By Magnus Troilius

INTRODUCTION BY C. P. SANDBERG. SINCE the discussion On steel rails in America has forcibly drawn attention to the value of chemical analysis, if not as a necessary stipulation, at least as a guide to control the usual mechanical tests, some doubt has been thrown upon the accuracy of the analytical results Obtained by different chemists. To any One having the least acquaintance with chemistry., it is quite clear that if exactly similar results are to be obtained from the same borings of steel, exactly the same methods must be used by the different analysts. Hence the necessity (if complications are to be avoided) of establishing what I may call standard or normal methods, to be used both by the inspectors and by the chemists at the works. Remembering that the application' of chemistry to steel-rail inspection is yet in its infancy, it is of great importance to possess a perfect acquaintance with the best methods in use. Being myself a grateful pupil of Professor Eggertz, of the School of Mines in Sweden, it Occurred to me, two. years ago, that I could not do better than start a laboratory of my. own, and engage One of his pupils, Mr. Troilius, for the purpose of analyzing the steel borings from mechanically-tested rails, so that I might thus Obtain without delay thoroughly accurate determinations. Moreover, in Order to carry on the, operations in perfect accordance with the methods used at the steel works in England and Germany, where I had to control the manufacture, I deemed it desirable to allow Mr. Troilius to go through a course of training at these works; and I gladly seize this opportunity of expressing my grateful acknowledgments to several works in England and in Germany for affording every facility for such an exchange of information as was found necessary in arriving at the best analytical methods to be used.

Jan 1, 1882

Jan 1, 1929

By R. M. Rose, K. A. Jones

Resistive measurements ulere made on superconducting niobium single crystals in transverse magnetic fields. Crystals were grouln in both high and ulfrahigh vacua, doped with stnall quantities of oxygen, and annealed in ultrahigh vacua at temperatures from 900' to 1350°C. Maxima in the fluxoid pinr~ir~g force were observedfor the [100] and [210] directions. The increase of the critical current density with dissoved oxygen was seen to saturate at relatively low concentration. This behavior, and the variation of J, and residual resistivity (as a function of oxygen content and annealing) of both clean and dirty gassy) crystals, is seen as a consequence of the formation of clusters with (210)~b habit planes and (200)ffo common boundaries. These suboxide clusters are apparenlly stable at high temperatures and very low oxygen concentrations. It is generally known that dissolved oxygen at concentrations well below the solubility limit sharply increases the critical current density of superconducting niobium.' Such a result would not be expected if Nb-0 solutions were random, not even as the result of segregation on the scale usually encountered in solid solutions. According to the Kim-Anderson theory of flux creep,' the critical transport current density is determined by the pinning force Fp associated with some feature of the microstructure. As the Lorentz force. a or (J X R), of the transport current in the magnetic field approaches Fp, flux creep and then flux flow occur. The pinning force is expected to be quite small if the heterogeneity involved is significantly smaller than tte range of coherency which for niobium is circa 250~.~ Although the strain field of an individual oxygen atom in the niobium lattice is relatively large, it does not seem plausible that individual atoms could be so effective as to account for the data. Also, ~ramer~ found that straining and strain aging specimens containing small amounts of oxygen on occasion decreased the residual resistivity. A possible explanation for the above behavior may be found in the work of van Ooijen and van der Goot,= who found that annealing changed J, for niobium foils containing oxygen, and they attributed the changes to ordering of the oxygen atoms. This phenomenon has been observed by other investigators using X-ray and PROCEDURE Cylindrical 4-in.-diam niobium single crystals with axial orientations [ill], [110], [112], and [oo~] were grown from pure niobium, see Table I for analysis, in an ion-pumped ultrahigh-vacuum system using the electron beam floating zone technique. Total pressure during growth was lo-'9 torr: the oxygen partial pressure was less than lo-" torr, as determined by a mass spectrometer. These crystals will be referred to as the "clean" crystals. Similar crystals were also grown in another system at a pressure of 5 X 10"6 torr. These crystals will be referred to as the "dirty" crystals. Specimens 14 in. long were cut from the as-grown crystals and one end was polished down to no. 600 carbide paper smoothness. A back-reflection Laue photograph was then taken in order to fix the crystallo-graphic directions transverse to the crystal. The critical current density J,, the current density necessary to produce a voltage drop of 1.0 pv between voltage leads placed a in. apart, was determined as a function of the magnitude and direction of the transverse magnetic field and of the oxygen concentration. The technique and experimental arrangement was essentially similar to that of Tedmon et al.' In the remainder of this paper, the azjmuthal angle $ for the field H is referenced to the [ I101 direction in all four crystals, and oxygen was added in small equal increments by anodization and annealing.7 The resistivity ratio, RR, of the resistance at room ternperature to that at 4.2"K (H =7.00 kG) was determined as well.

Jan 1, 1970

By David R. Mitchell, Byron M. Bird

THE revision of this chapter has presented a problem in that heavy-medium jigging has come into the picture since the chapter was originally written (seven years ago), a practice in which an artificial medium is built up and maintained in the jig circuit. As this development makes the jig a "true" heavy-medium process, the method belongs in the chapter dealing with such processes. Although putting this development in its proper position in the book involves some repetition, this seems to be the best procedure, and it has been followed. As the chapter on jigs in its original form was intended to be more or less a handbook on jigging for the use of the practical man, and the great bulk of the material therein is still generally applicable, the text has been re-used in large measure. Two major changes should be noted: (1) the portion of the text relating to the refuse-withdrawing mechanism of the McNally-Pittsburg jig has been entirely rewritten, and (2) a description of the hutch valves on the Jeffrey jigs has been added. Jigging is the stratification of a mass of solid particles in upward and downward pulsations. The stratification usually is effected in a rectangular open-top container having a perforated bottom through which the pulsations of water are applied to the materials to be separated; in separating coal, to a mass of coal and refuse. Jigging usually is a continuous process involving three steps: (1) the reception of the raw coal, (2) the stratification of the coal and refuse so that the refuse settles to the screen plate, and (3) the overflow of the cleaned coal and the withdrawal of the refuse collected on the screen. The jig is the most universal washer ever devised. It is handling in practice a wide range of closely sized coals and ores, mixed sizes of coal from 8-in. to 0 through 3/4-in. to 0, and mixed sizes of ores down to 7/32-in. to 0and even smaller. It is treating materials ranging in specific gravity from that of gold at 19 to that of coal at 1.30. It is handling feeds in which the proportions of high-gravity materials range from 90 per cent or higher, as for some iron ores, to 10 per cent or less for some coals. It is handling feeds containing all shapes of particles-round, rectangular, and flat. It is handling simple separation problems and difficult separation problems.

Jan 1, 1950

By W. H. Herrnstein, J. B. Clark, E. C. Utley, A. J. McEvily

The ratio of the endurance limit (10' cycles) to tensile strength of age-hardened aluminum alloys is approximately 0.3, whereas the ratio for annealed alloys is about 0.5. The lower value for the age-hardened alloys has been associated with the instability of coherent precipitate during cyclic loading, but it has not been definitely established whether this instability is due to overaging or reversion during cyclic loading. The results of the present investigatzon support the reversion viewpoint. In this work specimem of 2024-T4 aluminum alloy were aged for 16 hr at 150°C after cycling for 10 pct of the life at 25.000 psi. These specimens were then tested to failure and exhibzted a marked increase in fatigue life. It is proposed that during the early stages of fatigue in this alloy dislocations cut through the coherent precipitate and bring about the reversion of the precipitate. Subsequent aging at 150ºC induces reprecipitation in the precipitate-free zones so that the weakened regions are strengthened and the fatigue life is extended. It Is recognized that the fatigue strengths of precipitation hardened aluminum alloys are unusually low relative to their tensile strength.'-= This feature is illustrated in Fig. 1 where it can be seen that age-hardened alloys have lower fatigue ratios (the ratio of the fatigue strength to the tensile strength) than those in the annealed or cold worked state. Further, as shown in Fig. 2, the more an alloy is dependent upon precipitation hardening for its total strength, the lower is the ratio of the fatigue strength to the tensile strength. This state of affairs has been associated with an instability of the metastable metallurgical structure of precipitation hardened aluminum alloys during cyclic loading. Evidence2 in support of this view is that the fatigue ratio increases in these alloys as the test temperature is lowered, thereby indicating that thermo-mechanical instability, rather than some other factor such as a non-uniform distribution of precipitate, is the factor responsible for the low fatigue ratio at room temperature. Two mutually exclusive proposals have been ad- vanced to account for this instability. Hanstock has proposed that overaging takes place during cyclic loading, and in support of this view, Broom et a1.2 have indicated that an overaging process might be promoted by the large numbers of vacancies which are created during cyclic loading. The creation of vacancies by radiation4 has been shown to lead to rapid overaging. Hanstockl obtained visual evidence of overaging in an aluminum alloy after cyclic loading, but in this instance it has been pointed ou? that because of the high frequency used (60,000 cpm) the observed effect may have been due to normal high temperature precipitation around energy dissipating cracks. Efforts to discern visual evidence of overaging in this alloy at lower test frequencies were not successful.3 The alternative postulate3 is that reversion takes place during cyclic loading and leads to localized soft spots at which fatigue cracks are readily initiated. Evidence for this process has recently been provided by Polmear and Bainbridge5 who demonstrated metallographically that regions depleted of precipitate were created during cyclic loading of an aluminum alloy. Inasmuch as precipitate particles bordering the depleted region had not grown in size, it was concluded that the solute atoms which had constituted the missing particles had gone back into solution. No mechanism for the reversion process was presented. The present study was undertaken to investigate further the conditions leading to instability during cyclic loading, and to determine whether reversion or overaging had taken place as a result of cyclic loading. BACKGROUND AND TEST PROCEDURE In order to differentiate between the processes of reversion and overaging, rest periods at an elevated temperature, which ordinarily would insure additional precipitation, were used in this investigation. It was expected that after a period of cyclic loading an elevated temperature rest period would result in a decrease in the remaining life of the specimen if overaging were occurring during cyclic loading, whereas in the case of reversion, reprecipitation would occur and the fatigue life would be extended. Such an expectation is based on the assumption that the crack-nucleation phase is a significant portion of the total fatigue life, and that such a treatment is of influence in the crack-nucleation stage and is relatively unimportant thereafter.

Jan 1, 1963

By M. L. Holzworth, Philip R. Sperry, Paul A. Beck

INTRODUCTION THE basic work of Z. Jeffries1,2,3 has long ago established the main features of grain growth in the presence of a dispersed second phase. Working with sintered specimens of initially fine grained tungsten, to which various amounts of thoria have been added, Jeffries found that grain growth was inhabited, that is, practically prevented, up to a certain annealing temperature. When this temperature, which increased with the thoria content, was exceeded, extremely large grains developed abruptly from the fine grained matrix. Such a "coarsening temperature" was later found by Gross mann13,14 in certain types of steel, while Bain showed" that in other steels grain growth was gradual, without inhibition and abrupt coarsening. Later work16,17,18,19,21 demonstrated the connection between coarsening and aluminum additions. The viewpoint that the direct cause of inhibition and coarsening in aluminum killed steels is a fine dispersion of aluminum oxide21 appears to be held quite generally, although some doubts have been voiced even very recently.20 In steels with Ti additions the titanium carbide phase is considered responsible for the inhibition effects found.20 The coarsening temperature increases, with the titanium content. That coarsening may occur, as a result of certain heat treatments, even in low carbon rimmed sheet steel, was shown by Samuels,22 He also detected coarsening in a steel ingot of similar composition, after giving it the same heat treatment as that used by him for the sheet material, In this instance the identity of the inhibiting phase has not been determined, However, Tangerding found 23 that even the few small carbide particles, which occur in carbonyl iron, have a very marked inhibitive effect. As a result of an oxidizing anneal at 850°C, large grains begin to form at the surface of the carbonyl iron specimen, and gradually grow inward as the subsurface oxidation of the carbide particles progresses and eliminates the obstruction, The carbide particles can be removed also by annealing in hydrogen, with similar results. But if the oxidizing anneal of 10 hr at 850°C in air, is followed by annealing in hydrogen for 75 hr at the same temperature, grain growth is more spectacular; usually the whole specimen is transformed into a single crystal (approx. 1,5 cm X 5 cm). The reversed procedure, that is, hydrogen annealing followed by oxidizing annealing leads to smaller grains. Tangerding arrived at the logical conclusion that there must have been in his specimens some additional obstruction to grain growth resulting from a minor impurity, other than carbon. It seems likely that this obstruction was caused by an oxide formed during the oxidizing anneal and gradually reduced during the subsequent hydrogen-annealing. Other instances of grain growth inhibition of varying severity, associated with a dispersed second phase, have been described by several authors. Notable examples: lead with 0.06 pct Cu or Ni,24 cartridge brass with 0.12 pct Cr,25 or with up to 0.15

Jan 1, 1948

By R. F. Mehl, C. S. Barrett, A. H. Geisler

THE studies of the mechanism of precipitation and of the resulting property changes in aluminum-silver alloys1-3 have presented some new concepts of the aging reaction-concepts that may be fundamental in establishing a complete quantitative theory of age-hardening. With both aluminum-copper and aluminum-silver alloys, thin platelike aggregates form parallel to the Widmanstätten planes of precipitation.1,4 These platelets grow in lateral dimensions and in thickness with aging time until they are thick enough to produce an X-ray diffraction line pattern. Their structure is that of a transition lattice which is coherent with the matrix, since the atomic spacings in the matrix and the precipitate are the same on each side of their common interface.2,4 The equilibrium precipitate forms later from and at the expense of the transition lattice. Since age-hardening occurs during the formation and growth of the transition lattice, the major contributor to the hardening no doubt is the stress condition in the matrix resulting from the matrix holding the precipitate in the coherent condition. The development of these stresses also appears to be responsible for an increase in the electrical resistance superimposed on the normal decrease resulting from a change in the concentration of the matrix during aging.3 The two consecutive reactions constituting the aging process are accompanied by characteristic microstructural alterations. The initial precipitation process results in the formation of a Widmanstätten figure, while the later transformation of the transition lattice to the equilibrium lattice is accompanied by a coalescence, in the case of aluminum-copper alloys,5 and by the appearance of light areas at the grain boundaries with aluminum-silver alloys showing a structural rearrangement of matrix and precipitate.3 This latter reaction is similar microscopically to the so-called "discontinuous precipitation." Possibly discontinuous precipitation is a process that often if not always follows true precipitation of a coherent lattice and during which the transformation of the coherent transition lattice to the equilibrium lattice takes place accompanied by matrix recrystallization.3 EXPERIMENTAL PROCEDURE The alloys were made using 99.97 per cent Al or distilled magnesium, with

Jan 1, 1943

By R. R. McNaughton

The Consolidated Mining and Smelting Company of Canada, Ltd. at Trail, B. C., inaugurated a comprehensive program of investigation about 15 years ago to develop the most economical process of recovering the metal in the large accumulated stock of by-products of the lead smelter and the zinc plant. Two principal methods of recovery were followed to a successful conclusion—an electrothermic process to treat zinc-plant residues and cold slag and the fuming of hot slag from the lead blast furnaces. The latter was selected because it showed a saving over the former in its ability to handle hot blast-furnace slag, thus obviating the necessity of granulating, handling and eventually remelting the same slag for the electrothermic process. The design of a fuming plant was commenced in 1928, and construction, which was started immediately, was completed in July 1030. Operating intermittently for a general tuning up, the plant was officially blown in for regular operation in August. During this month the vagaries of a slag-fuming plant were studied and an operating crew was trained. A history of slag fuming at Trail and the development of plant design is given in a paper by G. E. Murray in the Transactions of the Canadian Institute of Mining and Metallurgy for 1933. Fuming Plant The fuming plant at Trail (Fig. 1) is a separate unit although of necessity interlocked closely with the lead smelter. The plant consists essentially of a fuming furnace with its accessories, a waste-heat boiler followed by an economizer, and a suction-type baghouse. The plant was built as the first of two 400-ton units with the intention of adding the second unit within a year, so that flues, fans and buildings were built to handle double the original load. Furnace.—The furnace as originally built (Fig. 2) was of water-jacket construction, 10 ft. wide, 20 ft. long and 6 to 10 ft. high. The roof height was made variable to check experimental work, which had indicated that this dimension affected the rate of reduction. Coal and air were supplied

Jan 1, 1937

By J. V. Emmons

It has long been known that the outside skin of tool steel frequently exhibits properties widely different from the interior of the mass.

Jan 1, 1915

By R. F. Mehl

Jan 1, 1936

By Charles H. Fulton

There are comparatively few accurate data on the melting-or the freezing-point temperature of metallurgical slags, or on related physical phenomena, such as fluidity near the melting-point, specific heat, latent heat, etc. With the exception of the work of H. 0. Hofman,' and some older work by R. Akerman, P. Gredt, and H. M. Howe, no information is available that is of direct interest to the metallurgist. Hofman's valuable work is the only one that refers to slags produced in the metallurgy of copper and lead. The classic work of J. H. L. Vogt,2 who views slags from the standpoint of physical mixtures (solutions in which the entities are minerals), has opened up a new field in the study of slags, and has placed the investigation of such properties as melting-temperatures, etc., on a rational basis. The recent work of A. L. Day, E. T. Allen, and W. I?. White, of the Carnegie Institution, at Washington, and of European investigators3 on certain systems of silicate minerals confirms the value of the investigation of silicate series from this standpoint, and it is my aim to apply this method to metallurgical slags, in order to gain exact data of value in metallurgy. The work recorded in the present paper is the result of an investigation of reverberatory-furnace slags made for a Western smelting company to determine exactly the influence of change in composition, within comparatively narrow limits, on the melting-point. For a general discussion concerning the mineralogical character of slags and the principles on which this investigation is based, reference should be made to other work: for the subject is too large to be stated in this paper, except very briefly in the following outline:

Jan 1, 1913

By A. W. Peake, F. O. Prior

Considering the great advance in the development and application of electricity, it is not strange that eventually a big field for its use has been found in oil-field operations. So far as is known, the first electric drive in oil-field operations was in the Russian field of Baku in 1900. The first application in this country was made by the South Penn Oil Co. near Folsom, West Va. in 1903. In 1916, electric power was first used in the Burma fields of India for drilling and pumping. Between 1916 and 1922, The Empire Gas & Fuel Co. made the first large electrical installation in the Mid-Continent fields. But although the first application was made 27 years ago, it is only within the last 10 years that oil companies have begun to look upon its use with much favor. Within the last few years, there has been a steady increase in the use of electricity in the oil fields. The first application of electricity for oil-field operations in Wyoming was in the Lander field in 1919; the second was in 1924 in Salt Creek; and the third, and last to date, was made by the Continental Oil Co. in the Big Muddy field during 1926. Lander Field The electrification of oil-field operations in Wyoming was initiated by J. W. Steele, superintendent of the Producers & Refiners Oil Corpn., in the Lander field in 1919. At that time, 32 wells were being pumped from five band-wheel powers, with oil engines as the prime movers. Eight barrels of fuel oil were used for power per day and at the price of 90 c. per bbl. the fuel bill was $36 per day. It was decided to try a 15 to 35-hp. oil-field motor on one of these powers. Electric power was generated with steam at the old Wind River refinery station. This test was so successful that in 1920 all five powers were equipped with 15 to 35-hp. oil-field motors, the power being obtained from the Sinks Canyon hydroelectric station. Four of these powers pumped wells at an average depth of 1450 ft., and the fifth pumped wells at an average of 2100 ft. In 1920, the average production per day from the 32 wells was 325 bbl. The power bill on the

Jan 1, 1928

By Yoon T. Auck, Milton E. Wadsworth

Column leach studies of two low grade prophyry copper ores were made with variables of size, flow rate, pH, drainage rate and tempature. Evidence is presented to show that, in some types of ores, sulfide minerals block leaching channels and regulate the rate of dissolution of gangue constituents. Basic iron sulfates, dissolved by introducing acid, provide oxidizing agent in the form of ferric ion in the absence of oxygen. Ferric ion then acts to release copper from the ore. Oxygen up-take was found to increase with the lowering of the pH and to follow parabolic kinetics attributable to the precipitation of basic iron salts within the pore channels. Slow drainage of residual gravitational water can seriously retard oxygen up-take during oxidation for particles in the coarse sand range. A model is presented for dump leaching in which a reaction zone connected by channels to the surface of the ore particle moves topo-chemically during the course of the reaction.

Jan 1, 1973

[ ]

Jan 1, 1938

By W. P. Sykes

In connection with a study of tungsten steels, Honda and Murakamil reported an investigation of the system iron-tungsten. This report included a tentative equilibrium diagram, photomicrographs of various alloys in the series, and qualitative measurements of hardness and magnetic properties. The present investigation originally had as its object the study of the hardness and tensile properties of a series of carbon-free iron-tungsten alloys. But, as the work progressed it became evident that the system possessed other features of interest, so the scope of the investigation was enlarged. Materials The iron powder used in preparing the alloys was obtained as follows : Iron oxalate was precipitated from a ferrous-sulfate solution by the addition of a solution of oxalic acid. This oxalate, after thorough washing, was ignited to iron oxide, which after reduction in hydrogen at about 1000" C. yielded iron powder containing but about 0.2 per cent. iron oxide and about 0.005 per cent. carbon. Tungsten metal in the form of powder, such as is used in the manufacture of filaments for incandescent lamps, was the other constituent. This material analyzed 99.8 per cent. tungsten and contained no carbon. The metal powders, in the desired proportions, were mixed by tumbling and formed, under pressure of 20 tons per sq. in., into rods 3/8 by 3/8 by 10 in. To form the alloys without contamination, sections of the pressed rods were placed on alundum slabs and heated in an alundum tube wound with a tungsten resistor and packed in heat-insulating material. While the resistor was heated, a stream of hydrogen was continually passed through both the tube and the case containing it. The tungsten winding on the tube, as well as the material heated within the tube, was thus protected from oxidation. Such a furnace will operate constantly for several days at temperatures up to 1500' C. and for shorter periods

Jan 1, 1926

Schedule of Events

Jan 1, 1977

By Norman Weiss

IF we were to measure progress this year in terms of large new mills and discoveries of fundamental significance we should certainly be disappointed. Outside of the uranium field there was little of a spectacular nature. San Manuel and Reserve completed their first year of operation; Erie approached readiness; the Toquepala project in southern Peru broke ground and gained speed. Important mill enlargements occurred at Inspiration, Anaconda, Ray, and Climax Molybdenum. A 3000-ton copper concentrator was completed at Pima, near Tucson. The Republic Mill of Marquette Iron Mining Co. started up in April. Abroad, the great developments in the African Copper Belt can be likened to the rapid growth of the porphyry coppers in this country. Fundamental research was confined nearly entirely to iron ore flotation and recovery of metal values from leach solutions, particularly uranium. The large number of review articles this year reflected a desire to take stock and consolidate past gains before taking the next bold steps. Undoubtedly a shortage of competent young engineers and technicians is stunting the natural growth of theoretical investigation in the field of minerals beneficiation, as well as the conversion of ideas into action. We find our small stock of talented young scientists concentrated in a few centers of erudition because there are not enough to diffuse through the industry. It is safe to say that among mine administrators and managers there is more interest in the education, training, and welfare of the young engineer than ever before.

Jan 2, 1957

By H. H. Klepfer, K. J. Gill, P. Chiotti

SOME observations relative to the U-Zn system have been made by other investigators. Chipman1 and Carter2 have reported the preparation of several U-Zn alloys and point out that these alloys are generally difficult to prepare. Chipman1 reported evidence for a high melting compound at about 90 atomic pct Zn and the possible existence of a eutec-tic between the compound and uranium. Raynor," in a theoretical discussion of the alloying properties of uranium, included zinc among the elements predicted to have little or no solubility in a, p, or y uranium. In the present investigation, thermal analyses, X-ray, metallographic, and vapor-pressure data were obtained to determine the phase boundaries. The relatively high zinc pressure over most of the alloys at temperatures of 900 °C and above proved troublesome and special techniques had to be employed in preparing suitable alloys. Materials and Preparation of Alloys The metals employed in this investigation were Ames Laboratory biscuit uranium containing less than 500 ppm total impurities and Bunker Hill slab zinc or Baker Analyzed reagent granulated zinc, both with a purity of 99.99+ pct. Due to the high vapor pressure of zinc and the high reactivity of both uranium and zinc with oxygen at only moderately high temperatures, alloys were prepared in closed containers which had either been evacuated or evacuated and filled with helium. High purity magnesia, magnesia containing 10 pct calcium fluoride, and tantalum proved to be suitable crucible materials. Tw-o different procedures, described below, were used to prepare alloys, the latter being the most satisfactory. The metals, uranium turnings and granulated zinc, were cleaned with dilute nitric acid, rinsed, dried, and placed immediately in a helium-fill'ed dry box. The two metals were placed' in a 10 mil Ta crucible. The charge was enclosed in the tantalum crucible by welding on a preformed tantalum cap. This assembly was enclosed inside a stainless steel (AISI 309) bomb. The bomb was made by welding a piece of stainless steel plate on each end of a stainless steel pipe. All these operations were carried out in a helium atmosphere. These assemblies were heated in a muffle furnace at temperatures between 1100" and 1200°C for 10 to 15 min or held as long as 15 to 20 hr in the 950" to 1000°C temperature range before quenching. Spectrographic and chemical analyses showed no tantalum pickup by the alloys, indicating no reaction between the alloys and the crucibles. However, some of these crucibles failed, probably due to imperfections in the welds of the stainless steel or tantalum crucibles. The second and most satisfactory method was to prepare the alloys by powder metallurgy techniques. The procedure was to press degreased and acid-etched uranium turnings with granulated zinc into 20 g compacts under 20,000-psi pressure. The compacts were placed in MgO crucibles, and sealed in evacuated Vycor or fused silica tubes. The alloys were then heated as long as two weeks at about 550°C in a muffle furnace. The pressed compacts were observed to expand by several volume percent during heating and it was necessary to make allowances for this expansion in order to avoid breaking the crucible and Vycor tube. This method was found very satisfactory for preparing alloys which were suitable for thermal analysis or vapor pressure studies. Experimental Methods and Results The phase diagram for the U-Zn system at 1 atrn pressure, shown in Fig. 1, is based primarily on vapor pressure measurements and on thermal analysis taken at temperatures below 950°C. Fig. 2 shows the U-Zn diagram at 5 atrn pressure, constructed on the basis of thermal analysis of alloys in sealed containers up to 1150°C and on the basis of metallographic, X-ray, and analytical data. The alloys sealed under vacuum were actually under their own vapor pressure and those sealed in an atmosphere of helium were under an additional pressure due to the helium. At temperatures up to 1100°C the zinc pressure is 5 atrn or less for these alloys; consequently the maximum pressure over the alloys sealed under a helium atmosphere was 10 atrn or less at temperatures up to 1100°C. Changes in pressure of this order of magnitude do not appreciably alter the position of most solid-solid or liquid-solid phase boundaries. In constructing the phase diagram for a pressure of 5 atm, the effect of pressure on all phase boundaries except those for liquid-vapor or solid-vapor regions was considered negligible.

Jan 1, 1958

NEW MEMBERS The following list comprises the names of those persons who became members during the period Feb. 10, 1919, to Mar. 10, 1919. ALLEN, ROLLAND CRATEN State Geol., Appraiser of Mines, Lansing, Mich. ALTMAYER, MAURICE ERNEST, Ingenieur des Arts et Manufactures, 145 Rue de la Pompe, Paris, France. AUSTIN, CHARLES L., Assayer, Highland Boy Mine, Utah Cons. Min. Co., Bingham Canyon, Utah. BARTLETT, ARTHUR J., Chief Engr., Louisville Coal & Coke Co. Goodwill, W. Va. BOIES, ORLOW W., Research Chem., Roessler & Hasslacher Chemical Co., 1632 Tenth St., Niagara Falls, N. Y. BRAGG, G. A., Mgr., Experimental Copper Leaching Plant, Mellon Inst. of Industrial Research, Thompson, Nev. BRUSCANTINI, GIOVANNI, Min. Engr., Gen'l Mgr., Sindicato Minero de Cuba, Box 370, Santiago, Cuba. COLONY, R. J Instructor in Geol., Columbia University, New York, N. Y. DAVENPORT, FRANK B., Cons. Engr., 806 Coal Exchange Bldg., WiIkes-Barre, Pa. EATON, S. FORD 120 E. 85th St., New York, N. Y. EBY, J. H., Min. Engr Box 433, Spokane, Wash. ENGELHARDT, EDWARD A., Mgr., Surinaamsche Bauxite Mij, Paramaribo, Dutch Guiana, S. A.

Jan 4, 1919

By W. E. Hale, G. J. S. Govett

An orientation survey was conducted over a known disseminated copper deposit and a Au-Cu vein deposit and employed geological, geophysical, and geochemical methods. Geochemical techniques proved the most effective and economical means of locating and defining areas underlain by these types of mineralization. Six additional, widely separated occurrences were also investigated and mineralization was confirmed by determination of cold-extractable copper in stream sediments. The length of anomalous drainage varies from several to 16 km and depends on the type and tenor of mineralization. Despite generally marked relief and extreme physical and chemical weathering, cold-extractable copper anomalies in soils appear to reflect closely variations in the ore mineral content of immediately underlying rocks. Threshold values vary with local geological conditions and type and grade of mineralization. Significant thresholds in stream sediments are about 65 ppm and 10 ppm for cold-extractable copper in disseminated and vein copper occurrences respectively. Similar differences are encountered in soils. This necessitates the use of a scale of threshold values at progressive stages in each exploration program. Dis-seminated copper occurrences are presently the major source of mineral production m the Philippines. Much potentially productive ground remains to be investigated and applied geochemistry appears to offer the best available approach. The Institute of Applied Geology (I.A.G.), a joint project sponsored by the University of the Philippines, the Philippine Bureau of Mines and the United Nations Development Program (Special Fund) undertook during 1965-66 a number of field projects in Northern Luzon Island (Fig. 1). These field operations were of a two-fold nature and involved both orientation and exploration. During approximately six weeks, an orientation survey, involving geological mapping, geophysical surveying and geochemical prospecting, was conducted over a partly developed, disseminated copper deposit at Santo Nino (Fig. 1). This study demonstrated the economic and technical feasibility of geochemical ptospecting, relative to the other methods tested, for the location and delineation of a typical disseminated copper occurrence characteristic of those that represent the major source of metal in the Philippines.' Geochemical techniques, similar to those tested at Santo Nino, were then applied in a second orientation study of a vein occurrence at Suyoc (Fig. 1). The results of these two orientation studies suggest that, in reconnaissance work in this region, stream sediment analyses, combined with the determination of pH in the same streams, can be used to indicate areas underlain by rock containing anomalous concentrations of copper, whether it occurs in the large tonnage, low grade, disseminated deposits or in the comparatively small tonnage, higher grade, gold vein occurrences. Furthermore, the orientation surveys demonstrate that soil sampling and analysis serve effectively to outline more closely the mineralized zones within the generally anomalous areas identified from the stream reconnaissance. To further test the methods selected from the two earlier trials, six additional, widely separated prospects were investigated. The geological and geochem-

Jan 1, 1970