By D. A. Thomas, E. S. Meieran

Tungsten wires were examined by transmission electron microscopy after drawing and after high-temperature annealing. Drawn wire consists of highly elongated grains called fibers, whose long axis is parallel to [110]. Each fiber is ribbon-shaped, with the wide dimension of the ribbon parallel to (001) and the narrow dimension parallel to (110). Furthermore, most fibers are bent about [I10] and twisted along their length. The fibers are divided into cells, which in some cases contain a platelet substructure lying on (110) planes. The misorien-tations of these platelets accumulate to allow the macroscopic twist of the fibers. During annealing, several competing reactions occur, starting at different temperatures and progressing at different rates. Among these processes are fiber-boz~ndary migration, polygonization, dislocation rearrangement, and possibly impurity segregation. The fiber-boundary migration accompanied by the formation of transverse boundaries during polygonization leads to an equiaxed grain structure although recrystal-lization does not occur. There is a relationship between the flow stress of the wires and their average subgrain width in the form sy = s0 + kyd-1/2 . Also, there appears to be a relatio'nship between wire ductility and the formation of transverse boundaries during annealing at about 800°C. THERE have been many investigations of the structures and properties of tungsten wires1-4 due to their commercial importance for use as lamp filaments. The structural studies have so far been limited to optical microscope and replica electron-microscope studies. due to the difficulty of .-me- paring from wires thin foils which can be examined by transmission electron microscopy. However, this difficulty has been recently overcome,5 and it is now possible to examine tungsten wires by transmission electron microscopy as well as by other techniques. In this paper, the structure of drawn tungsten wire is described, as are the changes in the structure during high-temperature annealing. Some discussion of the relationship between structures and properties is also given. EXPERIMENTAL MATERIALS AND PROCEDURES Commercial 0.030-in.-diam doped tungsten wires drawn at progressively decreasing temperatures between about 1400° and about 800°C were examined. The composition, mechanical properties, and optical microstructures are described in detail elsewhere.' All experimental materials were vacuum-annealed for 10 ot 30 min at temperatures at 100°C intervals between 700° and 2000°C. Specimens were thinned for examination in the Siemens Elmiskop I electron microscope by the method of Meieran and Thomas.5 STRUCTURE OF AS-DRAWN WIRE The optical microstructure of as-drawn tungsten wire has been described by Peck and Thomas.7 They observed that wire in longitudinal section consists of highly elongated grains called fibers whose width varies between 1 and 10 µ, while in transverse section the fibers appear to be elliptical in cross section and bent about their common [110] wire axis. They explained this unusual appearance as being due to the drawing of a bcc material with a [110] texture, and predicted that the wide and narrow planes of the fiber cross section would be parallel to (001) and (110), respectively. The fibers apparently bend about the [110] axis during drawing to maintain grain boundary continuity during drawing. Transmission electron microscopy offers a way of checking these predictions as well as providing a more detailed picture of the wire structure. Figs. 1, 2, and 3 are typical electron micrographs of

Jan 1, 1965

By A. E. Austin, J. R. Doig

Ti-Cr alloys age harden after B-quenching by formation of an W-phase. The structure and orientation of this transition phase have been determined. The hardness ap-pears to be caused by strain in the B-matrix produced by concurrent enrichment of alloy content in the W-phase. EARLY studies of age hardening in B-stabilized titanium alloys revealed the formation of a transition phase named o' This phase was detected by X-ray diffraction in binary alloys of Ti-Fe, Ti-Cr,

Jan 1, 1958

By O. N. Carlson, E. D. Gibson, D. W. Bare

SEVERAL investigators have recently contributed to a clarification of the controversy concerning the allotropy of chromium. Ross and Hume-Rothery1 and Vasyutinskii et a1.2 have reported high-temperature X-ray data on unalloyed chromium from which they have concluded that no allotropic transformation occurs in this metal. Bechtoldt and vacher3 in their investigation of the Cr-Ni alloy system found no evidence for a transformation in chromium and Smart and Haynes4 in critically analyzing the data presented to date concerning this system could find no evidence for a eutectoid reaction in this system. Wyder and Hoch5 in research concurrent with our

Jan 1, 1964

By C. S. Smith, K. K. Ikeuye

In an earlier paper1 one of the authors called attention to the significance of the relative free energies of grain boundaries and interphase boundaries in alloys in determining the shape and distribution of micro-constituents. The ratio of the interphase and inter-crystalline boundary energies (that is, —?12, where ?12 is the energy of the interface between a crystal of phase 1 and a crystal of phase 2, and ?11 is the energy of the boundary between two crystals of phase 1) will be denoted by F. It is this ratio that determines, by the simple triangle of forces relation, the dihedral angle, ?, of phase 2 where it adjoins a boundary between two grains of phase 1. On a metallographic sample various angles are actually obtained because of the random orientation of the plane of observation, but the statistically most frequent angle is the true one. These basic principles were discussed in detail in the earlier paper. The experiments described below show the effect of both composition and temperature on ? and T for some alloys containing a liquid phase, and provide data on the rate of approach to the equilibrium angles in both solid and liquid phases. All the alloys were melted in a graphite crucible and cast into ingots 3/4 by 11/8 in. cross-section. Some of the aluminum alloys consisted of two immiscible liquids from which uniform castings could not be obtained. The amount of liquid phase varied locally to a considerable extent and the analyses were meaningless. Nevertheless, the composition of the liquid would not differ from that in an alloy of the intended gross composition, and the synthetic composition of the alloys was therefore used in considering the surface energy results. The ingots were given initial deformation by cold-rolling to 50 pct reduction, annealed, and given a second 50 pct reduction prior to cutting into small samples for heat treatment at the times and temperatures subsequently reported. The resulting micro-samples were carefully prepared metallographically and examined at magnifications of 650, 1280, or 2500. The objectives used were 21X, 0.40 NA (dry); 41X, 0.65 NA (dry); and 80X, 1.40 NA (oil emulsion). The appropriate angles were measured by rotation of the stage of a Bausch and Lomb metallograph to align the appropriate boundaries successively with a cross-hair in a micrometer eyepiece. About 250 angles were measured on each phase. Though the angles were read to 1°, the accuracy is probably not above 3°, because of uncertainty in setting the cross-hair tangent to the sometimes curved boundary. The corners of very small particles, particularly in early stages of adjustment after cold-rolling, were difficult to measure and the results were slightly dependent on the magnification used (compare Fig 1-C and 1-D). With particles of larger size and more nearly equilibrium shape, magnification made no difference (vide Fig 1-F and 1-G). The measured angles were grouped in 10° intervals (5° if ? was less than 20°) and plotted in bar

Jan 1, 1950

By S. Singh, R. C. Deshpande

RECENTLY metallographic studies of copper slugs recovered after firing shaped charges in deep containers of water were reported.' The present note describes the metallographic examination of a steel

Jan 1, 1960

By A. Soundraraj, S. Singh, R. C. Deshpande

THE detonation of a high-explosive charge having a metal-lined conical cavity (shaped charge) results in a fast-moving jet and a slow-moving slug.1-4 Clark and Bruckner reported the metallographic studies of a cast-iron slug. The present note describes the metallographic studies of a copper slug and discusses the principle of flow involved. The shaped charge consisted of a 5-cm diam cylinder of cast high explosive (60-40 RDX-TNT mixture) having a 45 deg and 0.16-cm thick copper cone. The copper (99.5 pct purity) had a grain size of 0.06 to 0.08 mm diam and a hardness of 65 to 75 Hv. These were fired into a deep container of water and the slugs were recovered undamaged. The longitudinal and transverse sections of the slug were polished, etched, and examined for mi-crostructural changes. Macroexamination revealed a radial grain flow inwards towards the center and a downward component of flow towards the base of the slug. Fig. 1 shows schematically the micro-structural changes observed on the longitudinal section of the slug. The region D near the apex and also along the outer surface of the slug was characterized by the presence of heavily deformed and twinned grains. Some of the grains were having bent or crossed twins, Fig. 2. The grain size in this region was of the same order as that of the

Jan 1, 1960

By J. H., R. W. Guard, Westbrook

In 1953 Kornilov and Mints' presented data on thermal expansion and electrical conductivity of the compound Ni3A1 which indicated the possibility of a transformation in Ni3A1 at about 600°C. The present paper gives results of some observations

Jan 1, 1960

By Kichizo Niwa, Toshio Yokokawa, Mitsuo Shimoji, Yoshihiko Watanabe, Satoshi Kado

A LTHOUGH a systematic research on diffusion in liquid metals has not been carried out, partial studies have been developed by various workers in several systems. A few recent papers among them have shown that this line of approach is quite useful for understanding the structure of the liquid state. Furthermore, it has been found in kinetic

Jan 1, 1958

By A. U. Seybolt

In part 111' of this series it was shown that during the selective oxidation of a 3 1/4 pct Si-Fe alloy in damp hydrogen, only silica, (observed at room temperature) as low cristobalite or low tridy-mite or both, was formed as an oxidation product. In some in- „ stances where the film was fairly thin (probably well under 100A) there was some suggestion of an amorphous form of SiO2. The present investigation of oxidation rate showed that the selective oxidation of silicon-iron can be rather complicated, and apparently impossible to rationalize in an unequivocal manner. In some temperature regions, notably near 800" and 1000°C, the data seem to obey the familiar parabolic rate law. However, at intermediate temperatures complications were noted, some of which are possibly due to the order-disorder reaction in the silicon-iron solid solution. IN an earlier report' it was shown that during the oxidation of 3 1/4 pct Si-Fe alloys in H2O-H2 atmospheres only silica films were formed in the temperature range from 400° to 1000°C in hydrogen nearly saturated with water at room temperatures, or at dew points as low as -45°C. In the work to be reported here, some observations are made on the rate of oxide film formation. As in the earlier investigation, electron diffraction patterns generally showed either low tridymite or low cristobalite or both, except for some very thin films. These sometimes showed diffuse rings, presumably due to a very small crystallite size, or in a few cases, diffuse bands probably caused by an amorphous film. EXPERIMENTAL PROCEDURE Vacuum-melted silicon iron made of high-purity materials was rolled into strips 0.014 in. thick, and cut into samples 1/2 in. wide by 1 in. long. Chemical analysis showed 3.2 pct Si and 0.002 pct C. All samples were surface abraded with 600-grit paper, were solvent cleaned, and then placed in an paper,apparatus containing a "Gulbransen type"2 micro-balance. Here the gain in weight of the samples of about 5 sq cm area could be followed as a function of time during the oxidation caused by the water in atmospheres of various controlled water-hydrogen ratios. The water-hydrogen ratios can most easily be described as varying from a dew point of 0°C (PH2O-p^2 = 6.2 x 10-3 , to K (P j -40°C (PH2O/PH^= 1.3 X 10-* Most of the experiments were conducted at the 0°C dew-point atmosphere because drier atmospheres caused so little gain in weight that the accuracy of measurement was poor. Because of this, only the data obtained at PH2O,/P,,,= 6.2 x X3 will be reported. The temperature range extended from 800" to 1000°C; and most of the oxidation runs lasted for about 24 hr. The reproducibility of any reading was about ± 1 ?, but the sensitivity of the balance was about 0.2 ?. The atmosphere, flowing at 200 cm per-min, was preheated to the furnace temperature before contacting the specimen. While the gas flow caused a measurable lift on the sample, it was ordinarily sufficiently constant so that it was not an appreciable source of error. X-ray and electron diffraction checks of the samples before and after oxidation showed no evidence of preferred orientation, either on the metal samples or on the silica films formed. EXPERIMENTAL RESULTS The data obtained are summarized in Table I, and some are given in detail in Figs. 1 to 4. In the fourth column of Table I, kp refers to the parabolic rate constant in the expression (?/cm2)2 = kpt + c [1] where ? = micrograms gain in weight kp = parabolic rate constant in units r2 /cm4 t = time in minutes c = constant It will be noted that in many cases no value for kp is given; this is because in these instances the data did not obey the parabolic rate law. The silica film thicknesses given in the last columns are values calculated from the weight gain, an average tridy-mite-crystobalite density, and by assuming a perfectly plane surface. Fig. 1 shows the data plotted in the form of Eq. [I], hence a linear plot indicates parabolic behavior. It has been frequently observed in the literature that

Jan 1, 1960

By J. J. Gilman

Zinc monocrystals, when compressed nearly parallel to their basal planes (within 20), deform in a new way; and certain deformation markings, called "-bands," are typical of this new mode. Characteristics of these bands are described. Mechanical behavior of low angle zinc monocrystals was investigated in some detail. Recrystallization did not occur upon annealing of banded specimens that were free of deformation twins. -Bands do not seem to be the result of nonbasal slip, but rather, a result of a microbuckling mechanism. u-Bands differ qualitatively and quantitatively from ortho kink bands. A dislocation model, consistent with some of the features of u-bands, is described. THE plastic deformation of zinc monocrystals with slip planes (0001) nearly parallel to the stress axis was studied in this investigation. In a previous investigation, it was shown that some low angle zinc crystals (those with slip planes making angles of more than about 2.5+1° with the compression axis), deform by ortho kinking while others (those with slip planes making angles of less than 2.5+1° with the compression axis) deform in a new way.' This new mode of deformation will be described in some detail here. Some of its striking features are: 1—it operates only for compressive stresses, 2—its temperature dependence is anomalous, and 3—it exhibits a new type of "yield-point" behavior. The mode of deformation to be discussed is not new in the sense that no previous evidence of its existence had been reported. The markings that it creates on the cleavage surfaces of zinc crystals have been described by several investigators.'" However, this is the first time that it has been made to operate under controlled conditions so that its response to mechanical variables, temperature, and aging treatments could be investigated and its geometry completely described. Apparently. Jillson' as well as Holden3 and Pratt" believed that the small bands they observed were simply small versions of ortho kink bands. In fact, two of these authors3,6 "alled the markings "micro kink bands." In spite of the precedence, it is felt that this term is not entirely suitable because these bands do not have the same genesis as kink bands, and they are qualitatively different in structure. As will be indicated by later discussion, the bands seem to be related to the tensile deformation bands observed in aluminum. The present author has chosen to call the bands "micro deformation bands," or simply ",ubands," and the deformation process, ''p-banding." Experimental Methods Crystals were grown from 99.999+ pct Zn obtained from the New Jersey Zinc Co. The details of the technique are given elsewhere." It should suffice to say that the crystals were seeded for orientation control, and precision pyrex tubes were used for molding them. About 40 crystals were used, yielding some 130 specimens. Fig. 1 illustrates the typical form of the specimens and shows how the orientation angles are defined. The crystal specimens were usually 1 3/4 in. long and about 150 mil in diameter. The angle between the slip or cleavage plane (0001) and the specimen axis is designated by xo, while a is the angle between the maximum slope of the (0001) plane and the nearest close-packed direction [1210], vary ing from 0°to 30°. The crystals were cut into specimens with a jeweler's saw and the ends were squared by filing (specimens held in V-block). Crystals of this orientation are stiff toward bending, so this procedure introduced only deformation localized at the ends. Then the specimens were polished either chemically in 50 pct HNO³ or electrolytically in 20 pct chromic acid. The mechanical tests were made with an Instron testing machine. This machine weighs by means of electric strain gages on elastic bars and is quite stiff, since the full-load deflection of its load cells is at most 0.002 in. Most of the testing was done at a

Jan 1, 1956

By Ulrich H. Roesler

RECENTLY, C. Zener1 published a new thermo-dynamic treatment of the a/y transformation in iron alloys. His interpretation differs from the previous theories2-0 ainly through the separation of the free energy difference, Ga—G, into two additive

Jan 1, 1957

By David A. Thomas, John F. Peck

Fibrous microstructures and their development have been studied by metallography and by hardness and quantitative metallographic measurements. Thin, curved grains were observed in transverse sections of commercial tungsten wire and were developed in laboratory-drawn iron wire at reductions greater than about 70 pct. The unusual grain shapes are attributed to the nonuniform mode of deformation of the grains associated with the characteristic [I101 preferred orientation that develops in bcc metals during drawing. Transverse sections of heavily swaged iron wire showed a ospiral nebulao structure that appears to result from the elliptical shape of the cross section of the swaging dies and their rotary motion. Hardness and quantitative metallographic results show unusual trends that parallel the changes in microstructure. Other phenomena are considwed in light of the results, including the strength of fine wires of bcc metals, ocylindricalo textures, and the ductility of fibrous tungsten. 1 HE microstructure of tungsten wire in a longitudinal section shows grains highly elongated in the working direction, giving the appearance of a bundle of parallel fibers, Fig. l(a). Wires of tungsten and other bcc metals show a pronounced preferred orientation in which a [I101 direction is parallel to the wire axis.l The microstructure and texture of tungsten develop during warm working (working above room temperature but below the recrystallization temperature) into wire by swaging and drawing. Fibrous tungsten so produced has limited but useful room-temperature ductility, whereas annealed tungsten is brittle at room temperature. During an investigation of the effect of recovery annealing on the substructure of commerical 0.030 in. diam tungsten wire, it was found that transverse sections of the as-received material showed thin, curved grains, Fig. 1(b), instead of the expected equiaxed grains. The fact that Figs. l(a) and (b) show different sections of the same material at the same magnification is at first disconcerting, because the long dimension of the curved grains in the transverse section is several times the average fiber width in the longitudinal section. However, a longitudinal section cuts most of the curved grains across their narrow dimension, giving the appearance of a multitude of narrow fibers. On the other hand, the plane of a longitudinal section occasionally includes a long dimension of a curved grain, resulting in a broad ofibero, such as A in Fig. l(a). EXPERIMENTS AND RESULTS To investigate the origin of fibrous microstructures and particularly the unusual transverse-section structure of tungsten, rods of iron (also bcc) were drawn and swaged in the laboratory. One rod of annealed Ferrovac E was drawn in six steps to a total reduction in area of 87 pct (0.10 to 0.036 in. diam), and a second rod was swaged to the same reduction, using approximately the same reduction steps. Longitudinal and transverse sections of the swaged and drawn iron wires are shown in Fig. 2, for reductions in area of 39, 73, and 87 pct. A fibrous microstructure in longitudinal section is first evident at 73 pct reduction, and it is further developed at 87 pct reduction. The grains in transverse section remain equiaxed until about 73 pct reduction, when they become somewhat elongated and curved. At 87 pct reduction, the drawn wire shows thin, curved grains in the transverse section, similar to those observed in tungsten. The transverse sections of the iron wires swaged 83 and 87 pct reduction in area show the striking ospiral nebulao structure in Fig. 2(d). This struc-

Jan 1, 1962

By G. K. Manning, A. R. Elsea, C. R. Simcoe

Boron increases the hardenability of hypoeutectoid steels by decreasing the nucleation rate of ferrite and bainite. It is postulated that concentrations of lattice imperfections, such as exist at the grain boundaries, furnish the necessary energy for nucleus formation. Boron, because of its atomic diameter, will concentrate at lattice imperfections where sites of suitable size are present. Boron will decrease the energy of these local areas by occupying these sites. This mechanism accounts for the large increase in hardenability observed with small amounts of boron. The loss of the boron hardenability effect and the boron precipitate formation are explained on the basis of increased concentration of boron at the grain boundaries either with increasing boron content of the material or with increasing temperature. COMMON alloying elements affect both the nucleation and growth rates of the austenite decomposition reactions.' This effect is largely a result of the slow diffusion rates of these elements. Although a small addition of boron markedly increases the hardenability of steel, the diffusion rate of boron, which is of the same order of magnitude as that of carbon, can hardly account for this effect. An addition of boron in the range of 0.001 to 0.003 pct is about as effective as an addition of 0.30 pct Mo, 0.40 pct Cr, or 1.25 pct Ni in increasing the hardenability of a 0.40 pct C steel;' however, increasing the carbon content of the steel decreases the effectiveness of the boron addition."' The difficulty in understanding why so small an addition of boron can replace much larger quantities of the more strategic alloys, together with the erratic behavior sometimes encountered in boron-treated steels, has interfered with their general acceptance by industry. In the belief that an understanding of the mechanism by which boron increases the hardenability of steel should lead to a more general acceptance of boron-treated steels, a research investigation to determine this mechanism was undertaken at Battelle Memorial Institute under sponsorship of Wright Air Development Center. Experimental Work In order to study the effect of boron on the transformation of austenite to ferrite and bainite, a group of steels was made with a basic composition similar to that of the SAE 8600 series. This base composition was chosen because it has sufficient hardenability to permit accurate measurement of the times required for transformation to start at various temperatures. The chemical analyses of the steels used in the first part of this investigation are listed in Table I. These steels were made as 200 lb heats in an induction furnace. The furnace charge was Armco ingot iron with the alloying elements added as ferroalloys. After the alloy additions were made, the heat was deoxidized with 0.125 pct Al. A 100 lb ingot was cast and an addition of 0.003 pct B, as ferroboron, was made to the metal remaining in the furnace. This metal was cast into a second 100 lb ingot. The ingots were forged to 11/4 in. diam bar stock from which end-quench hardenability specimens were obtained. Part of this material was further reduced by hot rolling to lx¼ in. bar stock from which specimens were obtained for isothermal transformation studies. Studies of Nucleation and Growth: End-quench hardenability tests were performed on these steels, using an austenitizing temperature of 1600°F. The hardenability curves, shown in Fig. 1, indicate that boron treatment resulted in considerable increase in hardenability of the steels. Any such change in hardenability must result from a change in the transformation rate of the austenite, and these rate changes can be established readily by isothermal transformation studies. Isothermal transformation studies were conducted on these steels as follows: specimens were austeni-tized at 1600°F for 15 min, transferred to a lead bath operating at a constant subcritical or intercritical temperature, held for various lengths of time, and water quenched. The specimens were sectioned for metallographic examination to determine the amount and the type of transformation products present. In order to determine the effect of boron on the formation rate of ferrite, isothermal transformation tests were made on the 0.20 pct C steel in both the boron-treated and boron-free condition at an intercritical temperature of 1375°F where ferrite is the only decomposition product of this low carbon austenite. The results of these tests are shown in Fig. 2, where the percentage of ferrite formed is plotted as a function of time at temperature. It is apparent that boron markedly decreased the transformation rate of austenite to ferrite at this temperature.

Jan 1, 1956

By R. H. Atkinson

With the object of improving the melting, casting, and working of palladium and 95.5 pct Pd-4.5 pct Ru, the effects of different melting atmospheres (reducing, oxidizing, and neutral), crucible linings, and annealing atmospheres have been studied. Some interesting observations are included about the solubility and diffusion of gases in palladium. THE object of the present work was to ascertain the effect of oxidizing, inert, and reducing ambient atmospheres on the melting and casting of palladium and a Pd-Ru alloy commonly used for jewelry. The need for such a study was indicated during World War I1 when jewelers experienced difficulty in their attempts to make small castings of the torch-melted Pd-Ru alloy by the lost-wax process. When the metal was melted under oxidizing conditions similar to those used for platinum, the castings were gassy; on the other hand, if the melting atmosphere was reducing, the castings were hot-torn and brittle. General Experimental Procedure Pure palladium sponge (99.9 pct Pd) and pure ruthenium powder (99.8 pct Ru) were used for making small ingots (50 g) of palladium and 95.5 pct Pd-4.5 pct Ru by induction melting. The coil, 3 in. high by 2 in. ID with 16 turns, was energized by a 20 kva Ajax high frequency converter. The melting crucibles, so-called sand crucibles, which were made of a highly refractory fireclay, were lined with different materials, including proprietary magnesia, alundum, zircon, and zirconia

Jan 1, 1957

By W. Ivanick, Frank W. Glaser

ORDERING reactions of Fe-Si compositions in the a region have been mentioned in a number of review articles.7-8 However, little is known in regard to the critical temperature, T at which this transformation takes place. Greiner and Stoughton,' in a study of the constitution of iron-rich Fe-Si alloys below 800°C, placed the onset of order at a composition of about 4 to 5 wt pct (7.5 to 9.5 atomic pct) Si. They observed that at this composition the ductility and strength begin to decrease sharply and brittleness develops. During X-ray studies they observed only the appearance of superlattice lines for compositions containing 12.5 atomic pct Si. More recent X-ray diffraction studies- etected the appearance of superstructure lines (corresponding to the calculated positions of [Ill] and [ZOO] reflections) for alloys containing 9.5 atomic pct. This fact confirms Greiner and Stoughton's original hypothesis in regard to the onset of order at compositions containing about 7.5 to 9.5 atomic pct Si. The physical properties.of Fe-Si alloys containing more than 10 atomic pct Si have been studied only to a limited extent. Their extreme brittleness and difficulties of sample preparation render them of little industrial use in comparison with alloys in the 0 to 10 atomic pct Si range. The properties of Fe-Si alloys reported to date are mostly properties measured at room temperature on ordered compositions It appears that because of experimental difficulties fully disordered alloys could not be produced in the critical composition ranges and their properties could therefore not be reported. In Figs. la, lb, and lc, a summary of physical properties of Fe-Si alloys, measured during recent investigations of the influence of silicon additions to iron, is presented. No mention of determination of the critical temperature, T for disorder could be found in the literature. The following is an account of work done in an attempt to: 1) produce the disordered state of various Fe-Si alloys and establish the critical temperature, T for disordering, and 2) compare the electrical and thermal conductivity characteristics of the ordered and disordered phases as functions of composition. Materials, Preparation of Test Samples, and Testing Methods Fe-Si alloys with high silicon contents (about 10 atomic pct) are usually prepared using powder metallurgy techniques. This method insures accurate compositions and high purity through the use of protective atmospheres during solid state diffusion alloying of the mixed powders."" Iron and silicon powders were mixed in the desired proportions, cold or hot pressed, and then homogenized at 1150°C for periods ranging from 6 to 12 hr under a protective getter and in a hydrogen atmosphere. Fully homogenized samples were quenched in water from various and successively higher temperatures to establish the critical temperature for disorder. Temperatures were determined using Pt—Pt-Rh thermocouples in contact with the test samples. Test bars were approximately 0.6x1.25x7.5 cm. Electrical measurements were made at room temperature by determining the potential drop over a 1.5 cm span for a current of 10 amp. Densities of the samples were determined by immersion. High temperature electrical resistivities were measured using previously described techniques.'" Specific heat conductivity up to 200°C was measured by heating one end of the test bar and water-cooling the other; heat conductivity was then obtained by subtracting the rate at which heat entered the water from the

Jan 1, 1957

By J. R. Low, M. B. Reynolds, L. O. Sullivan

The effect of neutron bombardment upon the stability of type 347 austenitic stainless steel has been investigated by a magnetic technique. The relation of the ferrite content of a stainless steel to its magnetic properties is given, and an apparatus suitable for the measurement of the ferromagnetic saturation induction of small specimens is described. Results of measurements on irradiated specimens are tabulated. Exposure to a neutron flux was found to cause a slight increase in the ferrite content of type 347 stainless steel, the change increasing with increasing length of exposure and with increasing initial ferrite content. The similarity of the effect of irradiation to the effect of annealing is pointed out. Possible effect of irradiation upon density of austenitic stainless steel is discussed. COMMERCIAL austenitic stainless steels are alloys of iron, chromium, and nickel, plus small quantities of other elements. Although these alloys are normally used in the austenitic condition, this state is thermodynamically metastable at ordinary temperatures and transformation to a more stable state takes place under favorable conditions. In the austenitic state, these stainless steels have the face-centered-cubic crystal structure characteristic of y iron, but the stable state at room temperature is a mixture of austenite and body-centered-cubic ferrite. The transformation from the pure austenitic condition may be brought about by cold working the alloy at a temperature below that at which the aus- tenite becomes thermodynamically unstable (about 400°C), the completeness of transformation increasing with increasing severity of cold work and decreasing temperature. The behavior of the austenitic stainless steels under ordinary conditions of use is rather well known. However, use of these alloys in a nuclear reactor introduces a new variable: the effect of neutron bombardment upon the transformation from the austenitic to the ferritic state. It was with this in mind that a study of the radiation stability of austenitic type 347 stainless steel was undertaken. Magnetic Technique for Ferrite Determination Commercial austenitic stainless steels such as type 347 undergo little transformation under normal conditions of fabrication and use. In view of this fact, it seemed likely that neutron irradiation would change the ferrite content of the alloy but little. The method chosen for measurement of the effect of neutron irradiation was thus limited to one which would be quite sensitive to small changes in the ferrite content of the alloy. Of the properties of the stainless steel which can be measured, the magnetic characteristics are most sensitive to the quantity of ferrite present.

Jan 1, 1956

By J. T. Norton, N. J. Grant, A. M. Gervais

An investigation of the creep deformation of coarse-grained high-purity aluminum at temperatures approaching the melting point permitted the formulation of a theory of subgrain formation. Subgrain boundaries were found to be formed by two different processes: kinking and polygonization. Polygonization is considered as the main factor in subgrain formation. SINCE "slipless flow" was first discussed in detail by Hanson and Wheeler,' many studies have been undertaken to determine how metals deform at high temperatures. Several types of observations have been reported. Jenkins and Mellor,² working on the creep of mild steels and various grades of commercial irons, found metallographic evidence of a kind of substructure within the grains after deformation at high temperatures. Homes" observed after creep deformation of steel at high temperatures that the original X-ray spots were sharply divided into several small ones. The same phenomenon was reported by Hirst4 from his studies on lead and later by Crussard5 from his work on aluminum. The works of these investigators demonstrated beyond any doubt that the splitting of the X-ray spots was due to the fact that the grains underwent a division into subgrains during deformation at high temperatures. Since then, numerous experiments have been undertaken on aluminum in order to determine the mechanism of formation of subgrains. Research workers can be divided, for the purpose of discussion, into two different groups as regards thinking on subgrain formation. On one hand, based on the work on polygonization by Cahn,6 Guinier and Lacombe,7 Greenough and Smith," Crussard,10,11 and Servi, Norton, and Grant," it was concluded that subgrain formation was a consequence of the simultaneous effects, first, of inhomogeneous deformation which produced bending of the lattice, and second, polygonization. On the other hand, Wood and coworkers13-16 based their work on the results of an earlier report" which dealt with crystallite size and a fragmentation theory. It is interesting to note that while Greenough and Smith8 and Wood et al. performed similar experiments, their conclusions were quite different. Wood et al. did not recognize polygonization as a fundamental mechanism and said that aluminum, at the beginning of the deformation, fragmented immedi- ately into subgrains in order to permit deformation of the metal, the number of these subgrains being a function of strain rate and temperature. They concluded that deformation of grains occurred by flow along the subgrain boundaries. In view of the contradictory conclusions, it would appear that the data were not explicit enough to provide an unambiguous conclusion. It appears that the techniques by which most of the results were obtained, namely, X-ray work, were not enough by themselves to solve the problem. Another approach was needed. In the present research, therefore, an extensive metallographic study was planned to supplement the X-ray work. The importance of revealing the subgrain boundaries metallographically was realized, and this will explain the extensive development and use of etching techniques. In order that subgrains would be considerably larger and therefore more readily visible under a microscope, the creep experiments were performed at very high temperatures approaching the melting point of aluminum. Development of Experimental Technique Creep tests were run at constant load on high purity (99.995 pct) aluminum specimens having a very coarse grain size. None of the specimens was run to fracture. The specimens were originally round (diameter, 0.187 in.; gage length, 1 in.) and had parallel flats milled in the gage section to permit

Jan 1, 1954

By B. G. Ricketts, A. Kelly, P. A. Beck

The isothermal kinetics (at 200" to 400°C) of subgrain growth and of softening were studied in a 99.997 pct pure Al crystal rolled to 80 pct RA, under conditions where recrystallization did not take place. It was found that the kinetics of subgrain growth and of softening were similar, and that the correlation between subgrain growth and softening was in first approximation independent of the annealing temperature. It has been shown by Heidenreich' by means of electron transmission microscopy and by Hirsch and Kellar2 by means of an X-ray microbeam technique that the crystals of heavily cold-worked polycrystalline aluminum consist of subgrains of approximately 2µ diam, which are slightly disoriented with respect to each other. This substructure is found on cold working at room temperature, without annealing. A preliminary study has been previously published3 of the softening upon annealing at 350°C of a heavily cold-rolled aluminum single crystal. Softening and X-ray line sharpening for such a rolled aluminum crystal were later studied in more detail as a function of annealing time and temperature.4 Perryman5, 6 has studied the recovery of polycrystalline aluminum after cold rolling. By means of phase contrast microscopy he found that the subgrain size increases with the annealing temperature but does not alter very much with annealing time at a given temperature. In the present work further study was made of softening as a function of annealing time and temperature and subgrain sizes were determined by two different techniques in an attempt to find any correlation that may exist between softening and subgrain growth. Subgrain size measurements were made both by the X-ray microbeam technique and by transmission electron microscopy. EXPERIMENTAL PROCEDURE For the X-ray studies specimens were cut from

Jan 1, 1960

By D. A. Thomas, M. F. Comerford

Poly crystalline wires of Fe-3.2 wt pct Si were cold-drawn to 31, 66, and 87 pct reductions of area. Mechanical properties and tnicrostructures were studied after recovery and re crystallization. An initial increase in strength during recovery was ascribed to strain aging, and subsequent softening was largely due to polygonization rather than re-crystallization. No unique actioation energies could be determined for the recovery process. Rather, activation energies ranged from 60,600 cal per mole at 10 pct recovery to 83,200 cal per mole when recovery was 50 pct complete. Sites for the nucleation of recrystallization were found to depend on time and temperature. In the early stages of re-crystallization, nucleation occurred in deformation hands. Later, or at high temperatures, recrystal-lized grains were nucleated primarily al grain boundaries. Polygonized structures did not seem to be preferred sites for nucleation. MUCH of the research on deformation, recovery, and recrystallization processes in bcc materials has been performed on single crystals or lightly worked polycrystals. Little study has been devoted to the relation of mechanical properties to micro-structure in polycrystals after severe deformation and subsequent annealing. This paper presents the results of a study of the tensile properties and microstructures of Fe-Si wires drawn varying amounts and annealed at a series of temperatures. EXPERIMENTAL PROCEDURE The experiments were carried out on an alloy of the following composition: 3.2 wt pct Si, 0.08 Mn, 0.016 C, 0.005 0, 0.0002 N, 0.0001 H, 0.008 P, 0.034 S. The material was received as l-in.-sq bars cut longitudinally from a hot-rolled slab provided by the Armco Steel Corp. The bars were forged to 3/8-in. rounds, centerless-ground to 0.250 in., and swaged to '0.108 in. All subsequent reductions were performed by room-temperature wire drawing at the rate of 2 in. per min. Each preliminary draft gave approximately 30 pct reduction of area and was followed by a l-hr anneal at 1010°C in dry hydrogen. Three lots of wire were made with ultimate cold reductions of 31, 66, and 87 pct reduc-

Jan 1, 1965

By M. von Heimendahl, G. Thomas

The microstructure of TD-Ni has been examined by transmission electron microscopy in the extruded, annealed. and deformed states. The tensile properties hove been correlated with the observed microstructures and the results ore com-pared with those obtained from pure nickel. The important conclusions are that the thorin particles in TD-Ni act as strong burriers to dislocntion motion during both deformation (slip) and annealing (climb). During deformation. the dislocations tangle around the particles and a cell structure is devleloped after 10 pct or more strain. The cell size appears to be determined by the spacing of the largest particles and is about five times smaller than that in pure nickel for the same strain. The higher work-hardening rate in TD-Ni compared to nickel is probably due to the more rapid rate of dislocation multiplication in the alloy as a result of dislocation-particle interactions. The Th0,particles inhibit recrystallization and twin growh so that some strengthening may arise from the high density of small annealing twins. THE strengthening of materials due to the presence of a dispersed second phase has been the subject of considerable experimental and theoretical investigation in recent years. One of the newest dispersion-strengthened alloys to be developed is TD-Ni,1 a system of approximately 2 vol pct thoria (ThO2) dispersed in a matrix of commercially pure nickel. This material is fabricated by powder-metallurgical techniques and offers high-temperature stability and useful mechanical properties virtually to the melting point of the base metal. While the mechanical properties of this system have been investigated,2,3 there have been no reports in the literature concerning the microstruc-ture of TD-Ni and its correlation to mechanical properties. This paper describes a transmission electron microscopy investigation of the micro-structure of TD-Ni together with its mechanical properties. The results are compared with the structure and properties of pure nickel.

Jan 1, 1964