By V. I. Purcell, R. E. Snow, S. C. Sun

FATTY acids have been used as standard collectors for floating the matrix1-8 but not the leached zone phosphate ores. After a series of investigations, Davenport9 and Tarbutton10 concluded that the Florida leached zone ores tested were unamenable to fatty acid flotation and must be upgraded by floating the siliceous gangue with Armac-T as collector. The cationic flotation was estimated11 to cost almost ten times as much as a fatty acid process that would ideally give the same flotation grades and recoveries of phosphates. Mineralization: Extensive deposits of leached zone aluminiferous phosphate occur in The ore sample used for this work was obtained from the Virginia-Carolina Chemical Corp., Clear Springs area, Florida. The ore is a potential source of uranium and aluminum as well as phosphorus. Since the uranium and the recoverable aluminum are contained in some of the phosphate minerals, an upgrading of phosphate results in a corresponding enrichment of both uranium and aluminum. The phosphate minerals in the ore are primarily pseudo- wavellite, millisite, and carbonate fluorapatite, with a minor amount of wavellite. Quartz and clay are the common gangue minerals, quartz being pre- dominant. Others present in small amounts are ilmenite, hydrated iron oxides, staurolite, monazite, and zircon.

Jan 1, 1957

IN CIRCLES where mining men are wont to fraternize, a statement often heard is: "Yes, I spent six (or two, or ten, or thirty) years down at 'Chuqui.' " This means Chuquicamata, the site in Chile of what in all probability is the world's largest deposit of copper ore. One hears similar remarks regarding Braden and Andes, and, in fact, regarding a score of other big mines in South America, Africa, and elsewhere, but Chuqui seems to lead the others as the locale of engineers who have done a stint in foreign countries. One reason probably is that it is the Anaconda Company's premier foreign operation. Because of its unusual size and the diversity of its operations a great many men are needed. It is a sort of training school for young engineers; but, also, Anaconda has sent down a great many mature members of its big organization for special assignments like metallurgical research or plant construction. Chuquicamata is about 150 miles northeast of Antofagasta, at an elevation of 9,500 ft. It is in an almost rainless desert country where the wind (it is alleged by some) blows most of the time. However, the copper mining entrepreneurs have done their best to make up for what nature has neglected to do in creating a pleasant environment for the people who operate the mines. These include about 160 "foreigners" of whom 86 are from the United States, most of them accompanied by their families. There are 165 Chileans on the staff. Comforts, conveniences, and many luxuries are provided to offset in some measure the disagreeable features of the climate. Nevertheless, as I have implied, engineers at Chuqui generally jump at the chance to become "alumni" when opportunity offers. At the same time, they appear to take pride in their alma mater.

Jan 1, 1957

By D. T. Goettge, E. L. Robinson

The phase changes occurring in low carbon steel during hot strip mill rolling are shown to be metallurgically significant when related to commonly used temperature control points, particularly finishing and coiling temperatures. In combination, these temperatures are shown to have an important influence on the level and uniformity of hardness, grain size, and carbide characteristics of the finished hot and cold rolled sheets. PRODUCTION of wide flat-rolled products ordinarily requires a number of operations in sequence to prepare the material for shipment to the customer. Most products are tailor-made for specific end uses, with each operation contributing certain properties to the finished material. Since the characteristics imparted to the semifinished product by a given step in processing carry through to the finished product in varying degrees, it is important that the intermediate stages of production of flat-rolled strip be carried out with the same care which characterizes the last or finishing operations. The step of hot strip mill rolling is common to the production of all of the various types of flat-rolled product; therefore, the hot strip rolling is an especially important point at which to recognize and control those variables which have an effect on the surface characteristics and metallurgical properties of the finished product and which influence the ease of conducting subsequent operations. Orders entered at a producing mill usually show an end use or describe an article or part into which the ordered product is to be fabricated. Applying his experience as to the properties necessary in a finished sheet to suit the end use and to perform successfully in the fabrication involved, the metallurgist selects a steel of suitable composition and deoxidation practice, and slabs of appropriate dimensions are produced for rolling on the hot strip mill. At this stage of processing, the metallurgist faces the problem of controlling hot strip mill practice in the light of his diagnosis of the properties necessary to meet the end use, paying due attention to the accompanying problem of producing a strip which can meet processing requirements on subsequent units in the mill. It is the purpose of this paper to describe some of the factors which he must consider in solving these problems and to indicate some of the principles which guide him. Equipment, Physical Requirements of the Strip, and Temperature Measurement The metallurgist must, of course, be familiar with the physical layout of the mill, the temperature-measuring equipment available, and the physical requirements of the hot strip product before he can apply his metallurgical knowledge to the problem; hence, the first section will consist of a brief discussion of these matters. The usual hot strip mill consists of reheating furnaces, five or six roughing stands including a scale-breaker, holding table, and second scalebreaker, six-stand finishing mill, runout table with spray cooling facilities, and coilers. A schematic diagram of a typical layout is shown in Fig. 1. Slab temperatures are primarily a function of heating time and furnace temperatures, while mill speeds, spray practice, drafting practice, available water pressure, temperature of the cooling water, cross sectional dimensions of the strip, coil size, and equipment limitations, either singly or in combination, determine what rolling temperatures are practical on a given hot strip mill unit. Thus, it is possible that a set of temperatures which can be utilized successfully on one mill cannot be used on another. However, adjustments in temperatures and rolling practice can usually be made to develop the desired metallurgical properties. In addition to the metallurgical properties developed through proper temperature control, the hot strip mill must also provide strip with certain physical attributes which may be summarized as follows: Strip Cross Section—The strip contour should conform to a section which will give the best results in the cold reduction operation. This is generally recognized as a strip with 0.001 to 0.003 in. crown or shoulder-to-shoulder convexity depending on width, and freedom from concave, flat, or wedge-shaped cross sections which cause metal buildup in cold reduction. Excessive drop off in thickness at the edges can also be very detrimental in cold reducing to light gages. Gage, Width, and Camber—All of these must be controlled. For example, rundown or increasing thickness from the front to the back of the coil results in nonuniformity in the thickness of hot-rolled sheet product and in added difficulty with gage and welds in cold reduction. Similarly, excessive width variation is the cause of guide trouble and excessive edge scrap at later stages of processing, while excessive camber is the source of a variety of processing troubles. Type of Oxide—Product intended for pickling should have a predominance of the type of oxide most easily removable in sulfuric acid. It is generally recognized that this type is obtained by use of maximum table cooling water and cold coiling

Jan 1, 1957

By J. P. Zannaras

Referring to the article by R. J. Charles and P. L. de Bruyn, let us assume that W = weight of glass bar; P = weight of hammer; e = total deformation; K = unit of deformation; K = potential stress energy; E = modulus of elasticity; L = length of the bar; 7 = coefficient of inertia; h = height, ft; V = velocity, fps; and a = cross section area. The portion of kinetic energy which is effective in producing stress energy in a fixed bar struck horizontally is given by the formula" 1 + 1/3 W/P K =1+1/3w/p/(1+1/2w/p)2 P.V2/2g = Ph where 1 + 1/3 W/P ? (1 + 3W/P/(1=1/2w/p)2 [8] Putting e e = W/P =------------ From the above equation it can be seen that the maximum transfer of kinetic energy to stress energy is when e = 0 or W/P = 0 which indicates that the weight of the hammer must be very large as compared with the weight of the impacted rod. Eq. 8 diametrically opposes the conclusions reached by the authors of this article. In fact, if their suggestions were followed to the extreme when e = co when P = 0, there would be no transfer of kinetic energy to stress energy at all, as 7, becomes zero. Eq. 8 presumes that the velocity with which the stress is propagated through the bar is infinite, whereas the authors claim that the compression waves reflected are reaching the struck end of the bar prior to the complete transfer of the kinetic energy to cause such modification of the conditions there as to make them reach the reverse conclusions demonstrated by the above formula. That such interference exists is unquestionably demonstrated by the authors and others. However, if my observations are correct, such interference for this specific experiment and also for practical comminu- tion is insignificant, and the conclusions of the authors are in error and must be reversed to comply with Eq. 8. Eq. 5, w. = AE 2/2, given by the authors on page 51, is derived from the following equation (Eq. 9): K = 1/2Pe, where P = Sa, S = ?E, e = EL, and L = 1. The above formula, Eq. 9, cannot be applied in this case. This formula is applicable for static loads where the load increases from zero up to its final value, P, in such a way that the deformation at different instants is proportional to the loads acting at those instants and actually represents the area of a right triangle in the strain load diagram of base e and height P. The typical photographs shown in Figs. 3 and 4 represent the familiar strain load diagrams, and since the line of the wave marks the existence and intensity of the strain with the unquestionable conclusion that such strain has been caused by the action of a load acting continuously all along the wave until it reached the horizontal axis, the work stored at this point is represented by the area under the wave line and the horizontal axis and not by the area of the fictitious triangle given by the authors. Then if this is correct, even visual estimation of these areas at gage stations given in the typical photographs of Figs. 3 and 4 suffice to contradict the authors' calculation given in Figs. 6a and 6b and Figs. 7a and 7b. The typical photographs presented by Charles and de Bruyn show a considerable variation of the intensity of the strain at different stations but very small variation of areas which actually represent the stress energy at the corresponding stations. And, apparently, by squaring the small quantities, the authors magnified their error tenfold. J. M. Frankland's paperV iscusses the relative strain intensity and not the total energy for different types of impact loading. He states in his paper, "The reader is explicitly warned not to confuse the results in this report with those obtained when the load is applied by a blow as from a hammer. In this case the peak load rises to very large but mostly unknown values. The accompanying large deflections and stresses are the result of high values of P, not of the dynamic load factor n. According to Frankland "the dynamic load factor" is the numerical maximum of the response factor. It therefore appears that the authors followed the same procedure in obtaining the relative strain energy ab-

Jan 1, 1957

By W. O. Philbrook, L. D. Kirkbride

IN the normal operation of the iron blast furnace, reduction of the iron oxides is accomplished almost entirely above the tuyeres.' Blast furnace slags usually contain less than 0.5 pct FeO, although higher values may occur with abnormal operation. There is reason to conjecture, however, that incompletely reduced ore may sometimes reach the hearth and enter the slag as a result of heavy slips or, perhaps, even from cores of excessively large lumps of a charge material of poor reducibility. The possibility of reoxidation of iron droplets falling in front of the tuyeres has been considered by several writers. It would be of interest, to know how rapidly iron oxides reaching the slag for any of these reasons could be reduced by reaction with coke or with the high carbon liquid iron in the hearth. In comparison with the hundreds of papers that have appeared on various aspects of the reduction of solid iron oxides by gases and in the presence of several forms of carbon, little work has been published on the reductioin of liquid oxides or slags. Dancey measured rates of reaction of the pure liquid oxides, both FeO and Fe,O,, with molten iron containing about 4.3 pct C. The oxide was dropped into the cup formed in the upper surface of the iron by rotating the crucible and melt. Under these conditions, reduction of either FeO or Fe,O., was completed in less than 10 sec. The present study was concerned with the reduction of FeO from blast furnace-type slags containing less than 5 pct FeO and melted over carbon-saturated iron in stationary graphite crucibles. The results were considerably different from those found by Dancey, as will be discussed later. Although this work is of interest in relation to hearth reactions in the blast furnace, interpretations must be made with caution because the experimental conditions do not duplicate those within a furnace and may not even lead to the same reaction mechanism. The authors were motivated in undertaking this work by an additional interest—the part played by FeO reduction in the mechanism of de-sulphurization of iron by slags under similar experimental conditions. Derge, Philbrook, and Goldman eveloped detailed experimental evidence to support a three-step mechanism for desulphurization like that originally proposed by Holbrook and Joseph' (These reactions are written in molecular form for convenience, but this is not intended to imply the existence of molecules of FeS in the bulk metal phase nor to deny the likelihood of ionic reactions in the slag.) Earlier work by Chang and Goldman" had shown that the overall reaction follows first-order kinetics with respect to sulphur and that the rate of reaction is proportional to the slag-metal interface area, which observations have been confirmed by subsequent work. Later studiese,' have established the influence of al.loying elements on the first and last steps of the reaction. This paper reports a study of step 3 alone, uncomplicated by the simultaneous process of sulphur transfer. Apparatus and Procedure The experiments were made in a conventional high frequency induction furnace powered by a 35 kva Hg spark gap converter. The graphite crucibles used for most of the runs were 14 cm (5.5 in.) deep and 4.8 cm (1.9 in.) ID with 0.75 cm (0.3 in.) wall. An insulating cover with a small opening for withdrawing samples was used to minimize heat loss and infiltration of air into the furnace. The crucible was charged with 300 g of carbon-saturated iron and either 65 or 100 g of prefused slag analyzing 38.0 pct SiO,, 15.4 pct A10 and 47.1 pct CaO. To obtain the cleanest possible interface at the start of the reaction, the metal and slag were brought to temperature together to prevent the rejection of kish graphite that would have been caused by the chilling effect of a large addition of cold slag to carbon-saturated iron. After temperature control had been established, the desired amount of iron oxide was added in the form of a prefused slag of composition 73.6 pct FeO, 7.7 pct AWX and 19.0 pct SiOl. This slag addition was observed to be molten in somewhat less than 1 min, and a very vigorous reaction proceeded for 1 to 2 min after its introduction. Zero time was taken as 2 min after the ferrous silicate slag addition. Slag samples weighing about 0.5 g each were taken periodically by a copper chill sampler." The weight of the initial slag was large relative to the weight of samples removed, so that the slag weight never varied by more than 5 pct during any run. Temperature was measured by a calibrated W/Mo thermocouple immersed in the metal, with a graphite tip cemented over the fused silica protection tube to prevent attack by slag and metal. After some difficulties with uncertain temperatures during the first two runs, the practice adopted to position the thermocouple for reproducible results was to lower the protection tube to touch the bottom of the crucible and then raise it 0.5 cm. The apparent temperature gradient between the bottom of the crucible and the top of the slag was found to be 15°C (27°F). but much of this spread was probably the result of inadequate immersion of the protection tube to off-set conduction losses along the graphite tip when the thermocouple was inserted only into the slag. The temperature of the bath was controlled within 25°C (9°F) during a run.

Jan 1, 1957

By H. C. Rogers, B. W. Roberts

Vanadium foils and wires, either cold-worked or recrystallized, show a ductile-brittle-ductile fracture sequence with temperature. At about 150°C the hydrogenated vanadium wires are found to be ductile. At room temperature the wires show brittle fracture, and at liquid nitrogen temperature the wires are again ductile, although to a lesser extent than found at 150°C. Hydrogenated cold-rolled vanadium foils have been found to fracture in unusually straight lines along the [100] texture directions. The hydrogen content required to show this [loo] texture fracture is limited to a few atomic percent in range. Hydrogen content above this range causes fracture to occur in random directions. PRELIMINARY experiments with hydrogenated vanadium foils indicated that the embrittling effect of the hydrogen on the vanadium, which was severe at room temperature, was reduced at both lower and higher temperatures. In order to investigate more quantitatively the ductility changes with temperature, vanadium wires were tested in tension at three temperatures. The reduction of area was measured and the fractures examined. Specimen Preparation—The material used was kindly supplied by A. U. Seyboltl in the form of M-in. rod. The nominal analysis was: 99.2 pct V assay, 0.2 pct C, 0.01 pct Si, 0.01 pct Fe, 0.015 pct Ca, 0.02 pct O,, 0.01 pct N2, and 0.003 pct H,. The specimens were 0.035-in. diam wires. These were prepared by cold-swaging the supplied rod to the final diameter without intermediate anneal. They were finished with long-bearing dies. The surface was then given a light polishing with 0 emery paper and degreased in trichlorethylene. An X-ray check indicated that the cold-swaged wire had a fairly strong [110] fiber texture. The wires were then recrystallized in vacuum in continuously pumped quartz tubes at two temperatures to give two different grain sizes. One group of wires was given 45 min at 800°C; another, 60 min at 1000°C. The microstructures in Fig. 1 show the wires after they have been electropolished and elec-troetched in 10 pct HCI. After the 800°C anneal, the vanadium grains had a diameter of 1 to 2p and there appeared to be a tendency to elongation in the longitudinal direction. However, the latter may be an etching effect. After the 1000°C anneal, the grains appeared to be equi-axed, but there was a very large spread in grain size, probably due to some impurity segregation in the wire, Fig. 1, right. The grain diameters varied between the limits of 1 to 150p. The small particles shown particularly clearly in Fig. 1, left, are also visible on the polished surface of all samples before etching and are undoubtedly carbides and nitrides of vanadium. An X-ray check indicated these annealed wires had a strong [110} recrystallization fiber texture. The hydrogenation was carried out in an iron retort with dry hydrogen flowing through it, the retort and contents being heated in a tube furnace with a hydrogen atmosphere. The hydrogenation temperature was approximately 500°C. The hydro-genation times chosen were approximately those which would be just enough to cause the vanadium to be brittle at room temperature and thus allow the greatest chance for ductility to occur at the other two temperatures. Part of the fine grained specimens were hydrogenated for 21/2 min at 490°C. Part of the coarse grained specimens were hydro-genated for 11/2 min at 515°C.

Jan 1, 1957

By Stuart S. Forbes

Changes and additions made to the Canadian Copper Refiners Ltd. electrolytic refinery between 1949 and 1955 are reviewed. The effect of high current density on current efficiency and section work is discussed. OPERATING and physical changes which have been made to the electrolytic tank house of Canadian Copper Refiners Ltd. suggest a review of present conditions. Previous papers1 a have described the general arrangement. Since then, expansion, closer anode spacing, and higher current densities have increased annual cathode capacity from 112,000 to 182,000 tons. A recent extension to the tank house, begun in the spring of 1954 and completed in August 1955, was undertaken to handle the monthly production of about 3,000 tons of anodes from Gasp6 Copper Mines. The anticipation of these additional receipts and large stocks of unrefined copper caused by the increase in custom smelting at Noranda made it necessary to increase production without immediately available additional cell capacity. Accordingly, from December 1954 through March 1955, the tank house was operated successfully at a current density of 24.0 amp per sq ft. Again, as of September 1955, one of the two tank house circuits is being operated at this high density. Although other refineries may operate at current densities higher than 24 amp per sq ft, none is doing so with anodes which contain silver and gold content as high as those being refined at Canadian Copper Refiners Ltd. General Arrangement The original building consisted of two parallel bays, each 660 ft long and 60 ft wide, with a 24 ft pump bay extending along the west side of the building. A previous expansion, completed in 1939, was to the west of the original building and consisted of two 60 ft parallel bays 240 ft long. The length of these two bays was extended in 1954 to 540 ft, adding one stripper and 12 commercial sections to No. 2 electrical circuit. Space is still available for an additional six commercial sections and one stripper section. Construction on these seven sections started in September 1955, and will be completed early in 1956. The tank house capacity will then be 206,000 tons of cathodes per year. In the two tank houses there is a total of 900 cells distributed as follows—commercial, 468; stripper, 36; total, 504 in the No. 1 tank house (No. 1 circuit): commercial, 360; stripper, 36; total, 396 in the No. 2 tank house (No. 2 circuit). Section arrangement consists of nine cells to a tier and two tiers or 18 cells to a section. Anodes, weighing 620 lb each, are cast with a Baltimore groove and are refined by the multiple system. Solution enters each cell through a bottom inlet at one end and overflows at the top of the opposite end. Rate of solution flow through the cells is controlled by valves at each section to 4.5 gpm. Electrical power to the tank house is now provided by nine 675 kw motor generator sets. Each set consists of a 135-12 v 5000 amp dc generator, driven by a 980 hp 2300 v synchronous motor. When No. 1 circuit is operated at 22,000 amp, five sets, at 4400 amp each, are connected in parallel. As the maximum allowable current on No. 2 electrical circuit has recently been set at 18,000 amp, only four sets are connected in parallel on No. 2 circuit. A tenth set, now being installed, will be reserved as a spare, for use in either circuit as required. Recent Changes In 1949, the annual capacity of the tank house was increased from 112,000 to 132,000 tons by closing the

Jan 1, 1957

By J. H. Frye, S. G. Holder, E. E. Stansbury

Internal friction studies on annealed and cold-worked pure silver and alloys of silver with 4.5 atomic pct each of Cd, Sn, and Sb are reported. Small amounts of cold work, introduced by stretching pure silver, decrease the internal friction; large amounts of cold work, by wire drawing, cause this decreased internal friction to rise. Results of severol anneoling histories on the room-temperature in-ternal friction indicate a rather complex recovery and recrystallization behavior. A rather system-atic alloy effect is observed for the elements of Period V-B in silver in both the annealed and cold-worked states. DURING recent years internal friction measurements at very small stress levels have been interpreted in terms of structural models and mechanisms occurring within the metal or alloy.These measurements have been made over wide ranges of frequency of vibration and of temperature. While the effects of impurities, alloying, and plastic deformation have been studied by numerous investigators, no investigations of the effect of a series of solutes related by their position in the Periodic Table on a given solvent seem to have been reported. The present paper reports internal friction measurements on silver and on certain silver-base solid solutions to determine the values of room-temperature internal friction associated with varying amounts of plastic deformation and after different annealing

Jan 1, 1957

By R. D. Burlingame, T. L. Joseph, Gust Bitsianes

DESPITE almost fifty years of commercial practice, the sintering of iron ore has received little fundamental study. Much of the theoretical work1-'has dealt with the constitution of sinter produced under widely varying conditions. While these studies have broadened our knowledge of the changes that occur in the sintering zone and in the freshly formed sinter during the early stages of cooling, they provide little insight into the changes that precede the formation of sinter. These preliminary changes merit study as a part of the overall process. Hessle. working with beds of Swedish magnetite concentrates, was one of the first investigators to study the sintering process in its entirety. On the basis of temperatures observed at various levels of the bed during sintering, he postulated a number of distinct reaction zones to account for the chemical changes leading to the formation of sinter. A more direct method of attack is that of arresting the sintering zone after it has progressed part way through the bed. A study of a vertical cross section through such a quenched bed provides direct information on the changes taking place at various levels. This method was used by McBriar et al.' to show that several well-defined zones of chemical change existed within beds that were typical of British sintering practice. The same general method of attack was developed independently in the present investigation to study partially sintered beds typical of American practice. Experimental Sintering Equipment The sintering operation was carried out on an experimental scale with the equipment shown in Fig. 1. The refractory-walled sintering chamber A was 11 in. deep and averaged 9 in. in diameter. Air was introduced through a tapered flow section B, which contained the orifice C for accurate metering of the incoming air. This section was located directly above the square ignition housing D, which in turn rested upon the sintering chamber A. The bed was ignited with burner E. The required suction for the operation was furnished by a fan F, which had an air capacity of 500 cfm (stp). Hot exhaust gases from the sintering chamber were cleaned in the dustcatcher G before entering the exhaust fan. In the study of partially sintered beds, it was essential to find some technique for removing the entire charge from the sintering pot without disarranging the unsintered bottom portion. This problem was finally solved by sintering the charge in a removable basket, which snugly fitted the sintering chamber. This basket was constructed of two thicknesses of window screen and was lined with a 3/16-in. layer of asbestos paper. The bottom of the basket consisted of two thicknesses of wire screen, which were fastened to the basket wall. For high fuel mixtures, additional insulation was provided by a somewhat thicker layer of asbestos cement. Preparation of Partially Sintered Mixtures The moist feed was carefully placed in the sintering basket, to prevent segregation of the particles, which varied widely in size and composition. A thermocouple was placed in the center of the basket with the hot junction halfway down, and the mixture was evenly distributed around it. During ignition and throughout the sintering of the upper half of the bed, the hot junction temperature increased very little. When the sintering zone reached the halfway point, as indicated by the sudden increase in the hot junction temperature, the charge was quenched. During quenching the suction was turned off and the orifice was tightly stoppered to prevent further influx of air. At the same time, nitrogen was admitted to the sintering chamber through the orifice tap. As soon as the nitrogen had displaced the air and products of combustion, the charge was removed from the sintering pot for immediate dissection. It is impossible to preserve the exact zone structure of the bed at the instant that combustion is arrested unless the downward transmission of heat is also immediately stopped. Fortunately, heat transfer is very slow in beds containing a stationary fluid, especially if the particle size is small. It follows that the minimum quantity of nitrogen should be used to displace the air and that static conditions be established as soon as possible. A very steep temperature gradient across the combustion zone for some time after the quench was evidence of in-

Jan 1, 1957

By W. Ivanick, Frank W. Glaser

ORDERING reactions of Fe-Si compositions in the a region have been mentioned in a number of review articles.7-8 However, little is known in regard to the critical temperature, T at which this transformation takes place. Greiner and Stoughton,' in a study of the constitution of iron-rich Fe-Si alloys below 800°C, placed the onset of order at a composition of about 4 to 5 wt pct (7.5 to 9.5 atomic pct) Si. They observed that at this composition the ductility and strength begin to decrease sharply and brittleness develops. During X-ray studies they observed only the appearance of superlattice lines for compositions containing 12.5 atomic pct Si. More recent X-ray diffraction studies- etected the appearance of superstructure lines (corresponding to the calculated positions of [Ill] and [ZOO] reflections) for alloys containing 9.5 atomic pct. This fact confirms Greiner and Stoughton's original hypothesis in regard to the onset of order at compositions containing about 7.5 to 9.5 atomic pct Si. The physical properties.of Fe-Si alloys containing more than 10 atomic pct Si have been studied only to a limited extent. Their extreme brittleness and difficulties of sample preparation render them of little industrial use in comparison with alloys in the 0 to 10 atomic pct Si range. The properties of Fe-Si alloys reported to date are mostly properties measured at room temperature on ordered compositions It appears that because of experimental difficulties fully disordered alloys could not be produced in the critical composition ranges and their properties could therefore not be reported. In Figs. la, lb, and lc, a summary of physical properties of Fe-Si alloys, measured during recent investigations of the influence of silicon additions to iron, is presented. No mention of determination of the critical temperature, T for disorder could be found in the literature. The following is an account of work done in an attempt to: 1) produce the disordered state of various Fe-Si alloys and establish the critical temperature, T for disordering, and 2) compare the electrical and thermal conductivity characteristics of the ordered and disordered phases as functions of composition. Materials, Preparation of Test Samples, and Testing Methods Fe-Si alloys with high silicon contents (about 10 atomic pct) are usually prepared using powder metallurgy techniques. This method insures accurate compositions and high purity through the use of protective atmospheres during solid state diffusion alloying of the mixed powders."" Iron and silicon powders were mixed in the desired proportions, cold or hot pressed, and then homogenized at 1150°C for periods ranging from 6 to 12 hr under a protective getter and in a hydrogen atmosphere. Fully homogenized samples were quenched in water from various and successively higher temperatures to establish the critical temperature for disorder. Temperatures were determined using Pt—Pt-Rh thermocouples in contact with the test samples. Test bars were approximately 0.6x1.25x7.5 cm. Electrical measurements were made at room temperature by determining the potential drop over a 1.5 cm span for a current of 10 amp. Densities of the samples were determined by immersion. High temperature electrical resistivities were measured using previously described techniques.'" Specific heat conductivity up to 200°C was measured by heating one end of the test bar and water-cooling the other; heat conductivity was then obtained by subtracting the rate at which heat entered the water from the

Jan 1, 1957

By E. E. Underwood, L. L. Marsh

Aluminum single crystals, alloyed with 0.042 atomic pet Cu and 0.11 and 1.1 atomic pct Mg, were subjected to constant stress creep tests, tensile tests, and hot hardness measurements within a temperature range of 300° to 866OK. Calculations based on Dorn's temperature-compensated time parameter, 6, gave a value of DH, = 27,000 cal per mol for the activation energy of early creep in aluminum single crystals. Correlations have been obtained for aluminum alloy single crystals with the parameter E for solid solution strengthening, as well as with the parameter F for solid solution hardening, by using a valence of three for aluminum. Limited measurements on tensile specimens show that the slip band density tends to decrease with increasing temperature and with decreasing solute concentration. INCREASING interest is being shown in the mechanisms of plastic deformation in single crystals during tensile and creep testing. The complexity of deformational processes in polycrystalline materials has led to a search for simpler experimental conditions. Numerous creep and tensile investigations have been conducted with pure, metallic single crystals. To a lesser degree, the effects of alloying elements on the tensile properties of single crystals have been determined. However: the literature dealing with the effects of alloying additions in single crystals under creep conditions is vanishingly small. This paper represents an attempt to narrow this gap in the knowledge of the subject. Previous investigations of creep behavior at the Battelle Memorial Institute1-1 have been of great value in the analysis of the present single crystal data. It is equally desirable, however, to ascertain the extent of correspondence between the behavior of single crystal and polycrystalline materials. For this purpose, correlations, similar to those developed for polycrystalline aluminum alloys by Dorn and co-workers, have been made with the single crystal data. The results from this study have tended to confirm and extend those correlations to the case of alloyed single crystals. Materials and Procedures Three dilute binary aluminum alloys were prepared for this investigation from 99.99 + wt pct Al, 99.8 wt pct Mg, and 99.92 wt pct (electrolytic) Cu. The nominal compositions of the alloys were 0.042 atomic pct Cu, and 0.11 and 1.1 atomic pet Mg. Precautions were taken to avoid contamination of the stock during melting and casting of the alloys. After a heat treatment of 8 hr at 925°F the alloys were extruded, then machined into) threaded tensile specimens with a 3 in. reduced section and a 0.505 in. diam. Spectrographic examination showed less than 47 ppm metallic impurities in each alloy. The single crystals were grown by the strain-anneal method, with a critical strain of about 11/4 pet giving the optimum results. In general, 3 in. crystals were obtained with the Al-Cu alloy, but smaller crystals in the magnesium alloys necessitated the use of 2 in. and 1 in. gage lengths with the low and high magnesium alloy specimens, respectively. After an electrolytic polish, the orientation of that portion of the specimen containing the largest single crystal was determined from Laue back-reflection photographs. Tensile tests were conducted at a constant load rate of about 2 lb per min. Creep runs were made in a constant temperature room, under constant stress at the higher creep temperatures, and constant load at the lower temperatures. The eloneation was measured to within ±5 microin. by a specially designed capacitance extensometer. The ex-tensometer arms were attached to the 3 in. specimens at the shoulders of the test piece or, where the crystals were smaller than 3 in., by knife-edge grips.

Jan 1, 1957

By C. G. Dunn, P. K. Koh

The primary recrystallization textures of 11 single crystals cold rolled 70 pct were determined. The effect of crystal orientation on recrystallization behavior was investigated also and found to be large. An exception was found to the relationship that strong components of the recrystolliza-tion texture are rotated from the cold rolled texture by 30° about <110> axes, but generally this relationship was found to hold quite well. Evidence supporting oriented nucleotion was found and discussed in terms of probable active slip systems and <110> edge dislocations. THE present paper is one of a series&apos;.&apos; on recrys-tallization phenomena in cold rolled 31/4 Si-Fe single crystals and is mainly concerned with the textures produced on recrystallizing from stable end orientations. Data for the cold rolled textures of the crystals used have been reported by Koh and Dunn." Their results showed that the sharpness of the cold rolled textures varied throughout the range of stable end orientations and that the tendency to re-crystallize was related to the sharpness of the cold rolled texture, wherein the rate of recrystallization increased and the size of recrystallization grains decreased with decreasing sharpness of the cold rolled texture. In the project under consideration the cold rolled crystals involved a range of initial orientations that, together with those studied earlier,&apos; provide information on several points. The first point is whether the recrystallization texture from a (111) [112] cold rolled texture, a stable end orientation that can be approached from different directions, correlates in any way with the initial orientation before cold rolling, or whether the recrystallization texture is entirely determined by the observable features of the cold rolled texture. The second point involves a preliminary study to see if the main components of the recrystallization textures correlate with the most probable active slip systems. The third point is to determine what effect departure from slip on one slip system has on the tendency to recrystallize. Experimental Procedure Nine specimens from a previous investigation and two additional ones from thicker stock (lot D) but of similar composition to the others were used in the present work. The latter two crystals, like the nine, were cold rolled to a reduction in thickness of 70 pct and the amount of widening was determined. Depending on their primary recrystallization behavior, the cold rolled crystals were given short or long anneals at temperatures of 980°C or higher. Table I summarizes the data on initial orientations, the textures obtained by cold rolling, and the anneals given to provide samples for the present work. Fine grained specimens were thinned to 0.002 in. thickness and placed in an integrating specimen holder. Chart recordings using a transmission X-ray method and MoKa radiation were obtained for diffraction from (110) planes. This method,&apos;,3 which gives data for all of the pole figure except a central region of 30" radius, proved sufficient to give generally five, and sometimes six, of the six possible pole concentration areas of any one component of the texture. These data, therefore, were generally adequate for a positive identification of each component present. The first texture obtained for specimen B-2 was poorly defined because of too coarse a grain structure and therefore too few crystals in each component for satisfactory X-ray reflections. The same

Jan 1, 1957

By D. A. Vaughan

COMPOUNDS in the U-N system have received little attention since the work of Rundle, Baen-ziger, Wilson, and McDonald in 1948.&apos; They described the three nitrides UN2, U2,N2, and UN as the only phases in this system. The region between UN and U,N, was reported to consist of the two phases while the region between U,N, and UN, is a homogeneous solid solution in which the U,N3, structure transforms with increasing nitrogen content into the UN, structure. This report presents the results of an X-ray diffraction study of the phases present in the region of the diffusion gradient on uranium reacted with nitrogen at several temperatures between 500" and 915°C. Several samples of uranium used in U-N gas-metal reactions by Mallett and Gerds were available for X-ray diffraction study of phase composition through the diffusion gradient. X-ray diffraction data were obtained using filtered iron radiation at intervals through the diffusion layer of the several samples on filings or turnings at approximately 0.001 in. increments down to the base metal. Representative X-ray diffraction patterns from various layers through the case on uranium after nitriding at 850°C are shown in Fig. 1. These data show that three different phases are present in the

Jan 1, 1957

By R. A. Generes, H. C. H. Darley

Laboratory tests showed that at elevated temperatures a reaction takes place between all metal hydroxides and clay muds, which results in a thickening or solidifying of the mud, the extent of which depends on the nature of the ingredients. Calcium hydroxide gave the strongest solidification whereas barium hydroxide only caused a mild thickening, indicating that the use of barium hydroxide muds instead of lime muds would be a good way of preventing high-temperature solidification. It was found possible to prepare barium mud in the laboratory with caustic soda and a thinner in the same manner as lime muds, and these barium muds had the same or better toleration of high solids content, resistance to salt contamination, and low gel strengths as the corresponding lime muds. Three field trials have been made with barium mud. The principal difficulty encountered was in determining the correct proportions of the tourly treatments required to maintain low gel strengths. A satisfactory systern was finally developed, and low gels were maintained throughout the third test. The wells on which the trials were made were not carried deep enough to test the resistance to solidification adequately, but oven tests at 350°F were made periodically and no tendency to solidification was noted except immediately after severe cernent contamination had introduced excessive amounts of calcium into the system. Although barium hydroxide costs considerably more than lime, the total mud costs were as low, and on the last well significantly lower, than the average cost of lime mud wells drilled in the vicinity. INTRODUCTION The advantages of repressing dispersion and hydra-tion of clay cuttings carried in the mud, particularly when drilling through thick clay formations, are well recognized. This repression is generally achieved by the use of lime, and lime muds have in consequence the desirable characteristics of high toleration of solids, low thixotropy, and good resistance to contamination. They have, however, the disadvantage of high-temperature solidification. This phenomenon has been described in detail by Gray et al, who have shown that it is the result of a chemical reaction between the hydroxides and the clay minerals. The work described in this paper was undertaken to find a substitute for lime which would not cause this solidification. LABORATORY EXPERlMENTS The principal positive requirement for a substitute for lime is that it should repress the hydration and dispersion of clay. It is well known that monovalent cations promote hydration while polyvalent cations repress it. Therefore, a few representative polyvalent salts and hydroxides were tested to determine whether they could be used as substitutes for lime. Their efficiency at repressing hydration and dispersion was measured by means of the clay-volume test. It has been shown elsewhere&apos; that this test is a good measure of degree of dispersion of clay in suspension and that hydration accompanies and correlates with dispersion, so that measuring one measures the other. The test is made by centrifuging a 1:100 mixture of mud and 1-N NaCl and observing the volume of sediment—the greater the volume, the greater the dispersion. The tendency to caux solidification was measured by heating the muds in pressure vessels for 16 hours at 150°F and 370°F. An approximate quantitative

Jan 1, 1957

Jan 1, 1957

By H. W. Mossman

Three aspects of magnetite smelting are discussed. The first is the working out of equilibrium conditions for eliminating sulfur. The second is the influence of magnetite solubility on the difficulty of tapping the reverb matte. The third is an approximation of the equilibrium conditions in the reverb gases which govern whether magnetite is mode or reduced in the reverb slag by these gases and by any iron sulfide in the slag. MAGNETITE has had a varied history in the Hurley Smelter since its start in 1939. Magnetite determinations on the smelter products are made regularly only on the monthly composite samples. Variations on the monthly averages are shown in Table I. Magnetite which drops from the slag and matte in the reverb has some slight bottom buildup which comes and goes, but no substantial accumulation from this source has been found at the end of a normal nine months&apos; furnace campaign. However, there has been some low grade magnetite bearing material mixed with considerable A1,0,, which has slid down from the bottom of the sloping flue between the reverberatory furnace and the waste heat boilers. This accretion has required drilling and blasting near the skimming end of the furnace. The magnetite has interfered with tapping at times. When the smelter was first started, tapping trouble from magnetite was extremely severe. Increasing the reverberatory furnace temperature by putting in an air preheater and a Dutch oven has helped greatly, although there still is occasional tapping trouble. When the present series of physical chemistry articles on copper smelting started coming out in 1950, they were read with interest, but no immediate application was seen for them. Results of some laboratory work in 1952 aroused a much stronger interest in this physical chemistry. A series of melts was made on some converter slags, which had magnetite in very large grain sizes, with the object of reducing the grain sizes in the slag, as it was known that it was easier to handle in the reverb in that condition. Anything done in the tests greatly reduced the grain sizes—even in the controls, where nothing was done except melt the slag and cast it. There was more magnetite in the slags after the tests than before, and with wide variations. There were no obvious reasons lor much of what happened in these tests. Much of the base material published in English in this field was made available for study. Recalculations were made on many of the type problems, and part of the data was reduced to local temperatures and compositions. Explanations were found for what happened in the 1952 series of tests on converter slags, and the same principles turned out to be a description of much of what magnetite does in the reverb. This article is to present the results of that study, from the viewpoint of applying the technical material in definite numerical form to the operating conditions in both the converters and the reverberatory furnaces at the Hurley smelter. Table I. Magnetite Variations on Monthly Averages, 1939 to 1955 Pet Magnetite Lowest Highest Average Converter slag 13.6 43.3 25.4 Roverb slaa 2.7 20.9 8.7 Matte 28 15.9 98 In general it was found that magnetite is made or reduced in both the converters and the rever-beratory furnace, depending on variations of temperature, matte composition, and reverb gas composition occurring in ordinary plant operation. Within reasonable limits, the field conditions for formation or reduction can be predicted, and probably can be set up and maintained. Converter conditions affecting magnetite formation can be put into numerical values better than for the reverb from purely technical calculations. The converter can be operated so as to keep the magnetite in the slag down to between 12 and 14 pct and still give satisfactory life for the converter brick. This depends upon having converter flux available which will make a slag with a good separation without raising the temperature too high. In the Hurley reverb and others with similar conditions, it is likely that a compromise of conditions will give a reasonably good control of combustion and still keep the magnetite from building up on the bottom. This discussion consists of three main parts. The first is the working out of the equilibrium conditions in the converter for determining in which direction the reaction 3 Fe,,O, (s) + FeS (1) F? 10 FeO (1) + SO, will go under actual converter operating conditions. The second deals with the influence of the solubility of magnetite in the slag and matte in the reverb on the difficulty of tapping matte. The third is an approximation of the equilibrium conditions in the

Jan 1, 1957

By Robert G. Nisle

In conducting a pressure build-up test on an oil well, it is often necessary to shut-in the well for a short time prior to initiation of the test. The effect of such a short tern shut-in on the resulting pressure build-up curve is derived. The derivation is based on the Kelvin point-source solution and is a straight forward extension of the fundarnental theory. The magnitude of the effect is evaluatecl and illustrated by an example. It is shown that if the production subsequent to the short term shut-in is at least 10 times the duration of the shrct-in, the effect will he less than 10 per cent. INTRODUCTION It often happens that before a pressure build-up test can be made an additional valve must be mounted on the wellhead, or on arrival at the well, it might be learned that the well had been shut-in several hours the previous day because of a shortage of tankage. In such cases the question is How will such an interruption of production affect the results of a pressure buildup test This work explains how to take account of such a short term shut-in in order that the test can proceed without further delay. The solution presented here makes use of the Kelvin point-source solution used by Horne1 in his treatment of the pressure build-up in wells. Use is also made of the super-position theorem. MATHEMATICAL DERIVATION The well is assumed to have been in production at a constant rate for a relatively long time (several days or more). It is then shut-in for a short time, after which it is again placed in production at the previous constant rate. It continues to produce at this rate until shut-in for a pressure build-up test. The Kelvin point-source solution is expressed by Eq. 1. The sequence of production rates is listed in Table I. TABLE 1 — SEQUENCE OF PRODUCTION RATES Time interval Production Rate At time AT the pressure will be the resultant of the sequence of production rates shown in Table 1. An expression for the super-posed effects may be derived from this table. (Effect of + q for T + ? T) + (Effect of - q for T + ?T-t,) + (Effect of + q for T + ? T - t,) + (Effect of - q for ? T) = Resultant........(2) The desired result is obtained by substituting the effect defined by Eq. 1 for the terms in Eq. 2. The result is Eq. 3. When the logarithmic approximation is made for the exponential integrals and the terms collected the result is Eq. 4. Let T — t2 = T = flowing time following short term shut-in t2 — t1 = 6 = duration of short term shut-in Then T - t1 = r + 6 Substitution of these quantities in Eq. 4 gives p(rw ?T) = P,, -When d<<t - AT then d—&apos;-, T— approaches 1. r + AT In this case the effect of the short term shut-in may be ignored. In order to get some idea of the numerical magnitudes involved take the worst possible case, when AT = 0, that is at shut-in. If the error is made less than some maximum acceptable value at this time, it will be less than the maximum for all subsequent times. d + r Let the difference between the value of y-— and 1 be less than 0.1. Then —6+r — 1 < 0.1 S < O.l T Therefore, if the flowing time following a short term shut-in is at least 10 times the duration of the short term shut-in, the error introduced by ignoring the short term shut-in will not exceed 10 per cent of T+AT A T

Jan 1, 1957

By L. A. Willey

IN 1953, a method for filtering a liquid phase from solid phases while in equilibrium at elevated temperatures was devised at the Alcoa Aluminum Research Laboratories. Since then, it has been applied to the investigation of liquid-solid equilibrium in metallic systems. In application, the method simplifies the centrifuge filt.ration procedure as developed by Scheil and described by Gebhardt Fig. 1 shows a sketch of the filtering apparatus located within a thermal analysis furnace. It consists of a stainless steel filter crucible A, into the bottom of which a porous carbon filter disk B, 1 3/4 in. diam by 1/4 in. thick, is sealed to the shoulder and rim with carbonaceous cement. The base of the filter crucible, machined to an angle, fits into a tapered seat at the mouth of a stainless steel vacuum chamber C. A connecting tube from the vacuum chamber to a vacuum line also serves as a means for supporting the apparatus from the base of the furnace. An alundum crucible D of 25 ml capacity is placed with- in the vacuum chamber below the filter for collecting the filtrate. Two thermocouples E, in stainless steel protection tubes, which extend from 1/16 to in. above the center of the filter, are mounted on the rim of the filter crucible. One thermocouple is used in differential connection with the furnace control thermocouple to regulate rates of heating and cooling. The other serves as a means for recording the temperature of the alloy prior to filtering. A suitable mold coating is used on exposed surfaces of stainless steel parts to guard against attack upon these parts as well as to avoid contamination of the alloy samples. A mold wash prepared from precipitated CaCO, is suitable for aluminum alloys. The porous carbon for the filter disks and the carbonaceous cement, grade 200 (graphite base), were obtained from the National Carbon Co. Porous car-bon, grade Nos. 10 to 60, has been employed. Grade No. 40, however, appeared to give the optimum advantages in operation. In operation, an alloy sample is remelted and heated to about 50°C above its liquidus temperature. At the same time, the filter apparatus is preheated to about the same temperature. The alloy then is cast into the filter crucible.

Jan 1, 1957

By C. S. Samis, D. P. Seraphim

In the presence of oxygen, galena is oxidized in an aqueous medium containing ammonium acetate in accordance with the following reaction: PbS + 1/2 0, + 2 NH~Ac -» PbAc, + So + 2 NH: + H2O. This reaction was studied in an autoclave under oxygen pressure by polarographic measurement of the concentration of lead ion in solution. Oxidation rate is parabolic. The reaction products are lead acetote and elemental sulfur, the latter forming a film on the galena crystal. Reaction kinetics appear to be determined by the diffusion of lead from the galena phase to the solution interface through the film of sulfur. RECENT applications of pressure leaching on a commercial scale have emphasized the metallurgical importance of the oxidation of sulfide minerals in aqueous media by oxygen under pressure. Research experience has shown that sulfates, thio-nates, and metal oxides are the products of humid oxidation of sulfide minerals in basic solutions. The metal oxides may be solubilized in the presence of a complexing ion.&apos; Certain oxide minerals are also amenable to treatment by this type of oxidation.&apos; Several kinetic studies have been made of reactions of this type. Stenhouse&apos; found that pyrite (FeS?) oxidized in a sodium hydroxide solution to produce a soluble sulfate and an insoluble layer of iron oxide and that the kinetics of the reaction were controlled by oxygen diffusion through the oxide layer. Andersen&apos; studied the oxidation of galena (PbS) in a sodium hydroxide solution under oxygen pressure. He found the lead and sulfur to be simultaneously oxidized to produce plum bite ions and sulfate ions, and that the reaction rate was proportional to the surface area of the galena. The kinetics appeared to be determined by the reaction of oxygen and water with the galena surface. In each of the above reactions the metal and sulfur components of the mineral were oxidized simultaneously and at equal rates. In the present study the alkaline medium has been replaced by an approximately neutral solution of ammonium acetate in which lead sulfate is soluble. Under the conditions no sulfate was produced and no sulfur could be detected in the solution. The metal component of the mineral was solubilized and the liberated sulfur remained as a film of elemental sulfur on the surface of the galena crystal. A kinetic study of this reaction was undertaken to establish the kinetic mechanism and to determine the rate controlling step. Specific reaction rates were determined by oxidizing crystals of galena of measured surface areas in an autoclave maintained at the desired temperature and oxygen pressure. The rate of reaction was followed by measuring the concentration of lead in the ammonium acetate solution with a cathode ray polarograph, employing stationary platinum electrodes incorporated in the autoclave. Experimental Materials and Equipment Crystals of galena obtained from Violamac Mines, Retallack, B. C., were selected for oxidation because

Jan 1, 1957

By I. Fatt

This paper proposes the network of tubes as a model more closely representing real porous media than does the bundle of tubes. Capillary pressure curves are derived from network models and pore size distributions are calculated from these curves. In this way is shown the difference between the true and calculated pore size distributions when the capillary pressure curve is used to obtain pore size distribution for porous media. INTRODUCTION Despite the technological importance of the laws governing flow through porous media, many of these laws have not yet been clearly formulated. This is especially true of the laws governing multiphase flow. The static properties, such as the capillary pressure curve, are also not at present interpretable correctly in terms of the pore size distribution and other structural properties of porous media. In the absence of any well founded theoretical description of fluid flow through porous media, many empirical descriptions have been proposed. In addition to the strictly empirical flow equa- tions, some equations have been developed rigorously from simple geometrical models of the pore spaces. These equations are only as valid as is the model used in their development. The two models used in the past, the sphere pack and the bundle of tubes, have been too simple, and as a result, the equations derived from them have failed to predict the observed properties. Agreement between theory and observation has been achieved for these models by inserting parameters of doubtful physical significance. The work to be reported here was undertaken in the belief that the study of a model more closely resembling most real porous media than does the sphere pack or bundle of tubes would yield useful information concerning the structure of real porous media and the relation between structure and flow properties. There was no intention of developing any calculational procedures, as for example calculating relative permeability from capillary pressure data. The objective of the study was instead to develop a better qualitative understanding of the relation between the various measurable properties of porous media. The model chosen for study is the network of tubes in which each tube represents a pore space in the porous medium. Microscopic observations leave no doubt that sandstones and clastic carbonates are three-dimensional irregular networks of irregularly shaped pores. The irregularity of these structures makes any accurate theoretical study of their properties impossible. Results from an oversimplified model such as the bundle of tubes are worthless when applied to real systerns. The sphere pack model, on the other hand, not

Jan 1, 1957