Search Documents

By Liang Li

Thermodynamic analysis and experiments were conducted in order to verify the feasibility of preparing crude titanium tetrachloride (TiCl4) via the carbochlorination of low-grade titanium slag in molten salt. Titanium slag, assaying 74.6 wt% TiO2 with high calcium and magnesium oxide impurities, was treated by an optimized carbochlorination process in NaCl molten salt. These impurities in the titanium slag were chloridized simultaneously, and chlorination products FeCl2, MnCl2, MgCl2, CaCl2 and CrCl3 were collected in the furnace slag. XRD and SEM/ EDS analysis of residue shown that SiO2 and Al2O3 in titanium slag were difficult to chlorinate completely. Theoretical calculations and industrial-scale experimental studies reveal the content of TiCl4 in the products was more than 98.8 wt% and thus proved the feasibility of utilizing low-grade titanium slag for TiCl4 preparation by molten salt chlorination technology.

By Mei Song, Qingyu Deng, Xuewei Lv, Lu Liu, Chenguang Bai, Meilong Hu

"The carbochlorination of several silica materials was carried out in the temperature range from 900 °C to 1200 °C. In this study, silica oxides and gaseous chlorine with carbon as reductant were used. The optimal carbon silica mole ratio in different temperature was calculated by Factsage software and the results showed that the optimal values are 1.2, 1.4, 1.6, 1.8 at 900 °C, 1000 °C, 1100 °C, 1200 °C, respectively. According to the experiments, the chlorination ratios of several silica materials were increased with temperature increasing. In the same temperature, the chlorination ratio of diatomite is the maximum and the chlorination ratio reaches 79%% when C/SiO2 reaches 3 at 1100 °C.1, IntroductionPolycrystalline silicon is the main material to manufacture the silicon polished section, solar battery[1] and high purity silicon wafers[2], also which is the most basic function material of semi-conductor industry, electronic information industry and solar photovoltaic battery industry[3]. The conventional manufacturing process of polycrystalline silicon would be divided into three parts: the improved Siemens method, which was introduced and became the main process to produce the polysilicon products in China. Silane method and fluidized bed method. Silicon tetrachloride and chlorosilans have been employed as by-products in several fields like electronic, telecounications and metallurgy[4-6]• At present, the main applications of silicon tetrachloride include production of trichlorosilane by catalytic hydrogenation, synthesis of fumed silica and ethyl orthosilicate, production of optical fiber grade silicon tetrachloride.The conventional routes for the silicon tetrachloride production have been reported, including the direct chlorination and the chlorination process of ferrosilicon, abandon catalyst and silica[7]."

Jan 1, 2013

By Jie Li

Series of carbon compounds as anode materials were prepared for super lithium ion capacitor using graphite and active carbon (AC) as raw materials. Their electrochemical properties were investigated by constant current charge-discharge test. The results showed that the compound anode had good capacitive performance as well as Li-ion battery performance. The potential of the capacitor could be as high as 3.5V vs Li/Li+ when compared with 2.5V vs Li/Li+ in the AC-AC capacitor, accordingly, the energy density increased from 21.7Wh/kg to 40.3Wh/kg. The compound anode also had excellent rate performance that as the current density increasing from 0.1A/g to 1A/g,the capacitance decreased only 1.3F/g, and good cycle performance that the capacitance holding remained 96.7% after 10 times cycles even at the highest potential of 3.5 V vs Li/Li+.

Jan 1, 2009

By James O'Brien, Lyman Frost, S. Elangovan, J. Stephen Herring, Joseph Hartvigsen, Carl Stoots, Anthony Nickens

"Carbon dioxide recovered from concentrated sources, such as metallurgical reduction furnaces, cement kilns and fossil power plants can provide a valuable feedstock for a synthetic fuels industry based on energy from nuclear, solar, wind and hydropower sources. High temperature co-electrolysis of CO2 and steam to produce synthesis gas has been demonstrated using reversible solid oxide fuel cell technology. Where a source of high temperature process heat is available, such as from an advanced high temperature nuclear reactor or solar dish concentrator, the endothermic electrolysis reactions can utilize both thermal and electrical inputs in such a way that the conversion efficiency within the cell is 100%. Synthesis gas produced in a coelectrolysis cell has been further reacted over a catalyst to produce conventional hydrocarbon fuels. Widespread implementation of synfuel production from CO2 will enable a much larger reliance on intermittent renewable energy than can be accommodated by conventional electric demand profiles.IntroductionFor the past several years, Ceramatec, Inc and the Idaho National Laboratory (INL), have been studying the feasibility of high temperature solid oxide electrolysis for large-scale, nuclearpowered hydrogen production under the U.S. DOE’s nuclear hydrogen initiative (NHI) as an alternative to the thermochemical process. Parallel to this effort, the INL and Ceramatec have been researching high temperature co-electrolysis of mixtures of steam and CO2 to produce syngas:"

Jan 1, 2008

By Fuming Wang, Xin Lu, Hao Bai, Hebin Zhu

"In this study, CO2 emissions and carbon footprint of a typical steel works with integrated process and iron and steel industry in China was calculated and analyzed by a carbon footprint method based on the model of process CO2 emissions in iron and steel making. The carbon footprint of iron and steel industry from 1991 to 2010 in China showed a rapid increasing tendency. In 2008, the CO2 emissions of iron and steel industry in China was 1.289 billion tons, 19.71% of the national total CO2 emissions, and the corresponding carbon footprint was 159.13 million hm2 of green area. Carbon deficit of iron and steel industry also go up gradually if considering the carbon storage by green vegetation. Thus, the internal carbon reduction strategy, such as energy structure optimization and energy saving technology, was mainly encouraged for the sustainable development of iron and steel industry in China.IntroductionThe Global Warming resulting from the increase of Greenhouse Gases (GHGs), in particularly CO2, in the atmosphere has become the main reason of global climate change, and large emission reductions are required for sustainable development [ 1]. The iron and steel industry is the largest energy consuming manufacturing [2] in the world and the largest emitter of CO2 emissions. In 2005, it accounted for about 20% of global industrial energy use and 30% of energy and process CO2 emissions from industry [3]. In China, the crude steel has firmly been ranking at first of the world recent years and kept growing tendency year by year. With the production growth, the CO2 emissions of iron and steel industry also increased significantly and hence the steel industry has become one of the most sources of CO2 emission in China [4], which has attracted more and more attention to seek the carbon reduction strategies.Carbon footprint is an important and useful concept originating from Ecological Footprint, which was used efficiently to quantitatively analyze the impact of the human activities on ecological system, in particularly impact of the human energy activities [5]. In the view of Life Cycle, the carbon footprint is efficient to analyze the direct and indirect CO2 emission in the whole life of various products used in human activities. As to the iron and steel, the important materials and products in the human life, the carbon footprint analysis is quite necessary to evaluate the CO2 emission impact on the corresponding ecological system and global environmental."

Jan 1, 2013

By Tianzu Yang, Weifeng Liu, Lin Chen, Wei Chen, DUCHAO ZHANG, HUI XIAO

Carbonaceous refractory materials are widely accepted in many reducing smelting processes such as iron and ferroalloys. Oxidizing processes such as copper concentrate smelting traditionally use magnesia and/or alumina/silica refractory materials. The main objection to the use of carbon-based refractories as the exposed working lining in oxidizing applications is the potential for free oxygen to react with the carbon at high temperature, which could rapidly degrade the refractory lining. In 2013, Outotec and GrafTech conducted joint trials of a thermally conductive, carbonaceous lining for smelting copper concentrates in the Outotec® pilot-scale top-submerged-lance (TSL) furnace in Dandenong, Australia. This testwork had two equally important goals; to demonstrate the ability of carbon refractories to withstand oxidizing process conditions, while ensuring that neither furnace operating conditions nor process stability were negatively affected by the refractory material. The paper discusses the input parameters of the trials, key observations during the testwork program, and the results and conclusions from both process and refractory design standpoints.

Jan 1, 2016

By Jilai Xue

Industrial wastes containing 30-50 wt.% Al2O3 and 40-60 wt.% SiO2 may serve as an alternative resource for producing Al-Si alloys. Various raw materials such as used refractory materials from metallurgical furnaces, coal fly ash, andalusite residues, and so on were tested in laboratory to produce Al-Si alloys using carbon-thermal reduction process. A mixture of anthracite and petroleum coke was used as reducing agent. One of the most important operations was to prepare the briquettes made of different raw materials with varying contents of Al2O3 and SiO2. The effects of briquette property, A/S ratio (mass ratio of Al2O3 and SiO2), the amount of carbon reducing agent, on the reduction process and the resulting metals were investigated. The results are useful for development of an alternative technology for Al-Si alloy production, which has the potential application in recycling metals from industrial wastes containing Al2O3 and SiO2.

Jan 1, 2010

By John Hanna

The University of Alabama Mineral Resources Institute (MRI) has developed a unique process for selective fatty acid flotation of carbonate gangue from sedimentary apatites (francolite) in the pH range of 4-6, without collector conditioning of the pulp. The process, which does not require an apatite depressant, was modified to beneficiate a high MgO siliceous phosphate matrix from South Florida. The modified process includes two flotation stages, one for carbonate removal, as mentioned above, and the other for phosphate recovery from the siliceous gangue. The selective flotation separation of the carbonate and phosphate from siliceous constituents of the matrix at various pH levels and collector dosages are discussed. In the carbonate flotation stage, about 70% of the MgO was rejected in the froth, and the phosphate flotation stage produced concentrates analyzing about 31% P20S' 0.7% MgO and 4% acid insolubles. The overall P20S recovery in the two stages is about 85%.

Jan 1, 1989

By Manjie Li, Mingrui Yang, Haijun Peng, Shuxing Qiu, Wei Liu, Shengfu Zhang

It is important to produce and utilize highly reactive coke in order to reduce the energy consumption and CO2 emissions through improving shaft efficiency in blast furnace. The present study aimed to investigate the transformation of iron minerals and properties of iron coke (the coke mixed iron ore fines). Along with the increase of iron ore fines, cold strength displayed a slight downtrend and the pore structure wasn’t inferred to be a major factor affected the properties of iron coke. During carbonization, the majority of mixed iron oxides were reduced to metallic iron by CO and H2 and the degree of metallization achieved to approximately 75%. Nevertheless, produced metallic iron was oxidized by pure CO2 during gasification. Iron coke reactivity index (ICRI) was obviously enhanced and the iron coke strength after reaction (ICSR) drastically decreases, which were also significantly influenced by crystal structure of carbon.

Jan 1, 2015

By Run Huang, Xuewei Lv, Lei Lei, Guibao Qiu, Chenguang Bai

"The TiO2-rich slag and pig iron can be produced from ilmenite concentrate by the electric furnace process. In this study, ilmenite concentrate was reduced in a vertical furnace equipped with a weighting data acquisition system. The effects of reducing agent (carbon) amount on the iron reduction were studied. The phase transformation, morphology and chemical compositions of reduced samples were investigated by X-ray diffractometry (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS), respectively. It was found that the reductive degree of ilmenite concentrate increased with the increase of reducing time. The phases of reduced samples were mostly iron, rutile, Ti3O5 and Fe2TiO5. The mass loss percentage increased with increasing the carbon amount from 8% to 12%. When the carbon amount exceeded 12%, the mass loss percentage decreased with the increasing of carbon amount.IntroductionIlmenite and rutile are the main raw materials for producing titania pigment and titanium metal. With the development of the titanium industry, huge amounts of titanium resources are needed. As sources of high-grade titania mineral decrease worldwide, more attention should be paid to the processes involving low grade mineral such as ilmenite ore. In ilmenite, MgO and CaO are the gangue parts. Therefore, the ilmenite refining becomes more and more popular. In the previous studies, the methods of ilmenite refining are electric furnace smelting, direct acid leaching, selective chlorination and thermal reduction [1]. Electric furnace smelting method is widely used in the titanium industry, however, which consumes a great deal of energies and has a high CO2 emission. Its essence is to remove iron oxides and obtain a high titania slag. So the thermal reduction of ilmenite concentrate is an important step in titanium industry, which can decrease carbon reagent consumption and save energy.Over the past several decades, many studies have been carried out on the mechanism and kinetics of the reduction of different ilmenite ores, which are as follows: The carbothermal reduction of Panzhihua ilmenite initiated at about 860 oC. In the temperatures ranging from 900 oC to 1400 oC, the reaction rate was changed like a shape of “M”. That was to say that the reaction rate increased with the growth of temperature at first, then decreased, afterward increased again and at last the reaction was arrested [2]. The Mohammad A.R group [3, 4] showed that the carbothermal reduction of primary ilmenite concentrate was faster in hydrogen and initiated at a lower reduced temperature than in argon and helium. The reduction in argon and helium had about the same rate and extent. Titanium oxycarbide started at 1000°C in hydrogen. The conversion of primary ilmenite concentrate to metallic iron and titanium oxycarbide at 1200 °C was completed in 300 minutes. Monoxide as the reductant to reduce ilmenite had been studied intensively by a few research groups [5, 6]. The rate and the degree of reduction depended on the formation of a metallic shell of iron which inhibited the transfer of CO to the reaction zones; titanium had a strong effect on the mechanism and rate of reduction of iron oxides. Wang and Yuan [7] studied the reductive kinetics of the reaction between a natural ilmenite and carbon. At temperature below 1100°C, chemical reaction was the rate controlling step, at 1100 to 1250°C mixed controlling was rate controlling step, above 1250°C diffusion through the product layer controlled the reaction. Zhang [8] investigated the reduction of natural, sintered and preoxidized ilmenite concentrates in hydrogen methane mixtures. Preoxidation and sintering of ilmenite concentrates changed their phase composition and caused a sharp decrease in specific surface area of raw materials and an increase in carburization temperature. Sintering also increased the metallization temperature of iron."

Jan 1, 2011

By Sutham Niyomwas

Synthesis of alumina-mullite-silicon carbide composite (Al2O3-Al6Si2O13-SiCw) was obtained in situ by carbothermal reduction of a mixture of kaolin and two different silica sources. The carbothermal reduction was carried out in a horizontal tube furnace under flow of argon gas. The standard Gibbs energy minimization method was used to calculate the equilibrium composition of the reacting species. The synthesized products were mixtures of alumina, mullite and silicon carbide in the form of whiskers. The effects of adding two different silica sources of rice husk ash and silica powder to the mixture of kaolin and activated carbon were investigated. XRD and SEM analyses indicate complete reaction of precursors to yield Al2O3- Al6Si2O13-SiC as product powders, with the SiC having whisker morphology.

Jan 1, 2006

By Dinabandhu Ghosh

The stability diagram of the ternary system Ti-C-O is drawn in the present work for four temperatures, 1473 K, 1573 K, 1673 K and 1873 K, showing the stability fields of TiC, Ti, TiO, Ti2O3 and TiO2. An analysis of the system reveals that it is not possible to produce Ti in a carbon-saturated system; instead, the stable product is TiC. However, Ti can be an equilibrium product in a carbon-unsaturated system at prohibitively low values of pCO and pCO2; for example, at 1873 K, these limiting values are: pCO = 10-6.76 atm and pCO2 = 10-13.36 atm, which, when exceeded, produce TiC and TiO respectively. The magnesiothermic reduction is examined through the stability diagram (log pO2 vs. 1/T) of the system Ti-Mg-O, drawn for a number of pMg values, presenting the pairwise stability fields such as Mg(l) + Ti(s), Mg(v) + Ti(s), MgO(s) + Ti(s), etc. The diagram shows that magnesium reduction of TiO to Ti is possible only at T < 1641 K with pMg = 1 atm and only at T < 1569 K with pMg = 0.5 atm. An experimental scheme for Mg vapor reduction of TiO2 is proposed in which an argon stream is passed over a Mg(liquid) evaporator at temperature T1 (say, 1234 K); the resulting Ar-Mg mixture at 1 atm is subsequently flown over a bed of TiO2 at temperature T2. A thermodynamic analysis establishes that complete reduction to Ti is possible and that the best results are obtained when T1 = T2.

Jan 1, 2006

By W. K. Connor, O&apos

The Bureau of Mines has conducted beneficiation, carbothermic reduction, and leaching tests of Mn oxide ores as part of its evaluation of the Mn and Co resources of the West- Central Arkansas District. The major Mn oxides in the ore include cryptomelane, psilomelane, pyrolusite, and lithiophorite. Cobalt is contained within the Mn oxides. Nonbeneficiated ore was reduced at 800&apos; C with coal and leached in ammonium sulfate and ammonium carbonate leach liquors. Ore concentrates were calcined at 600" C prior to reduction under the same conditions as the raw ore. Head analyses reported up to 21 ptt Mn and 0.11 pct Co. Extractions of 70 to 90 pct Mn and 40 to 60 pct Co were achieved.

Jan 1, 1992

By Animesh Jha

The carbothermic reduction of chalcopyrite has been studied in the temperature range 1073 to 1273K in presence of lime. The role of lime during the reduction process is explained and the phase equilibria leading to the metallisation of copper and iron are discussed. The effect of coal and carbon monoxide on the reduction process have been studied and the rate governing steps are identified. This investigation also cites examples of possible mechanisms of physical separation of metallic Cu from iron during the reduction process.

Jan 1, 1992

By Bing Song, Fei Xi, Xuewei Lv, Kai Zhang

The electric arc furnace process is a common method to produce high TiO2 slag from ilmenite. The pre-reduction process was proposed in recent years in order to reduce electricity consumption. In order to enhance the pre-reduction degree, high energy ball milling was proposed to improve the specific surface area of the ilmenite prior to reduction. In this study, the carbothermic reduction behavior of milled ilmenite concentrate was investigated. It was found that the ball milling method can result in a higher reduction rate and improved metallization of iron. The metallization of iron increased with increasing the time of ball milling. The metallization of iron with milling reached 89.49% when the time of ball milling was 70 min., while the FeO content decreased with 70 min. of milling from 11.84% to 4.76%.

Jan 1, 2014

By B. L. Chulu

In the carbothermic reduction of lead sulfate to produce lead, the inclusion of soda ash (Na,CO,) in the charge provides for the control of sulfur dioxide in the effluent gas. An important mechanism in the process appears to be the carbothermic reduction of the sodium carbonate whereby sodium gas and carbon monoxide are produced. These intermediates then participate in the reduction of the lead sulfate to produce lead metal and stable sulfur species in the molten slag phase. In addition, there is some evidence that the presence of lead metal in the charge may also serve to increase the lead recovery in the process. These aspects were investigated by conducting laboratory-scale smelting tests with small charges (;3g), at 1173°K(9000C). Recovery did not exceed 74w% and the role of incipient lead metal in the charge could not be clearly assessed.

Jan 1, 1993

By J. J. Moore

The application of plasma technology to process metallurgy is briefly discussed. Experiments involving in-flight reduction of minerals (taconite, chromite, in particular) with a solid-based carbon reductant are described. The resultant metallic and slag product analysis is discussed with respect to thermodynamic and kinetic considerations.

Jan 1, 1985

By Eoghan T. M Doyle

Oxide mixtures of nickel (NiO), cobalt (COO) and chromium (Cr203) were prepared with graphite in stoichiometric amounts and the powder mixtures were compacted to produce cylindrical pellets. The composition of chromium oxide in these mixtures were varied. Pressed pellets were reduced in a flowing stream of argon-4% hydrogen gas (500 ml/min). Both slow and rapid heating methods were adopted to raise the temperature of a pellet during reduction of oxides to form superalloy powder. The reduction temperature was varied between. 1523 and 1623K. The effect of heating rate and niobium oxide addition on the microstructure of the superalloy produced was studied by using ordinary light and scanning electron microscopes. New phases formed as a result of reduction were identified by X-ray powder diffraction technique. The mechanism of reduction of oxides together with the microstructure of NiCrCo alloy are discussed. The thermodynamics of formation of ternary alloy phase is elucidated on the basis of binary phase equilibria and Gibbs free energy of mixing data for the constituent alloy compositions.

Jan 1, 1992

By Stanko Nikolic

The Top Submerged Lance (TSL) technology, developed in the 1970s, is now widely used for the processing of a range of materials. TSL technology for continuous converting was first patented in the 1990s. The process is based on the use of calcium ferrite slag. Although this slag system had been applied elsewhere the phase equilibria had not been thoroughly investigated. This lead to a collaboration between the Process Technology group of Mount Isa Mines, now part of Glencore, and the Pyrometallurgy Innovation Centre (PYROSEARCH) at The University of Queensland. Through multiple research programs this complex system was successfully investigated. The results were then implemented within thermodynamic modelling tools. This combined new knowledge was then applied to the design and industrial implementation of the TSL continuous converting technology, ISACONVERT™. This paper describes the key findings of the research and how this was applied to the industrial implementation of the technology.

By Maria Margarida Lima, Maria Lucelinda Cunha, Dora Algarvio

"The main goal of the present work is the quality improvement of the recycled aggregates produced by a construction and demolition waste (C&DW) recycling facility located in Montemor-o-Novo, Portugal. The recycling process was developed on a pilot plant scale with 50 t/h of capacity. Process operations are the hammer mill comminution, magnetic separation and screening.In order to improve the knowledge on the C&DW, a characterization procedure was implemented by hand-sorting, magnetic and density separation on representative samples. On the other hand, to improve the quality of the produced aggregates, the bar screen size fractions were analysed, according to the Portuguese Standard (NP EN 933-1 2000).Wood was identified as the critical contaminant, representing 17% by weight of the total contaminants. Sieving results showed that about 97%, 76%, 56%, 98% and 57% were on the correct size range, which lower results are probably due to the type of screens and/or the material characteristics of the recycled aggregates.IntroductionThe construction and demolition waste problemConstruction and demolition waste (C&DW) is generated by the construction activity, resulting from both, buildings or other structures construction and old structures demolition. As a reference, it can be told that C&DW comprises about 40 to 50% of rubbish (concrete, asphalt, bricks, blocks and dirt), 20 to 30% of wood and related products and 20 to 30% of miscellaneous wastes [1]. In Portugal, C&DW is classified in the LER (Portuguese nick name for the European Waste List), Chapter 17, and includes a diversity of wastes, like concrete, bricks, ceramics, bricks, wood, glass, plaster, copper, zinc, lead, iron, steel, as well as insulation and roofing materials. C&DW stream has several characteristics which make it particularly difficult to deal with and are summarized in the following five items.(1) Lack of information on quantities generated: In Portugal, the C&DW sector has been neglected over the past years, which meant that there are not consistent information concerning the quantities and composition of these wastes yet. Several estimates, based in different assumptions, indicate different results, which may vary from 219 Mt to 10 931 Mt [2]."

Jan 1, 2008