallel to the columnar axis. One portion of the plate was rolled at room temperature parallel to the columnar axis to a reduction in thickness of 84 pct. The remaining portion of the plate was rolled also at room temperature across the columnar axis to a reduction of 66 pct, at which point the crystals began to separate at the boundaries. After rolling, nine individual crystals were removed from the strip by cutting along the crystal boundaries with a jeweler&apos;s saw. Fig. 1 shows the original orientations of the six crystals that were straight-rolled and of the three crystals (4, 7, and 8) that were cross-rolled. Each rolled crystal was carefully etched to approximately 0.002 in. thick. Textures of the cold-rolled crystals were determined by use of the diffractometer with a non-integrating sample holder. The pole figures were made for the (200) poles using molybdenum Ka radiation and were plotted by an automatic stereographic projection recorder.&apos; Spurious poles were determined by rerunning portions of the pole figures using strontium oxide to filter out the Ka radiation. The central portions of the pole figures have not been determined. The pole figures were completed to about 55 deg from the periphery at which point the sample holder interfered with passage of the beam. Following the determination of the cold-rolled

Jan 1, 1959

By R. B. G. Yeo

The effects of alloy additions on the M, and A, temperatures of an Fe-22.5 pct Ni alloy have been determined. Increasing amounts of titanium, colum-bium, vanadium, and silicon raise and then lower M,while raising A, cmtinuously. Cobalt raises both M, and A,. Aluminum has little effect on Ms but raises A,. Chromium md nickel lower M, and A,. It is proposed that elements raise M, in accordance with their effect on the Ae3 temperature of iron until the lattice becomes stiffened against the shear transformation so that M, is then lowered. An anomaly, first pointed out by Zener,1 arises in steels when the addition of elements, such as molybdenum and tungsten, which raise the Ae3 temperature, also lower the M, temperature.2&apos;3 During the development of a series of martensitic precipitation-hardening (maraging) steels, the effect of several elements on the transformation of austenite to martensite was studied. The results show that under suitable conditions several elements which raise Ae3 also raise the M, and A, temperatures. PREPARATION OF MATERIALS STUDIED A series of alloys was made in which cobalt, titanium, columbium, vanadium, silicon, aluminum, molybdenum, chromium, and nickel were added to an iron base containing 22.5 pct Ni. The compositions of the alloys prepared are given in Table I. The residual manganese contents of the heats were in the range of 0.030 to 0.35 pct, silicon 0.05 to 0.1 pct, carbon 0.0008 to 0.009 pct, and nitrogen from 0 to 0.004 uct. The allois were made as 50-lb induction heats starting with electro-iron and electro-nickel, melted in air to oxidize impurities. Additions of silico-manganese and ferro-silicon were made after which the power was turned off to allow the products of deoxidation to rise and be skimmed from the surface of the melt. The furnace chamber was pumped down to a pressure of 5 p and the charge was heated to 2900°F for the addition of other alloying elements. The heats were poured into five 10-lb ingots, making successive alloy additions to each. The ingots were soaked for 2 hr at 2300°F and hot-worked to 3/4-in.-diam bars. This stock was heated to 1500°F for 1

Jan 1, 1963

Membership at the end of the year 1951 was 19,711 including 2228 Student Associates. The data in the third column include these Student Associates. 1. This includes all the cash dues income received from new and old members of all grades. 2. All cash initiation fees received. 3. Net income received from advertising in the three journals. The figure was $72,273, for MINING ENGINEERING; $39,844 for the JOURNAL OF METALS; and $31,564 for the JOURNAL OF PETROLEUM TECHNOLOGY. Income in 1950 was $54,572, $30,390, and $18,443 from these sources, respectively. 4. Receipts from individual sales, nonmember subscriptions, and multiple subscriptions of members. 5. Includes Transactions volumes and the Petroleum Statistics volume. 6. Sales of all other printed matter except special volumes sponsored by certain Funds. Includes a considerable sale of preprints and reprints of technical papers. 7. Does not include dividends and interest from certain Funds whose income reverts to those Funds. 8. Miscellaneous income not included in any of the above categories. 9. The total income compares with $493,197 -in 1950, an increase of $29000.

Jan 1, 1952

By Jean-Jacques Prompsy, J. S. Rinehart

Some time ago a study was initiated at the Colorado School of Mines in an effort to arrive at a better understanding of the stress fields developed within drill bits under dynamic loading and the influence that these stress fields could have on the failure of the bits. Particular emphasis has been given to the influence that bit shape has on the establishment of highly localized, potentially destructive stress inhomogeneities within the bit. The study has been divided into three phases involving three velocity regimes: impacts at very low velocities, 0 to 20 ft/sec, a velocity range in which dynamic effects are just beginning to be found; impacts at velocities ranging from 20 to several hundred ft/sec, a range commonly encountered in practical drilling operations; and impulsive loading through the detonation of explosives, a region in which the dynamic effects are greatly exaggerated and made more identifiable. The ultimate objective is to provide basic data which will enable the mitigation through judicious design of the frequency and severity of these transient concentrations of intense stress, thereby prolonging and increasing drill efficiency. This paper presents results of the third phase of this study — the development of a better understanding of the dynamics and mechanics of failures caused by transient stress-wave interactions. The impulsive loading or transient waves in these experiments were generated by detonating small explosive charges placed on the ends of Plexiglas cylindrical rods terminating in truncated cones. Under such intense loading, dynamic effects are greatly exaggerated and, hence, made more identifiable. The explosion generates a high-intensity transient stress disturbance which moves through the rod, reflects from surfaces which lie in its path, and establishes momentarily narrow regions of high concentrations of stress where failure of fracture may occur. The peregrinations of these waves, their interactions and their effects have already been described in the literature (see, for example, Refs. 1 and 2). The locations and extent of the regions quite apparently are strongly dependent on specimen shape, making it possible through judicious shaping of specimens to relocate the highly stressed regions, minimize their extent, or eliminate them entirely. These experiments were designed, first, to identify more clearly the vulnerable regions in geometries relevant to drill-bit design and, then, to modify these regions in a predictable way by changing specimen shape. Through this latter process, it is anticipated that better bit design might evolve. The specimens used in the experiments were cylindrical rods, 1 1/2 and 1 1/8 in. in diameter, ended by a truncated cone, with the cone angles ranging from 45° to 130°. Upper cone face diameters were 1/2, 3/4, or 1 in. A small plastic-covered electric blasting cap detonated on the axis of the specimen produced the spherical shock wave. The detonators used were Olin Mathieson No. 6, which induced into the rod a transient saw-toothed stress disturbance of about 3-microseconds duration, corresponding to a wave length of 0.3 in. in the Plexiglas. Five distinct systems of fracture were observed: (1) along the axis of the rod, a lower system of fractures, the cracks focusing around one point for specimens having cone angles of 80° and 90° and, as the cone angle was increased, spreading downward; (2) just above these fractures, an upper system of fractures composed of horizontal cracks observable in some specimens but not of any appreciable extent; (3) a third system of axial cracks still above the latter, observable in the small cone-angle specimens; (4) in the upper part of the specimen, a system of radial fractures extending from the blasting point; and (5) circular spalling due to reflection of the wave on the boundary of the cylinder. Only the first three systems, the axial fractures, are examined here. LOWER TENSILE FRACTURE SYSTEM The first, lower system of tensile fractures, shown in the photograph of Fig. 1, was observed in almost all of the specimens. It was due to the reflected tensile wave coming in from the boundary of the cylinder as shown in Fig. 2. The reflected wave was cylindrically convergent and focused

By John Wulff, J. H. Hollomon

THE opinion has been widely held that the corrosion of alpha brass occurs by the selective solution of zinc. As late as 1939, Fink1 and Evans2 suggested that in the initial stage of the corrosion the selective solution of zinc produces copper-rich areas, which subsequently act as cathodes that facilitate the deposition of copper. Previously Abrams3 had shown that most of the copper found on corroded brass was redeposited and not residual, although he did not consider the nature of the initiation of the corrosion process. Enough data exist to indicate that any metal surface is sufliciently heterogeneous to provide the anodes and cathodes necessary for the initiation of corrosion .4,5 Thus, for alpha brass we need postulate not an initial selective solution of zinc, but only the existence of local differences in electrochemical potential. The heterogeneity responsible for potential differences may arise from oxide and other films as well as from alloy concentration gradients. Even though selective corrosion may be possible in some alloy systems, previous data on alpha brass as well as the experimental work reported in this paper do not require this supposition. Bengough and May,6 in a discussion of Abrams&apos; paper, first suggested the addition of small amounts of arsenic (0.03 per cent) to alpha brass to prevent the redeposition of copper (dezincification). This suggestion was later substantiated by Nixon.7 In their studies of the inhibiting influence of arsenic, Evans and Fink were led to the selective-solution hypothesis in order to explain the initial corrosion of such alloys. "I hey believed that an arsenic film covered anode areas and prevented the formation of copper-rich spots capable of acting as cathodes for the deposition of copper. They (lid not consider, however, the mechanism by which the arsenical film was formed. Bengough and May,8 in another publication, suggested that the commonly found gray or black arsenical film may act to: (1) carry oxygen to the brass surface, (2) increase the discharge potential of copper on brass, (3) precipitate cuprous chloride from colloidal suspension in chloride solutions. Masing9 assumed that the film found upon arsenical brass was metallic arsenic. His measurements of hydrogen overvoltage of bulk arsenic led hint to believe that the inhibition of dezincification occurs because the overvoltage of a brass surface is lowered by the arsenic film. He reasoned that this film would permit the more rapid reduction of hydrogen at the cathode, which would prevent the redeposition of copper. In a recent paper,10 we have pointed out that the film formed (luring the corrosion of arsenical brass and copper in stagnant solutions is essentially arsenious oxide (AS208)

Jan 1, 1942

By F. P. Bullen

Empirical relationships between fracture stress, orientation angle, and diameter of crystal have been determined at 77°K. Orientation ranges of markedly different behavior were found—a law of constant normal stress&apos; of value a (diameter)-1/2 for the fracture of ductile crystals, and a condition of shear stress (or strain) for more brittle crystals. The observations are not consistent with current theories. An interpretation is advanced which is also applicable to observations on the effect of prestrain at room temperature on the subsequent fracture stress at 77°K and to the effect of cyclic stressing on the cleavage strength.&apos;&apos; The law of constunt normal stress&apos; and the brittle ductile transition are also explained. The interpretation is more consistent with the initiation of cracks by intersecting dislocations than with theories based on stress -concentration by dislocation arrays. ZINC single crystals are particularly suited to the study of cleavage because fracture occurs on the basal plane over a wide range of crystal orientations. Analysis of the conditions of stress and strain at fracture in crystals of different orientations should indicate which parameters control the cleavage process. Unfortunately, controversy has arisen over the correct empirical relationship between tensile fracture stress and orientation. Schmid&apos;s observations1,2 favored a &apos;law of constant normal stress&apos;, as observed in other materials.2 For zinc, however, the observed values are far below the theoretical strength and cannot represent the true limit of cohesion between neighboring atomic planes. Hence, the interpretation of such a &apos;law&apos; is not straightforward. Deruyttere and Greenough3,4 found a complex variation between tensile fracture stress and orientation; this variation did not agree with a &apos;law of constant normal stress&apos;. Two theories have been advanced to account for their observations: a) the propagation of cracks from low-angle boundaries,5 and b) the release of energy from piled-up dislocations during crack-propagation.4 The present work resolves the apparent discrepancy between the observations and shows that neither of the above theories are applicable to the tensile fracture of zinc single crystals. A phenomenological explanation, along the lines suggested by Gilman,&apos; is advanced and successfully applied to previously unexplained effects. EXPERIMENTAL DETAILS &apos;Crown Special&apos; redistilled zinc was used, except for one comparison series op tests using &apos;Tadanac&apos; electrolytic zinc. Crystals of 1 mm diam, subsequently called &apos;1 mm crystals&apos;, were grown from the melt in vacuo in precision-bore Pyrex tubes internally coated with graphite. Several specimens 1 in. long were cut from each crystal and chemically polished. Jigs were used to minimize handling strains, and crystals were mounted in the Polanyi machine the day prior to testing to allow recovery from any such strains. One-mm crystals were chemically polished for long periods to obtain 0.1 mm (approx) crystals. One-mm crystals were cemented into miniature gimbals by &apos;Araldite&apos; casting resin. The Appendix gives the reasons for using gimbals and the results obtained by other methods. More complete details of all techniques are given elsewhere.7 The symbols and terminology used are as follows: X = orientation angle (angle between tensile axis and line of greatest slope in the basal plane). T = tensile stress (on true cross-section) S,N = shear and normal stress (components of T with respect to the basal plane) ? = shear strain D = crystal diameter. The subscript &apos;f&apos; will be used to denote values at fracture. PART I-ANNEALED CRYSTALS EXPERIMENTAL OBSERVATIONS One-mm crystals were used to establish the variation of fracture stress at 77°K with orientation at fracture (Xf), Fig. 1. For 18 deg = Xf = 55 deg, a &apos;law of constant normal stress&apos; was observed. For Xf > 55 deg, the fracture condition approximated to a constant shear stress. At Xf< 18 deg, twinning occurred before fracture so that the results were not typical of homogeneous single crystals,4,8— such specimens will not be considered herein. The dependences of fracture stress upon Xf were of similar type for 6 mm,* 1 mm, and 0.1 mm crystals,

Jan 1, 1963

By R. J. Borg, C. E. Birchenall

The self-diffusion coefficients for a iron have been deternzined between 980° and 1167° K using Fe55 as the tracer. With decreasing temperature the diffusivity was found to decrease more rapidly than predicted by the Arrhenius equation in the region of the Curie temperature. The diffusion coefficients obtained well above the temperature of the magnetic transformation are more precise ard differ substantially from all the previously reported values. In the temperature region beginning at least 50" above T,, the diffusion coefficient is given by D = 118 (±2) exp 1 HE self-diffusion coefficients for a iron have been reported previously as the result of four independent investigations The general lack of agreement and the poor precision of most of the previous work prompted the redetermination by the present authors. The possible effect of the onset of ferromagnetism upon the diffusivity5 provided an additional impetus for this investigation. The earlier measurements of Birchenall and Mehl1 gave low values for the diffusion coefficient at temperatures below the Curie temperature, Tc. However, the precision of these measurements is not sufficient to establish an indisputable correlation between the low values and the magnetic transformation. The results of this investigation along with all the previous ones are shown in Fig. 1. EXPERIMENTAL Small rectangular samples, approximately 1 by 0.5 by 0.3 cm, of high-purity iron (Vacuum Metals Corp., "Ferrovac") are first heated in hydrogen at 900°C for24hr in order to remove possible trace amounts of dissolved carbon and oxygen. The small

Jan 1, 1961

By Byron Bird

WHILE Mr. Fahrenwald has been working on the fundamentals of ore-dressing, in Idaho, the Northwest Experiment Station of the U. S. Bureau of Mines, in cooperation with the University of Washington, has been studying the corresponding fundamentals for the closely-allied subject of coal-washing. In this work many of the principles outlined in Mr. Fahrenwald&apos;s paper have been touched on, one important exception being that phase of his studies where conditions were approximated between those existing on a table and those existing in a hindered-settling classifier. During the past three years this work has been given over almost exclusively to a study of coal-tabling to devise better methods of cleaning fine sizes of coal, particularly the coals of the Northwest, which are very difficult to wash. One important result of this study thus far has been the development of a satisfactory hindered-settling coal classifier, now in use in several commercial plants. Recently table stratifica-tion has been the subject for study. This latter phase of the work with coal,. as well as the earlier portion dealing with hindered-settling classification, has in a measure paralleled Mr. Fahrenwald&apos;s work with ore. Without going into details about the results of the coal experiments, I shall merely say that, from a quali-tative standpoint, they are, in general, concordant with Mr. Fahrenwald&apos;s, but that from a quantitative stand-point the results, particularly those with, table strati-fication, are somewhat different. These differences may disappear as the work progresses-Mr. Fahrenwald is further ahead with his experiments than we are at the Northwest Station-but if not, the disparity would not be surprising, and indeed would be what one might reasonably expect when investigators work on two very dissimilar materials and use different apparatus and methods of study. However, this- mention of our coal-washing experiments is made only in passing. A principle of general application that may be estab-lished from Mr. Fahrenwald&apos;s paper is that different types of stratification should be used in successive&apos; gravity-concentration processes to. obtain best results.

Jan 3, 1927

By W. C. Hagel

Previous inuestigators have repovted unusually low H* and Do values for self-dzf@szon in certazn bcc metals, e.g., chromium nnd y -uvanium. It has been postulated that this is nn experimental crl -tetion for the existpnce of a four -atom ring meclzanzsm, mid there could be. zmpovtant theoretrcal Implicatlons. By utilizing a precise sectioning technique with Cr51 as the tracer, self-dzffi-lsion measurements in large grains of 99.99-pct Cr were extended from 1200° fo 1600"C. A least- squares analysis of the data yields that D 0.280 exp (-73,20U/RT) cm2 sec-&apos;. These AH* and Do unlues are not anomalous; there is little reason to believe that n vacancy mechanism is not opevatiue. Apparent differences at lower temperatures may result from preferential diffusion along short-circuititing paths and/or sample contamination. WITH continued technological effort, chromium and chromium-base alloys should ultimately become useful high-temperature structural materials. Accurate measurements of self-diffusion coefficients in the pure metal are necessary for a quantitative understanding of sintering, grain growth, creep, and other related rate processes. However, two conflicting determinations have been reported.* Using an Since careful diffusion studies normally yield Do values ranging from 0.1 to 10 cm2 sec-l, the Paxton-Gondolf results require independent experimental corroboration before an undue amount of speculation arises to explain the apparent anomaly. As discussed by Nowick6 and clearly shown by Hoffman and Turn-bull7 for self-diffusion in silver, a low AH* and Do can arise from preferential diffusion along grain boundaries or other short-circuiting paths. The most reliable data come from high-temperature measurements where volume effects predominate. Following a precise sectioning technique developed for determining silver diffusion in the intermetallic compound AgMg8 and cation diffusion in the corundum oxide Cr2O3,9 the purpose of this study was to measure true volume diffusion in high-purity, large-grain samples at higher temperatures than considered previously. Another point of interest is the frequent proposal10-12 that chromium undergoes an allotropic transformation between 1375" and 1800°C where the diffusion data might then show a discontinuity. I EXPERIMENTAL 1) Sample Preparation. The highest purity (99.997 pet) Cr currently available is produced by reduction of chromium tri-iodide. Three pounds of the resulting crystal bar were shipped in a sealed container with a complete chemical analysis from the vendor.* In conformity with the procedure used for

Jan 1, 1962

By E. B. Thornhill

Discussion of the paper of E. B. THORNHILL, presented at the San Francisco meeting, September, 1915, and printed in Bulletin No. 104, August, 1915, pp. 1653 to 1670. D. B. HUNTLEY, Oakland, Cal.-About 15 years ago it chanced to be my lot to cyanide some mill tailings, assaying about $5 per toll in gold and, a few cents in silver. It was in southern Idaho, a. desert region where costs are nearly as large as in central Nevada. We knew that we had a lot of tailings that had been amalgamated and contained about 1 lb. of quicksilver per ton. We knew that we would dissolve some of the quicksilver when we cyanided them with say 0.25 per cent. cyanide solution. We figured (optimistically) that the cyanide would dissolve all of the quicksilver, and we thought to capture all of that, 1 lb. per ton; and we figured out profits as partly gold, partly silver, and partly quicksilver from the recovery in working those tailings. Actually, however, we did this: We had a battery of three large, old-fashioned silver-mill retorts. We retorted our zinc-dust precipitate, recovering about ¼ lb. of quicksilver per ton treated. That was only a loss of 75 per cent. of what we originally had, but still it was profitable by virtue of the conditions. I mention it partly to call attention to the crude old way of doing it, and partly to call attention to how chemical methods for recovering quicksilver have developed in the last 15 years.

Jan 12, 1915

THE RELATION OF THE ENGINEER TO RECONSTRUCTION FIFTY-THIRD MEETING OF BOSTON SECTION The fifty-third meeting of the. Boston Section was held April 28. The speaker of the evening was the new president of the Institute, Mr. Howard V. Winchell, who spoke on "The Relation of the Engineer to Reconstruction." He told of the part engineers had played in the war and paid tribute to Herbert E. Hoover as an example of what engineers can do. He said that engineers are not taking enough interest in politics, although it is badly needed as shown by the evidences of Bolshevism even in America. Conditions have suddenly changed; whereas we formerly borrowed money we are now loaning widely to foreign countries and our investments, abroad have to be protected. A committee is badly needed to investigate and determine the actual conditions. The Government has already been invited to cooperate with the Institute along professional lines and this should lead to closer contact between our Society and the Government. Mr. Winchell then went on to describe some of the mining conditions in Russia. He brought out the point that the rich platinum deposits are exhausted and only the poorer sands remain. The largest copper properties average less than 2 per cent. copper and there are some 4,000,000 tons available in .the Caucasus region near Batum. There are approximately 100,000,000 tons of high-grade manganese ore scattered in small deposits in the eastern Ukraine. There are some copper mines in the East, butt they are almost exhausted. The Baku oil field is the second largest in the world and there is probably oil in Persia. There are also manganese in Siberia and coal veins of enormous thickness.

Jan 7, 1919

COMMITTEES Committee on Arrangements DAVID H. BROWNE, Chairman BRADLEY STOUGHTON, Vice-Chairman LAWRENCE ADDICKS BURR A. ROBINSON PERCY E. BARBOUR E. MALTBY SHIPP GEORGE D. BARRON JOSEPH STRUTHERS J. V. N.. DORR E. B. STURGIS J. R.. FINLAY T. T. READ Louis D. HUNTOON R. H. VAIL

Jan 4, 1916

By Mary Barrett, Walter Rose

INTRODUCTION The conventional way to program reservoir problems* for solution on the electric analyzer1 is one which concentrates the block units towards the inner radius of the prototype system being represented by the analog model. This is achieved by the device of considering block units of equal value radial resistance, leading to the consequences: (1) the ratio of the external to the internal radius of each block unit is a constant (i.e. r1/ri-l = constant a); (2) the external radius of the nth block unit is equal to the innermost radius of the system times the constant a raised to the nth power: (3) the capacitance of the block units increase by a factor of a2 going out radially from the innermost to the outermost boundaries of the system; (4) given n block units in the radial direction, the capacitance ratio of the outermost to the innermost block unit is a (2n-2); and (5) the vertical resistance of the block units decrease by a factor of a going out radially from the innermost to the outermost boundaries of the system, such that the ratio of the maximum to minimum vertical resistance is also given by the factor a(2n-2) PRESENT PROGRAMMING METHOD While this conventional way of programming problems is quite adequate for routine uses of the electric analyzer, it leads to difficulties in those cases where the inner radius of the prototype system (e.g., the well-bore) is small compared to the external radius (e.g.. the external reservoir boundary). To handle such a case by the conventional method would require either that a large value be selected for the constant a or that a large number n, of radial block units be chosen. In consequence, the capacitance and vertical resistance ratios become impossibly large, as will be evident from the relations given above. In any event, the size of the smallest and largest capacitors will always be limited by the size of commercially available components, and the analyzer itself will determine how many mesh points are available for radial block units. For example, it can be shown that if the maximum capacitance ratio which can be electrically handled is a factor of l04, the maximum external radius of the system which can be considered (assuming an internal wellbore radius of 0.25 ft is: It is thus seen that in direct consequence of having the inner wellbore radius small compared to the external radius, models extending beyond 30 to 40 ft are not possible when the capacitance ratio is limited to l04. (NB. A value of 10-9 farads can perhaps be taken as the minimum electrical capacitance possible if corrections for the capacitance of the lead wires are to be avoided. Values greater than 10-5 farads would require the use of unstable and inaccurate electrolytic capacitors). On the other hand, models extending out to 500 to 5,000 ft may be desired in single-well problems, and hence the need for a revised method of problem programming. * REVISED PROGRAMMING METHOD The revised method of programming is one which attempts to retain the desirable features of the conventional method (viz. concentration of block units towards the inner boundary, simplicity in computation, etc.) without having as a consequence that impossible capacitance and vertical resistance ratios will be required. Other advantages will also be achieved by the revised

Jan 1, 1957

By J. J. K. Daemen, C. Fairhurst

Introduction The stress field around a supported tunnel can be considered as being composed of: i) the virgin (pre-mining) stress in the rock ii) the (elastic) change in this stress field caused by creating the opening iii) the (time-dependent ) change in the stress field produced by (i) and (ii) as a section of the rock breaks up iv) the (time-dependent) influence of the stress build-up in the support. Several authors have examined the conditions necessary to produce static equilibrium between the support, the rock, and the regional (in-situ) stress field. The analysis used by Labasse (1) is typical. Consider a circular tunnel radius R in a hydrostatic stress field (P), and a radial pressure pi exerted by the support. According to Labasse, the radius ‘b’ to which the rock will break* for a given support pressure, pi, can be calculated from: - the equilibrium equation: [ ] As a zone of broken rock develops around the opening, the stress circle for a point on the elastic-broken rock boundary moves to the right in the Mohr diagram until the radial stress in the broken zone s equal to the radial stress in the elastic zone.

Jan 1, 1971