Search Documents

By J. H. Swisher

The rate of internal sulfidation of austenitic Fe-Ti alloys in H2S-H2 gas mixtures is controlled primarily by sulfur diffusion, with counterdiffusion of titanium playing a minor role. At temperatures below 1100°C, enhanced diffusion along grain boundaries becomes important. The rate of internal sulfidation at 1300°C is approximately equal to the rate computed from the sulfur diffusion coefficient. The diffusion coefficient of titanium in y iron has been determined from electron microprobe traces in the base alloy near the subscale interface. The solubility of sulfur in Fe-Ti alloys has been measured in the temperature range from 1150° to 1300°C. The equilibrium sulfur content is found to increase with titanium content, due to the large effect of titanium on the activity coefficient of sulfur. The Ti-S interaction becomes stronger as the temperature decreases. TITANIUM as an alloying element in stainless steels is an effective scavenger for interstitial impurities, carbon in particular. Titanium is known to form stable sulfides; however extensive thermodynamic data on the Ti-S system are not available. Schindlerova and Buzek1 have shown that the Ti-S interaction in liquid iron is moderately strong. There have been no previous studies of the Ti-S interaction in solid iron. Internal sulfidation of Fe-Mn alloys was the subject of a recent investigation by Herrnstein.2 He found the rate of internal sulfidation to be an order of magnitude greater than predicted from available solubility and diffusivity data. A satisfactory explanation for the discrepancy could not be given. In the present study, the solubility of sulfur in austenitic Fe-Ti alloys was measured using a standard gas equilibration technique. Fe-Ti alloy specimens were also internally sulfidized. The rate of internal sulfidation was measured as a function of temperature and alloy composition. Supplementary electron micro-probe measurements were made to provide additional information on the nature of the internal sulfidation process. EXPERIMENTAL The starting materials were alloys containing 0.12, 0.24, 0.38, and 0.54 wt pct Ti. The alloys were made in an induction furnace by adding titanium to electrolytic iron that previously had been vacuum-carbon-deoxidized. The major impurity in the alloys as determined by chemical analysis was carbon. The carbon content of the alloys averaged about 100 ppm; metallic impurities were presented in concentrations of 50 ppm or less. Specimens were made in the form of flat plates, 0.03 by 2 by 4 cm for the equilibrium measurements and 0.5 by 1.5 by 3 cm for the rate measurements. The experiments were performed in a vertical resistance furnace wound with molybdenum wire and containing a recrystallized alumina reaction tube. In the gas train, flow rates of the reacting gases were measured using capillary flow meters. The source of H2S was a mixture of approximately 2 pct H2S in H2, which was obtained in cylinders from the Matheson Co. A chemical analysis was provided with each cylinder. The H2-H2S mixture was diluted with additional hydrogen to obtain the desired ratio of H2S to H2, and the resulting mixture was diluted with 30 pct Ar to minimize thermal segregation of H2S in the furnace. Argon was purified by passage over copper chips at 350°C and subsequently over anhydrone. Hydrogen was purified by passage over platinized asbestos at 450°C and then over anhydrone. The H2-H2S mixture was purified by passage over platinized asbestos and then over Pas. The samples used in the solubility measurements were analyzed for sulfur by combustion and iodometric titration. The subscale thickness in the internally sulfidized samples was measured on a polished cross section, using a microscope with a micrometer stage. Electron microprobe traces for titanium in solution were made on several samples that had been internally sulfidized. A Cambridge microanalyzer was used, and the known titanium content at the center of the specimen was used as a calibration standard. The procedure for the microprobe measurements will be described further when the results are presented. RESULTS AND DISCUSSION Equilibrium Data. Fig. 1 shows the sulfur concentration as a function of gas composition for three alloys equilibrated at 1300°C. The dashed line is based on data published by Turkdogan, Ignatowicz, and pearson3 for pure iron. The breaks in the curves are the saturation points for the alloys. The fact that the initial slope decreases with increasing titanium content indicates that titanium interacts strongly with sulfur in solution. To obtain information on the composition of the precipitating sulfide phase, the measurements described in Fig. 1 were extended to higher sulfur partial pressures. These results are shown in Fig. 2. (The initial portions of the curves are reproduced from Fig. 1.) The highest PH2s /pH2 ratio used is believed to be below the ratio required for the formation of a liquid sulfide phase. Time series experiments were used to study the approach to equilibrium in the samples. It was found that equilibrium with the gas phase was reached in less than 4 hr at 1300°C.

Jan 1, 1969

By A. S. Emanuel

A correlation has been developed for calculating the phase behavior of, gas-condensate systems at reservoir conditions. The correlation is based on the principle of corresponding states and has been coded for an IBM 7094. Experimental K-values were determined for several gas-condensate systems at reservoir conditions to evaluate various semi-empirical parameters of the correlation. The approximate range of application of the correlation is 150 to 300F and 1,500 to 6,000 psi. INTRODUCTION The rapid development of digital computers during the past several years has made feasible the calculation of hydrocarbon phase behavior by methods based on rigorous thermodynamic principles. Good correlationsl have been developed for low to moderate pressures, but these techniques have not yet been extended successfully to reservoir fluids at high pressures. Consequently, the determination of phase behavior of oil and gas systems at reservoir conditions is still based almost entirely on generalized data correlations or on experimental studies of the fluid in question. While these methods have been used successfully many times, they do have inherent limitations that restrict their applicability. Generalized correlations, such as the NGShlA K-charts, are limited to the range of pressure, temperature and components for which the data were determined. The accuracy of these correlations is often questionable because the effect of total system composition is not well defined. Experimental studies offer a reliable method for determining phase behavior, but usually the studies are costly and time consuming. Recently, Leland and co-workers presented a new approach to calculating phase behavior from the principles of corresponding states.6-8 Corresponding states methods determine the thermodynamics properties of a given system by comparison with a reference substance whose properties are known. The accuracy of this approach depends on close chemical and structural similarity between the reference substance and the system in question and between components within the system itself. For high accuracy, it is usually necessary to correct for chemical and structural dissimilarities. In principle, however, the corresponding states method should be no less accurate at high pressures than at low pressures, provided reference substance properties are known. This paper describes an empirical modification of the basic correlation proposed by Leland, et al.6 for the specific purpose of calculating the phase behavior of gas-condensate fluids at reservoir conditions. The modified correlation, which has been programmed for an IBM 7094, may be used for either approximate or precise determination of fluid behavior depending on the amount of analytical and, experimental data available for the system. BASIC THEORY The basic theory of the corresponding states phase equilibria correlation was first published by Leland, Chappelear and Gamson.6 Subsequently, Leland, Chappelear and Leach published methods for improving the accuracy of the original theory.7-9 The aim of the correlation is to calculate the K-value of each component of a given system as a function of pressure, temperature, and over-all composition, where Once the K-values are known, the phase behavior may be determined directly by an appropriate flash calculation. The basic equation for calculating component K-values was taken from the work of Joffe. 4 For any component i of a mixture, the K-value is given by

Jan 1, 1969

By Robert E. Green, Wolfgang Sachse

Simullaneous ultrasonic attenuation measurements of both quasishear waves propagating in single cryslals of aluminum indicate that, in the undeformed annealed state, the dislocation density is generally not uniform on all slip systems. Change oof attenuation measurements made during plastic defortnation of crystals , which possessed specific orientations ideal for studying the orientation dependence of dislocation damping, indicate that, for low strain levels, dislocation motion occurs on additional slip systems besides the primary one, even for crystals oriented for plastic deformation by single slip. THE sensitivity of internal friction measurements permits such measurements to be used successfully in studying the deformation characteristics of metal crystals. On the basis of experimental observations, T. A. Read1 was the first to associate internal friction losses with various dislocation mechanisms. Since that time further work2-' has been performed and a dislocation damping theory has been formulated by Granato and Lucke.6 In the amplitude independent region, this theory predicts the attenuation a to be dependent on an orientation factor O, a dislocation density A, and an average loop length L. if is a constant, independent of crystallographic orientation. For a given crystallographic orientation, changes in dislocation density and loop length give rise to the observed attenuation changes accompanying plastic deformation. The Granato-Liicke theory suggests the investigation of the orientation dependence of attenuation measurements in hopes of obtaining information to separate dislocation motion losses from other losses.7 An experimental study of the orientation dependence of attenuation in undeformed annealed single crystals should yield an insight into the uniformity of dislocation distribution throughout the entire specimen. A similar study on crystals plastically deformed in a prescribed fashion should give information about the alterations in the dislocation distribution on the slip systems activated during plastic deformation. The possible modes of elastic waves which can be propagated in aluminum,8 copper,9 zinc,10 and other hexagonal metals" have been calculated. Associated with each mode of wave propagation are dislocation damping orientation factors, which are based on the resolution of the stress field of that particular elastic wave onto the various operative slip systems in the material. These orientation factors have also been calculated as a function of crystallographic orientation in the papers cited above. Einspruch12 obtained agreement between predicted and observed attenuation values of longitudinal and shear waves in (100) and (110) directions of two undeformed aluminum crystal cubes. He ascribed the slight deviations between predicted and observed values to a nonuniform dislocation distribution, or to other loss mechanisms. In shear deformation of zinc crystals, Alers2 found that the attenuation of shear waves having their particle displacements in the slip plane was very sensitive to the deformation, while the longitudinal wave attenuation was affected only when the wave propagation direction was not normal to the slip plane. Using aluminum single crystals oriented for single slip, Hikata3 et al. found that during tensile deformation the change of attenuation of the shear wave (actually quasishear) having particle displacements nearly perpendicular to the primary slip direction exhibited the easy-glide phenomena, while longitudinal waves did not. Similar results were reported by Swanson and Green5 during compressive deformation of aluminum crystals. These results are in qualitative agreement with the calculated orientation factors for specimens of this orientation. In well-annealed, undeformed aluminum crystals, the damping is expected to be due to dislocations vibrating on all twelve slip systems. The orientation factors associated with this initial damping will be designated by O2 and O3, where a, represents the average orientation factor for the slow shear (or quasishear) wave and O3 represents the average orientation factor for the fast shear (or quasishear) wave. The calculation of these values for aluminum crystals by Hinton and Green8 shows that they vary very little as a function of crystallographic orientation—at most, by a factor of 2.47. If the dislocation density and loop length are uniform, then in the initial undeformed state, Here the subscript zero refers to the initial value of the attenuation. Also for aluminum, the calculations8 show that the orientation factors for primary slip only, associated with each shear wave, exhibit a sharp minimum for particular crystallographic orientations. A composite plot of the two shear wave orientation factors for primary slip only is shown in Fig. 1. Since these orientation factors are associated with dislocation motion occurring on the primary slip system only, the proper condition to check these factors might be attained by slightly deforming a single crystal oriented for primary slip. For dislocation motion on the primary slip system only,

Jan 1, 1969

By Charles M. Packer, Oleg D. Sherby, Roy H. Johnson

Originally round tensile specimens of a eutectic Zn-A1 alloy develop elliptical cross sections during superplastic deformation. This observation, coupled with a detailed study of the microstructure and preferred orieniation, suggests that crystallographic slip and continuous grain boundary migration or re-crystallization are important processes during super-plastic deformation. In spite of the extensive activity in superplasticity1-15 and the numerous explanations proposed, no single model has had universal acceptance. It has been established, however, that the general requirements for superplastic extension of two-phase alloys include an extremely fine, stabilized grain size of the order of a few microns, a temperature about equal to or greater than one-half the melting point, a critical range of strain rate, and a similarity in the mechanical strength of the major phases. The proposed models can perhaps best be characterized in terms of the important phenomena associated with them. These phenomena include: phase instability,1 diffusional creep by volume diffusion3 or grain boundary diffusion4,5 slip and continuous grain boundary migration or recrystalliza-tion,= grain boundary Sliding,7-9,13,14 and dislocation glide.'5 In this paper, experimental observations will be reported which support a model involving slip and continuous grain boundary migration or recrystalliza-tion. Specifically, a correlation will be made between this model and the development of elliptical cross sections as originally round specimens are superplas-tically deformed. For the most part, superplasticity studies have been conducted with eutectic or eutectoid alloys. Probably the most thoroughly studied material has been the monotectoid Zn-A1 alloy.1,2,6,12,13,15 No attention to the eutectic Zn-A1 alloy has previously been reported, and the results discussed in this paper represent part of a general study of the superplastic properties of this alloy. MATERIALS The alloys used in this investigation were prepared by melting appropriate quantities of 99.99+ pct A1 and 99.999 pct Zn in air, mixing, and pouring into a water- cooled stainless-steel mold. Wet-chemical analysis was conducted with each heat of alloy prepared, using the procedure of Fish and smith.16 The composition of the eutectic alloy was 95.1 wt pct Zn. Ingots about 2 in. thick were rolled to 0.4-in. plate at about 300°C with a reduction of 5 to 10 pct per pass. Specimens were machined from the plate with the tensile axis parallel to the rolling direction. The specimens were round, with 0.150-in.-diam, 1.25-in.-long gage length, and 0.25-in.-diam threaded grip sections. EXPERIMENTAL PROCEDURE Specimens were mounted inside a uniform-temperature quartz tube which was surrounded by a double elliptical radiant furnace with a 12-in.-long uniform-temperature hot zone and a low thermal capacity. The tube extended through the top and bottom of the furnace and permitted rapid quenching of the loaded specimens when quickly filled with cold water at the conclusion of the test. The quench precluded any effects on specimen microstructure from a normal, slow cool. Constant stress was applied to test specimens by suspending a load on a constant stress cam of the type described by Hopkin.17 The design of this cam permitted application of a constant stress for elongations up to 200 pct. For greater elongation, approximately constant stress conditions were maintained by systematically reducing the load manually. RESULTS As part of an investigation of the superplastic properties of the eutectic Zn-A1 alloy, evidence was obtained for the development of elliptically shaped cross sections as originally round specimens were extended. For example, after an elongation of about 100 pct, a round specimen with an initial diameter of 0.150 in. became elliptical with major and minor axis of 0.128 and 0.88 in., respectively. Photographs are presented to illustrate the ellipticity developed during superplastic deformation, Fig. 1. The specimen shown was deformed at a stress of 500 psi, at a temperature of 285°C, and a strain rate of 2.28 x 10-2 min-1. The strain-rate sensitivity exponent* was measured at *The strain-rate sensitivity exponent, m, is defined as d In o/d In c where o is the steady-state flow stress and E is the strain rate. this temperature and in the strain rate range 10"3 to 10-1 min-1 was found to be about 0.5. This value is typical of those observed with superplastic materials. The material studied exhibited negligible strain hardening during superplastic deformation, the creep rate remaining constant under constant stress and temper-

Jan 1, 1969

By G. W. Healy, L. F. Sander

was investigated by reacting thin discs of calcium oxide with gas mixtures of CO2, CO, and Son. Its value was 19,300 * 300 cal independent of temperature in this range. No solid solubility of sulfur in calcium oxide was detected within the limits of the experimental method and it is estimated to be below 0.025 pct by weight. The importance of lime in desulfurization is well-established but complete information on the pure phase equilibrium: CaO + 1/2 s2 = CaS + +02 [11 is not yet available. The goal of this work was to evaluate solid solubility of CaS in CaO and to determine the free-energy change associated with Reaction [I] at temperatures of 1400" to 1650°C. The equilibrium constant for Reaction [1] can be written: It is convenient to rewrite Eq. [2] in the form: where A = {Ps /PqJ1'2 has been referred to' as the "sulfurizing power' of a gas mixture. In this work, thin discs of CaO were suspended in a vertical tube furnace and exposed to CO + CO2 + SOz gas mixtures having known values of A. The samples were then analyzed for sulfur. As expected, X-ray diffraction confirmed that CaS was the only sulfur-bearing phase formed at the relatively low oxygen pressures used. EXPERIMENTAL PROCEDURE Reagent-grade CaCO3 was pressed in a 3/8-in.-diam pill die and prefired in air to produce CaO discs weighing between 0.004 and 0.01 g. Several discs were used to provide a suitable weight for chemical analysis while maintaining a large surface area to react with gas mixtures. These were placed in a platinum mesh basket and suspended in the gas stream in the hot zone of a vertical tube furnace. Desired gas mixtures were prepared from cp grade CO and CO2 and anhydrous grade SO2. The method of soap bubble displacement was used to calibrate capillary flow meters. While this gave excellent results with CO and Con, some problems with bubble insta- bility and soap film "drag" arose with the use of SO2 at low flow rates. Hence, frequent sampling and analysis of gas mixtures was carried out to insure proper control of the ingoing SOZ. The furnace used for gas:solid equilibration was a vertical mullite tube externally wound with 60 pct Pt-40 pct Rh wire having a diameter of 0.028 in. An inner tube of $ in. ID served as the reaction chamber having Pyrex ground joints sealed to the mullite to provide gas-tight connections at top and bottom. A Pt-Pt 10 pct Rh thermocouple was inserted into a protection tube adjacent to the sample basket to measure sample temperature during a run. Constant-temperature control to 2C was observed at any desired set point within the range of this investigation. This was accomplished by a control thermocouple imbedded in the furnace windings which served to actuate an electronic controller wired for high-low operation. The sulfur analyses of the solid samples were carried out using a stoichiometric combustion technique based on the method of Fincham and Richardson. Some analyses were done using a modified evolution method3 but these were used primarily to check the results of the combustion method. The results were in good agreement but the combustion technique of-ferred an advantage in economy of time and material. CALCULATION OF GAS EQUILIBRIA Heating a given mixture of CO + CO + SO2 to high temperatures gives rise to a large number of product species. The details of calculating the partial pressures of these products of interaction and dissociation can be found in several references4,5 and need not be repeated here. The thermodynamic data selected for the major species in the gas mixtures are shown in Table I. Equilibrium constants from these reactions were combined with oxygen, carbon, and sulfur balances and a computer program written to facilitate the calculations. Some early difficulties in reproducing experimental results were finally traced to the effect of atmospheric pressure changes. No reference to consideration of this question had been found in the

Jan 1, 1969

By Francis Cameron

Gloomy predictions that domestic mineral reserves are approaching exhaustion are unwarranted and may be harmful, this author contends. Specific mineral forecasting errors in the Paley Report are cited to support this contention, and steps that can be taken to insure a progressive mineral industry capable of keeping pace with the major raw material needs of the nation through advancing technology are suggested. Mining is both exciting and rewarding —although at times somewhat frustrating— and we all can have real pride in our industry, in its people, and in its accomplishments. It is, however, with concern that I have noted a deterioration in this Country in what might be called mining's stature and in the growth of a belief in many quarters that our mineral reserves are rapidly approaching exhaustion. In other words, there is a popular image that we are fast becoming a "have not" nation in many respects and that the domestic mining industry can no longer be considered, in the vernacular of Wall Street to offer much in the way of "growth potential." I do not subscribe to this hypothesis, nor do I be-li4ve that the record of the mining industry bears this out. However, let me add that we can, in time, talk ourselves into this frame of mind and we can hasten the day when this very well might come about by unnecessary and unwise legislation or regulation. My remarks today are basically designed to give my reasons for refuting this negative philosophy and to review our record. With your help, I know we can improve our image, and the public's recognition of our industry's peculiar problems. The progress of our civilization over the centuries has been fundamentally based upon proper use of raw materials, both agricultural and mineral, and upon energy, human or otherwise. As the standard of living has progressed century by century, the demands for mineral raw materials have increased in an irregular, but steadily rising progression. Fortunately, those minerals on which we depend most, i.e., iron, coal, petroleum, copper, aluminum, lead, and zinc have been neither too difficult to find nor to process into useful form. Iron, the most useful of all metals, is present in various amounts in most rock types and soils. Gold, seemingly the most generally desired (but certainly not the most useful of all metals), occurs in sea water in a far greater total tonnage than has been won from all of the world's known gold mines. If the latter is true, then why do we not see large installations treating sea water for the recovery of its gold content? The answer, of course, is that even the French, who seem, from their recent actions, to value gold above all else, have not devised a way of doing this at a profit. Theoretically, it is possible, but not with today's technology at a cost which would justify the effort. Man has exploited only those mineral concentrations which accidents of nature have placed within his so far limited means of finding and utilizing. What we geologists and engineers refer to as an orebody is nothing more than a concentration of minerals, exploitable with available knowledge, that will yield a value greater than the value attached to the energy and capital required to produce it. What is "ore" and what is not "ore" is, in the end, a matter of economics. The economic problem stems from the physical and chemical character of mineral deposits. The good Lord stacked the cards heavily in favor of rising costs by limiting the amount of the higher grade ores easily available. As the best and most accessible ores are depleted, it becomes necessary to work harder and with greater ingenuity to produce more from less accessible and lower grade resources. The quantity of mineral raw materials we can have in the future will be determined largely by what we can afford to pay for them in terms of human effort, capital outlay and production energies. We will always have the problem of cost with us and our only real means of keeping ahead of rising costs is by continually improving our technical abilities. We, in this country at least, no longer have open to us large and unexplored virgin wildernesses in which a pick-and-shovel prospector might uncover an untouched mineral bonanza. The rest of the world also has few conventional frontiers left in which the explorer-prospector is free to roam. We do, however, have enormous land areas unexplored, and untouched po-

Jan 1, 1969

By Alan J. Strauss

The Group IV elements germanium, tin, and lead form nine 1:1 compounds with the Group VI elements sulfur, selenium, and tellurium. This paper reviews the properties of the pseudobinary solid solutions formed by these compounds, including the extent of mutual solid solubility, temperature-composition phase diagrams, transport properties, deviations from stoichiometry, optical properties, and energy band structure. Particular emphasis is placed on the Pbl-xSnxTe and Pb1-xSn,Se alloys with rocksalt structure, because of current interest in these malerials for generating and detecting infrared ,radiation. ThE Group IV elements germanium, tin, and lead form nine 1:1 compounds with the Group VI elements sulfur, selenium, and tellurium. Some of the physical and electronic properties of these compounds, including their melting points1-8 and energy gaps,4'9-12 are listed in Table I. Four compounds (SnTe, PbS, PbSe, and PbTe) have the cubic rocksalt (Bl) structure. At room temperature GeTe has a rhombohedra1 structure closely related to the B1 structure, into which it is transformed at about 400°C. Four compounds (GeS, GeSe, SnS, and SnSe) have the orthorhombic B29 structure. In samples which have not been intentionally doped with impurities, the electrical conductivity is due primarily to electrons or holes produced by the ionization of donor or acceptor lattice defects associated with deviations from stoichiometry. Undoped samples of PbS, PbSe, and PbTe may be either n type or p type, depending on whether they contain excess lead or an excess of the Group VI element, respectively, but only p-type samples of the other compounds have been reported. This paper will review the properties of the pseudo-binary solid solutions formed by the nine 1:l compounds. The topics to be considered include the extent of mutual solid solubility, temperature-composition phase diagrams, transport properties, deviations from stoichiometry, optical properties, and band structure. Particular emphasis will be placed on the Pb]-xSnxTe and Pbl-xSnxSe alloys with B1 structure, which are promising materials for generating and detecting infrared radiation in the 8 to 14 µm atmospheric window and beyond. MUTUAL SOLID SOLUBILITY The extent of mutual solid solubility in the pseudo-binary systems has been investigated for fourteen of the eighteen ternary systems (in which the two terminal compounds have a common element) and for nine of the eighteen quaternary systems. In most cases, X-ray diffraction measurements made at room temperature were used to determine the structure and lattice parameter(s) of the phase(s) present in samples of various compositions prepared by freezing from the melt. In many investigations, including the extensive studies of Krebs and co-workers,13'14 the samples were annealed at elevated temperatures before X-ray measurements were made. In some cases, metallographic examination and thermal analysis have also been employed. The results for the ternary and quaternary systems are summarized in Tables II and III, respectively. (The original references should be consulted for the annealing temperatures.) The solubility of one compound in the other is at least 5 mol pct in all cases, and is often much larger. Complete solid solubility has been observed in all systems so far investigated in which the terminal compounds have the same structure, although in the PbS-PbTe system complete solubility is limited to elevated temperatures. Thus complete solid solubility occurs in five systems where both compounds have the B1 structure (SnTe-PbTe, PbS-PbSe, PbS-PbTe at temperatures above 805°C, PbSe-PbTe, and SnTe-PbSe) and in three where both compounds have the B29 structure (GeS-SnS. GeSe-~n~e-, and SnS-SnSe), as well as in two involving GeTe and a compound with B1 structure (GeTe-SnTe and GeTe-PbTe). On the basis of thermal analysis data, complete solid solubility at sufficiently high temperatures has also been reported for the GeSe-GeTe2 and SnS- pbS22 systems. This seems unlikely, however,

Jan 1, 1969

By N. G. W., Cook

When an excavation is made underground the original rock stresses are removed from the surfaces of the excavation. These surfaces converge to partially close the excavation and the superincumbent rock mass moves down towards the excavation. If the convergence of the surfaces of the excavation were controlled, energy generated by their motion against the controlling forces could be extracted. Since the total forces in the rock mass are not significantly affected by the excavation, stress concentrations arise around the excavation, which compensate exactly for those stresses no longer transmitted through the excavation. These phenomena give rise to two general principles which provide the basis for analyzing the effects of making any underground excavation. The first of these is that the total force resulting from the stresses across any plane in the rock, including any plane through the excavation, must be the same before and after the excavation is made. The second of these is that energy must necessarily be released as a result of making an underground excavation.

Jan 1, 1969

By Y. Kondo, S. Yamazaki, Z. Asaki

Thermal deco7nposition of Pyrite particles in a fluidized bed with inert gas stream was studied. Assuming that heat transfer from the surroundings to the fluidized particles controls the overall decomposition rate, rate equations for the batch process and for the continuous process were derived. In the batch experiment, a linear rate equation satisfies the experimental results and the overall heat transfer coefficient calculated from the rate constant agrees fairly well with that obtained by Leva.l1 For the continuous process, two rate equations were derived, one on the assumption of complete mixing of particles and another on the upward piston flow of particles in a fluidized bed. The former holds for a bed containing a higher fraction of decomposed pyrite realized at lower feeding rates. The latter can be applied for a bed at higher feeding rates. Thus, segregation of particles in the fluidized bed was indicated at higher feeding rates. Bed temperatures also correspond to these conditions. ThERMAL decomposition of pyrite may be represented by Eq. [I]. The pressure of diatomic sulfur gas reaches 1 atm at about 690°C. The thermodynamics,' kinetics,2'3 composition, and properties3-5 of decomposed products of such a reaction have been studied. Pyrite is a very common sul-fide mineral and is often accompanied with other sul-fides. It is of basic interest in nonferrous metallurgy to clarify the behavior of pyrite in the pyrometallur-gical processes of sulfide minerals of metals such as copper, lead, zinc, nickel, and so forth. Interest in this reaction increased recently because of possible elimination of arsenic from pyrite in processing highly purified iron oxide pellets. Producing elemental sulfur from pyrite, instead of sulfuric acid, also aroused interest in this reaction. It is indicated that the thermal decomposition of solid particles, such as calcium carbonate, proceeds through three major sequential steps: heat transfer, interfacial chemical reaction, and mass transfer.637 It is known that the decomposed product of pyrite is very porous2, 3 and the diatomic sulfur gas evolved can easily escape through this layer of decomposed product. It depends upon the circumstances, therefore, whether the heat transfer to the interface within particles or the chemical reaction at the interface determines the overall decomposition rate. The enthalpy change in the decomposition of pyrite is about 33 kcal per mole FeS2 which is comparable to that of calcium carbonate. The decomposition of calcium car- bonate becomes more and more dependent on the rate of transport of heat when reaction temperature increases, such as occurs in a fluidized bed.6'7 It is reasonable to presume, therefore, that the thermal decomposition of pyrite, an endothermic process, carried out in a fluidized bed may be analyzed according to the heat transfer controlling model. This work intends, first, to propose a mathematical model that determines the overall rate in a fluidized bed for the decomposition process and, second, to investigate a few characteristics of the fluidized bed based upon the experimental results obtained. KINETICS OF THERMAL DECOMPOSITION IN A FLUIDIZED BED It is intended in this section to obtain rate equations for thermal decomposition of pyrite in a fluidized bed by assuming that the overall rate is determined by heat transfer from the surroundings to the particles. Both batch and continuous processes are considered. 1) Batch Process. To obtain the rate equation in the batch process, the following two additional assumptions are made. First, the temperature of preheated inert gas, tg, blown into the fluidized bed is assumed to be the same as the temperature of the fluidized bed, tf. Thus, no heat exchange occurs between the gas and particles in the bed and only the heat transfer from the reactor wall kept at tw to the particles is to be considered. Second, the decomposition is assumed to start at the outer surface of the particles and to proceed toward the center. At any given time during decomposition, undecomposed pyrite remains in the tori at a temperature: td. The decomposed shell is composed of FeS1+x whose outer surface is at tp Diatomic sulfur gas evolving at the interface is heated to tf during its escape through the decomposed shell. This is illustrated in Fig. 1. With the above-mentioned assumptions of heat transfer, we have:

Jan 1, 1969

By Atsushi Watanabe

Japanese Operations Research Committee for Mining Industry is one of the committees in The Union of Japanese Scientists and Engineers. Members of the committee are Dowa Mining, Furukawa Mining, Mitsubishi Metal Mining, Mitsui Mining and Smelting, Nippon Mining and Sumitomo Metal Mining. This paper is an annotated summary of study reports of the committee.

Jan 1, 1969

By E. A. Steigerwald, G. L. Hanna

The influence of work-hardening exponent on the variation of fracture toughness with material thickness was studied for high-strength steel, aluminum, and titanium alloys. The results indicate that, when materials are compared at similar fracture toughness to yield strength ratios, the material with the lower work-hardening exponent undergoes the transition from flat to slant fracture at a larger thickness than material with a high work-hardening exponent. In the thickness range where complete slant fracture is obtained the reverse is true and a lower work-hardening exponent results in a lower fracture toughness. The influence of work-hardening exponent on fracture toughness is, therefore, dependent on the particular fracture mode. In the transition region a low work-hardening exponent is beneficial for fracture toughness while in the 100 pct slant region it is detrimental. THROUGH the use of fracture mechanics analyses, the influence of geometric variables on the crack propagation resistance of structures can be interpreted with reasonable consistency. However, in order to gain a more complete understanding of the fracture process, the influence of material parameters on crack propagation must be defined and coupled to the macroscopic fracture mechanics approach. The work-hardening exponent, which characterizes specific material behavior, may serve as an effective parameter to allow some degree of coupling to be accomplished. In the extension of a crack in a specimen of suitable dimensions the propagation process occurs in a stable manner when the crack extension force is balanced by the resistance to crack extension, which exists in the material at the crack tip. As the applied stress, and therefore the crack extension force, on the specimen increases, the resistance also increases primarily because the effective plastic zone at the crack tip, which is the main energy absorption process, becomes larger. Since the work-hardening rate of a material influences the stress-strain relationship, it will also influence the energy absorption process in the plastic enclave at the crack tip and hence should have an effect on crack propagation. A number of studies have been made correlating the strain-hardening exponent or the strain to tensile instability with the ability of a material to resist fracture. Gensamer1 concluded that a low-strain-hardening exponent would result in a steep strain gradient at the base of a notch. He reasoned that a large work-hardening coefficient would result in high-energy ab- sorption due to the increased area under the stress-strain curve. Larson and Nunes2 experimentally observed in Charpy tests on steels heat-treated to below 200,000 psi yield strength that the energy to failure in the fibrous mode, i.e., above the brittle-to-ductile transition temperature, was logarithmically related to the strain-hardening exponent. In order to avoid the complicating effects present in studying materials which undergo a brittle-to-ductile transition, Ripling evaluated the notch sensitivity of a variety of fcc metals with varying work-hardening exponents.3 The results indicated that the relative notch sensitivity, as determined from tests on specimens with a sharp notch, decreased with increasing values of strain hardening. Although the energy required for ductile or fibrous fracture increases with increasing work hardening, high-strength steels often exhibit improved crack propagation resistance when heat-treated to obtain low values of strain hardening.4,5 An analysis of whether low strain hardening is beneficial or detrimental to crack propagation resistance must depend on the particular fracture criterion involved. At temperatures where the material is relatively ductile and the development of a critical strain is required for fracture, high strain hardening increases the energy required to produce failure. In the transition region and below, however, a critical stress law appears to be valid6 and a low rate of work hardening may produce superior resistance to semibrittle crack propagation. The experimental program is aimed at studying these possibilities and determining the specific influence of strain hardening on the crack propagation resistance of several high-strength materials. MATERIALS AND PROCEDURE The alloys, chosen as representative of various classes of high-strength materials, are summarized in Table I. The heat treatments evaluated along with the smooth tensile properties are presented in Table 11. Pin-loaded sheet tensile specimens were employed to determine the smooth tensile properties. A strain gage extensometer (measuring range 0.200 in.) was used at a strain rate of 0.02 in. per in. per min. The work-hardening exponents were determined from the stress-strain curves generated in the smooth tensile tests and the assumption that the portion of the stress-strain curve beyond the yield point can be described by the power relationship: where a is the true stress, P is the true plastic strain,

Jan 1, 1969

By M. B. Bever, A. K. Jena

THE heats of formation ?H at 273°K of the compound AgMg as a function of composition have been measured by solution calorimetry.1 The value at the stoichiometric composition is -4.41 kcal per g-atom. From electromotive force measurements2'3 the heat of formation at 773°K of stoichiometric AgMg has been determined as -5.19 kcal per g-atom.4 The combination of these two values results in an unusually high negative temperature coefficient of the heat of formation d?H/dT = ?Cp = -1.6 cal per g-atom-OK. By contrast, published heat contents of the compound AgMg and the component elements above room temperature5 indicate that the temperature coefficient of the heat of formation of AgMg is nearly zero. In this communication calorimetrically measured heats of formation of A.K.JENA,Junior- MemberAIME,andM.B. BEVER,Member AIME, are Staff Member, Division of Sponsored Research, and Professor of Metallurgy, respectively, Massachusetts Institute of Technology, Cambridge, Mass. Manuscript submitted July 1, 1968. IMD AgMg below room temperature are reported and the temperature dependence of the heat of formation is discussed. The heat effects of additions of samples of the compound AgMg containing 50.1 at. pct Mg to liquid tin-rich solutions at 623°K were measured in a solution Calorimeter.6 The heat effects of additions plotted against the average of the atom fractions of solutes in the solution before and after each addition were a linear function of composition from which the heat effect at infinite dilution was obtained, Table I. The calorimeter was calibrated by additions of tin; the heat content (H623°K - H273°K) of tin was taken as 4.08 kcal per g-atom.4 The heat effect at infinite dilution of an addition of where heat of formation of AgMg at T°K, T = temperature from which samples are added (78°, 195°. and 273°K), Xi = atom fraction of i in AgMg, ?Hi = relative partial gram-atomic enthalpy of i in tin-rich solution.

Jan 1, 1969

By A. F. Crowley, D. W. G. White

AS part of a continuing program of liquid metals research, the densities of liquid lead, tin, zinc, cadmium, and indium have been measured by a pycnometric method. The pycnometers are made of high-density graphite to the design illustrated in Fig. l(a). In pursuing this research program, emphasis has been placed on detailed experimental care. As a result, claims are made for densities accurate to within ± 0.05 pct over temperature ranges varying from about 100° to 200°C above the melting point. A paper reporting the densities of tin, lead, and Pn-Sn alloys has recently been published,' while papers dealing with

Jan 1, 1969

By R. W. Stormont, F. Wald

The phase diagram of the Pseudobinary section PbTe-Fe was determined. It was found to contain a monotectic and a eutectic reaction, the latter one taking place at 14 at. pct Fe and 875° * 5°C. The solid solubility of iron in PbTe was found to be 0.3 at. pct by electronmicroProbe analysis. No solubility of PbTe was detected in iron. Slight deviations from true pseudobinary behavior were found to occur in the range of - 5 to 10 at. pct Fe. In the course of a general investigation of reactions of various metals with lead and tin telluride,' the lead telluride-iron system was reinvestigated. It had been established much earlier than iron does not chemically react with lead telluride but forms a eutectic with a melting point of 879" The eutectic composition or other related information has never been reported, but for a number of years iron has been in general use for contacting of lead telluride and lead telluride alloys for thermoelectric applications. It seems therefore desirable to clarify the exact constitution of the system to furnish a base for the long-term evaluation of bonds made between lead telluride and iron either by pressure contacting or by brazing methods. I) EXPERIMENTAL METHODS Lead telluride-iron alloys were prepared in 10-g charges, using premelted lead telluride. This material was prepared from high-purity, semiconductor-grade lead and tellurium obtained from the American Smelting and Refining Co. and described as 99.999 pct pure. The iron used was "Armco" iron; the major impurities found here were 0.02 pct C, 0.018 pct Si, and 0.015 pct Cr. All remaining impurities were less than 0.01, the total of all impurities not exceeding 0.15 pct. Charges were prepared in closed quartz arnpoules which were evacuated and in some cases backfilled with high-purity argon to retard excessive lead telluride evaporation and deposition in slightly cooler parts of the ampoule. For high iron concentrations, this can lead to total separation of the constituents, since the vapor pressure and the sublimation rate of PbTe are quite high.4 Nevertheless, since the ampoules are closed, no change in overall composition was expected and the nominal composition of all alloys was assumed to be retained. X-ray diffraction analysis, thermal analysis, and microsections were used in the evaluation of the alloys. The nature of the system was such that X-ray diffraction was not particularly helpful. It merely served to establish that at all concentrations PbTe and a! iron were in equilibrium at room temperature. Thermal analysis was carried out by taking direct temperature vs time curves on a Sargent recorder where a width of 10 in. was kept as 1 or 0.5 mv by use of an automatic bucking voltage network. Quartz ampoules with minimized dead space, coated with boron nitride and fitted with a thermocouple reentrant, were used as containers for the charge. At high temperatures and over long periods of time, boron nitride reacts with iron. For the thermal analysis runs, however, this was not significant. More significant was the fact that the vapor pressure of PbTe at some of the meas -uring temperatures apparently exceeded I atrn quite considerably. This, in some cases, caused the slightly softened quartz tubes to blow out if great care was not taken to contain them and minimize time and temperatures used. As containers pure nickel tubes were used which also served to avoid temperature gradients in the quartz ampoule. Nevertheless, the experimental difficulties at high temperatures were severe and the monotectic temperature could therefore not be determined accurately. In general, the accuracy reached by the thermal analysis setup in this case is *4"C as determined with gold, silver, and tin, under the conditions of analysis here. Inherently, the apparatus is capable of reaching accuracies better than i 1°C. Also, difficulties were encountered in microsection-ing. They were related to polishing, since it is rather difficult to avoid pulling the iron out of the weak and brittle lead telluride matrix. It proved best to follow a procedure where, after grinding to 600 grit on carborundum paper, a polish with 6 p diamond was used on nylon cloth. Finally, #3 "Buehler" alumina and an automatic polisher were used for -5 min only, to avoid relief. The best etching results were achieved with

Jan 1, 1969

By Colin J. Dixon

The full realization of the potential of computers in geological in- formation system demands new approaches to the machine representation of information. At the same time, the feasibility of such a system, particularly in commercial field, demands greater freedom in input preparation and a degree of standardization in the arrangement of subject matter system. The paper describes some of the basic notions of project "GEOSEMANTICA 70". The aim of the project is to devise means of storing real geological informations in a machine rather than the representation of the information in human language form. This is seen as the only long-term solution to the problems of the complex vocabulary of geology and the complex syntax of geological description. Effectively, a machine language is being defined, consisting of a set of symbols and a date structure for representation of geological and related information. Beyond this, is the definition of a set of rules allowing the use of constrained text as an input/output medium. The investigation is oriented primarily to the representation and handling of information about mineral deposits and the associated geographic, economic and engineering information.

Jan 1, 1969

By R. W. Heckel, R. E. Trabocco

The recovery process in 400 Monel filings was followed, principally, by using the Warren-Averbach technique of X-ray peak profile analysis. The deformation fault probability, a, was 0.006 in samples of unannealed filings. a , the twin fault Probability , was approximately 0.002 in samples of unannealed filings. Both a and 0 were found to "anneal out" at 600°F. The effective particle size and mzs strain increased and decreased in the (111) direction, respectively, with increasing annealing temperature. The actual particle size was found to be almost equivalent to the effective particle size. Tile small values of deformation and twin fault probabilities accounted for the similarity in values of the effective and actual particle sizes. Stored strain energy and dislocation density calculations based on rms strain decreased with increasing annealing temperature. The dislocation density decreased from 10" per sq cm in the unannealed filings to 10' per sq cm in the partially re-crystallized filings. The square root of the dislocation density based on strain to that based on particle size indicated a random dislocation distribution in the unannealed filings. The dislocation arrangement changed to one with dislocations in cell walls with increasing annealing temperature. THE recovery processes which occur in metals are generally thought to be a redistribution and/or annihilation of defects.' Investigators' have shown that recovery processes can be characterized by X-ray line-broadening analyses. Michell and Haig4 measured the stored energy of nickel powder by calori-metry and found the value to be greater by a factor of 2.5 than that from X-ray data obtained by the Warren-Averbach technique.= Minor increases in particle size occurred up to 752°F (recovery), while above 752°F the particle size increased greatly due to recrystalliza-tion. X-ray microstrain values decreased between room temperature and 392"F, remained constant from 392" to 752"F, and decreased from 752°F to a negligible value at 1112°F. Faulkner developed an equation for calculating stored strain energy based on X-ray line-broadening data which gave a closer correlation of measured and calculated stored strain energy based on the data of Michell and Haig. The stored strain energy released during recovery is predominately dependent on the decrease in dislocation density which was p-enerated from cold work.7 Stored energy has been measured8 in alkali halides during recovery and recrystallization and 80 pct of the stored energy was found to be released during recovery. Dislocation distributions have been studiedg in a number of fcc metals by thin-film electron microscopy. Howie and Swann" found the stacking fault energy of copper and nickel to be 40 and 150 ergs per sq cm, respectively. ~rown" has pointed out that these stacking fault energy values should be corrected to 92 and 345 ergs per sq cm, respectively. The dislocation distribution of a metal is directly dependent on the stacking fault energy of the system. Metals of high stacking fault energy such as aluminum cross-slip readily and do not form planar arrays of dislocations. Metals of lower stacking fault energy such as stainless steels" do not cross-slip readily. Cold-worked nickel has been found to form a cellular dislocation structure after annealing.13 The relatively high stacking fault energy of nickel and copperlo to a lesser extent favor cellular structures of dislocations rather than planar arrays after deformation. The present study of recovery was carried out on a Ni-Cu alloy (Monel 400) to compare with prior studies for pure nickel and pure copper. X-ray line-broadening techniques were used to measure the effect of recovery temperature on rms strain and particle size and the results were compared with previous studies on copper'4-'7 and nickel., Calculations were also made on stacking fault probabilities, dislocation density, dislocation distribution, and stored strain energy as affected by temperature. EXPERIMENTAL PROCEDURE The nominal analysis of the Monel 400 used in this investigation was: 66.0 pct Ni, 31.5 pct Cu, 0.12 pct C, 0.90 pct Mn, 1.35 pct Fe, 0.005 pct S, 0.15 pct Si. The annealed material was cold-reduced in two batches, one 50 pct and the other 80 pct. It was originally planned to conduct line-broadening studies of these bulk samples; however, rolling textures that developed produced low-intensity peaks which were not suitable for line-broadening analysis. Filings were prepared at room temperature from both the 50 and 80 pct cold-reduced specimens, series A and series B, respectively, and were not screened prior to heat treatment or X-ray studies. Heating to the annealing temperature, 200" to 120O°F, was accomplished in a matter of minutes in a hydrogen atmosphere. Following heat treatment, some of the filings were mounted and polished for microhardness measurements with a Bergsman microhardness tester, using a 10-g load. A G.E. XRD-5 diffractometer using nickel-filtered Cum radiation was used to obtain all diffraction patterns. Only (111)- (222) line-broadenin data were used in the present study since the {400f peaks were too weak to use. The Fourier analysis of the (111) and (222) peak

Jan 1, 1969

By M. I. Jacobson, A. S. Yue, A. E. Vidoz, F. W. Crossman

An equation governing the concept of constitutional supercooling under the combined effect of concentration and temperature gradients was used to produce platelike Al-CuAl2 eutectic composites for mechanical properties studies. Compression specimens were prepared from a single-colony Al-CuA12 eutectic composite ingot, 2 in. in diam and 12 in. long. The specirrzens were cut such that the platelets were oriented parallel, 45 deg, and perpendicular to the compression direction. Since the ingot was of eutectic composition, The aluminum-rich matrix could dissolve 5. 7 wt pct Cu in solid solution, and therefore could be strengthened by precipitation hardening. Specimens were tested at room temperature and elevated temperatures in the unidirectionally solidified, solution-treated, and solution-treated plus aged conditions. The results were compared with those for the conventionally cast and extruded specimens. For the controlled material, the highest strengths were obtained with platelets oriented parallel to the compression axis. In the unidirectionally solidified condition, 0.2 pct offset yield strength was 32,000 psi; however, this was increased to 59,000 psi by solution treatment, and further increased to 90,500 psi by solution treatment and aging. The attainment of high compressive strengths in the Al-CuAl2 eutectic composites was interpreted in terms of the buckling of elastic CuAl2 platelets in the plastically deformed a aluminum matrix. SINCE the discovery of high-strength whiskers,' scientists and engineers have made significant progress toward incorporating these whiskers into metallic matrices, forming composites for basic studies and structural application. The general procedure is to produce the whiskers first and then to bind them together with a ductile matrix. The production of whisker-reinforced composites requires tedious handling techniques,, particularly when it is desired to align the whiskers unidirectionally. Furthermore, the interfacial bond between the whisker and the matrix is frequently poor3 so that the resulting composite has strengths lower than expected. These disadvantages are generally true for any metallic composite produced by physically mixing the components. It is possible to eliminate these shortcomings by growing whiskers directly in the matrix material by eutectic solidification.4-8 In eutectic solidification, the matrix phase and a whisker phase are grown approximately simultaneously from a liquid of the same overall composition at the eutectic temperature. If the solidification process is controlled by varying the freezing rate, the temperature gradient, and the impurity content, platelike or filamentlike whiskers are produced parallel to the growth direction. The morphology of the grown-in reinforcement, i.e.. plates or rods, generally depends on the volume fraction9 of the dispersed phase present in the eutectic mixture. Since the unidirectional eutectic solidification is a one-step process, i.e., the liquid-solid transformation process, an excellent interfacial bond between the matrix and whisker is obtained. An additional advantage is that no special handling technique for whiskers is needed. In recent years, many investigators10-13 have studied the effects of growth variables on the micromorpholo-gies of binary eutectic alloys produced by controlled solidification. The study of their mechanical properties was initiated by Kraft and coworkers14-16 who found that the strength of cast A1-CuA12 eutectic alloy can be increased threefold by unidirectional solidification. In the A1-AL3Ni system, a strength of 50,000 lb per sq in, was reported for the unidirectionally solidified eutectic alloy, a value five times higher than for conventionally cast material. Thus, the unidirectionally solidified eutectics can be used as fiber-reinforced composite materials. In this paper, we shall first use an equation17 as a guide for the production of eutectic composites in general and the Al-33 wt pct Cu eutectic in particular. Experimental data supporting the theoretical prediction are given. Second, the compressive properties of the grown A1-33 wt pct Cu eutectic were thoroughly investigated in terms of platelet orientations, thermo-mechanical treatment, and temperature. The experimental data are interpreted in terms of a buckling model of fibers in elastic fiber-plastic matrix metallic composites. EXPERIMENTAL PROCEDURE Crystal Growth. The following experimental procedure was adopted for the production of controlled microstructures in the A1-33 wt pct Cu eutectic alloy. The controlled solidification was accomplished with a movable resistance-wound radiation furnace. Fig. 1 is a schematic drawing of the solidification apparatus. A water-cooled chiller was placed into a degassed high-purity graphite crucible containing the charge. Rubber stoppers wrapped with aluminum foil were used to seal both ends of the quartz tube through which a dried argon atmosphere was passed under a slight positive pressure. At both ends of the quartz tube, radiation shields were used to minimize heat loss. The quartz tube was held in place by two steel clamps and the furnace was drawn vertically by means of a steel cable against the steel truss which permits the furnace to move without touching the tube. The drive mechanism consisted of two pulleys, a counter weight.

Jan 1, 1969

By E. C. Tveter, R. B. Tippin

The separation of minerals by heavy liquids is a standard laboratory technique which goes back at least 50 years, but commercially economic application of this principal to ore concenfration has been prevented by problems of liquid recovery. Recent investigations which demonstrate the different types of liquid-solid systems on various ores using the two major heavy liquids - methylene bromide and tetra-bromoelhane — are discussed in this article. As a result of these studies, over-all liquid recovery, and especially desorption of heavy liquid from the mineral surface, was improved by the use of surfactants as well as both thermal and mechanical energy. The examples given in the article indicate that heavy liquids which should find major commercial use in ore concentration are now available. The sink-float process using a heavy liquid medium has long been recognized as a nearly perfect method of mineral separation based on the differences in density of the minerals. The use of heavy liquid separation (HLS) offers the potential of an ore dressing method that provides the maximum possible natural concentrate grade and high recovery. In addi- tion the process requires no water, causes no waste disposal problems, and is extremely simple — the crushed ore is merely introduced into a liquid whose density is between that of the minerals to be separated. The minerals lighter than the liquid float while those heavier than the liquid sink. As such, HLS has become a standard laboratory tool but major commercial application has been prevented by the requirement for complete recovery of the heavy liquid, imposed by economics and materials handling hazards. Investigations, both in the United States and abroad, have shown that improved liquid stability as well as improved chemical engineering techniques brighten the future for HLS in ore dressing. The available commercial heavy liquids suitable for mineral separation cost from $2.00 to $20.00 per gallon1 and on this basis alone their complete recovery is economically desirable. Possibly of even greater importance is the fact that any residual heavy liquid remaining on the products could create a serious toxicity hazard. Consequently, to make the process commercially attractive requires (1) essentially complete removal of the liquid from the ore products and (2) optimum recovery of the liquid for reuse. Until recently these two stipulations have remained as obstacles but laboratory and pilot plant research now in progress suggests that these may soon be overcome. Various heavy liquid recovery systems have been proposed to meet these requirements and might be classified into one or more of the following three general classes: Solvent Wash (Fig. 1): The dissolution of the heavy liquid from the ore with a less expensive solvent,

Jan 1, 1969

Jan 1, 1969

By G. S. Coe, G. F. Bolling

The columnar-to-equiaxed transition (CET) has often been studied as a function of concentration, C, temperature gradient in the melt, G, and rate of solidification, R. Although it may not be immediately obvious it is sure that the CET, expressed as some ratio G/R necessary to suppress equiaxed nucleation for a given C,' cannot be a single-valued function of C. This restriction which is ignored in theoretical presentations is most trivially illustrated by the following simple reasoning. An ordinary casting is an unconstrained system where the thermal conditions change continuously with progressive solidification, and thus where the ratio G/R decreases from the outset. A CET occurring early in a casting (much equiaxed material) must then mean a higher value of G/R at transition, in comparison with the late CET which implies a more columnar ingot. Therefore, when we choose to experiment under constant superheat for all alloys across the simplest binary, and we find an inversion in the amount of equiaxed material, we shall find two values of C satisfying the G/R condition. However, in addition to this simple instance, the early experiments of ~orthcott' seem to show that the amount of equiaxed material in cast ingots may be a multivalued function of composition in a given binary system. In the present investigation, the CET has been examined in Pb-Sb, Pb-Ag, Pb-Sn, and Sn-Pb under several types of casting conditions. First, we have used the "bidirectional" ingot section Simulation;~ and we have used .'i~z situ" ingot solidification where a hot mold already filled with liquid is chilled so that there is no disturbance provoked by pouring. Differences in method are trivial to our purpose except for the fact that certain variations are more simply observed by one technique than by the other. Second, we have varied the mode of superheating from the simple extreme of casting all alloys from the same temperature regardless of composition to the careful casting at a standard superheat, calculated with respect to the alloy liquidus. Third, we have made provisions for decanting and interface observation, so that some "castings" were not completed. The results obtained with Pb-Sb are exemplary; some of these are shown in Fig. 1 along with explanatory captions. At 9 to 10 at. pct Sb, and thus above the solid-solubility limit Cs = 5.8 at. pct Sb and yet below the eutectic concentration Ceu = 17.5 at. pct Sb, there is a persistent anomaly in all the variations. Measurement was easy enough and standard enough so that we may forgo discussion of either method or possible error, in view of the forceful self-consistency shown by experiment. Solute distributions were measured along the bidirectional ingots in order to determine if a solute buildup had occurred at the CET. No anomalous changes in concentration were observed along the bars at either side of the solute anomaly of 10 at. pct Sb. The microstructures of the ingots were also examined across the range of composition investigated. At concentrations less than 9 at. pct Sb the micro- and macrostructures were typical of the cellular-dendritic growth usually reported for the columnar zone. Above the anomaly, both the columnar grain size and the amount of primary phase decreased. This microstruc-tural observation can be correlated with observations made of decanted interfaces. Below 9 at. pct Sb, the interface reveals the "normal" columnar dendritic structure; however above the anomalous concentration range, preferential growth of certain dendrites appears to form a "super dendrite" pattern. In Fig. 2 a microstructural view of the etched '(super dendrites'' shows their constitution both in terms of relative phase proportion and in terms of the ordinary smaller dendrites.

Jan 1, 1969