By M. Kawakami

In relation to the designing of a new-type blast furnace, the reaction of carbonaceous materials with CO2 is expected to occur at as low temperature as possible. In order to get a highly reaetive carbonaceous material at low temperature, the reaction kinetics was investigated by measuring such quantities as the reaction rate from weight loss, the amount of CO adsorption and specific surface area by BET method. The reaction rates were large in the order of the Bintyo char, metallurgical coke, graphite and glassy carbon. If the rate was converted to the rate per unit area, however, those of the Bintyo char was smaller than that of graphite. Thus, it is suggested that the rate of the Bintyo char is influenced by the pore diffusion of CO2. The rate had a positive relation with the amount of CO adsorption, showing that the rate determining step would be the desorption of CO from the active side on the surface. The rate independent of surface area was derived, combining all the obtained data.

Jan 1, 2003

By M. Kawakami

In relation to the designing of a new-type blast furnace, the reaction of carbonaceous materials with C02 is expected to occur at as low temperature as possible. In order to get a highly reactive carbonaceous material at low temperature, the reaction kinetics was investigated by measuring such quantities as the reaction rate from weight loss, the amount of CO adsorption and specific surface area by BET method. The reaction rates were large in the order of the Bintyo char, metallurgical coke, graphite and glassy carbon. If the rate was converted to the rate per unit area, however, those of the Bintyo char was smaller than that of graphite. Thus, it is suggested that the rate of the Bintyo char is influenced by the pore diffusion of C02. The rate had a positive relation with the amount of CO adsorption, showing that the rate determining step would be the desorption of CO from the active side on the surface. The rate independent of surface area was derived, combining al\ the obtained data.

Jan 1, 2003

By Peter C. Hayes

"The high temperature reduction of solids through the use of reactive gas atmospheres has application in a wide range of industrially important processes. Whilst significant advances have been made in understanding and describing these processes, some key aspects of the chemical reactions and reaction mechanisms operating in these systems, for example, the transformation from metal oxide to metal, remain poorly understood. A number of different product morphologies have been identified in these reaction systems and the reaction rates have been shown to be critically dependent on the product structure.Theoretical examination of the elementary process steps taking place in the region of the gas/metal/metal oxide interface, combined with electron microscope studies of the resultant product microstructures, have enabled the key process and material variables responsible for the development of the various product morphologies to be identified. By considering i) established criteria for the stability of moving interfaces in a thermodynamic potential gradient, ii) the relative rates of chemical reactions on the oxide and metal surfaces, and iii) key process phenomena and physico-chemical properties of the solid phases, the mechanisms and conditions for the formation of various product morphologies are identified. Interestingly the analysis points to direct analogies between these phase transformations and, the phenomena and microstructures observed in metal solidification, and the potential to develop generic models of these fluid/solid reaction systems."

Jan 1, 2013

By Tangstadm Merete, Eli Ringdalen

"This paper presents an overview of results from The Norwegian Research Institution SINTEF and the Norwegian University of Science and Technology, NTNU regarding new and ongoing research in silicon production. The main studies are related to condensation of SiO gas and cavity formation. If SiO gas condensation is increased at the top of the furnace resulting in SiO content in the off-gas closer to equilibrium, the Si yield will be increased significantly. Experimental work, simulating a cavity under industrial conditions, has shown that the cavity grows downwards from one layer. Physical appearance of zones in industrial furnaces, and selected reactions in these, are discussed based on results from excavation of industrial furnaces and results from laboratory experiments. Experimental studies of reaction rates for the formation of SiO are presented. Quartz properties are demonstrated to vary between differing quartz types and the effect of this is discussed.Introduction Both the theoretical and industrial issues associated with the production of silicon are described in detail in the textbook written by Schei et al [1]. This book covers the knowledge of silicon production process up to 1998. Together with the work by Myrhaug [1] and by Aasly[2], this is the main basis for this paper. Recent and ongoing research at SINTEF and NTNU focusing on production of Si and SiO in the high temperature zone, dissociation of SiO and condensate and cavity formation will be discussed."

Jan 1, 2012

By B. J. Zhao, F. L. Han, L. E. Wu, M. Chen, Y. H. Chen

Magnesium is the lightest structural metal with a density only two-thirds of aluminium and one-quarter of steel. It can be produced by electrolysis of fused magnesium chloride or high temperature reduction of the oxide. The predominant method for magnesium production is the Pidgeon process which is a batch process starting from calcined dolomite and ferrosilicon. CaF2 is commonly used in the process as the catalyst. Analyses of the slag samples and thermodynamic calculations indicated that liquid phase plays important role in the reduction process. Effects of chemistry, temperature and gas pressure on the production have been discussed and compared with the operating data. Understanding of the reaction mechanisms will provide a fundamental base for alternative processes of the magnesium production.

Mar 1, 2017

By R. Cavanagh

Studies relating to the fixation of sulfur by reaction of 4 to 8 mm diameter cylinders of calcined limestone or dolomite with high strength sulfur dioxide in the temperature range 880°C to 1020°C were undertaken. Dolomites are far superior in sulfate capacity and reactivity than dense limestones even at high strength SO2. The sulfation reaction was first order with respect to SO2 concentration below 100 percent. Zero reaction rate at 100 percent SO2 concentration indicates that sulfate was the exclusive reaction product and that sulfite had no role in the reaction. At relatively low SO2 concentrations gaseous diffusion through the reaction product layer has a marked effect on the rate. As SO2 concentrations were increased up to 100 percent more complex rate controlling mechanisms unfold. By sectioning partially reacted dolomitic limestone pellets a moving interface was observed. Reaction ceased because of pore plugging for dense non-porous limestones at 30% conversion. With dolomitic material virtually complete sulfation of the calcium was observed. S.E.M. analysis showed that the average atom ratio Ca:S was 1.01, thus supporting the argument that little if any of the magnesium was sulfated.

Jan 1, 1996

By Guojun Qi

This work relates to wafer bumping technologies for flip chip packaging applications in the electronics industry. Nickel and its alloys are alternative under bump metallization (UBM) materials because of their slower reaction rates with Sn-based solder as compared to Cu-based UBMs. In this study, we compared the morphologies of the intermetallic compounds (IMC) formed between Sn-bearing solders (Sn3.5Ag and eutectic Sn-Pb) and two types of nickel- based UBMs, electroless Ni-P (EN) and sputtered nickel. Both chunky-type and needle-type of intermetallics were observed between the EN UBM and the solders. In the case of sputtered Ni UBM, there is only a layer of scallop-type intermetallics formed. The morphology change and growth kinetics of the IMC in thermal aging process were analysed. Kirkendall voids were noticed from samples of Sn3.5Ag solder vs Ni-P UBM that have undergone prolonged thermal aging at high temperature.

Jan 1, 2003

By Guojun Qi

This work relates to wafer bumping technologies for flip chip packaging applications in the electronics industry. Nickel and its alloys are alternative under bump metallization (UBM) materials because of their slower reaction rates with Sn-based solder as compared to Cu-based UBMs. In this study, we compared the morphologies of the intermetallic compounds (IMC) formed between Sn-bearing solders (Sn3.5Ag and eutectie Sn-Pb) and two types of nickel- based UBMs, electro less Ni-P (EN) and sputtered nickel. Both chunky-type and needle-type of intermetallics were observed between the EN UBM and the solders. In the case 'of sputtered Ni UBM, there is only a layer of scallop-type intermetallics formed, The morphology change and growth kinetics of the IMC in thermal aging process were analysed. Kirkendall voids were noticed from samples ofSn3.5Ag solder vs Ni-P UBM that have undergone prolonged thermal aging at high temperature.

Jan 1, 2003

By Jan Pan, Deqing Zhu, Xianlin Zhou, Yanhong Luo, Zixing Xue

"Magnetic roasting process, aiming at obtaining magnetite concentrate, is the principle method of exploiting siderite as a raw material in iron and steel industry. Study on preparing DRI from siderite through coal based reduction technology is sporadic. To make the process of how siderite is reduced to iron clear, roasted ore reduced from siderite by lignite under different time periods were analyzed. The results indicated that: at the temperature of 1050°C, siderite was rapidly decomposed into magnetite, and further reduced as Fe30r?FeO?Fe, the later step was slower than the previous one. A fracture of particles was found during the process of thermal decomposition and the reduction of newly formed magnetite. As the reduction proceeded, metallization rate of products increased, and the iron grain grew along with time.IntroductionWith the rapid development of economy, China demands more and more iron ores for the iron and steel industry. China has rich iron ore resources, but 97% of them are below 30% in iron grade, many are refractory and unutilized [1], therefore large quantities of imported iron ores are in a desperate need. China imported 686 million tons of iron ore in 2011 (data from the China Customs), accounting for nearly 60% of the total consumption. To guarantee the healthy development of iron and steel industry, domestic refractory iron ores have to be utilized both economically and environmentally."

Jan 1, 2013

By K. Murayama, M. Kawakami, T. Takenaka, S. Yokoyama

"Cokes play an important role of spacer in blast furnace. However, they degenerate during Boudouard reaction. Blast furnace cokes are reacted with pure C02 at I 072 to 1673 K. Reaction rate was obtained by the weight change of spherical specimen. The specimen after reaction was examined by microscopic observation. The reaction rate increased with temperature and was expressed by two Arrhenius type lines. The activation energy was 126 KJ/mol at higher temperature than 13 73 K and 202 KJ/mol at lower temperature range. At the higher temperature range, the reaction proceeded from the surface leaving unreacted core, whereas homogeneously whole inside at lower temperature. The porosity increased from the center to surface at higher temperature, whereas it was almost constant at lower temperature.IntroductionThe cokes have the function of fuel, reductant and spacer to keep gas and liquid flow in the blast furnace. Thus, the reaction mechanism of coke with several gas and the strength after the reaction should be important factor to control the blast furnace operation. The reaction mechanism of coke with C02 has been studied extensively. The rate equations were derived by Gadsby[ I], Ergun[2] and Turkdogan and Vinters[3]. They were compared and discussed by Kobayashi and Omori [ 4]. Effect of crystallization degree on the reaction rate was examined by Kashiwaya and Ishii[5]. Catalytic enhancement effect of ash componets have been clarified by Kashiwaya et. al. [6]. Although degradation of coke in blast furnace has been examined recently[7], however, the degradation of coke after the reaction with C02 has not been well clarified yet. In the present work, the metallurgical coke specimen was heated in N2 and C02 and the reaction mechanism and degradation behavior after the reaction was investigated."

Jan 1, 2000

By Chengyi Ding, Xuewei Lv, Senwei Xuan, Chenguang Bai, Kai Tang, Gang Li, Yang Xu

Perovskite easily forms during sintering of vanadium titanium magnetite (VTM) and is unfavorable for the following blast furnace. Steelmaking can concomitantly produce a great quantity of oxidized scale composed mainly of FeO and Fe3O4. Calcium ferrite (CaOFe2O3, CF) can be formed by oxidized scale with lime in air atmosphere and then added to the VTM during sintering. X-ray diffraction (XRD) results indicated that perovskite is not generated at low temperature but only when the temperature increases to 1473 K in the CF–TiO2 system. Therefore, VTM sintering can be performed with a low-temperature process with doping of CF. Perovskite formation is mainly divided into two steps. First, CF melts and produces CaO. TiO2 and CaO then combine to produce perovskite. This paper also discussed the reaction mechanism of CaO–Fe2O3–TiO2 ternary system to compare the generation routes of perovskite.

Mar 1, 2018

By E. J. Peuraniemi

Oxidation of chalcopyrite concentrate and two low-iron copper mattes were studied using a laboratory scale laminar-flow furnace simulating the phenomena taking place in different zones of the reaction shaft of a flash smelting furnace. In the experiments, screened fractions were fed into the furnace and sampled after short reaction time intervals by quenching them into a water film. Experimental conditions included temperatures of 1100 and 1300°C with reaction gas oxygen contents from 21 to 75 vol.%. Samples were analysed chemically for Cu, Fe and S to define removal rate of sulphur. Optical and scanning electron microscopy with EDS-analyser were used to examine the samples. In this paper, oxidation kinetics as well as ignition of particles are discussed. Changes in particle morphology, size, and composition are viewed to closely define the proceeding of the oxidation, and, consequently, to compose a detailed model of dust formation and reaction mechanisms. Data obtained in the experiments broadens the knowledge of physical and chemical phenomena in flash reactions and serves as reference for computer simulations.

Jan 1, 2000

By Peter G. Smith

Tri-calcium aluminate (TCA) is a dominant alkaline component of the red mud residue from the Bayer process. A method being considered for industrial implementation partially neutralizes the residue by contacting it with gaseous CO2. This paper outlines the chemistry of CO2neutralisation of TCA under conditions relevant to the treatment of Bayer residue. CO2 neutralisation of the liquor is fast. It results in the formation of amorphous aluminium hydroxide and dawsonite that agglomerate together. Neutralisation of solid TCA is slower and leads to the formation of calcite, dawsonite and amorphous aluminium hydroxide. The dissolution of TCA in partially neutralised slurries causes pH reversion. However the carbonated solutions contain a store of bicarbonate that can supply aqueous carbon dioxide to complete the transformation. The pH at which the carbonation is carried out will affect the degree of TCA transformation during the carbonation process. In particular, if the pH of the carbonation is too low (near 7.0), calcite precipitation is inhibited and the degree of transformation is low. Controlling the carbonation pH helps to optimise the neutralisation process.

Jan 1, 2003

By Masayuki Kudoh, Kiyotaka Matsuura

"Molten aluminum and nickel cast onto a steel block exothermically react and produce molten nickel monoaluminide, NiAI, which is simultaneously joined to the steel. The heat of the exothermic reaction is transferred to the steel block, and steel near the surface of the block is melted. The depth of the melted steel increases with both the initial temperature of the steel block and the thickness of the produced NiAI. Iron from the melted steel dissolves in the molten NiAI, and an intermetallic compound of NiAI-Fe pseudo-binary system is produced. During solidification of the intermetallic compound, it is strongly joined to the steel. The Ni.Al-Fe intermetallic compound has an excellent resistance to oxidation and corrosion.IntroductionAn intermetallic compound of nickel monoaluminide, NiAl, offers many advantages over conventional superalloys, such as higher melting temperature, lower density, greater specific modulus and higher thermal conductivity [1]. NiAl also exhibits excellent high-temperature oxidation resistance when doped with zirconium or hafnium, and excellent high-temperature corrosion resistance when doped with chromium or yttrium, that are superior to existing high temperature alloys or coating materials [1-4]. On the other hand, NiAI is significantly brittle at temperatures below 600 K [5-7], which is the most sigriificant disadvantage of NiAI. A possible way to overcome the disadvantage and to utilize NiAl as an environmental-resisting high-temperature structural material may be joining of NiAl to a ductile material."

Jan 1, 2000

By Y. A. Chang, J. Woodford, C. R. Kao

Reactive diffusion studies between NbC and Si were carried out at 1300 °C under a vacuum of 10-5 torr and a uniaxial pressure of 1 MPa. The annealing time ranged from 8 to 100 hours. The Si used was single crystal silicon; the NbC was hot-pressed powder compact. A NbSi2+SiC two-phase reaction layer formed with NbSi2 as the matrix and SiC as discontinuous particles. The microstructure of the reaction product is homogeneous, dense, and fine. The NbSi2 grain size and SiC particle size are in the micron range. The growth of the reaction products follows parabolic kinetics. Extrapolation of the data to zero thickness suggests an apparent incubation time of 3.5 hours. However, for short annealing time «60 hours), the thickness data can be approximated by linear kinetics with an initial growth rate of about 2 11m/hr. Based on these experimental observations, a growth mechanism for the reactive diffusion between Si single crystal and NbC powder compact is proposed. We propose that the nucleation sites for the SiC particles are at the voids of the NbC powder compact. This proposed nucleation mechanism offers a potential way of controlling the SiC particle size by changing the void size and void density of the NbC powder compact. This hypothesis, if proven to be true, will allow us to control mechanical properties of the composites by tailoring the SiC particles formed. It is also pointed out that the microstructure requires Si to be the dominant diffusing species and to diffuse through the reaction layer, while Nb and Conly have to undergo local rearrangement.

Jan 1, 1996

By H. Sieber

Multilayer samples of tantalum and aluminum with the composition of Al-25Ta were prepared by cold rolling of elemental foils. The microstructure and phases were characterized by XRD, SEM and TEMISAED and the reactive phase formation was examined by DSC and DTA measurements in multilayer foils rolled for different deformation levels. The rolling procedure yields a decrease of the Ta particle size in the Al matrix and also results in the formation of a multilayer structure with a thickness of the elemental foils down to 200 nm in average. No phase formation is observed during the cold rolling procedure. While XRD and DSC measurements show no phase formation up to the melting of aluminum for samples rolled up to 40 F&R (fold and rolling) passes, in samples rolled for 50 or more F&R passes a first phase formation reaction yield an interfacial layer of TaAl3. Contrary to former studies in the investigated cold rolled Al- 25Ta multilayers the reaction starts at temperatures as low as about 340°C. The first stages of the reaction are associated with two exothermic maxima, that increase in amplitude and shift to lower temperatures with increasing number of F&R passes. At higher temperature the TaA13 reaction layer thickens very sluggishly and yields a third exothermic maxima at about 600°C. Isothermal DSC scans show the reaction is not finished for samples containing elemental particles larger than 1 pm after annealing at 550°C for 5h. In all the investigated samples no Al- Ta phase other than Tad3 was observed to grow for heat treatments up to 800°C. Multilayer samples heated up to 1400°C show a morphology consisting of small AITa2 particles embedded in a single phase TaA13 matrix. The multilayer microstructure and reaction product morphology are characterized by SEM and TEM investigations in cross-section and plan view geometry.

Jan 1, 1998

By Patrick R. Taylor

Coatings of TiCIFe have been produced by Reactive Plasma Spraying using ilmenite ore concentrate as the feedstock powder and methane as the reactive gas. A free energy minimization analysis of the ilmenite-methane system is presented. The coatings have been characterized by x-ray diffraction and SEM. The microstructure of the coatings indicates good interparticle cohesion. The composition of the coating is deficient in iron compared to the initial Fe to Ti ratio found in ilmenite.

Jan 1, 1998

By G. E. S. Lima, J. V. B. Lemes, F. G. D. Machado, S. Monteiro, L. G. Pedroti, L. A. F. Fioresi, W. E. H. Fernandes, R. C. S. S. Alvarenga

With advances in industrial processes, new products have emerged and become essential in everyday life. These activities generate different types of wastes, which can be harmful tothe environmentif not properly disposed. Having this problem in sight and considering the importance of concrete in the construction industry, this study analyzes the behavio of Reactive Powder Concrete (RPC) with addition of granite processing waste. Scanning Electron Microscopic (SEM) tests, compressive strength and Young’s modulus tests after 1, 3, 7 and 28 days of production and shear and flexural strength after 28 days of production were performed during the analysis. The results indicated that incorporation of this residue into RPC does not affect its performance. RPC was still able to present high compressive and flexural strength.

Mar 1, 2017

By N. Kanarin

A thermodynamic study is reported on the chlorination of Fe(1-x.)O, Fe2O3, Cr2O3, MgO, Mg2SiO4 with chlorine in the presence or the absence of reducing atmospheres. The reactivities of these compounds as well as that of Mg3Si2O5(OH)4 using Cl2+N2, Cl2+air, and Cl2+CO gas mixtures were studied by non isothermal thermogravimetric analysis between 20 and 1000 °C. The same solids were chlorinated in a horizontal experimental set, during two hours between 350 and 1000 °C, in reducing and oxidizing atmospheres: The chlorination products were examined by XRD and SEM, and possible reaction paths were examined. Results indicate that the carbochlorination of these solids was better than their chlorination; Furthermore, the carbochlorination was performed at lower temperatures than those of the chlorination. Finally, the reaction extent was higher in the case of carbo-chlorination of these compounds. Based on these results, a process was suggested for the selective recovery of chromium compounds from the chromite concentrate.

Jan 1, 1995

By N. Kanari

Reactivity of MgO towards C12+air, C12+N2 and C12+CO gas mixtures was studied up to 1000 °C. Carbochlorination of MgO occurs at temperatures lower than that of its oxychlorination. Effects of gas flow rate, temperature and partial pressure of the carbochlorinating gas mixture on the reaction rate were investigated. The apparent activation energy of MgO carbochlorination is 49 kJ1 mol between 425°C and 600°C. At 550 °C, the apparent reaction orders with respect to C12+CO, C12 and CO, are 2.37, 1.47 and 0.89, respectively. At this temperature, the maximum reaction rate was obtained using a C12+CO gas mixture having a Cl2lCO molar ratio equal to about 0.6.

Jan 1, 1998