By D. Chakraborty, Neeraj Kumar

"The study provides the comparative analysis of the performance of water only cyclones and hydrocyclone for iron ore fines processing at Joda Iron ore processing plant, Tata Steel. Joda iron ore deposits have higher proportion of kaolinite in the finer fractions and are meant to be separated with cyclones. The iron processing flowsheet of Joda comprises of water only cyclone for beneficiation of iron ore fines. Water only cyclones are used for the beneficiation of fines in the iron ore processing industry and have a larger cone angle compared to that of conventional hydrocyclones to enhance the density effect in the separation. They are aimed to achieve better product quality of underflow however; the desired result could not be achieved at the Joda processing plant. The water only cyclones were operating at the corrected cut-size of about 60 micron with an imperfection of 0.40 and water split to underflow was approximately 10%. The overall Fe recovery from the water only cyclones were 60%. Since the quality of fines produced from the water only cyclone couldn’t be improved, an attempt was made to process the fraction in the conventional hydrocyclone to achieve the desired product quality. The trial results indicated better product quality with the Fe recovery of 72% at corrected cut-size of 70 microns and imperfection of around 0.29. In view of above results it was recommended to replace the water only cyclones with hydrocyclones to achieve higher product quality of about 60% Fe content.INTRODUCTION Water only cyclones were installed at wet plant, Joda to process the classifier fines where the cyclone underflow is considered as concentrate and overflow is discarded as slime. Because of the lower capacity of the cyclones 30% of the classifier overflow was bypassed directly to thickener. Apart from this the quality of fines produced from the water only cyclone couldn’t be improved further hence an attempt was made to process the fraction in the conventional hydrocyclone to achieve the desired product quality and quantity. Hydrocyclone was installed at Joda after replacing stub-cyclone and came into operation on 23rd Aug’ 2017.The process variables of water only cyclones and hydrocyclones are tabulated below:"

Jan 1, 2018

By N. Dhawan

In the last decades, High Pressure Grinding Roll (HPGR) has gained significant importance in hard rock processing due to numerous metallurgical benefits such as energy savings, particle weakening, preferential damage of coarse particles, and preferential comminution-liberation. There are a limited numbers of lab-scale HPGR units throughout the world. The laboratory-scale HPGR machine at the University of Utah is first-ever lab-scale machine designed by late Dr Klaus Schönert, the inventor of HPGR. This HPGR is constructed with two counter-rotating hardened tool steel rolls, each 200 mm in diameter and 100 mm in width. The HPGR unit is equipped with eight sensors and a robust control system, which serves as an ideal system for fundamental studies and lab-scale testing. In HPGR operation, throughput, energy and product size distribution are intricately linked to specific grinding pressure, roll gap and rolls speed. The nip angle existing during the operation determines the volume of feed material above the rolls that is pulled into rolls without slip. In this paper, scale-up factors and some of the existing models have been reviewed. A number of experiments have been carried out with limestone and a slag material. The influence of operating variables and their complex relationship has been studied.

Sep 1, 2012

By A. I. A. Salama

In this paper, the problem of sedimentation and consolidation of poly-disperse suspensions is considered. The solid particles are assumed to be of different densities. If the sediment solids stresses are dropped out of the system equations and using the Richardson and Zaki hindered settling model, it has been found that in the limit, i.e., as time approaches infinity, the fluid is completely displaced to the top of the sediment zone. Furthermore, the species segregate completely with the heavier and coarser particles at the bottom of the sediment and the lighter and finer particles at the top of the sediment. Practical observations do not support these behaviors and physical-ly such behaviors do not exist; consequently, results of this kind in the literature are unrealistic. Here, a mathematical structure of the poly-disperse sedimentation and consolidation problem has been proposed. In this case the compaction zone species solids stresses are introduced in the momentum balance equations of the system. The species solid stresses in the sediment are constrained so that the system equations are consistent, i.e., sedimentation and consolidation of two or more identical species should behave as a mono-disperse system. Such a condition has not been recognized and imposed in some of the studies in the literature, which has led to unreliable results. Two practical forms of species stresses that satisfy the system consistency condition are here proposed. It should be noted that the study of sedimentation and consolidation of poly-disperse suspensions could result in more realistic suspension interfaces compared to mono-disperse suspensions, and could lead to more reliable engineering designs of tailings ponds. Predictions of sedimentation and consolidation in models of poly-disperse suspensions are demonstrated using published data.

Jan 1, 2014

By Richard A. Williams

The mineral processing community have been amongst the pioneer developers and early adopters of key platform technologies in analytical methods, chemistry, physical separation and advanced modelling. Fundamental research will continue to have a significant impact driven by the continued development of sustainable practices. Major drivers and challenges for change in our industry in the next two decades include: reduction in energy uses in processing; discovery of new energy materials; adoption of green chemistry routes; safeguarding of water resources; and demonstration of adherence to best practice at all times. With increasingly global mining enterprises, the provision of internationally accepted benchmarks for performance will continue to drive the creative process. This lecture highlights major opportunities around a new paradigm of Multi-scale Measurement coupled with Multi-scale Modelling, based on advanced sensors, communications and computing. Connecting real-time measurement sensors with dynamic simulation models opens up new horizons for visualising the process behaviour from an experimental and theoretical basis. Examples are given of the potential of this methodology and its implications for better design.

Jan 1, 2003

By Ye Junjian

The feed ore is the concentrate of low intensity magnetic separation of pyrite tailings, containing TFe47.47%, S19.41% and SiOpyrrhotite. The exploratory tests showed that using a process of flotation followed by magnetic separation could respectively obtain a sulphur concentrate of S 31.08% with a recovery of 82.89%, and an iron concentrate of TFe 59.97% and S 9.52%with a recovery of 30.93%. The reason of iron concentrates with high sulphur grade was that the sulphur grade of flotation tailings was 7.03%. So enhanced flotation for pyrrhotite was investigated in this research. Results show that when the natural pH of ore pulp varied from 5.5 to 6.0, a reagent combination of FS, LH, and BJ displayed the optimum flotation performance for pyrrhotite. After comparisons made on different flotation processing, the previous flotation flow of ?one roughing, one cleaning, one scavenging system and middling reprocessing?, was found, among others, to have the best flotation effect, as the grade and recovery of sulphur concentrate were 31.08% and 82.89%, respectively, and sulphur content of the flotation tailings was 7.03%. The above results indicated it was difficult to raise further the effect of flotation desulphurization. The authors therefore suggested that oxidizing roast should be adopted following the magnetic process for the purpose of further desulphurization. Besides, flue gas containing SO2 8.25%. And the valuable minerals are magnetite and 2 generated from roasting could be reused for sulphuric acid production. Keywords: pyrrhotite, enhanced flotation, desulphurization

Sep 1, 2012

By T. J. Chen

Vanadium-beard bone coal is one of important vanadium resources in China.To extract vanadium tailings from Stone coal is produced after extracted vanadium from stone coal through the roasting, leaching and other processes. About 120-150 tons of tailings will be produced in extracting 1 ton of vanadium pentoxide. A lot of tailings that are willfully piled up have caused serious environmental pollution and wasting of resources; it is therefore necessary to realize its resource utilization. This study increases the activity of vanadium tailings by means of alkali fusion, and then uses different alkali activators to react with vanadium tailings so that geopolymer with high value added is produced. Sample of geopolymer is acquired from a mixture containing vanadium tailings, alkali activators, water and a little sodium aluminate through compression-molding process under 20MPa pressure. After cured in room temperature for three days, the maximum compressive strength of the sample can reach 36.2MPa. XRD analysis indicates quartz, the major crystal phase in vanadium tailings is decomposed,and the activity of vanadium tailings is heightened. FTIR and SEM analyses show: structural change having an important impact on the mechanical strength of geopolymer occurred during the process of vanadium tailings generating geopolymer.

Sep 1, 2012

By A. D. Bas

Copper minerals present difficulties during the cyanide leaching of gold ores leading to excessively high consumption of cyanide (and oxygen) coupled with low extraction of gold. Copper cyanide species, if present at high levels, adversely affects the downstream processes such as the activated carbon adsorption and the effluent treatment. In this study, the extraction of gold from a copper-bearing gold ore by ammoniacal cyanide leaching was studied. Furthermore, ammonia leaching as a pretreatment process ahead of cyanide leaching was also examined. Only ~12% of gold was extracted by direct cyanide leaching of the ore. The addition of lead nitrate did not affect the leaching of gold. When ammoniacal cyanide leaching system was used, the extraction of gold was significantly improved to >90%. Similarly, the pretreatment of the ore by ammonia leaching was shown to lead to high gold extractions (98%), in subsequent cyanide leaching with significant reductions in the consumption of cyanide. This appeared to be linked with the ready dissolution/removal of copper during ammonia leaching.

Sep 1, 2012

By C. R. Mambote

Vanadium is an important metal that is used mainly in ferrous and non-ferrous alloys due to the high tensile strength, hardness, fatigue resistance and corrosion resistance. Vanadium consumption in the steel industry represents about 85% of the vanadium-bearing products produced worldwide. The primary sources of the metal are patronite, roscoelite, and mottramite. Vanadium has also been produced as a by-product of the uranium production program which uses carnotite ores as a source of uranium. Vanadiferous magnetite iron ores are used for producing vanadium as well. In addition, it is known that vanadium can be recovered from the ashes of crude oil and petroleum coke. The process for treating boiler residues, fly ash and petroleum coke is similar to the process used to treat spent catalysts and ores. However, some of these materials may contain high carbon that must be removed at specific stage of the operation. Several processes are available for obtaining vanadium from fly ash, such as roasting vanadium bearing materials in the presence of sodium salt. The salt roasted calcine is subsequently leached with an alkaline or acidic solution. To obtain a cal-cine from which the vanadium can subsequently be recovered, the carbon in the source materials has to be eliminated prior to the roasting process. Other processes use the conventional hydrometallurgical route, in which fly ash is leached with sulphuric acid to obtain an impure vanadium pentoxide. The impure vanadium pentoxide is then treated with a sodium carbonate solution under atmospheric conditions to subsequently precipitate vanadium as ammonium metavanadate. Actually, the salt roasting process is the only process used commercially. In the present study, the progress in the technology of vanadium extraction from secondary materials is reviewed. The perspectives and the challenges for new process development are discussed.

Jan 1, 2014

By K. Gonçalves

One of Vale?s sponsored research project is aimed at the implementation of a practical scale-up procedure for flotation. In this context, detailed flotation kinetics characterization is of critical importance. This work presents the results of a campaign aimed at characterizing flotation kinetic parameters with respect to particle composition. MLA analysis was carried out for 40 narrow-sized iron ore particles with known flotation time from a controlled flotation kinetic test. The iron ore sample studied (59% hematite and 41% quartz) comes from a mine in the southeast of Brazil and the type of reagents applied are the same as used in the plant. For the reagent conditions tested, the overall rougher concentrate (sink) yielded 79.1%, pure quartz and hematite recoveries to the froth were 56.0% and 4.8%, respectively. The results from the kinetic tests show that the flotation rate of the particles doesn?t vary much (~0.03s-1) with composition and that the fraction of floatable particles in each grade controls the separation action. The results show that the rate of flotation is controlled by transport and that the selectivity is controlled by the fraction of floatable particle of each phase.

Sep 1, 2012

By P. Gao, J. W. Yu

"Pre-concentration is a necessary step for upgrading low-grade iron ores, and its aim is to remove gangue minerals for improving efficiency of downstream separation process. The most important pre-concentration technique for iron ores, including hematite, siderite and limonite, is magnetic separation based on the appreciable differences between the desired iron minerals and gangue minerals in magnetic susceptibility. In this paper, the separation efficiency of one-stage low-intensity magnetic roughing combined with two-stage high-gradient magnetic scavenging for the pre-concentration of a low-grade hematite from Donganshan was investigated. It is a BIF type of ore containing hematite, magnetite and a bit of siderite, and an average content of Fe is about 34.6%. The effects of grinding fineness and magnetic field intensity for scavenging I and II were studied and optimized. The results showed that a magnetic preconcentrate assaying 42.7% with a recovery of 95.4% was obtained under the conditions of ore grinding fineness of -74 µm 70%, magnetic field intensity of 300 mT and 800 mT for scavenging I and II, respectively. Over 20% of the feed was rejected as the final tailings assaying 6.4% Fe. Meanwhile, the XRD, iron chemical phase and SEM analyses of different stage products revealed that hematite, magnetite and siderite could be recovered successfully by magnetic separation. However, some ultra-fine hematite particles (-10 µm) were difficult to be captured by magnet, and lost in the final tailing, resulting in lower iron recovery.INTRODUCTION Donganshan iron ore belongs to sedimentary-metamorphic iron formation called banded iron formation (BIF), which is formed in the Precambrian with a layered structure composed of ore bodies (Shen, 2012). Such type of iron deposit contains various iron-bearing minerals like hematite, magnetite, and siderite, suggesting it may be amenable to pre-concentration with magnetic separation. The pre-concentration process is effectively applied in recovering hematite, magnetite and siderite from iron ore, due to its benefits of further upgrading iron ore and improving separation efficiency. The most important pre-concentration technique for iron ore is magnetic separation, including low-intensity magnetic separation and high-gradient magnetic separation, based on the fact that there are appreciable differences between the desired hematite, magnetite or siderite and the gangue minerals in magnetic susceptibility."

Jan 1, 2018

By Tingting Li, Guodong Li, Dezhou Wei, Cong Han, Shuling Gao, Yanbai Shen

"The aim of this study is to solve the problem of tungsten leaching from scheelite concentrate using sodium hydroxide in the presence of phosphate by an autoclaving process, which is one of main development techniques for tungsten recovery. To understand the applicability and leaching performance of tungsten leaching from scheelite concentrate, the main work is to investigate the effects of leaching parameters such as initial concentrations of NaOH and Na3PO4, reaction temperature, stirring speed, liquid-to-solid ratio and reaction time on WO3 dissolution rate to obtain the optimal leaching conditions. The chemical composition and phase composition of the samples were evaluated by means of XRF and XRD. The content of WO3 in the leaching residue obtained via washing, filtering and drying was analyzed by thiocyanate spectrometric method. The optimal leaching conditions were found to be NaOH concentration of 6.76 mol·L-1, Na3PO4 concentration of 1.35 mol·L-1, reaction temperature of 180°C, stirring speed of 400 rpm, liquid-to-solid ratio of 2.0 and reaction time of 90 min. The results showed that tungsten leaching rate of 99.20% was reached under the optimal conditions. The technology exhibited superior leaching performance, which not only reduced the consumption of sodium hydroxide but also greatly decreased reaction time in comparison to a conventional autoclaving process. INTRODUCTION Tungsten is an important strategic metal, which is widely utilized in a variety of industries due to its high melting point, superior mechanical properties and heat-resistant performance [1-3]. The chief raw materials for the production of tungsten in nature are wolframite and scheelite [4, 5]. Among them, approximately two-thirds of the tungsten reserves contain scheelite deposits in the world [6, 7]. With the progressive exhaustion of high-quality wolframite resources, scheelite has become a predominant primary resource for the production of tungsten [8, 9]."

Jan 1, 2018

By G. J. Mei

Separation of hematite and iron-containing silicate gangue - aegirine by Flotation using fatty acid collector and (NH4)2SiF6 depressant was investigated in this paper. The flotation tests with single minerals show Ammonium hexafluorosilicate (AHFS) is a selective depressant for aegirine in hematite flotation in weakly acidic medium, which can strongly reduce the flotation recovery of aegirine in the pH range of 4~5 while has no evident effect on the flotation of hematite. The results of flotation tests with actual ores show the separation of hematite from aegirine gangue by forth flotation was possible, and good selectivity was achieved. Chemisorptions were observed on aegirine mineral surface treated by AHFS solution by using SEM and IR spectrum measurements. On the basis of coordination chemistry, a comprehensive mechanism, which reasonably explains the selective depression of AHFS for iron-containing silicate, is also proposed.

Jan 1, 2014

By H. Y. Ran

Magneto-flotation is a recently developing technology of mineral processing. This technology combines the traditional magnetic separation with flotation and provides a magnetic and buoyant force compound field to separate different minerals based on the differences of magnetism and floatability between useful minerals and gangue minerals. Magneto-flotation is applicable to separate ferromagnetic from nonmagnetic minerals, especially to separate magnetite from floatable gangue minerals. This magneto-flotation column is equipped with pulse electromagnetic field in the middle upper part, a bubble producer and upwell water inlet in the bottom. The pulse time of electromagnetic field in the column can be optionally adjusted and the maximum intensity of pulse magnetic field can reach 35mT. Pulse magnetic field can not only restrain magnetic minerals from entering into the froth layer, but also destroy the magnetic agglomeration to ensure a higher recovery and a higher concentrate grade. The results of experiments with magnetite show that pulse magnetic field has remarkable influence on flotation process. Compared with single flotation, magneto-flotation column can improve the recovery of magnetite by ten percent. After one time?s magneto-flotation processing, the grade of iron concentrate can increase from 65.4% to 69.5%, the content of silicon oxide in iron concentrate decreases from 7.4% to 2.8%, and the total recovery is above 96%.

Jan 1, 2014

By X. L. Song

A large amount of tailings in concentrators bring a series of problems to the environment and society. It is significant to reclaim the huge tailings and reuse them in industries in order to utilize mineral resources adequately. Primarily Lead-Zinc tailings with a certain quality of clay and feldspar were used to produce ceramic tiles by sintering method under specific technical conditions. By testing the properties of the ceramic tiles, it was shown that the amount of Lead-Zinc tailing used in the tiles was 60%~70%, and the mechanics properties were good. The optimum proportion parameters were Lead-Zinc tailing 60%, clay 35%, feldspar 5%, and the maximum flexural strength of tiles was up to 38.2MPa when it was sintered at 1090? for 30min. Its flexural strength, water absorption and thermal shock resistance reached the State Standard of GB/T4100.4. The product is suitable to be used in pavements and paths of parks.

Jan 1, 2014

By Kevin Galvin, Simon Iveson

Fine particles are the most valuable because they are the most liberated. However, they are also the most expensive and difficult to recover and concentrate. The Reflux Classifier is a novel invention that combines many of the virtues of existing fine particle separation technologies in a way that provides profound synergies. Multiple parallel narrow channels create a laminar-shear separation zone. The laminar flow provides a well-defined velocity gradient that exposes particles on the wall to a conveying velocity that is approximately proportional to their size, thus reducing the dependence of elutriation velocity on particle size. The high shear rate in these channels generates a hydrodynamic lift force that selectively lifts low-density particles off the channel wall and thus causes them to be preferentially conveyed out in the overflow. Particles that are not elutriated slide back down into the mixing reflux zone beneath the inclined channels which gives them multiple opportunities to re-enter the channels. The resultant suspension of both coarse and fine high-density particles in the fluidized bed zone at the base of the unit generates a strong autogenous dense medium that helps to direct large low-density particles back up to the overflow. The fluidization water also simultaneously de-slimes the high density underflow product. When placed in a centrifuge, the benefits of these features multiply with the improvements in capacity and selectivity that arise from high G-forces. When inverted, these features can be used to perform flotation well beyond the conventional flooding limit. Hence this invention platform has the potential to dramatically improve both gravity and flotation separation performance across the minerals processing industry.

Jan 1, 2014

By I. Nishkov, I. Grigorova, M. Ranchev, S. Dzhamyarov

"Chelopech concentrator (part of Dundee Precious Metals) is located in central-western Bulgaria. The current process plant utilizes conventional primary crushing and SAG mill grinding, copper and pyrite rougher and cleaner flotation stages to produce a marketable gold-rich copper and pyrite concentrates. As in the most processing plants, the pyrite depression is carried out alkaline media using lime. The subsequent activation of pyrite mineral is achieved by adding sulfuric acid, which has an adverse effect on the flotation equipment. Therefore, a series of laboratory flotation experiment for activation of lime depressed pyrite by ammonium salts, such as ammonium chloride (NH4Cl), ammonium sulfate (NH4)2SO4 and ammonium bicarbonate (NH4HCO3), have been conducted. The obtained results showed that ammonium bicarbonate proved to be the most appropriate reagent choice for pyrite mineral activation. These results are confirmed by X-ray photoelectron spectroscopy (XPS), performed to determine the surface chemistry of pyrite in its natural state, after lime treatment and subsequent treatment by NH4HCO3. The registered XPS spectra indicate that the hydrophilic phases on the pyrite surface could be efficiently removed by using the ammonium salt NH4HCO3. The industrial use of NH4HCO3 as an activator of lime-depressed pyrite is a possible alternative for sulfuric acid replacement as a most widely used pyrite activator. Flotation experiments with addition of 200, 400, 600 and 800 g/t from each of the studied ammonium salts have been conducted. Furthermore, the impact of the flotation pulp pH within the scope of 9.00 – 10.50 was also investigated. The obtained results from the laboratory flotation experiments, showed that the pyrite activation with ammonium bicarbonate is an excellent possibility for replacing the sulfuric acid as main pyrite activator reagent, in order to eliminate the gypsum accumulation during the flotation of pyrite in Chelopech concentrator.INTRODUCTION The Chelopech deposit, located about 60 km east of Sofia is one of the largest Cu-Au deposits in Europe. The ore have complicated mineralogical and chemical composition. The main ore minerals are represented by pyrite, enargite (luzonite), tennantite, chalcopyrite and bornite. The average copper content of the mined ore is about 1.1 % and the gold content is about 4.0 g/t."

Jan 1, 2018

By F. H. Wang

The Yinmao Lead-Zinc Mine Co. Ltd. has got 50 years of mining history. In recent years, the manganese grade in the flotation tailings has been continuously increasing. In order to make fuller use of the existing resources, as well as to increase the company?s economic efficiency, our company adopted the technique ?magnetic separation? and ?iron removal? to effectively recycle the manganese concentrate resources.

Jan 1, 2014

By N. S. Phala

Declining gold grades, mineralogical complexity of ore bodies, increasing input costs, more stringent conditions in the licenses to operate, and uncertain gold price dynamics combine to exert significant ongoing pressure on margins of gold producers. Innovative approaches of extracting the metal from its ores are required to realize value from existing and future assets. In a conventional gold processing plant, size reduction of mined ore to produce floatable or leachable product is a significant cost contributor. A step change in cost reduction will be attained if radically energy efficient grinding approaches can be developed, replacing tumbling mills. In the path towards that goal, some quick wins are possible through waste rejection before grinding, and pre-treatment of mill feed to reduce grinding energy demands. Gold locked in complex mineralizations puts pressure on margins by increasing cost per oz (typically high $/t and low metal recoveries) in the hydrometallurgical steps. Gold miners are primarily price takers. The current narrow range of gold uses (predominantly investment and jewellery) is not an entirely desirable state. Some diversification into commercial uses would potentially be a price stabilizer. In this paper, promising research directions, some not always fully explored in the gold metallurgy research space, are highlighted to stimulate radical innovation for substantial value enhancements. The author strongly believes a shift from a traditionally conservative and incremental innovation approach to a more aggressive one, across all aspects of the gold metallurgy value stream (processes to products), is what the industry needs. Keywords: gold metallurgy value stream, thiobaccilus ferroxidants, HPGR

Sep 1, 2012

By V. Ross

"The Upper Group 2 (UG2) reef in the Bushveld Complex in South Africa hosts an estimated 40% of the world’s Platinum Group Metal (PGM) resources. The processing of this ore via flotation poses two particular challenges: limiting the levels of chromite in the concentrate to reduce downstream smelting problems, and enhancing the recovery of ultrafine (typically -10 micron), liberated PGMs. Conventional ways of suppressing the entrained chromite, such as froth washing, is not effective in PGM operations, which are dominated by mechanical cells. The recovery of fine particles is hampered by low collision efficiencies with air bubbles, as well as oxidised surface layers especially in tailings operations. This paper documents the results of laboratory tests on a run-of-mine PGM UG2 ore, investigating the application of a pneumo-mechanical column (PMC) and its effect on PGM flotation and its selectivity with regard to chromite. A key feature of the device is the stage-wise release of aerated slurry from an agitated downcomer, thus creating conditions where the superficial velocity profiles of air and slurry change axially within the separation zone. This aids segregation of the silicates and chromite-rich fractions in the separation zone, concentrating the latter towards the bottom of the column and minimising its entrainment into the concentrate. Comparison of the performance of the PMC to that of mechanical laboratory cells under equivalent operating conditions showed improved PGM flotation kinetics and recovery. This was accompanied by a decrease in gangue recovery compared to the mechanical cells by more than 40%, thus doubling the final rougher concentrate grade from 50 to 100 g/t. Significantly, whilst the overall Cr2O3 recovery was reduced by more than 60%, the selectivity (PGM recovery vs Cr2O3 grade in the concentrate) was doubled.INTRODUCTIONThe Bushveld complex in the northern part of South Africa hosts the world’s largest reserves of Platinum Group Metals (PGMs), representing approximately 40% of the total PGE. It is characterised by three main PGM bearing reefs, namely Merensky, Upper Group 2 (UG2) and the Platreef. The Merensky and Platreef are dominated by silicates in the form of pyroxenites, and carry economically recoverable amounts of copper and nickel, in the form of chalcopyrite and pentlandite. The UG2 on the other hand is a chromitite ore with chromite as (ideally, FeO.Cr2O3) the most abundant gangue, often constituting more than 70% by mass with a PGM grade of around 4.5 g/t. Other key gangue minerals are pyroxene, feldspar and talc. The PGEs occur in a wide variety of minerals, with platinum and palladium sulphides typically accounting for about half of the total. Base metal sulphides such as chalcopyrite, pentlandite and pyrrhotite occur in only very minor amounts, accounting mostly for less than 0.1% by mass."

Jan 1, 2018

By Grant C. Lukey, Jannie S. J. van Deventer

"The environmental effects of the mining and mineral industry include destruction of natural habitats, changes in river regimes and water tables, and other serious ecological impacts. In this century, it is likely that water will become a critical resource, and in most countries the mining industry competes for a share of this resource. The Kyoto Protocol may at first seem only relevant to the coal mining and power industry, however, it should not be forgotten that the mining and mineral industry is a significant consumer of power. Therefore the ratification of the Kyoto Protocol by most developed countries and the introduction of a carbon credit trading scheme will impact on the industry by potentially increased costs in utilities and waste discharges. It is clear therefore that the mining industry faces many challenges in the coming years. The mining industry?s commitment to sustainable development needs to continue to evolve, in order to meet these challenges effectively. With the advent of globalisation of the industry, it is now an opportune time for the industry to gain international agreement on how they want the industry to achieve sustainability in future years; such a progressive approach is necessary, otherwise government will force the industry to change, which may not necessarily be the best outcome for the industry.INTRODUCTIONThe Earth Summit in Rio de Janeiro in 1992 was an opportunity for world leaders to assemble and discuss strategies and initiatives that provide for further industrial growth without adverse effects on the environment. The World Summit on Sustainable Development held last year in Johannesburg, South Africa, was an opportunity to evaluate those initiatives implemented over the past 10 years, and to set a new and sustainable direction for the future. It is clear that industrial and technology development will continue at a rapid pace in order to serve the needs of a growing world population, but it is essential that the course of this development is well planned, well executed, and that it is sustainable. In reality, while government officials and politicians continue to debate policy and international protocols, the environment continues to suffer and the effects of climate change and global-warming become more real each day."

Jan 1, 2003