Search Documents

By F. C. Wagner, E. P. Klier, D. E. Nulk

The presence or absence of plastic strain at a cleavarage surface is a question of much importance, and upon its answer depends future possible theoretical work. To investigate this question back-reflectinn X ray patterns were obained on the cleavage facets of ferrite grains. The test set-up consisting of FeK colli- mated radiation, single grain material and stationary cassette and specimen will not lead to a diffraction pattern, in general, but is an ideal arrangement for the exami-nation of surface effects. A pattern taken on hydrogen purified

Jan 1, 1949

By William J. Priestley

Much time has been devoted, by metallurgists, to the study of steel after solidification and remarkable strides have been made in the heat treatment of steel, but less knowledge is available of the thermophysical activity of the constituents of steel prior to solidification in the mold. It is known that certain elements added to steel produce marked changes in physical properties, also that other elements added to steel produce similar changes, but we have only meager knowledge as 'to. how these elements combine in steel under different conditions of solidification. It is not sufficient to know, from chemical analysis, that a certain element is present in steel. We should know how this element is in combination with the other elements and whether the combination is such as will give the greatest physical properties. Certain elements go into solid solution with the iron, while others segregate to the grain boundaries and combine with the impurities collected there. Until it is known where an alloy produces the most beneficial effect and a means is determined for controlling its physical location by altering solidification conditions, or otherwise, we will not obtain the maximum value from our alloys. When molten steel freezes, it forms a heterogeneous mass of various crystalline constituents; and as the transformation of steel from a liquid state to the solid crystallized state is a critical step, involving as great a transfer of heat as any other operation in the making of finished steel, a variation in the rate of this heat transfer will have much to do with the arrangement of the various constituents in the solid state. The object of this paper is to show some of the effects on steel caused by variations in the rate of cooling in the ingot mold, particularly as to ingotism, segregation, dendrites, and intergranular material.

Jan 1, 1924

By R. A. Kinzie

In a conventional cement plant, the drying and heating of the raw material takes place in the upper section of a cylindrical kiln where the heat exchange is poor. In a Lepol kiln this part of the process is carried out on a traveling grate where the heat exchange is efficient. The increase in fuel economy justifies the greater complexity of the installation.

Jan 2, 1950

By Lucien Eaton

THE changes that have occurred in metal mining in the past 75 years include almost everything that we know about modern mining. It is true that in odd corners of the world mining is still carried on as it was before that period, but in the United States such instances are rare. Everything has changed to some extent. Even picks and shovels have changed in design and materials. At the beginning of this period steam power had been used for pumping and hoisting for nearly 75 years, but almost every other operation underground was performed by manpower. Although mining was carried on in a small way east of the Appalachian Mountains before the Revolution, and continued thereafter on an increasing scale for more than 100 years, it was not until the discovery of the iron and copper deposits in Michigan and Minnesota and the opening of the mineral areas of the West after the building of the transcontinental railroads that the real development of modern metal mining began. In the same period many problems of deep mining in South Africa were solved by new techniques in shaft sinking and hoisting. Before this time knowledge of mining and skill in its performance were handed down from father to son by the apprentice system, and the son learned to do things in the way his father and grandfather had done them. The rapid expansion of mining in the United States after the Civil War required more men than the apprentice system could supply, and the

Jan 1, 1947

By Alden Greninger

THE time-honored description of the growth of metal crystals to form polycrystalline aggregates is one in which two important steps are con-sidered: (1) nucleation, and (2) dendritic growth, each dendrite starting from its individual nucleus and resulting (upon slow cooling, assuming no solid phase changes) in a macrograin. This picture of the process of crystallization is incomplete, and it is with the hope of enlarging upon it that the following summary and correlation of experimental results are given. MOSAIC STRUCTURE For an exact definition of the mosaic structure of metal crystals-if, indeed, one can be found that will hold for all metals-one must await the results of much experimental work in this field. The writer's investiga-tions have been confined almost entirely to copper and a few of its alloys. The following terms are proposed, and will be used in this report: Macromosaic Structure l.-Large-scale mosaic structure; more specif-ically, mosaic structure of a scale large enough to produce splitting of Laue spots on back-reflection Laue X-ray patterns2. The deviation from exact parallelism of neighboring macromosaics varies from a few

Jan 1, 1935

By D. G. Osborne

Transportation cost is a key factor in both the profitability and competitiveness of coal marketing. With coal exportation growing rapidly, moisture control is important. Although in some cases, too much moisture reduction can lead to losses in transportation and pollution problems, there is normally justification for reducing moisture by mechanical means as much as possible. This paper reviews current technology of dewatering coal fines and examines the comparative capabilities of screens, filters, and centrifuges. Financial considerations are stated and implications of capital and operating costs on selection are discussed.

Jan 1, 1985

By George Rice

A PROBLEM of possible subsidence of the surface from mining opera-tions, which might have had disastrous results, arose in 1913 at the Brier Hill mine, of the Penn Iron Mining Co., near Norway, Mich., now managed by Pickands, Mather & Co. for the Bethlehem Steel Co. A double track and sidings of the Chicago & North Western Railroad passed over part of the mine, and if subsidence had reached the surface it might have affected the stability of the tracks. The chief purpose of this paper is to record the facts disclosed by investigations of underground movement from 1913 to 1919, when the tracks were moved, and subsequently at intervals, as engineering data of value from mining carried on below the tracks in the steeply pitch-ing lenses. A secondary purpose of this paper is to describe a novel method for determining the rate of speed of upward breaking above the mine excava-tions. This method was found effective and might be used elsewhere under similar conditions. The mine workings under consideration were developed from the Brier Hill shaft, which was circular, concrete-lined, 14 ft. in diameter, and about 900 ft. deep. They extended about 800 ft. westward from the shaft, and nearly parallel to a corresponding length of the railroad tracks. The highest part of these workings was at a depth of 400 ft. below the tracks (Figs. 1-12). The mining company had the right to remove the ore, the railroad assuming that the surface would be sup-ported. Finally, without legal controversy, an amicable adjustment was reached as to what should be done to lessen or obviate the hazard of subsidence.

Jan 1, 1934

By B. W. Frazier

Jan 1, 1882

ZAY JEFFRIES, Cleveland, Ohio (written discussion?).-The authors conclude that there is a certain average size of precipitated CuAl2 par-ticle which produces maximum strength and hardness in duralumin; that when the size of particle is smaller or larger than this particular size the hardness decreases. The writer agrees with this conclusion, because it seems to he directly indicated by the facts. Why does duralumin present this apparent discrepancy? Let us con-sider some physical aspects of the precipitation of CuAl2 from a saturated solution on cooling. When a molecule of CuAI3 is removed from the solvent, or matrix, and added to another group of CuAl2 molecules, as is known to occur on slow cooling, the forces of adhesion between the CuAl2 molecule and the solvent have been exceeded. Since a. change in tem-perature only is sufficient to cause precipitation, it must also be sufficient to cause the loss of adhesion bonds between the excess CuAl2 molecules and the solvent, or matrix. Lost adhesion bonds means loss of cohesion of the mass as a whole. When duralumin is cooled from 500° in a furnace, globules of CuAl2, large enough to be seen easily with a high-power microscope, are formed. There are, however, globules so small as to be hardly distinguishable, and others too small to be resolved are suggested by the non-uniformity of the surface appearance of the section. As the smallest globule of CuAl2 resolvable with a high-power microscope contains about 2,000,-000,000 molecules, it is evident that with rapid cooling submicroscopic particles of CuAl2 must be present in large numbers; in fact, after quench-

Jan 12, 1919

By Peter Soo

Pvestrained Ferrovac E iron has been neutron-irradiated at approximately 90°C to an integrated flux of 1020 nut (E > 0.82 mev]. The irradiation was found to produce an incveased temperature dependence of the flow stress in addition to a greatly increased athemal stress. Measurements of the flow stress and stress relaxation, from which the activation volume and activation energy for slip were deduced, show that neutron irradiation changes the rate -controlling slip process to one based on dislocation interactions with tetragonal distortions which are Produced around submicroscopic interstitial loops in the lattice. The study indicates that without prestraining prior to irradiation the chances of detecting a change in the rate -controlling slip process are greatly reduced because in the initial stages of slip a substantial fraction of the radiation defects are swept out of the slip plane by gliding dislocations. Thus, activation parameters which are subsequently measured are representative of a greatly reduced defect density and would not differ appreciably from those for unirradi-ated material. The large increase in the athermal component of the flow stress is probably connected with the presence of depleted zones in the lattice which are introduced by irradiation. ALTHOUGH fast neutron-irradiation has not been observed to markedly alter the activation parameters for slip in bcc metals,' small but significant changes do occur. Most experimenters agree that irradiation predominantly increases the athermal component of the yield stress.'-= In addition to this, Laidler and smidt7 have shown that in iron irradiated to 5 X 10" nvt and molybdenum irradiated to 10" nvt, changes occur in the activation volumes for slip. A similar conclusion has been reached by Milasin and Malkin8 for irradiated iron. Work by Ohr et a1.5 shows that for Ferrovac E iron, irradiated to 1.2 X 1016 nvt, small increases in the activation energy for slip also occur. So far these changes in the activation parameters have not been explained on a firm theoretical basis. One important factor which would minimize the chances of detecting a change in the slip mechanism upon irradiation is the presence of "channeling" which has been observed in molybdenum,9 niobium,10 and iron.11These channels are formed by gliding dislocations which sweep irradiation defects out of the active slip planes and thereby create zones in which continued dislocation motion is encouraged. The activation parameters for the dislocations gliding in the defect-free channels would, therefore, be similar to those for unirradiated iron and a change in the rate-controlling slip process would be difficult to detect. In the present work, an attempt has been made to reduce the effect of uneven deformation on the measured activation parameters for slip in neutron-irradiated Ferrovac E iron polycrystals, so that a more realistic assessment of the effects of neutron-irradiation could be made. Primarily, the experiments involve the irradiation of specimens which had been prestrained to 9 pct elongation at room temperature prior to insertion into the reactor. It was hoped that the introduction of a large number of evenly distributed dislocations would substantially decrease any channeling effect which might otherwise occur. MATERIAL AND EXPERIMENTAL PROCEDURE The starting material was vacuum-melted Ferrovac E iron, an analysis of which is given in Table I. The standard tensile specimen had a gage length of 1.125 in., a cross-sectional diameter of 0.120 in., and a re-crystallized grain size of 1.2 x 10-3 in. All tensile tests were conducted on a floor model "Instron" tensile machine at a strain rate of 3 x 10-4 per sec. The irradiation of the prestrained specimens was performed in the Brookhaven High Flux Beam Reactor to an integrated flux of 1020 nvt (E > 0.82 mev) at a temperature of about 90°C. All specimens were excap-sulated in high-purity aluminum sheaths which were lightly swaged around the samples to ensure good thermal contact. Subsequent measurements on the irradiated specimens showed that within experimental accuracy the swaging had not deformed them. EXPERIMENTAL RESULTS Fig. 1 shows the flow stresses for a series of unirradiated control samples. In order to produce a comparable dislocation substructure throughout the test sm range, all specimens were prestrained

Jan 1, 1970

By H. R. Payne, A. F. Gorton, H. A. Schwartz

In a previous paper1 we published what we believed to be a correct stable equilibrium diagram for an iron-carbon alloy containing + 1.20 per cent. silicon. The purpose of the present paper is to record the results of studies concerning the effect of silicon on the location of the eutectoid points of both systems, including also certain incidental observations of general interest. We prepared white cast irons containing roughly 21/2 per cent. carbon, 0.05 per cent. manganese, and 0.03 per cent. each of phosphorus and sulfur, but of accurately known silicon contents which varied from 0.40 to 3.32 per cent. These were completely graphitized, and both A1 points determined, as in our previous work, the specimens being converted from the stable to the metastable condition and vice versa by appropriate heat treatments. Each stable alloy was heated to a few degrees above Arl for 3 to 7 hr., quenched and analyzed for total and graphitic carbon, the difference being the "combined" or, better, agraphitic2 carbon content of the saturated solid solution just above the eutectoid transformation. One specimen was lost through accident, and the 0.40-per cent. silicon material gave an anomalous result ascribed to difficulty in maintaining the stable system in the presence of but little silicon.

Jan 1, 1923

By Paul Gordon

It is shown that equations for grain-boundary migrntion given by Gordon and Vandermeer, based on a theory first advanced quantitatively by Lucke and Detert, satisfactorily explain recent data on both GRAIN boundary migration in recrystallization and in postrecrystallization grain growth has been the subject of extensive studies for many years. Only solute-independent and solute-dependent boundary migration during recrystallization in zone-refined, poly crystalline aluminum, and during grain growth in zone-refined tin. with the advent of zone-refining, however, has it been possible to carry out such studies on high-purity metals, and thus to delineate quantitatively the major effect On the migration rates of very small percentages of dissolved imPurities. Earlier exPerimental work almost invariably gave migration rate parameters which disagreed with theoretical predictions

Jan 1, 1963

By W. A. Tiller, S. O’Hara

Grain refinement in stirred melts has previously been shown to arise from dendrite segmentation. The present work discusses experiments capable of distinguishing between remelting and mechanical effects which result from fluid motion. Nucleation of still un-dercooled Sn-1 pct Pb melts with a single-crystal seed shows that the grain size of the resulting ingots decreases as the undercooling at nucleation increases up to about 1Z0C, then increases again for larger undercoolings. Pure melts exhibit little refinement as a result of nucleation at any undercooling up to 12°C. The presence of fluid motion gives rise to grain multiplication in pure melts, but the magnitude of this effect is partly obscured by solid-state pain growth. The results indicate that two grain-multiplication pvocesses can operate, one which involves dendrite remelt ing, and another associated with fluid motion. Small ingot experiments indicated that an equiaxed transition can be caused by fluid motion. THE presence of forced convection during recales-cence of undercooled Sn-1.3 pct Pb melts has been shown to give rise to extensive grain refinement during solidification of small ingots of this alloy.''2 In Ref. 2, this refining was shown to result entirely from dendrite fragmentation and not from any nucleation mechanism. The purpose of the present work is to establish what processes lead to dendrite segmentation. Experiments were therefore carried out to determine the resulting structure of both pure tin and Sn-1 pct Pb melts, nucleated at various undercoolings by single-crystal seeds in the absence of forced or natural convection. By comparing the information obtained from these experiments with the results of Refs. 1 and 2, the effects of fluid motion on the ingot structure, and the details of the segmentation mechanisms, should become clear. The results of these experiments should also be helpful in understanding the solidification structures of larger ingots since natural convection, which is known to play an important role in determining ingot structure13 differs only in degree from the fluid-motion effects studied here. I) EXPERIMENTAL PROCEDURE The apparatus shown in Fig. 1 was constructed to permit controlled nucleation of stirred or unstirred supercooled melts using a seed oriented in the tin dendrite growth direction. Because the melts, in all cases, were capable of larger supercoolings than the one used in each experiment, the structure observed always resulted from a single nucleation event at the surface. The sequential procedure was as follows: Tin was melted under purified hydrogen and the oxide removed at a temperature of 450°C . Electromagnetic stirring was then used to clear the surface completely and during this time the guide tube was lowered underneath the melt surface. A pointed Czochralski-like crystal was then propagated from a specially prepared tin dendrite seed4 inside the guide tube while the temperature of the bulk melt was held just above the melting point, ensuring a perfectly clean seed which was epitaxial with the original dendrite. The dendrite and epitaxial seed, still in the guide tube, were withdrawn from the melt which, in turn, was undercooled to 2C° below the temperature at which the nucleation experiment was to be performed. The melt was held there for several minutes, both in stirred and in still-melt experiments. The temperature was next raised to the required value and the melt nucleated by the carrot seed inside the guide tube, the heater power being shut off just after nucleation. In experiments where quenching after nucleation was required, a high-density graphite crucible was used, but otherwise the procedure was as described above. The temperature gradient in the melt before nucleation was kept below 1C° per cm by carrying the experiment out just below the center of the heater shown in Fig. 1.

Jan 1, 1968

By P. S. Kotval

THE nominal composition of "hconel" alloy 718 is 53 pct Ni-19 pct Cr-19 pct Fe-3 pct Mo-5 pct Cb-0.8 pct Ti-0.6 pct A1-0.05 pct C. The nature of the fine strengthening phase in this alloy has been open to debate. iseelstein' has identified the strengthening phase in the matrix of "Inconel" alloy 718 as a colum-bium-rich fcc y' precipitate. Wagner and Hall2 have noted that the metastable y' precipitate overages to an orthorhombic Ni3Cb precipitate which manifests itself as an acicular phase. These authors thus clarify Kaufman and Palty's earlier suggestion3 that the strengthening phase is orthorhombic NisCb. Wagner and Hall's review also reports work by cometto4 which suggests that the fine strengthening phase is not fcc / but bct with a Ni3V type structure and based on the Ni3Cb composition. Kir man and warringtons have shown by analysis of electron diffraction patterns that the metastable strengthening phase in a 55 pct Ni-15 pct 0-25 pct Fe-5 pct Cb alloy is bct and based on the Ni3Cb composition. Raymond~ has provided electron diffraction evidence which indicates that "y'" in "Inconel" alloy 718 is bct in structure. This note presents unambiguous data on the structure of the strengthening phase in "Inconel" alloy 718* ihe samples of this alloy were provided by courtesy of the ASTM task group on phase identification in 'superalloys. after prolonged aging. The electron diffraction patterns presented show that strengthening phase is not y' but bct as was proposed by cometto,' supported by Raymond,~ and identified by Kirman and warringtons in a similar system. Fig. 1 shows a selected-area diffraction pattern taken from a thin foil of "Inconel" alloy 718. The sample had received a final aging treatment of 1118 hr at 1200°F to precipitate the strengthening phase in the matrix. Fig. 2 is a schematic representation of the features in the diffraction pattern. The matrix orientation is (0i2)~,, as is shown by the indexed zone in Fig. 3. Figs. 4, 5, and 6 illustrate that the pattern, Fig. 1, is composed of three bct zones, viz., (0i4), (2i0), and (i01), respectively. These three zones correspond, respectively, to the alignment of the c axis of the bct unit cell with the [001], [loo], and [OlO] directions of the fcc matrix and serve to illustrate the fully coherent relationship of the precipitate structure with the matrix. The streaking of certain reflections is also consistent with the above orientation relationship. The interpretation of the diffraction effects presented here shows the metastable strengthening precipitate in "Inconel" 718 alloy to be bct in structure and demonstrates that it is not an ordered fcc y' phase.

Jan 1, 1969

By Nicholas T. Camicia

Coal is one of our oldest known commodities. Historic evidence indicates that this fossil-formed fuel was used in China and in Wales some 3000 to 4000 pears ago. Coal was discovered in North America in 1679 by French explorers in northern Illinois, and in 1700 a colony of Huguenots came across bituminous coal in Virginia. One might think by this long history of a single commodity that the string was about played out. Quite the contrary, coal is in greater demand than ever before and coal mining today is a modern industry. It is in an unprecedented growth period as the nation-and the world-demands more and more energy coincident with dwindling reserves of other fossil fuels. By the year 2000 the demand for coal is expected to at least double the current level of some 600 million tons annually despite the advent of nuclear power. To meet this challenge, the coal industry is vitally in need of an increasing supply of technically trained and progressive manpower. And, coupled with a serious shortage of engineers and technicians, it represents a rich vein of occupation opportunities-all the way up to top career levels. Today, coal mining is a complex, highly specialized industry concerned with more than just getting coal from the earth and putting it into the furnaces of the consumer. The industry is concerned with the environment, with maintaining a viable ecology. Recognizing the ramifications of global economics, the industry is very much aware of its important position in contributing to a constantly rising standard of living throughout the world. The key to rewarding employment in the coal industry is skill-skill that has been developed by education, training, and experience. None of these alone is enough; all three are necessary today to produce the skill needed to meet the employment requirements of the coal industry. Routine manual labor will no longer do the job in coal mining. In the United States coal mining has been mechanized to a degree unsurpassed anywhere else in the world, and the coal worker must be thoroughly

Jan 1, 1973

JAMES A. BARR Consulting Engineer Mt. Pleasant; Tennessee Washington, D.C. BEHRE DOLBEAR G COMPANY Consulting Mining Engineers and Geologists 11 Broadway New York 4. N. Y. BLANDFORD C. BURGESS Registered Professional Engineer Mining Consultant Monticello, Georgia LENVILLE A. COLLINS Mining Engineer Uranium examinations Cable "Coins" 210 La Arcada Bldg. Santa Barbara, Calif.

Jan 1, 1952

(Under this heading will he published notes sent to the Secretary of the Institute by members or other persons introduced by members.) No. 488.-Mining engineer, member, technical graduate, married, age 38, desires position of superintendent or assistant superintendent. Has had 15 years' practical experience as miner, millman, machinist, surveyor, engineer, foreman, and superintendent in the West, Southwest, and Mexico. Speaks Spanish. Now employed as superintendent of copper property in Southwest. Can give the best of references. Minimum salary $250. Available now. No. 491.-Mining engineer, member, married, age 43, desires to connect with some-good coal company as superintendent or manager. Is thoroughly conversant with flat and pitching systems of coal mining. Has had 23 years experience from the bottom up; 7 years experience as superintendent and manager. Good organizer. Has handled all classes of labor acid has always made good. Available now. No. 492.-Metallurgist and chemical engineer, member, with 8 years executive experience in research and technical direction of all departments of nom-ferrous metallurgical manufacturing, is open for change in position. Specialist in raw materials-and supplies, reclamation of wastes, and standardized control of processes. No. 493.-Member, age 37, technical education, married. Seventeen years' experience as superintendent, engineer, chemist, and assayer, exploration engineer in United States, Central and South America, Siberia and India. Especially in iron, manganese, copper, and rare metals. Desires to make a change. No. 494. Electrometallurgical engineer, member, age 30, A. M. and Ch. E. degrees, thoroughly trained in electrochemistry, metallurgy and electrometallurgy. Three years in charge of experimental work on and operations of electric furnaces. Desires responsible position in investigative or executive work with commensurate salary.

Jan 11, 1918

By K. M. Myles

The vapor pressure of palladium over a series of Rlz-Pd alloys has been measured by the torsion-effusion method. The thermodynamic properties of the alloy system at 1575=K have been calculated from the vapor pressure data. The activities and the free energies of formation exhibit large positive deviations from ideal behavior. The enthalpies of formation are endother-mic. The entropies of formation are positive and larger than the ideal entropy of mixing. All of the thermodynamic properties suggest that a strong tendency toward phase separation exists in the solid solutions. The possible origin of the phase instability and the various factors that influence the thermodynamic properties are discussed. RECENT studies of the thermodynamic properties of alloys of palladium with nontransition elements have indicated that a significant contribution to the enthalpy of formation is related to the redistribution of the conduction electrons upon alloy formation.'-' The present work was undertaken to ascertain the importance of this contribution in Pd/transition-metal alloys. The Rh-Pd system was chosen for this investigation for several reasons: 1) The thermodynamics of the system were unknown. 2) Rhodium and palladium are completely soluble at high temperatures; below 1118OK the solid solution becomes immiscible.', 3) The difference in magnitude between the vapor pressures of rhodium and palladium permitted the use of an existing effusion apparatus. 4) Additional information was known about the alloy system that would facilitate the interpretation of the thermodynamic results. EXPERIMENTAL PROCEDURE The thermodynamic properties of the Rh-Pd alloy system were calculated from the vapor pressure of palladium over solid palladium and over several solid Rh-Pd alloys. The vapor pressure was measured by means of the torsion-effusion apparatus that has been described previously. In this method, an effusion cell is suspended from a tungsten filament inside a high-temperature furnace. Two orifices are located eccentrically such that the effusion of the vapor creates a rotational torque in the filament. The angle of rotation is directly related to the total vapor pressure within the cell. As the vapor pressures of rhodium and palladium are approximately five orders of magnitude apart," the total vapor pressure was considered to be effectively equal to the equilibrium vapor pressure of palladium. The effusion cells were made from high-purity alumina since auxiliary experiments indicated that essentially no reaction occurs between alumina and solid Rh-Pd alloys. Unfortunately, because the orifices were irregular, an accurate calculation of the Free- man-Searcy correction factors" could not be made. The constants were determined in an independent experiment where the vapor pressure of copper, as measured in the alumina cell, was compared with an accurate value of the vapor pressure, which had been determined previously.4 Depletion of palladium from the surfaces of the specimens was minimal as the deflection of the cell remained constant, for at least 15 minutes, at each of the experimental temperatures. Lattice parameter measurements of the postrun alloys also indicated that no changes in the composition of the surfaces had occurred. The alloys were prepared by arc melting the requisite amounts of the 99.99 pct pure elements. The four most palladium-rich alloys were remelted in a levita-tion furnace since complete melting of the components had not occurred in the arc furnace. All of the alloys were subsequently homogenized at elevated temperatures in sealed alumina thimbles. After heat treatment, the alloys were analyzed chemically and were in essential agreement with the nominal compositions. The thermal histories and nominal compositions of the alloys are given in Table I. Lattice parameters of the heat-treated alloys were computed, by means of the method described by Mueller et a1. ,I2 from X-ray diffraction powder patterns obtained with filtered copper radiation in a 114.6-mm-diam Straumanis-type Debye-Scherrer camera. The results, which are tabulated in Table I, exhibit a slightly greater negative deviation from Vegards' law than the values reported by Raub et al.13 The diffraction lines were sharp and well-resolved and thus indicated that the alloys were homogenous. RESULTS The logarithms of the individual values of the vapor pressure of palladium were fit, by the least-squares method, as a linear function of the reciprocal of the absolute temperatures. The constants of the equations are given in Table I along with the temperature range over which the data was accumulated. The latent heat of vaporization at 298.15"K for pure palladium, calculated by the third-law method,14 showed no systematic temperature dependence. The average value of 88,920 * 20 cal per g-atom agrees favorably with the average of the results obtained in the most reliable previous investigations.15"19 The activities of palladium were computed from the vapor pressure data at 1525', 1575", and 1625OK. Consistent with the mass spectrometric study of the atomicity of palladium vapor,lg the vapor was assumed to be monoatomic. The activities of rhodium were determined by integrating the Gibbs-Duhem equation with the aid of the a function.20 In the calculations, the activities of the pure solid metals were assigned the value of unity. From the activities, the partial and integral free energies, entropies, and enthalpies of formation at 1575° K were computed; they are assembled in Table 11.

Jan 1, 1969

By Ebert L. J., G. Sachs, Jr. Brown W. F.

It is a generally recognized fact that a steel quenched from the austenitic range and tempered to yield a structure composed of tempered martensite becomes increasingly more ductile with increasing tempering temperature. However, the conventional tensile test fails to yield any value that is sensitive to differences in behavior on tempering among the various low-alloy steels or among different heats of a particular steel. The notched impact bending test, on the other hand, has been recognized for a considerable length of time as capable of revealing differences in impact properties among various steels tempered to 'the same strength level (i.e., the same tensile strength in a conventional tensile test). However, this test is very complex and its significance has not been clarified up to the present time. Of its three characteristic features—the high speed, the notch, and the bending—the notch has been found by Davidenkov2 to be the most potent embrittling factor. Recent investigations on low-alloy steels have shown static notch-bar tensile tests to be more lucid and to evaluate the metal properties in much the same manner as impact tests. In an attempt to analyze the fundamental nature of this test, it was found possible to separate the effects of the two basic characteristics of the stress pattern introduced by the presence of a circumferential notch, the stress state and the high initial stress concentration at the notch bottom. The major conclusions drawn from these previous investigations were as follows: I. The magnitude of the triaxiality at fracture depends primarily on the initial notch depth. Its effect is a great reduction in the average ductility (contraction in area at fracture in the notched section) as compared with that observed in uniaxial tension. This triaxial stress state occurs at a point in the interior of the notch specimen. It determines the notch ductility if the notch is mild and/or the metal possesses a considerable ductility. On the contrary, brittle specimens probably fracture on the metal surface (at the notch bottom) at which point biaxial stress state is present. This biaxiality also considerably reduces the ductility of the metal. For small notch ductilities the notch strength and the notch ductility become very sensitive to embrittling factors. This is contrary to the behavior. of the ductility values derived from a conventional tensile test, which are comparatively insensitive.

Jan 1, 1947