Earnings of engineers in the period 1956 to 1958 continued the upward trend observed in the previous survey interval, 1953 to 1956. The overall median (all graduates) was $6500 in 1953, $7750 in 1956 (a 19 pct upstep or about 6.5 pct annually), and $8750 in 1958 (up 13 pct from 1956 or 6.5 pct average yearly). The latter represents an increase from mid-1956 to mid-1958. For this same two-year span the Consumer Price Index rose 1.5 pct and the Average Gross Weekly Earnings for Production (Manufacturing) climbed close to 10 pct. Median earnings for the major classifications studied are presented in Table I. The increase in engineering earnings are not distributed equally among the various activity classifications or among the experience levels of the survey. Summary results of the changes of the median lines for the major divisions are presented in Table 11. Data in this table are approximations- dollars are rounded to the nearest $50 unit and percentages to the nearest full percentage.

Jan 1, 1959

By J. Chipman, T. P. Floridis

The equilibrium of gaseous H2O-H2, mixtures with liquid iron is used to establish the activity coefficient of dissolved oxygen as log f o = — 0.20 [%O]. Discrepancies in earlier work are explained or eliminated. Additions of cobalt, molybdenum, tungsten, and platinum increase the activity coefficient of oxygen whereas copper and gold decrease it. THE importance of dissolved oxygen as a refining agent in liquid steel has led to a number of studies of its thermodynamic properties. It is the purpose of this paper to examine the effects of a number of alloying elements on the activity of oxygen in the steel bath. As a preliminary to the study of the effects of alloying elements, it seemed desirable to examine certain minor discrepancies in the published data on the properties of oxygen in simple iron-oxygen solutions. The activity and free energy of oxygen in liquid iron were studied by chipman1 in 1933 by means of the reaction h2(g)+-o = H2O (g);K; = PH2O/PH2[% O] [1] The data were in fairly good agreement with calculations from results on the similar reaction CO (g) + O- = CO2 (g); K2 =P CO2/P CO [% O] [2] which had been obtained by Vacher and Hamilton2 as an incidental part of their study of the reaction of carbon with oxygen dissolved in the melt. It was found that the equilibrium ratio k1 was not a true constant but varied with the oxygen concentration in the manner shown in Fig. 1, which is copied from the original paper. This early observation has been refuted in subsequent work but is confirmed in the present paper, and an explanation of the discrepancy can now be presented. In Fig. 1, the two points on the extreme right were disregarded in drawing the

Jan 1, 1959

By E. F. Thomas

THE late George S. Rice was active in the inves--I- tigation of bumps, particularly in the last ten years of his career as chief mining engineer of the U. S. Bureau of Mines. Since most of his investigation was carried out in Great Britain, continental Europe, and—to a lesser extent—Canada, his thinking on prevention was influenced considerably by the experience of those countries. It is not surprising, therefore, that when he was called upon a few years before his retirement to investigate bumps in the U. S. and suggest ways to prevent them, he turned to longwall mining. A longwall method had been most successful in combating the bump hazard in mining coal under deep cover, especially in Great Britain, but the prevailing method there at the time was advancing longwall mining, which he knew was uneconomical under U. S. mining conditions. For this reason he proposed a modified retreating longwall system that he believed included the best features of the advancing method. As brought out by Rice,' if the cover is 2000 ft and 50 pct of the coal is extracted, the static load on the remaining pillars will be about 4000 psi, which exceeds the ultimate crushing strength in most instances. If the pillar coal is overloaded before a pillar line is established, then the abutment zone preceding a line of extraction is no place to split pillars or extract them by any method other than an open-end system. Rice therefore advocated open-end mining, preferably by longwall, but he was willing to compromise with long-face mining if the longwall method was not acceptable. Rice's system was put into operation in a mine in Harlan County, Kentucky,3 but subsequent experience has shown that it did not take into account two important factors—avoidance of pillar-line points and maintenance of adequate development in advance of the pillar-line abutment area. For ten years after Rice's retirement the USBM did little investigation and research on bumps, chiefly because so few were occurring that there was not much cause for alarm. But in 1951 there were three occurrences involving fatal injuries, and the Bureau began a statistical survey in that year. C. T. Holland, head of the department of mines at Virginia Polytechnic Institute, was retained as a consultant. The resulting study' of 117 case histories brought out these important conclusions: 1) Almost invariably the bump occurred in a locality affected by the abutment zones of one or more pillar lines. 2) In most cases the locality of the bump was influenced by the abutment zones of more than one pillar line. The term pillar-line point has been used for many years in the Appalachian region for such a situation. Point is used in the geographical rather than the mathematical sense. 3) In pillar-line extraction the following practices are safest in preventing bumps: a. The mine layout should provide for pillars of uniform size and shape along the extraction line. b. The mine layout should be planned so that no development need be done in the abutment zone of a pillar line. c. The layout should permit open-end extraction of pillar lines from the next goaf, so that it will not be necessary to resort to pocket mining, splitting pillars, or any practice that will involve driving in the direction of the goaf within the abutment zone. d. Pillars should be large enough to support area without undue roof and floor convergence before establishment of a pillar line. These are, of course, generalities, and while they are useful in laying out areas where bumps can be expected, they are of limited help in many mines that were committed to a system of mining before it was realized that they were subject to bumps. Under such conditions it becomes necessary to choose between the following alternatives: 1) Abandon the territory, except for pillars that offer no extraction problems. 2) Through experience select the pillars that are most heavily loaded, and, by augering, induce bumps from a safe vantage point so that impinged loads are relieved. This method was first developed at the Gary, W. Va. mines of U. S. Steel Corp. and later adapted to mining thick coal beds at Kaiser Steel's Sunnyside mine in Utah. No scientific method is available to determine where to drill within a loaded pillar. Although this method of unloading has worked very successfully at Gary—with one exception—

Jan 1, 1959

By G. Derge, R. E. Grace

A S detailed studies of mass transport in hetero- geneous systems are made, a knowledge of the chemical diffusion coefficients in various liquid and solid phases is necessary to understand the kinetics of any total reaction. For example, in zone refining some information must be available about the diffusion coefficients of various species in the liquid and solid regions near the moving interface. In liquid-liquid reactions, of which slag-metal reactions are of particular interest to metallurgists, the diffusion coefficient of a transferring species must be known accurately in both phases in order to predict a transfer coefficient for the over-all process. Diffusion data for various elements in liquid iron and iron-carbon alloys have been roughly deter-

Jan 1, 1959

By J. L. Walter, W. R. Hibbard

A GREAT deal of work has been done on the rolling of single crystals of iron. Barrett and evensoon studied end orientations of heavily cold-rolled iron crystals and found that some crystals maintained a sharp single orientation during rolling. Others rotated into two or more orientations, and some fragmented and approached the entire polycrystalline texture depending on the original orientation of both the normal and rolling directions. Barrett, Ansel, and Mehl2 studied iron-silicon alloys and found that the addition of silicon to the iron had little effect on heavily rolled polycrystalline material. Dunn3 has extensively studied the cold-rolling and recrystallization of silicon-iron single crystals. Dunn found that for single crystals having initial orientation between (110) [001] and (111) [112], the principalcomponent of the cold-rolled texture is (111) [112]. Koh and Dunn4 studied the cold-rolled textures of single crystals having initial orientations in the range (001) [110] to (111) [IT01 and found that these are stable end orientations. They also found that all orientations having a [110] direction parallel to the transverse direction rotate to either the (001) [110] or the (111) [112] stable end orientation except for orientations near (112) [11], which divide and produce a final texture consisting of (001) [110]and (111) [112] components. Crystals having a (111) <112>-type texture re-crystallized to a (120) [001] or (110) [001]-type texture. Crystals having orientations with a range of (001) to (335) in the rolling plane and [110] in the rolling direction recrystallized5 to a wide spread of the initial orientations resulting from a multiplicity of 30-deg rotations about several (110) poles. The present study was undertaken to relate other orientations of crystals of silicon-iron to their cold-rolling and recrystallization textures, so that one might rationalize polycrystalline recrystallization data on the basis of the known deformation texture and the behavior of single crystals in these orientations. PROCEDURE Samples were obtained from a cylindrical ingot of 3 pct silicon iron prepared as follows: Armco iron was melted with high-purity silicon flakes under an atmosphere of argon to minimize oxidation. The alloy was poured into a special mold to form an ingot which consisted partially of large columnar crystals. Plates were cut from the columnar portions of the ingot with the longitudinal direction parallel to the columnar axes and ground to 0.040 in. thick. The plates were heavily etched to a thickness of 0.032 in. to remove the cold-worked surface. Orientations of seventeen crystals were determined by Laue back-reflection techniques keeping the mean columnar axis as the reference direction. The plate was then cut in two, parallel to the columnar axis. One portion of the plate was rolled at room temperature parallel to the columnar axis to a reduction in thickness of 84 pct. The remaining portion of the plate was rolled also at room temperature across the columnar axis to a reduction of 66 pct, at which point the crystals began to separate at the boundaries. After rolling, nine individual crystals were removed from the strip by cutting along the crystal boundaries with a jeweler&apos;s saw. Fig. 1 shows the original orientations of the six crystals that were straight-rolled and of the three crystals (4, 7, and 8) that were cross-rolled. Each rolled crystal was carefully etched to approximately 0.002 in. thick. Textures of the cold-rolled crystals were determined by use of the diffractometer with a non-integrating sample holder. The pole figures were made for the (200) poles using molybdenum Ka radiation and were plotted by an automatic stereographic projection recorder.&apos; Spurious poles were determined by rerunning portions of the pole figures using strontium oxide to filter out the Ka radiation. The central portions of the pole figures have not been determined. The pole figures were completed to about 55 deg from the periphery at which point the sample holder interfered with passage of the beam. Following the determination of the cold-rolled

Jan 1, 1959

By S. B. Twiss, P. R. Basford

The relationship between areas of iron powders, briquettes, and sintered compacts and tensile strength has been determined. It has been found necessary to distinguish between two types of areas which exist in such powders—a macroscopic area due to the shape and size of particles and a microscopic area due to pores and cracks in the surface. Only the macroscopic area, specifically the area due to particle irregularity, contributes to tensile strength; the microscopic area cannot be forced into contact with adjacent particles ond does not participate in bond formation. Of the two methods of area measurement employed in this study—permeability to liquids and gas-phase adsorption—only the former is useful for determining the roughness factor. A measure of this roughness, (area measured by permeability to liquid) -f- (orea of powder with the same size distribution, but made up of spherical particles), is shown to be uniquely related to tensile strength at constant density. The other important factors in determining the strength of sintered-metal compacts are the density and presence or absence of surface oxide. THE manufacture of metal parts by the process of powder metallurgy is an important and rapidly growing industry. Progress has been rapid and continuous, largely because of the excellent research in the field. Nevertheless, the process remains inherently complex and empirical. Several investigators have shown that the properties of the final compact must depend on many variables; namely, shape,&apos; size distribution,"-" nd compositiona of the original particles, the pressure necessary to compress to the desired density, the density of the compact, the time and temperature of sintering, and so on. Through the application of some new techniques to the study of powders and compacts, and the correlation of a number of observations of known variables, the present paper attempts to clarify and simplify the underlying theory of the powder-metallurgy process. Any theory must start with the obvious fact that the strength of a compact, its most useful property, is due to the formation of welded areas between adjacent particles, and attempt to deduce what effect other variables will have on (a) the area and (b) the intrinsic strength of these welds. Such welded areas can be demonstrated by electron micrographs, as in Fig. 1. It was believed that (a) could be most directly studied by means of surface-area measurements on the original powders and on the compacts made from them; the area decrease should be related closely to the welded area. A representative group of eleven iron powders from commercial sources, and made by a variety of processes, was chosen for this study. In addition to the surface-area measurements, correlations were established between the tensile strength and all the known variables which might possibly affect it. The results are quite unexpected. They indicate that the situation is much simpler than the authors had anticipated. The strength of the sintered compact is determined, indeed, by no more than three variables; viz., the irregularity of the original particles, the density of the compact and, in exceptional cases, the amount of surface oxide. All three had been recognized previously as having some effect on the tensile strength, but in the absence of the special techniques and interpretations to be developed here, there could be no suspicion that they were the only relevant variables. Materials and Methods Material—All the iron powders were commercial products obtained from the Amplex Division of Chrysler Corporation. Powders A, B, C, and J were very pure electrolytic iron. Powder D was made from oxidized scrap reduced by heating with an excess of cast iron. Powder E was a high-grade iron ore reduced by hydrogen. Powder I was prepared by atomizing molten cast iron in an air blast, quenching the droplets in cold water, and crushing the coarse powder. Mill scale (oxide) is added and the mixture heated to reduce the high carbon content. The other powders were all prepared by reduction of iron oxides, such as mill scale. They

Jan 1, 1959

By A. J. Terrones

THE classical papers on contact metasomatic deposits by Lindgren on the Clifton-Morenci district,&apos; by Barrell on Marysville, Mont.,&apos; and by Gold-schmitt on the Oslo district, Norway,&apos; laid the foundation for understanding of the importance of separating the metamorphic process from the subsequent metasomatic stage. Knopf&apos; made a big step forward by recognizing that sulfide ore minerals are invariably younger than silicates and by further stressing the importance of structural control" in ore finding. Some years later Harrison Schmitt" fought the idea that contact metasomatic deposits are erratic, irregular, bunchy, economically marginal, and of small size, concluding that these descriptions have little factual basis. He emphasized the importance of detail mapping and careful geological study as fundamental requirements for a better understanding of these deposits. This article presents a comparative description of the structural features at the Magistral, Antamina, Morococha, Vilca, Ferrobamba, Katanga (Quibio), Tintaya, and Huarca contact deposits (Fig. 1). Further, it will describe how these structural features controlled the emplacement of the intrusives, their shape, distribution of metamorphic and metasomatic halos, and sulfide deposition in post-skarn structural channelways. Finally, the modifications introduced by a superimposed hydrothermal stage recognized at some localities will be discussed. Primary exploration and careful sampling of recognized structural targets were instrumental in outlining the copper ore potential at the Antamina and Tintaya districts, thus proving the benefits and reward of careful geological examinations in this type of deposit. The Magistral District: This district lies in the Province of Pallasca, Department of Ancash, in northern Peru, at 8o 16&apos; S and 77" 47&apos; W. High to medium grade copper orebodies in garnetite, bordering a quartz monzonite stock, are exposed at the bottom of a glaciated valley in the western slope of the Andes at 4250 m (14,000 ft)* elevation.

Jan 1, 1959

By M. E. Wadsworth, R. L. Pearson

THE dissolution of UO, in carbonate solutions can occur only il the tetravalent uranium is oxidized to the hexavalent state. The carbonate system is of particular interest because it provides a means whereby the oxidized uranium may be dissolved by forming the complex ion UO,(CO3)3-1. In the presence of oxygen the over-all reaction may be written UO+1/2O,4CO3T+2HCO2UO,(CO4)11+H2O [1] UO, was used in this study because it could be obtained in high purity and also because it is representative of the most refractory of the primary uranium minerals. The mineral ulrichite is the natural counterpart of the synthetic UO, used. The kinetics of the leaching of UO, should be similar for any of the uraninite type minerals. A pressurized system was used not with the hope it could be extended to commercial systems as a primary purpose but simply to provide the means whereby important temperature and pressure parameters could be varied for the evaluation of the kinetic processes. The importance of such pres-

Jan 1, 1959

By J. B. Clark, A. S. Yue

IN recent years, zone melting1 has been applied extensively to the purification of metals having a very low vapor pressure.2-4 This note describes the zone melting of a high vapor-pressure metal, magnesium, where the melting takes place inside a refractory surface skin. The effects of zone speed and the number of passes of the molten zone on the purification have been determined and the effective distribution coefficients for the principal impurity elements were calculated. A schematic diagram of the zone-melting apparatus is given in Fig. 1. The Vycor tube containing the graphite boat with its magnesium charge (an extruded rod—3/8 in. in diam, 10 in. long) is pulled through the stationary furnaces. A molten zone approximately one-fourth the length of the charge is produced under each of the two central furnaces. Two grades of magnesium were studied—electrolytic magnesium and magnesium with a very low alloy content. The spectrographic analyses of these materials, within * 5 pct of the values stated, are given in Table I. Molten magnesium will vaporize severely if protected only by an inert atmosphere such as argon. Consequently an enveloping container is required. In zone melting, a rigid opaque container surrounding the charge is inconvenient because visual control of the zone length is prevented. A more satisfactory container is a strong flexible skin on the surface of the metal charge which is capable of supporting the molten zone. SO2 reacts with magnesium to form a thin coherent surface film of MgSO, and MgO. An atmosphere of SO, of commercial purity was maintained during the zone melting. Enough oxygen was present within the system and the commercial SO, for the satisfactory formation of the protective skin, so that any rupture of the skin during the zone refining was healed immediately.

Jan 1, 1959

By N. E. Rogen, N. J. Grant

AGE-hardening in nickel-chromium-titanium-aluminum alloys in the composition range characterized by the Nimonic alloys, is dependent upon the precipitation of the Ni3(AI,Ti) (y&apos;) phase.1 This phase is found to precipitate at about 700°C.1 Ni,Al is a face-centered-cubic ordered structure with a lattice parameter of 3.560 A. The atomic configuration is such that the aluminum atoms occupy the cube corners and nickel occupies the cube faces with titanium substituting for the aluminum preferentially. A maximum of three out of every five aluminum atoms can be replaced by titanium atoms in the -y &apos;phase.&apos; When the solubility of the y&apos;-phase is exceeded for titanium the T(Ni,Ti) phase is formed. The T-phase is an ordered close-packed hexagonal intermetallic structure which shows little solubility for the other elements in these alloys. The lattice parameter for T-phase is a - 2.5454 kr and c = 8.2900 kx units."

Jan 1, 1959

By G. Derge, M. Bourgon, G. M. Pound

A STUDY of electrical conductance in molten Cu-Fe sulfide mattes&apos; has shown that pure molten Cu,S behaves like a semi-conductor in that it is an electronic conductor and its specific conductance, of the order of 100 ohm-&apos; cm-&apos;, increases with increase in temperature. On the other hand, pure molten FeS, another electronic conductor, behaves like a metallic conductor in that its specific conductance, about 1500 ohm-&apos; cm-&apos;, decreases with increase in temperature. Molten solutions of Cu,S and FeS follow a roughly additive rule of mixtures with respect to both specific conductance and temperature coefficient. The behavior of molten Cu,S may be understood, by analogy to the situation in solids, in terms of semiconductor theory.&apos; It is thought that, although the melt consists of cuprous and sulfide ions, the bond between these atoms has a certain degree of cova-lency. According to the simplest concept the electrons in the partially covalent bonds are thermally promoted to a conduction band. In another concept, small amounts of impurities (undetermined) provide donor or acceptor levels in the forbidden zone between the valence and conduction bands and thus facilitate semi-conduction in the usual way. However, the metallic behavior of molten FeS is difficult to explain, because one might expect from similar reasoning that it too should act like a semi-conductor. It was suggested that the apparent metallic behavior of molten FeS might be explained by a large negative temperature coefficient of density. Thus if molar conductance instead of specific conductance were plotted versus temperature, the slope might prove to be positive, indicating semi-conduction instead of apparent metallic conduction. Accordingly, density measurements were made in order to answer this question in regard to molten FeS and also to provide data for conversion of specific conductance to molar conductance for molten Cu,S and a molten 50-50 wt pct Cu-Fe sulfide matte. Experimental Diagrams of the apparatus are given in Figs. 1 and 2. A 3 x 8-cm dense alundum crucible containing the prefused specimen is positioned in the uniform temperature zone of an induction furnace tube and melted under a helium atmosphere. Then the cell assembly, consisting of two 3-mm spectro-graphite rods, one of which is in a 1-cm ID open

Jan 1, 1959

By William T. Folwell

The Lucky Friday mine east of Mullan, Idaho, is an outstanding example of a property in the Coeur dlAlene district where a small and insignificant-appearing silver-lead-zinc vein at the surface has changed at depth into a large vein of great importance. The Lucky Friday vein has little if any surface expression and above the 1200 level the ore shoots are small and discontinuous. Between the 1200 level and 2450 level, the lowest developed level, the main ore shoot has shown remarkable improvement on each succeeding lower level, and today the mine is one of the major lead-silver producers in the Coeur d&apos;Alene district. History: The Lucky Friday property is on the north side of the South Fork of the Coeur d&apos;Alene River in sections 25, 26 and 35, T. 48 N., R. 5 E., Hunter mining district, Shoshone County, Idaho. This is about one mile east of the town of Mullan, which serves the eastern portion of the Coeur d&apos;Alene district. The southern part of the property is crossed by a branch line of the Northern Pacific Ry. and by U. S. Highway 10. This highway is the principal road crossing the panhandle of Idaho and connects the district with Spokane, Wash., on the west and Missoula, Mont., on the east. The main portal and surface plant of the Lucky Friday mine is at an elevation of 3365 ft, only a short distance above the valley floor and a few hundred feet from U. S. Highway 10. so the mine is readily accessible for year-round operation. The property is comprised of six claims, known as the Lucky Friday group, owned outright by the Lucky Friday Silver-Lead Mines Co. There are four patented claims, Good Friday, Lucky Friday, Northern Light, and Lucky Friday Fraction No. 2 (Mineral Survey No. 3028), and two unpatented claims, Hunter and Creek. In addition, Lucky Friday owns an undivided one-half interest in the Hunter Creek property. which adjoins the Lucky Friday group on the north: a 90 pct interest in the mineral rights in the Jutila Ranch (160A), which adjoins the Lucky Friday group on the east; and a 60 pct interest in the Lucky Friday Extension claim group, which adjoins the Lucky Friday group on the west. The company also has a long-term mining lease on the Hunter Ranch, which adjoins the Lucky Friday group on the west. The claims of the Lucky Friday group were located between 1899 and 1906. The Lucky Friday Mines Co. was organized in 1906 and did considerable exploration work by surface trenching and shallow underground workings, only to see the property sold by the Shoshone county sheriff to satisfy labor claims totaling $2000 in 1912. Another firm, Lucky Friday Mining Co., bought the claims in 1914 and spent 12 years driving what is now known as the tunnel level crosscut. This tunnel intersected a vein previously exposed in a higher tunnel, but it was only a few inches wide. The vein was followed a short distance westerly but was so unpromising that the work was discontinued in favor of extending the main crosscut tunnel several hundred feet north. No ore was found and all work was discontinued. The property was held in such low esteem by the firm that it let taxes amounting to less than $15 a year go delinquent for nine years. Then the property lay idle for two more years until in 1938 John Sekulic, a Mullan service station operator, took a lease, with a $15,000 purchase option, on the advice of an old miner who had worked in the mine. Sekulic re-opened the tunnel level crosscut and explored the vein with an easterly drift for about 200 ft. The vein was too narrow to be of commercial value but was believed interesting enough to warrant further exploration at depth. Lacking funds to explore the vein at depth, Sekulic tried to get the district&apos;s larger operating companies to take over his lease and option. They were not interested because of the lean tunnel level showing and the fact that the property lay between the White Ledge fault on the north and Osburn fault on the south, an area which geologists always considered unworthy of exploration. Sekulic then organized the present company and assigned his lease and option to it for stock. This was in 1939. Enough stock was sold locally to finance sinking of a shaft 100 ft from the tunnel level east drift. The vein at this additional depth still was not commercial but showed some improvement. Treasury stock was offered at 5 to 10C a share

Jan 1, 1959

By J. J. Gilman

WHEN a cleavage crack that is moving through a crystal intersects a screw dislocation, a jog is created in the crack front. As the crack continues to move, the jog leaves behind a cleavage step. This mechanism was proposed by Amelinckx and Votava,&apos; Pratt, bnd Gilmanh t about the same time. At that time the evidence for the mechanism was largely indirect. Other evidence has been presented by Low, Bilby and Smith,5 and Forty.&apos; It is the purpose of this paper to present more direct evidence of this mechanism and to show that observations of cleavage steps can be used to detect screw dislocations. Experimental Lithium-fluoride crystals that were purchased from the Harshaw Chemical Company, as well as natural mineral crystals and metal crystals, were used in the experiments. Although cleavage steps can be observed on transparent crystals with a metallurgical microscope, the contrast is poor. Marked improvement in the contrast is obtained by depositing thin (1000A) films of silver or aluminum onto the surfaces. The contrast also can be improved by using a phase-contrast microscope, but the simpler silvering method gives just as good results. Tolansky interferometric microscopy, and electron microscopy were used to measure the heights of cleavage steps. The etching techniques developed by Gilman and Johnstonh ere used to detect dislocations in the LiF crystals. Results The dislocations that create cleavage steps can originate in three ways: a) They can be grown into crystals b) They can be introduced by plastic deformation prior to cleavage c) They can be formed just in front of the tip of a propagating cleavage crack.&apos; These three situations will be considered in turn. Grown-in Dislocations—It is not possible to see the individual monomolecular cleavage steps that emanate from isolated screw dislocations in crystals.

Jan 1, 1959

By Howard L. Hartman

The past 15 years have seen rapid advances in the metallurgy of materials for drill machinery and bits, but rock drilling itself continues to be largely an art. Jet piercing, roller bit rotary drilling, and rotary percussion are all promising new techniques, but the percussion rock drill, still used for 90 pct of the blastholes in U. S. hard-rock mining, has under- gone no major modification since pneumatic machines were first used successfully in the 1860&apos;s. This singular lack of progress stems directly from ignorance of the nature of impact failure of rock and the fundamentals of rock penetration in general. For nearly three-quarters of a century, mining engineers did not know what went on at the bottom of a drillhole.

Jan 1, 1959

By W. M. Albrecht, M. W. Mallett

The solubilities of hydrogen in titanium and several of its alloys were determined at 600 to 1000°C and pressures of 0.05 to 10µ of mercury. Solubility increases with increasing beta phase in the alloys. Factors found to affect degassing rates are specimen size and presence of thick surficial oxide. Removal of hydrogen by heating in vacuum and in flowing inert atmospheres was studied. Practical curves predicting minimum degassing times are presented. THE presence of hydrogen in titanium and titanium alloys has detrimental effects on the mechanical properties of the metal.&apos;"," The hydrogen content of commercial titanium is sometimes of the order of 200 ppm by weight&apos; and varies with alloy composition. As a consequence, titanium and some titanium alloys as normally processed are sometimes not ductile unless treated to lower the hydrogen content. The best known hydrogen-removal treatment is heating the material in a vacuum. The rate of removal (degassing) at a give temperature determines the duration of the treatment required to attain a satisfactory low hydrogen level.

Jan 1, 1959

By R. O. Williams

A study utilizing neutron diffraction, electrical resistance, and chemical extraction has been carried out to clarify the chromium-rich part of the miscibility gap previously proposed for this system. This gap appears to be more symmetrical than previously supposed and is very flat. This flatness is believed to be the result of a cooperative phenomenon perhaps of magnetic origin; in particular, it is believed that the chromium-rich phase is antiferromagnetic. The presence of antiferromagnetism is believed to result in an additional strengthening mechanism very sinzilar to that for ordered precipitates. Likewise, it is proposed that the quenched alloys which are known to be ferromagnetic have antiferromagnetic regions which accounts for the maximum in hardness around 75 pct Cr. It is also believed that the existence of antiferromagnetism in other alloys of transition elements might explain some of their anomolous characteristics. THE iron-chromium phase diagram at low temper atures has recently been constructed as shown in Fig. 1(a)1 based upon that work and the work of Fisher, et al2 This system exhibits a number of extraordinary features but perhaps the most striking is the odd shape of the miscibility gap (in the

Jan 1, 1959

Jan 1, 1959

By C. H. Wayman, D. W. Fuerstenau

The effect of bubble size and concentration of certain reagents on the terminal velocity, shape, path, and drag coefficients of single air bubbles in distilled water has been investigated. Bubbles of a certain size range rise considerably faster than Reynolds number-drag coefficient relationships predict, whereas a small amount of frothing agent reduces their terminal velocity. The rapid velocity at which bubbles rise in distilled water appears to result from slip at the boundary and from circulation within the bubbles. Surface-active agents retard bubble motion through prevention of both circulation and slip at the boundary. A surface tension concentration gradient helps maintain bubble sphericity. HE gas phase is one of the indispensible in-gredients in flotation operations. Flotation depends on the collision of an air bubble and a mineral particle in a pulp and their ability to remain in contact long enough for adherence to take place. Before it is possible to understand the mechanics of air bubble-mineral particle encounter, it is necessary to learn more about the nature of bubbles themselves before collision with a mineral particle has taken place. To date, little work has been done on air bubbles in flotation systems. In 1945 Fahren-wald&apos; presented a study of the role of frothers on air bubbles and on aeration in flotation, and recently Wark and Sutherland&apos; discussed the work of Rosenberg- in relation to flotation. The research reported in this present article was undertaken to investigate systematically the effect of bubble size and the concentration of certain reagents on the terminal velocity, shape, path, and drag coefficient of single bubbles in distilled water. Most of the work is concerned with the effect of a-terpineol on bubble motion in water, but studies were made with potassium chloride, potassium hydroxide, potassium ethyl xanthate, and potassium amyl xanthate. Experimental Method and Materials: To obtain free bubble rise and reduce wall and surface effects, the investigators used a tank of 5½x5½x30-in. internal dimensions, filled with water to within 4 % in. of the top.&apos; The tank was made of acrylic plastic so that the walls would have good optical properties. Distilled water, which was re-distilled in a block tin still and saturated with air before each test, was used in all the experiments. All solutions were made with reagent-grade chemicals. During each experiment the water was at room temperature, and during the course of an experiment the temperature did not fluctuate more than 0.5°C. Since the experiments were performed over a period of six months, the temperature varied between 25° and 27°C. The temperature at which each series of experiments was conducted is recorded with the data. The experimental apparatus is presented dia-grammatically in Fig. l. Individual air bubbles were generated from purified compressed air through a capillary of 0.003-cm internal diameter at a rate

Jan 1, 1959

By D. E. Swets, P. C. Frank, D. L. Fry

THE hydrogen-steel system has received considerable attention in the past several years. Recent experiments in this laboratory have shown that another group of operations, namely, sanding and grinding,&apos; must be added to the already well-estab- lished list of phenomena that cause hydrogen to permeate steel. Qualitative tests which have been made with a very sensitive ion-gage type of detector similar to that used by Norton,&apos; showed that sanding a steel surface caused hydrogen permeation. A metal type 6~6 vacuum tube was used as the ion gage with an electrometer to measure the ion c~rrent.~ The protective enamel coating was removed from the tube.

Jan 1, 1959

By M. E. Steidlitz

FABRICATION of semiconductor devices.requires the formation of electrical contacts, often involving the use of lead, tin, and lead-tin solders. In several recent instances when germanium had been bonded to nickel with lead, a new metallic phase appeared, unattached to either germanium or nickel, but rather suspended as a continuous foil wholly contained within the lead matrix. Since such metallic structures do not form in nickel-lead or lead-germanium systems under identical conditions, a brief study was made of the characteristics and possible formation mechanisms of this material. EXPERIMENTAL Specimens were prepared by placing single crystal, transistor-grade germanium discs, 30-mils in diam by 6-mils thick, into a depression in a graphite boat. =A* nickel washers, 125 mils in diam by 5-mils thick, containing a center hole of 10-mils diam, and coined into a soup bowl shape, were loaded on top of the discs, so that the bottom of the

Jan 1, 1959