Search Documents

By Michael J. Nicol

This paper summarizes some of the results of a study of the reactions involved in the Caron leaching process and identifies the roles of the major dissolved species in the kinetics of dissolution of iron alloy particles formed during reductive roasting. Using rotating disk electrodes and synthetic leach solutions, the reduction of water with the evolution of hydrogen was found not to occur on a dissolving iron surface under typical leach conditions. It has been established that the oxidative dissolution is governed primarily by a reaction involving reduction of Co(III) to Co(II) ions. The reduction of oxygen was also found to make a significant but largely indirect contribution to the kinetics of the dissolution process. The dissolution rates of various iron-nickel-cobalt-copper alloys which simulate the dissolving alloy particles in a Caron plant were measured in synthetic leach solutions under aerobic and anaerobic conditions. The initial dissolution rates of iron, nickel and the iron alloys were found to increase in the presence of thiosulphate, whereas the thiosulphate had a negative effect on the dissolution rates of cobalt and copper. It is shown that the eventual passivation of the iron occurs sooner in solutions rich in Co(II) ions. Whilst these conditions are present in the quench slurry, on-site measurements have shown that due to the very high concentration of reduced dissolved species, passivation does not occur until the slurry is strongly aerated. In the light of these fundamental findings, options for optimizing the rate of dissolution and minimizing the extent of passivation of the iron and iron alloys are discussed. Keywords: Ammonia, leaching, alloy, kinetics, passivation.

Jan 1, 2004

By L. Katgerman, E. N. Straatsma, Suyitno

"Single-roll strip casting process is studied using computational fluid dynamics which takes into account fluid flow, heat transfer and solidification. The computational model is based on the conservation Jaws of momentum, energy and continuity. Correlation of strip thickness, solidification zone length, and puddle shape on single-roll strip casting of Al-1 %Mn is explored. Feeding pressure and roll speed are investigated. The results show that the··strip thickness slightly increases with pressure, similarly the length of solidification zone. The variations of strip thickness and solidification zone length with roll speed show a sharp decline for strip thickness and slight decline for the length of solidification zone with increasing roll speed. The constraint and free-jet flow have different feature in term of flow field. Severe turbulence is observed on the free-jet flow.IntroductionThe near-net shape casting of strip metals is a demand nowadays. The demand is particularly stimulated by the challenge to become more competitive through enhanced performance. The improvement in the existing processes and new innovative technologies are introduced by the metal industry to gain better product quality, more efficiency in energy consumption, low throughput, yield and operating costs [1-3].There are many advantages that can be obtained by the direct casting of strip. The most prominence is the elimination of hot rolling. Beside that the high rate of heat extraction associated with strip casting offers the possibility of a finer, Jess segregated cast structure. The microstructure will result in the improvement of mechanical properties compared to conventional material, or alternatively the opportunity of using grades of metal outside the normal range for continuous casting.The concept of single-roll strip casting has been difficult to commercialize, because of the complex interactions between fluid flow, solidification, shrinkage, and stress, which lead to serious quality problems. Besides that, the quality and the thickness of the strip are affected by the thermal properties of the strip, roll cooling conditions, roll geometry, and other process parameters. To understand how these parameters affect the strip formation, some researchers have modeled the process [4]."

Jan 1, 2004

By R. I. Rodriguez

Since the 1973 energy crisis, high fuel oil costs have been eroding the economics of the Nicaro and Punta Gorda Plants that employ the Caron Process for laterites processing. Since 1995, Cuban crude oil production has growth dramatically, with progressive utilization in power generation, cement and nickel plants. This paper shows how Nicaro and Punta Gorda plants have been able to shift from expensive Bunker C Fuel Oil to heavy but cheaper Cuban Crude Oil of high Sulfur content and achieve a significant reduction in operating cost. Problems related to the high sulfur content of the Cuban crude oil have demanded extensive investigations of the process chemistry and novelty solutions are proposed, with corresponding changes in process conditions. Innovative options are shown that will allow further cost reductions in the future. Keywords: Cuban Crude Oil, Sulfur, Ammonia.

Jan 1, 2004

By Elias Rigopoulos

In the present study the reductive behavior of dust from the rotary kilns (RK), in ferronickel production from nickeliferous Greek laterites, is investigated. The study concerns dust of various origins (washing towers, electrostatic filters, polycyclones) and pellets made from the dust. Reducibility was studied in the temperature range of 700 °C to 850 °C in a laboratory tube furnace. Experimental results showed that reduction degree increases with temperature up to about 800 °C. The rate of reduction is great during the first minutes, giving a reduction degree R% equal to about 25%, in only a few minutes. After this, the rate is decreasing until it diminishes to zero after about 10-20 minutes of reaction. Maximum reduction degree achieved is 26 to 28%. Rates and reduction degrees at various temperatures are higher for the dust samples than those of the respective pellet samples. Keywords: Ferronickel, metallurgy, laterites, pellets, reduction

Jan 1, 2004

By Stober, Frank Allan

The paper describes the development of components in an lntegrated Furnace Control system for shielded-arc smelting focusing on operation and crucible integrity enhancement. The paper reviews the mechanisms of power, feed and energy input and losses into the shielded-arc smelting process and describes the furnace control system module development and integration to tailor the process. The ultimate success of a furnace control system application is transfer of knowledge, training, and operational support during furnace start-up and ramp-up phases and a model for how this has been achieved is discussed. The control modules of a shielded-arc laterite smelting furnace are described in detail including measured results and screen captures from application in a laterite smelting furnace. This paper focuses on developments in Integrated Furnace Controls tailored to shielded-arc laterite smelting but development of common furnace control modules for improved crucible and tapping operation integrity applied to other furnace processes, including immersed-arc smelting, is also covered. Keywords: IFC, Power, Feed, Supervisory, Control

Jan 1, 2004

By Santo Ranieri

We will briefly review the nickel market in 2003 and look forward to the supply demand balance for the next few years focusing in on the key factors influencing future price dynamics. On the supply side we will examine slated brownfield and greenfield expansions including the Norilsk factor and the small to mid-range 'supply creep'. We will also review the cost side of the industry and what to expect going forward. On the demand side, we will discuss the stainless steel and non-stainless demand, the China factor and the stainless steel scrap supply cycle. We will conclude by pinpinting where the market is on the current price cycle, and where we believe the mid-term direction is headed.

Jan 1, 2004

By A. Patti, S. Reutzel, D. M. Herlach, L. Ratke, I. Egry

Cu-Co shows a metastable miscibility gap in the region of the undercooled melt. Undercooling of the melt below the binodal leads to separation of the melt into a Co-rich LI-phase and a Curich L2-phase. Experimentally, undercooling into the metastable miscibility gap is realised by means of electromagnetic levitation (EML), processing in drop tube (DT) and by melt flux embedding. As undercooling is large in these experiments, the velocity of the solidification front is high and the microstructure is frozen in instantaneously. Samples have been undercooled and solidified in the TEMPUS-facility (container less electromagnetic processing under weightlessness) during parabolic flight under reduced gravity conditions. Microstructures of solidified samples have been analysed and compared to those processed under gravitational conditions. The influence of convection on phase growth is much lower in reduced gravity. The microstructure shows spherical droplets of the minority phase, statistically dispersed in the majority phase.

Jan 1, 2004

By Tracie Zoeller, G. Paul Neitzel, Jr. Sanders

"As-cast aluminum alloy microstructures are highly segregated. Coring occurs when solute is rejected during solidification resulting in a non-uniform solute distribution across the dendrite arms. Furthermore, coarse constituent phases are formed in the interdendritic channels as a result of coring. These constituents are either soluble or insoluble and can form from the major solute elements, or the impurity elements iron and silicon. The dissolution of these constituents, or precipitates, is an important consideration in determining the microstructural evolution of an alloy. The properties of an alloy are significantly affected by the morphology of the precipitates. Precipitates can be either beneficial or detrimental to the properties of the alloy. Regardless of the nature of the precipitates present, it is useful to understand the dissolution process. A diffusion-limited dissolution model for planar precipitates is presented and compared to an analytical solution and to models in the literature. Experimental data for the dissolution of AhCu precipitates in a dilute alloy are compared to the proposed model, and found to have good agreement.IntroductionDuring the processing of precipitation hardening alloys, beginning with the solidification step and ending with the final solution heat treatment step, there are a variety of particles that form. Some of these particles must be dissolved and solute redistributed and re-precipitated in a more homogeneous distribution than as it first appears in the as-cast microstructure. The particles can be classified by size as microstructure develops during processing. Coarse particles that form during solidification can either be soluble, partially soluble or insoluble. These particles can be the result of coring of the major solute elements as well as the limited solubility of elements such as iron and silicon. Iron and silicon can combine with the major solute elements such as copper in 2xxx alloys forming coarse phases often referred to as constituents. Figure l(a) shows the as cast microstructure with the constituent phases, Al2Cu and the insoluble phases containing Al-Fe-Mn-Cu-Si [7]. During preheating the soluble phases such as AhCu that were formed by eutectic decomposition must be taken back into solution, whereas the insoluble phases remain essentially unchanged by most thermal operations. Figure l(b) and (c) show some of these constituents after subsequent preheating steps. In Figure l(b), AhCu platelets are shown and in Figure l(c) the remnants of the AhCu phase are noticeable, along with Mn-bearing dispersoid phases. Reduction in the volume fraction and size of these phases improves the ductility and fracture toughness as well as reducing the inhomogeneities that occur during coring. Also adjacent to the dendrite arm boundaries are smaller AhCu phases that precipitate by a solid-state transformation on cooling to room temperature."

Jan 1, 2004

By Ashish D. Patel, Ramesh S. Minisandram

"Vacuum Arc Remelting (VAR) is the final and, hence, critical melting step for the production of a sound, segregation-free ingot for the manufacture of alloys used in rotating components in aircraft engines. A mathematical model for this process has been developed by the Specialty Metal Processing Consortium (SMPC). The model predicts temperature distribution in the solidifying ingot, flow in the molten metal pool, and the electromagnetic field in the ingot. These predictions may be used to estimate the effect of melting parameters on the pool profile in the ingot. In this paper, typical pool shapes and flow fields during VAR of Alloy 718 and Ti-6Al-4V are presented. The differences in the pool profile are primarily due to vastly different melting conditions. The model predictions are compared to the observed pool shapes from industrial-size VAR ingots.1. IntroductionVacuum Arc Remelting (VAR) is a process in which an electrode is melted in vacuum by the heat from a DC electric arc. Metal droplets from the electrode fall into the molten metal pool, which solidifies in a water-cooled copper crucible to form the ingot, as shown in Figure I. The ingot obtained from VAR is sound, and has superior cleanliness and chemical homogeneity. Hence, the process is the final melting process for most nickel-base superalloys and titanium alloys used in the manufacture of critical rotating components (discs & blades) of aircraft engines. Modeling of this process provides an insight into the effect of melting parameters on the molten metal pool in the solidifying ingot, which is a key first step in process optimization and defect prevention. In this paper, typical pool shapes, both measured and predicted, for VAR of Alloy 718 and Ti-6Al-4Vare presented. Alloy 718 is the most common VAR-processed nickel-base superalloy; whereas Ti-6Al-4V is the ''workhorse"" alloy for titanium-based alloys."

Jan 1, 2004

By John G. Reid

When the paper "Operations at the Greenvale Nickel Project Mine and Refinery" was delivered at the 1st International Laterite Symposium in February 1979, the Yabulu Caron plant had been operating for four years and production had just stabilized. The design had been based closely on the Caron plant at Nicaro, Cuba, built in 1944, also by Freeport. Yabulu had 10 Herreshoff ore roasters and production in 1978 was 18,682 tonne nickel as impure oxide sinter and 763 tonne cobalt in a mixed sulphide with a cobalt to nickel ratio of 1 :2.5. In the 25 years since the 1st Symposium, two more roasters have been added, but dry ore processing rate has remained relatively unchanged at 2.4M Uyr to allow a lower feed rate per roaster with associated higher recovery. The ore source has changed from the domestic Greenvale mine to imports from New Caledonia, Indonesia and the Philippines. Nickel production between 1978 and 2003 has risen by 67%, cobalt has risen by 146% and the products have changed to high purity nickel compacts and "ChemGrade" cobalt salt. The plant changes that have contributed to the increased recovery, production and product value are discussed. Keywords: Caron, Yabulu, nickel, cobalt, ammonia

Jan 1, 2004

By Gordon A. Irons, Diancai Guo

"Uneven movement of scrap during melting in an Electric Arc Furnace causes operation problems: cave-ins interrupt electric power input. The movement also influences the radiation heat loss to water-cooled side panels and roof. An apparatus has been built to simulate the flow of scrap that may be interlocked. It has been observed that flow starts at the point where the suspended length of the pile bottom reaches the average scrap size, and proceeds in the form of cave-ins, but scrap pieces slide with each other as ordinary granules. After a cave-in, the pile angle usually remains much larger than the normally observed angle of repose. The force balance of a partially suspended scrap pile has been analyzed, and the equivalent cohesion due to interlocking estimated. A numerical model has been developed to simulate the scrap flow. Simulated results agree reasonably with observed phenomena.IntroductionWhen one considers the melting of steel scrap in an electric arc furnace (EAF), it is helpful to understand the movement of the material during meltdown. As industrial experience demonstrates, scrap movement greatly affects EAF operation. In a typical operation, scrap is dropped into the furnace from scrap buckets. The roof and electrodes are swung into position, and power is applied to the electrodes situated over the scrap. The electrodes ""bore"" into the scrap by melting into the steel in the immediate vicinity of the electrodes as they are lowered. If solid scrap pieces gradually slide towards the arc area, the electric power supply can be maintained at a high level, with few interruptions or drastic electrode adjustments. This results in a high production rate and low power consumption per tonne of steel produced. On the other hand, if the charge moves down unevenly, i.e. in large surges, usually called cave-ins, the electrodes must be drastically raised, and power supply frequently interrupted. This is also accompanied by a high level of harmonics induced in the power network, deteriorating the quality of electricity supplied to other users.In addition, the movement of scrap in an EAF also influences the furnace heat efficiency, as the scrap pile is much closer to the electric arcs compared to the furnace wall and roof, and absorbs more radiated heat. Early exposure of the wall and roof to the arcs will increase the heat loss due to radiation, and reduce the service life of the furnace."

Jan 1, 2004

By Emmanuel N. Zevgolis

After the Krupp-Renn process was shown to be unsuitable for treatment of the Greek nickeliferous laterites, the LM process was developed. It involved roasting reduction up to metallic iron in a Rotary Kiln (R/K) and smelting in an Electric Furnace (E/F). Ferronickel (with 15% Ni) produced in the E/F, was upgraded to 90-95% Ni in an 02 converter. Raw Ni was then electrolyzed to pure Ni. The LM process was not applied for very long however, due to various problems. So, the Larco process was developed, i.e., pre-reduction in R/Ks, smelting of the calcine in E/Fs for ferronickel production (15% Ni) and enrichment to 20% Ni, in an O2 converter. Until now, many technological improvements have been invented and applied or adjusted to the process, which have made it a fully reliable and competitive one. sohe of the improvements were the invention and application of a new granulation process for liquid ferronickel, the modification of the existing R/Ks, E/Fs and converters and the design of new ones, and others that are described in the paper. Keywords: Ferronickel, metallurgy, laterites, LM process, Larco process

Jan 1, 2004

By J. Murdoch Mackenzie

Two commercial nickel solvent extraction plants treating laterite leach solutions and using LIX®84-I have been operated in Australia. These circuits employ similar extraction chemistry but differ in their leaching and stripping operations. An alternative process involving elements of both can be conceived. The preparation of the feed solution to solvent extraction plays an important role in nickel extraction using LIX®84-I and the special features of manganese removal and cobalt oxidation in the preparation of the PLS are discussed. This paper compares these three circuit configurations with special reference to the extraction and reductive stripping of cobalt, the transfer of zinc and copper to the strip aqueous, ammonia transfer and sulfur transfer. The potential degradation of the organic and remediation using re-oximation is discussed. Keywords: Nickel, Solvent Extraction, Oxime

Jan 1, 2004

By A. Dutta, B. Devulapalli, A. Mukhopadhyay, E. W. Grald

"Computational Fluid Dynamics (CFO) has matured over the past two decades as an analysis tool for conducting virtual experiments with significant time and cost savings. It complements and reduces physical testing. CFO has penetrated the diverse materials industry in much the same way as Computer Aided Design (CAD) did more than a decade ago. As the basic numerical algorithms used in CFO have steadily improved, so have the reliability, consistency and user-friendliness improved significantly, too. Other recent trends have also contributed to the rapid growth and widespread adoption of CFO. In this presentation, CFO applications from several materials processing industries will be presented using case studies. Emphasis will be on metals, glass and semiconductor applications.IntroductionThe term materials processing covers a diverse array of industrial applications and products today. From the continuous casting of steel, to the deposition of semiconductor materials atom by atom, to the extrusion of molten polymers, materials processing applications span an incredible range of length scale, process times, pressures, temperatures and velocities. The properties of the materials themselves, in terms of density, viscosity, thermal conductivity, etc., can be complex functions of temperature, shear rate, chemical composition and time. And the processing equipment may be very complicated in geometric shape.Computational fluid dynamics (CFD), the technique of solving the governing equations of fluid motion and other related phenomena using a computer, has enjoyed widespread and rapid growth, which started in the aerospace and automotive industries. More recently, CFD has also been successfully applied to a great many materials processing problems, in spite of the challenges described in the previous paragraph. The reasons for the growing usage of CFD in materials processing are many. Using CFD to test design options and reduce the number of physical prototypes can decrease the time and cost associated with new product and process development. CFD gives insight and provides detailed predictions of operating conditions in lieu of difficult, intrusive and often expensive experimental methods. CFD can be used as an aid to scale-up processes from lab or pilot scale to full production. Troubleshooting the performance of existing equipment is often carried out with the help of CFD. Determining how an existing piece of process equipment will operate under new conditions, or with new input ,materials, is also a common task for CFD."

Jan 1, 2004

By Wilhelm Brandstätter, Johannes Steiner, Alois Triessnig, Christian Redl

"The results of numerical simulations of bubble detachment from an orifice in a horizontal plate submerged in liquid are presented. The bubbles are created by forcing gas through this orifice into stagnant liquid. The simulations are performed with a two-dimensional incompressible Lattice Boltzmann (LB) scheme. In previous works the same problem was investigated by two-phase simulations in which surface tension effects were considered by an interaction potential formulation between the phases. In contrast, in the present work a volume of fluid (VOF) model consisting of a carrier fluid and a passively advected scalar function for the calculation of gravitational and surface tension forces, respectively, is used. The aims of this study are to examine the applicability of the one-phase LB method to the numerical analysis of bubble formation and to verify the theoretical and experimental predictions of the dependencies of the departure diameter on gravitational forces, surface forces and wettability effects. To this purpose the simulations were performed at different values of gravitational acceleration g, surface tension coefficient s and contact angle ß. Nonlinear fits to the data yield functional dependencies which are in good agreement with the predictions. IntroductionBubble formation behavior is an extensively studied subject, especially in chemical engineering, power industries and metallurgical processing. Knowledge of the underlying physics of bubble motion is, for example, required for the design of chemical reaction towers and agitation tanks. Another important application is the argon gas injection through the wall of the tundish nozzle into liquid steel stream to deter clogging with solid inclusions. Argon bubble motion and its effect on flow depends greatly on different parameters, e.g. gas flow rate and size of the bubbles. Thus, if these bubbles are not managed properly, they can become encapsulated upon solidification and result in undesirable impurities in the material [1, 2]."

Jan 1, 2004

By Vanessa M. Torres

Cia. Vale do Rio Doce is currently developing Niquel do Vermelho Project. The laterite deposit is located at Carajas Mineral Province at less than 15 km from Sossego Copper Project, scheduled for start-up in 2004. The available infrastructure, includes paved roads, large capacity railroad and port complex owned by CVRD, power supply and good quality water. The project was evaluated in the past for ferronickel production. In the late 1990s, CVRD switched its attention to investigating the usage of pressure acid leaching. The combination of good metallurgical behaviour for pressure acid leach (PAL) process route with reasonable mineable grades, and existing infrastructure justified the start of engineering studies in 2002. The project approach at the engineering phase is based on the dual objective of minimizing risks while maximizing project profitability and value. CVRD is currently completing the Niquel do Vermelho prefeasibility study. This paper outlines the main outcomes of the study and future perspectives for the project.

Jan 1, 2004

By Nicholas Zabaras, Deep Samanta

"Solidification of metal aluminum and aluminum alloys is modeled on uneven surfaces characterized by sinusoidal curves. Wavelengths and amplitudes of these sinusoidal surfaces are varied to study their effects on processes like solidification, macro-segregation and inverse segregation. Solidification and macro-segregation are modeled using a slightly modified form of a stabilized finite element method developed recently to model high Rayleigh number solidification and porous media flows. For pure metal solidification, the effect of varying amplitudes and wavelengths is observed in heat transfer, fluid-flow ~nd phase change processes. The relative importance of shrinkage driven flow and solutal convection on the redistribution of solute for an alloy solidifying in a rectangular cavity is compared. The analysis is then extended by modifying one of the surfaces to a sinusoid. In this case the effects of varying amplitudes and wavelengths are studied in heat transfer, fluid flow, phase change, macro-segregation and inverse segregation processes.1 IntroductionTransport phenomenon during solidification of alloys is a major cause ofcasting defects such as segregation, micro-voids, hot tears, porosity, internal and surface cracks. Heat flow across metal and mold surfaces directly affects the phase change process and plays an important role in determining freezing conditions within the metal. In alloys, natural convection and shrinkage play an important role in determining the final solute redistribution, macrosegregation and evolution of solid macromorphology. Surface unevenness plays an important role during the early stages of solidification. It influences the heat transfer rate and fluid flow in the melt, which in turn affect the morphology and shape of the solid-liquid interface. The effect of surface unevenness on solute redistribution is important during solidification of alloys, where solute driven flow in the mushy zone is prominent. Thevik and Mo in [7] and [8] used a one dimensional model for studying surface segregation and macrosegregation in alloys under the influence of exudation and solidification shrinkage. Air-gap formation in their model was expressed through a variable convective heat transfer coefficient at the boundary. Tsai et al. in [3] and [4] have modeled macrosegregation in an aluminum-copper alloy driven by shrinkage and solutal convection. They used a single domain model based on mixture theory and solved the transport equations using finite difference methods. Our aim is to model solidification of aluminum followed by macrosegregation and inverse segregation in aluminum-copper alloys on uneven surfaces by finite element methods. These surfaces are modeled as sinusoids characterized by amplitudes, ?s and wavelengths, As, By varying As and ?s, changes in heat transfer, fluid flow, phase-change and macrosegregation are studied."

Jan 1, 2004

By Mike Adams

A comprehensive pre-feasibility study has been conducted by Companhia Vale do Rio Doce CVRD) for Niquel do Vermelho nickel laterite deposit. Within this study, five integrated flowsheet options were evaluated via batch and pilot campaigns at Lakefield Oretest, over an intensive six-month period from receipt of ore to final reporting. Key technical objectives set by the client included demonstrating the technical viability of the beneficiation of several ore types, processing through integrated pressure acid leach/mixed hydroxide precipitation (PALIMI-IP) and mixed sulfide precipitation (PALIMSP) circuits, and the treatment of barren liquors to meet stringent environmental requirements. Refining of the MHP was by ammonia re-leach and solvent extraction (SX) to produce LME-grade nickel cathodes, NiCO3, NiO and CoS. LME grade nickel and cobalt was also produced by oxidation of the MSP and hydrogen reduction on the leachate. The database and data acquisition system, along with web-based reporting, enabled rapid turnaround on both daily and more comprehensive run reports, making it possible for speedy and confident decisions on operating conditions of the complex flowsheets. The high value of developing such data is emphasized and discussed as pivotal in the successful progression of laterite projects through to sustainable commercial viability. Keywords: Flowsheet, CVRD, Nickel, Piloting, Pressure, Leach, Refining.

Jan 1, 2004

By David A. Neudorf

Known resources of nickel laterites considerably exceed nickel sulfide resources and there is a growing consensus that most new nickel production will be sourced from laterites. The development of nickel laterite projects is very capital intensive due to inherently low grades, inability to concentrate ore prior to processing, complex processing technology and typically large infrastructure requirements. This has resulted in most recently proposed projects being "mega-projects," to achieve economics of scale. However, this may result in unacceptable project risk in many cases. Furthermore, many known laterite resources are not large enough to support a mega-project. This paper describes an alternative model for nickel laterite project development that allows, smaller scale and reduces capital exposure. The requirements of this model in terms of process technology, infrastructure and commercial innovation are described. Keywords: Nickel, Laterite, Project, Economics

Jan 1, 2004

By Frank Mucciardi, Hujun Zhao, Pietro Navarra

"A heat pipe is a device having a very high effective thermal conductivity in which two-phase flow and heat transfer takes place. Recent research at McGill University has led to a new type of heat pipe that contains a flow modifier. This improvement has enabled the device to operate at the high heat fluxes encountered in the metallurgical industry.This paper summarizes the progress made to describe the fluid flow in the evaporator section of a McGill heat pipe with the goal of understanding how the flow modifier configuration is linked to the film boiling and dry-out limitations. A separated flow model, an instability analysis, a lift-off model and an energy balance model are used to calculate the theoretical CHF with varying flow modifier configurations and operation conditions. A summary of the current work to relate the flow modifier to the dry-out limitation is also given.Determining how the flow modifier affects both the film boiling and dry-out limitation will give insight into improving the flow modifier design so as to extend the operational range of McGill heat pipes in terms of maximum heat flux and heat load capabilities.IntroductionThe McGill heat pipe is a specialized two-phase heat exchanger developed for several metallurgical applications where temperatures and heat fluxes are typically close to or beyond the maximum safe range of conventional cooling technology.Over the last few years, several breakthroughs have brought this device beyond the proof-of concept stage and a series of industrial trials have been performed with success. These trials include two oxygen injection applications for the ferrous and non-ferrous industry [l], and two light metals permanent-mould casting applications [2,3]. Current projects include a blast furnace copper taphole cooling application [4], a copper smelting application and a thermal analysis probe application."

Jan 1, 2004