Search Documents

By R. E. Anderson, R. S. Busk

The mechanical properties of many nonferrous alloys can be modified by heat-treatment. This is almost always effected by controlling the amount of alloy in solid solution and the amount and distribution of second-phase material. The latter often is accomplished through precipitation or age-hardening treatments. The procedure is to solution-heat-treat the metal to provide a supersaturated solid solution and then cause precipitation of the dissolved material at some temperature below the solvus for the alloy. The generally used magnesium sand-casting alloys arc based on the ternary alloy system Mg-Al-Zn. Solid diffusion reactions in the system are slow enough so that a substantially completely supersaturated solulion is maintained even though the metal is relatively slowly cooled from heat-treating temperatures. Consequently, it is general practice to air-cool magnesium-alloy castings from the heat-treatment temperature prior to aging at an elevated temperature. Since it is necessary with many other alloys to cool quite rapidly before aging if optimum benefit from the aging is to be obtained, this study was undertaken to determine the effects of quenching on magnesium alloys. The] alloys used are shown in Table I, being selected as typical of the presently used magnesium alloys. Cooling Rates Since quenching is a means of rapidly extracting heat, there are two factors of interest in its study: (I) the rates of cooling that can be obtained and (2) the effect of various rates on the as-cooled as well as subsequently aged metal. The cooling rates were measured by drilling a hole 1/16- in diameter longitudi~lally in the center of a cylinder % in. in diameter and 3 in. long. The drilling was stopped to place the end of the hole at the center of the long axis of the cylinder. An iron-constantan thermocouple was inserted in this hole and wedged in place. The temperature drop during rapid quenching was recorded by a special1y built General Electric potentiometer recorder capab1e of measuring ' 500°F. temperature drop in 1/10 sec. For the slower cooling rates in air or oil, the temperature drop was measured by a Leeds and Northrup potentiometer recorder with the chart speed increased to One inch per minute' The cylinder was heated to the desired temperature, quenched as desired, and the temperature-time curve recorded. The cooling rates in still air, in oil at 350°F., in water at 180°F. and in a cold, high-pressure water spray were determined in this manner. The results of this study are presented in Fig. I. There is a great difference between water quenching and either air or oil quenching. There is little difference between the hot water quench and the cold water spray. Cooling rates were also

Jan 1, 1945

By C. K. Stoddard, R. G. Knickerbocker, E. T. Leidigh, R. R. Lloyd, K. L. Mattingly

During July 1941, a study was initiated at the Boulder City Experiment Station of the Bureau of Mines on proposed methods for the production of magnesium metal. The major emphasis was placed upon development of a process that required minimum reliance upon the sale or utilization of by-products to meet economic competition from processes already in operation. It was felt that only through the development of such a process could the nation's vast resources of dolomite and low-grade magnesite that are contiguous to large blocks of firm power be properly utilized. During the course of exploratory tests on electrolytic and electrothermic processes, it was noted that fused magnesium chloride would dissolve appreciable quantities of magnesium oxide in the presence of small amounts of boric oxide. The use of such a solution in an electrolytic cell employing a graphite anode and a steel cathode caused the deposition of magnesium at the cathode and the evolution of carbon oxides at the anode with minimal amounts of chlorine The original results were sufficiently encouraging to justify further investigation on an enlarged scale, since the process seemed to present advantages over other proposed processes.1,2 for the direct use of magnesium oxide in a fused chloride electrolyte. When work oil a larger scale was initiated it was found that the addition of boric oxide to the electrolyte resulted in dispersion of metal and constantly decreasing current efficiency. However, by this time solubility studies had shown that magnesium oxide was sufficiently soluble in magnesium chloride melts containing no boric oxide to effect the same anode reactions, and development work was continued. Over two years of development work have been carried out, and considerable work remains to be done. It is desired to emphasize the fact that many of the difficulties met require a long period of continuous operation before they become serious enough to affect operation of the cell. ACKNOWLEDGMENTS This paper is one of many reporting on various aspects of the Bureau of Mines' program initiated in August 1939 by passage of the Strategic Minerals Act the scope of which was greatly expanded by subsequent legislation. Some of these papers are published as war minerals reports. others as bulletins, technical papers, reports of investigations

Jan 1, 1949

By L. M. Pidgeon, W. Curlock

FREE energies of formation of zinc sulfide and magnesium sulfide had previously been estimated to an accuracy of ± 5.0 kcal per g mol. In the present work, these values were determined experimentally. As the determinations of the free energies of formation of zinc sulfide and magnesium sulfide presented different problems, separate experimental procedures were employed for each. ZINC SULFIDE It is difficult to measure the free energy of formation of either zinc sulfide or magnesium sulfide by measuring their decomposition pressures directly, as they are very stable compounds. An attempt was made by Jellinek and zakowski3 to study the equilibrium. zns(s) + H2(g) = Zn(g) + H2S(g) [I] They passed hydrogen over zinc sulfide and analyzed the gases leaving the reaction zone for H2S. They were unable to determine the true partial pressures of the H2S by this method, as some of the H2S on being cooled from the reaction temperature, reacted with the zinc in the gas to produce ZnS. Consequently, they were unable to establish any true equilibrium data for reaction [I]. More recently,' the equilibria ZnS(sphaledte) + Fe (s) — FeS(s) + Zn(g) [2] and ZnS(sphalerite) + 2Cu(s) — Cu2S(S) + Zn (g) [3] were studied. As the standard free energy of formation of Cu2S is known to * 3.0 kcal, and of FeS to ± 1.0 kcal, it should be possible upon performing equilibrium studies on reactions [2] and [3] to deduce the standard free energy of formation of ZnS (sphalerite). However, as both of these equilibria involve 2 solid sulfides, and as it is possible for these sulfides to dissolve in one another, it is necessary first to ascertain the activities of the various sulfides in these solid phases.

Jan 1, 1959

By Francis Clark

WHEN 60:40 brass is heated to 825° C., given a drastic quench to obtain the beta solid solution, and reheated, various changes take place in the structure. Reheating at 200° C. causes a fine, granular, sorbitic structure to appear which has been considered alpha solid solution. These particles coalesce at higher temperatures of reheating, and at 470° C., the alpha forms twins. A further study of these transformations was considered worth investigating. EXPERIMENTAL WORK The object of the experimental work was to study the effect of mechanical work on rolled 60:40 brass, quenched and reheated, and the mechanism of twinning in the alpha reeds of a furnace-cooled specimen. It was desired to determine the effect of mechanical work on the transformations taking place on reheating the quenched material, both at 200 and at 470° C. A study of the nature of the structure resulting from the breakdown of the beta at 200° C. and a study of the mechanism of twinning above 470° C. were considered problems for investigation. The question of the twinning of the alpha reeds was also an important phase of the work. With high-power magnifications, there was hope of following these processes.

Jan 1, 1927

By Herbert Johnson

DURING the past 10 or 12 years very little information has been made generally available concerning the commercial possibilities of separating materials by means of static electricity; and yet during that same period important improvements have been made in various branches of the science of electricity, which, when taken together, and applied to electro-static separation, have resulted in important improvements in that art as well. For example, much improvement has been made in high-voltage electrical equipment such as full-wave vacuum-tube rectification and improved mechanical rectification. Great strides have likewise been made in the development of insulators for high-voltage work, not only in the materials used but also in the design of the insulators themselves. Again, in another field, the development of air-conditioning equipment has improved the technique of controlling the surface condition, through drying or humidifying, of the various materials that are passed through the electrostatic separator. In many authoritative publications and textbooks, the electrostatic separation process is declared to require a balance far too sensitive for general commercial application. For example, one publication1 in the past has referred to an unfavorable effect on the process caused by varying atmospheric conditions such as humidity. Some2 have even gone so far as to state that sunlight and shadows may seriously affect the separating efficiency of the process. Such statements may have been true in the early development of the art, when the source of static elec-tricity was derived from a friction disk machine, such as the Wimshurst. The Blake Mosher equipment and the work of Huff in applying motor-generator sets, transformers and mechanical rectification overcame much of this kind of objection to the commercial application of the elec-trostatic separating process.

Jan 1, 1938

By H. R. Thresh, A. F. Crawley, D. W. G. White

The densities of liquid tin, lead, and Sn-Pb alloys have been measured over a range of temperature above the liquidus. In all cases, data can be adequately represented by an equation of the type p = a + bT. For pure tin, the values of a and b are, respectively, 7.139 and 7.125 x 10-4, and for pure lead, 11.060 and 12.220 x 10-4. At constant temperature, molar volumes in the Sn-Pb system vary linearly with composition. DURING the course of a long-term program at the Department of Energy, Mines and Resources, Ottawa, Canada, the densities of liquid tin, lead, and Pb-Sn alloys were studied. The work reported herein draws on two sets of results independently achieved by Thresh, on the one hand, and by Crawley and White, on the other. EXPERIMENT The method and apparatus were originated by Thresh and have been described in detail in Mines Branch reports.172 In operation, the 14 cu cm graphite pycnometer is put in the furnace as shown in Fig. 1 after a machined charge has been placed inside the pycnometer and the lid screwed down. The dimensions of the charge are such that, upon melting, a small excess of liquid metal is discharged through the capillary hole to displace the weighted float above. When the pycnometer has been equilibrated at the experimental temperature, the

Jan 1, 1969

By Franz Wever

ACCORDING to Tammann,1 the explanation of the effect of mechanical deformation in producing changes in the properties of metals is one of the most important problems of physical metallurgy, taking rank with the study of the constitution of alloy systems; and this problem has long attracted-the attention of practitioner and scientist alike. Its solution was not advanced materially until Tammann2 set up his translation hypothesis with its crystallographic basis, while other hypotheses, such as the amorphous metal hypothesis of Beilby3 and Rosenhain,4 have been shown by more intensive studies to be less and less satisfactory. The principles of the Tammann translation hypothesis have proved to be useful even up to today and in spite of all of the recent accumulation of experimental data, while the differences of opinion which have arisen relate to the extent to which the hypothesis accounts for the observed changes in properties and to what extent further assumptions are necessary. Stimulated by the proposals of Tammann, there soon developed a lively experimental activity which aimed at the elucidation of the structural or crystallographic changes produced by the mechanical deformation of metals. Parallel movements of crystal "blocks" along definite crystal slip planes had already been observed by lowing and Rosenhain5 in 1900, in metals which had been moderately deformed but without shedding light on the crystallographic nature of the processes accompanying more severe deformation. The solution of this important problem was not advanced until a much later date, or until the methods of X-ray crystal analysis had become available. Shortly after the discovery of the diffraction of X-ray by crystals, symmetrical diffraction effects were

Jan 1, 1931

By Robert H. Richards

DuRing the winter of 1868-9,I was called upon by Professor F. H. Storer, to put up the Bunsen filter pump in the chemical laboratory of the Masschusetts Institute of Technology. As the laboratory is on the lower floor, it was found necessary to use a great deal of cumbrous pipe and apparatus to get the necessary column. It was then suggested that if an instrun~ent could be devised which would make use of the hydrant pressure in the service-pipe, it would do away with the objectionable features of the Bunsen pump. After using the Bunsen pump for some years, the jet pump to be described in this paper was devised, and it has since been adopted by Prof, Wing in the quantitative laboratory of the school. I am much indebted to Prof. Wing for his aid in starting the manufacture in brass of these jet pumps, whieh are now to be had in Boston. The jet pump much resembles the Giffard injector in form. It, differs from it in the fact that water is the impelling fluid, and air the impelled, while with the injector steam is used to impel water. The principle of condensation of steam, which is availed of in the injector, is entirely wanting in the jet pomp. The jet pump consists in a water jet, w, (see figure), a constriction or waist, a, and a waste tube, o. The success of the jet pump depends on the follow ing conditions: 1. The relation between the sizes of sectional area of a and w. ' 2. The proximity of n and w. 3. The form and angle of the two hollow cones whose vertices make the constriction a. 4. The relative size of sectional area of w and o. 5. The zigzags, or an equivalent means of making foam. In the following discussion, let a, w, and o repre sent the diameters of these parts of the jet pump. A number of experiments were' .tried to ascertain

Jan 1, 1879

By F. L. Bosqui

INTRODUCTION The history of the development of gold metallurgy in South Africa is divisible into two periods: That preceding the introduction of the cyanide process on a commercial scale in 1890; and the 24 years intervening between that important event and the present time. The period between the discovery of the banket reefs of the Witwatersrand and the year 1890 was one of phenomenally rapid progress in mining development, but of no special interest to the metallurgist. There were no strikingly original or distinctly local advances in the treatment of gold ores. Californian practice in stamp milling and amalgamation prevailed, in mills ranging in equipment between 5 and 50 stamps, operating within a wide range of efficiency, and under the trying conditions usually en¬countered in a new and isolated field. The somewhat incomplete records of gold output of that period show that in December, 1887, there were 20 producing companies in the Witwatersrand district, of which 10 had mills, the largest being of 20 stamps. The only official record of returns for May, 1887, was that of the Wemmer mine, whose modest achievement with a 5-stamp, mill was 100 tons crushed, producing 887 oz. 3 dwt. of gold. This is interesting in view of the .present-day output of this field, which in 1913 reached 8,430,998 oz. The rapid increase of production during this first period (May, 1887, to January, 1891) is shown by the following summary for the year 1890:1 Total tons crushed 702,828 Number of stamps in operation 1,046 Average number of tons crushed per stamp per day 2.36 Yield of gold, ounces 494,817 Yield per ton, pennyweights 13.36 The stamp duty ranged between 1 ½ and 4 tons per day, according to weight of stamp, fineness of screen, and operating skill available. The prevailing weight of stamp was about 900 lb., and the screen, 900 meshes to the square inch.

Jan 5, 1915

By Paul Merica

ONE of the most useful, and at the same time least commonly used, methods of thermal analysis for the determination of transformations in metals and alloys consists in the recording of the tune intervals required for successive increments of temperature change during heating or cooling, the temperature of the furnace containing the specimen being altered at a uniform rate. The curve obtained by plotting these time intervals as a function of the mean temperature of the specimen during the interval is called the inverse-rate curve. It is probably due to the fact that no simple and convenient method has apparently been available for the measurement of the successive time intervals that this method has not been so generally used as, for example, the differential method, for which several tykes of automatic or semi-automatic apparatus have been designed. Whenever this method has been used, the intervals have usually been measured with the use of a chronograph; its operation as practised at the Bureau of Standards' is as follows: The temperature of the specimen is measured by a thermocouple and a dial potentiometer. The operator sets the potentiometer at successive values of the electromotive force differing by equal increments, usually 0.02 millivolt, and records the exact instant on the chronograph, by pressing a contact key, at which the galvanometer coil passes through its null position. Two-second intervals are also recorded on the chronograph record, and the number of 'seconds elapsing between successive signals is afterward counted from the record and plotted as a function of the electromotive force or of the temperature. This is an admirable method and by it most minute thermal arrests may be detected, but it requires a good chronograph, which is generally difficult to obtain, and the time of one operator during the recording and, subsequently, to read the intervals from the record; the latter operation often takes from one to two hours.

Jan 7, 1919

By C. T. Bischoff

DURING the past few years geochemical testing for traces of heavy metals in water, soil, rock, and vegetation has aroused increasing interest. Various techniques for field and laboratory determinations have been described in the literature, as have some of the results of application. However, little information has been published regarding application to glacial terrain. Over 90 pct of the Canadian Shield is overburdened, resulting in high costs for mineral exploration once the outcropping ore deposits have been found. This has been largely responsible for the widespread application of mining geophysics in Canada, permitting concentration of effort on area or zones considered most favorable. However, geophysical interpretation has its limitations, since at least 90 pct of the structures indicated thereby contain no valuable minerals. A more direct approach is therefore highly desirable. If underlying base metal mineralization can be detected by sampling soil or vegetation at moderate cost this should prove of great help in locating new discoveries or extending known ones. A large proportion of Canadian ore deposits contain appreciable copper or zinc, even where these are not the principal economic metals. Consequently the field of application is a broad one.

Jan 1, 1954

By J. H. Swisher

The solubility of graphite in CaO-S2O2-Al,O3 slags was measured by equilibrating slag samples with graphite crucibles and CO gas. Carbon contents as high as 2 ut pct were obtained in CaO-saturated, CaO-A1,O3 slags, and 1.3 wt pct in slags of the composition CaO.Si0,. Although the observed conditions for Sic formation were in agreement with those predicted from thermodynamic data, CaC, was found to form at a lower temperature than predicted frotn thermodynamic data. From measurements of the equilibrium carbon content as a function of CO Partial pressure, it was found that carbide ions dissolve in CaO-A12O3 melts with a valence of minus two. The carbon content increased with CaO concentration in Ca0-Al,O3 melts and increased with SiO, content along the CaO'AlO3-CaOSi0 join in the ternary system. When solid CaC2 was added to CaO-A12O3 and CaO-SiO2-A12O3 slags, it was found that one of the oxides in the slag was reduced by the carbide (Al2O3 in the forrner and SiOz in the latter). In electric furnace steelmaking, a double-slag practice is frequently used to meet alloy specifications. Initially a flush slag, which is oxidizing in nature, is used to remove phosphorus and carbon from the steel bath. Later in the refining period, the flush slag is replaced by a highly reducing carbidic slag. When calcium carbide is formed in or added to a finishing slag, the slag is effective as a desulfurizing agent and also permits alloying elements such as chromium, vanadium, and tungsten to be added to the slag in the form of oxides. The oxides are readily reduced by calcium carbide, thereby minimizing the use of expensive ferroalloys. More work has been done on the thermodynamics of silicon carbide in slags than on calcium carbide. Baird and alor' and Kay and alor' determined the free energy of formation of Sic by measuring the partial pressure of CO in equilibrium with solid silica, silicon carbide, and graphite. Using a similar technique, they determined SiOz activities in CaO-SiOz and Ca0-Si0,-A1203 slags. Rein and chipman3 also determined the free energy of formation of Sic using slag-metal equilibrium measurements. A literature survey has uncovered only one experimental study of the behavior of CaC, in slag systems. Shanahan and cooke4 report the results of some preliminary experiments on the solubility and stability of CaC, in a CaO-A1,03 and a Ca0-Si0-A1,03 slag at a temperature of about 1500". The carbon solubility as CaC, in a slag containing 50 pct CaO and 50 pct A1203 was reported to be 0.6 pct. They also review earlier work on the binary CaO-CaC, system. A eutectic exists in this system, but various investigators disagree on the eutectic temperature and composition. eal has given an explanation for carbide furnace erruptions in terms of the thermodynamic properties of CaC,; his analysis is not based on experimental data, but on compiled data for the free energies of formation of CaC, and CO.' , These data for steel-making temperatures are all extrapolated from the results of low-temperature measurements. In the experiments described in this paper, slag samples were equilibrated with graphite crucibles and with mixtures of CO and argon or with CO gas at 1 atm total pressure for measurement of the carbon solubility. Most of the work was done on Ca0-A1203 binary slags, although in some experiments CaO-SiO, and Ca0-Si0,-A1,03 slags were used. EXPERIMENTAL Slag samples of the desired composition for the solubility measurements were obtained by blending pre-fused master slags. The master slags were prepared by fusing mixtures of reagent-grade CaC03 with either A1,03 or Si0, in a graphite crucible. The master slags were crushed, then decarburized in air in a muffle furnace at 1200O C. A schematic diagram of the apparatus is shown in Fig. 1. The source of carbon for the solubility meas-

Jan 1, 1969

New Products Equipment

Jan 10, 1951

By C. H. Bowen

Industry needs a generally applicable means of defining average grain sire and grain size distribution. Students of sediments have explored this field, employing methods that might also prove useful in engineering problems. Before attempting to solve specific problems it is well to review the derivation of commonly used grade scales and the reasons for their selection. This aspect of the problem seems largely to have been lost, and a review of basic factors may suggest causes for failures in using size analysis data.

Apr 1, 1956

By G. L. Kehl, Emilo Jaraiz F., J. S. Brett

The transformation of eutectoid beryllium bronze has been quantitatively investigated at 550° and 592°C, the temperature region where the products of p decomposition are a fine lamellar eutectoid and a coarse lamellar aggregate which replaces the fine eutectoid with prolonged annealing. Metallographic evidence indicates that the coarse lamellar aggregate forms preferentially in the most densely lamellated regions of the fine eutectoid and favors the hypothesis that the development of the coarse lamellar aggregate in the fine eutectoid is due to the occurence of a cellular segregation reaction. WHEN eutectoid beryllium bronze (Cu-94 pct, Be-6 pct) is isothermally transformed at high temperatures in the and y region after quenching from the fl field, the principal initial decomposition process is G one of growth of approximately spherical nodules composed of a number of lamellar colonies of the a and y phases. After the initial reaction has proceeded substantially or completely, depending on the transformation temperature, a second reaction occurs wherein the fine lamellar eutectoid is replaced by a coarser lamellar aggregate composed of the same oand yphases.' This reaction is not simply a spheroidization of the initial fine eutectoid but the nucleation and growth of a coarser, structurally different, and more stable distribution of the @and yphases. Fig. 1 illustrates the replacement of the initial fine lamellar structure by a coarse lamellar aggregate. The a phase is the dark mottled constituent; the light constituent the y phase. The phase diagram for the copper-rich end of the Cu-Be system2 is shown in Fig. 2. The a phase has the face-centered cubic structure characteristic of copper-rich solid solutions. The B phase is a disordered body-centered cubic structure, while the y phase is body-centered cubic, ordered (CsC1, B2 type). A. viswanathanS investigating Debye patterns of Cu-6 pct Be discovered that a transitory phase appeared on very rapid quenching from the /3 region which was absent when the quenching velocity was moderate. The phase could be assigned a body-centtred cubic structure with a lattice parameter of 2.876. Tempering at 100°C for 2 hr after quenching resulted in complete disappearance of the phase. The work of Fillnow and Mack' is the only previously published study of the isothermal transformation of eutectoid beryllium bronze. Their study elucidated the nature of decomposition at various subcritical temperatures in an exploratory fashion. The purpose of the research reported in this paper was principally to obtain quantitative information on the isothermal decomposition of the fl phase and to clarify the relationships existing between the fine lamellar eutectoid and the coarse lamellar aggregate. EXPERIMENTAL PROCEDURE The material used in this investigation was an almost eutectoid Cu-Be alloy bar furnished by D.J. Mack. The alloy had been melted under a protective carbon cover and centrigugally cast into a graphite mold preheated to 490 "C. Segregation was minimized by violent agitation during melting and pouring. The analysis of the casting was 93.85 pct Cu, 5.60 pet Be with traces of Si, Mg, Mn, Co, and Al. To determine the minimum soaking time necessary to insure specimen homogeneity, a number of specimens were held in the P region at 788OC for times fron 1 min to 12 hr and isothermally transformed at 550°C. Specimens betatized less than 12 min exhibited partial transformation at times shorter

Jan 1, 1961

By Irwin Roman

The literature of geophysics as applied to the discovery of mineral deposits has been very extensive during the past few years,' but there seem to be few references to the use of the method of least squares for obtaining better interpretations of the observed data.2 There seems to be a general reluctance among geologists and engineers to acquire the technique of least squares, in spite of the fact that a thorough knowledge of the theory is not necessary for the use of the method.

Jan 1, 1932

By E. W. Dewing

ROLIN1 in 1961 published a phase diagram for the CaF2-Na3AIF6 system in which substantial (-20 wt pct) solid solubility of CaF2 in Na3A1F6 at the eutectic temperature (945°C) was indicated. The evidence was that the halt in cooling curves associated with the eutectic was lowered progressively on the Na3AlF6 side. H olm2 has recently confirmed the experimental fact, but attributes it to evaporation losses shifting the composition into the ternary NaF-CaF2-Na3A1F6 system with a consequent lowering of the eutectic temperature

Jan 1, 1970

By Frederic P. Dewey

This old and well-known method of determining silver is, in bullion work, so far superior to the furnace-assay that it is looked upon with reverential awe by many, if not by most, users, and its ease of execution, with proper equipment, commends it highly where much commercial bullion work on silver is required. The method is so thoroughly well known that a description of it here may seem to be unnecessary, but many thousands of determinations are annually made by it in the U. S. Mint Service and its practice is there reduced to an art. This is necessary both for the sake of economy of time, and because high-grade work with it requires constant practice. It is useless for a person who uses it only occasionally to expect to attain high accuracy with it, without spending more time upon a detemination than is warranted in a busy commercial laboratory. It is always employed in the Mint service whenever possible, but its chief field is in the determination of silver in standard silver (ingots and coin), which is 900 fine in silver and 100 fine in copper, and I shall first briefly outline its use on this metal and then take up various points in detail, especially as related to the accuracy of the results obtained. For this determination 1,115 mg. of standard metal are weighed and transferred to a glass-stoppered bottle, the metal is dissolved in nitric acid, and 100 cc. of a standard solution of NaCl run in. The bottle is then vigorously shaken and a measured portion of a decimal salt solution added, and again shaken, if necessary. These operations are repeated until the silver is precipitated. Standard metal being 900 fine, 1,115 mg. should carry 1,003.5 mg. of silver, which is a convenient figure to work with.

Jan 1, 1914

By Jose M. Sobral

Approximate figures for petroleum production in Argentina for 1929 show an increase of only about 300,000 bbl. over production for 1928. This increase is due to greater yield in the Plaza Huincul and in the Salta regions. Table 1 shows the distribution of production in the various fields of the whole country, using estimates for the later months of the year. The outlook for production remains about the same as in 1928. It is believed that in northern Argentina there are regions that contain oil, but they are yet unexplored. Notable traces of oil at depths between 1280 and 1390 m. have appeared in a 1500-m. boring in Comodoro Rivadavia, but their importance is unknown.

Jan 1, 1930

By S. Floreen

Measurements have been mode of the effects of tempering and austenitizing heat treatments, the work-hardening characteristics, and the effects of test temperature and strain rate on the properties of a low-carbon Fe-18 pet Ni martensitic alloy. In many respects the alloy behaved quite similarly to cold-worked iron. One notable quality was the excellent ductility at temperatures as low as 20°K. Many of the qualities of the maraging steels could he related to the properties of the Fe-Ni matrix. THE 18 pet Ni maraging steels have demonstrated that unusual combinations of strength and toughness may be obtained by age hardening a low-carbon Fe-Ni martensite matrix.' These properties must, to some extent, reflect the properties of this Fe-Ni matrix, and therefore an understanding of the properties of this matrix is a prerequisite to a complete understanding of the steels. There have been several recent studies of Fe-Ni-C martensites, but not much attention has been paid to alloys with very low carbon contents. At low carbon levels the crystal structure of these alloys is essentially bee.2 Electron transmission microscopic examination of a 20 pet Ni binary alloy showed martensite platelets separated by low angle boundaries.3 Plastic deformation of the low-carbon alloys has been shown to proceed by wavy glide.4 The hardness of these martensites is typically RC 28, and their yield strengths are 70 to 80 kg per sq mm.2, 5 Their ductility is excellent. Room-temperature tensile elongations of 18 pet and reductions of area of 70 pet have been observed in an Fe-18 pet Ni binary alloy.5 These observations have provided a qualitative understanding of the flow characteristics of these alloys. To date, however, no thorough study of their properties has been made. In particular, it is not known to what extent the deformation characteristics of low-carbon martensites are similar or dissimilar to those of pure iron or other bee metals. The present work was undertaken to provide more detailed information on the flow characteristics of a low-carbon Fe-18 pet Ni martensite. PROCEDURES, RESULTS, AND DISCUSSION Materials. A 40-lb heat of the Fe-18 pet Ni alloy used in this study was made by vacuum-induction melting. The charge materials were electrolytic iron and electrolytic nickel. A carbon boil was used to achieve deoxidation. After the boil the heat was refined by additions of 0.1 wt pet Ti and Al. These additions are commonly used in the maraging steels to keep the carbon and nitrogen contents in solid solution at a minimum. After casting, the heat was

Jan 1, 1964