By Kazuyoshi Sato, Keizo Uematsu, Nozomu Uchida

"Confocal fluorescence scanning laser microscope was applied to characterize the surface flaw of ceramics in great detail. A high potential -of the characterization technique is presented first. Then the technique was applied to clarify the relationship between the flexural strength of ceramics and the surface flaw. This kind of direct information of surface flaw should be essential for the fundamental study in this area, but has been lacking. The examination revealed that large defects are present on the machined surface of ceramics. Their size is consistent to the flexural strength measured on the material. The characterization tool was also applied to examine the formation of surface flaw in machining of ceramics.IntroductionClarification of fracture origin should be the starting point in the study on strength in ceramics. However, this task has been extremely difficult in some ceramics, such as an alumina ceramics. It may break from both internal and surface flaws. The former should reflect the quality of production process and the latter the machining. Examination of surface flaws should be very important for developing a better machining method for ceramics. The knowledge may valuable for establishing a better production process also.ExperimentAlumina Referceram (JFCC) was used as samples. They are cut to size of 3x4x40mm, and the surfaces were ground to meet the requirements of testing method for flexural strength of fine ceramics, JIS R 1601. They were soaked in an aqueous solution of fluorescence dye and evacuated with an aspirator for an hour to allow the solution penetrate into surface flaws. After excessive solution remained on the surface was removed by gentle washing, the specimens were dried at 120°C for 48 hours. The 4 point bending mode was applied to measure the fracture strength."

Jan 1, 2000

By T. Watanabe, T. Fujiwara, S-Wan Song, Y. Nakagawa, R. Teranishi, M. Yoshimura

"We have tried a new method to fabricate cobalt oxide films onto porous films directly by an electrodeposition method at low temperature. The porous substrate films (membrane-filters and paper) were placed between a LiOH solution and a CoSO4 solution and treated under electricalcurrents of ~1 mA/cm2 using carbon cathode and anode. Effects of temperatures, flow rates and electrical currents have been investigated. As a result, we found that the LiCoO2 films and Co3O4 films were successfully fabricated on paper and/or porous PTFE filters at 120 °C, while CoOOH films were deposited at 80 °C. Furthermore, LiCoO2 films did not cover whole the substrates, but was fabricated just over the anode. The chemical reactions of electrodeposition were also considered from these results.IntroductionRecent agreements on global environment require rapid progress of low energy and low waste processings for the fabrication of thin films that succeed to the mass production with the high consumption of the fossil fuels (such as physical vapor deposition°, chemical vapor deposition2), dip coating with firing3) etc.). The total energy consumption in aqueous systems should be the lowest among all these processing routes, because a much lager excess of energy is necessary to create melts, vapor, gas, or plasma than to form an aqueous solution at the same temperature4)The ""Soft Solution-Process"" (SSP) was one of the best concepts to realize the low energy and low waste fabrication of inorganic materials. 5) Generally speaking, SSP gives similar results to any other processing using fluids (such as vapor, gas plasma) and/or beam/vacuum processing. However, the total energy consumption of all these possessing routes should be the lowest in aqueous systems, because a much larger excess of energy is necessary to create melts, vapor, gas or plasma than to form an aqueous solution at the same temperature (Fig. 1). This idea can be easily demonstrated, using the simple example of BaTiO3. The energy diagram for the formation of BaTiO3 from various precursors is shown in reference 4. The driving forces (AG) for representative synthesis reaction of (1), (2), (3), (4) and(5) are 38, 727, 3685, 17 and —14kcal/mol, respectively at room temperature. 6' 7"

Jan 1, 2000

By Kurt Svens

"As zinc consumption is gradually increasing all the time in the world, many zinc plants are looking for possible expansions. As the sulphuric acid market as well as the fertilizer market in many areas is saturated, the costs for the roasting-acid plant section of the zinc plant will create problems when making feasibility calculations for possible expansions. For solving the customers' situation, two proven zinc concentrate direct leaching technologies are available. A third one, which is possible, does not have any industrially proven applications in the zinc area.IntroductionTime to time, the zinc plants in the world scrutinize their operations with respect to their cost efficiency, the total zinc recovery and the near-by or far-away consumer markets, especially the for zinc and sulphuric acid. Their preliminary profitability calculations can show that a possible total expansion is not economical, when they are looking to expand the whole roasting/acid plant - leaching - solution purification - electrowinning - casting route, as the possible market price for the sulphuric acid is low or the sulphuric acid market is too far away. Based on these facts, their economical study often indicates that implementing a zinc concentrate direct leaching option could be more favourable. Regarding this situation, several aspects concerning three alternative direct leaching methods will be discussed, of which pressure leaching and the atmospheric leaching processes have several industrial applications in the zinc industry, as the ultrafine grinding - conventional leaching process at present has none. As iron is also dissolved during zinc concentrate direct leaching, iron removal processes generally used in the zinc industry are additionally discussed below."

Jan 1, 2012

By R. W. Adams

A new process has been developed for leaching zinc sulphide concentrates at atmospheric pressure using air or oxygen plus nitrogen dioxide in dissolved or gaseous form as? an oxygen carrier. The process is flexible and can cope with variations in the degrees of retention and regeneration of dissolved nitrogen dioxide in the leaching phase. By controlled addition of concentrate a leach solution with low residual nitrate concentration can be produced. Following separation by filtration of unleached solids and elementa1 sulphur and conventional oxidation/precipitation of dissolved iron, the leach liquor can be treated with metallic zinc to remove the remaining nitrate and other meta111c impurities such as copper, cadmium and cobalt to provide a solution suitable for electrolytic recovery of zinc. Pilot scale testing of the process .has given zinc recoveries in the high nlnet1es, production of a hi.gh grade jarosite-free Pb/Ag residue (50% Pb.) and a saleable high grade of elemental sulphur. .A wide range of concentrates can be treated containing substantial levels of lead and copper as well as zinc. Indicative cost estimates suggest that the new process is competitive with alternative procedures such as pressure leaching.

Jan 1, 1990

By S. E. Khalafalla

A method for preparing ferrochromium alloys containing less than 2 pct carbon has been devised in a single vacuum furnace reactor. This method can conserve chromium and should reduce the capital and energy requirements relative to chromite electrothermal reduction. Reduced products containing less than 2 and as low as 0.01 wt pct carbon were obtained by reacting pellets of chromite and carbonaceous reductant mixtures at pressures of 0.1 to 1 ton and temperatures of 1,230° to 1,320° C. The extent of reduction increased with increased temperature and decreased pressure; however, operating conditions were limited due to the onset of significant chromium vaporization at higher temperatures and lower pressures. Foundry coke, anthracite, and carbon black were found to be superior to graphite as reductants. The reduction of chromite to metallics was found to proceed via the carbide intermediates Fe3C or Cr3C2. Lime accelerates the. rate of solid state reduction of chromite and can shorten the furnacin1r time at 1,3000 C under vacuum from 13 hours to less than three hours. Additional lime and silica are added to the hot reduced chromite after releasing the vacuum and raising the furnace. temperature to 1, 700° C. Soaking the charge for about 20 minutes gave a button of low carbon ferrochromium alloy beneath a well-defined slag layer.

Jan 1, 1985

By Andre Thess, Oleg Zikanov

"Direct numerical simulation methods are applied to study the influence of a constant magnetic field on turbulent flows of liquid metals. The flow is assumed to be homogeneous and the problem is reduced to the classical case of the turbulent flow in a 3D box with periodic boundary conditions. The main subject of the study is the anisotropy developing in a liquid metal flow affected by constant magnetic field.To investigate the long-time evolution of initially isotropic flow the large-scale forcing is applied to maintain the flow energy at a statistically steady level. It is found that the flow evolution depend strongly on the magnetic interaction parameter (Stuart number). In the case of small Stuart number, the flow remains three-dimensional, turbulent, an approximately isotropic. At large Stuart number (strong magnetic field) the turbulence is suppressed rapidly and the flow becomes two-dimensional and laminar. Very interesting is the intermittent flow evolution at moderate Stuart number. Long periods of almost two-dimensional, laminar behavior are interrupted by strong turbulent three-dimensional bursts.The influence of a constant magnetic field on scalar transport properties of liquid metal turbulence is investigated using the simplified formulation of homogeneous flow driven by an imposed mean temperature gradient. Such a flow consists primarily of two turbulent antiparallel jets providing an effective mechanism for heat transfer. It is shown that the magnetic field parallel to the mean temperature gradient stabilizes the jets and, thus, enhances heat transfer considerably."

Jan 1, 1999

By Lin Li, Xiang Li, Yifang Zheng, Jilai Xue, Jun Zhu

"Al drops and gas bubbles in the anode-cathode space of aluminum electrolysis cell are of great importance for cell operation improvement in metal loss, current efficiency and energy consumption. A direct observation on the Al drop, gas bubble and ultrasound was carried out through a see-through cell. The Al drop immersed into the cryolitic melt was found moving up and down irregularly in the anode-cathode space without electrolysis, which was then completely dissolved into the melt. During electrolysis, the Al drop came to the anode area and reacted with the gas bubbles generated on the anode. Under ultrasound, the gas bubbles were removed from the anode surface while the Al drop was kept on the side of anode. The observed phenomena were useful for technology improvement in reducing the anode-cathode distance or lowering the energy consumption in aluminum electrolysis.IntroductionDuring aluminum electrolysis, aluminum metal drop and anodic gas bubble are in close contact each other within the anode-cathode space, and the interaction between them can produce significant impact on metal loss, current efficiency and energy consumption. The motions of the Al drop and the gas bubble are also related to the dissolution of aluminum metal into cryolitic melt and the cell voltage drop due to the bubble layer covering the anode surface.A number of studies have been carried out using different types of see-through cells, where the dissolving process of metal Al into cryolitic melts (metal fog) in the anode-cathode space was directly observed and photographed [1, 2]. With the similar method, some direct observations on the anodic bubble behaviors with and without ultrasound were performed during aluminum electrolysis [3-6]. However, to our best knowledge, there is no published work on direct observation on the behavior of Al drops and anodic gas bubbles staying together within the same anode-cathode space, as well as the motion and interaction of them in cryolite-alumina melts."

Jan 1, 2011

By You-Hai Wen, Yinkai Lei, Tian-Le Cheng

A phase field model is developed to simulate the performance of SOFC electrodes. By solving the conduction equations on both the electrolyte and electrode phases, and incorporating the three-dimensional microstructure and reaction front at triple phase boundaries, the current-voltage relation of an electrode is directly simulated. By further coupling it to our recently developed coarsening model, we are able to investigate the effect of initial microstructure on the performance degradation in SOFC electrode. This model is applied to LSM-YSZ cathodes with different LSM volume fraction. The volume fraction effect on the electrode performance and its degradation rate has been analyzed and discussed.

Mar 1, 2018

By Hui-gang Wang, Mei Zhang, Min Guo

Metal-doped Ni–Zn ferrite with spinel structure was directly synthesized from treated zinc-containing electric arc furnace dust (Zn-containing EAFD) by solid state reaction method, realizing the transformation of Zn-containing EAFD from solid waste to high value-added material. A certain mass of NiCl26H2O was added to the treated Zn-containing EAFD before calcination. Then the effects of the mass ratio of treated Zn-containing EAFD to NiCl26H2O (RTZE/N, g g−1) and calcination temperature on the synthesis and magnetic properties of as-synthesized samples were systematically investigated by X-ray Diffraction, Raman Spectroscopy and Physical Property Measurement System. It is indicated that RTZE/N and calcination temperature had important influences on the synthesis of single-phase spinel ferrite and their magnetic properties. Pure metal-doped Ni–Zn ferrite, which exhibited good magnetic properties of higher saturation magnetization (Ms, 60.5 emu g−1) and lower coercivity (Hc, 49.8 Oe), was obtained when the calcination temperature was controlled at 1100 °C for 2 h with RTZE/N of 1:0.9.

Mar 1, 2017

By Takeshi Azakami

By combining the iron reduction process with the usual rotary kiln process, the direct production of metallic zinc from EAF dust is proposed. After thermodynamic estimation and desk-top experiments it is confirmed that the process is hopeful under suitable conditions. In order to get some practical test data the enlargement of the process scale was planned and the bench scale tests were carried on successfully. In these experiments a zinc ingot of PW grade was produced from EAF dust.

Jan 1, 2003

By L. M. Abrantes, A. P. Paiva

"A brief review of some innovative methods for the direct recovery of metals from loaded organic phases is presented; emphasis is given to electroreductive stripping and cementation, which are described and illustrated by examples: of current research. The recovery of silver using a two-phase electrolysis - by direct application of an electrical potential to a mixture of a metal loaded organic phase· containing Cyanex 471X, obtained by solvent extraction, and a stabilized sodium thiosulfate solution - is more extensively discussed. The overall efficiencies are analyzed and compared with data obtained by conventional stripping procedures. Some preliminary results achieved for the recovery of the precious metal using galvanic stripping, applied directly to similar organic solutions and involving zinc and iron powders as reducing agents, are also evaluated.Introductory ReviewThe application of hydrometallurgical methods to the recovery of metal values from ores and concentrates has been receiving a growing interest, either from researchers or from the mining industry [1].For the concentration / purification of the relatively low concentrated metallic solutions resulting from the leaching of those raw materials, solvent extraction (SX) is a well established technique [2]; the loaded organic solvent is then conventionally contacted with a suitable aqueous solution, the metal in its final form being usually recovered from this solution by electrowinning.As an efficient and / or selective stripping is sometimes difficult to achieve, depending on the specific characteristics of the system under consideration, some alternative procedures have been analyzed in order to overcome this problem. One of the chosen routes, mainly developed by Hirai and Komasawa, is to promote the reduction of the desired metal species in the organic phase, in such a way that the stripping stage becomes feasible; for the selective stripping of vanadium from a solvent containing a mixture of vanadium and molybdenum, the authors successfully used reductive [3], electro-reductive [4,5] and photo-reductive [6] techniques. The two latter methodologies have also been applied to the recovery of europium from a solvent containing europium, samarium and gadolinium [7,8].However, further processing is necessary to recover the metal in its solid state; therefore, methods causing the direct reduction of the metal species in the organic phase to their fmal metallic form would be of interest, as an intermediate step would be avoided"

Jan 1, 1997

By E. V. Redin, B. A. Dubrovsky, E. V. Knyazev, A. I. Starikov

"Ti-V magnetite is one of the most abundant composite ore resources in the world. This ore cannot be fully processed via blast furnace technology because of high content of Ti02. According to the investigations carried out in the USA and Japan ITmk3 RHF (Rotary Hearth Furnace) technology is a breakthrough in Ironmaking. Reduction, melting and slag removal can be achieved in just 10 min. The main objective of the investigation is to establish optimum operation conditions for the production of iron nuggets from Ti-V magnetite ore via the ITmk3 by means of the lab scale testing. Samples of ore from the Maly Kuybas deposit (Southern Ural), carbon reductant and fluxes were chemically analyzed. Green pellets were processed via a lab chamber furnace to simulate RHF conditions. The nuggets and slag were chemically analyzed. This preliminary test work provides valuable information which may be used for large-scale testing in a commercially sized RHF.IntroductionThe ITmk3 process upon which this paper focuses was developed by Kobe Steel in its research facilities [l]. After pilot testing at Kobe Steel's Kakogava Works in 1999-2004 the pilot demonstration plant was built and operations were successfully carried out by Mesabi Nugget joint venture in 2002-2004. Steel Dynamics put into operation the commercial plant at the Mesabi Nugget site in Hoyt Lakes (Minnesota) in 2010. Results were consistent with nugget characteristics confirming ITmk3' s flexibility with respect to raw material inputs. At the same time, no research in the field of nugget from the Ti-V magnetite bearing ore with high content of Ti02 and Alz03 has been done. It is well known, if a lot of Ti02 and Alz03 enter the blast furnace, slag becomes viscous. The viscous slag is obstacle for stable operation of the blast furnace. Besides, high content of Alz03 raises the melting temperature of gangue minerals disturbing the coalescence of reduced iron to the nuggets."

Jan 1, 2013

By K. Sadrnezhaad

Industrial and experimental induction furnaces are used for melting various types of iron ingots, returned scraps and DRI sponge pellets to produce high purity cast-iron and steel heats. The lowest consumption of the electrical energy is determined for continuous feeding operation to be 0.3 KWH/Kg for production of cast-iron in 1.5-ton industrial furnace and 0.45 KWH/Kg for production of steel in 25-Kg experimental furnace. The optimum feeding rate for lowest energy consumption is obtained to be 12.5 grams per second for continuous feeding of DRI in 25-Kg induction furnace. Similar measurements show that the optimum size of the DRI pellets is around 8 millimeter.

Jan 1, 1988

By Zongliang Zuo, Mengqi Wei, Huaqing Xie, Qingbo Yu, Qin Qin

The resource utilization of copper slag is an attractive option of iron resource. Thermal energy recovery and direct reduction (TER-DR) system was proposed in this study. By theoretica lanalysis,the exergy efficiency of this system can reach to 57.3%. To investigate the feasibility of TER-DR system, copper slag composite pellets within lignite were prepared. As a new binder, pinesaw dust was added into the pellets. The diameter of pellets was 20 mm in experiments and the compressive strength of them was up to 831 N when the addition ratio of biomass was 29%. The results showed that the overall iron recovery reached to 90% and the separated iron concentrate was up to 93.5% when thetemperature is at 1423 K for 90 min with CaO addition ratio of 0.3. The process reduces the secondary environmental pollution of copper slag and will be applied well in the future.

Mar 1, 2018

By Roberto Parra

The selective reduction smelting of Cu2O in Cu2O-FeOx-SiO2 melts has been studied at laboratory level, using as a feed a dead roasted calcine from a copper concentrate. The purpose of the study was to evaluate the kinetic and mechanisms of the indirect reduction with CO and the direct reduction with graphite from 1260°C to 1350°C. The reduction rate by CO was found to be 10-2 to 10-1 mole Cu2O m-2s-1. The graphite reduction macrokinetics for FeO and. Fe2O3 containing melts, was found to be a first order reaction with respect to the Cu2O concentration, with a kinetic constant of 104 to 10-3 s-1. The reduction rate was not sensitive to temperature nor to stirring, in the range studied. The measured reduction rate is almost one order of magnitude larger than the observed rate for the direct reduction of FeO.

Jan 1, 1999

By Ryosuke O. Suzuki

A combined process of electrolysis of CaO in the molten CaCl2 and of calciothermic reduction, so-called OS process, was applied to prepare metallic vanadium directly from V2O3. The fine metallic powder containing 1860 mass ppm oxygen was obtained using 0.5mol%CaO-CaCl2 melt for 10.8 ks at 1173 K. The oxygen level did not decrease further even when twice electricity was applied. Because the metallic vanadium could be electrochemically deoxidized to the level of 10 ppm oxygen from 1.48 %, the large amount of by-product, CaO, due to reduction and the large surface area of the fine particles are the reasons of high oxygen content in the reduced powder.

Jan 1, 2006

By Rui-Qing Li, John G. Peacey, Peter J. Hancock

"Noranda has been investigating a pyrometallurgical process for the direct recovery of zinc from zinc concentrate and zinc and iron containing residues. The process consists of injecting dry zinc concentrate and secondary zinc materials into a molten iron oxysulphide bath, volatilizing metallic zinc into furnace off gas essentially free of sulphur or S02, fixing sulphur contained in the feed materials as iron oxysulphide matte which is disposed, and recovering metallic zinc in an ISP type lead splash condenser. Combustion of petroleum coke with air or oxygen enriched air inside the oxygen containing matte supplies part of the heat, and the products of combustion dilute the zinc-laden gas to a desired level.This paper describes the process concept, thermodynamic background, experimental tests, mass and heat balance calculation for a conceptual flowsheet, environmental stability of the residue and advantages and disadvantages of the process. Experimental tests have successfully proved the process concept and thermodynamic predictions. Direct smelting of zinc concentrate and residues inside an iron oxysulfide bath has a great potential to become a cost effective and flexible zinc smelting process.1. INTRODUCTIONZinc is mainly produced by a roast-leach-electrowinning process route, which accounts for about 80% of the world primary zinc production. This process produces high quality zinc with very high zinc recovery (>95%) but suffers from several major drawbacks such as using high cost electricity as reductant, producing environmentally problematic iron containing leach residue (jarosite or goethite) and the difficulty in treating secondary zinc feed materials containing high impurity levels, such as electric arc furnace dusts from the steel industry, and other complex sources. Also in some areas, markets for sulphuric acid are distant resulting in negative realizations on acid sales.The Imperial Smelting Furnace (ISF) process is the major pyrometallurgical process to treat zinc-lead concentrate. The advantage of this process over the electrolytic zinc process is its flexibility in treating high-lead, bulk concentrates with high recoveries of lead, copper and precious metals. However, this is a two-stage process involving sintering of Zn-Pb concentrates followed by blast furnace reduction. The process requires large amounts of high-quality coke which is a major operation cost, and the sintering process which results in serious environmental problems."

Jan 1, 1996

By W. K. Connor, O&apos

Thermal Treatment Technology Division Albany Research Center, U.S. Dept. of Energy Oregon. This evaluation included a characterization study and direct smelting tests conducted in a bench-scale electric arc furnace (EAF). In contrast to other thermal treatment technologies considered for these wastes (i.e., fluidized bed combustion), direct smelting in the EAF can process 100% of the wastes without prior beneficiation, and utilizes solid oxidant additions (in this case iron ore) rather than air to oxidize the carbon. This solid oxidant addition is advantageous because it results in the production of several value-added furnace products. These products include cast iron resulting from the reduction of the iron oxides, baghouse dust containing virtually all of the zinc from the residues, and a clean (nonhazardous) slag product suitable for recycle as concrete aggregate or construction fill. Offgas from the smelting furnace also holds potential as fuel gas for cogeneration. The direct smelting tests conducted thus far were successful at producing the desired furnace products, exhibiting the potential for complete recycle of the waste pile. A cast iron product of comparable quality to conventional cast irons was produced, at nearly 80% iron recovery to the metal. The slag product was determined to be nonhazardous, based on the EPA TCLP. Lead and zinc partitioning to the dust product was greater than 99%. The material balance over the furnace indicates that for every ton of feed processed, 540 lb. of cast iron, 600 lb. of slag, and 150 lb. of dust would be produced. Energy consumption was roughly 1.10 kWxh/lb of feed material. Prior experience suggests that these figures measured in the bench-scale furnace would translate to 0040 to 0.50 kWxh/lb at the industrial-scale.

Jan 1, 2000

By K. Soldenhoff

The Bulong deposit, situated near Kalgoorlie in Western Australia and owned by Resolute Limited, is a lateritic deposit containing on average 1.1% nickel and 0.09% cobalt. A process has been developed and tested at the mini-plant scale for direct solvent extraction and separation of Co and Ni from solutions derived by acid pressure leaching of Bulong ore. In this paper, two solvent extraction processes are described. The first process uses Cyanex 272 to extract cobalt and reject nickel to the raffinate. The second process uses Versatic 10 to extract and purify nickel. The loaded strip nickel solution is suitable for electrowinning. Results of both batch laboratory tests and continuous mini-plant trials are presented. The selectivity of the solvents with respect to the major impurities such as Mn, Mg, Ca, and Zn is also discussed.

Jan 1, 1998

By Guiqing Zhang, Liansheng Xiao, Zuoying Cao, Li Zeng

A new process of direct solvent extraction of nickel from sulfuric acid leach solutions of low grade and complicated nickel resources using a novel extractant HBL110 was proposed. The basic performance of new organic system was investigated and the continuous pilot plant and the industrial test were conducted. The results indicated that the extractant of HBL110 can be used to directly extract nickel selectively over iron, aluminum, manganese, magnesium, calcium and chromium from sulfuric acid leach solutions. The loaded organic solution can be easily stripped using dilute H2SO4 solutions. Both kinetics of extraction and stripping of nickel were fast. The continuous pilot plant test with the sulfuric acid leach solution of laterite containing 6.22g/L Ni2+, 14.1g/L Fe3+, 0.73g/L Fe2+, 33.9g/L Mg2+, 1.58g/L Al3+, 0.495g/L Ca2+, 0.97g/L Mn2+ and 0.5g/L Cr3+ as feed in mixer-settlers showed that the process had run stably with 98% recovery of nickel. The concentration of nickel in strip liquors reached as high as 50 g/L while the removals of Fe3+, Fe2+, Mg2+, Al3+, Ca2+, Mn2+ and Cr3+ were 98.5%, 91.5%, 99.95%, 99.8%, 99.1%, 98.6% and 99.5%, respectively. The industrial test with the sulfuric acid leach solution of electroplating sludge containing 11.5g/L Ni2+, 2.68g/L Fe3+, 7.54g/L Cr3+, 0.61g/L Mg2+, 2.09g/L Al3+, 0.68g/L Ca2+, 0.022g/L Mn2+ and 0.154g/L SiO2 as feed in mixer-settlers also showed that the process had operated successfully with 99.5% recovery of nickel. The concentration of nickel in strip liquors reached 42.7 g/L while the removals of Fe3+, Cr3+, Mg2+, Al3+, Ca2+, Mn2+ and SiO2 were 99.2%, 99.77%, 99.73%, 99.56%, 99.57%, 98.51% and 98.75%, respectively. The new process exhibited big advantages of short flow sheet, high recovery of nickel, high removal of impurities, low chemical reagent consumption and low cost. Application of this process in industry is expected to make important impact on the extraction of nickel from sulfuric acid leach solutions and to deliver good environmental and economical benefits.

Jan 1, 2016