By Daniel Hoffman, Katerina Aifantis, Ibrahim Miskioglu, Jaroslaw Drelich

"A new method to determine the elastic modulus of a material using the atomic force microscope (AFM) has been proposed by Tang et al. (Nanotechnology 2008, 19, 495713). This method models the cantilever and the sample as two springs in a series. The ratio of the cantilever spring constant (k) to diameter of the tip (2a) is treated in the model as one parameter (a=k/2a). The value of a, along with the cantilever sensitivity, are determined on two reference samples with known mechanical properties and then used to find the elastic modulus of an unknown sample. To determine the reliability and accuracy of this technique it was tested on several polymers. Traditional depth-sensing nanoindentation was preformed for comparison. Using both methods, the elastic modulus of the polymers tested was calculated. The elastic modulus values from the AFM were within ±(5-20)% of the nanoindenter results.IntroductionThe atomic force microscope (AFM) has proven to be a useful tool for characterizing materials on the micro- to nano-scale. The most common use of AFM is to image and measure the topography of the sample surface, but AFM has also been used to characterize the mechanical properties of materials [1-3]. With AFM's ability to scan the sample surface, features of interest can be found and indented. It provides an advantage over traditional nanoindenters that use optical microscopes and thus cannot resolve nano-scale features. This makes AFM a useful tool for characterizing materials on the nano-scale."

Jan 1, 2011

By David E. Hardt

"One of the critical variables to be controlled during arc welding is the size or geometry of the weld pool. The measurement of pool geometry has become an increasingly important problem with the advance of welding automation and control, and this paper addresses that problem. The basic concept of pool size estimation via measurement of pool dynamics is presented. The theory underlying this concept is discussed and is followed by a review of the current work in this area. It is concluded that pool dynamics can be characterized by natural frequencies of oscillation, for stationary welds, and that these can be measured by appropriate signal processing performed on the arc voltage. However, it appears that only full penetration welds show a strong correlation between weld size and natural frequency. Also, the extension of these results to the realistic case of moving welds has yet to be considered in detail. Nonetheless, this method of in-process measurement for real-time weld process control is still quite attractive where applicable since it can be accomplished simply by modifying the arc current schedule and by signal processing of the arc voltage.INTRODUCTUIONThe study of welding process control has been dominated by research into methods of in processing sensing of the weld pool geometry. While it has been shown feasible to measure the topside pool geometry using video methods [1,2], the penetration or backside bead width have remained elusive quantities. This is particularly true if a topside sensor location is required.The concept of using weld pool motion as a pool geometry sensing method was proposed by Hardt et al. [3] and later demonstrated by Hardt and Zacksenhouse [5] and Richardson and Renwick [6]. The concept is based on the fluid dynamics of a pool constrained by a solid container and by significant surface tension forces (i.e. a small shallow pool, not a ""pond"" or ""lake""). Such a pool, if subjected to external forces, will exhibit a surface motion is a function of that force, the properties of the fluid, the surface tension, and the shape of the container. Thus, if this motion can be excited and measured, and the relationship to the pool geometry determined, a means of sensing pool shape will exist."

Jan 1, 1986

By Aly M. Abdel-Rehim

The present work deals with a study of the mechanical activation of processing of Egyptian monazite by its simultaneous ball-milling and pressure leaching in order to improve the recovery of thorium and lanthanides from monazite. Experiments of simultaneous ball-milling and alkaline leaching of monazite contrary to autoclave leaching were carried out in stainless steel ball-mills of cylindrical shape under different conditions of temperature, pressure, time and alkali amount and strength. The ball-mills were heated and mechanically rotated in an electric furnace by means of roll mechanism. The effective rotation speed was fixed at 130 rpm in all tests. The charge of steel balls of different diameters was equivalent to 45% of the total mill volume. Monazite was charged in ball-mill without preliminary grinding. It is found that high rate of monazite leaching by ball-milling leaching method is achieved at lower temperature, shorter time and lower expense of alkali than in autoclaves. The results obtained show that complete recovery of thorium and lanthanides from monazite (99.8%) by simultaneous ball milling and alkaline leaching is attained at 140°C within 2 h. It is concluded that processing of monazite by its simultaneous ball-milling and leaching is mechanically activated and accelerated as a result of grinding action of steel balls that caused the continuous removal of the hydroxide product from reacting particle surfaces. This leads to the exposing of fresh and activated monazite particles surfaces to alkali leach solution and consequently the acceleration of the reaction of monazite processing.

Jan 1, 2006

By Mohamed Y. Bakr, Aly M. Abdel-Rehim

The present work is related with mechanical activation of processing of Egyptian wolframite by simultaneous ball-milling and pressure alkaline leaching, to improve the recovery of tungsten from wolframite. The results show a total recovery of tungsten from wolframite (97.8- 98.7%) by simultaneous ball–milling and alkaline leaching at temperature 175-200oC. It is concluded that processing of wolframite by simultaneous ball- milling and leaching is mechanically activated and accelerated as a result of the grinding action of steel balls that caused the immediate rupture by continuous removing the product layer of the reaction ( sodium tungstate and iron and manganese hydroxides ) from reacting particle surfaces. This leads to the exposing of fresh and activated wolframite particle surfaces to alkaline leach solution and consequently the acceleration of the reaction of wolframite leaching .The results of the kinetic study 0f alkaline processing of wolframite and its mechanical activation show that the system is under kinetic control.

Jan 1, 2015

By Dmitri Goljandin, Jaan Kers, Xiangjun Zuo, Lifeng Zhang, Priidu Peetsalu

"In this paper, the mechanical milling of the electronic wastes was carried out. The metal parts and plastic parts were roughly separated. The final plastic powder size could be as small as ~100 µm. Then the pyrometallurgical recycling Printed Circuit Boards (PCB) was executed. The mechanisms of thermal degradation and combustion are investigated using TG/DTA and MS. Some chemical powders, such as Na2CO3, NaHCO3, NaOH and CaCO3 are used to control the exhausted toxic gas such as Br2. Introduction Waste electric and electronic equipment (WEEE), or electronic wastes (E-wastes), has been taken into consideration not only by the government but also by the public due to their hazardous material components [1-3]. From the point of material composition, electronic wastes can be defined as a mixture of various metals, particularly copper, aluminum, and steel, attached to, covered with, or mixed with various types of plastics and ceramics [4]. Precious metals have a wide application in the manufacture of electronic appliances, serving as contact materials due to their high chemical stability and their good conducting properties. Platinum group metals are used among other things in switching contacts (relays, switches) or as sensors to ascertain the electrical measurand as a function of the temperature [5]. Table 1 [6] gives examples of the metal composition of different electronic scraps from literatures. Additionally, non-ferrous metals and precious metals content have gradually decreased in concentration in scraps. The value distributions for different electronic scrap samples are shown in Table 2 [6], where the metal price data are from London Metal Exchange (LME) (Octoebr 2007). It can be seen that for cell phones, calculators, and printed circuit board scraps, the precious metals make up more than 70% of the value, for TV boards and the DVD player they still contribute to about 40%. This indicates that the major economic driver for recycling of electronic waste in industry is from the recovery of precious metals. Behind the precious metals come copper and zinc, while Al, Pb, and Fe are less value. Recycling of electronic waste is an important subject not only from the point of waste treatment but also from the recovery aspect of valuable materials."

Jan 1, 2008

By Sergio N. Monteiro

Natural lignocellulosic fibers are successfully replacing synthetic fibers in many engineering applications. In addition to well-known conventional lignocellulosic fibers, others with promising properties are now being considered. The present work investigated the mechanical and structural characteristics of a relatively high strength fiber, curaua (Ananas erectifolius) from the Amazon region of Brazil. The results obtained from tensile tests confirmed the superior strength while scanning electron microscopy (SEM) analysis displayed features that justify the possibility of using the curaua fiber as an effective reinforcement for polymeric composites.

Jan 1, 2006

By Helvio Pessanha Guimarães Santafé Jr.

The coir fiber extracted from the husk of the coconut has been extensively used as polymer composite reinforcement in a variety of industrial applications ranging from civil construction to automobile seat cushions. The hydrophilic coir fiber does not act as an effective reinforcement owing to its low interfacial strength with hydrophobic polymers. As a consequence, coir fiber composites display relatively low mechanical strength. The objective of this work was to investigate the effect of an acetylation treatment of the coir fiber surface on the mechanical behavior of epoxy composites with amounts of fibers up to 30% in volume. Coir fibers were immersed in an acid solution of acetic anhydride for one hour, washed and dried, before mixing with DGEBA/TETA epoxy to fabricate the composites. Flexural mechanical properties were obtained by bend tests. The results showed significant differences to similar composites with alkali treated coir fibers that have been previously investigated.

Jan 1, 2010

By Sergio N. Monteiro

Polymeric matrix composites reinforced with coir fibers are being used in many industrial applications such as automobile interior panels and cushions. These composites have relatively low mechanical strength due to the weak fiber/matrix interface. The objective of the present work was to investigate the effect of a surface alkali treatment of the curaua fiber on the mechanical behavior of polyester composites with different amounts of these fibers. The treatment, also known as mercerization, was performed with distinct concentrations, 0.1 and 10% of NaOH at 1 min and 1 hour, before incorporation of the coir fibers into the polyester composite. The results showed no significant change in comparison to similar untreated coir fiber composites. A microstructure analysis revealed that, in addition to reducing the hydrophilic characteristic of the fiber,the treatment also affects the surface morphology and impairs the fiber/matrix interfacial strength.

Jan 1, 2009

By Lucas Lopes da Costa

Bamboo fibers were characterized in terms of diameter distribution and tensile properties. Polyester matrix composites reinforced with these fibers were investigated for their flexural mechanical behavior. Specimens with up to 30% in volume of continuous and aligned bamboo fiber composites were bend-tested until fracture. The results showed an improvement in the composite strength and stiffness with the amount of bamboo fiber. A microstructure analysis by scanning electron microscopy revealed a reasonable adhesion between the fiber and the polyester matrix which justifies the improved mechanical properties of the composites.

Jan 1, 2010

By Wilson Acchar, Fernando Barcelos, Luis Carlos Pereira

"Porous ceramics have been extensively investigated as structural materials for flow of fluids in many applications, such as filters for molten metals, water purification and hot gases, thermal protection systems and heat exchangers. This class of material must have two special features: high permeability and mechanical strength. However, these parameters are influenced in different ways by the processing method and the consequent cellular structure. In this work two different types of commercial ceramic filter materials are investigated. Characterization included the evaluation of the strength values as well as the permeability behavior and microstructural analyzes of the surface fracture. The results indicate that the strength values are strong dependent on the filament defects.IntroductionCeramic materials with a cellular structure have been extensively investigated as structural materials for flow of fluids applications [1-3]. Microstructural aspects such as morphology, size of the cell and the degree of interconnectedness are mainly parameters that influence the properties of these porous materials [4-6]. The most used industrial process to produce cellular ceramics for filter application is the polymeric sponge replication method. This technique consists in dipping the polymer foam into slurry containing an appropriate binder and the necessary ceramic materials, followed by a heating treatment [2,5].Mechanical properties of cellular ceramics depend basically on cell size, degree of interconnectedness and density [1,2,5,8,9]. Materials used as filters required a good strength and also permeability values. These properties are inversely proportional to each other. Higher porosity increases permeability values but decreases the strength values [1,2,5]. The objective of this work is to study the strength resistance of a commercial porous ceramic material (10, 20 and 30 ppi) based on silicon carbide."

Jan 1, 2012

By H. Kohno

The Onahama No.3 tankhouse started commercial operation in early 1973, with the capacity of 8,500 metric tons per month. When the No.3 tankhouse was constructed, the starter sheet stripping section was rebuilt at the No.2 tankhouse and electrolyte purification section was expanded. The previous AIME paper in 1976 described the design principles of the No.3 tankhouse and its layout, This paper describes the starter sheet stripping machine in the No.2 tankhouse and the electrodes handling system in the No.3 tankhouse and all these equipments were developed for the operation of the No.3 tankhouse. A Hazelette continuous casting machine was also introduced in order to cast thin anodes with accurate shape. Owing to the adoption of thin anodes, gold, silver and copper inventory is reduced by 40%. Jumbo tanks and newly developed mechanical equipments were adopted and no work on cells during pulling up operation was achieved. Using thin anodes with accurate shape, inspection work was completely abolished while maintaining high current efficiency and high cathode quality. Labor cost was reduced by 70% and only six operaters can produce? 8,500 metric tons of cathodes per month. The same new electrolysis process is appreciated and has been used as a newly built independent tankhouse by Kidd Creek Mines Ltd., in Canada in 1981 with excellent results

Jan 1, 1987

By Hideyuki Takahashi, Taro Aichi, Kazuyuki Tohji, Makoto Muramatsu, Rie Sato

"There are several ways to condition lead-based alloy anodes for zinc electrowinning: electrochemical treatment, chemical treatment and physical treatment. Two advantages of physical treatments are their productivity and variety. In this report, physical treatments, including blasting with silica, alumina, steel grit and cut zinc wire, were tested. The laboratory tests confirmed there were differences in the formation of anode scales during electrowinning and in the suppression of lead dissolution from the anodes. With an increase in the surface roughness, the misfit between the PbC""2 and the MnC>2 was mitigated and the anchor effect was promoted; these effects resulted in dense Mn oxide scales on the anode.IntroductionZinc is widely used for hot-dip zinc plating and for die casting alloys. As a supplier of materials, we have endeavored to produce zinc that is economical and contains as little impurity as possible. As a result of our efforts, a technology for consistently providing special high-grade (SHG) zinc has been established. However, as seen in the issuance of the Restriction of Hazardous Substances (RoHS) Directive, public awareness of the industrial impact of heavy metals on the environment has been heightened. Increasing efforts to control environmentally sensitive substances will be necessary for our production processes.Electrolytic SHG zinc is produced by electrodeposition in an acidic solution with a Pb-Ag or Pb-Ag-Ca alloy for the anode and an Al alloy for the cathode. Pb alloy anodes are widely used because of their excellent durability; however, they are a source of Pb, which is the main impurity of the product."

Jan 1, 2012

By K. Koike, N. Masuko, Y. Takasaki

At the Zinc & Lead'95 symposium, one of the authors presented several modifications of Pb-Ag-Ca alloy anodes for the zinc electrowinning process, and also, the behavior of some organic additives in the electrolyte. In this study, the mechanical properties of the electrode materials composed by Pb-0.5 wt% Ag-(0~0.8) wt% Ca were studied by the tensile and Vickers hardness methods. Furthermore, experimental research on the influence of rolling and annealing treatments on the electrolytic behavior and mechanical properties of these alloys was carried out. The tensile strengths of the annealed Pb-0.5 wt% Ag-(0.1-0.8) wt% Ca alloys were the same or higher than those of the as-cast Pb-0.9 wt% Ag alloy. The anode potential using the as-cast Pb-0.5 wt% Ag-0.6 wt% Ca alloy decreased compared to the as-cast Pb-0.9 wt% Ag alloy. Moreover, the annealed Pb-0.5 wt% Ag - 0.6 wt% Ca anode after rolling showed a lower anode potential than the as-cast Pb-0.5 wt% Ag - 0.6 wt% Ca anode.

Jan 1, 2000

By J. R. Rendón

Cylinders of commercial aluminium alloy 6063 were homogenized under different conditions. The experimental results indicated that the general mechanical behaviour as related to curves of 0.2% yield strength, ultimate tensile strength and Brunnell hardness versus homogeneizing process is the same in both cases. The mechanical properties as compared to those required by plant specifications, tend to be better with increasing values of % Mg2Si in the alloy, as expected. The electron microscopy investigations revealed that in both homogeneizing processes the resulting microstructure consist of significant spheroidizing of the alpha phase (AlFeSi) and fine-needle type structure of beta phase. The alpha phase was also present in a Chinese type scripture. Furthermore, the slow cooling within the furnace resulted in the nucleation and growth of Mg2Si precipitates generally along the grain boundaries.

Jan 1, 1997

By Meghan McGrath

Third generation advance high strength steels with microstructures of acicular ferrite and retained austenite were investigated and meet mechanical property goals. A good combination of strength and ductility were achieved with duplex ferrite and austenite microstructures where cementite formation was suppressed. Transformation induced plasticity (TRIP) behavior produced rapid work hardening. The mechanical properties of two hot-rolled steels with duplex microstructures were compared and had the following compositions: (1) Fe-0.14C-13.87Mn-1.42Si-3.51Al; and (2) Fe-0.06C-14.2Mn-1.85Si-2.38Al. These steels were cast, homogenized, and hot rolled at 900ºC to obtain a refined microstructure with ultimate tensile strengths and elongations to failure of 865 MPa and 39% and 1,217 MPa and 28%, respectively. The amount of metastable austenite in both compositions decreased after tensile testing from 58% and 28% to 6% and 0%, respectively. Microstructures were characterized using optical microscopy, scanning electron microscopy (SEM), and x-ray diffraction.

Jan 1, 2010

By W. Y. Kim, K. H. Song, K. Nakata

"The present study was carried out to evaluate the mechanical properties of friction stir welded Inconel 600/SS 400 lap joints. In this process, friction stir welding (FSW) was performed at a tool rotation speed of 200 rpm and welding speed of 100 mm1min, and argon gas was utilized to prevent surface oxidation during the welding. Application of FSW notably decreases the grain size of Inconel 600 alloy from 20 µm in the base material to 8 ~ in the stir zone. However, the grain size of SS 400 in the weld zone was slightly coarsened, when compared to the base material. Also, the hooking in the advancing side and the intermetal1ic compounds (M7C3) in the weld interface between Incone1 600 and SS 400 were well formed. These intermetallic compounds and hooking were effective to increase in mechanical properties such as tensile and peel strengths.IntroductionFriction stir welding (FSW), applicable welding process at solid state, has several advantages in defect suppression such as blow hole, segregation and cracking which mainly occurs in fusion welding [1, 2]. Notable grain refinement in the stir zone due to FSW can expect the outstanding increase in mechanical properties of the welds. In constructing the chemical and power plants, Ni base superal10ys have been used in many parts, moreover, fusion welding as construct method, such as gas tungsten arc welding, electron beam welding and laser welding, has been mainly used [3-5]. However, fusion welding has a limit in an increase in chemical and mechanical properties in the welds. Lately, Ni base superalloys to which FSW applied have been reported with notable enhancement in mechanical properties, which resulted from refined grains in the welds [6-10]. These researches showed the possibility in applying the FSW, directly."

Jan 1, 2012

By Hidefusa Takahara, Koichi Miyake, Dierk Raabe

"Mechanical properties of copper wires were examined. The copper wires containing 5-10 mass % chromium and 1-3 mass % silver were produced through heavily cold deformation. It was expected that the copper wire was easily fractured during cold deformation because of the existence of brittle chromium phase in the alloy. In fact, the copper wire was fractured due to large work hardening, when the true strain [n] exceeded 5. However, the copper wire annealed at 1273K for 6 ks ·in the middle of deformation process could be smoothly drawn to 11=8. After precipitation treatment for silver phase at 473k for 1.8 ks, the wire was able to further drawn to n=8.4. The final deformed wire showed tensile strength higher than 1200MPa.IntroductionDownsizing of electronic devices has led to the demand of finer and higher strength materials for cables. Conventional copper alloys have about 800MPa in ultimate tensile strength. These strength are mainly obtained by precipitation hardening. Nowadays, a process for higher strength wire has been developed, where dual phase copper alloy is used. When it is drawn heavily, the' second phase is elongated along drawing direction and the wire gets high strength due to fiber reinforcement (1). That alloy is so called in-situ formed fiber reinforced ·alloy. Cu-Ag(2), Cu-Nb(3) and Cu-Cr(4) systems are well known as such alloys. It is also well known that chromium is brittle material except single crystal and high purity of chromium. However, Mihara et al. C5l have achieved 1 GPa in ultimate tensile strength in the Cu-Cr-Zr and Cu-Cr-Ti alloys by appropriate thermo-mechanical processing.In this study, the Cu-Cr-Ag systems were investigated: The alloys contained 10 or 5% chromium and 3 or 1 % silver. It was demonstrated that silver precipitated in copper matrix contributed on further hardening."

Jan 1, 2000

By Duclerc Fernandes Parra, Washington Luiz Oliani, Christiano Gianesi Bastos Andrade, Ademar Benevolo Lugão, Danilo Marin Fermino, Francisco R. Valenzuela Diaz

This work concerns the study of the effect of discarded bond paper on the mechanical behavior of polypropylene/organophilic clay nanocomposites. A brown polycationic bentonite from the state of Paraíba, Brazil, was treated with sodium carbonate to transform it into a bentonite that swells in water and then treated with hexadecyltrimethylammonium ammonium chloride to transform it into a bentonite that swells in organic liquids. Polypropylene with 3 % polypropylene graft compatibilizer (PP-g-AM) was mixed with 1 % and 2 % by weight of discarded bond paper and with 1% and 2% by weight of organophilic clay using a twin-screw extruder. The specimens were prepared by the injection process. The clay as received and after organophilization was characterized by XRD, SEM, and capacity of swelling in water and in organic solvents. The nanocomposite specimens were characterized by XRD and thermal analysis. The mechanical behavior of the injected specimens was evaluated by strength, flexural and impact tests. The nanocomposites showed improved mechanical properties compared with the polymer without filler.

Jan 1, 2015

By F. A. Fasoyinu

The mechanical properties of yellow brass (C85800), high strength yellow brass (C86300), and high manganese brasses (C99700 and C99750) cast in permanent molds have been studied. The tensile properties as well as fracture and impact toughness of these alloys are strongly dependent on the chemical composition. Alloys and/or compositions exhibiting relatively high zinc equivalent often exhibited high ultimate tensile strength and yield strength with significant reduction in ductility (% elongation). In order to achieve optimum properties with a good balance between strength and ductility, a calculation of the zinc equivalent before alloy preparation can be useful.

Jan 1, 1999

By Kaspar Tall, Dmitri Goljandin, Kristiina Vilsaar, Jaan Kers, Valdek Mikli, Lifeng Zhang, Riho Tarbe, Viktor Laurmaa, Mart Saarna, Priidu Peetsalu

In this paper, the mechanical milling of the Printed Circuit Boards (PCB) was carried out. First goal of the work was to examine the management of the WEEE, in particular the re-use of PCB. Firstly, recycling methods of PCBs were summarized. During the study mechanical separation methods (magnetic-, density- and air separaten), electrical, and chemical methods were examined. Secondly the optimal particle size for air-classification was determined. Several tests were carried out to find the most effective separation method for separation of different material groups from PCB scrap. The new air classification stand was developed for testing the separation of lightweight particles like tinfoil stripes and plastics. The test results showed sufficiently good separation of heavier Al and Cu. For milled materials characterization the SA, IA, laser diffraction analysis and SEM were used. The chemical composition of the PCB powders was studied by means of energy dispersive X-ray microanalysis (EDS).

Jan 1, 2011