By San-chuan Tang, Wen Chen, Shun-ming Ning, Kan-ping Yu, Qiang Zhao, Xue-yong Xing

"A new type of desilication agent (PA-2) was selected by experiment based on the analysis of the characters of silica gel, and the influence of desilication type, desilication dosage, pH value, temperature and aging time on the desilicating effect was studied. The test results showed that on the conditions that pH was 2.0, temperature was 20""C, aging time was12 hours and the dosage of desilication agent was 0.23%, the desilication rate was higher than 93% in solution.IntroductionVanadium is an important strategic resources, which applies to steel industry and petrochemical industry. The main materials for vanadium product are steelmaking vanadium slag, stone coal and containing vanadium waste catalyst, etc. And stone coal is a low-grade carbonaceous silicified vanadium resource, which is unique material for vanadium extraction in China. Meanwhile, our stone coal reserves is No.l throughout the world.The silica acid solution containing vanadium is produced by acid leaching of raw stone coal or its roasted ore. The silica content of this solution is mostly high, besides, when pH is higher than 2 , the solution is unstable. Furthermore, it is very easy to generate gel substance with the increasing of pH value and standing time. 'Ibis silica gel is composed of colloidal particles with the size in 0.001 - 0.1 um. As a result, it is very hard even impossible for the following operation of solution."

Jan 1, 2013

By Jinxia Nie, Yunnen Chen, Dachao Zhang

"Rare earth resources are strategic and non-renewable resources. But disordered exploitation on rare earth metals leads to resources waste, environmental pollution and ecosystem destroyed. In this paper, soil collected from garden was cultured in thermostated incubator. Adding exogenous rare earth to the soil and the effects of recombination action of rare earth lanthanum, cerium and yttrium on soil enzymatic activities were studied. The results showed that single metal La and Ce can increase urease activity, but Y inhibits its. Coexist La/Y or La/Ce in soil inhibit the urease activity, coexist Y /Ce or coexist three metals promote its. Single metal La, Y and Ce can promote catalase activity, and that of coexist three metals. Pairwise coexist La, Y, Ce in soil inhibit catalase activity. With certain concentration of rare earth recombination action, urease activity in soil has been very significant direct proportion to ionic impulse, but catalase activity been insignificant inverse proportion to its.1. IntroductionThe increase of rare earth element content due to anthropogenic inputs frequently takes place in agro-industrial areas, leading to soil pollution episodes that may cause serious environmental problems because of their potential toxicity to microorganisms, plants, animals and human beings [ 1]. China is abundant in lanthanides resources. Rare earth metals are used in many frontier technologies such as photic devices, magnetic materials, and fine ceramics, and the amount of the rare earth metals used in these industries has been increasing. In addition to their use in industry, rare earth metals are more widely applied to cropland as microelement fertilizers due to their ability to promote growth and productivity of some crops [2]. As a result, more and more rare earth metals are moving into the ecosystems. While a permanent contamination of soils results in populations of micro-organisms with high resistance to rare earth metals, a short-term burden of contaminants at high concentrations could exert inhibitory effects on microbial carbon [3]. They accumulate in soils, bioaccumulate in crops, and enter the food chain, causing a potential problem of rare earth metals environmental pollution in China [4]. This contamination may also severely influence organisms and soil activities [5]."

Jan 1, 2011

By Jintao Gao, Zhancheng Guo, Chong Li

A new approach to enrich MFe and RO phase from the converter slag by super gravity was investigated. The samples obtained by the gravity coefficient G=600 and cooling rate V=5K/min from 1623K to 1373K appeared significant stratification and the MFe gathered at the bottom of sample. With the help of metallographic microscopy and X-ray diffraction, it is found that large quantity of white RO phase gathered at the lower part of the sample as the concentrate, with volume fraction appearing gradient distribution along the direction of super gravity, while the upper part was mainly composed of dicalcium silicate as the tailing. The mass fractions of the FeO, MgO and MnO in the concentrate are up to 40.46%, 6.9% and 3.91%, while that in the tailing are just 11.65%, 2.15% and 1.55%. The recovery ratios of FeO, MgO and MnO in the concentrate are 60.35%, 58.45% and 72.24%, respectively.

Jan 1, 2016

By Shengli Wu, Jiacong Zhang, Kai Gu, Bingjie Wen, Heng Zhou

In practical production process, the average of silicon content in hot metal (HM) of COREX process (the average is 1.58%) is obviously higher than that in blast furnace (the value is below 0.6%), which leads to an increase in the cost of steelmaking. In this work, the factors affecting and impact mechanism of silicon content in HM were investigated by statistical analysis using actual operating data. The analysis indicates that the fuel rate, binary basicity of slag and the temperature of HM are positively correlated with the silicon content, while the sulfur content of HM and binary basicity of burden are negatively correlated with the silicon content. On this basis, a back propagation neural network was developed to predict and control the silicon content in HM. All the findings of this work are useful for guiding and optimizing the COREX operation.

Mar 1, 2018

By Saynbaatar, Gangping Ma, Jianhua Fu, Qiqige, Jinghua Wang

The influence on the performance of foam concrete made by replacing cement with some industrial waste residues was researched in this paper. The result shows that the 7d and 28d compressive strength of foam concrete increases firstly and then decreases with the increasing amount of industrial waste residue. The proper added range is 10%-20% for steel slag, blast furnace slag and coal ash, but, 8% for desulfurized fly ash. With the proper adding ratio, the compressive strength of foam concrete always increased comparing with the pure cement foam concrete. When adding 48% of the compound industrial waste residues, the 28d compressive strength of the foam concrete reached the 2.9MPa which could match the pure cement foam concrete. The results indicates that there is a synergistic effect among the compound industrial waste residue, and this effect is benefit to improving the compressive strength of foam concrete.

Jan 1, 2015

By Jian-Xun Fu, Hong-Qiang Liu, Si-Yu Liu

The production of zinc-bearing solid dust is up to 4%~8% of total crude steel in steel plant, which is difficult to be recycled in traditional methods. To fully utilize the resources and reduce environmental pollutions, Chinese steel plants are using rotary hearth furnace (RHF) process to recycle solid dust. A consequential life-cycle inventory was carried out to assess the impact of dust recovery on greenhouse gas emissions based on the local production status. In the study system, the selected steel plant named which have 10.5 million tons of Crude steel productivity and 0.48 million tons solid dust come out meanwhile. To research, a RHF production line of 0.3 million tons directly reduced iron (DRI) a year was established to recycle the solid dust. The DRI will be obtained from RHF and sent to the blast furnace as raw materials to reduce the demand for iron ore and coke in steelmaking processes. By researching on the life-cycle inventory in the system, the steelmaking process with RHF was 2299.3kgCO2/ton steel. It’s a little higher while compared with the process without RHF, which data is 2297.0 kgCO2/ton steel. The small production of DRI make a small difference to reduce the carbon footprint of steelmaking process, the added carbon footprint of RHF process is more than BF and other steelmaking processes reduced. It is concluded that dust recovery has no contribution to the greenhouse gas emission reductions in the technic condition of Chinese steel plants currently.

Jan 1, 2016

By Xin Li, Zurui Hu, Fuming Zhang

High blast temperature is one of the important technical characteristics of modern blast furnace (BF), which is also an important technical approach for the green development of ironmaking. Increase blast temperature can improve and promote the BF operation smooth and stable, reduce coke rate, fuel consumption and CO2 emission. Top combustion hot blast stove technology has been applied in Shougang Jingtang’s 5500 m3 BF for 8 years. Under the condition of burning single BF gas, high efficiency energy conversion and over 1250 °C high blast temperature have achieved. The combustion and heat transformation process were researched by numerical simulation technology to optimize the structure design. The high efficiency annular ceramic burner and checker brick were developed and applied, the flue gas waste heat was recovered and reused to preheat the combustion air and gas. Prominent achievement of high blast temperature under the condition single BF gas burning has been realized.

Mar 1, 2018

By Guangliang Wu, Dong-chang Huang, Xin-bin Liu

High temperature mechanical properties of 50Cr5MoV roll steel was investigated by Gleeble 1500 thermal simulator testing machine The morphology, composition and microstructure of fracture surface were observed and analyzed by OM, SEM and EDS The results are indicative of that, there are two brittle temperature zones of 50Cr5MoV roll steel at the temperature of 600°C~950°C and 1300°C~1450°C, respectively. The section shrinkage rate is less than 60% The fracture mode changes from mixed ones dominated by intergranular to toughness transgranular one with the increase of temperature at the range of 650°C~1300°C. The fracture is along the solid--liquid phase at the range of 1300°C~ melting point It is crucial to formulate the 50Cr5MoV casting technology, to prevent the cracks and improve the quality of 50Cr5MoV roll steel.

Jan 1, 2016

By Lv Guozhi, Niu Liping, Shi Guanyong, Liu Yan, He Jicheng, Du Yanjun, Dou Zhihe

"We proposed thermit reduction-electroslag remelting method of preparing the large scale CuCr alloy. But there are pores and oxide inclusions in CuCr alloy prepared by thermit reduction process. This paper studied mainly the effects of ratio of reactant and additive on the inclusion type and their occurrences in CuCr alloy. The alloy prepared in different process conditions was characterized via XRD, SEM, OM and TEM and metallographic microscope, in which the existing state and micro-structural defects of inclusions are analyzed. The results show that there are three distinct regions: copper-rich regions, chromium-rich regions and the inclusion regions. Inclusions are mainly in the form of stomata and Alz03 phase, mainly locating in the copper-rich phase and the interface area of chromium-rich phase and the copper-rich phase. Adding Na3AlF6 and heating agent can effectively reduce the inclusion content in the alloy.1 IntroductionIn recent years, with the development ofhigh power vacuum and high-pressure technology ,the CuCr alloy contact material which has many advantages gradually replaced the traditional W-Cu and Cu-Bi series alloy contact material, and become the first choice of material in high-voltage and high-power vacuum switch contacts['-3l. The traditional powder metallurgy method, infiltration method and vacuum arc melting method[4-SJ are using metal Cu powder and Cr powder as raw material by casting molding, and have disadvantages such as high production costs, complicated process, poor product density and low yield, especially in the large size alloy ingots[9-12l. At present, the world regards CuCr alloy new preparation technologies as the first place, and how to achieve a large size the CuCr alloy ingot preparation has become a hot research of CuCr alloy[3l. Zhang Ting-an and Dou Zhihe[l-3l who are supported by national natural science fundation of china successfully successful developed new technologies and core equipment to prepare large-size copper-chromium alloy through aluminum thermal reduction-secondary refining method, and obtained two national invention patents. The method includes two key steps: one is get CuCr alloy consumable ingot by Thermit-SHS with electromagnetic stirring, the other is to refme the CuCr alloy ingot to remove the pores, inclusions and other defects by electroslag remelting technology to get dense and uniform CuCr contact material. The preliminary study results show that means of electromagnetic stirring evidently inhibit effect of alloy ingot macrosegregation during the electromagnetic casting stage, but there are still microstructure defects such as alumina inclusions and pores in the alloy ingots. Therefore, Zhang Ting-an et al refer new ideas of using the electroslag remelting to refine Cu Cr alloy ingots and effectively remove the defects of the ingots such as pores and inclusions [3l _ At present, there is no report of study on the electroslag remelting refining processes of CuCr alloy (the refining slag, remelting current). This article will research mode of occurrence and distribution law of inclusions in the large-size CuCr alloy ingots by Al Thermit-SHS under magnetic field stirring action and provide a theoretical basis for chosing refining slag to remove inclusions by electroslag refining. Meanwhile the article analyses the effect of reduction conditions of Thermit-SHS on the types of inclusions, mode of occurrence and distribution of regular inclusions in alloy ingot, and refer theory for inclusions regulation in the large-size alloy ingots."

Jan 1, 2013

By Lv Guozhi, Niu Liping, Liu Yan, Zhang Zhiqi, He Jicheng, Zhang Ting’an, Dou Zhihe

"CuCr alloy can be extensively used as contact materials in integrated circuit, electrodes, electric contact and high strength conductor. We proposed thermit reduction-electroslag remelting method of preparing the large scale CuCr alloy. But there are pores and oxide inclusions in CuCr alloy prepared by thermit reduction process. This paper studied mainly the effects of ratio of reactant and additive on the inclusion type and their occurrences in CuCr alloy. The slags and CuCr alloy were characterized respectively by XRD and SEM. The results show that when the additive is Na3AlF6, the slag consist of Al2O3 and Cr. When the additive is CaF2, the slag consist of Al2O3, Cr, CaF2 and CaAl4O7. The inclusions in CuCr alloy are mainly Al2O3 and pores which disperse in Cu-rich zone and Cu-Cr phase interface. When 5% CaF2 and 5% KClO3 are added, there are fewer pores and inclusions, and the more better microstructure.1 IntroduceCuCr alloy is the contact terminal material with an eximious properties[1,2], which gradually replaces CuBi alloy becoming the first choice for contact terminal material in the medium and high power vacuum switch after the 1970s. The traditional preparation methods of CuCr alloy mainly contain powder metallurgy, infiltration process and vacuum electric arc melting methods. But the above methods exist some shortcomings, such as poor product quality, high cost of production, processes complex ect[3-9]. CuCr alloy is made by the thermit reduction self-propagating method, which uses CuO, Cr2O3 and Al as raw material to get the high-temperature melt, and then casts to manufacture CuCr alloy ingot, which response equation follows as:"

Jan 1, 2012

By Aiyuan Ma, Kun Yang, Weiheng Chen, Jinhui Peng, Shiwei Li, Feng Xie, Libo Zhang

In this thesis, a new process of recovering zinc sulfide ores was developed. The novel synthetic coordination leaching process mainly included two steps: microwave assisted phase reconstruction and compound coordination leaching. By applying various techniques, such as chemical composition analysis, X-ray diffractometry (XRD) and Raman spectroscopy, it could be concluded that sulfide phases would directly oxidized to zinc oxides under the 500 ºC microwave roasting and adding 30% Na2O2. What’s more, zinc leaching rate reached to 61.16% within 2 hours. Compared to the current technologies, this procedure had the advantage of avoiding SO2 emission, high leaching efficiency, simple process, manipulate easily, and low cost, which could be expected tremendous application potentials.

Jan 1, 2016

By QinGuo, Shenghui Guo, Jinhui Peng, Linqing Dai, Libo Zhang

This paper adopts a simple and novel preparation. Taking cellulose as a template, a tubular morphology structure of micro/nano ZnO crystals was obtained by microwave roasting at high temperature. The higher the microwave roasting temperature, the larger the degree of crystallization. The experiments indicate that the best photo catalytic effect can be obtained at 850 : At this temperature, the oxidation of cellulose is complete. Large quantities of hexagonal shaped ZnO crystal can be observed, specifically the (0001) crystal face. Under ultraviolet-visible irradiation, taking long arc mercury lamp as light source, the material had good photocatalytic activity. The decomposing efficiency of methylene blue reaches 97% in 60min, which is superior to that of preparations without templates at the same temperature.

Jan 1, 2016

By Hiroyuki T. Takeshita

Ca-Ni based alloys were investigated on structures, hydrogenation properties and the effect of additive elements on hydrogenation properties. CaNi, samples were decomposed to form a new hydride with a CsCl-type structure on the constituent metal atoms at high temperatures such as 673K in a hydrogen atmosphere. The candidate of the third element which was added to stabilize the original compound was investigated by using the Miedema's semi- empirical model and, as a result, Pd was chosen. The hydrogenation of CaPd was conducted with a Sieverts' type apparatus and the synthesis of Ca-Ni-Pd ternary alloys was performed by high frequency heating.

Jan 1, 2002

By Xiao-hui Fan, Xu-ling Chen, Zhi-yuan Yu1, Guanghui Li, Min Gan, Yun-song Huang, Tao Jiang

Compared with the traditional de-NOx processes by cleaning the waste gas, a new approach for reducing the formation of NOx during sintering process is proposed. Since more than 90vol% of NOx comes from the fuel combustion, the influence of sintering coke breeze pretreated by CO(NH2)2 additive on the NOx emission is researched. As adding CO(NH2)2, the reduction agents (NHi) are generated during the pyrolysis of CO(NH2)2, which reinforce the NOx reduction, And the appropriate content of CO(NH2)2 is 1.0 mass% of coke breeze.

Jan 1, 2015

By Zhiqiang Zhou, Libin Zhu, Zizong Zhu, Hao Xiong, Yuchuan Ding

In order to utilize the lean ore resources from XinJiang rationally and optimize mixture, laborarory measurements have been carried out under different basicity, various mixed carbon content as well as the properties (ratio) of fuel particle size by the sintering pot for further microstructure analyses. The results show that sinter strength falls by 5.0%, low temperature reduction disintegration index (RDI) drops off to the lowest in certain ranges. The natural degradation index of sinter is much higher when sinter basicity is between 1.65 and 1.75. The sinter strength increases when sinter basicity is between 1.75 and 2.0. Meanwhile, the sinter strength and RDI +3.15 improve with increasing carbon content. And the sinter strength and RDI+3.15 both decrease with the decrease of the distribution ratio of small fuel particle, thereby decreases the yield of sinter. Microstructural analyses have been investigated to figure out the mechanism of the influence of the three factors on sinter.

Mar 1, 2017

By Guangliang Wu, Dongchang Huang, Xinbin Liu

Oxidation Kinetics of SPHC was analyzed by TGA, and the curve of oxidation weight gain with different temperature was acquired. It is found that, when the oxidation temperature is between 500 and 600 , all the curves are linear; when the oxidation temperature is above 700 , the curves are close to parabolic. At the temperature of 900 , the oxidation weight gain increases dramatically. The TGA results indicate that the activation energy of SPHC steel is 146.19 kJ/mol at the temperature of 500 900 , and an oxidation kinetic model was set up for variable temperature. Based on the temperature change during rolling process, numerical simulation of oxide scales evolution was carried out for SPHC steel, and the simulation result agreed well with measured ones. It can provide a basis for estimating the scale growth and controlling the temperature on site.

Jan 1, 2016

By Wei Yin, Bin Xu, Qian Li, Yongbin Yang, Tao Jiang

Copper anode slime is an increasingly significant resource for precious metals such as Au, Ag and Pd. The extraction of Au, Ag and Pd from decopperized anode slime by different pretreatments and different lixiviants including cyanide, chloride, thiourea and thiosulfate have been investigated. When oxidizing roasting pretreatment was carried out under the conditions of roasting time 120min and temperature 625 ℃, the removal ratios of S and Sb could reach 82.18% and 98.52%, respectively. And the following alkaline leaching of calcine could result in the dissolution of 46.40% Cu and 98.48% Pb. The optima leaching ratios of Au, Ag and Pd reached 99.48%, 97.69%, 94.79% by cyanide leaching, and 95.01%, 79.84%, 96.59% by chloride leaching, and about 95.21%, 95.66%, 48.79% by thiourea/thiosulfate leaching.

Jan 1, 2015

By Li Kaihua, Li Liang, Miao Qingdong, Wang Cong

The current process of production of titanium sponge involves the use of TiCl4 as a feed material and a huge amount of heat is generated during the magnesiothermic reduction process. For this reason, it is possible to agglomerate into a titanium lump with the partial high temperature. And, it is difficult to obtain soft titanium sponge with low content of impurities. In order to solve the current problems in the titanium sponge production process, process optimization experiments study of TiCl4 feeding speed, vacuum distillation temperature, system pressure and time control had been conducted for obtain high quality titanium sponge. Experimental results show that lower feeding speed can improve the output capacity of titanium sponge and softer products can be obtained. The product grade rate of titanium sponge improved significantly.

Jan 1, 2015

By R. E. Moore

The lining systems currently in use in BOF furnaces, certain steel ladles, and the slag line of electric are furnaces were developed during the late seventies through the mid-eighties using a trial and error method of combining aggregate, carbon sources, additives and binders. They are currently based on magnesia, graphite, metal additives and resin binders, the selections of each being tied to the anticipated intensity of the use conditions. The general functions of the respective constituents are well appreciated, however, there is still a great deal that is not known about how the socalled antioxidants protect the graphite nor how impurities from the graphite and the aggregate enter into the wear processes. In a simplified assessment of wear processes, it appears that if the deoxidized layer can be kept very thin, less than 810 mm in depth, and if the viscosity and quantity of the matrix glassy phases can be controlled to resist erosion of the deoxidized layer, lining life can be maximized for the various applications. This paper will discuss the characteristics of the starting materials systems currently being employed for applications requiring a deoxidation function to realize extended wear. It will not attempt to explain all the complex interrelationships between the respective constituents but will point to the potential for improvements through the use of improved constituents.

Jan 1, 1991

By Runsheng Xu, Haiyang Wang, Pengcheng Zhang, Tengfei Song

Semi coke, a byproduct in the chemical industry, is a new fuel for blast furnace injection in China. In this study, semi coke and bitumite were milled into different size, ranged from 0.147mm to under 0.074mm. The content of volatile matter and ash, which affect the combustibility of semi coke, were measured using muffle furnace. The mixture, in which the proportion of coal in different sizes changed, was blend by semi coke and bitumite with different size. Activation energy calculation and the comprehensive combustion characteristic index of all kinds of blends was also discussed. The result obtained by Thermogravimetry –Derivative Thermogravimetry curves indicates that the smaller the size of mixture is, the lower for the characteristic temperature, and the better for its combustibility, Semi coke can be a substitute for anthracite in blast furnace injection.

Jan 1, 2015