By Eiichi Kuzuno, Atsushi Shibayama, Toyohisa Fujita, Kazuo Koike, Toshio Miyazaki, Hitoshi Masuda

"A solid sulfur is more useful to recover and store than a sulfuric acid as a by-product in the zinc hydrometallurgy. In this experiment a zin concentrate (sphalerite) was leached with ferric sulfate at about 373 K for 3 to 6 hours. Zinc was leached more than 95%. After a solid-liquid separation, the leached residue contained solid sulfur was obtained. The particles in the residue were dispersed by lignin and the solid sulfur of approximately 85% was recovered as float product by a flotation with frother in the pH 4. The dried float product was heated at 413K for 2 hours. The pure solid sulfur was recovered. On the other hand in the leached liquid a zinc oxide was ·added and ferrous .iron was oxidized to ferric iron by blowing oxygen. This ferric iron was returned to the zinc leached process after solid-liquid separation.IntroductionZinc concentrate is usually roasted as pretreatment in zinc hydrometallurgy and the produced S02 is changed to sulfuric acid. However, recently in Japan the utilization of sulfuric acid has been limited and it is more costly to store. Instead of producing sulfutic acid the solid sulfur recovery has been examined by direct leaching of zinc_ concentrate in this experiment.In the direct leaching, several kinds of effects have been studied for leaching of sphalerite in ferric sulfate solution. The addition of lignine siilfonate1 • 2) and fine· grinding3) increases the · speed arid leaching fraction of sphalerite. The leaching ratio depends on impurities in sphalerite ores4 • 5). Here, the zinc concentrate is leached ferric sulfate solution under atmospheric pressure at 373K. The solid sulfur in leached residue is separated as float products from other solids by sink-float separation and flotation. The sulfur in float products is purified by evaporation at 413K and recovered."

Jan 1, 2000

By Serdar Aksu, Fiona M. Doyle

"CMP will be an essential process in the production of integrated circuits containing copper interconnects. This study aims to improve our mechanistic understanding of the role that organic chelating agents might play in the reactive slurries used in copper CMP. Copper dissolution behavior in EDTA arid glycine was first examined by producing potential-pH diagrams for the copper-water-EDTA and copper-water-glycine 'systems. The results of potentiodynamic polarization experiments were then considered in light of these diagrams. . In-situ polarization experiments were conducted to gain insight into the electrochemistry of copper during dynamic polishing in slurries prepared from EDT A and glycine.IntroductionCopper has recently started to replace aluminum as the interconnect metal in integrated circuits. Copper interconnection offers faster and more reliable integrated circuits due to its higher electrical conductivity and superior electromigration resistance (1). The damascene method is used to form multilevel interconnects in the manufacture of integrated circuit devices with copper metallization (2, 3). Copper is deposited by CVD or electroplating into vias and trenches etched in the interlayer dielectric (IDL), over a diffusion barrier usually made from titanium, tantalum or their nitrides. Chemical mechanical planarization (CMP) then prepares the wafer for the next deposition step, by removing excess copper and planarizing the surface. During CMP, the wafer is rotated and pressed against a rotating platen covered with a polishing pad. Chemically active slurries containing submicron size abrasive particles (Si02, Al20 3, ceria, diamond, etc.) are applied. Both the mechanical action of the abrasive particles and the chemical action of slurry constituents remove material from the wafer surface. Planarization results because material is removed faster from protruding regions on the surface than from recessed regions. Since CMP can globally planarize .the entire wafer, it has become one of the key technologies for producing integrated circuits with copper metallization."

Jan 1, 2000

By Fu-Shen Zhang, Mengjun Chen, Jianxin Zhu

"In the present study, different types of cathode ray tube (CRT) glasses were examined by sequential extraction combined with TCLP to provide possible explanations for how Pb and Ba leach out from the waste CRT glasses and to give possible reasons for why they leach out. Sequential extraction results showed that Pb and Ba in the CRT glasses dominanfly presented as the residual fraction. The exchangeable fractions of Pb and Ba were extremely low, less than 0.01 % of the total content, but they were higher than those required by the regulation limits, 5 and 100 mg/L for Pb and Ba, respectively. TCLP tests of the original CRT glasses and CRT glasses residues after each step of sequential extraction demonstrated that the extremely high leaching toxicity of CRT glasses mainly caused by its exchangeable and carbonate fractions of Pb and Ba.IntroductionIn recent years, the amount of cathode ray tube (CRT) contained monitors or TV sets in the market were sharply reduced, since they were substituted by novel and better electronic and electric equipments such as LCD and PDP, leaving huge amount of end-of-life CRTs. 50-85% of the total weight of this kind of computer monitor or a TV set is glass[1,2], which was classified to three categories according to their chemical compositions: black & white glass (BW), color panel glass (CP) and color funnel glass (CF)[3]. In order to provide shielding from X-rays generated during the picture projection process, lead, barium and strontium oxides were used in the glass. In general, a color CRT contains 1.6-3.2 kg of lead . Therefore, these glasses have attracted wide and tense attention due to the potential risk to the environment and human health."

Jan 1, 2011

By František Molnar, Zsolt Szentirmai, Juraj Schmiedl, Felix Sekula

"Hydrometallurgical nickel production in Sered Nickel Plant (Slovakia) that treated roasted Albanian ore left behind a considerable amount of the solid leaching residue. About 6 million tons of this fine-powder residue containing approximately 52 wt.% of iron in the form of oxides is to the present day stored in a stockpile. However, its iron content makes it a potentially interesting secondary raw material for iron production. This secondary raw material is not, unfortunately, suitable for direct treatment in iron and steelmaking processes.This paper presents results of the laboratory tests of pyrometallurgical method of processing of the leaching residue by its roasting and subsequent refining melting. The objective of the selective reducing agglomeration roasting was to reduce iron oxides and to simultaneously avoid reduction of chromium oxides and silica. Refining melting is carried out in an inert atmosphere. The products of melting are technically pure iron and slag.IntroductionThe leaching residue stockpiled on waste dump near already non-existing Nickel Plant Sered, Slovakia, is considered to be one of the most important environmental burdens in this country. The 40-years of an on-going effort focused on finding the methods for extracting metals and thus remove the waste dump have not been successful [1,4,5,6]. From the literature survey it is evident that past investigations have been following three main routes:1.Removal of chromium by mineral processing methods prior to its metallurgical treatment to achieve final chromium concentrations below 0.3 wt.%.2.Pelletization of solid leaching residue and its subsequent reduction in blast furnace and steelmaking plant and simultaneous removal of chromium.3.Pelletization of solid leaching residue followed by metallurgical processing of preliminary reduced semi-product in electric arc furnace (EAF) accompanied by partial reduction of chromium."

Jan 1, 2008

By Baokuan Li, Fang Wang, Meilong Shan

"As the advantage of uniform bus loading, the electroslag remelting (ESR) furnaces with three - phase installation by delta or star connection are mainly used to produce the large or super large ingot. The electrical efficiency is significantly improved as the short circuiting through the molten slag. However, little is found about fiindamental research on the electromagnetic field of the ESR system with three -phase installation. A three-dimensional (3D) finite element model was developed to simulate the current density, magnetic field, electromagnetic force and Joule heating for a system of electrode, slag and ingot in the ESR system with three -phase installation.IntroductionThe metallurgical performance of the ingot is the fundament and precondition to obtain the large forging of high quality, which has a critical role in the producing of forging. The electroslag process (ESR) to product the metal materials of high homogenization and clarity become more and more popular[1].The electroslag process is a special smelting technology of producing small ingots, which originate in 1950[2].At present the three, four or six electrode is used in large scale electroslag furnace. It has been found that the deeper molten pool and the wider of the two-phase zone with only one large diameter of electrode to product large ingot effect the solidification microstructure of ingot[3]. However, the molten pool becomes shallow relatively with several electrodes producing the large ingot, which is benefit to the solidification microstructure of ingot. Three electrodes electroslag remelting furnace take the three phase equilibrium power supply to making the load and electric power network balance, avoiding the distortion phenomenon induced by single phase power supply and saving electric power. It also can uniformize the distribution of heat source."

Jan 1, 2012

By Alexander V. Derevyanko, Victor P. Popov, Alexander I. Raitchenko

"If an electric current flows along some electroconductive suspension in columnar form the solid particles are 'experienced thermal, mechanical, and electromagnetic influences.The objects were suspension Sn (liquid) - Ni-Cr-Mo-W alloy (solid particles). This is refractory alloy on the Ni base. The direct constant current (with density -106 A/m2 ) flowed through the named suspension during 180+300 sec. At the beginning of experiments samples were ones containing particles suspended uniformly in volume. Although density of solid particles was ~9x103 kg/m3 , i. e. higher than density of liquid Sn (-6.8x103 kg/m3 ), after end of this processing, the non-uniform distribution of particles in volume of samples was observed: concentration of Ni-alloy particles in lower part was smaller than their concentration in upper part of samples, and simultaneously their concentration is increased near outer surface. There was probably the natural convection of Benard-Rayleigh type which had carried, so lid particles upwards, and, in same time, there was the action of spatial Lorentz-forces directed to center forcing the radial movement.The knowledge of named phenomena can be useful for elaboration of technology of gradient dispersed materials and development of some materials science fields.IntroductionThe liquid metal with the electric current or under the alternating magnetic field is experienced compression. This action causes the pressure within metal and the change of the surface of the metal column (see, for example, [1-4]). One of results of such an electromagnetic compression is extraction of the foreign solid particles from a cylindrical liquid sample to surface in the radial directions. However, more complicated paths of the inclusions are observed under some conditions of electric treatment."

Jan 1, 1999

By Roger Wilmoth

Exposed, open pit mine highwalls contribute significantly to the production of acid mine drainage (AMD) thus causing environmental concerns upon closure of an operating mine. Four innovative technologies were evaluated under the U.S. Environmental Protection Agency?s, Mine Waste Technology (MWTP), Prevention of AMD Generation from Open-Pit Highwalls Demonstration Project. This project is funded by the U.S. Environmental Protection Agency (EPA) and jointly administered by the EPA and the U.S. Department of Energy (DOE) through an Interagency Agreement. The objective of the field demonstration was to evaluate the technologies ability to decrease or eliminate acid generation from treated areas of the highwall in comparison an untreated highwall area. The field demonstration was performed at the Golden Sunlight Mine (GSM) a subsidiary of Placer Dome U.S., located near Whitehall, Montana. GSM is an operating gold mine. The highwall at GSM was divided into five plots measuring 15.24 by 15.24 metres (m) and each technology was assigned a plot with the fifth plot being used for comparison as a background control plot. The four technologies were spray-applied. The applied insitu treatment technologies included: 1) A modified, furfuryl alcohol resin sealant, utilizing wood and agricultural by-products to coat the rock surface. 2) EcobondTMARD, a phosphate based process that forms a stable, insoluble compound, coating the rock surface. 3) Two ARD passivation technologies, magnesium oxide and the Dupont technology developed to create an inert layer/coating on the pyrite, preventing oxidation. The technologies were evaluated using the following methods: 1) ASTM D 5744-96, Accelerated Weathering of Solid Materials using a Modified Humidity Cells, 2) mine wall residual wall rinse sampling, 3) microscopy, and 4) core drilling followed by water injection testing.

Jan 1, 2003

By Robert Kozicki, Eric Graham, George Wrightson

"IntroductionThe manufacture of Ferro Chromium involves the smelting of various ores and fluxes to produce the metallic product.Slag is inherent in the process. It has a much lower density than the metallic FeCr. Some chrome may be trapped in the slag as either FeCr or Cr203.Previous methods to estimate the slag in the FeCr have revolved around separating the slag and metallic portions by exploiting the differences in density. The downside with that procedure is that material will often contain pieces that are adhered FeCr and slag. The Metallic FeCr may also be completely encapsulated in the slag.An alternative and more precise method involves calculating the slag content based on chemical analysis of Mg and Al. The Mg and Al will be at relatively low levels (less than 0.1 % ) in the Metallic FeCr pieces and considerably higher in the slag (3% or greater). The overall sample will have a proportional amount and is calculated using simultaneous equations with the assumption there is only one kind of slag and one kind ofFeCr present. ""Pure"" slag and ""pure"" FeCr are needed in order to determine the Mg and Al in each. The detemlination of the Mg and Al in the overall sample would then be used to calculate the amount of slag.When the particle size is small, it is difficult to sample and get ""pure"" pieces of the slag and FeCr of sufficient quantity to perform a proper analysis. Often, historic data is used but that is dependent on the source of the FeCr and the materials used in its production. Mg and Al levels in slag can vary between 3% and 20% in different FeCr slags depending on their origin."

Jan 1, 2013

By Anne C. Chinellato, Alejandra T. Soria, Nelida L. del Mastro, Amanda C. S. Pereiral, Esperidiana A. B. Moura, Anibal V. Abreu

"This work presents a comparative study of the thermo-mechanical and morphological properties of sugarcane bagasse fiber/HDPE composite treated with electron-beam and gamma radiation. The composite samples obtained by extrusion and injection molding processes were irradiated at 50 and 90 kGy using either a 1.5 MeV electron beam accelerator or gamma irradiator EMI-9, at room temperature in presence of air. The irradiated and non-irradiated samples were submitted to mechanical and MPI tests, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), scanning electron microscopy (SEM), sol-gel analysis and X-Rays Diffraction (XRD) and the correlation between their properties was discussed. Improvement of the bagasse fiber/HDPE composite properties, using electron-beam or gamma radiation, was found.IntroductionResidues of sugarcane bagasse fiber are widely produced in Latin America and other countries: in Southern Africa, Egypt, South-Eastern Asia, India, China, Australia, Cuba, among other producers, as by-products of the sugar and bioethanol industry. The sugarcane industry in Brazil and Uruguay is well established and expanding with large potential to increase the production of sugarcane bagasse in the next years [1-3]. Although the major portion of the bagasse is currently burnt for energy supply in the sugarcane industry, the disposal of this byproduct is still inefficient and, consequently, it is critical for agricu1ture profitability and environmental protection. Sugarcane bagasse is a lignocellu1ose fiber mainly constituted by around 46 % cellu1ose, containing hemicellu1ose, lignin, fat and waxes, silica and other elements [3, 4]. Studies have reported that sugarcane bagasse can be used to produce thermoplastic polymeric composites with excellent properties for many applications. [5-8]. Based on this survey, the transformation of bagasse into high quality industrial products, such as bagasse-polymer composites, can provide its more effective utilization."

Jan 1, 2012

By R. P. King

The linear intercept distributions provide unambiguous and accurate characterizations of the texture of mineralogical materials. The relation between the measured linear intercept distributions and the spatial correlation function is shown to be given by: in the Laplace Transform domain. The linear intercept distributions of the two phases in a low- grade chromite-serpentinite ore were measured. and the spatial correlation functions for both phases were evaluated using the above relation. The correlation functions are the primary relations for integral geometric models of mineralogical texture and this work demonstrates the relation between the 10 stereological model and the 3D integral geometry model for mineral liberation.

Jan 1, 1991

By G. Gomathi, K. Asokan, K. Subramanian

An electrochemical reactor with anode and cathode chambers separated by a composite perfluoro polymer cation exchange membrane was designed, fabricated and used for the reduction of dissolved carbon dioxide under ambient conditions to formate. The flow reactor enhanced the mass transfer of carbon dioxide compared to the batch reactor. Experiments were conducted using two different perfluoro polymer membranes - Nafion 961. Efficacy of CO2 reduction on various cathode materials (Cd, Pb, Sn and Zn plated stainless steel woven mesh) were determined. Optimum values of flow rate and current density were evaluated for the energy efficient formation of formate in aqueous KHCO3 (pH 7.5-8.5) buffer solutions.

Jan 1, 2008

By T. Shibasaki

There is a strong demand in the photo industry to the higher quality of refined silver. Osaka Refinery produces about 27 mtpm of refined silver mainly from copper refinery slimes. Product quality is attained by controlling the impurity level in electrolyte. Copper is cemented with silver oxide and palladium is precipitated by a chelating agent. Both processes were operated previously in batchwise for treatment of bled out electrolyte, Recently these processes have been improved and made continuous to cope with the increased impurity.load. As a result the grade of fine silver has been maintained steadily at Pd < 3 ppm and Cu < 5 ppm.

Jan 1, 1989

By R. P. Rao

In rare earth (RE) based phosphors, high luminous efficiency is possible due to their restricted emission limited to specific narrow bands. In general, these phosphor materials consist of RE ions as activators/sensitizers and/or hosts. Development of various phosphor host matrices such as alkaline earth chlorophosphates, aluminates and silicates activated by Eu(2+) as blue component, borates and phosphates of lanthanides and alkaline earth aluminates doped, with Ce/Bi and Tb as green component and Eu(3+) activated yttrium oxide and vanadate as red component has been described. Luminescent characteristics, color coordinates and suitability of these phosphor materials in high efficiency new generation lamps are presented and discussed.

Jan 1, 1989

By P. Ruz

A melt transfer ladle was 3D modeled by means of a mathematical fluid dynamics and heat transfer program. Internal temperature profiles were calculated as a time function for a normal ladle and for a pre-heated refractory lined ladle. It was shown that in a normal ladle the molten metal cools down quickly forming accretions. By using an inner lining there are practically no accretions build up within a typical time of operation. Therefore, by applying a refractory lining to a melt transfer ladle and keeping it at a moderate to high temperature it is possible to reduce cold dope circulation in the smelter.

Jan 1, 1999

By K. C. Mills, P. N. Quested, A. P. Day, R. F. Brooks

"Methods have been developed to measure the physical properties of molten materials relevant to the fluid flow in high temperature processes. Data for the densities, viscosities and surface tensions of Al-, Ni- and Fe-based alloys are compared with (i) values for the pure metals and (ii) estimated values obtained from models making use of chemical composition of the alloy. Experimental values for metallurgical slags are also given and compared with estimated values.1 IntroductionPhysical property data has proved very useful in improving process control and product quality. For instance, in the continuous casting of steel the viscosity (TJ) of the mould flux is important since it determines (i) the optimum casting conditions, nVc = 2.5±1 dPas (m min-1) where V c is the casting speed and (ii) the level of slag entrapment (which leads to inclusions) in the metal. Thus data for properties like viscosity are exceedingly useful in understanding the process and the problems encountered and the causes of defects and problems.Another interesting development which has helped to increase our knowledge of processes and improve process control and product quality is the development of mathematical models of the fluid and heat flow in the process. These models have been developed to the stage where one of the prime requirements is for good physical property data for the industrial materials involved. Recently, Oxley [1] has shown that the use of reliable, experimental, property values for the commercial alloy in a commercial software package produced a significant improvement in the prediction of casting defects. Thus reliable property data are required for liquid metals but also for (i) liquid slags since many processes involve the use of a slag to refine and protect the metal or to lubricate the mould and (ii) refractories, sand and investment moulds."

Jan 1, 1999

By Vittorio Basilico, Marco Quattrone, Mario Bassan

"In Italian building market one of the reasons that often stop building contractors from not taking into consideration the possibility to recycle rubble from building is represented by the increase of costs for rubble separation. However the recycling of C&DW can also allow a decrease in disposal costs and a reduction in raw materials requirement.In this paper the results of a testing conducted on a case study through economic and technical analyses are presented.Results highlight that a wise management of demolition and disposal processes can generate a remarkable saving and that it is possible, on the other side, to achieve environmental benefits such as reduction of raw material consumption and dump life lengthening.IntroductionTwo major factors have been found to have considerably influenced the market of recycled aggregates in Europe and Italy: the EU and national regulations and environmental awareness. The market of recycled aggregate has grown in countries with limited natural resources.Waste disposal has also been one of the top EU political and environmental priorities. In the complex interaction between human activities and the environment, waste is proved to be one of the most environment-degrading products.In 1972 the European Commission introduced measures on waste reduction, reuse and recycling. In 2006, directive 2006/12/EC (European Commission) on waste was issued. It covers the scope of minimizing the waste, prevent hazardous waste, maximize reclamation, reuse, recycling and energy-recovery.No specific directive refers to management and recycling of construction and demolition wastes. However, in 1992 the European Commission listed debris among waste management priorities because of its growing amount.Only recently, effective environmental policies have been implemented in Italy, even though relevant environmental issues started rising as early as the beginning of the 1970s. In the 1980s the Government undertook the first significant measures to handle the waste management."

Jan 1, 2008

By Ali Unal, Ali I. Kahveci

Alcoa developed a fractional crystallization process some 30 years ago as a method to purify aluminum. Depending on the purity of feed metal, it has been commercially used to make 3N7-6N purity aluminum. As an extension of this technology, Alcoa has experimented with purifying various aluminum alloy scrap for the purpose of recycling. Purified aluminum alloy scrap can be reused for making the same alloy. This presentation will discuss Alcoa fractional crystallization technology and its application to alloy scrap processing. Process capabilities and the partitioning of eutectic and peritectic impurities during fractional crystallization will be discussed for the alloy systems investigated.

Jan 1, 2000

By Wayne Bell, Shivanand A. Borkar, Anish Upadhyaya, Matthew D. Andriese, Jiann-Yang Hwang, Zhiwei Peng

"A refractory ore body located in Michigan’s Upper Peninsula contains high concentrations of nickel and copper chiefly occurring in the minerals pyrrhotite, chalcopyrite, and pentlandite. Refractory ore bodies are difficult to treat by conventional mineral processing methods so microwave pre-treatment of the ore is employed to increase metallic-particle/host rock liberation by making use the differential thermal expansion properties of the mineral phases that absorb microwave energy. The Curie temperature measurement of metallic-bearing particles is in agreement with the known value for pyrrhotite occurring at 325°C. A nickel-rich iron sulfide mineral is found to be in occurrence and also appears to be magnetic under BSE imaging. It is shown the ore particles heat rapidly when exposed to microwave radiation for short durations of time mainly due to the high concentration of ferromagnetic mineral phases. Rapid heating causes thermal expansion of constituent mineral phases that produce cracks within ore particles. SEM imaging shows fracture occurring along grain boundaries and throughout host rock matrix. Ball milling experiments show an increased grindability of the ore resulting in a decrease in work index values.IntroductionCrushing and grinding operations consume 50-70% amount of energy used in mineral processing operations [1]. All these processes involve high energy impact of surfaces to develop compressive stresses that produce cracks to initiate breakage of particles. Microwave pre-treatment of certain types of ore might provide an energy savings to these type grinding processes by taking advantage of the tensional forces produced by selectively heating microwave absorbing type mineral phases. The heating of ore particles produces cracking by thermal expansion of the constituent mineral phases. Conventional heating has been investigated and shown to positively aid in grinding processes but determined energy inefficient to be used commercially."

Jan 1, 2011

By Wellington Pereira Inácio, Frederico Muylaert Margem, Artur Camposo Pereira, Sergio Neves

"Natural fibers are currently gaining attention as reinforcement of polymer composites for uses in engineering parts for automobile and building construction. In spite of environmental, economical and societal advantages, the natural lignocellulosic fibers are not as uniform in their dimension and properties as compared to synthetic. In recent works it was found that the variation in strength could be correlate to the equivalent diameters for several lignocellulosic fibers including the sisal fibers. In the present work an investigation on a possible correlation of the equivalent diameter with changes in density and elastic modulus was carried out. Precise measurements of the equivalent diameter, conducted in a profile projector, were correlated with the density and the elastic modulus by means of the Weibull statistic analysis. The results showed that an inverse correlation with the diameter also applies for both the density and the elastic modulus with a high degree of precision. SEM observation of the sisal fiber in structure and fracture aspects strongly indicate that defects and microfibril participation could be responsible for the inverse correlation.IntroductionAccording to Kalia [1], cellulose-based fibers are currently being pushed owing to their ""green"" image. Contrary to synthetic glass fiber, extensively used in our modem technology, these lignocellulosic fibers are renewable and can be incinerated at the end of the material's lifetime without adding pollution in the atmosphere moreover, the amount of CO2 released during incineration process is negligible as compared to the corresponding amount taken up by the plant throughout its lifetime. Even if an industrial processing equivalent of C02 release is added, the lignocellulosic fiber is considered neutral with respect to the emission of gases responsible for the global warming [2]."

Jan 1, 2012

By T. Inami

The chlorine leach of the anode slime was studied in order to improve the treatment process at the Niihama Nickel Refinery. The anode slime originates from the nickel matte electrorefining and, contains 3-5% of nickel as sulfides. A comparative study has been conducted on the filter cake resulting from the sulfur filtration of the molten anode slime. The kinetic factors of the chlorine leach such as temperature, grain size were defined. Under the optimized condition, 70-80% of the nickel is recovered from the slime or filter cake. On the basis of these results, the chlorine leach process for the treatment of anode slime has been established. The leaching plant has been installed and successfully operated since 1986.

Jan 1, 1988