Search Documents

By J. D. Hanawalt, C. E. Nelson, J. A. Peloubet

The subject of the salt-water corrosion resistance of magnesium alloys is somewhat like that of the pitting of stainless steels, in that it involves a relatively small. percentage of the applications but receives a much greater proportion of the publicity. Actually magnesium alloys are in use in many exterior applications as well as interior, with no trouble from corrosion. Magnesium and its alloys have a striking stability against atmospheric attack, being far superior to iron. Specimens exposed unprotected to atmospheric weathering for Io Years show only a superficial surface-film formation. The basic nature of magnesium and of its important alloys is that they are also resistant to the attack of salt water even in an unprotected state, giving substantially no loss in weight after one year of alternate immersion in 3 per cent NaCl solution (Fig. 1). This basic behavior is often masked because of the extreme sensitivity of these alloys to certain impurities and combinations of impurities. It is known, and the subject of increasing emphasis, that higher purity leads generally to greater stability for many materials, non-metallic as well as metallic. However, a review of the literature on the corrosion factors in magnesium alloys shows that almost all researchers worked with base metal in which metallic impurities varied in uncontrolled amounts. The major factor, that of metallic impurities, Probably greatly overshadowed the effects of minor ones such as flux inclusions, nonmetallic impurities, porosity, metallographic state, which these researchers presumed to study. In the present investigation the first observation of interest is that whereas magnesium of commercial purity (99.9 per cent pure) has a corrosion rate in alternate immersion in 3 per cent NaCl solution at room temperature of anywhere from 5 to Ioo mg. per sq. cm. per day, the corrosion rate of high.purity magnesium is 0.15 ± 0.05 mg, per sq. cm. per day. The principle followed in the experiments was to add to such base magnesium other elements, singly and in inin in controlled and known amounts and to observe the corrosion behavior of the resulting alloy. These experiments show the existence of what may be called tolerance limits" of magnesium and some of its alloys for certain impurities. The extremely small percentages of impurities involved and the sharpness of the corrosion discontinuities appear to be quite unpredictable, In order to carry on this work, it was necessary to develop an analysis technique suitable to the problem. In some cases it was necessary quantitatively to analyze impurities to less than 0,001 per cent. The experimental data to be presented are based on observation of about 5000 alloy specimens and on more than 50,000 quantitative analyses. while the primary purpose of this paper is to present the experimentally obtained data on corrosion rates as a function of composition, and particularly to demon-

Jan 1, 1942

By J. E. Burke, C. W. Mason

In attempting to study precipitation from a tetragonal lattice, using solid solutione of bismuth in tin, it was found that although a Widmanstätten pattern is observed1,4 only a qualitative analysis of the orientation relationships is possible, because of the unusual structural changes that accompany the precipitation process. Microscopical Studies Alloys were made from Chempur tin (Standard samples 42b and 426, National Bureau of Standards), and bismuth (Kahl-baum C.P.) by melting weighed quantities together under palm oil, stirring well, and castilig in a heated graphite mold. The polishing and etching techniques employed largely govern the visibility of the structural changes. The preliminary surfacing operations were similar to those recommended by Villela and Bergekoff,5 through Behr-Manning 3/0 abrasive papers, lubricated by a solution of paraffin in kerosene. A rough metallographic polish was next given, using a thin cotton cloth charged with relevigated alumina (maximum particle size of about 4µ) and soap solution; repeated etching and polishing served to remove disturbed metal. For high-power examination better preparation was necessary. It was found that on such soft metals the threads of the fabric, rather than the abrasive, cause most of the scratching. Cotton outing flannel, which had been brushed so that the nap lay down, was fairly satisfactory, but a heavy grade of silk velvet (not the noncrushable kind) was found to be better, especially after some use. A better procedure was as follows: The metal lap was warmed slightly, and a 4-in. circle of woolen broadcloth was cemented to its center by a thin film of melted paraffin. The broadcloth was then moistened with water, and a 30 to 40 per cent solution of sodium hydroxide heated to about 50°C. was poured over it, allowed to stand for I to 2 min. and then washed off. It was neither necessary nor desirable to remove all the sodium hydroxide from the cloth, since its etching action aided in the removal of the flowed layer from the sample. The cloth was then charged with a paste of the relevigated alumina in water. Since this lap did not remove deep scratches, it was necessary previously to polish the specimen on some material such as the silk velvet. The sodium hydroxide softens and partly gelatinizes the woolen lap covering, permitting a scratch-free polish, but its action continues, and the cloth deterioratcs after about 24 hr. This is not serious, because a new lap can be prepared in about 5 min., and only small pieces of cloth are used. Etching with a strongly acid solution of ferric chloride was found satisfactory for removing the flowed layer. For the final etching, the most satisfactory reagent was that of Tafls,7 the formula for which is: FeC13.6H2O, 2 grams; HC1, 5 c.c.; H2O, 30 c.c.; C2H5OH (95 per cent), 60 C.C. This etchant reveals differences in com-

Jan 1, 1942

By Gerhard Derge, Arthur H. Grobe, Harold Markus

The high corrosion resistance possessed by tin under most circumstances, combined with its generally satisfactory appearance and useful physical properties, has led to many and varied uses for the metal. These uses have been partly limited by the fact that tin is an expensive metal, therefore many applications have been developed in which tin has been employed in combination with lead, either by coating, as in tin-lined collapsible tubes, or by the formation of alloys containing various proportions of tin-rich and lead-rich phases, as tcrne plate. A detailed knowledge of the corrosion characteristics of the tin-lead couple therefore is of general interest and has become specially important at the present time, when every effort is being made to conserve tin as much as possible. The present study has been limited to carbonate solutions with a pH range from 8.4 to 11.2 so that the results may be related to earlier work on the corrosion of tin and its alloys. 1-3,6 In these papers, the effects of a number of anion and cation additions to these solutions have been observed. Apparatus and Method The electrodes for the corrosion cell were cut from rolled sheet about 1/16 in. thick. The length of all specimens was held constant at 7 in., while the width was varied from M to 2 in. These electrodes were fastened to brass electrode supports, which were attached to rubber stoppers fitting into tall-type one-liter Pyrex beakers that contained the electrolyte. The lead electrodes were prepared from Omaha pig* and the tin was rolled from a slab of Chempur.† After cutting to size, the sheets were polished with No. I emery paper and cleaned with carbon tetrachloride. The edges, back and upper parts of the specimen were coated with a synthetic lacquer, which was supplemented with beeswax for the lead electrodes. The binding posts were coated with beeswax after the electrodes had been clamped. The pH of the electrolyte was controlled by adjusting the ratio of carbonate to bicarbonate. Approximately 600 ml. of electrolyte was used in each beaker. The entire assembly was placed in an oil bath thermostatically adjusted to operate at 30°C. + 0.1". Potentials were measured against a saturated calomel electrode connected to the cell by an agar-agar salt bridge. The carbonate solution used in the salt bridge was the same as that used in the corrosion cell. Currents were measured with a milliam-

Jan 1, 1942

By F. N. Rhines, A. H. Grobe

At elevated temperatures the oxide of silver is unstable in the air at atmospheric pressure, consequently no external oxide scale forms upon pure silver under conditions of high-temperature annealing. When small quantities of certain alloying elements are present in the silver, the formation of a thin external scale is possible1 and in addition there may form a subscale composed of the oxide of the solute element precipitated within the body of the silver. Norbury2 and Leroux and Raub3 have reported internal oxidation (subscaleiormation) in alloys of silver with 2, 7.5, and 30 per cent of copper. The presence of the subscale is believed to be responsible, at least in part, for the objectionable "fire mark" in Sterling silver.4 Several other alloys of silver, after oxidizing heat-treatments, are known to exhibit undesirable polishing characteristics that may be the result of internal oxidation. Except for the absence of an external scale of silver oxide, it is to be anticipated that silver alloys will prove to be very similar in their oxidation behavior to the alloys of copper, the oxidation characteristics of which have been studied in some detai1.5,6 The present research confirms this anticipation. The oxidation of a series of 20 dilute alloys of silver has been studied metallographically; some types of subscale not encountered among the copper alloys have been found. Instances of internal oxidation in alloys of most of the metals of the 1-6 and VIII groups of the periodic system are on record, but evidence of this type of oxidation in alloys of the metals of the intermediate groups is lacking. A number of the metals of the intermediate group, among them cadmium, lead, tin, and zinc, appear to provide the conditions essential to subscale formation; i.e., they form oxides with a relatively low negative free energy of formation, they dissolve other metals that form more stable oxides, and, presumably, oxygen will diffuse through them. In a study of 40 alloys of these white metals only a few cases of internal oxidation have been found. The probable reasons for this difference in behavior will be discussed presently. Experimental Procedure Silver.—The silver alloys employed in the oxidation studies were prepared in heats of 30 grams each from high-purity silver (99.993 per cent Ag)* and the purest avail-

Jan 1, 1942

By A. William Johnson

It was pointed out in an earlier paper1 that our understanding of the atomic mechanism by which diffusion occurs in metallic alloys is scarcely in an advanced state. This unsatisfactory condition is the result not of any lack of interest, but of the difficulty of designing experiments that .will yield suitable data. The diffusion coefficient of an alloy, measured in the usual way, is simply a number specifying the rate of homogenization of a nonhomo-geneous metal; this number, of itself, can furnish neither the rate at which the individual atoms move nor information as to the mechanism by which they move. It does not necessarily follow, however, that such information cannot be obtained, even if the path to be followed is still not clear. Much success has been attained in the study of diffusion in ionic crystals. A number of experiments, for which there are few counterparts in connection with metals, yield information often indicating a detailed mechanism by which diffusion probably occurs. From such work, quite acceptable theories of lattice imperfections have been developed by Wagner, Schottky, Frenkel, Jost and others.2 It is postulated that real crystals of stoichiometric composition contain, in equilibrium, certain imperfections of which the most importarlt types are: (I) vacant cation sites, with an equal number of interstitial ions; (2) vacant anion sites, with an equal number of interstitial ions; (3) equal numbers of anions and cations in interstitial positions; (4) equal numbers of vacant anion and cation sites. The classification of a particular crystal according to this scheme then follows from studies of the variation of electrical conductivity with pressure of the electronegative component surrounding the crystal, with ion size, and with temperature; other physical phenomena, such as the Hall effect, have aided in establishing the classification. The relative mobility of the anion and cation may be determined by chemical analysis of the salt at the electrodes following electrolysis. With such information, and knowing that one ion never occupies the lattice site normally belonging to an ion of opposite sign, it is usually possible to ascertain the diffusion mechanism. It is clear that the same experiments are not applicable to metal crystals, and substitute experiments that yield as much information have not yet been devised. Much can be learned, however, about the mobilities of the two* kinds of atoms in alloys by the use of radioactive metals as indicators. Only one such experiment has been performed in the past. In 1933, Seith and Keil,3 in an effort to explain the great difference between the rate of diffusion of gold in lead and of lead in lead, measured the rate of diffusion of radioactive lead in 3 gold-lead

Jan 1, 1942

By G. Sachs, G. Espey

Simple methods can be used for the determination of the residual stresses in thin walled tubing if the stresses consist of high tensile stresses at the one surface and high compressive stresses at the other surface. Such a stress distribution is approximated in sunk tubing and in deep-drawn shells. It is possible to cut sections from such articles in such a manner that a major part of the residual stress is relieved by a bending of the Part that is separated from the adjacent metal. The circumferential stress is evaluated from the change in diameter D, occurring on splitting a length of tubing (Fig. Ib) or from deflection resulting from the cutting out of a circumferential tongue (Fig. Ia) .6 The bending moment M released by such a flexure is. M - EI (I-I) = EI R1-R0 I - u2(R0-R1) I -V2 R0XR1 where E = modulus of elasticity, v = Poisson's ratio, I = moment of inertia of the section, R0 =. mean radius before splitting, R1 = mean radius after splitting. The release of this bending moment corresponds to the release of stresses, which, in a thin section, vary linearly from one surface to the other, and have the following value in a particular fiber a certain distance (x) from the surface: S = c d I - V2 x c x d 2 2 RI - R0____E (d ) R1 - R0 X R0 X R1 ~ i - u2 (2 x) Ro X R1 where C is the section modulus and d is the thickness of the section, the ratio M:C being d: 2 for a rectallgular section.* The maximum stress values at the surfaces are. Smax = +E X d X R1-R0 I — u2- 2 R0 X R1 For most purposes the simpler equations: EXd AD1 = ± I - u2 x dm2 and will be satisfactory, where D,, is the aver. age of the mean diameters of the tubing

Jan 1, 1942

By Clarence Zener

IT has long been known that the density of a metal usually decreases with cold-work. Thus O'Neilll observed as early as 1861 that cold hammering of commercial hot-rolled copper is accompanied by a decrease of density of 0.2 per cent, and that subsequent annealing restores the original density. The origin of this density change, however, has remained obscure. In particular, experiment has not yet decided whether it is due to the presence of small cavities and an increase in inter-granular surface or to an actual expansion of the lattice itself. This uncertainty in the origin of the change in density is a reflection of our uncertainty as to the changes induced in a metal by cold-working. One school regards cold-working as a breaking up of the original grains into a large number of perfect crystallites somewhat randomly orientated with respect to one another.2 According to this viewpoint, the mere introduction of a large intercrystallite surface induces a net volume expansion. Another school regards cold-working primarily as a distortion of the grains. It is not obvious that this second viewpoint will lead to a net volume expansion. The purpose of the present paper is to show that this is indeed the case, and that this expansion is of the right order of magnitude to explain existing experimental data. The physical basis for the association of an expansion with distortion lies essentially in the variation of the elastic moduli with volume. This variation is considerable. Thus from Table I we see that a I per cent increase in volume for the case of copper will decrease the bulk modulus K by 10 per cent, the shearing modulus µ by 3.8 per cent. If we thus twist a rod through a given angle, we shall do less work upon it if it increases slightly in volume, thereby reducing the torsion modulus that involves as a factor the shearing modulus. A general principle3 in physics states that the rod will so adjust itself as to have a minimum potential energy consistent with the end restraints. It will therefore expand. In order to obtain a quantitative comparison with experiment, we follow Maier4 in comparing the lattice expansion with the latent energy of cold-work. This latent energy has been measured directly by Taylor and Quinney5 on copper rods subjected to torsion, and may amount to as much as 15 per cent of the total work done upon the specimens. We shall assume that this

Jan 1, 1942

Time as a Factor in the Making and Treating of Steel. By John Johnston. (Howe Lecture) (T.P. 1478) Influence of Chromium and Molybdenum on Structure, Hardness and Decarburization of 0.35 Per Cent Carbon Steel. By R. F. Miller and R. F. Campbell. (T.P. 1345) Mechanical Properties of Iron-manganese Alloys. By F, M. Walters, Jr., I. R. Kramer and B. M. Loring. (T.P. 1369) The Instability of Low-expansion Iron-nickel-cobalt Alloys. By I. R. Kramer and F. M. Walters, Jr. (T.P. 1370) The S-curve of a Chromium-nickel Steel. By B. M. Loring. (T.P. 1383) A Magnetic Determination of the A3 Transformation Point in Iron. By B. A. Rogers and K. 0. Stamm. (T.P. 1388) Rapid Tension Tests Using Two-load Method. By A. V. de Forest, C. W. MacGregor and A. R. Anderson. (T.P. 1393) Effects of Scrap in the Blast-furnace Burden. By C. L. T. Edwards. (T.P. 1270) Temperature Gradients through Composite Carbon Columns and their Application to Blastfurnace Linings. By F. J. Vosburgh and M. R. HatFIeld. (T.P. 1363) Correlations of Some Coke Properties with Blast-furnace Operation. By H. W. Johnson. (T.P. 1402) The Technical Cohesive Strength and Yield Strength of Metals. By D. J. McAdam, Jr. (T.P. 1414) Effects of Eight Complex Deoxidizers on Some 0.40 Per Cent Carbon Forging Steels. By George F. Comstock. (T.P. 1417) Significance of the Bessemer End Point. By H. T. Bowman. (T.P. 1428) Structural Diagrams of Nickel Irons and Steels. By J. T. EasE and N. B. Pilling. (T.P. 1432) Carbides in Low-chromium Steel. By Walter Crafts and C. M. OFFenhauer. (T.P. 1436) Hardenability Calculated from Chemical Composition. By M. A. Grossmann. (T.P. 1437) Recrystallization of Silicon Ferrite in Terms of Rate of Nucleation and Rate of Growth. By J. K. Stanley and R. F. Mehl. (T.P. 1438) The Solubility of Carbon as Graphite in Gamma Iron. By R. W. Gurry. (T.P. 1440) An Evaluation of the Factors Affecting Iron Oxide in the Open-hearth Bath. By J. E. Gould and H. J. Hand. (T.P. 1442) Precision in Creep Testing. By J. A. Fellows, Earnshaw Cook and Howard S. Avery. (T.P. 1443) Lattice Relationships in the Decomposition of Austenite to Pearlite, Bainite and Martensite. By G. V. Smith and R. F. Mehl. (T.P. 1459) Rate of Nucleation and Rate of Growth of Pearlite. By F. C. Hull, R. A. Colton and R. F. Mehl. (T.P. 1460) Weight Change as a Criterion of Extent of Decarburization or Carburization. By R. W. Gurry. (T.P. 1470) Observations in the Making and Use of Sulphite-treated Steels. By E. L, Ramsey and L. G. Graper. (T.P. 1476) Diffusion in Metal Accompanied by Phase Change. By L. S. Darken. (T.P. 1479) Engineering Properties of Heat-resistant Alloys. By Howard S. Avery, Earnshaw Cook and J. A. Fellows. (T.P. 1480) Distribution of Manganese and of Sulphur between Slag and Metal in the Open-hearth Furnace. By L. S. Darken and B. M. Larsen. (T.P. 1481)

Jan 1, 1942

Jan 1, 1942

Jan 1, 1942

Jan 1, 1942

Jan 1, 1942

Jan 1, 1942

By Max Y. Seaton

The scope of this paper will be limited to finished materials that contain a large preponderance (around 80 per cent or more) of magnesium oxide. The large and commercially important production of refractory dolomite and modified dolomites is not discussed here, and the production of magnesium basic carbonate for use as a heat insulator is barely mentioned. The discussion is confined mainly to magnesias produced in comparatively great quantity by direct processing of naturally occurring raw materials and hence excludes secondary or highly purified products such as pharmaceutical products or U.S.P. light and heavy calcined magnesias of commerce. Nomenclature The nomenclature of the magnesia products that will be discussed is somewhat confusing, in that it is customary in the trade to designate as "calcined magnesite" the materials that result from the calcining of magnesite to temperatures that remove the contained carbon dioxide. The finished product, therefore, is not magnesite at ali but simply a more or less pure magnesium oxide or magnesia. Furthermore, partly for statistical .and partly for commercial reasons, it has been customary, during recent years, to classify as "calcined magnesite" products that result from the heat-treatmerit of magnesium hydroxide precipitated from magnesium-containing brines; prod- ucts that, obviously, have no relationship whatever to magnesite. In the listing of magnesia-containing materials, tonnages of which are regularly reported by the Bureau of Mines, reports ordinarily are made under two headings: "caustic calcined" magnesite, in which all of the varieties of products treated at relatively low temperatures are lumped; and "dead-burned" magnesite, in which are included both high-purity and low-purity, and particularly both high-iron and irow-iron, materials that have been so heat-treated that the magnesium oxide occurs predominantly as crystalline periclase— materials used almost entirely for refractory purposes. In 1940 the apparent domestic consumption of "caustic calcined" magnesite was approximatcly 17,000 tons, "bout 95 Per cent of which was produced in this country. The apparent consumption of "dead-burned" magnesite was approximately 172,000 tons, some 82 per cent of which was domestically produced. In both total quantity and percentage of material produced within the United States, these figures are record highs for manY Years past. Utilization As indicated by these figures, the major tonnage outlet for magnesia is the refractories industry, in which magnesia is employed principally in three ways: (1) as dead-burned grain magnesite for the construction and maintenance of the hearths Or bottomS of basic open-hearth furnaces; (2) in the form of refractory magnesite bricks and shapes; and (3) as a chemical

Jan 1, 1942

By Howard I. Smith

The mineral trona was discovered on Government land in 1938, about 18 miles west of the town of Green River, Wyo., in the core of the John Hay, Jr., well, a test well drilled for oil by the Mountain Fuel Supply Co. in sec. 2, T. 18 N., R. IIO W., sixth principal meridian. Although no oil or gas was reported, the drilling led to a discovery of great potential economic importance and exceptional scientific interest. Trona is a relatively rare mineral found at various places in playa deposits but not previously found at any great depth. It is composed of hydrous sodium carbonate and sodium bicarbonate (Na2CO3 NaHCo3.2H2O). Pure trona con-tains the equivalent of 70.35 per cent of sodium carbonate. Total sodium computed to carbonate times 1.42 equals the percentage of trona in the absence of other sodium carbonate minerals in the sample. Analyses Two short pieces of core sent to the author a few days after the completion of the Hay well were analyzed by R. C. Wells† and found to be exceptionally Pure trona. A brief article on this discovery has already been published.1 Arrangements were then made through W. T. Nighten-gale‡ for the author to inspect and sample the core. The company log of the well included notations of sodium salt crystals from a depth of 1190 to 1820 ft. Not being able to identify all the minerals present, the author selected several specimens of the core for petrographic examinations and sampled the sections of trona for analysis. J. J. Fahey, of the Geological Survey, examined the specimens and reported most of the crystals to be a new anhydrous sodium carbonate and calcium carbonate mineral (Na2CO 3.2 CaCO3), which he named shortite,² after Maxwell N. Short." He analyzed the samples of trona, with the results shown in Table I. In addition to the 10 ft. 1 in. of trona in the first section, it is reasonable to assume that the 9 ft. 8 in. for which no core was available for sampling is either i mostly trona or some other soluble salt, but it should not be included in calculating | reserves. In the part of the core between i 1590 ft. 3 in. and 1600 ft. 4 in. the material insoluble in cold water, amounting to about 5 per cent, was estimated petrographically I to contain 70 per cent clay, 25 per cent shortite, and 5 per cent pyrite. Accompanying Minerals Fahey later secured about 600 ft, of the core for a detailed examination and study

Jan 1, 1942

By G. M. Kirwan, Joseph B. Perry

MagnEsitE is found in 22 California counties, but many of the deposits are too small or too impure to be of commercial value. Several of substantial size and quality were entirely exhausted by wartime operation. At present, three properties comprise the only known workable deposits in the state. Of these, the Western mine and the Patterson mine have been known and worked for many years, and have been described in considerable detail in various publications, therefore need only brief mention here, because of their proximity to the Bald Eagle mine. The latter, recently developed, is unusual in type of ore deposit, plant design and operation, as well as products made, and very little has been written concerning it. WESTERN MINE The Western mine, 32 miles south of Livermore, Calif., was formerly operated by C. S. Maltby. It has been a consistent producer for many years.l The ore is of amorphous variety, occurring along fracture zones in serpentine. The veins vary greatly in width, the average being perhaps 8 ft., with the maximum indicated in one early stope of 40 ft.; 2 ft. is considered the minimum for economical mining. The strike of the veins is predominantly north and south, with dip to the west varying from 40" to 75". Walls are well defined and as a rule firm and easily supported. Veins range in length from a few hundred feet to 1000 or more. Their maximum vertical extent is about 350 ft., but many run less. Early mining consisted of open-cut and glory-hole work on the larger outcrops. This was followed underground by a modified shrinkage system, the waste and low-grade horses being removed by hand sorting on the tramming levels and transported to surface dumps. Filled-stope mining is used now, in order to eliminate the handling of waste, which has

Jan 1, 1942

By Henry Mulryan

Diatoms are microscopic aquatic plants of the order Bacillariaceae. They are unicellular plants with skelctons made up of amorphous opaline silica. The skeletons show highly ornate, complicated geometrical designs. Diatoms live in water virtually everywhere. They are found in clean sea water, brackish water, and fresh-water lakes and ponds. When conditions are right, diatoms propagate by subdivision in huge numbers. Alkalinity, temperature, and the presence of high concentrations of silica in the water largely control diatom life. When the diatoms die the skeletons drop to the bottom of their habitat to form oozes of varying thicknesses. Diatomites Diatomite, or diatomaceous earth, is composed essentially of the siliceous remains of the diatoms, although other organic skeletons are also present, especially in sea-water deposits where radiolaria, sponges and silico-flagellates are common. Impurities are generally carbonaceous material, fine-grained silt, volcanic ash and dust, and occasional coarse grains of sand. Diatomites are marine, brackish, or fresh-water, depending upon types of diatoms and their method of deposition. Diatoms More than 8000 species of diatoms have been named and classified. Some are definitely classified as to their habitat; some are so well recognized as to their living conditions that they can be stated to be diagnostic types, and when encountered in a deposit determine the origin of the deposit. Some of the commoner types of diatoms found in the freshwater diatomites on the Pacific Coast are: Cymbella lanceolata Agardh Fragilaria virescens Ralfs Encyonema prostratum Ralfs Diatoma vulgare Dory Surirella biseriata Brebison Eunotia major Ehrenberg Amphipleura pellucida Kützing Stictodiscus niagarac Ehrenberg Gomphonema geminatum Lynberg Melosira granulata Ehrenberg Epithemia turgida Kützing

Jan 1, 1942

By George R. Mansfield

Interest in the reserves of phosphate rock in the United States and their proper conservation has recently been aroused by hearings held in different parts of the country by the "Joint Committee to investigate the adequacy and use of phosphate resources of the United States." This committee was appointed within a few days after a Presidential message to Congress on the same subject, dated May 20, 1938, and began to function almost immediately. Hearings were held in Washington, D. C., Pocatello, Ida., Wilson Dam, Ala., Knoxville, Tenn., and Lakeland, Fla. The resulting testimony, when published, comprised a volume of 1182 pages.l At the earlier hearings held in Washington and Idaho the seeming disparity between the great reserves of the West and the smaller reserves in the East led to some suggestions as to the desirability of curtailing or even prohibiting the exportation of phosphate rock so that eastern producers, becoming alarmed, cooperated in making available for the use of the committee information hitherto closely guarded. This information has provided an opportunity for new studies by official agencies, for a restatement of the reserves of Florida and Tennessee, and for some modification of figures for the Western States. The writer, representing the Federal Geological Survey, was given free access to the Florida material and has prepared for publication a report,² some features of which are summarized in this paper. The Tennessee material was studied by Dr. G. I. Whitlatch,³ of the Tennessee Division of Geology. Prof. J. Stewart Williams,* of the Utah State Agricultural College at Logan, has published a recent study of the phosphate resources of Utah and the writer has given some further study to reserves of western phosphate from the viewpoint of including material of lower grade than that hitherto considered. Technologic advances in the phosphate industry must be credited with a large share in the expansion of reserves by making available for

Jan 1, 1942

By E. C. Houston, H. S. Rankin

Olivine is considered a valuable potential source of metallic magnesium in the chloride electrolytic process. Treatment of olivine with hydrochloric acid can be carried out under conditions that prevent the formation of gelatinous silicic acid, which would inhibit the reaction by forming a covering around the ore particles. It is our hypothesis that the formation of gelatinous silicic acid is avoided by the dehydrating action of the magnesium chloride, which takes up water to form a series of hydrates and leaves the silicic acid in granular condition. Leaching serves to separate the magnesium chloride from the silicic acid and unattacked ore, which can be treated with fresh acid in successive steps until extraction is essentially complete. The leach solution can be i purified by the addition of caustic magnesia and the precipitated impurities removed by decantation or filtration. The resulting magnesium chloride contains: Fe, less than 0.001 Per cent; Mn, 0.012 ; per cent; Ni, none. Chlorination† of olivine has two major defects: (1) a large part of the chlorine goes to form silicon and iron chlorides, (2) the anhydrous magnesium chloride is held by absorption in the finely divided silica. SupplY It is well known that olivine, a silicate of magnesium and iron, is present in large amounts in several localities in the United States. The largest deposits occur in the southeast and on the Pacific Coast.' The southeastern deposits were surveyed by Lewis2 in 1896 and by Hunter3 in the period 1933-1940 It is estimated that high-grade olivine, conveniently located with regard to transportation and power, is present in excess of 230 million tons above local drainage level in western North Carolina and north Georgia. Previous Technical Work In the past few years, olivine has attracted considerable attention in the refractory field. In the chemical processing industry, however, it has long been thought axiomatic that the cost of processing silicates is an economic barrier to their utilization, especially where more reactive minerals, such as carbonates, oxides or salts, are available. This attitude is not entirely justified in connection with olivine. unlike most silicates, olivine is readily attacked by acids, chlorine and other reagents without resorting to fusion to break down the silicate structure. Olivine has been suggested as a raw material for making epsom salt by roasting with pyrites.4 Other processes include acid treatment6 and digestion with calcium chloride.6 Recently a small plant was built near Webster, N. C., for making epsom salt from olivine by treatment with sulphuric acid. This plant is now in commercial operation, producing approximately two tons per day. Olivine is also receiving attention from the fertilizer industry as an inexpensive source of soluble magnesium.

Jan 1, 1942

By Edgar R. Kendall

A knowledge of the fundamental principles of locating, sampling, testing and evaluating materials is essential in prospecting for mineral aggregates. In this discussion, mineral aggregates will be considered sand, gravel, crushed stone and slag that are used as materials of construction. The quantity of mineral aggregates produced in the United States during the year 1935 for such purposes was roughly 165,000,000 tons, about 60 per cent of which was sand and gravel, 37 per cent crushed stone and 3 per cent crushed slag. The total value of this material was approximately $100,000,000. It is apparent therefore that the prospecting for suitable mineral aggregates is of considerable economic importance. In prospecting for mineral aggregates, the methods employed are the same whether the organization is large or small. In the large organization there may be available geologists for locating sources of supply, a land acquisition department to arrange for the necessary options or permits, engineers to do the sampling, a laboratory for testing, and a board of consulting materials engineers to make the final selection. Even small organizations must follow the same general procedure, though the responsibility for the selection of aggregates may rest with one man, who may or may not be an engineer, but who must depend entirely upon his own judgment. Locating the Supply The initial step in prospecting for mineral aggregates is the locating of suitable, adequate and economic sources of supply for the project in mind. Commercial plants in the vicinity should be investigated and a survey made of the existing structures that have been built of aggregates from these sources. If the structures are rather old and show no signs of deterioration, it is fairly good evidence that the aggregate is satisfactory. If materials of the proper quality can be obtained from commercial sources in sufficient quantity, and delivered to the job economically, it

Jan 1, 1942