R. F. WOOD,* Sandusky, Ohio.-I made a few tests of gun-metal specimens, after I noticed the results on quenching -reported by the Bureau of Standards. The data of one such test are given herewith. The bars were heat treated and quenched before they were machined, and in all cases they were brought up to 700° or 800°. They became extremely brittle,, showed almost no elongation, except such as was caused by the failure of the pieces to fit together after they were pulled, and the tensile stength was reduced from around 35,000 to about 13,000 lb. per sq. in. In addition, the weakening effect of the quenching seemed to be almost as marked when the bar was allowed to slowly air-cool from red to black, and then quenched, as it was by quenching directly from the red heat. Test Bars.-Rough size, 9/16 in. diam. over test section, grips 13/16 in. diam. Cast two in a flask, one on each side of a block 8 by 4 by 1 in. and fin-gated thereto from the grips but not from the test section. Poured with flask in inclined position, with gate to lower end of block and riser from upper end of each test bar. Bars were machined to ½ in. over the test section, after heat treatment. Casting the Bars.-Charge of 1500 lb. consisting of 400 lb. of new metals and 1100 lb. of G turnings and scrap was melted in open-flame oil furnaces and then poured into a 1-ton ladle. From the ladle 150 lb. was poured into a preheated No. 50 crucible, land from this the flasks of test bars were poured. The six flasks are indicated below by the numbers 1 to 6 and the bars in each flask by the letters a and b, thus 4a and 4h, for instance, were the two bars in flask No. 4.

Jan 12, 1919

GEO. F. COMSTOCK,* Niagara Falls, N. Y. (written discussion?).-This interesting paper throws additional light on a question about which differences of opinion have apparently existed in the past, and the writer would like to record in this connection the agreement of his experience with that of Primrose and Prof. Smart in regard to the effect of quenching on the properties of gun-metal bronze. The writer's results have been published, so that there is no need for a detailed report, here, but his in-vestigations resulted in showing that both gun metal and manganese bronze are ruined by quenching in water from a red heat, apparently because they cannot stand the strains produced by the sudden cooling. The lines, mentioned by Prof. Smart, in a polished and etched section of the quenched metal have also been noticed by the writer, who however has not found them any different in quenched specimens than in annealed specimens. Since they appear only after etching, it would seem most probable that they are merely grain boundaries in most cases, though Prof. Smart's idea that they are indications of strains is by no means impossible. Fig. 1 shows how these lines appeared on the author's speci-mens of annealed gun metal, etched with ammonia and hydrogen per-oxide, and magnified 100 diameters.

Jan 11, 1919

By Herbert H. Uhlig

ALTHOUGH the mechanical properties of high-carbon manganese-iron alloys, particularly the Hadfield manganese steels, have been established, the literature discloses discrepancies in the reported properties for the low-carbon alloys. Hadfieldlo summarized the existing data up to 1927, including the investigations of Guillet, Arnold, Strauss, Burgess and Aston, and reported his own values for alloys containing for the most part from 0.06 to 0.15 per cent carbon. He noted: From these comparisons it will be seen that while there is a broad and general agreement as to the character of the alloys at the different manganese percentages, there are disparities in individual cases, especially as regards the degree of toughness or brittleness displayed by an alloy with certain percentages and with particular types of treatment. These differences are not always readily explainable. Ib His data showed that alloys containing 4 to 10 per cent manganese water-quenched from 1000°C. were brittle and hard with maximum brittleness at about 7 per cent. Slight improvement in ductility was obtained with compositions from 10 to 17 per cent manganese. Alloys containing up to 17 per cent manganese slowly cooled rather than quenched from 870°C., he found, were slightly improved in ductility with significant improvement in alloys analyzing 4.1 and 4.8 per cent manganese. Recently Walters, Kramer and Loringa reported mechanical properties for alloys made up from electrolytic manganese and ingot iron and containing from 0.02 to 0.04 per cent carbon. They showed that a tempering treatment at 540°C. (1000°F.) for one hour significantly improved the ductility of compositions ranging from 6.7 to 20.7 per cent manganese. The differences of these compared with Hadfield&apos;s results they considered to originate in this tempering treatment plus the fact that Hadfield&apos;s alloys contained higher carbon and phosphorus (0.06 to 0.15 per cent C; 0.06 to 0.07 per cent P compared with 0.02 to 0.04 per cent C, <0.001 per cent P). In this paper it is shown that of the low- carbon alloys (0.02 to 0.03 per cent) containing from 3.3 to 21.5 per cent manganese moderately or rapidly quenched from 1000°C. some are brittle or ductile, depending on presence or absence of hydrogen. Hydrogen is readily absorbed at high temperatures, and much of it is retained when the alloys are cooled to room temperature. The presence of hydrogen in the range of composition from 10 to 18 per cent manganese is a major factor in determining relative ductility. At 22 per cent manganese, and also at compositions below 10 per cent manganese, factors other than or in addition to hydrogen play a role. These are discussed. Also data are presented to show that hydrogen absorbed by the high-carbon alloys of Hadfield composition is without effect on their mechanical properties.

Jan 1, 1944

By A. M. Gaudin

THE large increase in the use of selective flotation as contrasted with the collective flotation of a few years ago has focussed attention on the desirability of achieving accurate control of the pH of mill circuits. Although it is well-known that alkaline circuits result in dropping pyrite and that acid circuits conversely float it, but drop the gangue, there is little that is known, beyond question, ass to the action of the acidity or alkalinity of the circuits. A complete answer is not available at present but experiments -are now in progress at the University of Utah, whose aim is to find out what the effect is on recovery of a change in hydrogen-ion concentration and how this change is brought about. Broadly speaking, a change in hydrogen-ion concen¬tration seems to affect either the mineral surface, as was suggested by A. W. Fahrenwald in his paper "Surface Reactions in Flotation"1 (TRANS. 70, 647) or the attachment of the collecting agent on the mineral surface.

Jan 1, 1929

By V. G. Mooradian, John T. Norton

THE diffusion of metal atoms into the crystal lattice of another metal and the assumption of regular positions to form a homogeneous alloy are some of the most fundamental phenomena of structural. metallurgy. The mechanism of this process has been the subject of a great deal of study from many viewpoints, but the picture is still far from complete. It is generally believed that if one metal is to diffuse into another, the first must have some solubility in the second1. This means that the solvent must be able to accommodate the stranger atoms, either on points of its own lattice or in the interstices between, without losing its own crystallographic identity. It is also a general observation that cold-working is a distinct aid in the diffusion process, causing it to take place with greater rapidity at the same temperature or with the same speed at a lower temperature. There is considerable doubt, however, as to the real significance of the deformation in its effect on the diffusion mechanism. Several factors associated with the cold-working. may be responsible for the increased diffusion rate. The plastic deformation causes a distortion of the solvent lattice, which may be an aid in the assimulation of atoms of another kind. There are many references2 in the literature that suggest that some distortion or "loosening" of the lattice is necessary for atomic migration and that diffusion cannot take place in the undis-

Jan 1, 1935

By V. G. Mooradian

THE diffusion of metal atoms into the crystal lattice of another metal and the assumption of regular positions to form a homogeneous alloy are some of the most fundamental phenomena of structural metallurgy. The mechanism of this process has been the subject of a great deal of study from many viewpoints, but the picture is still far from complete. It is generally believed that if one metal is to diffuse into another, the first must have some solubility in the second1. This means that the solvent must be able to accommodate the stranger atoms, either on points of its own lattice or in the interstices between, without losing its own crystal-lographic identity. It is also a general observation that cold-working is a distinct aid in the diffusion process, causing it to take place with greater rapidity at the same temperature or with the same speed at a lower temperature. There is considerable doubt, however, as to the real significance of the deformation in its effect on the diffusion mechanism. Several factors associated with the cold-working may be responsible for the increased diffusion rate. The plastic deformation causes a distor-tion of the solvent lattice, which may be an aid in the assimulation of atoms of another kind. There are many references2 in the literature that suggest that some distortion or "loosening" of the lattice is necessary for atomic migration and that diffusion cannot take place in the undis-

Jan 1, 1935

By S. Tandanand, Powell. L. R.

The US Bureau of Mines assessed the geological effects on the ratio of maximum subsidence and extraction thickness, known as the subsidence factor, to develop a simple method for predicting the maximum subsidence. The study is restricted to the Northern Appalachian Coal Basin where data were collected from 13 coal mines. A model previously developed to relate the subsidence factor with the lithology and with the width and depth of working panels was used in the assessment. The result shows the possibility of determining maximum subsidence without resorting to a rigorous method.

Jan 1, 1985

By F. W. Hillnhutter

In plant tests with a 9.7 m hearth diameter high top pressure blast furnace the influence of disintegration of sinter during low-temperature reduction on blast furnace performance was evaluated. The blast furnace burden during the test period consisted of 74% self-fluxing sinter with a basicity of CaO/Si02 = 1.3, 15% pellets, 6% lump ore, and 5% recirculated slags. The sinter for the test was produced in a modern sinter plant. By changing the fuel rate and/or the MgO content at a constant basicity CaO/Si02 sinters with different low-temperature disintegration properties could be produced. The blast furnace was equipped with pressure monitoring devices at medium height of the furnace stack wall. This device provided in addition to the normal operating data readings of pressure losses in the upper and lower part of the furnace. The basic physico-chemical factors determining low-temperature disintegration are explained. The testing devices and the extent of quality control measures of sinter during the test period are outlined. Conclusions are drawn from the plant test in relation to sinter properties.

Jan 1, 1977

By Paul Weir

DURING the past decade, methods of producing bituminous coal in the State of Illinois, which ranks third in production among the states in which bituminous coal is mined, have undergone great changes. From less than one million tons in 1923, the strip-mine production has gradually increased to a high of 11,725,870 tons in 1937. From a negligible amount prior to 1927, the amount of coal mechanically loaded underground had increased to a high of 28,374,362 tons in 1937. The amount manually loaded in 1937 reached a low of 12,332,023 tons. In this same year, this state ranked first in strip-mine production, also in mechanically loaded production. For this reason a study of the influence of mechanization on location of production in Illinois may be helpful in anticipating what may happen in other producing states. The reason for the changes in methods lies in the differences in costs of production. The Bureau of Research and Statistics of the National Bituminous Coal Commission has made public the following costs of pro-duction by various methods in the State of Illinois (district 10) for the last nine months of 1937: all mines, $1.7602 per ton; strip mines, $1.4319; mechanical loading mines, $1.7457; hand loading mines, $2.1793; all underground mines, $1.8703. These are weighted averages for the entire district. Inasmuch as production in 1937 was reported from 58 counties scattered over two-thirds of the area of the state and from five different seams varying in thickness from less than 3 ft. to as much as 12 ft., it is apparent that the location of production must be influenced by the extent of mechanization possible in the various producing counties.

Jan 1, 1939

By J. A. Herbst, D. W. Fuerstenau

The effect of mill speed and ball load on the dry ball milling of dolomite is examined in the context of the batch grinding model. Observed changes in the parameters of the model are interpreted, as far as possible, in terms of the mechanics of particle motion in the mill. A parameter estimation scheme previously proposed by the authors is shown to provide the basis for a successful simulation of grinding behavior over a wide range of mill speeds and ball loads. Finally, a combination of experimental and simulated results is used to determine the optimum mill speedball load for closed circuit grinding in this mill-material system.

Jan 1, 1973

By Shun-ichi Satoh

STUDIES by many authorities have proved that nitrogen exerts an injurious influence upon iron and steel, but in the casehardening of steel by carbon, nitrogen has the advantage of accelerating the process of cementation. Its influence upon special steels is quite remarkable; it can produce the hardest layer ever known in metallurgical products-a fact hit upon by A. Fry and studied and ascertained by L. Guillet. As there have been very few investigations on the influence of nitrogen on special steels, the writer has listed important articles dealing with this problem and has conducted experiments on nitrification. He also has tested the influence of nickel upon the penetration of nitrogen in electric-arc welding.

Jan 1, 1929

By D. A. Rice, R. L. Stone

Studies of the possible effect of plant water chemistry on the strength of unfired iron ore pellets apparently have not been reported in the literature. Naturally occurring soluble salts were removed from magnetic concentrate filter cakes obtained from several iron ore concentrators. Laboratory balling tests showed that unfired pellets made from these "clean" filter cakes were 50-100% stronger than the usual unfired pellets containing the salts. The fact that certain chemical additives dissolved in the water used for balling "clean" concentrates decreased the strength of unfired pellets indicates that salts in the plant process water may be responsible for lower strengths. According to chemical analyses of plant process waters at these plants, calcium and magnesium are probably the most detrimental salts in the plant circuits. It is suggested that calcium, magnesium, and other polyvalent cations in the mill process waters ion-exchange for lower-valence cations in the bentonite and thereby destroy the electrostatic-charge bonding in the green pellet. Some practical guidelines are also included for plant balling practices.

Jan 1, 1973

By D. J. McAdam, G. W. Geil, R. W. Mebs

AS shown in previous papers by the authors 9-l7† the resistance of a metal to fracture, like its resistance to plastic deformation, is a function of all three principal stresses.‡ A technical cohesion limit is the technically determined resistance to fracture under a specific stress system. The technical cohesive strength thus comprises an infinite number of technical cohesion limits corresponding to the infinite number of possible combinations of the principal stresses. The technical cohesive strength, therefore, may be represented by a surface in a diagram with the three principal stresses as coordinates. As shown in previous papers, 9-I8 the technical cohesive strength increases with plastic deformation, with decrease in temperature, and with increase in the strain rate. The technical cohesion limit, therefore, is affected by the same factors that affect the flow stress, § namely, the stress system, plastic deformation, temperature, and the strain rate. More- over, the influence of each of these factors on the technical cohesion limit has been shown to be qualitatively similar to the influence of the same factor on the flow stress.9-18 Advance of knowledge about the conditions determining fracture, of metals has been retarded by the reluctance of some investigators to abandon preconceived ideas about how metals "should" behave. The incorrect idea is still prevalent that the conditions determining resistance to fracture are very different from those determining the flow stress. Attempts are still being made to express resistance to fracture in terms of a single parameter, such as a limiting value of the greatest principal stress, the maximum shearing stress, or the volume stress (one-third the algebraic sum of the three principal stresses). In these attempts, a sharp distinction is sometimes made between a ductile or "plastic fracture " and a "brittle fracture." In making this distinction, however, the meaning attached to the term "brittle fracture" sometimes is not made clear. The term could mean fracture after very little plastic deformation or it could be used to designate the type of fracture. An ordinary fracture of a ductile metal at room temperature starts as a cleavage, generally transverse to the direction of the greatest principal stress, but eventually changes to a shearing fracture. In some conditions, however, the metal fractures entirely by cleavage, with no evidence of plastic deformation during the fracture; the surface of such a fracture may have a

Jan 1, 1947

By S. G. Malghan, J. P. Van Dillen

Some uranium minerals are paramagnetic and hence are amenable to concentration by high gradient magnetic separation (HGMS). This paper describes effects of the HGMS parameters-pulp velocity, field strength, matrix loading, and magnetic field gradient-on the product recovery and grade. Unsatisfactory separation of uranium minerals by HGMS is related to ore-specific properties, such as lack of liberation, fine dissemination of uranium minerals, uniform distribution of magnetic minerals throughout the ore matrix, and interference of fine-sized slimes. Experimental techniques to identify and resolve some of these problems are outlined.

Jan 1, 1984

By L. E. Young

THE purpose of this paper is to start a discussion on: (1) methods of supporting the immediate roof, particularly of local areas of poor roof, during the mechanical loading of coal; (2) methods of increasing the rapidity of the movement of the mining faces so that, without the use of cribs, jacks, pack walls, and filling, there will be no danger to men, equipment,, and working places from the subsidence of the overlying strata. In the Pittsburgh district the application of mechanical loading devices in mines working in the Pittsburgh seam, has been retarded by the difficulties of holding and handling the draw slate. Normally the thickness of this slate averages about 8 in. but the hardness varies, and a cut of coal cannot always be loaded without placing posts or crossbars to support the slate. Locally, the slate may be thicker and special methods of support may be required. If crossbars are placed to hold the slate when the coal averages 5 ft. in thickness, the standard methods of transporting the coal cannot be followed, and the use of conveyors may be desirable. Very little information is available on the effect of increasing the rate of movement of advancing or retreating break lines or longwall faces. A few British publications have presented some data but all such data relate to longwall faces that have moved not more than 6 ft. a day. The most rapid rate of movement of longwall faces in Germany is 6 ft. per day. In the ordinary hand-loading mine in western Pennsylvania break lines on full retreat will move about 2 ft. per day. If loading machines are used under similar conditions the, rate of retreat may reach 4 ft. per day. In a mine where coal is loaded by hand on conveyors three shifts per day, the rate of retreat has ranged from 11 to 16 ft. per day, with an average of 13 ft. If mobile loading machines could be used to load on con-veyors on break lines, the rate of retreat should be increased substantially.

Jan 1, 1938

By Albert Sauveur

THE following experiments were conducted in order to study the influence of the rate of cooling through and below solidification on the dendritic structure (macrostructure) and microstructure of some hypoeutectoid steel. The steel selected was of commercial grade and had the following composition: C, 0.40 per cent.; Mn, 0.85; Si, 0.70; P, 0.099; S, 0.043. After melting in vacuum in an Arsem furnace, the various samples were allowed to solidify and to cool to room temperature as indicated in Fig. 1. Samples were thus obtained representing all possible combinations of slow and fast cooling through the various ranges of temperatures indicated, namely: (1), zone of solidification or primary crystallization, (2) zone of granulation, and (3) zone of secondary crystallization. The location of the different temperature zones in the iron-carbon equilibrium diagram is shown in Fig. 2. The authors adopted. Belaiew&apos;s notations. The designations of the various samples readily indicate their treatment, as will be apparent from Table 1.

Jan 1, 1930

By R. A. Vik, C. B. Daellenbach, W. M. Mahan

The influence of reduction roasting and thermal shock on the grindability of a refractory low-grade Michigan iron ore was examined in bench-scale tests. The quantitative effects of the various treatments were evaluated at three sieve levels, 48, 100, and 400 mesh, with ball-mill-grindability and work-index parameters as response indicators. Data from the testing program were statistically analyzed to isolate the effects of cooling rate, roasting temperature, mesh level, and ore chemical condition. All four variables were found to have an important influence on the grindability of the treated ore. Ore chemical condition and roasting temperature had the most pronounced effects.

Jan 1, 1972

By M. A. Mahtab, J. D. Dixon

The results of a parametric study of the influence of natural features (stress field, rock strength, and strength and orientation of fractures) as well as the influence of induced features (undercut span, boundary slot, and other boundary-weakening measures) on the cavability of an undercut block of ore in mining by the block- caving method are presented. The two-dimensional finite-element analysis technique was used for this study. A coarse "mesh," along with linear homogeneous assumptions for rock properties, was used to model the problem of initiation of caving in a block of ore. Interpretation of the test results suggests that weakening the "abutments" of the block as well as certain orientations of natural fractures exercise significant influence on cavability. These findings hold promise for immediate application to known situations in block-caving mines.

Jan 1, 1977

By William Plank

In practically all rock-excavation problems there is need for a careful study of the rock structure, its fault, cleavage or bedding planes, and even the texture of the rock itself. These studies should form the bases upon which an excavation method is selected and they should be carefully considered in predicting the amount and extent of the excavation. The need for such studies was forcibly illustrated in the problems involved in a cut made in 1929, along and underneath a 200-ft. high rock projection for a State-highway near the City of Easton, Pennsylvania. The rock mass was badly faulted and also contained a number of cleavage planes at approximately right angles to the fault planes. Much of this structure was visible and could have been studied and analyzed before&apos; the work was begun. The State had rigid specifications as to finished grade and slope of cut, which apparently were made without reference to the geologic structure. The contractor complied with the specifications, under the close inspection of the State engineers. A tunnel blast was, placed in the base of the cliff, with the result that 65 per cent more rock was broken than was intended by the specifications. About four years after the blast, the writers of this paper studied the circumstances surrounding the operation, to determine the cause of this excess excavation.

Jan 1, 1935

By Zavis M. Zavodni, Carl D. Broadbent

During the past 15 years, rock mass structural properties have become acknowledged as the focal point for rock slope design. Re- search into the methods for measuring and incorporating structure into the design effort has taken many directions and has produced a variety of useful techniques. Among the findings at Kennecott has been the realization that structure-controlled instability can be categorized as regressive or progressive depending on the relative geometries of slope and structure and on the strength characteristics of the structures. It was further identified that a failure condition can initiate as regressive and in time become progressive should external stimuli increase or structure characteristics be altered due to extensive displacements. The transition point has been shown to be a useful indicator of the expectable collapse time. This paper defines three fundamental failure types as dictated by structure and offers discussion on the practical value of such a classification to slope design and failure control. Several prominent examples of failures typifying the categories of structure- controlled instability are discussed. An application of f allure prediction based on the regressive-to-progressive transition point is described.

Jan 1, 1983