Search Documents

By V. I. Lakshmanan, R. Roy

"TiO2 is used in paints, plastics, rubber, paper, inks, textiles and other miscellaneous applications. The demand for the pigment grade Ti02 is growing at 3.0%/year on average and this invites the development of innovative and cost effective processes. The current processes are not designed to recycle the reagents and thereby discharge the effluents into the environment, causing an environmental concern.During this study, synthesis of TiO2 from an ilmenite concentrate was investigated using an innovative atmospheric mixed-chloride leach process. The solution purification was carried out using solvent extraction in two stages. In the first stage iron removal was carried out and in the second stage titanium was extracted. The strip solution obtained from the second stage solvent extraction contained the purified titanium and from this stream pigment grade Ti02 was recovered. The barren solution was used for reagent recovery and the regenerated leach liquor was recycled."

Jan 1, 2011

By Luben Xie, Lin Hu, Qiang Wang, Min Gan, Tao Jiang, Wenqi Li, Yi Wang, Xiaohui Fan

"The mineralization behaviors of typical fluxes are studied by investigating the microstructures with optical microscope. The results show that the reactions begin with between iron ore and lime, limestone with small particle to form primary liquid. Then coarse limestone, dolomite and serpentine take part in reaction under the action of primary liquid. Limestone is the easiest to mineralization, next dolomite, and the last is serpentine. The higher basicity and smaller fluxes size favor the mineralization process of dolomite and serpentine.IntroductionThe purposes of adding fluxes into sintering are that:(1) to increase the basicity of sinter, so as to reduce even eliminate addition fluxes into BF(blast furnace) and decrease the coke ratio of BF[1,2]. (2) to decrease the melting point of sintering mixture to ensure sintering can be carried out at a lower temperature and reduce the energy consumption. (3) to improve the qualities of sinter by forming binding phase with iron ore fines [3].Flux is another significant component for sinter besides iron ore, especially for high basicity sinter[4]. The proportion of flux is usually higher than 10% in sinter mixture(excluding return mine).There were many reports about the influence of the flux types on sintering, such as limestone, dolomite, lime and so on[5-7]. It is very important to choose suitable fluxes for iron ore sintering. Although the effect of flux size on sintering also has been researched, the mineralization behaviors of the fluxes in the sintering process has not been illuminated. The paper will study the mineralization behavior of fluxes in sintering."

Jan 1, 2011

By David Hughes

The paper covers the utilization of on-line analysis in process control of solvent extraction in nickel leach solvent extraction processes in Finland and Australia and in copper heap-leach and solvent extraction in Chile. The goals of and requirements for controlling the solvent extraction stages of the processes are reviewed. The applications at three plants are compared. The development of the technology used is reviewed and design considerations are discussed. Requirements for on-line control and analyzer performance are compared. A new generation of analyzers and its effect on the set-up process of a project is introduced.

Jan 1, 2003

By Juan H. Rojas C.

The Chuquicamata mining and metallurgical complex is the main Division belonging to Corporation Nacional del Cobre de Chile (CODELCO-CHILE) and it accounts for 50% of the 1.4 Mt of fine copper output of the Corporation. It has been producing copper since 1915. The paper refers to the challenges that Chuquicamata has to solve in the near future. These challenges are: the increasing operation costs associated to a 800 m depth pit with low prices in an overstocked copper market; the increasing people's sensitivity to environmental preservation; and, the transformation needed for achieving high levels of organizational effectiveness. According to Corporate policy, Chuquicamata is making efforts to switch from a management style focused on supply to a management style focused on demand side of the industry. In this direction is tempting to establish strategic alliances to develop both new copper products and uses, to rise the metal demand. In more than 80 years of operation, Chuquicamata had exploited just one third of its geological resources. The exploitation of the remaining two third is a huge engineering challenge, taking into account the depth of the deposit, the impurities content, the decreasing ore grades and the transportation distances for waste dumping. All those factors are relevant in the economical process of transforming geological resources into ore reserves. Chuquicamata has other limitations. First, a 20,000 people town just aside the pit that limits the mining rates because of dust generation; second the scarceness of water in the desert area where Chuquicamata deposit is located; and, finally, the new tailing pond is a problem which solution will demand huge engineering efforts and investments. People are the principal factor associated to a company success. In this field, Chuquicamata have been progressing, but much more efforts from people will be necessary to reduce production costs for being successful as any other price-taker within the copper industry. Chuquicamata must develop the skills of its Supervisors to transform them into leaders and entrepreneurs, who additionally have the challenge of passing on their knowledge to non-professional workers. It is an ethic commitment to assure personal and professional growth of workers, as the only sustainable way to get real and integral success.

Jan 1, 1999

By T. T. Chen

Secondary copper anodes are generally rich in Sn, Pb, Ni and Sb, but are notably deficient in Se, Te and Ag. In the secondary copper anodes, most of the Ni, virtually all of the Ag, slightly more than one-fifth of the Pb, about one-third of the As and Sb, and approximately one-tenth of the Sn are in solid solution in the copper. The remaining impurity contents occur as 1-5 µm grain-boundary inclusions in the anodes, and these are mainly Cu2O, SnO2, Cu-Pb-As-Sb-Bi oxide, Pb-Sb oxide, Sn-Ni-Zn oxide, Cu-Sn-Ni oxide, Cu-Sb-Ni oxide (Kupferglimmer) and trace Cu2(Se,Te). Barium sulphate, which originates from the mold wash used in casting, is also present in the anodes. During electrorefining, the BaSO4, SnO2, Pb-Sb oxide, Sn-Ni-Zn oxide, Cu-Sn-Ni oxide and Cu- Sb-Ni oxide inclusions are liberated and accumulate in the slimes layer. Solid solution Ni dissolves and the Ni accumulates in the electrolyte. Solid solution Sn and Pb dissolve, but partly reprecipitate as Sn arsenate and PbSO4, respectively. Solid solution Ag dissolves but rapidly reacts to form Ag2(Se,Te), Ag powder, Ag-bearing Cu2O, (Cu,Ag)SO4 or a complex oxidate phase. Partial dissolution of the Cu-Pb-As-Sb-Bi oxide particles takes place; the Pb component is converted to PbSO4, whereas Cu, As, Sb and Bi dissolve. The reacted particles retain the morphology of the original Cu-Pb-As- Sb-Bi oxide phase. Some of the solubilized As, Sb and Bi remains in solution, but much reprecipitates as SbAsO4, As-Sb-Bi oxide, and as a poorly defined oxidate phase which consists mostly of Cu-Ag-Pb arsenate-sulphate. The high Sn contents of secondary copper anodes do not seem to affect the behaviour of the anodes during electrorefining.

Jan 1, 1999

By A. A. Hejja

"Liquidus temperature and electrical conductivity data measured on synthetic slags were modelled by the use of neural nets (NN). In this work the applied multilayer feedforward NNs were trained by a conjugate-gradient optimisation for which a three layer formulation was used. Very good fits were obtained for both the liquidus temperature and the conductivity data. The synthetic slags were prepared from pure oxides to represent a wide range of compositions likely to be encountered in ferromanganese and silicomanganese smelting. The slag constituents were in the following range: Mn0;5-30%, Ca0;20-35%, Mg0;5-15%, Si02;27-58%, Al20 3;5%. Liquidus temperatures varied from 1300° to 1380° and increased with increasing basicity ratio. The electrical resistivity of slags decreased with the increase of basicity ratio from 0.55 to 1.1 but above 1.1 basicity ratio the resistivity tended to increase depending upon the MnO content.Neural NetsVarious neural net (NN) topologies such as Hopfied nets, Hamming nets, Carpenter/Grossberg classifiers have been discussed in some detail by Lipmann (1). In this work, the applied multilayer feedforward NNs are not trained by backpropagation (BP) using the generalized delta rule (2) (GDR), but by a conjugate-gradient optimisation [3,4] - a procedure similar to that proposed by Barnard and Cole [5]. A neural net is capable ·of learning the non-linear functional relationship existing between a set of inputs and outputs [ 6]. In this capacity a neural net is used to determine the functional relationship that exists . between N dependent and independent variables, which characterize the system under consideration For a three layer neural net [1] the following function may be formulated, which relates X; inputs to the output Y 0 from node o:"

Jan 1, 1997

By N. M. S. Balbinot, A. L. Rodríguez, C. M. Mahlmann, R. de C. de S. Schneider

The use of sunflower oil co-products it was studied for production thermoplastic composites. Thermoplastic composites have been processed in polyethylene matrices of virgin linear low density polyethylene (LLDP) or recycled. Samples have been formulated with 10% mass fraction of sunflower bran, seed coat and mixture of bran and seed coat. The material characterization has been achieved by mechanical tensile test and Shore D hardness and by density physical testing. The results have demonstrated better properties to thermoplastic composites with sunflower seed coat.

Jan 1, 2008

By Francis Vanbellen

Umicore Precious Metals Refining operates an integrated precious metals smelting and refining plant in Hoboken, Belgium. Once a smelter and refiner of complex concentrates, the plant today?s feed consists exclusively of industrial and consumer recycled products, making it the world?s largest recycling facility for precious metals. Unlike the fairy tale of the Frog Prince, it took much more than a princess? kiss to successfully realize this makeover. A completely renewed plant has been built over the past decade. The most visible technological innovation was the commissioning of the Pb-Cu smelter. Its flexibility towards very different types of feed makes it perfectly suited as main entry to the Hoboken flow sheet. A new Cu-leaching & electro winning plant and precious metals refinery make up the Precious Metals Operations (PMO) whose targets are fast throughput and maximized yields for gold, silver and the platinum group metals. The Base Metals Operations (BMO), flexibly process the by-products from the PMO, valorizing ?impurities? like indium, tellurium, selenium and others. Off gas and waste water treatments ensure compliance with strict environmental standards. Precious metals recycling is an art that goes beyond mastering a unique flow sheet. Umicore Precious Metals Refining offers a complete recycling service, taking care of sampling and assaying, metals management and logistics. The quality of this integral service is recognized through the attribution of ISO certifications for our operational activities, sampling and the environmental care. And it?s an art that follows Michelangelo?s experience: ?Art is 5% of inspiration and 95% of transpiration.?

Jan 1, 2006

By Zhucheng Huang, Ronghai ZHONG, Tao Jiang, Jun ZOU

The method of reduction roasting and magnetic separation of low-grade, micro- fine disseminated refractory iron ore following granulation with coal produced unexpected success. Pellets of iron ore with diameter between 3 and 8mm were granulated with coal, bentonite and water. The raw pellets and reduction products were analyzed by scanning electron microscopy and x-ray diffraction. Results show uniformly distributed coal powders inside the pellets improved the kinetics of the reduction process and accelerated the reduction rate. Reduction time was higher at temperatures below 890℃, which resulted in the formation of substantial amounts of fayalite. When temperature was increased, micro- fine hematite was then quickly reduced to iron metal and the amount of fayalite decreased sharply. When pellets were reduced at 950℃ for 25min, reduction products with 56.73% metallization rate were obtained. After grinding and magnetic separation, a concentrate with 72.18% Fetot was obtained.

Jan 1, 2015

By Gunther Schimmel

Ag exudation in four different alloys (Ag-Cd, Ag-Sn, Ag-Sn-In and Ag-Zn) is characterized. The amount of exuded material is correlated with the volume increase due to oxide formation in dependence of the alloy concentration and different densities of the oxide and matrix phases. It is shown that all four alloys show similar amounts of volume increases, but different amounts of exuded material. It is concluded that internal stresses due to the volume increase cannot be the dominant driving force for Ag exudation. A gradient in the chemical potential of Ag that originates from the O concentration gradient inherent to internal oxidation is suggested as driving force. The exudation behavior is thus governed by the variation of the activity of Ag in the Ag fcc phase in the Ag-Me-O system that differs between the alloying systems.

Jan 1, 2010

By Yuanbo Zhang, Mingjun Rao, Guanghui Li, Chongzhong Ouyang, Shuhui Zhang

Oolitic hematite ore with high-phosphorus content is currently recognized as one of the most refractory iron ore resources in the world. The high-phosphorus content and unique structure of the oolitic hematite ore make it difficult to be beneficiated. The process of direct reduction followed by magnetic separation has significance to the utilization of oolitic hematite ore, and sodium salts can improve the dephosphorization. However, the behavior of phosphorus during reduction roasting, and the intensified dephosphorization mechanism of sodium salts are not clear. In this study, by using chemical analysis, chemical phase analysis, XRD analysis, optical microscopy, and scanning electron microscopy analyses, the behavior of phosphorus during reduction roasting of high-phosphorus content oolitic hematite ore and the effect of sodium salts on behavior of phosphorus were studied.

Jan 1, 2015

By Philip L. LeHoux

"Kennecott Barneys Canyon Mining Co. is a gold heap leaching facility that has been in operation since 1989. In 1994, a flotation plant was commissioned to remove sulphide minerals from refractory sulphide ore. Tailings from the plant are mixed with oxide heap leach material in order to produce a geotechnically stable agglomerate from which the gold is leached and recovered in a conventional heap leach cyanidation process. The experience to arrive at an effective blending methodology is discussed.IntroductionAgglomeration is the practice of binding fine particles to coarser rock or other fines in order to avoid the deleterious effects of mobilizing the fines during the course of heap leaching(l-Chamberlin). Agglomeration has been considered a key component of successful operation at many heap leach sites. If the ore is of sedimentary origin and crushed, there is a high likelihood that the resulting product will contain a significant quantity of fines and a skewed gradation, that i~, a disproportionate amount of coarse and fine particles, with few in the intermediate size range. The exact methodology for determining whether the practice of agglomeration will have to be integrated into the operating scheme has been well discussed. These conditions are primarily geotechnical and geochemical. This paper will deal with the specific experiences of Kennecott Barneys Canyon Mining Company in modifying the agglomeration practices to suit evolving operational requirements."

Jan 1, 1997

By Kenji Morinaga, Shigeru Fujino

"Preparation and vacuum ultraviolet (VUV) transmission spectra of aluminum fluoroberyllate glasses, MgF2-CaF2-SrF2-A1Fr BeF2 (MCSA-Be) and MgF2-CaF2-SrF2-AlFrYFrBeF2 (MCSAY-Be), were studied. The influence of YF3 and BeF2 on the thermal stabilization against crystallization and VUV transmittance was investigated. With increasing the BeF2 content, the crystallization tendency decreased and the absorption edge shifted to shorter wavelength in the MCSA-Be and MCSAY-Be glasses. The MCSA-20Be glass composition exhibited the shortest wavelength UV absorption edge (-147 nm) and the highest transmittance at 157 nm (60% for 2 mm sample thickness). The transmission values at 157 nm and the slope (steepness) of the absorption edge were found to be significantly influenced by the trace amount of Fe2+ derived from the BeF2 raw materials.IntroductionPure beryllium fluoride is known to be an only fluoride that forms one component glass on cooling from the molten state and is structurally similar to silica with [SiO4]4- tetrahedra. Molten BeF2 is highly viscous with a viscosity of about 106 poise near its liquidus temperature at 550""C[l]. The addition of modifying fluorides such as LiF, NaF or KF to BeF2 substantially decreases the viscosity[2]. Glass forming region of binary fluoroberyllate glasses has been mainly reported by several authors [3]. LiFBeF2 binary system is structually analogy for Mg0-Si02 system from their phase diagram and ratio of ionic radius for each cation and anion, respectively. LiF-BeF2 binary glasses seems to be promising candidates for the extreme deep vacuum ultraviolet (VUV) transmitting optical materials owing to their larger band gap. However, it is chemically unstable, and so, have no practical application for lens systems in micro lithography equipments and substrate materials for F2 (157nm) excimer laser[4]. There are also few reports on the VUV transparency of multicomponent aluminium fluoroberyllate glasses from the view point of their compositional dependencies. The purpose of this paper is to prepare deep VUV transmitting optical materials and determine the optimum glass compositions for aluminium fluoroberyllate glasses investigating their thermal stabilization against crystallization."

Jan 1, 2000

By L. L. Sutter

Fly ash is a by-product produced from the combustion of most hels including municipal solid waste. Currently, most combustion residuals are disposed of in landfills at a continually increasing cost and with questionable impact on the environment. Due to the presence of heavy metal compounds, municipal waste combustor (MWC) fly ash has the potential to leach these metals (e.g., lead and cadmium) above regulatory limits. The heterogeneous nature of MWC fly ash makes detailed characterization difficult. This research focuses on the identification of lead compounds in MWC fly ash. Samples obtained from the Olmsted Waste-to-Energy Facility in Rochester, Minnesota were examined in this study. The fly ash was fractionated into six size ranges and prepared as geological thin sections for analysis. The worked discussed in this paper involves using an electron microprobe analyzer to determine phase composition in MWC fly ash. In addition, backscattered electron imaging, digital image processing, and mineral liberation analysis software were used to determine phase distributions and phase associations as a function of particle size. Several lead containing compounds in several forms are identified. The results of this study show that lead can be identified in small sectioned particles which would not be apparent using normal backscattered electron imaging.

Jan 1, 1994

By Thomas J. Keefe, O&apos

The effects of cobalt, B-naphthol, glue and antimony on the polarization behavior of zinc sulfate electrolyte were investigated. It was found that B-naphthol was beneficial in reducing the detrimental effects of cobalt while antimony and excess glue were each harmful. Since the nu cl eat ion over potential was insensiti1ve to coba1t, other regions of the polarization curve were used to indicate electrolyte balance. The low? current density area occurring in the reverse or anodic sweep direction was? often an indicator when an ?unstable condition existed. The two parameters evaluated were the degree of inflection in the polarization curve in the low current density region during scanning and the rate of current rise observed when the sample was potentiostated at -0.781 Volts (SHE). Using this technique, a two-additive system was shown to be desirable to control cobalt and antimony containing electrolytes. The structure of the deposits was examined using scanning electron microscope techniques.

Jan 1, 1985

By M. O. Lai

"Metal matrix composite (MMC) with composition of Al-4.Swt.%Cu reinforced by IOwt.%TiB2 or ISwt.%SiC particulate has been successfully fabricated using powder metallurgy technique. Disk, compression and beam specimens were prepared with (a) layered structure containing ductile Al-4.Swt.%Cu with brittle Al-4.Swt.%Cu/TiB2 or Al-4.Swt.%Cu/SiC layers, and (b) homogenous constituent with composition of Al-4.Swt.%Cu/lOwt.%TiB2' The specimens for the fracture toughness measurement were built through three ductile-brittle-ductile alternating layers. For the beam specimens, the layers were built through brittle-ductile-brittle sequence. The brittle layer consisted of Al-4.S%Cu with fixed amount of reinforcement. Fracture toughness testing revealed an increase for layered composites although the total amount of the reinforcement was the same for all disk specimens. The increase in fracture toughness is due to the existence of ductile layers which manifests a strong influence on delaying the occurrence of fracture. It acts as a barrier to resist the propagation of crack and hence increases the fracture toughness of the layered MMC specimens, Delamination in the beam specimens was observed to be due to shear stresses. Fracture surfaces of both disk, compress and beam specimens were characterized using the SEM. IntroductionMechanical and thermal properties can be achieved by the incorporation of refractory secondary phases to constrain the plastic flow of the matrix in a metal matrix composite (MMC). The size of the reinforcement particulate incorporated must be in the range larger than the dislocation cell size and strongly bonded to the matrix (I). Particulate reinforced metal matrix composites hence provide high modulus, improved wear resistance and strength (2-4). Because of the incorporation of refractory phases which are generally brittle, the major limitation in the mechanical properties of MMCs is their limited ductility in comparison to their base metals. Cracks normally initiate from the reinforcement and voids (4, 5). Due to the lack of ductility, cracks propagate rapidly with increase in load. As a result, the interactions between reinforcement particles and propagating cracks have recently been of great research interest (6). In addition, volume fraction of reinforcement and aging condition of the matrix significantly affect the mechanical behaviour of MMCs. In the case of AI-3.5%Cu reinforced with varying volume fractions of SiC particulate, it has been found that the probability of particle fracture increased with increasing volume fraction of reinforcement (7)."

Jan 1, 1996

By Yanhui Liu, Xuewei Lv, Chenguang Bai

A thermodynamic model for determining the surface tension of molten slag by considering the surface tension and molar volume of the pure oxide component, and their ionic radii was extended to the slag bearing high TiO2 (varying from 80 to 67%) at 1973 K. The iso-surface tension curves for the FeO-TiO2-Ti2O3 ternary system at 1973 K are almost parallel to the FeOTi2O3 line. TiO2 plays a role of surface-active solute, and its surface-active effect is attenuating with increasing the TiO2 content. The iso-surface tension curve shifts away from the TiO2 corner, indicating that the surface tension of the ternary slag decreases along with the addition of SiO2. The reasons include the addition of SiO2 with lower surface tension and the decrease of the total ion moment at the surface. Both CaO and MgO can bring about that the iso-surface tension curve shifts towards the TiO2 corner, indicating that the surface tension of the ternary slag increases along with the addition of CaO or MgO. CaO has a more pronounced effect on increasing the surface tension of the ternary slag than MgO at an equimolar amount addition. The increase of the surface tension results from both the compositional change and the variation of the slag structure.

Jan 1, 2015

By Guan-zhou Qiu, Shui-shi Liu, Yu-feng Guo, Tao Jiang

"The preparation of high-quality synthetic ruitle from electric furnace titanium slag was systematically investigated by activation roasting followed by acid leaching process. The results showed that impurities such as Ca and Mg in titanium slag can be effectively removed and TiO2 grade of the product was markedly improved by the process. High-quality synthetic rutile containing 88.54% TiO2, 0.42% (CaO+MgO) was obtained under the conditions that roasted with 7.5%(wt) H3PO4 at 1000 oC for 2h, followed by two-stage leaching in boiling dilute sulfuric acid for 2h. Mechanism studies showed that anosovite solid solution and silicate minerals were reacted with phosphoric acid in the roasting process. As a result, titanium components in titanium slag turned into rutile (TiO2) and impurities were transformed into acid-soluble phosphate and quartz.IntroductionWith the gradual depletion of natural rutile and the rapid development of titanium industry in China, the natural rutile reserves cannot satisfy the requirement for production of titanium pigment and titanium sponge. Ilmenite is, therefore, becoming main raw material for titanium industry. However, because of its low TiO2 grade, it generally requires preconcentration to titanium-rich material such as titanium slag or synthetic rutile [1-3].Ilmenite resources are extremely rich in Pan-xi area of China, which account for 90.54% of total ilmenite reserves in China [4]. The titanium slag produced by electric smelting of ilmenite concentrate has high contents of Ca and Mg, and is not suitable as a raw material for chloride process and titanium sponge production. Therefore, upgrading titanium slag to prepare raw material suitable for chloride process and titanium sponge production has important significance for the development of China's titanium industry."

Jan 1, 2011

By C. H. Quan

Solvent extraction tests were carried out on a rare earth chloride solution derived from monazite processing to determine the effect of extractant and diluent on the distribution coefficients between organic and aqueous phases, and the separation factor between rare earths. The extractants were 20% by volume di-2-ethyl-hexyl phosphoric acid (DZEHPA) or 2-ethyl-hexyl phosphonic acid (Ionquest® 801). Four Shellsol diluents were tested ranging from nil to 100% aromatic content. D2EHPA gave the highest rare earth extraction for a given pH but was less selective than Ionquest. The geometric mean separation factor between adjacent rare earths varied from 2.41-2.56 for D2EHPA to 2.62-3.01 for Ionquest. The nil-aromatic diluents (Shellsol 2037 and 2358) gave better separation factors in Ionquest but, in D2EHPA, were slightly inferior to the 100% aromatic diluent Shellsol AB. Yttrium behaved as a pseudo-heavy rare earth with a distribution coefficient lying between Ho and Er, as expected from its ionic radius.

Jan 1, 1992

By L. I. C. Fernandez, E. B. Ferreira Filho, L. G. Pedroti, L. G. Justino, W. E. H. Fernandes, R. C. S. S. Alvarenga

More and more industries have been concerned with the disposal of the wastes generated in their production processes, once this generates a positive impact, both visual and economic enterprise, no more needing to have resources for transport and final disposal of wastes. In this context, and seen the importance of the Portland cement a sa building material, which aims the creation of an ecological cement from the mix of two wastes, the grits, which is a waste generated in pulp production, and the granite beneficiation waste. It proceeded initially with the chemical and physical descriptions of the wastes. Five mixtures, varying the percentages of the wastes and the preparation method of the raw materials, were prepared. After,the blends were sintered in a muffle furnace at 1300 °C for 15 min, forming new compounds that were compared with national cements, according to the Brazilian technical standards. It was concluded that the sintering of the product obtained satisfactory results, presenting good binder characteristics, however, some parameters were outside the limits for common Portland cements such as rapid setting time, large expandability and low compressive strength.

Mar 1, 2017