By F. R. Hensel

The present paper describes a number of experiments with fine silver, coin silver, silver-cadmium oxide and silver-nickei-copper compacts, prepared by powder metallurgical methods. The test data are of a preliminary nature, since most of the work was exploratory. Fine Silver Eject of Compacting Pressure on Hardness and Density during Cold and Hot Pressing The cold-welding properties of silver have received considerable attention and the welding characteristics are functions of such variables as: cleanliness of metal particles (impurities and adsorbed gases), chemical nobility of particles, plasticity and hardness, particle assortment, particle shape, particle porosity, apparent density, temperature, pressure, time, recrystalliza-tion characteristics. Chemical nobility, plasticity and low temperature of recrystallization after work-hardening are responsible for the excellent low-temperature bonding properties of silver. Several series of compacts were pressed at pressures of 5, 10, 20, 30, 40, 50, 60 70 and 80 tons per square inch, at temperatures of 32°C. (room temperature), l00°, 2000, 300°, 400°, and 450°C. Silver powder of minus 325-mesh, produced by displacing silver from a nitrate solution by means of copper, was used. The density was calcuiated from accurately measured and weighed compacts. The hardness was measured on the Rockwell F scale. The investigation shows that an increase in pressure promotes a higher density and hardness regardless of pressing temperature, up to a temperature of 400° C. The pressure-density curves at various pressing temperatures are shown in Fig. I, the pressure-hardness curves at various pressing temperatures, in Fig. z. The greatest increase in both hardness and density was obtained in the pressure range of 5 to 20 tons per square inch. A compact from each series was annealed at 300°C. in air, for various lengths of time. The hardness values after annealing are shown in Table I. A minimum hardness was obtained after one hour of annealing. No change in density occurred during annealing. The maximum density was obtained at 80 tons per sq. in., and at this pressure the hardness is equal to that of hard-drawn wrought

Jan 1, 1945

By W. R. Toeplitz

Probably a more descriptive title would be "Much Ado About Nothing." By "nothing," of course, I refer to the porosity which is the main feature of this type of bearing. Porosity has a decided effect on the manufacturing techniques, the structure and physical properties, the oil content, and on the installation and service of oil-retaining porous bronze bearings. A simple curve can be drawn by plotting specific gravity along the abscissa and percentage of porosity by volume on the ordinate. A bronze composition, analyzing 89 Per cent copper, 9.75 Per cent tin, and 1.25 per cent graphite, has an absolute solid specific gravity of 8.5. At this specific gravity, of course, occurs the point of zero porosity. Conversely, at loo per cent porosity, the specific gravity is zero. A similar curve can be drawn for bearings impregnated with oil; the only change being that the specific gravity at loo per cent oil will be 0.89 if we assume that that is the specific gravity of the lubricant. The curve is useful in determining the oil content by volume for any specific gravity. The normal range of oil content for porous bronze bearings of this composition is from 35 to 16 per cent, which is in the specific gravity range of from 5.8 to 7.3. In addition to the amount of porosity, the type of porosity is important. The first consideration here is that the porosity must be intercommunicating. This can be determined by a number of simple tests. The first method, which is very accurate, is to extract the oil in the bearing by cycling

Jan 1, 1945

By L. D. Jaffe, J. H. Hollomon

THE effect of tempering temperature and time upon the properties of quenched steel is clearly a subject of great practical importance, as well as of considerable theoretical interest. It would be very desirable to be able to predict the properties of a quenched steel when given any selected tempering cycle, with a minimum of experimental work upon that heat or even type of steel. Two problems are involved: one consists of relating the structure obtained to the physical properties, and will not be discussed here; the other, with which this paper deals, involves the relations of time, temperature and composition with the structure obtained on tempering. Indentation hardness is perhaps the most convenient quantitative measure of the tempered structure, or of what might be called the "degree of tempering." Undoubtedly, it is not an exact measure, and in some cases (as when temper-brittleness occurs) pieces of the same quenched and tempered steel may have widely differing properties at the same hardness. However, hardness has the advantage of being simple to determine and is certainly the most widely used indication of the degree of tempering. Moreover, for fully quenched steels that are not temper-brittle and do not contain retained austenite when quenched, it appears that, in general, if the hardness of the steel is the same, the tensile and impact properties will also be identical, whether a high or a low tempering temperature is used. The tempering charts available in the metallurgical literature usually give the hardness as a function of tempering temperature for only one tempering time. However, in practice, tempering times frequently vary, and a method of converting tempering curves for one time to tempering curves for some other time would be very valuable. It is also advantageous, in determining the tempering treatment necessary for a given part, not to have to temper samples at several temperatures for the time used for the commercial tempering operation. A more satisfactory procedure would be to employ times of the order of 10 to 30 min., rather than 5 or 10 hr., and if possible to use only one temperature. Furthermore, it is frequently desirable, for reasons such as temper-brittleness,* to obtain a given hardness with short times at relatively high temperatures, and it would be convenient to be able to compute without tests the time required to produce this hardness. Remarkably few quantitative studies of the hardness of quenched steel tempered over wide ranges of temperature and time

Jan 1, 1945

By Donald W. Scott, Nathaniel Arbiter, A. C. Richardson

THIS paper describes the application of amine flotation to a specific problem-that of increasing the grade of magnetite concentrates derived from an iron ore requiring extremely fine grinding for mineral liberation. Experiments conducted on an iron ore from Wisconsin had shown that concentrates containing 60 to 62 per cent iron and 12 to 14 per cent silica could be produced by magnetic separation. The residual silica occurred as quartz and hornblende, either entrained or locked with magnetite. Most advantageous utilization of the concentrate, however, necessitated that the silica content be reduced to about 5 per cent, equivalent to an iron content of 67.5 per cent. It had been demonstrated that tabling of the magnetic concentrate removed sufficient quartz and hornblende to yield an acceptable concentrate, but disadvantages inherent in tabling dictated that flotation be investigated as a substitute. The goals set for the flotation investigation were: (I) the production of concentrates of about 68 per cent iron content from the magnetic concentrate; (2) an iron recovery of about 85 per cent of that in the feed to flotation; and (3) minimum reagent cost. Both batch and continuous flotation tests were employed; the former, to establish the procedure and the latter to verify it. Although the data were obtained on a specific ore, and with a commercial application in view, it is believed that they have a bearing on other problems where amine flotation is being used or is anticipated. SAMPLES Two samples, designated "minus 100mesh magnetic concentrate" and "minus 150-mesh magnetic concentrate," were used for the batch experimental work. They differed only in the degree to which the crude ore was ground prior to magnetic separation. They were stored moist in steel drums in quantities sufficient for all the experimental work reported. This procedure had the advantage of allowing all tests to be made on common samples, but had the disadvantage that the individual flotation samples, because of the difference in storage time, were subject to various stages of surface alteration. Previous work had indicated that common samples were desirable for the batch studies, and it was decided that if these data appeared sufficiently promising the effect of surface alteration could be checked best by continuous tests. The size distributions and the assays of the samples are given in Table I. The minus 150-mesh magnetic concentrate, on which most of the flotation tests were made, assayed 60.9 per cent iron, 13.3 per cent silica, and 0.016 per cent phosphorus. The minus 325-mesh portion represented 78.1 per cent of the sample by weight, and assayed 67.9 per cent iron. Thus, the insoluble, mainly silica, was concentrated

Jan 1, 1945

By Raymond D. Sloan

During 1944, substantial gains were recorded in practically every phase of the petroleum industry in Oklahoma. With the spotlight of activity focused on other states during the more recent years, the production momentum that was achieved in Oklahoma through the discovery and development of such outstanding pools as Oklahoma City, Fitts. and major pools in the Seminole area during the late 1920's and early 1930's was practically spent by the end of 1943. However, with much of the industry's exploratory efforts greatly reduced in Illinois, Indiana and Kentucky, the strong demand for Mid-Continent crude and the optimism created by some discoveries in the state toward the end of 1943, Oklahoma has again become the recipient of much activity and interest, with its 1944 drilling activity, production and refinery runs to stills registering substantial gains over the preceding year. Development and Exploration Since the discovery of the West Edmond pool in April of 1943, with the substquent drilling and development boom, the scene of exploratory activity has shifted from the central. south and east portions of the state to the general trend of the . Granite Ridge, where leasillg and wild-catting were greatly activated within a wide radius of this high subsurface feature. Leasing activity, however, jumped the confines of the Granite Ridge trend and extended into all of the northwestern counties in the state. Seismograph activity at once began following and keeping pace with this shift in the leasing and exploration locale, by the concentration of a large number of seismograph crews in the area. At one time during the year,35 crews were concentrated in Oklahoma, the majority being west of the Granite Ridge and extending into the northwestern counties. To illustrate the increase in geophysical work done in the state during the year, records indicate that 377 crew months were worked in 1944, which is a 21 per cent increase over the 311.5 crew months activated in 1943. With the discovery in 1943 of several encouraging prospects and the finding of West Edmond as an incentive, drilling operations increased some 54.3 per cent, for a total of 1986 completions during the year. This is compared with a figure of 1287 for wells drilled in 1943, an increase of 699 wells. The industry, with a total of 1064 oil producers, enjoyed a success percentage of 53.6 per cent. Gas wells completed were 223, while 699 dry holes were drilled. In 1943, completions included 587 oil wells, 127 gas wells, and 573 dry holes. The number of oil producers completed during the Year was almost double the numher of wells in 1943. Of the total drilling wells completed in the state, 350, or 17.6 per cent, were wildcat operations—an increase of 5.1 per cent over the 194.3 total of 333. The wildcat success percentage was 13.4 per cent, 47 successful wells being completed for an average initial potential of 160 bbl. In the state, 23 gas wells were completed with an average initial production of

Jan 1, 1945

Jan 1, 1945

By T. W. Lippert

In these opening remarks, I will endeavor to give a background of continuous casting of metals. Only passing attention will be given to the different processes to be described by the authors whose papers are on the program, as they are far more familiar than I am with their subject matter. Suffice to say that over the past several years the brass, copper, aluminum and magnesium industries have shifted practically completely from conventional static molds to continuous casting machines. The Aluminum Company of America alone has more than 60 continuous machines in operation. The product as continuously cast is superior metallurgically, less scrap loss is involved, costs are generally lower, and the equipment requires little floor space. A continuous machine, operating as it does with deadly constancy, is a ravenous consumer of molten metal, and in most plants one or two machines are well able to handle large banks of melting and refining furnaces. In steel, interest in continuous casting is today more serious than ever before in history, and there is every reason to believe that continuous machines may secure a minor place in the ferrous industry, particularly for tool and alloy analyses. In the past, steel has been commercially cast continuously, and today many tons of steel are being turned out in this manner. It has been said that the cradle of every science is surrounded by dead theorists— and certainly there are innumerable examples of this in the metals industries. An excellent illustration, for instance, is the continuous rolling of metal, a tantalizing objective that for decades on end exhausted . the efforts of a long line of famous, infamous and unknown inventors. Finally, in 1922, John B. Tytus, of the American Rolling Mill Co., brought forth what now seems such an obviously simple scheme— a concave roll face, each stand of progressivcly less concavity. And out of this one change in design sprang today's wide continuous mill rolling steel sheet Ioo in. wide at 2000 ft. per minute. Another excellent example is the con- . tinuous casting of liquid metal into an intermediate form, preferably one requiring little subsequent breakdown. First, the casting of liquid metal alone was fascinating enough. Then someone passed the cast metal directly into a rolling mill, and shortly thereafter this continuously rolled strip was passed directly into a stamping machine. This leitmotiv of a continuous flow of metal from the liquid phase to a consumer end product, fast and inexpensive, and all housed within a small space, was enough to drive some 200 or so inventors into frenzy over the past hundred years. All the ideas, however, like mayflies, had only their brief afternoon of existence. They were born and they died on paper, as constant exemplification of that great void that always exists between mental production and commercial production.

Jan 1, 1945

By P. W. Bridgman

Flow and fracture are admittedly complicated phenomena of which we are yet only partially masters. There is not even nni-.persal agreement as to the details of the language best adapted merely to describe the phenomena, to say nothing of any theory. Certain points of view, however, are widely held, and there are certain general expectations as to what sort of procedures will prove permissible. A complete description of any situation involving fracture would demand a complete history of all the variables in the control of the experimenter. The experimenter endeavors so to choose his independent variables that they are adequate to determine completely the situation in the sense that when an experiment is repeated on the same initial material and with the independent variables running through the same sequence, all the other measurable properties of the system will also run through the same course. It is, I think, the universal conviction that when we are dealing with phenomena of flow and fracture, the most important of the necessary variables are the external forces acting on the various parts of the body; when the force history repeats, with certain obvious restrictions such as that temperature must be constant and non-mechanical forces, such as magnetic field, must be small enough to be ineffective, then the history of all measurable properties will repeat; in particular the alteration of geometrical shape due to flow will run through the same course, and when fracture comes, the character of the fracture will be reproduced. Complete mastery of merely the descriptive aspects of flow and fracture would demand the ability to predict the entire course of flow and complete characterization of the final fracture for every possible combination of forces, varying in time in all possible ways, when applied to bodies of all possible shapes. This full situation is obviously of prohibitive complexity. The first stage in reduction to manageable simplicity is to resolve the total situation into the sum of contributions made by small elements. Our thesis is that if each of the elements is adequately characterized, the behavior of the whole system is fixed. The element is usually taken of a simple geometrical shape, suggested by the mathematics best adapted to the particular situation. The forces acting across the faces of the elements are ultimately determined by the forces acting across the free faces of the whole system. The detailed process of finding the precise forces on the faces of all the elements in terms of the external forces involves the use of a special mathematical invention, the stress, a constructional quantity consisting of six components. The stress at any point in the body is determined by both the external force system and by the physical properties of the body at all points; quite different stresses prevail at the interior of bodies of the same shape under the same external forces in the elastic and plastic ranges. The forces on the faces of any element are, however, uniquely determined by the stress system at the element. Our fundamental thesis

Jan 1, 1945

By Michael Tenebaum, C. C. Brown

In recent years, the importance of slag control in basic open-hearth operations has been universally recognized. To effect such control during the working period of the heat, methods have been developed to measure or estimate slag oxidation and slag basicity. While satisfactory rapid chemical methods have been developed to determine slag oxidation, no completely adequate method of evaluating basicity has yet been provided. The most generally accepted control methods of measuring slag basicity are based on visual cstimates. While considerable benefit may be derived from such estimates, the need for some measurable indication of slag basicity has become increasingly apparent. In a recent paper, Philbrook and Jolly suggested a promising technique for making the basicity determination. Their method consists of measuring the pH of a mixture of powdered open-hearth slag and distilled water. It was found that a relation could be established between the slag basicity and the alkalinity of the water mixture as measured by the hydrogen-ion concentration. The general procedure followed in making the measurements and the considerations involved in constructing the original curves are given in the paper of Philbrook and Jolly and need not be repeated. It is the purpose of this paper to discuss some of the factors considered in applying the pH measurements to actual slag control and to present some of the results of its apphcation. Factors Involved in Measuring pH of Water-slag Mixtures To facilitate the application of the pH control system, it was desirable that no alteration be made in the routine methods of sampling and crushing the furnace slag. Some of the factors considered before establishing a curve to relate slag basicity with the pH reading arc reviewed individually in the following paragraphs. Effect of Cooling Rate Under actual operating conditions there can be considerable variation in the temperature of the piece of slag crushed for the pH determination. To determine whether variations in crushing temperature or in cooling rate would affect the pH reading, a series of four samples was prepared from each of two separate slags. These samples represented conditions far more extreme than would actually be encountered. To obtain these samples, a thick pancake of slag was poured. One piece of this pancake was crushed immediately after it had solidified. Another piece was water-quenched and then crushed. A third piece was allowed to air-cool to room temperature before crushing. The fourth sample was prepared from a chilled slag. This sample was poured onto a heavy inclined steel plate at the

Jan 1, 1945

By G. E. McElroy

THOUGH air jets occupy only a minor role in the ventilation of mines and other enclosures, their importance in this respect is greater than is commonly recognized and may be considerably increased as our conception of their modes of operation becomes clearer. The object of this paper is to discuss some of the ways in which air jets are involved in mine ventilation and some possible applications to the ventilation of mines and other enclosed spaces. The mention of air jets ordinarily suggests the use of some form of an air injector, such as the Venturi blower occasionally used for auxiliary ventilation in mines, or the Saccardo (injector) system used to a limited extent for ventilating railroad tunnels. Actually, the term covers such common phenomena as the discharge of air from fan pipes and coal-mine line brattices, and even from smoke stacks and fans. A knowledge of the general mode of air entrainment by jets also helps to explain certain phenomena-some mine-gas explosions, for instance-that otherwise would remain obscure. Jet action has been involved in three recent series of Bureau of Mines experiments in which the author has participated: experiments on fan-pipe discharge, on the dilution of gases discharged from a stack and on the ventilation of a ship's hold. Available data on the discharge of jets into large openings and on the design and performance of air injectors have been analyzed in considerable detail and supplementary experiments are planned for after the war. The results of the fan-pipe experiments have been combined with the analyses of data on jet discharge into large spaces, and have been published.1 The results of the stack-gas dilution tests, which refer to a jet discharged into a crosswind, have also been published2 and a paper on the design and performance of injectors has been prepared for publication.3 These technical experiments and analyses form the background and the documented evidence for the following nontechnical discussion of the use of air jets in mine ventilation. JET CHARACTERISTICS The jets commonly encountered are those in which the air is in turbulent-as opposed to laminar, or streamline-motion. The characteristics under discussion apply only to such turbulent jets and have their basis in theories of the mixing of turbulent air currents. Such jets have basic characteristics that are present, though variable in form, regardless of whether the jet expands freely in space, whether the expansion is limited by adjacent walls, or whether the jet propels air through a flow circuit. They expand at definite angles and entrain the surrounding air, even though the entrained air must be obtained by recirculation of their own air streams. As the quantity of air in motion in the mixed stream increases, the average velocity of the stream decreases. In the case of entrainment in the free

Jan 1, 1945

By J. Mazia, H. Rosenthal

An investigation has been made of residual stress in the head and body of caliber 0.30 cartridge cases. The head was divided into four ring-lie sections which were cut off by a jeweler's saw. Spring-out was measured after a radial cut had relieved the circumferential bending moment. The residual stress corresponding to the observed spring-out was calculated by formulas in which the computed stress was a function of wall thickness. All rings sprang open, indicating compressive stress on the inner wall and tensile stress on the outer wall. The production stress-relief anneal of 475 F. for 45 min. reduced the stress to almost half. The priming and crimping operation, however, again raised the stress, especially in the flange section. The dect of stress-relief heat treatments on residual stresses in the body of caliber 0.30 cartridge cases was investigated by the split-ring method. Although this method did not reveal any large stresses in the body, the neck before mouth anneal was found to contain a computed stress of 30,000 psi. at the surface. This value was reduced to 15,000 psi. in 120, 30, and 15 min. at 400, 475, and 500 F., respectively.

Jan 1, 1945

Jan 1, 1945

By N. Tiner

IN an article on magnesium and its alloys, Gann and Winston1 stated that manganese has a limited solubility in the liquid state. W. Schmidt2 showed a diagram according to Joseph Ruhrmann indicating that the solubility of manganese in liquid magnesium falls from about 2.65 per cent at 790°C. to about 0.5 per cent at 695°C. The curve was extrapolated to show zero solubility at the melting point of pure magnesium (Fig. I): This work suggested that at the lowest manganese contents it was not possible to detect either a eutectic or the formation of a solid solution, so that manganese was stated to be present in the structure as large individual crystals. Two years after the presentation of these results, Gann3 brought evidence to show that some manganese is capable of dissolving to form a solid solution, any excess of manganese present then assuming chiefly the form of small blue-gray particles scattered throughout the primary magnesium crystals, occasionally in clusters but seldom at the boundaries. He presented micrographs of cast alloys containing o.1, 0.4 and 1.0 per cent manganese that show a small amount of coring around the individual particles due to solid solution, and indicate that the location of the manganese particles is closely associated with the original dendritic structure of the primary crystallization. He also pointed out that the amount of manganese that can be dissolved in magnesium depends on the amount of other alloying elements present, the effect of the second alloying element being to decrease the amount of manganese retained in the alloy. E. Schmid and G. Siebe14 have determined the solid solubility of manganese and its variation with temperature by means of precision X-ray diffraction measurements. They found that the solubility is 3.4 per cent at 645°C and decreases to practically zero at 200°C. It is apparent that the X-ray diffraction measurements of Schmid and Siebel are not in agreement with the results of Ruhrmann as presented by Schmidt. This disagreement, and also the lack of data on magnesium-aluminum-manganese and magnesium-zinc-manganese systems, led the author to the present investigation, to determine accurately the liquid solubility of manganese and its variation with temperature. EXPERIMENTAL METHOD The experimental method for making solubility determinations consists of saturating the molten magnesium or the alloys with manganese at various temperatures and analyzing the dip samples taken from these melts. Melting is carried out in a cylindrical steel pot heated by an electric resistance furnace. The pot had a metallic outside coating to protect the steel against oxidation, and a graphite inside lining to prevent the contamination of the melt by prolonged contact with iron. The inside diameter of the pot was 4 in. and the depth 12 inches.

Jan 1, 1945

By C. R. St. John, R. W. Lindsay, Charles R. Austin

Many of the factors influencing the creep behavior of ferrous alloys have been investigated and reported upon in the literature, including such variables as grain size, steelmaking practice, nature and stability of the microstructure, and the effect of alloying elements in steels. However, with respect to the latter, the microstructures involved are usually heterogeneous and as a result the effect of the addition is related to its effects on the various phases present in the microstructure. In the instances where this structure consists of ferrite and carbide, the behavior of the alloy addition will be related to its action in strengthening ferrite and in opposing temperature softening of ferrite as well as coalescence of carbide. The present paper is the third in a series comprising a comprehensive review of investigations on the properties of iron binary alloys.l,2 Its purpose is to describe the results of isolating one microstructural phase, namely ferrite, and studying its creep characteristics in both the unalloyed and alloyed conditions. This should aid in establishing to a large degree the importance of ferrite in the creep behavior of steels consisting of the previously mentioned ferrite-carbide aggregate. In view of the fact that the present investigation deals only with the effects of silicon, manganese, chromium, molybdenum, nickel, and cobalt, and to a certain extent with the effects of carbon, the review of previous literature will be confined to these elements. Practically no references were encountered dealing with the influence of these elements on the creep characteristics of the isolated phase. However, various contributions have dealt with the creep behavior of low-carbon steels alloyed with the elements under consideration. A particularly concise review in this respect is given by Bullens (Battelle)= and much of this material has been drawn upon. The definite improvement in creep resistance and high-temperature strength conferred by molybdenum is well known. Published suggestions by the A.S.M.E.4 permit of an increase of some 2000 to 5000 lb. per sq. in. in permissible design loads over a temperature range from 650" to IOOO °F. as a consequence of additions of 0.40 to 0.60 per cent of this element in carbon steels of the order of 0.25 to 0.35 per cent carbon content. Babcock and Wilcox Tube CO.5 has published data showing the pronounced increase in stress necessary to cause one per cent creep per 10,000 hr. when additions of 0.5 or I per cent molybdenum are made to a plain carbon steel. These data apply to temperatures over a range from 800° to1000°F. 4

Jan 1, 1945

By Charles S. Barrett

THERE is a road into the microscopic realm that has remained untraveled through all these years of intense activity with high-power optical and electron microscopy. The road is worthy of careful scouting by metallurgists and other investigators, for it leads into relatively new country and it makes some areas accessible that heretofore could be reached only by very indirect paths or by the use of imagination. And when the road passes through familiar territory it frequently permits a new view of commonplace things that should prove of value from time to time. An accepted way to interest people in new sights such as this is to present an illustrated travelogue. This I propose to do, using many pictures taken in my recent exploration of this road. In the manner of travelogues, I shall touch briefly upon a large number of different subjects in physical metallurgy and shall, attempt to give an exhaustive treatment of none, for the objective is to provide a means for further research, to interest others in it, and to indicate what appears at the moment to be profitable directions for it to take. The method I shall present involves X-rays, but does not make use of the usual accompaniments of X-ray research such as reciprocal lattices, Fourier series, or the stereographic projection. The method is so simple in its fundamentals that it could have been developed 20 years ago, or perhaps even 30 years ago. It is well to have a destination for our travels, so that when we are through we shall have explored some region of importance, despite our preoccupation with the novel means of transportation and our interest in the sights to be seen along the way. So let us name the Cold Worked State as our destination, and make side trips into the territories known as Recovery, Recrystallization, and Precipitation-hardening. A great many investigations have been made of the nature of cold-worked metal, and a great variety of methods used, many of which are indirect, such as X-ray line intensities, X-ray line widths, calorimetric measurements, and magnetic measurements. Since comprehensive reviews of these investigations have been published in recent years, they need not be discussed here. The investigations that were the direct forerunners of the present work should be first mentioned. In 1931 I became interested in the structure of individual spots in X-ray diffraction patterns.1 When a crystal is placed in the narrow pencil of X-rays in a Laue camera, the spots recorded on the film are not always uniformly black, but may have an internal structure. The meaning of this may be understood from Fig. 1, which represents a narrow beam containing X-rays of many wave lengths ("general radiation") penetrating a crystal in the direction of the arrow and forming a pattern on the vertical film at the right.

Jan 1, 1945

By E. V. Potter, E. T. Hayes, H. C. Lukens

LARGE volumes of hydrogen are liberated at the cathode during electrolytic precipitation of manganese. Most of the gas escapes from the electrolyte, but a considerable amount may be entrapped in the manganese plate. Gas has been observed to escape from manganese melts in puffs that ignite at the surface. It has been reported that castings made with electrolytic manganese tend to rise in the molds; for this reason the manganese is often treated to remove hydrogen before the melt is made or it is premelted and used as cast manganese in making the alloys. The effect of hydrogen on the properties of manganese and its alloys is not known, but its effect on iron and iron alloys has been studied extensively.1.2 The close relationship between iron and man¬ganese suggests that hydrogen may have a similar effect on the properties of manganese and its alloys. The purpose of this investigation was to determine the amount of hydrogen or other gases in typical commercial electrolytic manganese sheet and to investigate ways of removing it most conveniently. APPARATUS The apparatus used is shown schematically in Fig. I. It consists of a chamber A in which the metal sample is placed, a vacuum or pressure gauge B, volume gauge C, vacuum pump D, hydrogen container E, auxiliary gas chamber F, and furnace G. The specimen chamber was made of two concentric quartz tubes. The outer one, a, connects with the closed gas system and is surrounded by the furnace G. A second tube, b, fits closely inside a and has a small end that projects into the space for the specimen and holds the thermocouple for measuring the temperature of the sample. The inner tube is joined to the outer tube outside the furnace, with rubber tape and sealing wax, to prevent gas leakage into or out of the closed system. This type of specimen container is loaded very easily and can be used several times if molten metal does not come in contact with the quartz. An ordinary mercury manometer B is used to measure the pressure in the system. The volume gauge C is essentially another mercury manometer, but the volume of the column is much larger than normal and the height of the mercury can be varied by raising or lowering the well H. In this apparatus the tube had a volume of I00 c.c. for a 60-cm. length. For larger changes in gas volumes; auxiliary containers F were used to increase the volume of the system by known amounts. Valves were arranged so that these auxiliary containers could be filled from the system and evacuated by the pump as often as necessary to accommodate the increases in the volume of gas in the system. The furnace G, used to heat the samples, was equipped with an automatic temperature controller, which maintained the desired temperatures within ± 5°C.

Jan 1, 1945

By Robert C. Stephenson

LARGE deposits of titaniferous magnetite occur associated with anorthosite and gabbro in the Lake Sanford area, Essex County, New York. The ore, gabbro, and anorthosite show consanguineous relations. Anorthosite grades through gabbroic anorthosite into gabbro but is locally intruded by gabbro. Structural and petrographic evidence suggests that gabbro was differentiated from anorthosite by filter pressing. Field and laboratory study of ore occurrences indicates that an ore residuum concentrated in the gabbro through magmatic segregation by normal crystallization and flowage. Ore occurs as bands which grade into gabbro, and also as large masses which replace anorthosite. Ore in the gabbro is finer grained and richer in ilmenite than ore in anorthosite.

Jan 1, 1945

By R. B. Mears, E. H. Dix, R. H. Brown

In the Institute of Metals Division Lecture of 1940, E. H. Dix, J~.(I)~ discussed the acceleration of the rate of corrosion by high constant stresses. Experimental data obtained on this subject at the Aluminum Research Laboratories and a theory compatible with these facts were included in that lecture. The present paper contains data and ideas subsequently developed at the Aluminum Research Laboratories. Dix pointed out that in order for acceleration of corrosion by constant stress to occur: (1) There must exist in the alloy a susceptibility to selective corrosion along more or less continuous paths, as for in- stance at grain boundaries, and (2) There must exist a condition of high stress acting in a direction tending to pull the metal apart along these continuous paths. Acceleration of corrosion rate by stress is not confined to any one alloy system. Table I lists some of the metals and alloys and some of the corroding environments in which acceleration of corrosion by stress was sufficient to cause cracking (stress- corrosion cracking). It will be noted that the variety of alloys in which stress-corrosion cracking has occurred is rather large. Also, it will be observed that

Jan 1, 1945

By V. C. Perini

The 1943 designation of districts for the Transactions† has caused some confusion because of the elimination of the West Central Texas district and the allocation of the counties of this district to the North Texas district and the North Central Texas district. The North Central Texas district as herein defined includes the counties of Brown, Callahan, Cole-man, Comanche, Coryell, Eastland, Erath, Fisher, Hamilton, Hood, Jones, Lampasas, Mills, Nolan, Palo Pinto, Parker, San Saba, Shackelford, Stephens, Stonewall, Summerville, Taylor, Throckmorton and Wise. These counties as listed are the counties of District 7B, State Railroad Commission. This district covers the south central crest and the west flank of the Bend flexure north of the Llano uplift. The west flank of the Bend flexure is on the east boundary of the Permian Basin of West Texas. The North Texas district, District No. 9, State Railroad Commission, includes the counties of Archer, Clay, Cooke, Foard, Hardeman, Jack, Knox, Montague, Wichita, Wilbarger and Young. The area of this district covers the crest and south flank of the Red River uplift and the north central crest of the Bend flexure. The greater part of the oil and gas produced in the past from the North Central Texas district has been from Pennsyl-vanian strata. Some oil and gas has been produced from the lower Permian (by the latest selection of the Pennsylvanian-Permian boundary') and minor amounts from the Mississippian and Ordovician sediments. Increasingly important quantities of oil and gas are to be expected from the older sediments by deeper development in proven fields and by new discoveries. Most of the oil and gas in the district has accumulated in localized, well-defined structural traps in limestone and sandstone reservoirs and in traps due to stratigraphic changes in sedimentation, mainly porosity traps in limestone and sandstone lenses, both usually associated with some structural feature. The Stripper Well Premium Plan as adopted by the office of the Federal Price Administrator has been an aid to the producers of stripper wells. The producers are pleased to receive the subsidy to prolong the plugging of wells, but they are not too pleased with the subsidy plan in principle. Most independent operators are in favor of, and think they are entitled to, an increase in the market price for oil. The price is not adequate to meet the requirements of the average independent operator with the continued advance in production, development and wildcatting costs. Old and new pipe lines for oil and gas leading out of the state are removing reserves at an alarming rate. Curves showing the rate of discovery versus production and pipe-line deliveries in and out of the state make a cross that sooner or later will be fatal to the state. Wildcatting not only needs a price increase but every other available incentive and encouragement.

Jan 1, 1945

By Howard W. Miller, Charles R. L. Oder

APPROXIMATELY 5000 tons of zinc ore a day was mined during 1943 in the Mascot-Jefferson City district in East Tennessee. This ore came from the Kingsport formation, a part of the Knox dolomite, of Ordovician age. The Kingsport is composed of 350 to 400 ft. of limestone and dolomite. Thin cherts, sandy layers and shales are numerous. Frequently, the limestones are altered to crystalline dolomite. The Kingsport is divisible into four main lithologic zones. These divisions are illustrated in an accompanying table, which gives detailed sections of the ore-bearing beds as found in the mines and shows the exact positions of the various ore zones within the formation. Key beds are described and the practical applications of stratigraphy in mapping, prospecting and mining are discussed.

Jan 1, 1945