By R. P. Smith

The diffusivity of carbon in iron, cobalt, and alloys of 89.7 and 79.3 wt pct Co has been determined by a decarburization method for the temperature range 850° to 1100°C. The Plots of log D us 1/T for the two Fe-Co alloys are linear through the region of the Curie temperature, showing that, unlike some cases of substitutional diffusion, carbon diffusion in these alloys is not affected by electron spin order. RECENT investigations1-' have shown that for substitutional diffusion in iron the change in diffusivity with temperature does not follow an Arrhenius equation, at temperatures near the Curie temperature. Data on the diffusivity of carbon in a iron5"9 indicate that this anomaly does not exist for interstitial diffusion; however, this has not been definitely established. Since cobalt and Fe-Co alloys, 80 to 100 pct Co, have Curie temperatures in a temperature range convenient for carbon-diffusion measurements they are suitable systems for studying the relation of interstitial diffusion and the Curie temperature. EXPERIMENTAL The carbon diffusivity, D, was determined by a decarburization method. The diffusion cylinders, made from small vacuum melts of electrolytic cobalt and plastiron, were about 0.76 cm diam and 6.3 cm long. A small amount of carbon was added to each melt to keep the oxygen content as low as possible. The cylinders were first treated with a hydrogen-3 pct water vapor mixture at 1100°C to constant weight, then carburized to the desired initial carbon content with a suitable CO-C02 gas mix-

Jan 1, 1964

By D. Bergekoff

IN the routine examination of a wide variety of metal specimens it is sometimes necessary to have special methods of polishing in order to retain and reveal certain details in each specimen. Among such special cases is the retention of graphite in malleable and gray cast irons, the preservation of all types of nonmetallic inclusions in both hard and soft steels, obtaining a scratch-free surface with soft metals, and avoiding the usual relief effects with very hard specimens such as tool metals con-taining various carbide and nitride phases. It is the purpose of this paper to give an account of some of these special polishing methods in use at the Union Carbide and Carbon Research Laboratories. The polishing procedures outlined have been found to give uniform results. It is obvious that only general rules and the most important working details can be given here. Following these rules, the polisher can obtain satisfactory results if he possesses the necessary patience and has a sincere desire to give as nearly perfect a finish as possible to his work.

Jan 1, 1939

By Ray Light, Everett M. White

Numerous articles have been written about the coal miner ; he has been compared with brave men who have gone out to conquer some unknown hazard throughout the ages. Now, however, modern mining is no longer something to be avoided, but a vocation that anyone can be proud of, with remuneration equal to or above that of almost any industry. A concerted effort is being made each day by both the operators of most mines as well as the state and federal inspectors to see that coal mines are as safe or safer than work places in any other industry. However, it is true that mine fires and explosions have occurred in the mining industry since its inception. One of the earliest accurate references to such an occurrence is found in the transactions of the Royal Society of London. In the Colliery Managers' Handbook, 1898, Caleb Pamely writes of an explosion that occurred at Fatfield, England in August 1708, resulting in the deaths of 69 persons. He states: "Three of them, viz, two men and a woman, were blown quite up from the bottom of the shaft, fifty-seven fathoms deep, into the air, to a considerable distance from the mouth of the pit." It is interesting to note that women were employed as miners in England during that period. In the United States, the first record of coal mined was in 1702 by the Jamestown colonists. In 1786, about 20 years after Pittsburgh, PA was first settled, a charter was granted by William Penn to mine coal on the banks of the Monongahela River. Then in 1803, the first important coal company, the Lehigh Coal Co., was established. From this beginning, the mining industry continued to grow in importance and the first state mining law was formulated in 1870. The Pennsylvania state mining law was followed in 1873 by Ohio's, and in 1876 by Maryland's. A mine explosion at Avondale, PA in 1869 stimulated state legislatures to formulate these early laws. In 1907 near the town of Fairmont, WV, there were, within three days, two explosions resulting in a total of 597

Jan 1, 1981

By C. M. Wayman, J. F. Breedis

The crystallography of the martensitic transformation in the Fe-30 Ni alloy was reinvestigated. The scatter in the habit Plane as determined from measurements on the mid-rib plane was smaller than reported previously, and the orientation relationship was determined from a martensite plate having known direction cosines. From agreement with crystallographic theory and from observations of the morphnlogy of the martensite plates, it is suggested that the mid-rib plane represents the starting region of the transformation. THE crystallography of the martensitic transformation in the iron-nickel system has been the subject of many investigations.&apos;-7 However, for iron alloys containing approximately 30 wt pct Ni, a wide scatter in the reported habit planes exists. In only one instance has a Laue determination of the orientation relationship been made, but the habit plane of the martensite plate studied was not determined experimentally. Because the most successful thermodynamic and kinetic analyses8 of the martensite transformation have been based on Fe-30 Ni alloys, it was considered desirable to reinvestigate the crystallographic features of the transformation in this alloy. Lieberman9 suggested that the most significant information for use in a theoretical treatment involves the determination of all the crystallographic observables from a single plate of the product phase. This was first done in essence by Greninger and Troiano10 for Fe-22 wt pct Ni-0.8 wt pct C, and is the method followed in this investigation. Some theoretical approaches11-13 in describing the martensitic transformation consider the overall transformation distortion to be comprised of a Bain distortion, or lattice deformation (PI, which produces the structure change, and a lattice invariant deformation (G), such as twinning, which together leave the interface or habit plane un-distorted. The incorporation of a rigid body rotation (R) results in a transformation distortion (E) such that the interface plane is left both undistorted and unrotated. In matrix notation, E = RPG where the lattice invariant deformation has "taken place" in the austenite. Bowles and Mackenzie14-16 in formulating a theoretical approach proposed an adjustable scaler quantity, denoted as 6, which represents a uniform dilation in the interface plane. This dilation acts to adjust the lattice spacings of the parent and product structures at the plane of contact. Using the dilation parameter as a variable, these authors were able to account for a continuous variation of habit planes in steels along a curve in the stereogram between {225}A and {259}A. she invariant line strain14 of the transformation is 6 RP, and the corresponding transformation distortion is E/6.) With the dilation parameter known, the invariant line is computed as the triple coincidence of the habit plane, the shear plane of the lattice invariant deformation, and the initial Bain cone.14 The contraction axis for the Bain distortion can be taken9&apos;17 as [010]A, and the correct permutation of the habit plane indices used. Kelly and Nutting 18 have established the shear plane (of twinning) in the tetragonal martensite of Fe-22 Ni-0.8C to be {112)M by means of transmission electron microscopy. The reasonable shear system is then {112}M which is equivalent to {011}A <01l>A. The as-

Jan 1, 1962

Jan 1, 1925

By F. V. Lenel, G. S. Ansell, E. C. Nelson

IRMANN&apos;S&apos; discovery that extrusions of fine alumi-num-flake powders possess remarkable high-temperature strengths has led to the production of a new class of engineering materials whose properties are derived from a fine dispersion of oxide particles in a metallic matrix. A fundamental study of such materials and elucidation of the mechanism whereby the oxide parti-

Jan 1, 1958

By John C. Draper

The principal object of an underground coal mine transportation system is to move coal from the face where it is produced to the outside of the mine where it is prepared for market. In addition to the movement of coal, a transportation system must also move supply materials to the inside ; it must move men in and out of the mine ; and it must move rock and other debris out of the mine for disposal. Usually, mine haulage is divided into three categories named for the various areas of the mine served : 1) Pace Haulage. This is used at face from the mining machine to the intermediate transport system. 2) Intermediate or Secondary Haulage. Generally this is used between face haulage and main haulage. Sometimes this is merely an extension of the main haulage. 3) Main Haulage. This extends from the secondary haulage to the outside and is usually either a track or conveyor system, sometimes a combination of both. Transportation modes of coal in the various areas pose different problems, but the whole system must be synchronized. For instance, at the face the coal should be removed quickly from the various places to facilitate the movement of machines, whereas the intermediate system just passes the same coal on to the main transportation system. Selection of the transportation system must be based on the seam height, mining methods used to extract the coal, capacity required, ease of coal handling, and haulage efficiency. When driving rooms, mine cars can be used. They often simplify supply haulage and rock handling because they can also handle these items. Conveyors could be used and would have a greater haulage capacity but they cannot handle supplies easily or segregate the rock. When using a different mining method, such as longwall, mine cars cannot be used because there is not sufficient space to move the cars at the face nor can the cars haul the coal without delays which would cause excessive losses in production. As for ease of handling

Jan 1, 1981

By E. P. Jennings

Large deposits of titaniferous iron-ore occur at Caribou, an old silver-mining camp in Boulder county, Colo., 17 miles west by south of Boulder, and a few miles northwest of the tungsten-mines. Professor Regis Chauvenet1 published a part analysis of the ore many years ago, but gave no description of the wall-rock. Caribou hill, which contains both the silver-bearing veins and the iron-ore deposits, is a low dome of gabbro surrounded by the Archæan schists and gneisses of the Front range of the Rocky mountains, the peaks of which, a few miles west of Caribou, attain an elevation exceeding 12,000 ft. The gabbro stock is roughly elliptical in outline, with approximate diameters of 1 and 3 miles. The crest of the dome is 10,500 ft. above sea-level, and the town and ore-cleposits are 500 ft. lower. Outcrops of the iron-ore occur in the town and extend NW. for 2,000 ft., where they disappear under the swampy meadows of Caribou park. Portions of the deposit are covered by drift, but one continuous outcrop is 900 ft. long and from 200 to 250 ft. wide. A second deposit is 0.25 mile south of the town along the eastern slope of the hill. It is not as well defined as the north bed, but is approximately 1,000 ft. long and from 100 to 200 ft. wide. The easily disintegrated ore does not form prominent outcrops, but the outlines of the deposits are readily traced by the large amount of ore fragments that cover the ground. Trenches and pits sunk on the outcrop expose a roughly banded magnetic iron-ore, with pyroxene as the principal gangue-mineral. The Gabbro. This rock was classified in the field as a gabbro from the presence of pyroxene and striated feldspars, and for convenience the field-name will be retained.

Jan 1, 1913

INTRODUCTION Data available on prophyry copper occurrences in the Andean, Caribbean, Appalachian, and Cordilleran orogens may be categorized in a manner to suggest a hypothetical evolution for deposits that occur in the western hemisphere. A classification of de- posits is also suggested. A classification dependent on internal structure of a porphyry copper deposit would lead to two broad categories, breccia pipe and stockwork models. A classification of this type is examined herein but it is not universally accepted in the literature. Modeling based on igneous petrography as well as metasomatism attendant with the sulfide mineralization is more widely accepted by economic geologists whose evaluation of porphyry systems is influenced by the presence or absence of a phyllic zone. Lowell and Guilbert model deposits ordinarily include a phyllic zone, whereas those of the diorite model do not. Position of the phyllic zone in the alteration sequence is a significant ore guide. Should the phyllic zone be absent, dependence on alteration zoning to identify metallization is weakened. Presence or absence of the phyllic zone therefore is a significant parameter in the economic evaluation of a porphyry copper deposit (Hollister. et al., 1975). The Lowell and Guilbert (1970) model commonly includes a phyllic zone in quartz- bearing rocks. Parameters of both calc-alkalic and the quartz monzonite models mentioned elsewhere in this volume are sufficiently close to the Lowell and Guilbert (1970) model that it should be expanded to encompass them. The diorite model remains separate and distinct because deposits of this type are characterized by an absence of quartz in the pluton, commonly highly gold: copper ratios, low molybdenum content, and regular absence of sericite in the alteration zones. Therefore, for the benefit of those

Jan 1, 1978

By Eugene A. Mizikar

A mathetnatical model of heal transfer in continuously cast steel slabs is described. The model, consisting of a unidimensional transient conduction equation and boundary condition equations, has been pvogrammed for computer solution. Temperatuve and solidification profiles calculated for a 6-in. slab, being cast under several conditions of secondary cooling, are presented and compared. Calculated solidification profiles are in agreement with reported expevinle~ztal values. For the mold zone, the predicted slab shell thickness can be described by: Resuilts of the study indicate that multibank spray cooling followed by radiant cooling should be employed when solidifying thick slabs with minimum surface temperature of 1600°F. Under these conditions, a 6-in. slab can be expected to solidify in about 8.3 min. Computer results also indicate that radiant cooling can replace spray cooling during solidification of the final 30 pct of slab with little increase in overall solidification time. CONTINUOUS casting has come to the forefront of the steel industry in recent years because of economic advantages resulting from increased yields and elimination of several processing steps. Considerable work, however, remains to be done regarding modifications to the process and operating procedures. Both a lack of operating plants in this country and the experimental difficulties associated with direct measurements on moving castings have made determination of solidification rates and temperature distributions difficult. An alternate approach is to mathematically simulate heat transfer in a continuously cast section, and then calculate the temperature distributions as a function of the controllable variables of the process. Simulation of heat transfer during solidification requires that a nonlinear mathematical problem be solved. As pointed out by Ruddle,&apos; there are two mathematical approaches to the problem- the analytical approach and the numerical approach. While the analytical approach is certainly the more elegant of the two, it does require a number of inexact assumptions because of the complexity of the problem. For example, noteworthy analytical treatments of heat transfer in continuous casting have been developed by Savage Hills,3 and pehlke4 only by making one or more simplifying assumptions such as invariant thermophysical properties, constant heat-transfer coefficients in the mold, and linear temperature profiles in the shell. Simplifying assumptions such as these can introduce considerable uncertainty in the validity of results calculated with analytical solutions. Numerical solutions, which are considerably more versatile, appear to be better suited for solving solidification problems. Complex variations in the boundary conditions and variable thermophysical properties can be handled readily with this technique. Whereas numerical computations can be long and tedious when done by hand, results can now be obtained quite rapidly with the use of either the digital or analog computer. Several numerical models of heat transfer in continuous casting have been published. In 1963, Adenis, Coats, and Ragones published a numerical model used to calculate temperature distributions in direct-chill-cast magnesium billets. More recently, Donaldson and Hess 6 presented results obtained with a numerical computer model of heat transfer in continuously cast steel billets. In the present study, a model of unidimensional heat transfer in continuously cast slabs is presented. The method of solution on a digital computer is also included. Calculated temperature distributions and solidification profiles for various schemes of secondary cooling along with attempts to verify the model are also discussed. MATHEMATICAL MODEL The schematic representation of the slab continuous casting process in Fig. 1 illustrates that the slab passes through three distinct zones of cooling. Accordingly, the mathematical model consists of three parts: 1) solidification in the mold; 2) solidification in the spray cooling zone ; 3) solidification in the radiant cooling zone. Heat-Transfer Equations. The model was developed bymaking a heat balance on a horizontal slice of slab over the time period required for the slice to proceed from the liquid metal meniscus in the mold to the cutoff station. As shown in Fig. 2, the imaginary slice extends from the center line to the surface of the slab. As the slice moves downward, heat is conducted from the center line to the surface of the slab at a rate governed by the surface boundary condition and thermophysical properties of the metal in the slice. The following partial differential equation describes the conduction of heat in a medium moving at velocity U in direction Z:

Jan 1, 1968

By Harry L. Washburn, Robert L. Llewellyn, W. J. Halvorsen

Many of the problems that occur in the preparation plant originate from practices in the mine. Impurities in raw coal can be in the seam itself or from extraneous material taken in mining from the roof or bottom. In the case of underground mines, the choice of mining equipment will affect the size consist and the amount of extraneous material included with the coal. Also, governmental regulations concerning the degree of rock dusting, gobbing underground, and cleanup have increased the dirt in raw coal. Sulfur dioxide emission standards, on the other hand, are pressuring the coal industry to clean coal more thoroughly. Coal supplied for coking purposes is nearly all upgraded by washing, while for the largest market, electric power generation, a high proportion is shipped as a raw product with processing, in whole or in part, only necessary when excess impurities are mined with the coal. This chapter will deal primarily with plants that process or wash coal to some extent (Fig. 1) and only incidentally with mines shipping raw run-of-mine coal crushed to a top size of, usually, 51 to 102 mm (2 to 4 in.), with little, if any, other treatment. JUSTIFICATION FOR COAL PREPARATION During the past decade, major changes have occurred affecting the market, profit, and long-range planning of the coal industry. Mining companies have become "partners" with consumers at many new and some old mines, both for steam and metallurgical coals. Coal properties have become "assigned" tonnages at mutually agreed upon conditions and prices. Lower unit-train tariffs have been instrumental in helping coal markets to compete against oil and nuclear energy. Coal prices for power plants are still on a Btu (British thermal unit)

Jan 1, 1981

By R. J. Charles

Previous study of simple impact systems indicated that energy required for fracture and size reduction of brittle materials is greatly dependent on the type of loading that is employed. In this regard it was postulated that fracture and size reduction of a brittle specimen might be accomplished by a high velocity impact at an energy level at which a low velocity impact would leave the specimen relatively undamaged. The finite time required to propagate energy away from the point of loading of an impacted object to other parts of the object and to its supports may permit a concentration of energy at the point of impact if the rate of loading is high. Localizing of energy at the point of impact could quickly initiate fractures that would propagate through the impacted material along with the traveling stress waves. As the cracks form, the initially absorbed strain energy would be released and portions of it travel ahead of the crack tips as stress waves. These secondary stress waves, combined with the initial stress waves derived from the impact, would produce high localized strain conditions in front of the fracture zone. The fracture zone would propagate and the specimen shatter. High rates of loading are brought about by short impact times, in turn obtained by employing high velocity projectiles that are of small mass compared to the impacted object.

Oct 1, 1956

By Chung Yu Wang, Guy C. Riddle

There are found in nature upward of II2 minerals containing antimony, but only a few of them, listed in Table I, can be considered as antimony ore-forming minerals. Stibnite (Sb2S3), antimony sulphide or glance, is the principal ore of antimony. The oxide ores—cervantite, kermesite, valentinite, sernarmontite—occur sparingly in nature. Dry methods are generally adopted for the extraction of the metal. Electrometal-lurgical methods have had much attention in America and Germany and have not yet found, on economic grounds, practical or extended application, except in a few places. During recent years, treatment of the poor grades of the ore, especially sulphide, by ore-dressing methods, has commanded some attention and been adopted at a few plants. The impure sulphide of antimony, resulting from the liquation process, is called lLneedle," "liquated" or "crude" anti- mony, and the refined metal itself is called antimony "regulus." The different processes for the treatment of antimony ores are shown in the diagram of Fig. I. Liquation of Crude Antimony The first step in the smelting of antimony is a simple one, the process of LLliquation," which produces crude or needle antimony. Ores containing $ 50 per cent Sb are used in the liquation process for the production of crude. The temperature required for liquation is between 550&apos; and 600°C. Ores to be liquated are broken to about walnut size. If the pieces are larger than this, the low heat used will not penetrate&apos; effectively, and if they are smaller the ore tends to pack too closely for adequate penetration. A packed charge also prevents the free escape of the fused sulphide. Intermittent Liquation in Crucibles The unique type of furnace that is in use in China for smelting is not highly efficient but is simple in construction and operation. The furnace is generally built

Jan 1, 1944

By K. Huessener

In presenting the following data on combustion in the open hearth furnace and the advisability of automatic combusion control, the author finds himself much more severely handicapped by the lack of reliable test results than he had anticipated when he first undertook to write this paper. In order thoroughly to investigate how the results of an open-hearth furnace are influenced by combustion, one would have to draw up a large number of heat-balance sheets, as Kinney and McDermottl have given for one heat in their extremely able paper on "Open Hearth Efficiency,&apos; presented before the American Iron and Steel Institute on October 27th,1 1922. Instead of covering only one heat, however, such heat-balance sheets would have to embrace a large number of heats, and not only for one kind of fuel, but for all the various fuels in customary use. Use of Radiation-protected Pyrometer Such tests necessitate extremely careful temperature readings, and here the first serious difficulty presents itself. Nearly all the temperature readings so far published have been taken with thermocouples for the lower ranges and with optical or radiation pyrometers for the higher ranges. This method of measuring reveals the temperature of the surrounding walls, or in the case of optical or radiation measurements, the temperature of that part of the opposing walls which has been focused by the instrument. The error in ascertaining the temperature of the gases entering or the waste gases leaving the checker chambers is probably not very large, as the flowing gases impart their temperature to the walls of the flues. On the other hand, the uptakes, where the preheat temperature of gas and air are usually measured, are under the influence of radiated heat from the port ends, and correct temperature readings can here be taken only by using a radiation-protected pyrometer of the aspirating type.

Jan 1, 1926

By William A. Johnson, Robert F. Mehl

It is now recognized that several important types of reactions in metallic systems proceed by the formation of nuclei and the growth of these nuclei. The process of freezing is a simple example of this, as Tammann pointed out years ago.1 Tammann held that the rate of freezing is determined by a rate of nucleation, expressed as the number of nuclei formed per unit volume of unfrozen liquid per second, and a rate of growth of these nuclei, expressed as the linear rate of radial growth in units of length per second. For isothermal freezing the conception is simple; for ordinary freezing, extending over a range of temperature, it is not as simple, for the values of the two constants must change with change in temperature. There is ample evidence that the postulated mechanism is correct even though a quantitative derivation of the rate of isothermal or of ordinary freezing in terms of the two constants has been lacking. In recent years other reactions have been found to proceed in a similar fashion. It has been well established, particularly by Bain12-8 that the formation of pearlite from the eutectoid decomposition of the solid solution austenite proceeds in such a way, and Polanyi and Schmid, Tammann and Crone, Karnop and Sachs, and others9-11 have shown that the process of recrystallization proceeds in a similar way. Isothermal reaction rates have been determined for eutectoid decomposition by a number of investigators. Bain&apos;s2-8 work on the formation of pearlite from austenite is especially valuable in this respect—the type of isothermal reaction curve obtained, as illustrated in Fig. 13, showed an initial slow rate, accelerating to an intermediate maximum rate which then decelerated to the completion of the reaction; similar curves have been obtained by Wever and his collaborators.12 Other eutectoid decompositions show similar behavior: for example, the decomposition of the beta eutectoid in the copper-aluminum system, studied by Smith

Jan 1, 1939

By William A. Johnson, Robert F. Mehl

It is now recognized that several important types of reactions in metallic systems proceed by the formation of nuclei and the growth of these nuclei. The process of freezing is a simple example of this, as Tammann pointed out years ago.1 Tammann held that the rate of freezing is determined by a rate of nucleation, expressed as the number of nuclei formed per unit volume of unfrozen liquid per second, and a rate of growth of these nuclei, expressed as the linear rate of radial growth in units of length per second. For isothermal freezing the conception is simple; for ordinary freezing, extending over a range of temperature, it is not as simple, for the values of the two constants must change with change in temperature. There is ample evidence that the postulated mechanism is correct even though a quantitative derivation of the rate of isothermal or of ordinary freezing in terms of the two constants has been lacking. In recent years other reactions have been found to proceed in a similar fashion. It has been well established, particularly by Bain12-8 that the formation of pearlite from the eutectoid decomposition of the solid solution austenite proceeds in such a way, and Polanyi and Schmid, Tammann and Crone, Karnop and Sachs, and others9-11 have shown that the process of recrystallization proceeds in a similar way. Isothermal reaction rates have been determined for eutectoid decomposition by a number of investigators. Bain&apos;s2-8 work on the formation of pearlite from austenite is especially valuable in this respect—the type of isothermal reaction curve obtained, as illustrated in Fig. 13, showed an initial slow rate, accelerating to an intermediate maximum rate which then decelerated to the completion of the reaction; similar curves have been obtained by Wever and his collaborators.12 Other eutectoid decompositions show similar behavior: for example, the decomposition of the beta eutectoid in the copper-aluminum system, studied by Smith

Jan 1, 1939

By L. F. Bishop

The ore bodies of the Butte district1 are found in many different vein systems having many different structural characteristics; some are narrow with self-supporting ore but with weak walls; some are wide with weak or strong ore and weak walls; some of the veins dip steeply and others do not; some have well defined walls, and others, in the "horsetail" area, are mined to sample limits. Consequently, many types of stoping methods are used in mining these ores. The stoping methods used in the Anaconda Copper Mining Company&apos;s properties are the square-set and cut-and-fill. The square-set method is the principal stoping method used because, generally speaking, the ore and walls are weak, the ore is high grade, and good extraction is required. These square-set stopes may be classified as conventional, vertical slice, slot, timber rill, and Mitchell slice types. The conventional type square sets are those of various shapes and sizes, mined by horizontal slicing to the boundaries of the stopes. The rock is slid to the chute and the filling is moved by gravity. The ore and waste may be handled with a scraper when local conditions require it. The vertical-slice square-set system is the type used in narrow veins that are mined in vertical panels. The slot stopes are stopes in wide veins that employ a slot across the vein instead of a con- ventional chute to handle the ore. The timber rill is a type of square set in which the ore is mined as in inclined cut and fill but the square-set timber is used. The Mitchell slice is the type used for some broken or heavy ore blocks, or for pillar extraction between two converging slot stopes. The cut-and-fill method is used where the ore will stand without much support although the walls may be weak. The principal type of this method is the horizontal cut-and-fill, with mechanical scraping. The inclined cut-and-fill, or rill, stopes are used in some veins too narrow for scraping. The production from the various methods in use for the second six months of 1944 are shown in Table I. This paper deals mainly with the vertical slice and slot types of square-set stoping, because of their effect on production locally and their potential possibilities here and in other districts, with sufficient reference to conventional square-setting for comparison.

Jan 1, 1946

By H. Y. Hunsicker

A graphic method has been devised for three-di-mensional analysis of hot deformation and for correlating the amount and directionality of the deformation with resulting directional properties. Deformation is evaluated in terms of dimensional change ratios referred to three orthogonal axes. Since all combinations of the three ratios can be represented in a triangular coordinate field with logarithmic scales, a two-dimensional chart of extent of deformation and degree of asymetry is possible. The entire gamut of shape changes from upsetting through flat-rolling to rod-rolling is accommodated. The resulting coordinate system is a base upon which can be represented the properties of the wrought products measured in the directions of the axes employed fir evaluating the deformation. When property data are available for many types and amounts of deformation, a three-dimensional figure can be constructed, and the projection of this figure is referred to as a &apos;&apos;3d&apos;&apos; chart. Experience in using such charts to plan fabricating operations for a variety of thick-section forged and rolled products of heat-treated aluminum alloys has verified its practical value for optimizing directionality relationships. MechANICAL anisotropy of thick section products of heat-treatable aluminum alloys is recognized by producers and users of these products, and the extent of the directional differences is apparent in property tabulations included in handbooks, standards, and specifications.&apos; Attention has also been directed to the existence of important directional differences in the resistance of these products to stress-corrosion cracking. Metallurgical structure factors responsible for these directional differences include, among other possibilities, shape and alignment of grains, voids and nonmetallic inclusions (when present), volume fraction and spatial distribution of secondary phase particles and solid-state precipitates, crystal-lographic textures, and Bauschinger effect. The contributions of the individual factors vary with alloy composition, heat-treated temper, type of working process (forging, rolling, extrusion), and the amount and directional nature of the deformation. In general, the cast ingot used as the starting material for producing these wrought products exhibits only a modest degree of directionality. A monotonic and continuous transition from this nearly isotropic state with progressive hot deformation would appear probable, assuming that the working temperature is sufficiently high to cause continuous dynamic recovery. Several years ago a project was undertaken to evaluate the effects of hot deformation and metallurgical structures on the directionality of thick wrought aluminum alloy products, and the method to be described was developed as an analytical tool in this investigation. DIRECTION NOMENCLATURE The nomenclature system adopted by industry for the three mutually perpendicular directions employed in testing aluminum alloy products includes four terms: "longitudinal", "transverse", "long transverse", and "short transverse". These terms are conventionally related to the external geometry of the product but also by implication to the deformation and resulting metallurgical structure. Occasions arise in which through use of unusual fabricating methods, intentional or otherwise, the structure does not have the usual relationship to external geometry or may be very complex because of inhomogeneity of deformation throughout the piece. The longitudinal direction is generally parallel to the primary rolling direction or to the direction of extrusion. In the case of forging, it is parallel to the direction of maximum extension (not maximum "working" or "flow", as frequently stated). The term transverse is applied to any direction perpendicular to the longitudinal direction in a product having symmetry about the longitudinal axis, and generally, although not always, the deformation to produce these forms is nearly symmetrical in the transverse plane. This term then may be applied to a round, square, hexagon, or other polygonal, symmetrical shape produced by extrusion or rolling or by forging, if produced by a simple, symmetrical drawing procedure. The type of microstructure generally associated

Jan 1, 1970

By J. Szekely, V. Stanek

Heat and gas flow interactions in nonisothermal packed beds were examined in the paper. A study was made of the response of the system to a step or pulse change in the inlet gas temperature, with a fixed value of the overall pressure drop across the bed. Under these conditions the heat flow and fluid flow transients are coupled because the convective heat transfer rate is alfected by the mass flow rate of the gas which, in turn, for a fixed pressure drop will depend on the temperature profile in the system. The Problem was stated in terms of differential equations, which were integrated numerically. The parameters used in the computation were so chosen to reflect the operation of the stack region of blast furnaces and sinterbeds. The computed results showed that the pressure drop-flou1 relationships and the rate of progress of the temperature fronts (waves) were strongly interrelated and were also markedly affected by variations in particle size and in void fraction. MANY metallurgical processes involve the contact of solid particles with a gas stream in a packed bed arrangement under nonisothermal conditions. Examples are shaft furnaces, regenerators, pebble heaters, and the sinter process. Although the heat and mass transfer aspects of packed bed processing have been extensively studied, the associated flow phenomena and in particular the effects of nonisothermality on the flow, have received little attention to date. :In fact, most of the previous workers considered the flow rate of the carrier gas time invariant and independent of the heat or mass transfer processSzekely and carr2 have shown that the pressure drop-flow relationships in nonisothermal packed beds may be strongly affected by the temperature profile within the system. These authors have devised a method for relating the pressure drop to flow for a given temperature profile. thus providing an extension of the Ergun equation to steady nonisothermal systems. Finally, in a recent paper willmot3 examined the response of regenerators to externally imposed changes in the gas flow rate. Both these investigations were somewhat specialized since, in general, neither the temperature distribution nor the gas flow rate may be regarded as truly independent variables, thus the heat transfer and the fluid flow problems have to be solved simultaneously. The work reported here is divided into two parts: in Part 1 the general formulation is given and a detailed discussion is presented of fixed bed systems. Part is devoted to systems in which a gas and particulate solids are contacted in a counter flow arrangement. FORMULATION Consider a nonisothermal fixed packed bed, extending from through which a gas is flowing. The problem is to develop a relationship between pressure drop and gas flow (with the gas flow being the dependent variable) and to evaluate the rate at which a change in the gas temperature, imposed at the inlet, travels through the system. Let us consider an infinitesimal section of the bed and establish differential heat, mass, and mechanical energy balances over this region. In addition, relationships are needed describing the temperature dependence of gas density (equation of state) and the temperature dependence of viscosity. These may be written as: where c, and are constants. It is noted that in this formulation we neglected any temperature gradients within the solid particles, thus assuming these to be either sufficiently small or of sufficiently high thermal conductivity to meet this condition. The justification and consequences of this assumption will be mentioned in the discussion.

Jan 1, 1970

By C. H. Li, R. J. Stokes, T. L. Johnston

Dislocation half-loops, artificially introduced by sprinkling with carborundum, were subjected to stress using three-point loading. The different stages of loop expansion and multiplication were then correlated with the macroscopic stress-deflection curve. Loop expansion started at approximately one-third of the "yield stress," defined here as the motivation stress. Above one-half of the "yield stress" simple multiplication commenced while about two-thirds of the yield stress gross multiplication developed short slip-line segments. These values were not affected by the age of surfaces exposed to both dry and wet air. Slip was not detected on unsprinkled crystals below two-thirds of the "yield stress." Thus the stress to activate intrinsic sources, defined here as the activation stress, was approximately twice the motivation stress. This relationship was independent of the strain rate used. It is concluded that lattice resistance takes the form of a viscous drag rather than a static type of force. THE importance of surface condition and environment as one of the more significant factors controlling the mechanical properties of ionic solids has recently received renewed attention.1-4 In some materials, notably the alkali halides, exposing freshly cleaved specimens to the atmosphere results in a progressive hardening and embrittlement of the crystals. This has been attributed to the surface layer becoming "aged," thereby restricting the motion of dislocations in such a way that pileup and eventually fracture results. It is necessary therefore in studying the mechanical properties of ionic crystals to inquire first into the density and distribution of dislocations in the normal cleaved surface and to understand the role these dislocations play in the onset of plastic flow. Knowledge of the effect of environment on this behavior will then assist in understanding the mechanism of embrittlement on aging. In the work reported here a method is described for studying the initiation of plastic flow from dislocation sources in the surface of magnesium oxide crystals. Preliminary results are described of the influence of surface age on this behavior. EXPERIMENTAL TECHNIQUES The magnesium oxide used in this investigation was obtained from the Norton Co. and had a nominal purity of 99.5.pct. Single-crystal specimens, having dimensions typically 1/4 by 1/8 in. cross section and 1 in. in length, were prepared by cleavage over (100) planes from the parent crystal. They were deformed under three-point loading with 3/4 in. spacing between the two end supports and a constant rate of deflection at the center of 0.001 in. per min. The maximum strain rate therefore was 1.5 X 10-5 sec-1. Reasons for choosing this particular form of loading will become apparent in a later section. In addition, a number of confirmatory type tests have been performed at higher loading rates where the maximum strain rate was increased to 1 x 10-3 sec -1. Following deformation the crystals were etched to reveal the dislocation distribution. In a previous paper5 we described a satisfactory etching solution consisting of 5 parts of saturated ammonium chloride, one part of sulfuric acid, and one part distilled water. Immersion of the crystals for 1/4 hr at room temperature developed reproducible conical etch pits at the points where dislocations emerged through the surface. It should be mentioned that dislocations freshly introduced by room temperature deformation gave sharply pointed etch pits which generally distinguished them from the almost flat-bottomed pits obtained on "grown-in" dislocations. The distinction is obvious in the photomicrograph included in Fig. 5(b). Annealing crystals at 1000°C for 12 hr on the other hand gave sharper etch pits on the grown-in dislocations and the distinction was no lower -possible; a similar observation has been reported for lithium fluoride. We have succeeded furthermore in chemically polishing magnesium-oxide crystals. Boiling in fresh 85 pct ortho-phosphoric acid for only 1 min resulted in a microscopically smooth surface which could again be etched to reexamine the dislocation distribution. This boiling time was sufficient to remove the surface damage introduced by cleavage (see next section). SURFACE DISLOCATION SOURCES There are a number of ways by which dislocations may be introduced into cleaved surfaces to act later

Jan 1, 1960