By Debbie Marshall

Nickel and cobalt in lateritic ores can be extracted by either a hydrometallurgical or a pyrometallurgical route. The high-iron limonitic fraction of a deposit is best processed' hydrometallurgically while the magnesium-rich transitional and saprolitic fractions are more suited for pyrometallurgical processing. During hydrometallurgical processing, it may be attractive, for economic reasons, to blend the limonitic component with transitional and saprolitic ores, which contain higher nickel levels. However, blending increases the concentration of magnesium in the feed, leading to increased acid demands. The decision on how much ore to process then becomes an economic one. Ore samples with different magnesium contents were prepared for the leach test program by blending limonitic and transitional ores. The ore samples were slurried in seawater and tested in the Falconbridge Hydrometallurgical Pilot Plant. As expected, acid consumption increased with increasing magnesium content of the ore. For target extractions of 95% nickel and 92% cobalt, the required residual free acid concentration increased from 30 g/L at 1.7% magnesium to 50 g/L at 2.7% magnesium. When the magnesium content was raised to 3.8% and 4.6% in subsequent pilot plant testing, the final free acid requirements did not increase beyond what was observed at 2.7% magnesium. Thus, the cut-off ore composition to maximize nickel units and minimize acid requirements is between 1.7- 2.7% magnesium. Keywords: high pressure acid leaching, laterites, magnesium

Jan 1, 2004

By V. Montenegro

Smelting of copper concentrates in Teniente Converter produces highly oxidized slag, containing from 4 to 10 % Cu and from 15 to 25 % of Fe304. Copper recovery requires magnetite reduction at a level of 5%, determining the degree of cuprous oxide co-reduction and the liberation of copper matte inclusions. The rate of slag reduction is controlled by the mass transfer to the reaction interface. Slag stirring affects the rate of reduction and enhances coalescence of mechanically entrained copper matte inclusions. Slag reduction and sedimentation in the AC electric furnace is a commonly used method of slag cleaning. Utilization of DC electric furnace creates beneficial conditions introducing slag electrolysis additionally to chemical reductions with carbon of coke and electrodes. Application of external magnetic field, interacting with a direct current in an electric furnace, induces magnetohydrodynamic phenomena, such as intensive stirring and electromagnetic buoyancy force acting on inclusions. Laboratory scale research in simulated DC electric furnace with a superimposed magnetic field showed a significant acceleration of the rate of slag reduction and copper removal. Continuous measurement of gas flow and composition allowed for determination of the reduction rate along the time. Application of external magnetic field in the reduction of the industrial slag in a crucible simulated DC electric furnace results such as the increase of the reduction rate from 2 to 3 times, compared with the identical conditions in the AC electric furnace. Interaction of non- homogeneous electric field with crossed permanent magnetic field induces vigorous slag stirring, enhance mass transfer and accelerate the rate of the slag reduction. Additional participations of the slag electrolysis in the magnetite and cuprous oxide reduction as well as the acceleration of the settling of the inclusions by the electromagnetic buoyancy force affect the slag cleaning intensification.

Jan 1, 2003

By V. Montenegro

Smelting of copper concentrates in Teniente Converter produces highly oxidized slag, containing from 4 to 10 % Cu and from 15 to 25 % of Fe304. Copper recovery requires magnetite reduction at a level of 5%, determining the degree of cuprous oxide co-reduction and the liberation of copper matte inclusions. The rate of slag reduction is controlled by the mass transfer to the reaction interface. Slag stirring affects the rate of reduction and enhances coalescence of mechanically entrained copper matte inclusions. Slag reduction and sedimentation in the AC electric furnace is a commonly used method of slag cleaning. Utilization of DC electric furnace creates beneficial conditions introducing slag electrolysis additionally to chemical reductions with carbon of coke and electrodes. Application of external magnetic field, interacting with a direct current in an electric furnace, induces magnetohydrodynamic phenomena, such as intensive stirring and electromagnetic buoyancy force acting on inclusions. Laboratory scale research in simulated DC electric furnace with a superimposed magnetic field showed a significant acceleration of the rate of slag reduction and copper removal. Continuous measurement of gas flow and composition allowed for determination of the reduction rate along the time. Application of external magnetic field in the reduction of the industrial slag in a crucible simulated DC electric furnace results such as the increase of the reduction rate from 2 to 3 times, compared with the identical conditions in the AC electric furnace. Interaction of non-homogeneous electric field with crossed permanent magnetic field induces vigorous slag stirring, enhance mass transfer and accelerate the rate of the slag reduction. Additional participations of the slag electrolysis in the magnetite and cuprous oxide reduction as well as the acceleration of the settling of the inclusions by the electromagnetic buoyancy force affect the slag cleaning intensification.

Jan 1, 2003

By Nam-Il Um

Bottom ash contains several ferrous materials (ferrous metals, Fe3O4, Fe2O3, FeS, etc.). In particular, ferrous metals contain heavy metal because Ni and Cr are chemically attracted to iron. Likewise, Cu is used to coat Ni and Cr metals as polish or to prevent corrosion. In this study, an Fe3O4-Fe2O3 double layer (similar to pure Fe) was found to have been formed in ferrous metal during air-annealing in an incinerator (1000°C). A strong thermal shock such as one that occurs during the water-cooling of bottom ash results in the breakdown of this oxidation layer, facilitating the degradation of ferrous metals and formation of corrosion products. Therefore, Fe-ion (heavy metal) oxides may be formed on ferrous metals and may be separated from bottom ash via magnetic separation. This study sought to investigate the separation ratio of heavy metals as magnetic separation and mineralogical formation of Fe-ion (heavy metal).

Jan 1, 2006

By Chao Zhang, Jian Guo, Chaoquan Yao, Leige Xia, Xinyu Li, Jianliang Zhang

In this research, analytical reagents were used for the sintering experiments. And the sinters were using X-ray diffraction, scanning electron microscope and mineralogical microscope analysis to study the effect mechanism of manganese on the silico-ferrite of calcium and aluminum (SFCA) bonding phase formation during the sintering process. The results indicated that the increasing content of manganese would greatly reduce the content of SFCA, and promote the formation of calcium aluminum silicate and the amount of pores and cracks. The existence of manganese inhibited the silicon form into the SFCA and a great deal of Fe2O3 was participated in the crystal transition to Fe3O4. When the ratio of the added manganese was less than 3% in the mixing, the calcium ferrite was in substantially interleaving corrosion with hematite and magnetite. Both the porosity and silicate glass phase content were low simultaneously, which contributed to the sintering production.

Jan 1, 2015

By R. W. Smith

The flotation response and electrokinetic behavior of Chlorella vulgaris and Chlamydomonas sp . when using dodecylamine hydrochloride as collector were studied in the absence and presence of Pb(I1). Also, an electron microscopy study was made of the algae after Pb accumulation. The flotation behavior of the organisms after Pb accumulation appears at least partially related to the location of the abstracted Pb onto or into the organisms.

Jan 1, 1991

By Donna Post Guillen

"Cyclopentane, a flammable hydrocarbon, is being considered as a working fluid for waste heat recovery applications using Organic Rankine Cycles with Direct Evaporators. A postulated failure mode consisting of a pinhole leak in a heat exchanger tube raises safety concerns due to autoignition of the working fluid. Experiments were conducted to determine the ignition delay time (IDT) of cyclopentane using an Ignition Quality Test™ (IQT™) device. Two sets of experiments were conducted per ASTM D6890 (with exception to charge pressure and temperature) to determine ignition delay of the fuel at atmospheric pressure for standard air (-20.95% oxygen) and vitiated air (13.3% oxygen) at a temperature of 803 K. Operation of the IQT device at a much lower pressure (1 bar) than normal operation (21.4 bar) with a standard injector led to very rich conditions and wetting of the stainless steel chamber walls. Catalytic effects are postulated to produce the small IDTs observed. Experiments were repeated with a modified injector to prevent wall wetting, resulting in average IDTs that are substantially longer.IntroductionCyclopentane is being considered for use as a working fluid in a Direct Evaporator of an Organic Rankine Cycle (ORC). In this configuration, the heat exchanger is placed directly in the flow of the hot exhaust gas, rather than using a secondary heat transfer loop to isolate the flammable working fluid from the heat source. This configuration offers the advantages of approximately 15% lower cost and improved efficiency over a standard ORC. However, placing a heat exchanger operating with a flammable hydrocarbon in the hot exhaust gas stream presents potential safety risks. If a pinhole leak were to occur in the heat exchanger, working fluid could leak into the hot exhaust stream. Gas turbine exhaust is provided to the Direct Evaporator at a temperature of approximately 803 K, whereas the autoignition temperature of cyclopentane is 634 K (Gallant and Yaws, 1993). Autoignition of the working fluid has been identified as the key risk for this type of system.Autoignition occurs when sufficient self-heating by chemical reactions takes place to accelerate reaction rates to produce full-scale combustion. This is in contrast to forced ignition, in which an external source (e.g., spark) is employed to initiate the combustion process. For combustion to occur, the fuel to oxidizer concentration must be between the lower (lean) and upper (rich) flammable limits. The reaction rate depends on the species concentration of the fuel and oxidant, the local temperature and pressure. Ignition processes are comprised of steps that take a fmite amount of time. This latent period prior to the start of combustion is referred to as ignition delay time (IDT)."

Jan 1, 2012

By W. G. Davenport

Chapter 11 determined the combinations of industrial oxygen, oil and blast preheat that will steadily produce 65% Cu matte from pure chalcopyrite concentrate. It showed that the . combinations are described by a flat plane. It also showed that the minimum energy requirement for making 65% Cu matte occurs with maximum oxygen enrichment, zero oil and zero blast preheat. This chapter examines the, effect of matte grade on industrial oxygen, oil and preheat requirements.

Jan 1, 2001

By Shaik Jeelani, Mahesh Hosur, Esperidiana A. B. Moura, Rejane D. Campos, Emilia S. M. Seo, Kerry Kirwan, Francisco R. V. Díaz, Maria Sotenko

The use of natural fibers with polymeric resins has spread rapidly. In order to improve the mechanical properties of material, in this work, two variables were used: mercerization and electron beam irradiation. This paper describes the preparation and characterization of biocomposites that were prepared in two different routes using green high density polyethylene (HDPE) and Brazil nut pod fiber (BNPF): the first was to irradiate the composite with 150 kGy and the second was to irradiate the matrix with 15 kGy followed by composite preparation. In both cases mercerized and non-mercerized fibers were used. The irradiation process was carried out using a 1.5 MeV electron beam accelerator, at room temperature and in the presence of air. The material was characterized to evaluate the effect of treatment on mechanical properties of material.

Jan 1, 2015

By Cheng Pan, Xuewei Lv, Guibao Qiu, Chenguang Bai, Meilong Hu

"Physic-chemical properties of slag at high temperature play an important role in the pyrometallurgical process of production of ferronickel alloy. It determines the operation efficiency, metal recovery ratio, energy consumption and the distribution of elements like S and P between the slag and metals. In the present work, the effect of MgO content in the slag on melting features and viscosity of the slag was investigated. The MgO content in the SiO2-CaO-MgO-Al2O3 -FeO in the quinary slag system varied from 14.5% to 22.5%. The results shown that all slag samples begin to softening at the same temperature, the softening temperature, melting temperature, flowing temperature decrease with the increase of MgO content when the MgO content is in range of 14.5 and 20.5 pct mass, and when MgO content up to 22.5 percent, the temperatures increase sharply. Besides the inflection point temperature of viscosity-temperature curve increase with the increase of MgO when the MgO content is in range 16 and 22.5 pct mass.IntroductionNickel is very important to modern society, without it, we would not be able to share many things in our daily life, such as airplanes, computers and many stainless steel appliances in our homes and workplaces1.. It is the essential element of the stainless steel making, and about 65% of the nickel consumed in the world is used to make stainless steel2., so with the increase of stainless steel, the nickel production and demand has continued to increase3.Nickel is produced from two distinct ore types: nickel sulfide deposits and oxide nickel laterite deposits. The great majority of world’s known nickel resources are contained in laterite deposits3.. The laterite ores are normal classified into two groups: the high-iron laterite ore and high-magnesia laterite ore1. Typical composition of high-magnesia laterite ore is in the range 1-3%, and these ores are suitable for pyrometallurgical process to produce ferronickel4."

Jan 1, 2012

By Shengli Wu, Juan Zhu, Wei Huang, Xinliang Liu, Kaiping Du, Kaifa Zhang

Based on the furnace burden of high content of Al2O3, the process of softening and melting and the characteristic of primary slag were studied with the increase of MgO content in the sinter and adding some MgO into the pellet. The results showed that the content of MgO in the primary slag increased with the increase of MgO in the sinter and pellet. Meanwhile, the permeability of the furnace burden was improved because of low viscosity of high MgO primary slag. Compared with the increase of MgO content in the sinter, the increase of MgO content in the pellet can improved the softening and melting characteristic of the comprehensive furnace burden more effectively. More Mg-bearing pellet should be chosen in the comprehensive furnace burden for the purpose of improvement the fluidity of primary slag and the permeability of the furnace burden in the burden of high Al2O3 content.

Jan 1, 2015

By Han Yihua, Zhang Caijun, Zhu Liguang, Zhang Qingjun, Wang Shuoming, Wang Yan

An industrial test on 210 t converter-LF-CC production line on high heat input welding shipbuilding structure steel DH36 has been taken in a factory in north China, the effect of adding microalloy elements V and Mg on casting billet microstructure has been researched. It was found that when the composition of V was between 0.03 and 0.05% and the composition of Mg was between 0.002 and 0.005%, a large number of acicular ferrite precipitate in austenitic crystal in as-cast structure and cross into a net structure. The inclusions size which induced intra-granular ferrite are mainly less than 4 lm, especially those between 2 and 3 lm account for 50.80%, in these inclusions the composite inclusions mixed with Mg accounted for more than 60%.

Mar 1, 2017

By Hüseyin Aydin

TWIP (Twinning-Induced Plasticity) steels have exceptionally good combinations of strength, ductility and damage tolerance which satisfy the recent requirements of automotive industries. Firstly, TWIP has the most beneficial effect on the work-hardening. It is believed that deformation twins increase the work-hardening rate by acting as obstacles against gliding dislocations. Moreover, TWIP steels have low to intermediate stacking fault energy and hence undergo extensive mechanical twinning during deformation, which in turn leads a good combination of both strength and ductility. To explain the mechanical characteristics and the mechanical behavior of the TWIP steels, we have been made some investigations and experiments that show the effects of microalloying elements and deformation mechanisms. In this study, three different compositions of TWIP steels have been produced. The microstructure and mechanical properties are characterized by using optical, electron microscopy and mechanical tests.

Jan 1, 2009

By Wen-long Zhan, Zhe Ning, Jun-hong Zhang, Ji-hui Liu, Zhi-jun He, Qing-hai Pang

The influence of microwave irradiation and ultrasonic vibration on granularity of 0.074 mm pulverized coal was investigated in this research. It is indicated in the results that the granularity of coal decreased after microwave treatment, which led to the increased in specific area of pulverized coal in combustion reaction and consequently optimized the kinetic condition of combustion reaction. Higher ultrasonic power may lead to better performance of PC in combustion. The optimum condition for ultrasonic treatment is 10 min under 350 W microwave power.

Mar 1, 2017

By He Zhi-jun, Ning Zhe, Pang Qing-hai, Zhang Jun-hong, Zhan Wen-long

In this study, Raman spectroscopy was utilized to investigate the evolution of char structure in pulverized coal (PC) during microwave irradiation. The results indicated that though microwave treatment was carried out at low powers of 132W or 264W, significant variation in char structure was still observed. Char structure turned out to be more irregular firstly under microwave irradiation. However, char structure of superior regularity was obtained with the extension of irradiation time. It can be conclude that short time microwave treatment may facilitate the chemical activity of coal, while long time microwave irradiation on PC may deteriorate its combustion or pyrolysis property.

Jan 1, 2016

By He Zhi-jun, Ning Zhe, Pang Qing-hai, Zhang Jun-hong, Zhan Wen-long

The effect of microwave irradiation on grinding property of coal was studied by using Hardgrove grindability index tester. Superior grindability of coal was obtained to varying extent after microwave irradiation treatment. The variation in microstructure of pulverized coal during microwave irradiation was observed by utilizing scanning electronic microscope (SEM). The results indicated that the different microwave absorbance of minerals and carbon matrix led to cracks on their interface, by which coal particles were further pulverized and therefore the granularity of coal powder was reduced. Due to the different formation process of various coals, bituminite and anthracite are very different in physical and chemical properties. According to the content of coal pulverization, it can found that microwave irradiation has a stronger pulverizing effect on bituminite in comparison to anthracite.

Jan 1, 2016

By Yang Guangqing, Shao Jiugang, Zhang Jianliang, Wan Dan, Fu Yuandi, Guo Hongwei

"Resource of metallurgical coke is becoming scarce, and although coke can be partially replaced by pulverized coal injection, there are many restrictions for further increase in coal ratio. Mixed charge of ore and lump coal from top to replace more coke was studied in this paper. Softening-melting property of the burden was affected by charge of lump coal. Softening-melting properties of mixed charge of ore and coke, mixed charge of ore and lump coal were tested respectively. Results show: the property of the burden mixed with coke is superior to the burden mixed with lump coal; lump coal would not deteriorate softening-melting property of the burden and some of them can even improve softening-melting property of the burden. Top charge of lump coal would not deteriorate softening-melting process, and this should be a new way to increase coal consumption to decrease coke rate.IntroductionThe blast furnace is still the predominant process for the reduction of iron ore and will probably remain so for the next decades. Metallurgical coke is becoming scarce and expensive, so the cost of hot metal can be decreased by reducing the consumption of metallurgical coke[l]. Coke can be partially replaced by pulverized coal injection, currently the highest rate of pulverized coal reached 266kg/tHM, most of blast furnace PCR is about 150kg/tHM, and it is very difficult to further increase of PCR. Nut coke is charged into blast furnace mixed with iron ore, not only for improving utilization of metallurgical coke, but also for lowering the coke rate. Presently the majority of blast furnaces in the world use nut coke although its amount is very different: from 10-20 to 70--100 kg/tHM and more[2-4].The effect ofnut coke in blast furnace is extensively researched, and the main conclusions recommend: to improve gas permeability of cohesive layer in blast furnace, to promote reduction of iron burden, protect metallurgical coke from the solution in the shaft due to higher reactivity of nut coke. There is no special requirement for the strength of nut coke[5-8]. Nut coke is also used for sintering fuel, which may lead to the shortage of the nut coke charging into blast furnace. So lump coal mixed with iron ore is considered to be charged into the blast furnace, not only to reduce the cost of grinding coal, but also to increase the use amount of coal."

Jan 1, 2013

By Xin-liang Gao, Qing Li, Gui-qin Fu, Duo Jin, Miao-yong Zhu

"Optical microscope together with alternative wet-dry cyclic accelerated corrosion tests and XRD, SEM were employed on bridge weathering steel samples with different Mn and Ni contents which were vacuum induction melted and rolled to study their effects on the microstructure and rust layer evolution in er' containing condition. The results show that the microstructure is mainly ferrite and pearlite when Mn and Ni contents are 0.75 %, 0.42 %, respectively. Both the increase of Mn and Ni contents will make pearlite disappear while granular bainite appear, meanwhile the grain size decreases. With the increase of Mn content, the corrosion rate decreases in the initial stage, but the effect becomes little in the later stage. The increase of Ni not only improves the corrosion resistance of steel base at the initial stage but also hinders the tendency of further corrosion. As Mn content increases, a-FeOOH contents in rust layer decreases. With increase of Ni content, the content of a-FeOOH in the rust increases while that ofy-FeOOH decreases.IntroductionWeathering steels had been ~radually applied in manufacture of bridges owing to reducing the corrosion rate remarkably [I- l .Good weldability was needed for high performance bridge weathering steels. Since carbon was thought to be bad for weldability, low carbon content steel was adopted and Mn was added to amend the mechanical strength loss. Some scholars[6, 7l believed that Mn was beneficial for increasing corrosion resistance performance of the steel in marine atmospheric environment. Some scholars [S, 9l thought that Mn had little effect on corrosion resistance in marine atmospheric environment. Presently, the effect of Mn on bridge weathering steel in marine atmospheric environment still remained poorly understood. Ni was considered to be beneficial for increasing corrosion resistance performance in marine atmospheric environment [JO-l4l However, the high cost limited its application range. What would bring to the rust and corrosion by decreasing Ni content needed further research.Most researchers assumed that microstructures only affected the corrosion behavior of bare steel. But the study of Guo et al. P5l showed that the homogenous microstructures were beneficial for the corrosion resistance of steels. The effect of Mn, Ni content change on microstructure and microstructure on corrosion still remained poorly understood. In the present work, the effect of Mn and Ni on the microstructures of steel matrix, as well as the microstructures on the rust and corrosion was investigated."

Jan 1, 2014

By Mei-le He, Min Chen, Xiang Shen, Lei Xu, Lei Liu, Nan Wang, Xue-liang Yin

In the current study, Al2O3-MgO-CaO refractories were prepared at 1400-1600 by the addition of MnO micro-powders, and the effect of MnO addition on densification behavior of the refractory was discussed. The results showed that the doped MnO dissolved to MgAl2O4 phase, and promoted the growth of MgAl2O4 grains by the formation of MgAl2O4 solid solution. As a result, the dense microstructure was obtained, with the apparent porosity decreased from 19.2% to 5.4% and the bulk density increased from 2.78g/cm3 to 3.15g/cm3 after firing at 1600 for 2h by the addition of 4% MnO. In addition, a texture microstructure was observed, which is considered to be favorable to improve mechanical properties and the service life of Al2O3-MgO-CaO system refractories.

Jan 1, 2016

By Juan Hernández Ávila

This work studies the Molybdenum effect on the microestructure, mechanical properties of an as-cast ductile iron. For this study five ductile irons with different amounts of Molybdenum each were made in an induction furnace. In this material nodule count and nodularity is affected by the Molybdenum additions; The iron´s matrix, nodules and the phase were analyzed using scanning electron microscopy detecting Molybdenum only in the matrix. Mechanical properties such as hardness, microhardness, tensile strength and yield strength show increments as the Molybdenum amount is increased. In the same way, ferrite and pearlite phases display a variation in their percentage as the contents of the alloy element increase. This element has a marked influence on the pearlite interlaminar spacing. From the obtained results we conclude that Molybdenum in these quantities dissolves in solid ferrite solution during the solidification process, improving the material´s mechanical properties.

Jan 1, 2009