By James Johnston

Synopsis.-A description of the working of the mills of this company and the metallurgical practice in vogue, by which a remarkably. complex silver ore, averaging 54 oz. of silver per ton (run-of-mine ore), is treated to give a 95.66 per cent. extraction. The main features of the, processes are: The cyanide amalgamation of the high-grade ore. The cyanide treatment of the low-grade ore, after extremely fine grinding and close classification, in a caustic soda solution. The use of a wet desulphurizing process to break up refractory silver minerals. The substitution of aluminum dust for zinc dust as a precipitant. The recovery and shipment of over 13,000,000 oz. of silver in bullion at. 997 to 999 fine since this metallurgy was inaugurated, about 2.5 years ago. On the completion and successful operation of the mill to treat their . high-grade ore,1 the Nipissing Mining Co., under the general management of R. B. Watson, started a series of investigations of the possible treatment of the low-grade ore by the cyanide process, so that they would be in a position to market only silver bullion. These tests were run in July, 1911, on a large scale, by G. H. Clevenger, on an average mixture of Nipissing ore. The results obtained by a partial amalgamation followed by cyanide treatment gave an extraction varying from 90 to 93 per cent. and were sufficiently encouraging to warrant Charles Butters, the company's Consulting Metallurgist, in recommending that the new low-grade ore mill under contemplation should be a cyanide mill, instead of a concentrator. The cost of such a mill, capable of treating 200 tons per day, to obtain a 90 per cent. extraction at a working cost of $3 per ton of ore treated, was estimated at $250,000.

Jan 1, 1914

By JAMES QATLEY

THE atmosphere, which plays such an important part in the manufacture of iron and steel, is the most variable element involved in its several processes; and particularly is this true of the blast-furnace process, which consumes air in large quantities. At no time since the blast-furnace became an important and widely used apparatus-even when it was operated in the most crude manner-have the variations in composition of the raw materials used been as frequent and as great as the variations in humility of the atmosphere. Important, improvements have been made in the blast furnace and its accessories, such as the hot-blast stoves, the increase in size and change in the shape of the furnace, more efficient blowing engines, the increased protection given to the bosh walls, and the careful preparation of' the raw material, all of which have exerted a pronounced influence on the furnace-operations from a metallurgical standpoint. But during the past eight years little advance has been made in this direction; the fuel-consumption has not diminished, nor has there been any material increase in production. Within that period, however, there has been witnessed the greatest development in appliances for the economical handling of material. So complete has been the work in this direction, that, except in isolated cases, in this country at least., a further extension does not hold out much promise of a satisfactory return on the investment required. It seemed that, with the exception of the gas-engine, we had about reached the limit, for like a strong wall, the atmosphere, with its humility as variable to-clay as when first blown into a primitive blast-furnace, appeared to stand as a Barrier to

Jan 1, 1905

By I. Lowthian Bell

THERE has been probably no improvement introduced into the manufacture of iron which created more surprise in the minds of practical smelters and of scientific men than Neilson's discovery of the hot blast. In 1829, Messrs. Dunlop & Co. consumed at the Clyde Works, near Glasgow, nearly 79 tons of coal to make a ton of pig iron, of which about 20 cwts. was employed under the boilers of the blowing engines, leaving nearly 7 tons for the consumption of the furnace itself. In the year 1833, by heating the air to 612' F. (322' C.), they redoccd the 79 tons to 3 tons by the mere burning of 8 cwts. of coal in the apparatus for raising the blast to this temperature. The statenlent just given is strictly true in a commercial sense, but when we come to consider the question as one of physical science, it is necessary to eliminate some of the conditions which conduced to so extraordinary a result. Anterior to Neilson's time the fuel employed in smelting iron was coke, and it was supposed at that period, erroneously, however, that coal in its raw state, when burned with cold air, was totsally unfit for the purpose in question. This mineral, as it was obtained from the Lanarkshire coal-field, contained about 35 per cent. of volatile matter, but the process of charring it was performed in so unskilful a manner that instead of receiving 88 cwts. of coke from 135 cwts. of coal, 60 cwts. only was the product of the operation. Again, the reduced colisumption of carbon in the furnace itself was accompanied by a corresponding diminution of blast, and this was followed by an economy of half a ton in engine coal. After making a proper allowance, however, for all these collateral circumstances, we are within the mark when we admit that in actual coke, which is really the form the fuel has to assume before it is burnt in the blast-furnace, not less than 30 cwts. was saved by heating the blast to 615° F. (322° C.). This unexpected economy, be it remembered, was obtained by the combustion of the 8 cwts. of coal, somewhat wastefully applied in the hot-air apparatus. Numerous have been the opirlions advanced by different authorities in the scientific world to account for the apparent anomaly, bat none,

For more than 100 years, the Republic of Chile has been one of the leading copper-producing countries of the world. Between 1877 and 1880 Chile accounted for over 50 pet of total world copper production. Today it has the world's largest known reserves of copper ore and a capability of producing over 600,000 tons per year. This capacity can and will be increased as the world demand for copper grows steadily during the remaining years of this century. The Potrerillos mine of Andes Copper Mining Co., a subsidiary of The Anaconda Co., was developed in the rugged, high Cordilleras in the early 1920's, and the townsite, concentrator, leaching plants, smelter, railroad, power and port facilities were completed so that it came into full production in 1927. Since then and until the closing o f the mine in June of last year, 1,762,192 tons o f copper were produced.

Jan 4, 1960

By W. C. Phalen

SALT-MAKING PROCESSES THE production of salt in the United States divides itself at the outset into two distinct classes: (1) The mining of rock salt and its purification and separation into marketable sizes, and (2) the production of salt by evaporation from brines, bitterns, and other solutions. The processes employed at the present time in the manufacture of salt by evaporation may be outlined as follows: 1. Solar evaporation. 2. Direct-heat evaporation (a) in open kettles; (b) in open pans. 3. Steam evaporation, (a) in jacketed kettles, (b) in grainers. 4. Vacuum-pan evaporation. In this paper only the solar-evaporation processes practised in different parts of the United States will be described. SOLAR EVAPORATION Localities In the Eastern States the solar-evaporation process is not generally employed for climatic reasons. In the Western States, particularly in California and Utah, the great bulk of the salt produced originates in the solar-evaporation process. Of the Eastern States producing salt, this process, so far as the writer is aware, is employed in New York State only.

Jan 9, 1914

By J. L. Tokich, A. R. Troiano

INTRODUCTION SINCE 1921, when Hull' discovered that cobalt can exist in the face-centered cubic and hexagonal close-packed modifications, the transitions that occur in cobalt have been extensively studied. It is generally agreed that on heating the hexagonal lattice changes to the cubic structure at temperatures ranging from 400 to 500°C although considerable doubt exists as to the exact temperature. Data concerning the temperature of the transformation on cooling are much less concordant and their interpretation has not been satisfactory. The study is further complicated by the fact that many investigators have reported the existence of a high temperature allotropic change in the range 850 to 1020°C, at which the cubic lattice reverts to the hexagonal modification. The transition on cooling, which has been reported as occurring at various temperatures from approximately 400 to 100°C, is of particular interest. Troiano and Greninger2 have recently suggested and considered the possibility of allotropic transformations occurring in pure metals by a shear-type, diffusionless (martensite) transformation. The case of cobalt was specifically discussed and certain observations of previous investigators evaluated in terms of this type of transformation. Table 1 briefly outlines the methods and results of previous investigators of the transformation temperatures of cobalt. MATERIALS AND METHODS The major portion of this investigation was performed with cobalt sheet containing a total of 0.2 pct impurities with carbon present to the extent of 0.1 pct. After melting in an induction furnace under an atmosphere of hydrogen, the carbon content analyzed 0.03 pct. Some observations were repeated with hydrogen reduced cobalt compresses analyzing 99.9 pct pure. No significant variations in results were observed employing the as-received sheet, the remelted stock, or the cobalt compresses. Filings for X ray diffraction analysis were sealed in evacuated glass ampoules. Pyrex glass tubing was used for temperatures below 600°C and for higher temperatures clear fused quartz was satisfactory. After appropriate heat treatment at various temperatures, the specimen ampoules were furnace cooled, air cooled or quenched by crushing under distilled water. This allowed a range of cooling velocities from less than one degree C per sec to greater than 1,000°C per sec. X ray diffraction patterns were taken with a Debye camera and filtered characteristic cobalt K-alpha radiation. The proportion of the existing phases was roughly approximated by visual examina-

Jan 1, 1948

By Sidney Diamond, Charles Wert

The anelastic behavior of Ni-C alloys of nominal 0.5 wt pct C has been determined over a wide temperature range. The most prominent damping effect, that due to the presence of C-C pairs, was measured both above and below the Curie temperature. The effect on diffusion of the C-C pairs by magnetic spin ordering is deduced to be very small. The diffusion coefficient for C-C pairs in nickel is given by the expression ThE solid-state diffusion of both interstitial and sub-stitutional solutes in ferromagnetic solvents has been the subject of a number of investigations. Measurements of the self-diffusion of iron,"' the diffusion of nickel1,4 gold,"1 and cobalt4 into iron, the diffusion of vanadium in an Fe-V alloy,' and the diffusion of cobalt and nickel in Co-Ni alloys9 show an unusual behavior. In both the ferromagnetic and paramagnetic regions, far removed from the Curie temperature, the diffusion coefficient, D, obeys an Arrhenius relation. However, in the ferromagnetic region D is markedly lower than would be expected from an extrapolation of D from the paramagnetic region; this results in an increase in the activation energy in the ferromagnetic region. The cause of this effect for self- and substitutional diffusion is uncertain. Since substitutional diffusion is presumed to proceed by the vacancy mechanism, it has been variously suggested that the increase in activation energy below the Curie temperature is due to one of the following causes: 1) an increase in the energy of formation of a vacancy because of local demagnetization around the vacancy,2,3 2) a decrease in vacancy mobility in the ferromagnetic state,' or 3) an effect on the entropy of motion of a vacancy in the ferromagnetic state.5 Quite another explanation for the observed effect has been proposed by Borg.7 The diffusion coefficient is a function of the elastic constants of a metal. Since the temperature dependence of the elastic constants often changes at the Curie temperature, the temperature dependence of D might be expected to undergo a universal change in the vicinity of the Curie temperature. The magnitude of the change in D would, of course, depend on the magnitude of the change in the elastic constants. One might attempt to differentiate between vacancy effects and elastic effects by making measurements on interstitial alloys, in which vacancy effects play no role. Some measurements of this type have been made; this paper reports additional observations. Measurements of the diffusion of carbon in a Fe by a tracer technique8 and of the diffusion of carbon in a Co and in Co-Fe alloys by a decarburization method9 reveal a small effect, if any, on D of the magnetic change at the Curie temperature. If the effect of spin ordering is only to alter the parameters controlling formation or mobility of a vacancy, interstitial diffusion should indeed remain unchanged through the magnetic transition, as these measurements imply.

Jan 1, 1968

A1 in carbon steel, equilibrium temperature, XLVII, 740-747. A2 and A3 in pure iron, critical ranges, XLVII, 665-739. Abbott, Ai Arthur: [biog. notice, Bulletin No. 27, Mar., 1909, xxvii]; death, XXXIX, . [xl]. Abbott, Arthur Vaughan: [biog. notice, Bulletin No. 16, July, 1907, 6581; death, XXXVII, [xxxix]. [ ]

Jan 1, 1918

By R. S. Craig, W. E. Wallace, G. S. Kamath

The destruction of long-range order in Mg-Cd, has previously been thought to occur as a second order process. In the present work a variety of X-ray diffraction techniques are employed to show that in this case and in Mg-Cd alloys containing frorn 20 to 33 1/3 at. pct Mg the process more nearly resembles an ordinary first order phase transformation. It is found that the ordered alloy, which occurs as a single phase at lgw temperatures, transforms with increasing temperature into a Cd-enriched disordered (P) phase and an Mg-enriched ordered (a) phase. The interval over which these two phases coexist under apparently equilibrium conditiovs extends from 25" to 87°C content. At 33 1/3 at. pct Mg the two-phase region has disappeared. Measurement of the long range order parameter, s, for the ordered phase in MgCd, (from superlattice line intensities) shows that it disorders only very slightly before it is transformed into the p form. Kinetic experiments reveal that when the a phase is formed frorn the p phase by suitably quenching so as to suppress phase segregation, the transformation is essentially complete and the a phase has acquired its equilibrium value of S in less than 1 min. In an earlier investigation carried out in this Laboratory1 the rate of disordering of the MgCd3 superlattice was determined over an extensive range of temperature. The process was found to be first order and the rate constant, k, was established. At the lowest temperatures studied k was found to increase exponentially with temperature. At higher temperatures, however, it passed through a maximum and for the 100 deg interval below the point at which the superlattice was destroyed k was observed to decrease with increasing temperature. The various theoretical treatments1-3 of order-disorder phenomena lead to a negative temperature coefficient for k near the superlattice critical temperature but this region for MgCdB seemed unusually wide. Detailed analysis of the point indicated' that either the long-range order parameter, S, for MgCda varied with temperature in an anomalous way or the disordering in this instance is more complex than in the cases which have been treated theoretically. The original objective in the present work was simply to determine S vs temperature for MgCda to ascertain whether the disordering was in conformity with theoretical expectations.2° In an early stage of the work it was noted, however, that under equilibrium conditions ordered (a) and disordered (0) phases coexist in MgCd, over a considerable range of temperature. Since on thermo- dynamic grounds the coexisting phases must differ in composition, the investigation was enlarged to permit the compositions of the two phases in MgCd3 to be determined and to establish the extent of the two phase regions for alloys containing from 20 to 33 1/3 at. pct Cd.

Jan 1, 1963

By Joseph Daniels

The Fritz Engineering Laboratory was built under the direction of John Fritz, and presented by him to the University. A view of the building, looking east, is shown in Fig. 1. The building was started in 1909, and completed in 1910, although all of the equipment was not placed until later. Mr. Fritz gave his personal attention to the details of construction and equipment, and it was his custom to drive over every day to the University from his home in Bethlehem and spend some hours watching the work, offering suggestions, making changes, and planning new work. The result is a building and an equipment which embody his practical ideas. The laboratory structure is of the steel mill-building type, of light-colored brick, 91 by 114 ft., of which a section is shown in Fig. 2 and the floor-plan in Fig. 3. The steel frame carries the roof and traveling crane-way. Ample light has been provided by numerous windows in the side and end walls, in the clerestory, and by a skylight 84 ft. long and 9 ft. wide in the north roof. The main aisle of the building is 49 ft. 2 in. between centers of crane-columns, and has a clear height of 40 ft. The remainder of the width is taken up by two side aisles, 18 ft. high. The laboratory consists of four sections: (1) A general testing-section containing the testing-machinery, a small machine shop, and an office; (2) a cement-testing room; (3) a room for making and storing concrete test-specimens; (4) a hydraulic section.

Jan 1, 1912

By J. J. Crowe, G. K. Burgess

PAGE, Theories of Allotropy of Iron........... 667 Previous Determinations of A2 and A3 in Iron........ 668 Critical Ranges as Determined by Expansion........ 669 Critical Ranges by Thermoelectric Observations........ Critical Ranges in Terms of Crystalline Structure....... 670 Critical Ranges as Detected by Mechanical Methods...... 670 Critical Ranges as Given by Electrical Resistance....... 670 Critical Ranges as Determined Magnetically........ 671 Critical Ranges as Determined Calorimetrically....... 673 Critical Ranges from Heating and Cooling Curves....... 673 Summary of Previous Determinations of A3 and A2 in Pure Iron.... 675 The Present Investigation............ 678 The Experimental Method........... 678 Arrangement of the Apparatus.......... 679 The Measurements of Temperaturc.......... 679 The Measurement of Time........... 679 The Thermocouples............ 681 Temperature Scale and Calibration of Thermocouples...... 681 Mounting of Thermocouples........... 682 The Differential Measurements.......... 682 The Furnace and Accessories........... 682 The Vacuum Pump............ 683 The Energy Supply............683 The Rheostat.............. 683 The Materials Investigated............ 685 Sources of Iron............. 685 Preparation and Description of Samples......... 685 Chemical Analyses............. 687 The Experimental Data............. 688 The Preliminary Observations.......... 688 The Definite Series............691 Description of the Plotted Curves........... 694 The Effect of Plotting at Different Intervals........ 694 The Curves of the Definite Series.......... 695 . The Curves of the Preliminary Series......... The Existence of Other Critical Ranges......... 696 The Microscopical Examination........... 697 Summary and Conclusions............ 698 Bibliography............... 701 Plates................ 704

Jan 1, 1914

By C. S. Barrett, D. B. Masson

Martensitic transformations have been found in AgCd both upon cold-working at room temperature and cooling to lower temperatures. The crystal structures of the transformation products were found to be close-packed hexagonal in the first case and or-thorhombic in the latter. The transformation characteristics also were studied. Similar treatment of AuZn alloys failed to yield any transformation. THE literature on martensitic transformations of body-centered cubic metals and alloys indicates widespread instability of this structure at low temperatures, a tendency which merits further study. The body-centered cubic ß-phase of CuZn, for example, when it contained less than 42 wt pct Zn, was found by Greninger and Mooradian' and others' to transform on cooling to subzero temperatures to a phase that was tentatively considered to be tetragonal. Further work by Massalski and Barrett" demonstrated that cold work at low temperatures causes a partial transformation of ß CuZn of higher Zn content. The structures of the strain-induced transformation products were found to be different from those induced by simple cooling. Another well-known martensitic transformation among body-centered cubic phases is that of ß AuCd, first studied with X-rays by Olander,' then very thoroughly by Chang and Read.5,6 Here again transformation was found to occur both as a result of cooling and of strain. The alkali metals Li and Na, as well as certain Li-Mg alloys, also undergo transformation from their normal body-centered cubic structure, both on cooling and on cold-working. The phase AgCd, the subject of the present report, should be expected to behave quite similarly to CuZn for a number of reasons. It is the chemical analogue of CuZn, silver being directly below copper and cadmium directly below zinc in the periodic table. The size factors (percent difference in size) of the atoms, possibly a consideration in the stability of the ß-phases, are +3.1 in AgCd and + 4.2 in CuZn. Likewise the relative electronegativities of the two pairs of metals are about the same, CuZn possessing an electronegativity difference of 1.0 and AgCd one of 0.8. These values are from a table of electronegativities given by Darken and Gurry." The phase diagrams of the two systems around 50 atomic percent are similar, both possessing a disordered body-centered cubic phase, ß, at high temperatures and an ordered bcc phase, ß, at room temperature; however, the ß and ß' phases of AgCd are separated by a hexagonal phase, [, stable in the range 220-440oC, which has no analogue in CuZn. There has been confusion in the literature as to the structures of the ß' and [-phases. The phase diagram in the ASM handbook'" has the structures of the two phases interchanged; however, Hansen" reports the correct relative positions and Muldawer" verified that ß', the low-temperature phase, is body-centered cubic. Work by the present authors also

Jan 1, 1959

By Nicholas J. Grant, Chih-Chung Wang

TO phase of the Ti-0 system has the structure of NaCl and has a wide range of solid solubility.' In the course of studying the Ti-Cr-0 ternary system, binary alloys were made of iodide titanium and high purity TiO,. It was found from X-ray studies of the binary alloys that a transformation of the TiO appears to take place at a temperature near 925°C. Evidence of this phase change is best seen in Fig. 1. Fig. 1A shows the X-ray spectrometer pattern (CUKa radiation) of an alloy of 25 wt pct 0 corresponding to the stoichiometric composition of TiO.

Jan 1, 1957

By Chas. Y. Clayton, Francis B. Foley, W. E. Remmers

DuRing the summer of 1919, the late Dr. Henry M. Howe, then Chairman of the Division of Engineering of the National Research Council, organized a committee to obtain a better insight into the behavior of carbon steels under the influence of various treatments by a proper control of the time and temperature factors. During part of 1919 and 1920, work in connection with this investigation was carried on at Dr. Howe's laboratory at Bedford Hills, N. Y. During 1921 there was an enforced hiatus in the work, occasioned by the illness which resulted in Dr. Howe's death in 1922. At that time one of the present authors compiled the results of the work which had been done and this was published in 1923.' Following the publication of this work, it seemed desirable to carry on in the same manner an investigation of steel of C 0.75 per cent., which steel had not been as fully treated as had the other steels of C 0.34 and 0.52 per cent., used in the published work. Furthermore, certain unusual results have been obtained in the treatment of C 0.52 per cent. steel by quenching and drawing, and repetition of this part of the work seemed advisable. This has been done during the past year at the School of Mines and Metallurgy of the University of Missouri at Rolla, Mo., by a cooperative undertaking of the School and the Bureau of Mines, working in conjunction with the Committee on Heat Treatment of Carbon Steels of the National Research Council. The present paper is a report of the results obtained in this work.

Jan 1, 1926

By J. B. Morrow

WITH numerous plans under consideration for coal classification, and with the advent of the Bituminous Coal Code, the intelligent sam-pling of coal has become increasingly important. To us it is rather significant that there have been very few fundamental studies of coal sampling in American technical literature since those of E. G. Bailey, which appeared in the Journal of Industrial and Engineering Chemistry in March, 1909. He covered the subject up to that time so thoroughly and in such an excellent manner that perhaps many other later students have felt that they could add very little to his findings. The recent studies of the British Engineering Standards Association have indicated the possibility of a somewhat different interpretation of Bailey's results, permitting the taking of smaller samples, and perhaps it will now be helpful to reopen this question. C. W. H. Holmes, in an informative series of articles on coal sampling recently published in Colliery Engineering, makes two rather interesting statements, as follows: It is scarcely surprising to find a lack of interest and knowledge regarding the sampling of coal not only in the mining industry itself but also among consumers of industrial fuel: at its best coal sampling is a dirty business, regarded as a nuisance and an expense by the commercial man, and usually as a nuisance and nothing else by the chemist. The writer can conceive only two classes of people who have never experienced any difficulty in obtaining representative samples of coal from wagons; those who have never tried to, and those who have never had the necessity or desire to check the accuracy of their work. The primary purpose of this paper is to present some tabulated data of the more significant results of a sampling investigation undertaken during the last four years to obtain certain fundamental data on the variables connected with coal sampling and to point out that often assumptions have been made that are not in accordance with the facts. One of the standard sampling methods states:

Jan 1, 1935

By D. J. Jr. McAdam

RESULTS of investigation of corrosion-fatigue of metals at the U. S. Naval Engineering Experiment Station have been presented by the author in four papers. 1,2,3,4 In those papers references were given to the work of Haigh in 1917.5 The investigation at Annapolis included a variety of ferrous and non-ferrous alloys. The experiments showed that even slight corrosion simultaneous with fatigue may cause failure at stresses far below the ordinary endurance limit. The experiments also showed that, for most metals, severe stressless corrosion prior to fatigue is much less damaging than even slight corrosion simultaneous with fatigue. The term "corrosion-fatigue" was restricted to mean the simultaneous action of corrosion and fatigue. The combined effect of corrosion followed by fatigue was called "prior-corrosion fatigue." A stress-cycle graph representing corrosion-fatigue is a curve approaching a horizontal asymptote, the ordinate of which may be called a "corrosion-fatigue limit." To avoid confusion in later discussion, the term "endurance limit" will be restricted to mean the fatigue limit obtained by tests in air with specimens as free as possible from stress concentration and from corrosion. The endurance limit as thus obtained presumably represents an inherent property of the metal.

Jan 1, 1929

By William R. Webster

At the Florida meeting of the Institute, in March, 1895, I presented a Note on a Proposed Scheme for the Study of the Physics of Cast-Iron,1 giving an outline which, for convenience of reference, I here repeat. Suggested Lines for DiScuSsion and IvestiGation. I.—Correspondence between chemical composition and melting-point, fluidity, shrinkage, fracture, chill, micro-structure, and other physical properties. II.—Influence of: 1. Cupola-mixture, use of steel and other scrap, oxidized or clean material, 2. Manner of melting, flux, etc., 3. Casting-temperature, A. Fracture. 4. Manner of handling melted metal and B. Micro-structure. method of casting, C. Physical properties. 5. Size and form of casting, D. Shrinkage. 6 Kind of mold, green sand (under dif- on E. Chill. ferent conditions of ramming, amount F. Residual strew of moisture, and skin-dried), dry sand, G. Condition and quan- loam, and chills, tity of carbon and 7. Rate and mode of cooling castings, other elements. 8. Manner and temperature of heating for annealing, 9. Additions of nickel or aluminum, III. —-Segregation as affected by : 1. Composition ; 2. Casting-temperature; 3. Rate of cooling ; 4. Size and shape of casting. IV. —Blow-holes, their volume and position as affected by: 1. Composition; 2. Casting-temperature; 3. Casting-pressure ; 4. Rate of cooling; 5. Size and ehape of casting ; 6. Special additions. It was hoped that a discussion might thus be elicited, similar in interest and value to the discussion of the physics of steel, which had been so widely and gratefully welcomed by students and practitioners in that department. That this hope was not

Jan 1, 1905

By Robert D. Pike

In November 1939, on behalf of the Harbison-Walker Refractories Co., the author undertook the study of the problem of utilizing the dolomite of northwestern Ohio for the manufacture of calcined magnesia suitable for use in refractories. Grateful acknowledgment is made of the unfailing assistance and encouragement throughout this work from the executive and technical staff of Harbison-Walker Refractories Company. The dolomite of the Niagara formation that is exposed or near the surface of a wide area in northwestern Ohio1 constitutes a vast supply of almost pure dolomite. It offers a virtually unlimited supply of cheap raw material of uniform dependable analysis for the manufacture of magnesia. A typical analysis of dolomite from the vicinity of Luckey, Ohio, follows: Stone Completely Calcined CaO(Sro)a............. 30.35 57.806 Mgo................... 21.55 41.050 SiO2. ................... 0.30 0.572 R2O3................... 0.30 0.572 Ignition loss............. 47.50 a SrO about 0.06 pct. Brines containing magnesium chloride or sea water can be reacted with calcined dolomite to produce magnesia.2'3 In such reactions the MgCl2 of the brine supplies some of the magnesia and the amount of dolomite required is thereby reduced by an equivalent amount, but brines of commercial importance containing magnesium chloride are some distance away from the purest grades of the dolomite of northwestern Ohio. It was decided therefore to concentrate upon the development of a suitable process for separating the lime and magnesia of dolomite, depending upon the dolomite itself as the sole source of magnesia. This would make it possible to place a plant at the dolomite quarry, thus eliminating the cost of transporting the stone and also rendering the calcined magnesia available at a most convenient production point, considering the cost of delivery throughout the steel industry. The selection of a process depending solely upon the dolomite as a source of magnesia also necessarily entails production of the lime content of the dolomite as a by-product. It was recognized that if such a lime by-product could be produced in a suitable form, a plant location in northwestern Ohio would also be advantageous for marketing the lime. The problem, therefore, was the discovery and development of a low-cost process for separating the magnesia and lime of the dolomite of northwestern Ohio and producing each in a form relatively free from the other, and meeting the respective requirements of established markets. A satisfactory solution of this problem has been found, and it is the

Jan 1, 1948

By Robert D. Pike

In November 1939, on behalf of the Harbison-Walker Refractories Co., the author undertook the study of the problem of utilizing the dolomite of northwestern Ohio for the manufacture of calcined magnesia suitable for use in refractories. Grateful acknowledgment is made of the unfailing assistance and encouragement throughout this work from the executive and technical staff of Harbison-Walker Refractories Company. The dolomite of the Niagara formation that is exposed or near the surface of a wide area in northwestern Ohio1 constitutes a vast supply of almost pure dolomite. It offers a virtually unlimited supply of cheap raw material of uniform dependable analysis for the manufacture of magnesia. A typical analysis of dolomite from the vicinity of Luckey, Ohio, follows: Stone Completely Calcined CaO(Sro)a............. 30.35 57.806 Mgo................... 21.55 41.050 SiO2. ................... 0.30 0.572 R2O3................... 0.30 0.572 Ignition loss............. 47.50 a SrO about 0.06 pct. Brines containing magnesium chloride or sea water can be reacted with calcined dolomite to produce magnesia.2'3 In such reactions the MgCl2 of the brine supplies some of the magnesia and the amount of dolomite required is thereby reduced by an equivalent amount, but brines of commercial importance containing magnesium chloride are some distance away from the purest grades of the dolomite of northwestern Ohio. It was decided therefore to concentrate upon the development of a suitable process for separating the lime and magnesia of dolomite, depending upon the dolomite itself as the sole source of magnesia. This would make it possible to place a plant at the dolomite quarry, thus eliminating the cost of transporting the stone and also rendering the calcined magnesia available at a most convenient production point, considering the cost of delivery throughout the steel industry. The selection of a process depending solely upon the dolomite as a source of magnesia also necessarily entails production of the lime content of the dolomite as a by-product. It was recognized that if such a lime by-product could be produced in a suitable form, a plant location in northwestern Ohio would also be advantageous for marketing the lime. The problem, therefore, was the discovery and development of a low-cost process for separating the magnesia and lime of the dolomite of northwestern Ohio and producing each in a form relatively free from the other, and meeting the respective requirements of established markets. A satisfactory solution of this problem has been found, and it is the

Jan 1, 1948

By H. G. Sell, G. W. King

An investigation was made of the lensile proper-ties of recrystallized high-purity tungsten and a W-1 pel ThO2 dispersed-phase alloy over the temperature region of 800° to 2400°C. The thoria addition resulted in a modest strengthening effect over the entire temperature region. A decrease in ductility of both materials occurred above 0.5 Tm which was caused by void formation. Current theories of IT has long been recognized that a second phase of hard particles has a strengthening effect on a pure metal. At low or intermediate temperatures (<0.5 Tm), the strengthening effect is thought to arise mainly from the interaction of dislocations with dispersed particles. Above 0.5 Tm, dynamic recovery processes greatly alter the deformation mechanisms from those simply involving glide, and grain bound- strengthening by a dispersed second phase do not adequately explain the tensile results. Melallographic examination suggests that the improved strength of tire alloy results from the effect of thoria on the mierostructure. Stress-dependent thermally activated processes were found to occur high temperatures. aries may act as sources of weakness rather than strength because of grain boundary sliding. Grain boundary sliding at high temperatures has been postulated to be the primary factor giving rise to the formation of voids or cavities at grain boundaries1-3 which in turn cause premature failure and poor ductility.4 Voids, once formed, can grow by the condensation of vacancies from the equilibrium concentration&apos; or from the excess vacancies produced by the deformation.4,5 The high-temperature tensile properties of unalloyed tungsten have previously been investigated by Sikora and Ha116 and also by Taylor and Boone.7 The purpose of the present work was to investigate

Jan 1, 1965